Switchable Photonic Crystals Using One-Dimensional Confined Liquid

Dec 28, 2016 - The PBG of the fabricated PC can be reversibly changed by switching the ... applications such as light modulators, smart windows, and s...
0 downloads 0 Views 804KB Size
Subscriber access provided by UNIV OF CALIFORNIA SAN DIEGO LIBRARIES

Article

Switchable photonic crystals using one-dimensional confined liquid crystals for photonic device application Seong Ho Ryu, Min-Jun Gim, Wonsuk Lee, Suk-Won Choi, and Dong Ki Yoon ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.6b15361 • Publication Date (Web): 28 Dec 2016 Downloaded from http://pubs.acs.org on January 3, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Switchable Photonic Crystals Using OneDimensional Confined Liquid Crystals for Photonic Device Application Seong Ho Ryu,† Min-Jun Gim,† Wonsuk Lee,† Suk-Won Choi,‡ and Dong Ki Yoon*† † Graduate School of Nanoscience and Technology and KINC, KAIST, Daejeon 34141, Republic of Korea ‡ Department of Advanced Materials Engineering for Information and Electronics, Kyung Hee University, Yongin 17104, Republic of Korea

ACS Paragon Plus Environment

1

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 22

ABSTRACT: Photonic crystals (PCs) have recently attracted considerable attention, with much effort devoted to photonic bandgap (PBG) control for varying the reflected color. Here, fabrication of a modulated one-dimensional (1D) anodic aluminum oxide (AAO) PC with a periodic porous structure is reported. The PBG of the fabricated PC can be reversibly changed by switching the ultraviolet (UV) light on/off. The AAO nanopores contain a mixture of photoresponsive liquid crystals (LCs) with irradiation-activated cis/trans photo-isomerizable azobenzene. The resultant mixture of LCs in the porous AAO film exhibits a reversible PBG, depending on the cis/trans configuration of azobenzene molecules. The PBG switching is reliable over many cycles, suggesting that the fabricated device can be used in optical and photonic applications such as light modulators, smart windows, and sensors.

KEYWORDS: Photonic crystals, Anodic aluminum oxide (AAO), Confinement, Liquid crystals, Switchable

1. INTRODUCTION Photonic crystals (PCs), defined as periodic structures of dielectric materials with different refractive indices,1 have attracted considerable attention in the fundamental sciences and for use in color displays, sensors, color printing, lasers, and many other photonic applications.2-8 The gamut of colors in PCs is obtained utilizing the forbidden propagation of light in a certain range of wavelengths, known as a photonic bandgap (PBG). The PBG strongly depends on the spatial arrangement of constituent materials;9 thus, numerous experimental approaches have been undertaken for fabricating PCs. A simple one-dimensional (1D) PC can be made in a form of a

ACS Paragon Plus Environment

2

Page 3 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

multilayer by alternately depositing different dielectric materials.10-13 More complex PC structures have been obtained for two-dimensional (2D) and three-dimensional (3D) lattices using lithographic techniques,14-16 colloidal particles,17-19 and self-assembled liquid crystal (LC) phases.20-22 Many studies addressed the question of PBG control by combining PCs with other functional materials. Among these, low molecular weight LCs are the most susceptible to electric and magnetic fields, as well as to electromagnetic waves.23-25 This characteristic becomes very important for switchable PC applications as well as for maximizing the anisotropy of LC materials. A typical LC molecule is anisotropic, with refractive indices depending on the molecular orientation. In the LC phase, there are two principal refractive indices: 1) ordinary and 2) extraordinary indices, no and ne, which can be measured when linearly polarized light propagates perpendicular and parallel to the optic axis of the LC molecule, respectively.26 Simple heating and cooling can change the refractive indices by phase transition between LC and isotropic phases; for example, by heating, the refractive index can be changed from no (or ne) to niso, here niso is the refractive index in isotropic phase ~ (2no+ne)/3. Up to this date, LCs have been incorporated into 3D opal or inverse opal structures for PBG control. In this approach, the LC refractive index can be controlled by varying the temperature, light irradiation, and by applying an electric field.27-32 However, achieving fine control of the LC refractive index remains challenging, because LC molecules should follow the spherical shape of colloids, implying that the LC molecules in a 3D structure are not uniformly oriented, even in the presence of an external field. Uniform arrangement of LC molecules is easily achieved in 1D structures,33-39 which exhibits only one principal refractive index. Therefore, a nanoporous anodic aluminum oxide (AAO)-based 1D PC is ideal for implementing this approach. A

