Syntheses, Structures, Magnetism, and Optical Properties of Lutetium

Oct 3, 2007 - F-Ln2S3 type structure with the eight-coordinate bicapped trigonal prismatic .... (Q ) S, Se)12-14 (UFeS3 type),24 γ-LnYbS3 (Ln ) La, C...
0 downloads 0 Views 476KB Size
Inorg. Chem. 2007, 46, 9213−9220

Syntheses, Structures, Magnetism, and Optical Properties of Lutetium-Based Interlanthanide Selenides Geng Bang Jin,† Eun Sang Choi,‡ Robert P. Guertin,§ James S. Brooks,‡ Corwin H. Booth,| and Thomas E. Albrecht-Schmitt*,† Department of Chemistry and Biochemistry and Center for Actinide Science, Auburn UniVersity, Auburn, Alabama 36849, Department of Physics and National High Magnetic Field Laboratory, Florida State UniVersity, Tallahassee, Florida 32310, Department of Physics and Astronomy, Tufts UniVersity, Medford, Massachusetts 02155, and Chemical Sciences DiVision, Lawrence Berkeley National Laboratory, 1 Cyclotron Road, Berkeley, California 94720 Received May 24, 2007

Ln3LuSe6 (Ln ) La, Ce), β-LnLuSe3 (Ln ) Pr, Nd), and LnxLu4-xSe6 (Ln ) Sm, Gd; x ) 1.82, 1.87) have been synthesized using a Sb2Se3 flux at 1000 °C. Ln3LuSe6 (Ln ) La, Ce) adopts the U3ScS6-type three-dimensional structure, which is constructed from two-dimensional ∞2 [Ln3Se6]3- slabs with the gaps between these slabs being filled by octahedrally coordinated Lu3+ ions. The series of β-LnLuSe3 (Ln ) Pr, Nd) are isotypic with UFeS3. Their structures include layers formed from LuSe6 octahedra that are separated by eight-coordinate Ln3+ (Ln ) Pr, Nd) ions in bicapped trigonal prismatic environments. Sm1.82Lu2.18Se6 and Gd1.87Lu2.13Se6 crystallize in the disordered F-Ln2S3 type structure with the eight-coordinate bicapped trigonal prismatic Ln(1) ions residing in the one-dimensional channels formed by three different double chains via edge- and corner-sharing. These double chains are constructed from Ln(2)Se7 monocapped trigonal prisms, Ln(3)Se6 octahedra, and Ln(4)S6 octahedra, respectively. The magnetic susceptibilities of β-PrLuSe3 and β-NdLuSe3 follow the Curie−Weiss law. Sm1.82Lu2.18Se6 shows van Vleck paramagnetism. Magnetic susceptibility measurements show that Gd1.87Lu2.13Se6 undergoes an antiferromagnetic transition around 4 K. Ce3LuSe6 exhibits soft ferromagnetism below 5 K. The optical band gaps for La3LuSe6, Ce3LuSe6, β-PrLuSe3, β-NdLuSe3, Sm1.82Lu2.18Se6, and Gd1.87Lu2.13Se6 are 1.26, 1.10, 1.56, 1.61, 1.51, and 1.56 eV, respectively.

Introduction Interlanthanide chalcogenides have been the focus of intense interest because of their remarkably complex structures, potentially tunable optical properties, and in some cases, atypical magnetism.1-22 One of the primary goals in * To whom correspondence should be addressed. E-mail: albreth@ auburn.edu. Fax: 334-844-6959. † Auburn University. ‡ Florida State University. § Tufts University. | Lawrence Berkeley National Laboratory. (1) Moreau, J. M. Mater. Res. Bull. 1968, 3, 427. (2) Moreau, J. M.; Mareschal, J.; Bertaut, E. F. Solid State Commun. 1968, 6, 751. (3) Mareschal, J.; Moreau, J. M.; Ollivier, G.; Pataud, P.; Sivardiere, J. Solid State Commun. 1969, 7, 669. (4) Rodier, N.; Laruelle, P. C. R. Seances Acad. Sci. Ser. C 1970, 270, 2127. (5) Coutures, J.; Coutures, J. P. J. Solid State Chem. 1976, 19, 29. (6) Mu¨ller-Buschbaum, H.; Graebner, P. -H. Z. Anorg. Allg. Chem. 1971, 386, 158.

