Synthesis, Morphological, and Electro-optical ... - ACS Publications

May 11, 2016 - Asuccessful implementation of a new class of materials or means of processing ..... edge financial support by the Austrian Science Fund...
0 downloads 0 Views 2MB Size
Subscriber access provided by UOW Library

Communication

Synthesis, morphological and electro-optical characterizations of metal/semiconductor nanowire heterostructures Markus Glaser, Andreas Kitzler, Andreas Johannes, Slawomir Prucnal, Heidi Potts, Sonia Conesa-Boj, Lidija Filipovic, Hans Kosina, Wolfgang Skorupa, Emmerich Bertagnolli, Carsten Ronning, Anna Fontcuberta i Morral, and Alois Lugstein Nano Lett., Just Accepted Manuscript • DOI: 10.1021/acs.nanolett.6b00315 • Publication Date (Web): 11 May 2016 Downloaded from http://pubs.acs.org on May 13, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Nano Letters is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

Processing and material characterization of Ga/GaAs/Si NW heterostructures. (a) Processing scheme: Epitaxial VLS-grown Si 〈111〉 NWs covered with 20 nm SiO2; Room temperature ion implantation of Ga and As (2 at% each) with samples mounted on a 45° tilted and rotating specimen holder; Formation of wired GaAs NCs after 20 ms FLA (54.2 J/cm2). (b) SEM image of a single Ga/GaAs/Si NW heterostructure with the respective µ-Raman spectrum acquired from the center of the GaAs NC (red arrow). Denoted peaks are identified as (I) GaAs TO: 272 cm-1, (II) GaAs surface phonon: 287 cm-1, (III) local vibrational modes of Si-doped GaAs: 360–410 cm-1, (IV) nano-crystalline Si: 487.5 cm-1 and (V) Si zone center phonon mode: 517.9 cm-1 (see Supplementary Information 3 for details). (c) SEM image of a Ga/GaAs/Si NW heterostructure with SiO2 shell and Si, Ga & As maps acquired from TEM-EDX analysis shown as a color overlay. HRTEM detail micrographs of the axial interfaces are shown in the right panel along with the respective fast Fourier transforms of the crystalline Si and GaAs and amorphous Ga segments in the insets. 88x46mm (300 x 300 DPI)

ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Electrical characterization of selected NW heterostructures. (a) I/V characteristics of a processed Si NW without NCs (NW1), a Si NW heterostructure with a GaAs NC (NW2) and four Si NWs with Ga/GaAs NCs (NW3–NW6). Axial lengths of the GaAs NCs are for NW2: 124 nm (□), NW3: 136 nm (△), NW4: 180 nm (▽ ), NW5: 245 nm (×) and NW6: 469 nm (○). The inset shows the SEM image of NW6 with electrical contacts and the direction of the bias VSD applied to the source contact next to the Ga segment is depicted. The drain contact as well as the Si substrate is grounded. (b) Scatter diagram of |VSD| values of measured NW heterostructures under reverse bias at |IS| = 200 nA as a function of GaAs NC length with a linear fitting curve. 73x31mm (300 x 300 DPI)

ACS Paragon Plus Environment

Page 2 of 27

Page 3 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

Simulated energy band diagrams. Band diagrams of a Ga/GaAs/Si heterostructure similar to NW4, calculated with the semi-classical device simulator Minimos-NT under reverse (left panel), zero (center panel) and forward (right panel) bias conditions. EV denotes the valence band maximum and EC the conduction band minimum. The Fermi level as well as the electron and hole quasi Fermi levels are denoted by EF, EF,n and EF,p, respectively. The heterojunctions were assumed to be defect-free and the work function of Ga was fixed to 4.3 eV.23 Under non-zero bias conditions, the main drift component of the current is sketched as electrons (Θ) entering the GaAs NC by tunneling through the Ga/GaAs Schottky junction (reverse bias) or the Si/GaAs heterojunction (forward bias). The cascade process responsible for generating electron-hole (+) pairs due to impact ionization of hot charge carriers is shown for the device operated under reverse bias. The inset shows the I/V characteristics of NW4 with marked operating points for the three bias conditions. 74x32mm (300 x 300 DPI)

ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Room temperature EL of a Ga/GaAs/Si NW heterostructure device. (a) SEM image, showing the two-terminal device (NW4) with a Ga segment next to a 180 nm long GaAs NC. (b) Optical microscope image (1 minute exposure time) of the same device under reverse bias conditions (VSD = -9.4 V, IS = -4 µA) with visible EL originating from the GaAs NC. Spectral decomposition of the EL spot is due to artefacts of the imaging system. (c) Corrected EL spectra acquired from NW4 under forward bias (VSD = 4.85 V, IS = 8.3 µA) and reverse bias (VSD = -9.4 V, IS = -4 µA). Black curves are fittings according to Equation (1), representing luminescence ascribed to Bremsstrahlung. Under reverse bias, band-to-band EL is superimposed, whereas under forward bias only Bremsstrahlung can be seen at high field conditions. 66x25mm (300 x 300 DPI)

ACS Paragon Plus Environment

Page 4 of 27

Page 5 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

EL spectra with designated transition energies. (a) Room temperature EL spectra obtained from NW3, NW5 and NW6 and the respective bias parameters. Vertical lines denote transition energies for the radiative b-b recombinations correlating with maxima in the presented EL spectra. (b) Sketch of the GaAs energy band structure between the Brillouin zone symmetry points L, Γ, X with the lowest conduction band, heavy-hole, light-hole as well as the split-off valence bands with the relevant energies obtained from ref. 28: EG = 1.42 eV, EL = 1.72 eV, EX = 1.91 eV, ESO = 0.34 eV. Radiative b-b recombinations identified by energy values of maxima in EL spectra of investigated NW devices are shown with colored arrows. Solid and dashed lines denote indirect (phonon-assisted) and direct transitions, respectively. 67x26mm (300 x 300 DPI)

ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

Synthesis, morphological and electro-optical

2

characterizations of metal/semiconductor nanowire

3

heterostructures

4

Markus Glaser†, Andreas Kitzler†, Andreas Johannes‡, Slawomir Prucnal§, Heidi Potts║, Sonia

5

Conesa-Boj║, Lidija Filipovic┴, Hans Kosina┴, Wolfgang Skorupa§, Emmerich Bertagnolli†,

6

Carsten Ronning‡, Anna Fontcuberta i Morral║, Alois Lugstein†,*

7



Institute of Solid State Electronics, TU Wien, Floragasse 7, 1040 Wien, Austria

8



Institute for Solid State Physics, Friedrich-Schiller-University Jena, Max-Wien-Platz 1,

9

07743 Jena, Germany

10

§

11

Rossendorf, Bautzner Landstraße 400, 01328 Dresden, Germany

12



13

1015 Lausanne, Switzerland

14



Page 6 of 27

Institute of Ion Beam Physics and Materials Research, Helmholtz-Zentrum Dresden-

Laboratoire des Matériaux Semiconducteurs, Ecole Polytechnique Fédérale de Lausanne,

Institute for Microelectronics, TU Wien, Gußhausstraße 25-29, 1040 Wien, Austria

15 16

KEYWORDS

17

Nanowires, heterostructures, Schottky, GaAs, Si, electroluminescence

18 1 ACS Paragon Plus Environment

Page 7 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

19

20

ABSTRACT

21

In this letter, we demonstrate the formation of unique Ga/GaAs/Si nanowire heterostructures,

22

which were successfully implemented in nanoscale light-emitting devices with visible room

23

temperature electroluminescence. Based on our recent approach for the integration of InAs/Si

24

heterostructures into Si nanowires by ion implantation and flash lamp annealing, we developed a

25

routine that has proven to be suitable for the monolithic integration of GaAs nanocrystallite

26

segments into the core of silicon nanowires. The formation of a Ga segment adjacent to longer

27

GaAs nanocrystallites resulted in Schottky-diode-like I/V characteristics with distinct

28

electroluminescence originating from the GaAs nanocrystallite for the nanowire device operated

29

in the reverse breakdown regime. The observed electroluminescence was ascribed to radiative

30

band-to-band recombinations resulting in distinct emission peaks and a low contribution due to

31

intraband transition, which were also observed under forward bias. Simulations of the obtained

32

nanowire heterostructure confirmed the proposed impact ionization process responsible for hot

33

carrier luminescence. This approach may enable a new route for on-chip photonic devices used

34

for light emission or detection purposes.