ACS Paragon Plus Environment

3

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 22

surprising finding was that modulated nanopores of AAO films can exhibit Bragg reflection. Since Wang et al. synthesized modulated AAO films using anodization under periodic voltage,40 many attempts have been made to control the color of the reflected light by modifying the experimental conditions such as the applied voltage, current, time, and temperature, which ensure that the PBG of the AAO PCs covers a very wide range of wavelengths, from ultraviolet (UV) to near infrared.41-48 In this study, we fabricated modulated 1D AAO PCs by varying the applied electrical current, and attempted to control the PBG using nematic (N) LCs doped with photo-responsive azo-LCs. In this approach, azo-LCs triggered the phase transition between the isotropic and N phases via cis-trans isomerization, which changed the refractive index of the LCs, enabling the PBG control. The resultant photo-responsive switching device is important to realize photonic applications such as smart window and color electronic book. We conducted direct investigations using polarized optical microscopy (POM) and a spectrometer, and monitored in-situ changes in the PBG under UV on/off conditions.

2. RESULTS AND DISCUSSION

ACS Paragon Plus Environment

4

Page 5 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 1. Pulse anodization and the 1D AAO PC. (a) Periodic constant currents during the pulse anodization and schematic illustration of the 1D AAO PC. Periodic porous structures that were observed using FESEM (b) before and (c) after the pore widening, and (d) the corresponding transmittance spectra. Fabrication of the 1D AAO PC was successfully completed using pulse anodization with alternating electrical currents (with jhigh and jlow of ~11 mA/cm2 and ~2.8 mA/cm2, respectively) that were applied to the sample for 24 s and 96 s, respectively. This process was repeated 200 times, to obtain 44-µm-long nanopores (Figure S1 in Supporting Information). In general, straight pores were obtained in the high current (jhigh) regime, while branching nanopores were obtained in the low current (jlow) regime at which the anodization voltage (V) gradually decreased from Vhigh (Figure 1a). Pore branching was initiated at V =

1 2

Vhigh .49 The resultant

AAO PC exhibited a periodically modulated porous structure (Figures 1b and S1). After the fabrication process, the pores widened, increasing the air volume (Figure 1c). Although the fabricated AAO film was composed of one material, aluminum oxide (Al2O3), the effective

ACS Paragon Plus Environment

5

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 22

refractive indices in the straight and branched parts were different, owing to the different air volume ratios. The AAO film exhibited a repetitive change in the effective refractive indices along the long axis of the nanopores; thus, the film could be considered as a 1D PC with processing-dependent PBG.47 As mentioned above, the selective reflection of light from a PC can be explained in terms of the constructive interference of light at the interfaces between two different porous structures; thus,

the

PBG

of

the

1D

AAO

PC

is

governed

by

Bragg’s

equation,

2 mλ = 2(lStraight (nStraight − sinθ ) + l branched (n 2branced − sinθ )) , where λ is the reflected wavelength,

m is the diffraction order, and nstraight and nbranched are the effective refractive indices of the straight and branched pores, respectively. The parameters lstraight and lbranched are the lengths of the nanopores with nstraight and nbranched, respectively, and θ is the angle of incident white light.50 If light is normally incident onto the 1D AAO PC, Bragg’s equation can be simplified to mλ = 2(l straight n straight + l branched n branched ) . Here, lstraight and lbranched are fixed because the same type

of the AAO PC was used in all experiments. The optical properties of the modulated 1D AAO PC before and after the pore widening were compared in terms of the transmittance spectra (Figure 1d). The minimum of the PC transmittance before the pore widening was at 638 nm; thus, the film reflected the red color. After the pore widening, the transmittance minimum blueshifted to 550–610 nm, which corresponds to the yellow-green color. Because the proportion of air in the AAO film increased after the pore widening, nstraight and nbranched decreased. From Bragg’s equation, the PBG can be expected to shift toward shorter wavelengths with decreasing refractive index, which is in good agreement with our experimental result.51 The quantities for calculating the effective refractive index are summarized in Table 1. The values of l and pore diameter (Dp) were measured directly from the FESEM images of the AAO

ACS Paragon Plus Environment

6

Page 7 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

PC, and the value of interpore distance (Dint) was predicted from the empirical equation, ~ kV (k ~ 2.5 nm V-1),52 where Vstraight and Vbranched were 55 and 31 V in the cycle, respectively. Based on the measured and calculated values, we obtained the values of porosity (P) from 2

 π  D p   . The values of nstraight and nbranched were calculated using the Bruggeman  P =   D  2 3  int  effective medium approximation,53