10.1021/ic701012j CCC: $37.00 Published on Web 10/03/2007

© 2007 American Chemical Society

this work is to obtain phases where the different lanthanide ions are present in the crystalline lattice in an ordered arrangement. There are several methods for achieving this goal including the selection of lanthanides from opposite ends (7) Ijdo, D. J. W. Acta Crystallogr. B 1980, 36, 2403. (8) Ito, K.; Tezuka, K.; Hinatsu, Y. J. Solid State Chem. 2001, 157, 173. (9) Deepa, M.; Varadaraju, U. V. Mater. Res. Soc. Symp. Proc. 1998, 527, 507. (10) Berndt, U.; Maier, D.; Keller, C. J. Solid State Chem. 1976, 16, 189. (11) Ito, K.; Tezuka, K.; Hinatsu, Y. J. Solid State Chem. 2001, 157, 173. (12) Rodier, N.; Julien, R.; Tien, V. Acta Crystallogr. C 1983, 39, 670. (13) Carre, D.; Laruelle, P. Acta Crystallogr. B 1974, 30, 952. (14) Mitchell, K.; Somers, R. C.; Huang, F. Q.; Ibers, J. A. J. Solid State Chem. 2004, 177, 709. (15) Jin, G. B.; Choi, E. S.; Guertin, R. P.; Brooks, J. S.; Bray, T. H.; Booth, C. H.; Albrecht-Schmitt, T. E. Chem. Mater. 2007, 19, 567. (16) Rodier, N.; Tien, V. C. R. Seances Acad. Sci. Ser. C 1974, 279, 817. (17) Rodier, N.; Firor, R. L.; Tien, V.; Guittard, M. Mater. Res. Bull. 1976, 11, 1209. (18) Rodier, N. Bull. Soc. Fr. Mineral. Cristallogr. 1973, 96, 350. (19) Carre´, D.; Laruelle, P. Acta Crystallogr. B 1973, 29, 70. (20) Gray, D. L.; Rodriguez, B. A.; Chan, G. H.; Van Duyne, R. P.; Ibers, J. A. J. Solid State Chem. 2007, 180, 1527.

Inorganic Chemistry, Vol. 46, No. 22, 2007

9213

Jin et al. of the series in an attempt to capitalize on the marked difference in size of the early versus late lanthanide ions. Therefore, ternary interlanthanide chalcogenides usually include one larger ion (Ln) and one smaller ion (Ln′) that are from opposite ends of lanthanide series with different coordination environments to avoid possible disordering. Early lanthanides, such as La3+ and Ce3+, are often found in eight- and nine-coordinate environments, whereas late lanthanides (e.g., Yb3+ and Lu3+) are usually found in sixand seven-coordinate environments. To this end, Ln/Yb/Q (Q ) S, Se) phases have been extensively studied. This group is represented by R-LaYbS312 (GdFeO3 type),23 β-LnYbQ3 (Q ) S, Se)12-14 (UFeS3 type),24 γ-LnYbS3 (Ln ) La, Ce),15 and LnYb3S616,17 (F-Ln2S3 type).25,26 Er- and Tm-containing ternary compounds have also been prepared, and a number of well-characterized examples exist including CeTmS3,18 La10Er9S27,19 γ-LnLn′S3 (Ln ) La, Ce; Ln′ ) Er, Tm),15 SmEr3Q6 (Q ) S, Se)20 (F-Ln2S3 type),25,26 and Sm0.88Er1.12Se320 (U2S3 type).27 Both Er3+ and Tm3+ ions are paramagnetic. In contrast, the Ln/Lu/Q phases have potentially simpler magnetism because there is at most one paramagnetic ion owing to the 4f14 configuration of Lu3+. Recently, we reported the synthesis and characterization of the interlanthanide sulfides δ-Ln2-xLuxS3 (Ln ) Ce, Pr, Nd).21 These compounds crystallize in the disordered CeTmS3 structure-type and have band gaps that are dependent on the choice of the lanthanide ion. The magnetic behavior of most lanthanide compounds is complicated, in part, because of substantial crystal-field effects. The δ-Ln2-xLuxS3 (Ln ) Ce, Pr, Nd) are no exception to this, and δ-Ce1.30Lu0.70S3 deviates from the Curie-Weiss law at low temperatures, a feature that can be ascribed to crystal-field effects. In this present study, we attempt to address the structural and electronic behavior of both ordered and disordered ternary lanthanide lutetium selenides. We disclose the syntheses, structures, optical, and magnetic properties of Ln3LuSe6 (Ln ) La, Ce), β-LnLuSe3 (Ln ) Pr, Nd), and LnxLu4-xSe6 (Ln ) Sm, Gd; x ) 1.82, 1.87). Experimental Section Starting Materials. La (99.9%, Alfa-Aesar), Ce (99.9%, AlfaAesar), Pr (99.9%, Alfa-Aesar), Nd (99.9%, Alfa-Aesar), Sm (99.9%, Alfa-Aesar), Gd (99.9%, Alfa-Aesar), Lu (99.9%, AlfaAesar), Se (99.5%, Alfa-Aesar), and Sb (99.5%, Alfa-Aesar) were used as received. The Sb2Se3 flux was prepared from the direct reaction of the elements in sealed fused-silica ampules at 850 °C. Syntheses. Ln3LuSe6 (Ln ) La, Ce) were synthesized from a reaction of 150 mg of stoichiometric Ln, Lu, and Se and 100 mg (21) Jin, G. B.; Choi, E. S.; Guertin, R. P.; Brooks, J. S.; Bray, T. H.; Booth, C. H.; Albrecht-Schmitt, T. E. J. Solid State Chem. 2007, in press. (22) Jin, G. B.; Choi, E. S.; Guertin, R. P.; Brooks, J. S.; Bray, T. H.; Booth, C. H.; Albrecht-Schmitt, T. E. J. Solid State Chem. 2007, in press. (23) Marezio, M.; Remeika, J. P.; Dernier, P. D. Acta Crystallogr. B 1970, 26, 2008. (24) Noel, H.; Padiou, J. Acta Crystallogr. B 1976, 32, 1593. (25) Schleid, T.; Lissner, F. J. Alloys Compds. 1992, 189, 69. (26) Fang, C. M.; Meetsma, A.; Wiegers, G. A. J. Alloys Compds. 1993, 201, 255. (27) Zachariasen, W. H. Acta Crystallogr. 1949, 2, 291.

