Synergistically Enhanced Optical Limiting Property ... - ACS Publications

Sep 1, 2017 - Meanwhile, the average thickness of the GO sheet was found to around 0.908 nm (Figure 1d), which are in accordance with previous works.(...
0 downloads 12 Views 1MB Size
Subscriber access provided by LUNDS UNIV

Article

Synergistic Enhanced Optical Limiting Property of Graphene Oxide Hybrid Materials Functionalized with Pt Complexes Rui Liu, Jinyang Hu, Senqiang Zhu, Jiapeng Lu, and Hongjun Zhu ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.7b10585 • Publication Date (Web): 01 Sep 2017 Downloaded from http://pubs.acs.org on September 2, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Synergistic Enhanced Optical Limiting Property of Graphene Oxide Hybrid Materials Functionalized with Pt Complexes Rui Liu,* Jinyang Hu, Senqiang Zhu, Jiapeng Lu, Hongjun Zhu* Department of Applied Chemistry, College of Chemistry and Molecular Engineering, Nanjing Tech University, Nanjing, 211816, China

*Corresponding author. Phone: +86-25-83172358. Fax: +86-25-83587428. E-mail: [email protected] (R. Liu), [email protected] (H. Zhu).

ABSTRACT: Recently, graphene-based materials have been well-known nonlinear optical materials for the potential application of laser protection. Two new GO-Pt complex hybrid materials (GO-Pt-1, GO-Pt-2) have been fabricated through covalent modification and electrostatic adsorption of different Pt complexes with graphene oxide (GO). The structural and photophysical properties of the resultant hybrid materials were studied. The nonlinear optical properties and optical power limiting (OPL) performance of Pt complexes, GO and GO-Pt hybrid materials were investigated by using Z-scan measurements at 532 nm. At the same transmittance, the results illustrate that functionalization of GO makes GO-Pt hybrid materials possess better nonlinear optical properties and OPL performance than those of individual Pt complexes and GO due to a combination of nonlinear scattering, nonlinear absorption, photoinduced electron and energy transfer between GO and Pt complex moieties. Furthermore, nonlinear optics and OPL performance of GO-Pt-2 are better than that of GO-Pt-1 due to not only excellent optical limiting of Pt-2 and more molecules on per area of GO, but also the way of combination of Pt-2 and GO. KEYWORDS: graphene oxide, Pt complex, optical limiting, photophysics, nonlinear optics

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1. INTRODUTION Recently, laser technology has been widely utilized in the civilian and military fields with applications in laser surgery, industrial processing communications, optical imaging and assault weapons.1 The high intensity of a laser beam can be potentially hazardous to human eyes and optical devices, thus much attention has been focused on avoiding damage from accidental laser radiation.2-4 Consequently, optical power limiting (OPL) technology has been making great progress under enormous demand.5 It is known for OPL materials that the high transmission remains under sustainable light intensities, whereas the decreasing transmission occurs gradually with increasing intensities. Nevertheless, the development of powerful optical limiters is a huge challenge because excellent optical limiting materials are still limited. To date, in order to develop highly efficient optical limiters, different mechanisms have been applied to reduce laser intensity, such as absorption, reflection and diffraction. Among these, it is worth noting that nonlinear optical (NLO) materials possessing strong nonlinear absorption or scattering responses are potential optical limiters for different laser pulses.1 Apparently, to achieve a better OPL effect, materials designed by a single strategy cannot satisfy various applications. Thus, multi-mechanistic combination and synergistic enhanced effects have been considered as promising methods to design next generation OPL materials. Due to the merits of multiple photophysical properties and varied applications in organic light-emitting diodes, low power upconversion, photocatalysis, OPL, etc., much attention has been focused on cyclometalated Pt(II) complexes.6 In addition, the optical properties and OPL performance of Pt(II) complexes could be easily tuned by structural modification of their ligands, including phosphine ligands, N-heterocyclic ligands, and acetylide ligands. By choosing the appropriate ligands, broadband and intensive reverse saturable absorption (RSA) or two-photon absorption (TPA) from visible to near-infrared region could be obtained, which is superior to that of other materials, such as C60, metalloporphyrins and metallophthalocyanines.7-10 Typical Pt(II) complexes with nonlinear absorption property are slightly colored in solution due to their main absorption bands located below ca. 400 nm and an extremely weak absorption band in the region of visible light, which endow good transparency to the OPL materials. It is worth noting that Pt(II) complexes also show superb photochemical and thermal stability, making them a class of well-known nonlinear optical materials for the potential application of laser protection.

ACS Paragon Plus Environment

Page 2 of 29

Page 3 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Graphene has attracted remarkable interest recently owing to its excellent optical transparency, mechanical flexibility and large surface area.11,12 However, the prospective applications of graphene are hampered by its poor solubility and processability because these properties are the first requirements for many practical applications. Meanwhile, as a two-dimensional carbon sheet, graphene oxide (GO) not only keeps the features of graphene, but also possesses oxygen-containing functional groups, such as carboxyl, epoxide and hydroxyl groups in the basal and edge. The presence of these functional groups allows the GO to readily swell and disperse in common solvents. Furthermore, these groups could permit the derivation from GO of small molecules and polymers, which are covalently linked to its oxygen functionalities or non-covalently absorbed on its surface.13 Feng et al.

14

observed the broadband

NLO and OPL properties of the graphene system, including GO nanosheets, graphene nanosheets (GNS), GO nanoribbons and graphene nanoribbons for nanosecond pulses (532 and 1064 nm). Moreover, it has been proved that GO-based materials exhibit multiple NLO mechanisms, such as RSA, TPA, and nonlinear scattering (NLS).15-17 These unique features make GO and its derivatives very promising candidates for designing OPL materials. GO is an excellent platform that can be employed to design and prepare novel materials with improved OPL properties by covalent or noncovalent combinations of other OPL-active substances. Over the past decade, a series of graphene-based hybrid materials functionalized, through covalent combination or electrostatic adherence, by porphyrin,18-20 phthalocyanine,21-24 oligothiophene,25 nanoparticles,26-29 carbazole,30 polymer,31-32 and ionic complexes33 have been reported. The enhanced OPL and NLO performance of hybrid materials was observed for ns pulses at 532 nm by the synergistic effect of nonlinear mechanisms (RSA, TPA and NLS) and photoinduced electron or energy transfer (PET/ET). To the best of our knowledge, however, the preparation of GO hybrid materials covalently and noncovalently functionalized with Pt(II) acetylide complexes, as well as their OPL performance, have not yet been reported. The hybrid materials are expected to qualify the improved OPL effect by synergism of different mechanisms. Meanwhile, a more in-depth study is required on the different OPL behaviors of covalently and noncovalently functionalized GO hybrid materials in one system, which is still a gap in this research field. Encouraged by these considerations, in this study, two new hybrid materials containing

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

graphene oxide functionalized with cyclometalated square-planar Pt(II) complexes via an amidation reaction and electrostatic absorption were developed (GO-Pt-1 and GO-Pt-2, scheme 1). Attachment of Pt(II) complexes to the surface of the GO, which can significantly improve its solubility, was characterized by transmission electron microscopy (TEM), atomic force microscopy (AFM), Raman spectra, Fourier transform infrared (FT-IR) spectroscopy, X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), ultraviolet–visible (UV–Vis) absorption and steady state fluorescence, which confirmed the successful functionalization of the GO by Pt-1 and Pt-2. A remarkable enhancement of OPL performance at 532 nm was observed for these hybrid materials by virtue of the efficient combination of varied NLO mechanisms. Moreover, the OPL performance of GO-Pt-2 prepared by electrostatic absorption was better than that of GO-Pt-1 prepared by covalent bonding, and the influences of NLO properties by composition and combination forms of GO and Pt(II) complex components are discussed. As a result, GO-Pt hybrid materials exhibited much improved OPL performance than GO and Pt(II) complexes at 532 nm, indicating an extraordinary synergistic enhancement effect via both the covalent and non-covalent links of GO to Pt(II) complexes.

Scheme 1. Schematic representation of the structures for GO-Pt-1 and GO-Pt-2.