35

36

MAIN TEXT

37

A successful implementation of a new class of materials or means of processing has a potential

38

impact on long-term future technology nodes. Fundamental investigations of electronic and

39

optical properties of nanowire (NW) heterostructures thus triggered tremendous research on 2 ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 27

40

novel device concepts1–3. Particularly, integrating photonic devices into the Si platform is a

41

challenge that requires the development of elaborate device designs4. Nanoscale Si-based

42

photonic devices would provide full compatibility with mature IC manufacturing processes, yet

43

owing to the inherent disadvantages of the indirect Si band gap, no efficient light emission can

44

be obtained. A hybrid Si platform, integrating III–V functionality into Si nanostructures, would

45

give access to a wide range of high-speed electronic and high-performance photonic

46

applications. However, the diverse natures of the III–V and Si device approaches, material

47

technologies and processing have posed a significant obstacle in the route for Si-based hybrid

48

optoelectronic systems in the past. Within the last years, a few approaches for Si-based hybrid

49

NW formation via bottom-up growth techniques5,6 or in combination with substrate etching7

50

were presented, which are restricted to semiconductors, with limitations in epitaxial integration

51

and in retaining the NW morphology. Recently, we published a novel approach for integrating

52

III–V nano-crystallites (NCs) into Si NWs by combining ion implantation and flash lamp

53

annealing, yielding InAs/Si NW heterostructures8. Within this study we present this approach to

54

be capable for integrating GaAs NCs into crystalline Si NWs. Due to a modification of the ion

55

implantation routine, NCs with increased axial lengths are obtained, exhibiting a metallic Ga

56

segment adjacent to the GaAs NCs. Such wired NC configuration ensures directed current flow

57

through the abrupt heterointerfaces.

58

We achieved the monolithic integration of GaAs and Ga/GaAs NCs into Si NWs by exploring

59

ion implantation and flash lamp annealing (FLA) routines. Such application of mature

60

semiconductor processing techniques9 allows to process wafer-scale NW samples along with

61

excellent control of NW morphologies. The main processing steps for NW heterostructure

62

formation are sketched in Figure 1a.

3 ACS Paragon Plus Environment

Page 9 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

63 64

Figure 1. Processing and material characterization of Ga/GaAs/Si NW heterostructures. (a)

65

Processing scheme: Epitaxial VLS-grown Si 〈111〉 NWs covered with 20 nm SiO2; Room

66

temperature ion implantation of Ga and As (2 at% each) with samples mounted on a 45° tilted

67

and rotating specimen holder; Formation of wired GaAs NCs after 20 ms FLA (54.2 J/cm2). (b)

68

SEM image of a single Ga/GaAs/Si NW heterostructure with the respective µ-Raman spectrum

69

acquired from the center of the GaAs NC (red arrow). Denoted peaks are identified as (I) GaAs

70

TO: 272 cm-1, (II) GaAs surface phonon: 287 cm-1, (III) local vibrational modes of Si-doped

71

GaAs: 360–410 cm-1, (IV) nano-crystalline Si: 487.5 cm-1 and (V) Si zone center phonon

72

mode: 517.9 cm-1 (see Supporting Information 3 for details). (c) SEM image of a Ga/GaAs/Si

73

NW heterostructure with SiO2 shell and Si, Ga & As maps acquired from TEM-EDX analysis

74

shown as a color overlay. HRTEM detail micrographs of the axial interfaces are shown in the

75

right panel along with the respective fast Fourier transforms of the crystalline zinc-blende Si and

76

GaAs and amorphous Ga segments in the insets.

77 4 ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 27

78

The samples consisted of 〈111〉 oriented zinc-blende Si NWs epitaxially grown on Si(111)

79

substrates via the gold-catalyzed vapor-liquid-solid (VLS) approach10. A low pressure chemical

80

vapor deposition system was utilized for NW growth, using SiH4 (2% diluted in He) as precursor

81

gas, a growth temperature of T = 788 K and a total pressure of p = 4 mbar, which resulted in

82

epitaxial and single crystalline NWs with typical lengths of 10 µm and mean diameters of about

83

130 nm. Prior to high fluence implantation of Ga and As ions, the gold catalyst was removed and

84

a 20 nm thick SiO2 layer had to be deposited by plasma enhanced chemical vapor deposition,

85

acting as a protective mold during implantation and millisecond FLA. In order to achieve a

86

homogeneous ion distribution and to avoid bending of the NWs due to high fluence ion