9214 Inorganic Chemistry, Vol. 46, No. 22, 2007

of Sb2Se3. For β-LnLuSe3 (Ln ) Pr, Nd) and LnxLu4-xSe6 (Ln ) Sm, Gd; x ) 1.82, 1.87), the reaction mixtures include 150 mg of Ln, Lu, and Se in a molar ratio of 1:1:3 and 100 mg of Sb2Se3. All of these starting materials were loaded into fused-silica ampules under an argon atmosphere in a glovebox. The ampules were flamesealed under vacuum and heated in programmable tube furnaces. The following heating profile was used for all reactions: 2 °C min-1 to 500 °C (held for 1 h), 0.5 °C min-1 to 1000 °C (held for 14 days), 0.04 °C min-1 to 550 °C (held for 2 days), and 0.5 °C min-1 to 24 °C. The major title products were found as large black chunks that were well separated from the Sb2Se3 flux. The separation of the flux from the products is achieved by slightly tilting the furnaces, which causes the flux to settle to the bottom of the ampules leaving the desired product higher up, making manual separation with the aid of a stereomicroscope trivial. The reaction ampules are located toward the back of the tube furnace, and the flux settles in the farthest and presumably coolest region of the furnace. Once the products were isolated, they were ground for powder X-ray diffraction measurements, which were used to confirm phase purity by comparison of the powder patterns calculated from the singlecrystal X-ray structures with the experimental data. Semiquantitative SEM/EDX analyses were performed on several single crystals for each compound using a JEOL 840/Link Isis or JEOL JSM-7000F instruments. Ln, Lu, and Se percentages were calibrated against standards. Sb was not detected in the crystals. The Ln/Lu/Se ratios for Ln3LuSe6 (Ln ) La, Ce) were determined to be approximately 3:1:6 from EDX analyses, while the ratios of Ln/Lu/Se were close to 1:1:3 for β-LnLuSe3 (Ln ) Pr, Nd) and LnxLu4-xSe6 (Ln ) Sm, Gd; x ) 1.82, 1.87). Crystallographic Studies. Single crystals of LnxLuySez (Ln ) La, Ce, Pr, Nd, Sm, Gd) were mounted on glass fibers with epoxy and optically aligned on a Bruker APEX single crystal X-ray diffractometer using a digital camera. Initial intensity measurements were performed using graphite-monochromated Mo KR (λ ) 0.71073 Å) radiation from a sealed tube and monocapillary collimator. SMART (version 5.624) was used for preliminary determination of the cell constants and data collection control. The intensities of reflections of a sphere were collected by a combination of three sets of exposures (frames). Each set had a different φ angle for the crystal, and each exposure covered a range of 0.3° in ω. A total of 1800 frames were collected with exposure times per frame of 10 or 20 s depending on the crystal. For LnxLuySez (Ln ) La, Ce, Pr, Nd, Sm, Gd), determination of integrated intensities and global refinement were performed with the Bruker SAINT (version 6.02) software package using a narrowframe integration algorithm. These data were treated first with a face-indexed numerical absorption correction using XPREP,28 followed by a semiempirical absorption correction using SADABS.29 The program suite SHELXTL (version 6.12) was used for space group determination (XPREP), direct methods structure solution (XS), and least-squares refinement (XL).28 The final refinements included anisotropic displacement parameters for all atoms and secondary extinction. Some crystallographic details are given in Table 1. Additional crystallographic information can be found in the Supporting Information. The structures of Ln3LuSe6 (Ln ) La, Ce) and β-LnLuSe3 (Ln ) Pr, Nd) are ordered. For these compounds, the assignments of the cation positions were straightforward. LnxLu4-xSe6 (Ln ) Sm, (28) Sheldrick, G. M. SHELXTL PC, An Integrated System for SolVing, Refining, and Displaying Crystal Structures from Diffraction Data, version 6.12; Siemens Analytical X-Ray Instruments, Inc.: Madison, WI, 2001. (29) Sheldrick, G. M. Acta Crystallogr. A 1995, 51, 33.