(1 - P)

ε Al O − ε eff ε − ε eff + P air = 0 , where εeff is the effective dielectric constant of the pore ε Al O + 2ε eff ε air + 2ε eff 2

2

3

3

(nAl2O3 ~ 1.7, nair ~ 1, and ε = n2). Table 1. Length of nanopores (l), pore diameter (Dp), interpore distance (Dint), porosity (P), and calculated refractive index (n) values. l (nm)

Dp (nm)

Dint (nm)

P

neff

Straight

132

62

137.5

0.18

1.570

Branched

56

37

75

0.23

1.534

The transmittance minimum calculated from the simplified Bragg’s equation was ~ 586 nm, similar to the experimental result.

ACS Paragon Plus Environment

7

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 22

Figure 2. POM images of the photo-responsive LC mixture. (a) The molecular structures of E7 and BMAB, the weight ratio of the photo-responsive LC mixture, and its thermal phase transition. The optical textures of the LCs in a sandwich cell made by glasses were observed (b) in the N phase after cooling from the isotropic phase and with UV irradiation on (c) and off (d), at 35 °C. To demonstrate the dynamic control of the PBG, photo-responsive azo-compound 4-butyl-4′methoxyazobenzene (BMAB) was mixed with a common rod-type LC mixture, E7 (Figure 2a). The azobenzene moiety in BMAB can induce cis and trans isomers that are reversibly switched by photo-isomerization when UV irradiation is on and off, respectively.54-56 This reversible transition was observed with the photo-responsive mixture of LCs prepared in a sandwich cell made of two glass substrates with a ~3-µm-wide cell gap. The optical textures were then examined using POM. Upon cooling from the isotropic temperature, typical schlieren textures were observed in the N phase (Figure 2b), in which BMAB molecules were well-mixed with E7 because BMAM was in the trans form that is similar to a rod-shaped LC molecule (Figure 2a). UV irradiation, however, induced dramatic changes, yielding a totally dark phase. This can be explained by the trans-to-cis conversion of BMAB molecules, and by the fact that a bent-like conformation of BMAB induced the isotropic arrangement of the LC mixture (Figure 2c). This dark image was reversibly changed to schlieren textures without UV irradiation (Figure 2d). This observation confirms that the N-to-isotropic phase transition of the photo-responsive LC mixture can be easily driven by light irradiation.

ACS Paragon Plus Environment

8

Page 9 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 3. Schematic illustration of the optical setup for measuring transmittance spectra.

Figure 4. Transmittance spectra during cooling from 70 °C (isotropic phase) to 35 °C (N phase). Before investigating the PBG of the sample under light irradiation, we estimated the temperature dependence of the sample’s optical properties. It is well-known that rod-type LC molecules are aligned parallel to the long axis of nanopores when the molecules are filled in an untreated AAO film.37-39 This can be explained in terms of the surface anchoring condition. In our system, the planar arrangement of the N phase LC molecules in the nanopores implied that

ACS Paragon Plus Environment

9

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 22

the optic axis of the LC molecules was parallel to the observation direction; thus, we measured no. At temperatures sufficiently high for transforming the LC molecules into the isotropic phase, the penetrating light experienced niso, which was higher than no (niso ~ 1.61, no ~ 1.547, ne ~ 1.742 at λ ~ 500 nm),57 resulting in a smaller refractive index difference. Temperature-dependent transmittance spectra were examined upon cooling from 70 °C (isotropic phase) to 35 °C (N phase) in the optical setup illustrated in Figure 3, and the results are shown in Figure 4. In the isotropic phase, the PBG of the sample was at ~702 nm, which was red-shifted compared with the vacant AAO PC sample, because the effective refractive index was increased. The phase transition was observed at 65 °C on cooling, and this critical temperature slightly differed from that for the bulk sample (~58 °C), likely owing to the nano-confinement effect or difference in stability of N phase that is usually observed in the mixture.58-60 Upon further cooling from 60 °C to 35 °C, the PBG blue-shifted to 693 nm, because no was lower than niso, which reduced nstraight and nbranched. The overall transmittance was also reduced, owing to the opaqueness of the LCs. This preliminary result can be compared with the results of the following dynamic photoresponse experiment.