2. EXPERIMENTAL SECTION 2.1. Materials and reagents All chemicals were purchased from Adamas-beta. GO was purchased from Suzhou graphene science and technology Co. Ltd. Dichloromethane (DCM), dimethyl formamide (DMF), triethylamine (Et3N), tetrahydrofuran (THF) and N,N-diisopropylethylamine (DIEA) were dried

ACS Paragon Plus Environment

Page 4 of 29

Page 5 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

and distilled under N2 before use. 4,6-Diphenyl-2,2´-bipyridine34 and phenylacetylide ligands35,36 were synthesized according to the reported literature methods. Synthetic routes for the hybrid materials are shown in scheme 2.

Scheme 2. Synthesis of GO-Pt-1 and GO-Pt-2.

2.2. Preparation of GO-Pt-1 hybrid material GO-Pt-1 were synthesized according to literature procedures.22 GO (50 mg) and excess of SOCl2 (15 mL) were refluxed for 24 h with the presence of DMF (catalytic amount). The redundant SOCl2 was removed by distillation. Then Pt-1 (300 mg) and Et3N (15 mL) were added to the GO-COCl suspension in DMF (anhydrous, 50 mL) under N2 protection. The reaction mixture was sonicated for 30 min firstly and then refluxed for 3 days. After finishing the reaction, the mixture cooled to room temperature. The water (800mL) was added to the reaction solution to precipitate the product. The residue was washed with ethanol, collected by centrifuge at 10000 rpm, and dried under vacuum to obtain the hybrid GO-Pt-1. 2.3. Preparation of GO-Pt-2 hybrid material The preparation of GO-Pt-2 is also shown in scheme 2 and GO-Pt-2 was synthesized according to the reported procedures.33 Under ultrasound, GO (50 mg) was dissolved in deionized water (100 mL), then 2% Na2CO3 solution (10 mL) was added to adjust solution pH ≈ 11. Then

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

the mixture was sonicated for 60 minutes to completely ionize the carboxy group in GO. After removing the excess Na2CO3 by washing with distilled water, the pH was adjusted between 7 and 8. 100 mL of Pt-2 (5 ×10-3 M) aqueous solution was added into the above residual. Resulting mixture was then sonicated at 25°C for 3 hours to enable GO to absorb Pt-2 sufficiently. Finally, the mixture was centrifuged at 10000 rpm, washed with ethanol or THF, and dried under vacuum to obtain GO-Pt-2. 2.4. Instruments and measurements 1

H NMR spectra of Pt complexes were measured on a Bruker AV-400 spectrometer

(DMSO-d6 as solvent, tetramethylsilane as internal standard). The results of elemental analyses for C, N, H were obtain on a Vario El III elemental analyzer. High resolution mass (HRMS) spectra were conducted on matrix assisted laser desorption/ionization-time of light mass spectrometer (MALDI-TOF-MS). High quality TEM images were taken on a JEM-2100 electron microscope and sample was fabricated by dispersing material in DMF under ultrasound and then dropping the mixture on carbon-coated copper grids. AFM images of GO-based materials were collected using the SPM D3100. Fourier transform infrared (FT-IR) spectra in this work were obtained on a Nicolet Nexus 470 spectrometer, and all samples were prepared to thin films with KBr (spectroscopic grade). XPS spectra of all samples were measured on a Thermo ESCALAB 250 spectrometer with a monochromatized Al Kα X-rays source (Ephoton = 1486.7 eV). Raman spectra of GO-based materials were performed on a HR800 (JY) spectrometer with an Ar+ (532 nm) as the excitation source. The thermal behaviors of all samples were provided by TGA curves on a Netzsch Sta 409PC instrument in N2 atmosphere. The content of Pt in GO-Pt-1 and GO-Pt-2 was determined by the inductively coupled plasma-atomic emission spectroscopy (ICP-AES), which were performed on a JY2000 Ultrace ICP Atomic Emission Spectrometer. The UV-vis absorption and fluorescence spectra were obtained by using U-3310 UV spectrophotometer (Hitachi) and LS-55 spectrofluorometer (Perkin-Elmer) respectively. The samples were dissolved in DMF, and then degassed with high purity N2 in a quartz cell for 30 min before measurement. The triplet excited-state lifetimes and transient absorption (TA) spectra of samples in degassed DMF were also obtained on an Edinburgh LP980 laser flash photolysis spectrometer, and the third harmonic output of a Nd: YAG laser (355 nm, 4.1 ns pulse width, 1 Hz repetition rate) was used as excitation source. The triplet excited-state absorption coefficient (εT)

ACS Paragon Plus Environment

Page 6 of 29

Page 7 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

at the maximum transient absorption band of each sample was calculated by the singlet depletion method. Relative actinometry was conducted to determine the triplet quantum yields (ΦT) by using SiNc in benzene (ε590 = 70 000 M−1 cm−1, ΦT = 0.20) as the reference. The NLO and OPL performance of the samples were investigated by open aperture Z-scan using a Nd:YAG laser (EKSPLA, PL2143B) and 532 nm pulses with 4 ns, operating at 10 Hz repetition rate.37 To facilitate comparison, all sample concentrations in dry DMF were adjusted to same 70% linear transmittance at 532 nm in NLO and OPL experiments. All samples were measured in 1 mm quartz cells. NLO coefficients were calculated according to literatures.23,30 The function of normalized transmittance and the position (z) is offered by TN(z)= Log[1+ p0(z)]/p0(z), and p0(z)=p00/ [1+(z/z0)2], z0 represents the length of the beam, and p00=βeff I0 Leff. βeff and I0 presents the effective nonlinear extinction coefficient and the intensity of the laser at focal point, respectively. Leff = [1-exp(-α0L)]/α0, and Leff presents the effective length of the sample, which was determined by the linear absorption coefficient α0, and actual optical path length through the sample.

3. RESULTS AND DISCUSSION 3.1. Synthesis Based on previous reports, in general, the organic functionalization of GO could be involved in two methods38: (i) covalent bonds between organic molecules with special functional groups and the oxygen-containing groups of GO, and (ii) the formation of π-π interactions or electrostatic effects between aromatic organic compounds and GO. The two approaches are extraordinary fascinating because of the fact that they allow the combination of all kinds of organic molecules onto the graphene sheets directly, which may result in effective interaction between the two parts and ultimately affect their photophysical and optoelectronic behaviors. Therefore, versatile strategies including the amidation reaction between the carboxylic groups of GO and the amino groups of Pt complexes, as well as electrostatic interaction between GO with negative charge and Pt complexes with pyridine quaternary ammonium salts were employed to prepare GO-based materials. Both methods successfully lead to the attachment of complexes to the GO surface without degrading its properties. The as-prepared hybrid materials (GO-Pt-1 and GO-Pt-2) were obtained by washing the product thoroughly with organic solvents. The GO-based materials

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

display better dispersibility than GO in DMF and result in a brown dispersion solution (Fig. S5). The structural features, photophysical properties, synergistic NLO properties and OPL performance of GO-based hybrid materials are discussed below. 3.2. Structure characterization 3.2.1. Morphological analysis The morphology of GO and hybrid materials were obtained from the TEM and AFM measurements. As shown in Figure 1a, the TEM image reveals that GO edges are smooth, without stacking and wrinkles. Meanwhile, the average thickness of the GO sheet was found to around 0.908 nm (Figure 1d), which are in accordance with previous works. 39-41 The average thickness of the GO sheet is larger than the theoretical value (0.34 nm) due to the large amounts of oxygen-containing functional groups presenting on its surface and edge. However, when GO was functionalized with Pt-1 complex by amidation reaction and Pt-2 complex by electrostatic absorption, a wrinkled texture with scrolled edge appears on the surface of both GO-Pt-1 and GO-Pt-2 hybrid sheets, as shown in Figure 1b and Figure 1c. Similarly, the average thickness of GO-Pt-1 for ca. 3.7 nm and GO-Pt-2 for ca. 7.8 nm (Figure 1e and Figure 1f) was higher than the thickness of GO in AFM images. The increased thickness may demonstrate the presence of the Pt-1 and Pt-2 complexes on the GO surface.

Figure 1. TEM image of GO(a), GO-Pt-1(b) and GO-Pt-2(c) sheets; AFM images and the thickness of GO(d),

ACS Paragon Plus Environment

Page 8 of 29

Page 9 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

GO-Pt-1(e) and GO-Pt-2(f) sheets on a mica surface.