Lutetium-Based Interlanthanide Selenides Table 1. Crystallographic Data for LnxLuySez (Ln ) La, Ce, Pr, Nd, Sm, Gd) formula fw color cryst syst space group a (Å) b (Å) c (Å) β (deg) V (Å3) Z T (K) λ (Å) Fcalcd (g cm-3) µ (cm-1) R(F)a Rw(Fo2)b a

La3LuSe6 1065.46 black orthorhombic Pnnm (No. 58) 14.6195(10) 17.5736(12) 4.1542(3)

Ce3LuSe6 1069.09 black orthorhombic Pnnm (No. 58) 14.5020(9) 17.4954(11) 4.1129(3)

β-PrLuSe3 552.76 black orthorhombic Cmcm (No. 63) 4.0052(10) 12.996(3) 9.865(3)

β-NdLuSe3 556.09 black orthorhombic Cmcm (No. 63) 3.9946(5) 13.0015(17) 9.8583(13)

1067.29(13) 4 193 0.71073 6.631 413.24 0.0273 0.0645

1043.52(12) 4 193 0.71073 6.805 430.70 0.0212 0.0485

513.5(2) 4 193 0.71073 7.150 495.66 0.0429 0.1049

512.00(11) 4 193 0.71073 7.214 503.36 0.0226 0.0601

Sm1.82Lu2.18Se6 1128.83 black monoclinic P21/m (No. 11) 11.3925(13) 4.0483(5) 11.6844(14) 108.915(2) 509.79(11) 2 193 0.71073 7.354 525.94 0.0300 0.0822

Gd1.87Lu2.13Se6 1140.50 black monoclinic P21/m (No. 11) 11.4274(12) 4.0542(4) 11.7160(12) 109.005(2) 513.20(9) 2 193 0.71073 7.381 534.34 0.0308 0.0817

R(F) ) ∑||Fo| - |Fc||/∑|Fo| for Fo2 > 2σ(Fo2). b Rw(Fo2) ) [∑[w(Fo2 - Fc2)2]/∑wFo4]1/2.

Table 2. Ternary Interlanthanide Sulfides Prepared Using Sb2S3 Flux at 1000 °Ca Tb3+ Dy3+ Ho3+ Er3+ Tm3+ Yb3+ Lu3+

Eu2+

La3+

b b b b b b b

(4 (4 ( ( ( 4

Ce3+

) ( ( ( )

Pr3+

4 4 )

Nd3+

4 )

Sm3+

4 4

Table 3. Ternary Interlanthanide Selenides Prepared Using Sb2Se3 Flux at 1000 °Ca

Gd3+

4

Tb3+ Dy3+ Ho3+ Er3+ Tm3+ Yb3+ Lu3+

Eu2+

La3+

b b b b b b b

0

Ce3+

Pr3+

Nd3+

Sm3+

Gd3+

4 2 2

4 4 2 2

4 4 4

4 4 4

0 ] 4 O 9

4 2 9

a Ordered structure types: 2 β-LnLn′S ,12-14 ( γ- LnLn′S ,15 9 U ScS ,32 3 3 3 6 b CaFe2O4.33 Disordered structure types: 4 F-Ln2S3,25,26 ] δ-LnLn′S3,18,21 27 34 0 U2S3, O Y5S7.

a Ordered structure types: 2 β-LnLn′S ,12-14 ( γ- LnLn′S ,15 9 U ScS ,32 3 3 3 6 b CaFe2O4.33 Disordered structure types: 4 F-Ln2S3,25,26 ] δ-LnLn′S3,18,21 27 34 0 U2S3, O Y5S7.

Gd; x ) 1.82, 1.87) compounds crystallize in the F-Ln2S325,26 type structure, which is highly disordered. All four cation sites, including one eight-coordinate position (Ln(1)), one sevencoordinate position (Ln(2)), and two octahedral positions (Ln(3) and Ln(4)), were assumed to be occupied by both metals at the beginning of the refinements. The final refinements showed that the occupancies of Lu atoms in Ln(1), Ln(2), Ln(3), and Ln(4) positions are 0.02, 0.32, 0.88, and 0.95, respectively, for the Sm-based compound and 0.04, 0.40, 0.84, and 0.86 for Gd case. These results gave rise to the formula of Sm1.82Lu2.18Se6 and Gd1.87Lu2.13Se6, which are consistent with the 1:1:3 ratios from EDX analysis. It is worth noting that Gd1.87Lu2.13Se6 has a higher degree of disorder than Sm1.82Lu2.18Se6 because of the decrease in the difference in the size of the cations, even though they have similar Ln/Lu ratios. Powder X-ray Diffraction. Powder X-ray diffraction patterns were collected with a Rigaku Miniflex powder X-ray diffractometer using Cu KR (λ ) 1.54056 Å) radiation. Magnetic Susceptibility Measurements. Magnetic susceptibility data were collected from powders in gelcap sample holders with a Quantum Design MPMS 7T magnetometer/susceptometer between 2 and 300 K and in applied fields up to 7 T. DC susceptibility measurements were made under zero-field-cooled conditions with an applied field of 0.1 T. Magnetic susceptibility for Ce3LuSe6 under zero-field-cooled (ZFC) and field-cooled (FC) conditions were measured with 0.01 T applied field between 2 and 25 K. Susceptibility values were corrected for the sample diamagnetic contribution according to Pascal’s constants,30 as well as for the sample holder diamagnetism. Experimental effective magnetic moments and Weiss constants for Ce3LuSe6, β-PrLuSe3, β-Nd-