ACS Paragon Plus Environment

10

Page 11 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 5. Transmittance spectra in response to switching UV on (blue) and off (red), at 35 °C. The optical properties of light-driven switching of the sample were measured by shining light in the N phase at 35 °C, at which cis-trans isomerization could be achieved. During this process, the refractive index of the LCs confined in the pores was changed from no to niso, and vice versa, with and without shining the UV light, respectively. Figure 5 shows the irradiation-induced changes in the transmittance spectra of the sample. When the UV light intensity increased from 0 to 20.8 mW/cm2, the transmittance of the sample increased and finally the PBG red-shifted to 702 nm (Figure S2), consistent with the transmittance spectrum in the isotropic phase (blue line in Figure 4). In this condition, bent BMAB molecules in the cis configuration disorganize the LC molecules in the N phase, inducing the isotropic phase in the entire photo-responsive LC mixture. Linear rod-like BMAB molecules were obtained after turning the UV light off, inducing the N phase again to exhibit a blue shift to 695 nm (red line in Figure 4). Although photoisomerization of azobenzene from cis to trans configuration was fast, the relaxation of the LC molecules could be hindered in the confined geometry owing to a strong surface anchoring condition.44 This might explain why the transmittance measured after the cis-to-trans transformation was not identical to the bulk transmittance (695 nm). This light-driven switching was also successful via photoisomerization in the smectic A (SmA) phase (Figure S3).

ACS Paragon Plus Environment

11

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 22

Figure 6. Reversibility test as a function of time and response time, with UV light on (blue) and off (red), at 35 °C. Irradiation-induced PBG switching time was determined by measuring the change in the transmittance intensity (Figure 6). UV light (~ 40 mW/cm2) was alternately switched on and off at 35 °C. Because the transmittance in the isotropic phase was higher than that in the N phase as shown in Figure 3, the change in the transmittance provides the evidence of cis-trans isomerization. When the 1D AAO PC was UV-irradiated, the isotropic phase was induced and the transmittance intensity increased (blue lines in Figure 5). The transmittance decreased in the absence of UV irradiation, indicating the transition to the N phase (red lines in Figure 5). This reversible switching was repeated and the intensity change was nearly the same over 100 cycles (Figure S4), demonstrating that the change in the refractive index of the LC molecules in the AAO nanopore is reversible and reliable. The response time of both transitions was evaluated using these data. The rise and fall times were measured as 1.47 s and 1.44 s, respectively. These results demonstrate that our light-driven LC-based 1D AAO PC is reversible and reliable during switching of the PBG.

3. CONCLUSION In summary, we successfully fabricated a photo-responsive azo-moiety-based PC with LCs in modulated AAO nanopores. The inner surface of the nanopores can induce the planar anchoring of the LC molecules in the initial state, which reveals no. The phase transition from the isotropic to the N phase (and vice versa) can be induced by cooling (or heating) the sample and by light irradiation. In this approach, the refractive index of the LCs changes from no to niso or the other way, resulting in the shift of the PBG wavelength. We also demonstrated that this light-driven

ACS Paragon Plus Environment

12

Page 13 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

switching of the PBG is reversible with respect to the UV light irradiation though the switching time is relatively long compared with the commercial display applications. As other applications suggest that light-induced transition is the most convenient way to control the optical properties, compared with applying an electric/magnetic field or mechanical shearing, we believe that the platform proposed here can be used for designing switching devices for modulating PBG of PCs for potential optical and photonic applications such as smart window and color electronic book. Furthermore, owing to its reliability and simplicity, the proposed platform is compatible with any photo- or heat-responsive soft materials.

4. EXPERIMENTAL METHODS Sample preparation: High-purity annealed Al foil (99.99%, Alfa aesar) was cleaned by ultrasonication in acetone, followed by rinsing in ethanol and deionized water. Subsequently, the Al foil was electrochemically polished using a mixture of perchloric acid and ethanol (volume ratio of 1:5) at 20 V and 3 °C, followed by anodization at 40 V in 0.3 M oxalic acid. The pre-patterned Al foil was obtained by chemically etching the first-anodized Al2O3 in a mixture of phosphoric acid (6 wt %) and chromic acid (1.8 wt %) at 60 °C. Second anodization was performed under the same condition for 1 h, to obtain a stem porous structure, and a 1D AAO PC was obtained by pulse anodization with periodic constant currents at 11 mA/cm2 and 2.8 mA/cm2 for 24 s and 96 s, respectively, during 200 cycles. The pore was widened in 0.1 M phosphoric acid at 38 °C for 40 min and the remaining Al substrate was then removed by immersion in a mixture of cooper chloride and hydrochloric acid. The glasses were cleaned by ultra-sonication in acetone and then rinsed with ethanol and deionized water and treated with O2 plasma for 10 min to impose planar anchoring. The