3.2.2. Raman analysis Raman spectroscopy is widely applied to research the carbon framework of graphene materials, identifying the existence of defects. The functionalization of graphene usually results in the formation of more defects in the graphene sheets, which thus provides evidence that the functionalization has actually occurred. The obvious structural differences between GO, GO-Pt-1 and GO-Pt-2 were observed in their Raman spectra (Figure 2, λex = 532 nm). The Raman spectrum of GO shows two characteristic bands at about 1357 cm−1 (D band) and 1595 cm−1 (G band), corresponding to the disordered modes and the sp2 carbon atoms, respectively.

42-43

In

contrast to GO, the G and D bands of GO-Pt-1 are broadened and shifted to 12 cm−1 and 20 cm−1, respectively. Moreover, a similar result of the blue-shift for D and G bands in GO-Pt-2 compared with those of GO was also obtained. The observation indicates that the functionalization of the carbon framework of GO by the Pt complex could impact the place and shape of the D and G bands. In addition, functionalization of GO could lead to changes of the ID/IG ratio (intensity ratio of D to G band).

20,23

ID/IG ratios increased from 0.86 for GO to 1.02 for GO-Pt-1, whereas it

should be noted that the ID/IG ratio of GO-Pt-2 did not change significantly compared with that of GO in this study. This could be explained that the Pt-2 complex contains a crowd of aromatic ring and also undergoes π–π interactions with basal planes of GO, simultaneously, which is different from the interactions between Pt-1 and GO.23 The result of high ID/IG ratios for GO-Pt-1 is consistent with the more scrolled edges observed in the TEM images of GO-Pt-1 compared to those of GO-Pt-2. The different kinds of functionalization play an important role in the ID/IG ratio and further influence the structure and property of GO.

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

2500 1357

2000

Intensity (a.u.)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 29

GO GO-Pt-1 GO-Pt-2

1595

1500

1000

1575

1345

1588

1337

500

1200

1400

1600

1800

2000

2200

-1

Raman shift (cm ) Figure 2. Raman spectra of GO, GO-Pt-1 and GO-Pt-2 hybrid materials.

3.2.3. FT-IR studies The FT-IR spectrum is an essential method to verify the functionalization of GO with metal/complex moieties. The FT-IR spectra of GO, Pt-1, GO-Pt-1, Pt-2 and GO-Pt-2 are shown in Figure 3. In the FT-IR spectrum of GO, the characteristic absorption peaks located at 1735 cm−1 (C=O) and 1411 cm−1 (O-H) are attributed to carboxyl groups. The absorption peaks at 3409 cm−1 (O-H) and 1049 cm−1 (C-O) are characteristic vibrations of hydroxyl groups on the GO surface. The peak at 1635 cm−1 can be ascribed to the stretching vibrations of C=C or non-oxidized graphitic domains in GO. These main characteristic absorption bands of GO are consistent with previous reports.44 In Figure 3a, the main characteristic absorption peaks of Pt-1 complex at 3417 cm−1 and 2075 cm−1 correspond to the N-H characteristic stretching band of the amino group and the C≡C characteristic stretching band, respectively. In comparison with GO and Pt-1, the characteristic peak observed in the spectrum of GO-Pt-1 at 2058 cm−1 originates from the C≡C bond, which indicates that the Pt-1 complex was introduced onto GO. Meanwhile, the peak at 1735 cm−1 almost vanishes and a new peak appears at 1651 cm−1, which is assigned to the C=O characteristic absorption peak of the amide group. These results clearly confirm the formation of an amido-bond between the Pt-1 molecule and GO. 19,45 In the spectrum of Pt-2 (Figure 3b), the characteristic absorption peaks at 2969 cm−1 and 2098 cm−1 could be assigned to the stretching vibrations of C-H in the ethyl chain and the C≡C stretching peak, respectively. For hybrid material GO-Pt-2, the spectrum clearly shows the presence of vibrational bands resulting from

ACS Paragon Plus Environment

Page 11 of 29

both GO and Pt-2. The peaks at 1730 cm−1 and 2067 cm−1 can be attributed to C=O group originating from GO and the stretching vibrations of C≡C coming from Pt-2. It is worth noting that the vibrational frequency is slightly different from that of Pt-2 due to the strong ionic and π–π interactions between Pt-2 and GO.33 The observations also indicate that the interaction of GO and Pt-2 is electrostatic absorption. These results confirmed the successful formation of GO-Pt complex hybrid materials via amidation reaction and electrostatic absorption, respectively. a

b Transmittance (a.u.)

Transmittance (a.u.)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

GO

Pt-1

GO-Pt-1

4000 3500 3000 2500 2000 1500 1000

Wavenumber (cm-1)

500

GO

Pt-2

GO-Pt-2

4000 3500 3000 2500 2000 1500 1000

500

Wavenumber (cm-1)

Figure 3. FT-IR spectra of (a): GO, Pt-1 and GO-Pt-1; (b): GO, Pt-2 and GO-Pt-2.

3.2.4. XPS studies The attachment of the Pt complexes onto GO surface was also supported by X-ray photoelectron spectroscopy. The XPS survey spectra of GO and GO-Pt-1 are shown in Figure 4. It is clear that only two peaks, centered at 531 eV and 285 eV, could be attributed to O1s and C1s in the spectrum of GO.46 After the covalent functionalization of GO, the XPS spectrum of GO-Pt-1 shows two additional peaks at 77 eV and 399 eV originated from Pt4f and N1s in Pt-1 complex respectively, which implies a successful incorporation of Pt-1 complex into the hybrid material. In addition, this deduction is also confirmed by the analysis of the N region in XPS spectra, which offers further evidence concerning the presence of amide groups in the functionalized GO surface. As shown in Figure 4b and 4c, the binding energies of the N1s region in the Pt-1 complex located at 397.78, 398.57 and 399.29 eV are attributed to C–N, C=N and NH2, respectively.47 In contrast to Pt-1, the peaks of GO-Pt-1 at 398.93 eV (C=N) and 399.63 eV (NH2) show a red-shift on account of the electron-withdrawing effect of GO. The peak at 400.56 eV(N–C=O) indicates the formation of an amide bond between GO and Pt-1.22 A similar outcome for GO-Pt-2 hybrid material was presented in Fig. S6. Taken together, the XPS spectra provide additional

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

confirmation of the successful combination of Pt complexes with GO. a

C1s

O1s

Intensity (a.u.)

N1s

GO-Pt-1

Pt4f

GO

0

200

400

600

800

1000

Binding Energy (eV)

c 398.57

399.29 397.78

392

396

400

404

398.93

Intensity (a.u.)

b Intensity (a.u.)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 29

408

399.63

400.56

392

396

Binding Energy (eV)

400

404

408

Binding Energy (eV)

Figure 4. The XPS spectra of (a) GO and GO-Pt-1 and the amplified N1s XPS spectra for (b) Pt-1, (c) GO-Pt-1.

3.2.5. Thermal properties The thermal performance of GO, Pt-1, Pt-2, GO-Pt-1 and GO-Pt-2 was evaluated by TGA measurement under N2 atmosphere. As shown in Figure 5, upon heating to 265°C, GO is unstable and suffers a 35% weight loss, which is attributed to the pyrolysis of erratic oxygen functional groups on GO. An additional 10% weight loss above 275°C comes from the elimination of more stable oxygen functional groups, which is consistent with previous reports in the literature.

48-49

Pt-2, with an onset decomposition temperature of 324°C, shows better thermal stability than Pt-1, whose onset decomposition temperature is 211°C. This may be related to the existence of amino groups in Pt-1. After coupling Pt-1 and Pt-2 to GO, the thermal stability of resultant GO-Pt-1 and GO-Pt-2 is better than that of GO. The mass of GO-Pt-1 and GO-Pt-2 still remains ca. 69% and 62% at 950°C respectively, which further confirms that strong interactions exist between GO and Pt complexes. Furthermore, the thermal stability of GO-Pt-1 was better when the attachment was obtained by covalent bonding than through electrostatic deposition,

ACS Paragon Plus Environment

Page 13 of 29

100 90

e Weight (%)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

80 70

d

60

c b a

50 40 180

360

540

Temperature

720 o ( C)

900

Figure 5. TGA curves of (a) Pt-2, (b) Pt-1, (c) GO, (d) GO-Pt-2, (e) GO-Pt-1.