LuSe3, and Gd1.87Lu2.13Se6 were obtained from extrapolations from fits between 100 and 300 K. UV-vis-NIR Diffuse Reflectance Spectroscopy. The diffuse reflectance spectra for LnxLuySez (Ln ) La, Ce, Pr, Nd, Sm, Gd) were measured from 200 to 2500 nm using a Shimadzu UV3100 spectrophotometer equipped with an integrating sphere attachment. The Kubelka-Munk function was used to convert diffuse reflectance data to absorption spectra.31

(30) Mulay, L. N.; Boudreaux, E. A. Theory and Applications of Molecular Diamagnetism; Wiley-Interscience: New York, 1976.

Results and Discussion Synthesis of Ln/Ln′/Q using Sb2Q3 Fluxes (Q ) S, Se). There are a large number of synthetic parameters that significantly affect the type of interlanthanide chalcogenide obtained in flux-based reactions. These parameters include the choice of flux, reaction temperature, stoichiometry, and choices of lanthanides and chalcogens. It has been shown that temperature changes as small as 50 K (1173 K vs 1123 K) can induce changes in product formation.20 In our work, we have focused on the use of Sb2Q3 (Q ) S, Se) fluxes to prepare ternary and quaternary interlanthanide chalcogenides.15,21,22 Eight different structure types have been identified for ternary interlanthanide chalcogenides prepared with these fluxes at 1273 K.12-15,18,21,25-27,32-34 These compounds are given in Tables 2 and 3. A change of the flux from KI to Sb2Q3 (Q ) S, Se) produces different compounds. For example, when La, Yb, and S are reacted in a KI flux at (31) Wendlandt, W. W.; Hecht, H. G. Reflectance Spectroscopy; Interscience Publishers: New York, 1966. (32) Rodier, N.; Tien, V. Acta Crystallogr. 1976, 32, 2705. (33) Becker, D. F.; Kasper, J. S. Acta Crystallogr. 1957, 10, 332. (34) Adolphe, C. Ann. Chim. (Paris) 1965, 10, 271.

Inorganic Chemistry, Vol. 46, No. 22, 2007

9215

Jin et al.

Figure 1. Illustration of the three-dimensional structure of La3LuSe6 viewed down the c-axis.

1123 K, β-LaYbS3 is obtained.14 In contrast, when the same reaction is performed using a Sb2S3 flux, γ-LaYbS3 crystallizes. We have not noted the same temperature sensitivity as observed for the halide fluxes and find instead that temperature primarily affects crystal growth. The structures of Ln/Ln′/Q phases depend highly on the choices of Ln and Ln′. This is especially true for La/Ln′/Se, which can adopt five different structures with the variation of Ln′. Ordered phases predominate when Ln and Ln′ ions have larger differences in size. Disordered compounds are often present when the difference in size of the lanthanide ions becomes too small because of the similar structural chemistry of lanthanides; some exceptions to this include LaLu3S6 and LaxYb5-xSe7. The limitations of using Sb2Q3 (Q ) S, Se) fluxes to prepare LnLn′Q include: (1) Attempts to prepare interlanthanide tellurides have not succeeded. (2) When the ionic radii of the two Ln3+ ions approach equality, the product fails to separate from the flux, and the resultant microcrystalline compounds do not diffract well. (3) Occasionally, the use of a stereomicroscope to distinguish and manually separate products from Sb2Q3 (Q ) S, Se) fluxes is difficult to accomplish. While this was not the case for this or previously published works, not all reactions yield crystals well separated from the flux. We have not found a good solvent or acid for dissolving the flux that leaves the product unreacted. Structures of LnxLuySez (Ln ) La, Ce, Pr, Nd, Sm, Gd). The Ln3LuSe6 (Ln ) La, Ce) compounds adopt the U3ScS6type32 structure. The unit cell of La3LuSe6, projected along the c-axis, is shown in Figure 1. There are three crystallographically unique Ln sites (4g) and two octahedral Lu positions (2d, 2b) in the structure. Both Ln(1) and Ln(2) atoms are surrounded by eight Se atoms and occur as bicapped trigonal prisms. Ln(3) sites are seven-coordinate in a monocapped trigonal prismatic environment. LnSe8 and LnSe7 polyhedra share faces or edges with each other to form