ACS Paragon Plus Environment

13

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 22

sandwich cell was fabricated using two glasses with a gap of ~3 µm, using silica beads. The photo-responsive LC mixture, composed of E7 (90.8 wt%) and BMAB (9.2 wt%) (Figure S5 in Supporting Information), was filled in the sandwich cell and the pores of the AAO PC at isotropic temperature via capillary action, and then cooled to room temperature at a rate of 1 °C min-1. Temperature was controlled using a heating stage equipped with a temperature controller (LTS420 and TMS94, Linkam). The excess LC material on top the AAO was removed by scrubbing. Characterization: The cross-sectional images of the 1D AAO PC were taken using fieldemission scanning electron microscopy (FESEM, S4800, Hitachi). The birefringent textures of the photo-responsive LCs were observed using POM (LV100POL, Nikon). The transmittance spectra of the LCs-filled AAO PC were collected using a spectrometer (USB-2000+, Ocean Optics) with a solid-state light source (SPECTRA X, Lumencor) for UV (365 nm) irradiations. Transmittance intensity was recorded as a function of time using a digital storage oscilloscope (DSO-X 2012A, Agilent).

ASSOCIATED CONTENT Supporting Information. FESEM images of the 1D AAO PC; Transmittance spectra as a function of UV light intensity; Transmittance spectra of the 1D AAO PC infiltrated with a SmA LC material; Reversibility test over 100 cycles; Phase diagram of the E7/BMAM mixture; “This material is available free of charge via the Internet at http://pubs.acs.org.”

ACS Paragon Plus Environment

14

Page 15 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

AUTHOR INFORMATION * E-mail: [email protected] ACKNOWLEDGMENT The authors thank Professor Sang Bok Lee for fruitful discussions. This work was supported by a grant from the National Research Foundation (NRF), funded by the Korean Government (MSIP) (2014S1A2A2027911 and 2014M3C1A3052537).

REFERENCES 1.

Joannopoulos, J.; Johnson, S. G.; Winn, J. N.; Meade, R. D. Photonic Crystals: Molding

the Flow of Light, 2nd ed.; Princeton University Press: Princeton, NJ, 2008. 2.

Arsenault, A. C.; Puzzo, D. P.; Manners, I.; Ozin, G. A. Photonic-Crystal Full-Colour

Displays. Nat. Photonics 2007, 1, 468-472. 3.

Fenzl, C.; Hirsch, T.; Wolfbeis, O. S. Photonic Crystals for Chemical Sensing and

Biosensing. Angew. Chem. Int. Ed. 2014, 53, 3318-3335. 4.

Kim, H.; Ge, J.; Kim, J.; Choi, S.-e.; Lee, H.; Lee, H.; Park, W.; Yin, Y.; Kwon, S.

Structural Colour Printing Using a Magnetically Tunable and Lithographically Fixable Photonic Crystal. Nat. Photonics 2009, 3, 534-540. 5.

Park, H.-G.; Kim, S.-H.; Kwon, S.-H.; Ju, Y.-G.; Yang, J.-K.; Baek, J.-H.; Kim, S.-B.;

Lee, Y.-H. Electrically Driven Single-Cell Photonic Crystal Laser. Science 2004, 305, 14441447.

ACS Paragon Plus Environment

15

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

6.

Page 16 of 22

Guldin, S.; Huttner, S.; Kolle, M.; Welland, M. E.; Muller-Buschbaum, P.; Friend, R. H.;

Steiner, U.; Tetreault, N., Dye-Sensitized Solar Cell Based on a Three-Dimensional Photonic Crystal. Nano Lett. 2010, 10, 2303-2309. 7.

Wierer, J. J.; David, A.; Megens, M. M., III-Nitride Photonic-Crystal Light-Emitting

Diodes with High Extraction Efficiency. Nat. Photonics 2009, 3, 163-169. 8.

Ergang, N. S.; Lytle, J. C.; Lee, K. T.; Oh, S. M.; Smyrl, W. H.; Stein, A., Photonic

Crystal Structures as a Basis for a Three-Dimensionally Interpenetrating Electrochemical-Cell System. Adv. Mater. 2006, 18, 1750-1753. 9.