3.3. Optical properties 3.3.1. UV-vis absorption spectra Figure 6 displays the UV–vis absorption spectra of GO, Pt-1, GO-Pt-1, Pt-2 and GO-Pt-2 in DMF. As shown in Figure 6a, GO exhibits a broad absorption, extending to 800 nm. The absorption in the ultraviolet region is attributed to the π-π* transitions of sp2 π-conjugated network from GO. For the Pt-1 complex, it shows structured major absorption bands below 400 nm that arise from intraligand π-π* transitions. Moreover, the broad but less structured band at 400–600 nm originates from metal-to-ligand charge transfer (1MLCT)/intraligand charge transfer (1ILCT)/ligand-to-ligand charge transfer (1LLCT) transitions, based on other reported Pt(II) C^N^N acetylide complexes.9 After the covalent combination of GO and Pt-1, the absorption peak at 295 nm appearing in the spectrum of GO-Pt-1 should correspond to the combination of the intraligand π-π* transitions of the Pt-1 moiety and π-π* transitions of GO. In comparison with the spectrum of Pt-1, the slight red shift (5 nm) of the π-π* transitions absorption peak could arise from some alteration of the ground state of the Pt-1 complex due to covalent attachment to GO. In Figure 6b, the Pt-2 complex also shows strong sharp π-π* absorption bands at 288 nm and 331 nm, and the weak absorption band at 417 nm could be assigned to 1MLCT /1LLCT /1ILCT transitions, similar to those presented by the Pt-1 complex. The low-energy absorption band of the Pt-2 complex with electron-withdrawing substituent (pyridine quaternary ammonium salts unit) on the acetylide ligand is blue-shifted in comparison with the Pt-1 complex with an electron-donating

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

substituent (amino group) on the acetylide ligand, which is also consistent with other Pt(II) acetylide complexes bearing C^N^N ligands.9 The GO-Pt-2 hybrid material displays similar absorption peaks compared to Pt-2. Notably, the trend of red shift from 331 to 338 nm (△λ=7 nm) is in accordance with the covalent attachment to GO. Meanwhile, GO-Pt-1 and GO-Pt-2 have a very broad absorption from ultraviolet to visible region, which also suggests interaction between Pt complexes and GO units.33,50 The broad optical window of hybrid materials GO-Pt-1 and GO-Pt-2 is quite beneficial to extend the spectral range for the broadband OPL application. Moreover, when the absorbance value at 700 nm of GO-Pt-1 and GO-Pt-2 was kept to be identical, the absorbance value at 286 nm for GO-Pt-2 is twice than that of GO-Pt-1 at 295 nm (as shown in Figure S8), which indicated more Pt-2 complexes in per graphene sheet. ICP-AES analyses also show that Pt takes 3.61% of the total weight in GO-Pt-1 and 4.23% in GO-Pt-2 hybrid materials. a

1.2

GO Pt-1 GO-Pt-1

1.0

Absorbance (a.u.)

0.8 0.6 0.4 0.2 0.0

b

GO Pt-2 GO-Pt-2

1.0 0.8 0.6 0.4 0.2 0.0

300

400

500

600

700

800

300

400

Wavelength (nm) c

d

1.6

Abs at 295 nm

1.5

1.5

0.9

0.8 0.4

a

0.0

0.6

8

16

24

32

40

Concentration (mg/L) 0.3 0.0

Absorbance (a.u.)

f

600

700

800

1.6

f

1.2

1.2

500

Wavelength (nm) Abs at 286 nm

Absorbance (a.u.)

1.2

Absorbance (a.u.)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 29

1.2

a

1.2

0.8

0.9

0.4 8

0.6

16

24

32

40

Concentration (mg/L)

0.3 0.0

300

400

500

600

Wavelength (nm)

700

800

300

400

500

600

700

800

Wavelength (nm)

Figure 6. UV/Vis absorption spectra of (a) GO, Pt-1 and GO-Pt-1; (b) GO, Pt-2 and GO-Pt-2 in DMF. Concentration dependence of the UV/Vis absorption of (c) GO-Pt-1 and (d) GO-Pt-2 in DMF (concentrations are 6(a), 12(b), 18(c), 24(d), 30(e), 36(f), respectively). Insets are the plots of absorbance at 295 nm (GO-Pt-1)/ 286nm (GO-Pt-2) versus concentration.

Excellent dispersion is particularly important for the applications of graphene and its

ACS Paragon Plus Environment

Page 15 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

derivatives. Solution-phase UV/Vis spectra have been widely used to evaluate the dispersion of GO according to Beer’s law.19-20 The absorption spectra of GO-Pt-1 and GO-Pt-2 in DMF solutions were measured in different concentrations and shown in Figure 6c and 6d. The absorption values at 295 nm for GO-Pt-1 and 286 nm for GO-Pt-2 against different mass concentrations (mg/L) exhibit a nice linear relationship at low concentration. The mass extinction coefficients of GO-Pt-1 and GO-Pt-2 were calculated from the slope of the linear equation according to Beer’s law, and the values are 0.039 L/(mg·cm) and 0.042 L/(mg·cm)) with R values of 0.995 and 0.986, respectively. In addition, the absorbance value of GO-Pt-1 and GO-Pt-2 in DMF at other wavelengths also accords with Beer’s Law. These outcomes demonstrate excellent dispersibility of the hybrid materials in DMF, which is helpful for the follow-up application in the field of OPL devices. 3.3.2. Phosphorescence spectroscopy Phosphorescence spectroscopy could be used as an effective method for investigating the electron donor-acceptor interactions. In order to evaluate the excited-state interactions of the Pt complex and GO in the hybrid materials, emission spectra of Pt-1, Pt-2, GO- Pt-1 and GO- Pt-2 are shown in Figure 7. For the convenience to comparison, the absorbance value at the excitation wavelength of all samples was adjusted to be 0.2.51 Pt-1 in DMF shows a maximum emission band at 581 nm, which is a typical phosphorescent emission according to related reports and the sensitivity to oxygen,8-9 while GO-Pt-1 shows a weak emission peak at 578 nm. Furthermore, the emission intensity of GO-Pt-1 was quenched by 83% in comparison with that of Pt-1. Similarly, compared with the emission peak of Pt-1, Pt-2 shows an emission band at 558 nm with a hypochromatic shift of ca. 23 nm. Meanwhile, the almost complete quenching of the emission intensity for the GO-Pt-2 in DMF was observed. Additionally, phosphorescent lifetimes of the Pt-1, Pt-2, GO-Pt-1 and GO-Pt-2 were measured. Among them, the decay lifetimes of Pt-1 and Pt-2 were monoexponentially fitted with a lifetime of 95 ns and 320 ns, respectively. However, the measurable decay lifetimes of for GO-Pt-1 and GO-Pt-2 were shortened to 3.56 ns and 1.09 ns, respectively, thus indicating the triplet excited state deactivation of Pt-1 and Pt-2 in the hybrid material. Two competitive processes of the PET and ET result in the effective phosphorescence quenching in hybrid materials because the Pt complex can serve as an energy and electron donor, while graphene serves as a good acceptor of energy and electrons.20,33 In the case of GO-Pt

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

hybrids with the same GO moiety, the PET/ET process should be especially affected by the Pt moiety and interaction between the GO and Pt complexes. More efficient phosphorescent quenching in GO-Pt-2 than that of GO- Pt-1 suggests that the PET/ET process between Pt-2 and GO would be further enhanced.52

400

a

Emission intensity (a.u.)

1200

Emission intensity (a.u.)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 29

Pt-1 GO-Pt-1

300

200

100

0 500

550

600

650

700

750

800

1000

b

Pt-2 GO-Pt-2

800 600 400 200 0 500

Wavelength (nm)

550

600

650

700

750

800

Wavelength (nm)

Figure 7. Emission spectra of (a) Pt-1 and GO- Pt-1(λex = 420 nm) ; (b) Pt-2 and GO- Pt-2 (λex = 457 nm) in deoxygenated DMF, with the same value of the absorbance at excitation wavelength (0.2) .