9216 Inorganic Chemistry, Vol. 46, No. 22, 2007

Figure 2. Unit cell of β-PrLuSe3 viewed along the a-axis. Pr-Se bonds have been omitted for clarity.

two-dimensional slabs extending in the [ac] plane. Furthermore, these slabs connect at the Se(4) positions to produce a three-dimensional structure. The gaps between these slabs are filled by isolated one-dimensional edge-sharing LuSe6 octahedral chains running down the c-axis. The bond distances for these two compounds, which can be found in Supporting Information, are normal compared to average values reported by Shannon.35 In the case of La3LuSe6, the bond distances for the LaSe8, LaSe7, and LuSe6 polyhedra range from 2.9982(8) to 3.3408(11), 2.9229(11) to 3.1116(11), and 2.6629(9) to 2.8257(6) Å, respectively. The series of β-LnLuSe3 (Ln ) Pr, Nd) are isotypic with UFeS3.24 The structure, as shown in Figure 2, is constructed from two-dimensional LuSe6 octahedra layers, which are separated by Ln3+ ions. The Pr3+ and Nd3+ coordinate to eight Se atoms with a bicapped trigonal prismatic geometry. The connectivities within LuSe6 layers are illustrated in Figure 3. The LuSe6 octahedral units are edge-sharing along the a-axis and corner-sharing along the c-axis. The bond lengths within these two compounds are regular. For example, the Pr-Se and Lu-Se distances in compound β-PrLuSe3 are in the range of 2.9035(18) and 3.3670(17) and 2.7102(10) and 2.8072(11) Å, respectively. Sm1.82Lu2.18Se6 and Gd1.87Lu2.13Se6 crystallize in F-Ln2S3type25,26 structure, which was detailed in one of our previous papers.22 As shown in Figure 4, the eight-coordinate bicapped trigonal prismatic Ln(1) ions (Figure 5) sit in the onedimensional channels formed by three different double chains via edge- and corner-sharing. These double chains, which all run down the b-axis, are constructed from Ln(2)Se7 (35) Shannon, R. D. Acta Crystallogr. A 1976, 32, 751. (36) Kittel, C. Introduction to Solid State Physics, 6th ed.; Wiley, New York, 1986.

Lutetium-Based Interlanthanide Selenides

Figure 3. Depiction of an individual LuSe6 octahedra layer viewed down the b-axis in β-PrLuSe3.

Figure 5. Illustrations of the coordination environments for Pr ions in β-PrLuSe3 and Sm(1)/Lu(1) ions in Sm1.82Lu2.18Se.

Figure 4. View of the three-dimensional channel structure of Sm1.82Lu2.18Se6 along the b-axis.

monocapped trigonal prisms, Ln(3)Se6 octahedra, and Ln(4)S6 octahedra, respectively. Within each double chain, the building polyhedra share edges with each other both in the direction of chain propagation and with adjacent chains. For Sm1.82Lu2.18Se6, the average distances for Ln(1)S8, Ln(2)Se7, Ln(3)Se6,and Ln(4)Se6 polyhedra are 3.0406(10), 2.9230(10), 2.8064(10), and 2.7791(9) Å, respectively, which are comparable to Shannon’s data:35 3.05 Å for SmSe8, 3.00 Å for SmSe7, 2.90 Å for LuSe7, and 2.84 Å for LuSe6. Magnetic Susceptibility Measurements. Figure 6 shows the temperature dependence of the inverse molar magnetic susceptibilities for β-LnLuSe3 (Ln ) Pr, Nd). Both compounds are paramagnetic and deviate from the Curie-Weiss law below 40 K. The effective magnetic moment and Weiss constant were obtained by fitting the high-temperature susceptibility data into the Curie-Weiss law. As shown in Table 4, the effective magnetic moments are close to

Figure 6. Temperature dependence of the reciprocal molar magnetic susceptibility for β-PrLuSe3 and β-NdLuSe3, under an applied magnetic field of 0.1 T between 2 and 300 K. The straight line represents the fit to Curie-Weiss law in the range of 100-300 K.

calculated values for free Ln3+ ions. The negative θp values indicate antiferromagnetic coupling between magnetic ions. The magnetic susceptibility of Sm1.82Lu2.18Se6 shows van Vleck paramagnetic behavior similar to the Sm metal, which is displayed in Figure 7. There is no magnetic transition down to 2 K, and the susceptibility data do not follow the CurieWeiss law. The difference between the ground state (6H5/2) and the first excited state (6H7/2) of Sm3+ is not large compared to thermal energy (kBT). Therefore, the excited states make significant contributions to the magnetic susceptibility at high temperature.37 The experimental effective magnetic moment of Sm3+ can be determined approximately Inorganic Chemistry, Vol. 46, No. 22, 2007