von Freymann, G.; Kitaev, V.; Lotsch, B. V.; Ozin, G. A., Bottom-Up Assembly of

Photonic Crystals. Chem. Soc. Rev. 2013, 42, 2528-2554. 10. Lotsch, B. V.; Ozin, G. A. Clay Bragg Stack Optical Sensors. Adv. Mater. 2008, 20, 4079-4084. 11. Colodrero, S.; Ocaña, M.; Míguez, H. Nanoparticle-Based One-Dimensional Photonic Crystals. Langmuir 2008, 24, 4430-4434. 12. Lotsch, B. V.; Ozin, G. A., Photonic Clays: A New Family of Functional 1D Photonic Crystals. ACS Nano 2008, 2, 2065-2074. 13. Wang, Z.; Zhang, J.; Xie, J.; Yin, Y.; Wang, Z.; Shen, H.; Li, Y.; Li, J.; Liang, S.; Cui, L.; Zhang, L.; Zhang, H.; Yang, B., Patterning Organic/Inorganic Hybrid Bragg Stacks by Integrating One-Dimensional Photonic Crystals and Macrocavities Through Photolithography: Toward Tunable Colorful Patterns as Highly Selective Sensors. ACS Appl. Mater. Interfaces 2012, 4, 1397-1403.

ACS Paragon Plus Environment

16

Page 17 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

14. Krauss, T. F.; Richard, M.; Brand, S., Two-Dimensional Photonic-Bandgap Structures Operating at Near-Infrared Wavelengths. Nature 1996, 383, 699-702. 15. Painter, O.; Lee, R.; Scherer, A.; Yariv, A.; O'brien, J.; Dapkus, P.; Kim, I., TwoDimensional Photonic Band-Gap Defect Mode Laser. Science 1999, 284, 1819-1821. 16. Akahane, Y.; Asano, T.; Song, B.-S.; Noda, S., High-Q Photonic Nanocavity in a TwoDimensional Photonic Crystal. Nature 2003, 425, 944-947. 17. Jiang, P.; Bertone, J.; Hwang, K.; Colvin, V., Single-Crystal Colloidal Multilayers of Controlled Thickness. Chem. Mater. 1999, 11, 2132-2140. 18. Schroden, R. C.; Al-Daous, M.; Blanford, C. F.; Stein, A., Optical Properties of Inverse Opal Photonic Crystals. Chem. Mater. 2002, 14, 3305-3315. 19. Aguirre, C. I.; Reguera, E.; Stein, A., Tunable Colors in Opals and Inverse Opal Photonic Crystals. Adv. Funct. Mater. 2010, 20, 2565-2578. 20. Cao, W.; Munoz, A.; Palffy-Muhoray, P.; Taheri, B., Lasing in a Three-Dimensional Photonic Crystal of the Liquid Crystal Blue Phase II. Nat. Mater. 2002, 1, 111-113. 21. Castles, F.; Day, F. V.; Morris, S. M.; Ko, D. H.; Gardiner, D. J.; Qasim, M. M.; Nosheen, S.; Hands, P. J.; Choi, S. S.; Friend, R. H.; Coles, H. J., Blue-Phase Templated Fabrication of Three-Dimensional Nanostructures for Photonic Applications. Nat. Mater. 2012, 11, 599-603. 22. Kikuchi, H.; Yokota, M.; Hisakado, Y.; Yang, H.; Kajiyama, T., Polymer-Stabilized Liquid Crystal Blue Phases. Nat. Mater. 2002, 1, 64-68.

ACS Paragon Plus Environment

17

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 22

23. Yoon, D. K.; Lee, S. R.; Kim, Y. H.; Choi, S. M.; Jung, H. T., Large-Area, Highly Aligned Cylindrical Perfluorinated Supramolecular Dendrimers Using Magnetic Fields. Adv. Mater. 2006, 18, 509-513. 24. Schadt, M., Voltage-Dependent Optical Activity of a Twisted Nematic Liquid Crystal. Appl. Phys. Lett. 1971, 18, 127-128. 25. Tazuke, S.; Kurihara, S.; Ikeda, T., Amplified Image Recording in Liquid Crystal Media by Means of Photochemically Triggered Phase Transition. Chem. Lett. 1987, 911-914. 26. Kleman, M.; Laverntovich, O. D. Soft Matter Physics: An Introduction. Springer: New York, 2003. 27. Xie, Z.-Y.; Sun, L.-G.; Han, G.-Z.; Gu, Z.-Z., Optical Switching of a Birefringent Photonic Crystal. Adv. Mater. 2008, 20, 3601-3604. 28. Ozaki, M.; Shimoda, Y.; Kasano, M.; Yoshino, K., Electric Field Tuning of the Stop Band in a Liquid‐Crystal‐Infiltrated Polymer Inverse Opal. Adv. Mater. 2002, 14, 514-518. 29. Kang, D.; Maclennan, J. E.; Clark, N. A.; Zakhidov, A. A.; Baughman, R. H., ElectroOptic Behavior of Liquid-Crystal-Filled Silica Opal Photonic Crystals: Effect of Liquid-Crystal Alignment. Phys. Rev. Lett. 2001, 86, 4052-4055. 30. Kubo, S.; Gu, Z.-Z.; Takahashi, K.; Ohko, Y.; Sato, O.; Fujishima, A. Control of the Optical Band Structure of Liquid Crystal Infiltrated Inverse Opal by a Photoinduced NematicIsotropic Phase Transition. J. Am. Chem. Soc. 2002, 124, 10950-10951.