Table 1 Electronic absorption and emission (room temperature) parameters for complexes Pt-1, Pt-2, GO-Pt-1 and GO-Pt-2.

λabs a /nm

λem b /nm

λT1-Tn c /nm

(ε/104 L·mol-1·cm-1)

(τem/ns, Φem)

(τTA/ns; εT1-Tn/L·mol-1·cm-1; ΦT)

Pt-1

290(3.5),370(0.8),477(0.4)

581(95, 0.005)

540 (110, 3317, 0.06)

Pt-2

288(3.8),331(2.9),417(1.2)

559(320, 0.031)

564 (420, 9542, 0.14)

GO- Pt-1

295,378,453

578(3.56, 0.0007)

533(12, 1103,0.01)

GO- Pt-2

286,338,416

558(1.09, 0.0001)

539(20, 2874,0.03)

a

Absorption band maximum (λabs) and molar extinction coefficient (εmax) in DMF.

b

Emission wavelength (λem)

and emission quantum yield measured in degassed aqueous solution of Ru(bpy)3Cl2 as the standard for the complexes and hybrid materials. c Nanosecond transient absorption band maxima, triplet extinction coefficients, triplet excited-state lifetimes and quantum yields in deoxygenated DMF. SiNc in C6H6 was used as the reference (ε590 = 70000 L mol 1 cm 1, ΦT= 0.20). −



3.3.3. Transient Absorption (TA) spectra The nanosecond (ns) TA spectra of the Pt complexes and GO-based hybrid materials were studied to realize the triplet excited-state behaviors and to predict the range where RSA arises. The ns time-resolved TA spectra of complexes and hybrid materials in DMF are presented in Figure 8,

ACS Paragon Plus Environment

Page 17 of 29

and the triplet excited-state lifetimes are listed in Table 1. Both Pt-1 and Pt-2 possess bleaching bands below ca. 500 nm and broad positive absorption bands from 500 to 700 nm. The position of bleaching bands is corresponding to the lowest energy ground state absorption of Pt complexes. The lifetimes of triplet excited state for Pt-1 and Pt-2 deduced from the TA decay are in accord with those measured from the emission decay. This fact indicates that the TA spectra for Pt-1 and Pt-2 originating from excited state could be same with the emitting state. Considering the short TA lifetimes and the shape of absorption bands, the triplet excited states of two complexes could be attributed to the 3MLCT/3ILCT states.9 Furthermore, The transient difference absorption spectra of GO-Pt-1 and GO-Pt-2, like Pt-1 and Pt-2, also exhibit a broad and positive absorption in the range 400-800 nm. While the continuous absorption in the 700-800 nm region arise from GO, the strong absorption in the 400-700 nm range may be assigned to the combination of GO and Pt complexes.53-55 It is also worth noting that the peaks of GO-Pt-1 and GO-Pt-2 undergo a hypsochromic shift compared with only Pt-1 and Pt-2, respectively. Meanwhile, the triplet excited-state lifetimes of the hybrid materials are shortened. On the basis of these TA and phosphorescence studies, we infer that the photoinduced electron transfer (PET) and energy transfer (ET) process could occur from the Pt complex moiety and GO simultaneously, which were consistent with the previous reports.19,30 These facts indicate that in the four materials, reverse saturable absorption happens at 532 nm. 0.009

0.015

0 ns 40 ns 80 ns 120 ns 160 ns

a

0 ns 240 ns 480 ns 720 ns 960 ns

b

0.010 0.005

△ OD

0.006

△ OD

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

0.003

0.000

0.000 -0.005

-0.003

400

-0.010

500

600

700

Wavelength (nm)

800

400

500

600

Wavelength (nm)

ACS Paragon Plus Environment

700

800

ACS Applied Materials & Interfaces

0.016

0 ns 5 ns 10 ns 15 ns 20 ns

c

0.008

0.008 0.004 0.000

0.004

0.000 400

0 ns 8 ns 16 ns 24 ns 32 ns

d 0.012

△ OD

0.012

△ OD

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 29

-0.004 500

600

700

800

400

Wavelength (nm)

500

600

700

800

Wavelength (nm)

Figure 8. The ns time-resolved TA spectra in deoxygenated DMF solution (λex = 355 nm). (a) Pt-1, (b) Pt-2, (c) GO-Pt-1 and (d) GO-Pt-2.

3.4. Nonlinear optical and optical power limiting properties Lasers at the 532 nm wavelength have been widely used in industrial processes, medical treatment and scientific research. However, the human eye and optical sensors are so sensitive to this wavelength that laser protection at 532 nm is particularly important in practical applications. The NLO and OPL properties of GO, Pt complexes and GO-based hybrid materials were evaluated by using Z-scans technique at 532 nm. During these experiments, as the sample with NLO behavior is moved slowly to focus, the laser intensity increases and the NLO effect enhances. All samples were individually dispersed in DMF by 30 min of ultrasonic processing and kept same linear transmittance of 70% at 532 nm.19,25,56 As shown in Figure 9a, upon excitation by 4 ns laser pulses of 532 nm, open-aperture Z-scans curves of all samples display decreased normalized transmittance as samples were closed to the focus. The normalized transmittances of GO, Pt-1, Pt-2, GO-Pt-1, GO-Pt-2 and benchmark OPL material C60 at the maximal input influence decrease to 87%, 84%, 75%, 45%, 28% and 48%, respectively. All six materials exhibit obvious NLO properties and the transmittance curves of GO-Pt-1 and GO-Pt-2 clearly indicate the greater reduction of transmittance at Z = 0 mm, which is comparable to the C60. Table 2 summarizes the information about the nonlinear absorption coefficient (βeff) and the third-order nonlinear susceptibility (Im{χ(3)}) of GO, Pt-1, Pt-2, GO-Pt-1 and GO-Pt-2. After functionalization with Pt complexes, the GO-Pt hybrid materials possess much larger βeff and Im{χ(3)} than that of GO and Pt complexes, which indicates a remarkable synergistic effect of the combination between GO and Pt complexes. Among them, GO-Pt-2 exhibits the largest

ACS Paragon Plus Environment

Page 19 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

third-order susceptibility and nonlinear extinction coefficient at 532 nm, which is also improved than those materials in early reports.22,24,30 Furthermore, NLS is regarded as an important factor for NLO effect of graphene and its derivatives.57 Figure 9b shows the fluence-dependent scattering measurement at an angle of 40o to the propagation axis of the transmitted lasers. The NLS responses of GO-Pt-1 and GO-Pt-2 were also remarkably enhanced when compared to individual GO, Pt-1, Pt-2 and C60, which exhibited tiny scattering response. Therefore, GO-Pt-1 and GO-Pt-2 are able to act as effective NLO materials. The OPL performance of different materials was studied in DMF with the same linear transmittance at 532 nm. The pure DMF solvent displays no OPL performance in the same conditions, implying that the observed OPL response should originate from the samples. As shown in Figure 9c, the OPL performance of GO and Pt-1 is almost identical at 532 nm. The property of OPL for Pt-2 is better than that of Pt-1, which is consistent with our early studies. The improvement of RSA is because of the electron-withdrawing substituent embedded to the acetylide ligands, which could lead to decrease the ground-state absorption and improve the triplet excited-state absorption.9 It can be observed that the OPL performance of GO-Pt-1 and GO-Pt-2 is much better than that of the individual Pt-1, Pt-2 and GO. In addition, the value of entering into the nonlinear optical region was 0.064 J/cm2 for GO-Pt-2, 0.070 J/cm2 for GO-Pt-1, 0.187 J/cm2 for Pt-1, 0.215 J/cm2 for Pt-2, 0.278 J/cm2 for GO. Therefore, hybrid materials can not only enhance the property of OPL, but also realize the protection of weaker laser intensity, which is greatly meaningful. Furthermore, it can be found that GO-Pt-2 hybrid materials have the largest effective optical limiting responses of the five materials tested. The OPL threshold (F50, defined as the incident density at where the transmittance falls to 50%) for different samples were studied. The GO-Pt-2 hybrid material reveals the lowest F50 value (0.85 J/cm2) in comparison with the GO-Pt-1, Pt-1, Pt-2 and GO, and the transmission decreases to 0.25 as the incident fluence reaches 1.79 J/cm2. The limiting threshold value of GO-Pt-2 is better than that of the benchmark OPL material C60 (2.2 J/cm2), GO nanosheets (>3.0 J/cm2), multiwalled carbon nanotubes (1.3 J/cm2 ),14,58 and MoS2 nanotubules with diameter at 300-400 nm (1.1 J/cm2).59 Consequently, these results further demonstrate that the preparation of GO-Pt-1 and GO-Pt-2 hybrid materials by amidation reaction and electrostatic absorption not only improves the solubility of the hybrid material, but also greatly enhances their NLO and OPL performance.