9217

Jin et al. Table 4. Magnetic Parameters for Ce3LuSe6, β-LnLuSe3 (Ln ) Pr, Nd), and Gd1.87Lu2.13Se6 formula

Pcal (µB)

Peff (µB)

θp (K)

R2

Ce3LuSe6 β-PrLuSe3 β-NdLuSe3 Gd1.87Lu2.13Se6

4.40 3.58 3.62 10.86

4.56(1) 3.509(3) 3.913(9) 11.77(1)

-20(1) -15.6(4) -25(1) -4.4(4)

0.99959 0.99993 0.99961 0.99991

aP 36 and experimental, respectively, effective cal and Peff: calculated magnetic moments per formula unit. b Weiss constant (θp) and goodness of fit (R2) obtained from high-temperature (100-300 K) data.

Figure 8. Inverse molar magnetic susceptibility vs temperature for Gd1.87Lu2.13Se6 under an applied magnetic field of 0.1 T between 2 and 300 K. The solid line represents the fit to Curie-Weiss law in the range of 100300 K. Inset shows the molar magnetic susceptibility at low temperature.

Figure 7. Molar magnetic susceptibility vs temperature between 2 and 300 K for Sm1.82Lu2.18Se6. Data were taken under an applied magnetic field of 0.1 T.

using µeff ) [3kBχmT/(Lµ0µB2)]1/2, where kB is Boltzmann constant, L is Avogadro’s number, µ0 is vacuum permeability, T is temperature (K), and χm is molar susceptibility. At T ) 300 K, µeff ) 1.02 µB, which is smaller than the calculated value (1.55 µB) for free Sm3+ ions using the van Vleck formula.37 This is probably caused by crystal-field effects. Sm1.82Lu2.18Se6 is an excellent example of the usefulness of incorporating a diamagnetic lanthanide into interlanthanide selenides. If another paramagnetic lanthanide been selected, as was done for Er3SmSe6,20 the van Vleck behavior of Sm3+ might have been masked. This is especially pronounced for Sm3+ because it has the smallest measured moment for a lanthanide. The magnetic susceptibility of Gd1.87Lu2.13Se6 obeys the Curie-Weiss law above the temperature ∼4 K where it undergoes a sharp antiferromagnetic transition, as shown in Figure 8. The effective magnetic moment and Weiss constant were obtained to be 11.77(1) µB per formula unit and -4.4(4) K. The magnetization measurement was performed at 2 K, and the results are presented in Figure 9. The saturation moment per Gd3+ ion is 7.5 µB, which is close to the value for the free Gd3+ ion (7.94 µB) assuming g ) 2. There is a weak spin reorientation transition at approximately H ) 0.5 T. Ce3LuSe6 shows a deviation from the Curie-Weiss law near 70 K caused by crystal-field effects. A magnetic transition was observed below 5 K, which is illustrated in Figure 10. A small divergence on the ZFC-FC measurements

(Figure 11) below this temperature may indicate a ferromagnetic component of the transition or might be caused by small temperature fluctuations. To investigate the magnetic transition in detail, the magnetization measurements at 2 K were conducted as well. Figure 12 shows the fielddependent magnetizations for Ce3LuSe6. M(H) increases abruptly at low field, which is consistent with ferromagnetic behavior. However, the lack of substantial difference between the ZFC and FC measurements, as well as the absence of magnetic hysteresis at 2 K, is indicative of soft ferromagnet behavior.38 The saturation moment per Ce3+ ion (1.13 µB) is substantially smaller than the moment for the free Ce3+ ion (2.54 µB), assuming g ) 6/7. This can probably be ascribed to crystal-field splitting of the ground state of the Ce3+ ion (2F5/2). The Weiss constant from the fit of the data from 100 to 300 K for Ce3LuSe6 was determined to be -20(1) K, indicating antiferromagnetic interactions between Ce3+ ions at higher temperatures. It is worth noting that the |θp| value may be enlarged because of the crystal-field splitting of the

(37) Van Vleck, J. H. The Theory of Electric and Magnetic Susceptibilities; Oxford University Press: London, 1932.

(38) Singh, S.; Sheet, G.; Raychaudhuri, P.; Dhar, S. K. Appl. Phys. Lett. 2006, 88, 022506.

9218 Inorganic Chemistry, Vol. 46, No. 22, 2007

Figure 9. Magnetization for Gd1.87Lu2.13Se6 as a function of applied field at 2 K. Inset shows the M(H) curve between 0 and 1 T. Red and green lines are linear fits extended from zero field and from 1 T, respectively. Slight increasing of the slope and the weak spin reorientation transition field at the junction (up arrow) can be observed.

Lutetium-Based Interlanthanide Selenides

Figure 10. Inverse molar magnetic susceptibility as a function of temperature for Ce3LuSe6 under an applied magnetic field of 0.1 T between 2 and 300 K. The straight line represents the fit to Curie-Weiss law in the range of 100-300 K. Inset shows the inverse molar magnetic susceptibility at low temperature.