ACS Paragon Plus Environment

18

Page 19 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

31. Kubo, S.; Gu, Z.-Z.; Takahashi, K.; Fujishima, A.; Segawa, H.; Sato, O. Tunable Photonic Band Gap Crystals Based on a Liquid Crystal-Infiltrated Inverse Opal Structure. J. Am. Chem. Soc. 2004, 126, 8314-8319. 32. Liu, Y. J.; Cai, Z.; Leong, E. S. P.; Zhao, X. S.; Teng, J. H. Optically Switchable Photonic Crystals Based on Inverse Opals Partially Infiltrated by Photoresponsive Liquid Crystals. J. Mater. Chem. 2012, 22, 7609-7613. 33. Kim, H.; Lee, S.; Shin, T. J.; Korblova, E.; Walba, D. M.; Clark, N. A.; Lee, S. B.; Yoon, D. K. Multistep Hierarchical Self-Assembly of Chiral Nanopore Arrays. Proc. Natl. Acad. Sci. U.S.A. 2014, 111, 14342-14347. 34. Lee, S.; Kim, H.; Shin, T. J.; Tsai, E.; Richardson, J. M.; Korblova, E.; Walba, D. M.; Clark, N. A.; Lee, S. B.; Yoon, D. K. Physico-Chemical Confinement of Helical Nanofilaments. Soft Matter 2015, 11, 3653-3659. 35. Lee, S.; Kim, H.; Tsai, E.; Richardson, J. M.; Korblova, E.; Walba, D. M.; Clark, N. A.; Lee, S. B.; Yoon, D. K. Multidimensional Helical Nanostructures in Multiscale Nanochannels. Langmuir 2015, 31, 8156-8161. 36. Kim, H.; Zep, A.; Ryu, S. H.; Ahn, H.; Shin, T. J.; Lee, S. B.; Pociecha, D.; Gorecka, E.; Yoon, D. K. Linkage-Length Dependent Structuring Behaviour of Bent-Core Molecules in Helical Nanostructures. Soft Matter 2016, 12, 3326-3330. 37. Ryu, S. H.; Yoon, D. K. Liquid Crystal Phases in Confined Geometries. Liq. Cryst. 2016, DOI: 10.1080/02678292.2016.1205674.

ACS Paragon Plus Environment

19

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 22

38. Ryu, S. H.; Ahn, H.; Shin, T. J.; Yoon, D. K. Direct Observation of Liquid Crystal Phases under Nanoconfinement: A Grazing Incidence X-Ray Diffraction Study. Liq. Cryst. 2016, DOI: 10.1080/02678292.2016.1234074. 39. Ryu, S. H.; Yoon, D. K. Molecular Orientation of Liquid Crystals on Topographic Nanopatterns. ACS Appl. Mater. Interfaces 2016, 8, 17707-17712. 40. Wang, B.; Fei, G. T.; Wang, M.; Kong, M. G.; Zhang, L. D. Preparation of Photonic Crystals Made of Air Pores in Anodic Alumina. Nanotechnology 2007, 18, 365601. 41. Guo, D.-L.; Fan, L.-X.; Wang, F.-H.; Huang, S.-Y.; Zou, X.-W. Porous Anodic Aluminum Oxide Bragg Stacks as Chemical Sensors. J. Phys. Chem. C 2008, 112, 17952-17956. 42. Zheng, W. J.; Fei, G. T.; Wang, B.; De Zhang, L. Modulation of Transmission Spectra of Anodized Alumina Membrane Distributed Bragg Reflector by Controlling Anodization Temperature. Nanoscale Res. Lett. 2009, 4, 665-667. 43. Liu, Y.; Chang, Y.; Ling, Z.; Hu, X.; Li, Y. Structural Coloring of Aluminum. Electrochem. Commun. 2011, 13, 1336-1339. 44. Yan, P.; Fei, G. T.; Shang, G. L.; Wu, B.; De Zhang, L. Fabrication of One-Dimensional Alumina Photonic Crystals with a Narrow Band Gap and their Application to High-Sensitivity Sensors. J. Mater. Chem. C 2013, 1, 1659-1664. 45. Shang, G. L.; Fei, G. T.; Zhang, Y.; Yan, P.; Xu, S. H.; Zhang, L. D. Preparation of Narrow Photonic Bandgaps Located in the Near Infrared Region and their Applications in Ethanol Gas Sensing. J. Mater. Chem. C 2013, 1, 5285-5291.