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 29

The strongly-enhanced NLO performance and OPL response of the GO-Pt-1 and GO-Pt-2 hybrid materials can be attributed to a synergistic effect between the two components. Pt(II) complexes bearing acetylide ligands are well known reverse saturable absorbers in the visible region. The NLO and OPL properties of GO suspension for ns pulses at 532 nm commonly result from NLS induced by micro-bubbles and micro-plasmas, TPA originating from the sp3 domains.60 In addition, we deem that two kinds of scattering centers are responsible for the optical scattering behavior of GO-based materials. When the incident is high and focalized on GO-based materials, one scattering center originated from GO-Pt-1 and GO-Pt-2 micro-plasma that formed through the complexes (Pt-1 and Pt-2) rapid transferring the excitation energy to the GO sheets, and the other one is the microbubbles derived from the surrounding solvent of micro-plasmas. Furthermore, taken the strong fluorescence quenching for GO-Pt-1 and GO-Pt-2 in consideration, the photo-induced electron and energy transfer between GO and Pt(II) complexes occurred due to the excellent behaviors of GO as acceptor and the Pt(II) complex moieties as donors, which has been observed for the hybrid materials of GO for optical limiting. In addition, ICP-AES analyses show more Pt-2 molecules in per area of GO. Therefore, the reasons for the better OPL performance of GO-Pt-2 are not only excellent optical limiting of Pt-2 and more molecules per area of GO, but also the means of combination between Pt-2 and GO. Table 2. Linear and NLO coefficients of GO, Pt-1, Pt-2, GO-Pt-1 and GO-Pt-2 in DMF. α0 = linear absorption coefficient; βeff=nonlinear extinction coefficient; Im{χ(3)}=imaginary third-order susceptibility. Sample

T (%)

α0 (cm-1)

βeff (cm/GW)

Im{χ(3)} (×10-12, esu)

GO

68.9

3.72

9.1±0.17

3.13±0.07

Pt-1

69.7

3.61

9.8±0.28

3.37±0.09

Pt-2

70.4

3.51

17.2±0.35

5.93±0.11

GO-Pt-1

69.9

3.58

64.3±0.51

22.1±0.14

GO-Pt-2

69.3

3.67

77.3±0.23

26.6±0.08

ACS Paragon Plus Environment

a

0.8

0.6

0.4

0.2 -15

GO Pt-1 Pt-2 GO-Pt-1 GO-Pt-2 C60 -10

-5

0

5

10

15

Z (mm)

Scattering response (a.u.)

1.0

Normalized transmittance

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Normalized transmittance

Page 21 of 29

10 8 6 4

b GO Pt-1 Pt-2 GO-Pt-1 GO-Pt-2 C60

2 0 0.1

1

Pulse energy density (J/cm2)

0.8

c 0.6

0.4

0.2

0.01

GO Pt-1 Pt-2 GO-Pt-1 GO-Pt-2 C60 0.1

1

Incident Fluence (J/cm2) Figure 9. (a) Open-aperture Z-scan curves, (b) scattering response, (c) Optical limiting performance of GO, Pt-1,

Pt-2, GO-Pt-1, GO-Pt-2 and C60 with the same linear transmittance of 70% to 4 ns, 532 nm optical pulses.

4. Conclusion The synthesis, structural and nonlinear optical properties of two GO-Pt hybrid materials were reported. The results of TEM, AFM, Raman, FT-IR, XPS and TGA confirm the successful fabrication of hybrid materials based on covalent functionalization and electrostatic adsorption between GO with Pt complexes. Additionally, the photophysical properties were measured by UV-vis absorption, steady-state fluorescence and nanosecond transient difference absorption. The NLO properties and OPL performance of GO, Pt complexes and GO hybrid materials were investigated using Z-scan measurements at 532 nm with 4 ns laser pulses. The results indicate that functionalization of GO results in the GO-Pt hybrid material having much larger NLO properties and OPL performance than those of individual GO or Pt complexes, which could be attribute to a combination of NLS and TPA arising from GO, RSA originating from the Pt complex moiety and the photo-induced electron and energy transfer from the donor Pt complex moiety to the acceptor GO. The present GO-Pt hybrid materials are expected to be good candidates for optical limiting.

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

More attention will be paid to in-depth researches concerning the solid state of graphene-based hybrid materials in further work, which could be used to fabricate films or glasses for practical applications.

Acknowledgements The authors greatly acknowledge the financial support in part by National Natural Science Foundation of China (21602106), Natural Science Foundation of Jiangsu Province-Outstanding Youth Foundation (BK20170104), Industry-Academy-Research Prospective joint project of Jiangsu Province (BY2016005-06) and National Key Research and Development Program of China (2016YFB0301703).

Supporting Information Synthetic route, 1H NMR, MS of Pt-1 and Pt-2, photographic image of the samples dispersion in DMF, XPS spectra of GO-Pt-2 and PL excitation spectra are provided.

References (1) Dini, D.; Calvete, M.; and Hanack, M. Nonlinear Optical Materials for the Smart Filtering of Optical Radiation . Chem. Rev. 2016, 116, 13043-13233. (2) Zhang, C.; Matsumoto, T.; Samoc, M.; Petrie, S.; Meng, S.; Corkery, T. C.; Stranger, R.; Zhang, J. F.; Humphrey, M. G.; Tatsumi, K. Dodecanuclear-ellipse and Decanuclear-wheel Nickel(II) Thiolato Clusters with Efficient Femtosecond Nonlinear Absorption. Angew. Chem. Int. Ed. 2010, 49, 4209-4212. (3) Hanack, M.; Dini, D.; Barthel, M.; Vagin, S. Conjugated Macrocycles as Active Materials in Nonlinear Optical Processes: Optical Limiting Effect with Phthalocyanines and Related Compounds. Chem. Rev. 2002, 2, 129-148. (4) Wang, J.; Hernandez, Y.; Lotya, M.; Coleman, J. N.; and Blauet, W. J. Broadband Nonlinear Optical Response of Graphene Dispersions. Adv. Mater. 2009, 21, 2430-2435. (5) Liaros, N.; Aloukos, P.; Kolokithas-Ntoukas, A.; Bakandritsos, A.; Szabo, T.; Zboril, R.; Couris,