Figure 11. Molar magnetic susceptibility as a function of temperature for Ce3LuSe6 under ZFC and FC conditions with an applied magnetic field of 0.01 T between 2 and 25 K.

Figure 13. UV-vis diffuse reflectance spectra of LnxLuySez (Ln ) La, Ce, Pr, Nd, Sm, Gd).

Optical Properties. There are few interlanthanide selenides reported in the literature. SmEr3Se6, a red compound, was determined to be a wide direct band gap semiconductor with a band gap of 2.0 eV.20 The series of compounds, β-LnYbSe3 (Ln ) La, Ce, Pr, Nd, Sm), are black in color, as are the title compounds.14 The UV-vis-NIR diffuse reflectance spectra (Figure 13) of LnxLuySez (Ln ) La, Ce, Pr, Nd, Sm, Gd) were collected, and the band gaps were extrapolated from the absorption edges.39 For La3LuSe6, Ce3LuSe6, β-PrLuSe3, β-NdLuSe3, Sm1.82Lu2.18Se6, and Gd1.87Lu2.13Se6, the band gaps were found to be 1.26, 1.10, 1.56, 1.61, 1.51, and 1.56 eV, respectively. The more condensed structure that Ln3LuSe6 (Ln ) La, Ce) adopts may be the reason for their considerably smaller band gaps compared to those of the Pr-, Nd-, Sm-, and Gd-containing phases. The smaller value for Ce3LuSe6 is the result of the relatively low energy of the 4f1 f 4f05d1 transition for cerium. The fine-structure observed in the spectra for β-PrLuSe3, β-NdLuSe3, and Sm1.82Lu2.18Se6 is actually caused by f-f transitions within the lanthanide ions. There is also pronounced tailing off of the transition observed for La3LuSe6 that could be attributed to an indirect band gap or to an impurity like Sb2Se3.40 Conclusions

Figure 12. Magnetization for Ce3LuSe6 as a function of applied field at 2 K.

full J ) 5/2 multiplet for Ce3+. To conclude, Ce3LuSe6 orders ferromagnetically with a weak antiferromagnetic component that might be the result of canted spins of Ce3+.

Molten Sb2Q3 (Q ) S, Se) fluxes have been proven themselves to be useful in the preparation of ternary and quaternary interlanthanide chalcogenides. The composition and structure of the products depends highly on the choices of lanthanides and chalcogenides. In this present study, we detailed the synthesis of lutetium-based interlanthanide selenides LnxLuySez (Ln ) La, Ce, Pr, Nd, Sm, Gd) using a Sb2Se3 flux. All of these compounds show diverse structures and physical properties as a function of the Ln ions. Magnetic measurements have shown that both β-PrLuSe3 and β-NdLuSe3 are Curie-Weiss-type paramagnets. Sm1.82Lu2.18Se6 exhibits van Vleck paramagnetism. Gd1.87Lu2.13Se6 was found (39) Schevciw, O.; White, W. B. Mater. Res. Bull. 1983, 18, 1059. (40) Sutorik, A. C.; Kanatizidis, M. G. Chem. Mater. 1997, 9, 387.

Inorganic Chemistry, Vol. 46, No. 22, 2007

9219

Jin et al. to have an antiferromagnetic transition around 4 K, whereas Ce3LuSe6 has soft ferromagnetic ordering below 5 K. Acknowledgment. This work was supported by the U.S. Department of Energy under Grant DE-FG02-02ER45963 through the EPSCoR Program. Funds for the purchase of the UV-vis-NIR spectrometer used in these studies were provided through the Chemical Sciences, Geosciences and Biosciences Division, Office of Basic Energy Sciences, Office of Science, Heavy Elements Program, U.S. Department of Energy under Grant DE-FG02-01ER15187. J.S.B. and E.S.C. acknowledge support from NSF-DMR 0203532. A portion of this work was performed at the National High Magnetic Field Laboratory, which is supported by the

9220 Inorganic Chemistry, Vol. 46, No. 22, 2007

National Science Foundation Cooperative Agreement No. DMR-0084173, by the State of Florida, and by the Department of Energy. Supporting Information Available: X-ray crystallographic files in CIF format for Ln3LuSe6 (Ln ) La, Ce), β-LnLuSe3 (Ln ) Pr, Nd), and LnxLu4-xSe6 (Ln ) Sm, Gd; x ) 1.82, 1.87), selected bond distances for Ln3LuSe6 (Ln ) La, Ce), β-LnLuSe3 (Ln ) Pr, Nd), and LnxLu4-xSe6 (Ln ) Sm, Gd; x ) 1.82, 1.87) (Tables S1, S2, and S3), and magnetization data for β-LnLuSe3 (Ln ) Pr, Nd) and Sm1.82Lu2.18Se6. This material is available free of charge via the Internet at http://pubs.acs.org. IC701012J