ACS Paragon Plus Environment

20

Page 21 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

46. Shang, G. L.; Fei, G. T.; Zhang, Y.; Yan, P.; Xu, S. H.; Ouyang, H. M.; Zhang, L. D. Fano Resonance in Anodic Aluminum Oxide Based Photonic Crystals. Sci. Rep. 2014, 4, 3601. 47. Chen, Y.; Santos, A.; Wang, Y.; Kumeria, T.; Li, J.; Wang, C.; Losic, D. Biomimetic Nanoporous Anodic Alumina Distributed Bragg Reflectors in the Form of Films and Microsized Particles for Sensing Applications. ACS Appl. Mater. Interfaces 2015, 7, 19816-19824. 48. Chen, Y.; Santos, A.; Wang, Y.; Kumeria, T.; Wang, C.; Li, J.; Losic, D. Interferometric Nanoporous Anodic Alumina Photonic Coatings for Optical Sensing. Nanoscale 2015, 7, 77707779. 49. Meng, G.; Jung, Y. J.; Cao, A.; Vajtai, R.; Ajayan, P. M. Controlled Fabrication of Hierarchically Branched Nanopores, Nanotubes, and Nanowires. Proc. Natl. Acad. Sci. U.S.A. 2005, 102, 7074-7078. 50. Snow, P. A.; Squire, E. K.; Russell, P. S. J.; Canham, L. T. Vapor Sensing Using the Optical Properties of Porous Silicon Bragg Mirrors. J. Appl. Phys. 1999, 86, 1781-1784. 51. Rahman, M. M.; Marsal, L. F.; Pallares, J.; Ferre-Borrull, J. Tuning the Photonic Stop Bands of Nanoporous Anodic Alumina-Based Distributed Bragg Reflectors by Pore Widening. ACS Appl. Mater. Interfaces 2013, 5, 13375-13381. 52. Nielsch, K.; Choi, J.; Schwirn, K.; Wehrspohn, R. B.; Gösele, U., Self-Ordering Regimes of Porous Alumina: The 10 Porosity Rule. Nano Lett. 2002, 2, 677-680. 53. Bruggeman, D. A. G.Berechnung verschiedener physikalischer Konstanten von heterogenen Substanzen Ann. Phys. 1935, 416, 636– 664.

ACS Paragon Plus Environment

21

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 22

54. Ikeda, T. Photomodulation of Liquid Crystal Orientations for Photonic Applications. J. Mater. Chem. 2003, 13, 2037-2057. 55. Urbas, A.; Klosterman, J.; Tondiglia, V.; Natarajan, L.; Sutherland, R.; Tsutsumi, O.; Ikeda, T.; Bunning, T., Optically Switchable Bragg Reflectors. Adv. Mater. 2004, 16, 1453-1456. 56. Kim, K.; Kim, H.; Jo, S.-Y.; Araoka, F.; Yoon, D. K.; Choi, S.-W. Photomodulated Supramolecular Chirality in Achiral Photoresponsive Rodlike Compounds Nanosegregated from the Helical Nanofilaments of Achiral Bent-Core Molecules. ACS Appl. Mater. Interfaces 2015, 7, 22686-22691. 57. Li, J.; Wen, C.-H.; Gauza, S.; Lu, R.; Wu, S.-T. Refractive Indices of Liquid Crystals for Display Applications. J. Disp. Technol. 2005, 1, 51-61. 58. Rauch, A. C.; Garg, S.; Jacobs, D. T., Phase Transitions in a Nematic Binary mixture. J. Chem. Phys. 2002, 116, 2213-2218. 59. Iannacchione, G. S.; Finotello, D. Specific Heat Dependence on Orientational Order at Cylindrically Confined Liquid Crystal Phase Transitions. Phys. Rev. E 1994, 50, 4780-4795. 60. Grigoriadis, C.; Duran, H.; Steinhart, M.; Kappl, M.; Butt, H.-J. r.; Floudas, G. Suppression of Phase Transitions in a Confined Rodlike Liquid Crystal. ACS Nano 2011, 5, 9208-9215. ToC figure