ACS Paragon Plus Environment

Page 22 of 29

Page 23 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

S. Nonlinear Optical Properties and Broadband Optical Power Limiting Action of Graphene Oxide Colloids. J. Phys. Chem. C. 2013, 117, 6842-6850. (6) Shelton, A. H.; Price, R. S.; and Schanze, K. S. High Efficiency Pt Acetylide Nonlinear Absorption Chromophores Covalently Linked to Poly(methyl methacrylate). ACS. Appl. Mater. Interfaces. 2013, 5, 7867-7874. (7) Shao, P.; Li, Y.; Yi, J.; Pritchett, T. M.; Sun, W. F. Cyclometalated Pt(II) 6-Phenyl-4-(9,9-dihexylfluoren-2-yl)-2,2′-bipyridine Complexes: Synthesis, Photophysics, and Nonlinear Absorption. Inorg. Chem. 2010, 49, 4507-4517. (8) Shao, P.; Li, Y.; Azenkeng, A.; Hoffmann, M. R.; Sun, W. F. Influence of Alkoxyl Substituent on 4,6-Diphenyl-2,2′-bipyridine Ligand on Photophysics of Cyclometalated Pt(II) Complexes: Admixing Intraligand Charge Transfer Character in Low-Lying Excited States. Inorg. Chem. 2009, 48, 2407-2419. (9) Liu, R.; Li, Y. J.; Li, Y. H.; Zhu, H. J.; Sun, W. F. Photophysics and Nonlinear Absorption of Cyclometalated 4,6-Diphenyl-2,2′-bipyridyl Pt(II) Complexes with Different Acetylide Ligands. J. Phys. Chem. A. 2010, 114, 12639-12645. (10) Zhang, B. G.; Li, Y. J.; Liu, R.; Pritchett, T. M.; Haley, J. E.; and Sun, W. F. Extending the Bandwidth of Reverse Saturable Absorption in Pt Complexes Using Two-Photon-Initiated Excited-State Absorption. ACS. Appl. Mater. Interfaces. 2013, 5, 565−572. (11) Park, S. J.; Ruoff, S. R. Chemical Methods for the Production of Graphenes. Nat. Nanotechnol. 2009, 4, 217-224 . (12) Geim, A. K. Graphene: Status and Prospects. Science. 2009, 324, 1530-1534. (13) Dreyer, D. R.; Park, S. J.; Bielawski, C. W.; and Ruoff, S. R. The Chemistry of Graphene Oxide. Chem. Soc. Rev. 2010, 39, 228-240. (14) Feng, M.; Zhan, H. B.; Chen, Y. Nonlinear Optical and Optical Limiting Properties of Graphene Families. Appl. Phys. Lett. 2010, 96, 033107. (15) Bao, Q. L.; Zhang, H.; Wang, Y.; Ni, Z. H.; Yan, Y. L.; Shen, Z. X.; Loh, K. P.; Tang, D. Y. Atomic-Layer Graphene as a Saturable Absorber for Ultrafast Pulsed Lasers. Adv. Funct. Mater. 2009, 19, 3077-3083. (16) Liu, Z. B.; Zhao, X.; Zhang, X. L.; Yan, X. Q.; Wu, Y. P.; Chen, Y. S.; Tian, J. G. Ultrafast Dynamics and Nonlinear Optical Responses from sp2- and sp3-hybridized Domains in Graphene

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Oxide. J. Phys. Chem. Lett. 2011, 2, 1972-1977. (17) Zhang, X. L.; Liu, Z. B.; Li, X. C.; Ma, Q.; Chen, X. D.; Tian, J. G.; Xu, Y. F.; Chen, Y. S. Transient Thermal Effect, Nonlinear Refraction and Nonlinear Absorption Properties of Graphene Oxide Sheets in Dispersion. Opt. Express. 2013, 21, 7511-7520. (18) Liu, Z. B.; Xu, Y. F.; Zhang, X. Y.; Chen, Y. S.; Tian, J. G. Porphyrin and Fullerene Covalently Functionalized Graphene Hybrid Materials with Large Nonlinear Optical Properties. J. Phys. Chem. B. 2009, 113, 9681-9686. (19) Xu, Y. F.; Liu, Z. B.; Zhang, X. L.; Wang, Y.; Tian, J. G.; Huang, Y.; Ma, Y. F.; Zhang, X. Y.; Chen, Y. S. A Graphene Hybrid Material Covalently Functionalized with Porphyrin: Synthesis and Optical Limiting Property. Adv. Mater. 2009, 21, 1275-1279. (20) Wang, A.; Long, L.; Zhao, W.; Song, Y.; Humphrey, M. G.; Zhang, C.; Cifuenteset, M. P.; Wu, X.; Fu, Y.; Zhang, D.; Li, X.; Zhang, C. Increased Optical Nonlinearities of Graphene Nanohybrids Covalently Functionalized by Axially-coordinated Porphyrins. Carbon. 2013, 53, 327-338. (21) Song, W.; He, C.; Dong, Y.; Zhang, W.; Gao, Y.; Wu, Y.; and Chen, Z. The Effects of Central Metals on the Photophysical and Nonlinear Optical Properties of Reduced Graphene Oxide–Metal(II) Phthalocyanine Hybrids. Phys. Chem. Chem. Phys. 2015, 17, 7149-7157. (22) Zhu, J.; Li, Y.; Chen, Y.; Wang, J.; Zhang, B.; Zhang, J.; Blau, W. J. Graphene Oxide Covalently Functionalized with Zinc Phthalocyanine for Broadband Optical Limiting. Carbon. 2011, 49, 1900-1905. (23) Song, W.; He, C.; Zhang, W.; Gao, Y.; Yang, Y.; Wu, Y.; Chen, Z.; Li, X.; Dong, Y. Synthesis and Nonlinear Optical Properties of Reduced Graphene Oxide Hybrid Material Covalently Functionalized with Zinc Phthalocyanine. Carbon. 2014, 77, 1020-1030. (24) Li, Y. X.; Zhu, J.; Chen, Y.; Zhang, J.; Wang, J.; Zhang, B.; He, Y.; Blau, W. J. Synthesis and Strong Optical Limiting Response of Graphite Oxide Covalently Functionalized with Gallium Phthalocyanine. Nanotechnology. 2011, 22, 2057041-2057047. (25) Liu, Y.; Zhou, J.; Zhang, X.; Liu, Z.; Wan, X.; Tian, J.; Wang, T.; Chen, Y. Synthesis, Characterization and Optical Limiting Property of Covalently Oligothiophene-Functionalized Graphene Material. Carbon. 2009, 47, 3113-3121. (26) Kavitha, M. K.; John, Honey.; Gopinath, Pramod.; and Philip, Reji. Synthesis of Reduced

ACS Paragon Plus Environment

Page 24 of 29

Page 25 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Graphene Oxide-ZnO Hybrid with Enhanced Optical Limiting Properties. J. Mater. Chem. C. 2013, 1, 3669-3676. (27) Feng, M.; Sun, R.; Zhan, H.; Chen, Yu. Lossless Synthesis of Graphene Nanosheets Decorated with Tiny Cadmium Sulfide Quantum Dots with Excellent Nonlinear Optical Properties. Nanotechnology. 2010, 21, 075601. (28) He, T.; Wei, W.; Ma, L.; Chen, R.; Wu, S.; Zhang, H.; Yang, Y.; Ma, J.; Huang, L.; Gurzadyan, G. G.; Sun, H. Mechanism Studies on the Superior Optical Limiting Observed in Graphene Oxide Covalently Functionalized with Upconversion NaYF4:Yb3+/Er3+ Nanoparticles. Small. 2012, 8, 2163-2168. (29) Wei, W.; He, T.; Teng, X.; Wu, S.; Ma, L.; Zhang, H.; Ma, J.; Yang, Y.; Chen, H.; Han,Y.; Sun, H.; Huang, L. Nanocomposites of Graphene Oxide and Upconversion Rare-Earth Nanocrystals with Superior Optical Limiting Performance. Small. 2012, 8, 2271-82276. (30) Bai, T.; Li, C.; Sun, J.; Song, Y.; Wang, J.; Blau, W. J.; Zhang, B.; Chen, Y. Covalent Modification of Graphene Oxide with Carbazole Groups for Laser Protection. Chem-Eur. J. 2015, 21, 4622-4627. (31) Li, P.; Chen, Y.; Zhu, J.; Feng, M.; Zhuang, X.; Lin, Y.; Zhan, H. Charm-Bracelet-Type Poly(n-vinyl- carbazole) Functionalized with Reduced Graphene Oxide for Broadband Optical Limiting. Chem. Eur. J. 2011, 17, 780-785. (32) Midya, A.; Mamidala, V.; Yang, J. X.; Ang, P. K. L.; Chen, Z.; Ji, W.; Loh, K. P. Synthesis and

Superior

Optical-Limiting

Properties

of

Fluorene-Thiophene-Benzothiadazole

Polymer-Functionalized Graphene Sheets. Small. 2010, 6, 2292-2300. (33) Balapanuru, J.; Yang, J.; Xiao, S.; Bao, Q.; Jahan, M.; Polavarapu, L.; Wei, J.; Xu, Q.; Loh, K. P. A Graphene Oxide-Organic Dye Ionic Complex with DNA-sensing and Optical-Limiting Properties. Angew. Chem. Int. Ed. 2010, 49, 6549-6553. (34) Lu, W.; Mi, B. X.; Chan, M. C. W.; Hui, Z.; Che, C. M.; Zhu, N.; Lee, S. T. Light-Emitting Tridentate Cyclometalated Pt(II) Complexes Containing σ-Alkynyl Auxiliaries: Tuning of Photoand Electrophosphorescence. J. Am. Chem. Soc. 2004, 126, 4958-4971. (35) Santiago, M. G.; Parthey, M.; Yufit, D. S.; Howard, J. A. K.; Kaupp, M.; and Low, P. J. Combined Spectroscopic and Quantum Chemical Study of [trans-Ru(C≡CC6H4R1-4)2(dppe)2]n+ and [trans-Ru(C≡CC6H4R1-4)(C≡CC6H4R2-4)(dppe)2]n+ (n = 0, 1) Complexes: Interpretations

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

beyond the Lowest Energy Conformer Paradigm. Organometallics. 2014, 33, 4947-4963. (36) Bonakdarzadeh, P.; Topić, F.; Kalenius, E.; Bhowmik, S.; Sato, S.; Groessl, M.; Knochenmuss, R.; and Rissanen, K. DOSY NMR, X-ray Structural and Ion-Mobility Mass Spectrometric Studies on Electron-Deficient and Electron-Rich M6L4 Coordination Cages. Inorg. Chem. 2015, 54, 6055–6061. (37) Yang, J.; Song, Y.; Zhu, W.; Su, X.; Xu, H. Investigation of Optical Nonlinearities and Transient Dynamics in a Stilbenzene Derivative. J. Phys. Chem. B. 2012, 116, 1221–1225. (38) Georgakilas, V.; Otyepka, M.; Kim, K. S. Functionalization of Graphene: Covalent and Non-Covalent Approaches, Derivatives and Applications. Chem. Rev. 2012, 112, 6156-6214. (39) Zhang, L.; Xia, J.; Zhao, Q.; Liu, L.; Zhang, Z., Functional Graphene Oxide as a Nanocarrier for Controlled Loading and Targeted Delivery of Mixed Anticancer Drugs. Small. 2010, 6, 537-544. (40) Shan, C.; Yang, H.; Han, D.; Zhang, Q.; Ivaska, A.; Niu, L. Water-Soluble Graphene Covalently Functionalized by Biocompatible Poly-L-Lysine. Langmuir. 2009, 25, 12030-12033. (41) Zhang, C.; Yuan, Y.; Zhang, S.; Wang, Y.; Liu, Z. Biosensing Platform Based on Fluorescence Resonance Energy Transfer from Upconverting Nanocrystals to Graphene Oxide. Angew. Chem. Int. Ed. 2011, 50, 6851-6854. (42) Kudinn, K. N.; Ozbas, B.; Schniepp, H. C.; Prudhomme, R. K.; Akay, I. A.; Car, R. Raman Spectra of Graphite Oxide and Functionalized Graphene Sheets. Nano. Lett. 2008, 8, 36-41. (43) Zhu, Y.; Murali, S.; Cai, W.; Li, X.; Suk, J. W.; Potts, J. R.; Ruoff, R. S. Graphene and Graphene Oxide: Synthesis, Properties, and Applications. Adv. Mater. 2010, 22, 3906-3924. (44) Si, Y.; Samlski, E. T. Synthesis of Water Soluble Graphene. Nano. Lett. 2008, 8, 1679-1682. (45) Niyogi, S.; Bekyarova, E.; Itkis, M. E.; McWilliams, J. L.; Hamon, M. A.; Haddon, R. C. Solution Properties of Graphite and Graphene. J. Am. Chem. Soc. 2006, 128, 7720-7721. (46) Hsiao, M. C.; Liao, S. H.; Yen, M. Y.; Liu, P. I.; Pu, N. W.; Wang, C. A.; and Ma, C. C. M. Preparation of Covalently Functionalized Graphene Using Residual Oxygen-Containing Functional Groups. ACS. Appl. Mater. Interfaces. 2010, 2, 3092-3099. (47) Compton, O. C.; Dikin, D. A.; Putz, K. W.; Brinson, L. C.; Nguyen, S. T. Electrically Conductive "alkylated" Graphene Paper via Chemical Reduction of Amine-Functionalized Graphene Oxide Paper. Adv. Mater. 2010, 22, 892-896.

ACS Paragon Plus Environment

Page 26 of 29

Page 27 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

(48) Bao, H.; Pan, Y.; Ping, Y.; Sahoo, N. G.; Wu, T.; Li, L.; Li, J.; Gan, L. H. Chitosan-Functionalized Graphene Oxide as a Nanocarrier for Drug and Gene Delivery. Small. 2011, 7, 1569-1578. (49) Georgakilas, V.; Bourlinos, A. B.; Zboril, R.; Steriotis, T. A.; Dallas, P.; Stuboscd, A. K.; and Trapalisa, C. Organic Functionalisation of Graphenes. Chem. Commun. 2010, 46, 1766-1768. (50) Xu, Y. X.; Bai, H.; Lu, G. W.; Li, C.; Shi, G. Q. Flexible graphene Films via the Filtration of Water-soluble Noncovalent Functionalized Graphene Sheets. J. Am. Chem. Soc. 2008, 130, 5856 -5857. (51) Wang, A.; Yu, W.; Huang, Z.; Zhou, F.; Song, J.; Song, Y.; Long, L.; Cifuentes, M. P.; Humphrey, M. G.; Zhang, Long.; Shao, J.; Zhang,C. Covalent Functionalization of Reduced Graphene Oxide with Porphyrin by Means of Diazonium Chemistry for Nonlinear Optical Performance. Sci. Rep. 2016, 6, 23325. (52) Song, W.; He, C.; Dong, Y.; Zhang, Wang.; Gao, Y,; Wu, Y.; and Chen, Z. The Effects of Central Metals on the Photophysical and Nonlinear Optical Properties of Reduced Graphene Oxide–Metal(II) Phthalocyanine Hybrids. Phys. Chem. Chem. Phys. 2015, 17, 7149-7157. (53) Barrejo´n, M.; Vizuete, M.; Go´mez-Escalonilla, M. J. A Photoresponsive Graphene Oxide–C60 Conjugate.Chem. Commun. 2014, 50, 9053-9055. (54) Karousis, N.; Sandanayaka, S. D.; Hasobe, T. Graphene Oxide with Covalently Linked Porphyrin Antennae: Synthesis, Characterization and Photophysical Properties. J. Mater. Chem. 2011, 21, 109-117 (55) Lim, G. K.; Chen, Z. L.; Clark, J.; Goh, R. G. S.; Ng, W. H.; Tan, H. W.; Chua, L. L.; Giant Broadband Nonlinear Optical Absorption Response in Dispersed Graphene Single Sheets. Nat. Photonics. 2011, 5, 554-560. (56) Liu, Z.; Tian, J.; Guo, Z.; Ren, D.; Du, F.; Zheng, J.; Chen, Y. Enhanced Optical Limiting Effects in Porphyrin-Covalently Functionalized Single-Walled Carbon Nanotubes. Adv. Mater. 2008, 20, 511-515. (57) Cheng X, Dong NN, Li B, Zhang X, Zhang S, Jiao J, Blau, W. J. Zhang L. and Wang J. Controllable broadband nonlinear optical response of graphene dispersions by tuning vacuum pressure. Opt. Express. 2013, 21, 16486-16493. (58) Chen, Y.; Bai, T.; Dong, N. N., Fei F.; Zhang, S. F.; Zhuang, X. D.; Sun, J.; Zhang, B.; Zhang,

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

X. Y.; Wang, J.; Blau, W. J. Graphene and its derivatives for laser protection, Prog. Mater. Sci. 2016, 84, 118-157. (59) Loh, K. P.;

Zhang, H.; Chen, W. Z.; and Ji, W. Templated Deposition of MoS2 Nanotubules

Using Single Source Precursor and Studies of Their Optical Limiting Properties. J. Phys. Chem. B. 2006, 110,1235-1239. (60) Tao, L.; Zhou, B.; Bai, G.; Wang, Y.; Yu, S.; Lau, S. P.; Tsang, Y. H.; Yao, J.; Xu, D. Fabrication of Covalently Functionalized Graphene Oxide Incorporated Solid-State Hybrid Silica Gel Glasses and Their Improved Nonlinear Optical Response. J. Phys. Chem. C. 2013, 117, 23108-23116.

ACS Paragon Plus Environment

Page 28 of 29

Page 29 of 29

ACS Applied Materials & Interfaces