87

bombardment11, samples were mounted on a 45° tilted stage and continuously rotated during ion

88

implantation. Due to nanostructure-related peculiarities of ion beam induced sputtering,

89

implantation parameters were derived from 3D Monte Carlo simulations using iradina12. Ga and

90

As ions were implanted alternatingly, resulting in a nominal concentration of 2 at% Ga and 2

91

at% As inside the NW core. Full amorphization and a significant shortening as well as a change

92

of the NW cross-section from hexagonal to circular was observed due to plastic deformation of

93

NWs during ion implantation13. Remarkably, the SiO2 shell was found to persist during

94

implantation with little intermixing at the interface to the Si core (see Supporting Information 1).

95

Finally the phase separation and actual formation of NW heterostructures by liquid phase epitaxy

96

(LPE)14 was induced by a 3 minutes preheating at 600 °C and subsequent 20 ms FLA, whereby

97

the SiO2 shell stabilized the molten core of the NWs. FLA was performed in Ar atmosphere with

98

a flash energy of 54.2 J/cm², resulting in peak sample temperatures of approx. 1470 K.8 Within

99

the cooling period after FLA, GaAs NCs formed with lengths varying from approx. 10 nm to 1

5 ACS Paragon Plus Environment

Page 11 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

100

µm (cf. Supporting Information 2). In addition, an adjacent Ga segment was observed for NCs

101

exceeding a length of about 75 nm.

102

The composition, morphology and crystallinity of such obtained NW heterostructures were

103

analyzed in detail by µ-Raman spectroscopy, transmission electron microscopy (TEM) and

104

energy dispersive X-ray spectroscopy (EDX). Figure 1b shows a typical µ-Raman spectrum

105

acquired from the GaAs NC depicted in the scanning electron microscopy (SEM) image. The

106

main Raman features were identified as the transverse optical (TO) phonon mode of crystalline

107

GaAs (peak I), a GaAs related surface phonon mode due to the cylindrical shape of the GaAs NC

108

(peak II)15 and GaAs local vibrational modes (peak III)16. The occurrence of GaAs local

109

vibrational modes indicates a high concentration of Si atoms occupying Ga or As lattice sites. As

110

the excitation laser spot exceeds the GaAs NC size, Raman features arising from the adjacent Si

111

NW (peak IV, V) were also detected (see Supporting Information 3).

112

Extensive high resolution TEM (HRTEM) and EDX analysis confirmed composition and

113

crystallinity of both the Si and GaAs segments with abrupt interfaces as indicated by Raman

114

investigations (see Supporting Information 4). Although a rapid annealing step was applied,

115

consisting of melting of the NW core during the 20 ms FLA step and recrystallization during

116

subsequent cooling, only a low number of crystallographic defects of the NW heterostructure

117

were observed in TEM investigations (see Supporting Information 5). As mentioned above, for

118

larger GaAs NCs we observed the formation of amorphous Ga segments, separating the GaAs

119

NCs from the Si NW core. Previous investigations indicated a liquid state for nanoscale Ga

120

droplets at room temperature17, which may also apply for the observed amorphous structure of

121

the Ga segments. Further EDX revealed As within the recrystallized Si NWs, thus expecting n-

122

type doping of the Si NW. In the HRTEM images of Figure 1c, the respective interfaces of the

6 ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 27

123

axially aligned Si/Ga/GaAs/Si segments are shown. Remarkably, the Si NWs, although fully

124

amorphous after ion implantation, recrystallize in 〈111〉 directions along the NW axis during

125

LPE, which is also the predominant growth direction for VLS-grown Si NWs with diameters

126

above 40 nm.18 The embedded zinc-blende GaAs NCs adopt the crystallite direction of the Si

127

NW as shown in the fast Fourier transform patterns in Figure 1c. Furthermore, the amorphous Ga

128

segment formed next to larger GaAs NCs exhibits an abrupt interface to both the GaAs and the

129

Si NWs.

130

To determine the electrical transport properties of wired GaAs NCs embedded in Si NWs,

131

individual NW heterostructures were integrated in four-terminal as well as two-terminal (cf. inset

132

in Figure 2a) devices resembling a back-gated NW field effect transistor with a 120 nm thick

133

SiO2 layer as gate dielectric and the substrate as common gate. Electrical contacts to nanowire

134

devices were processed by e-beam lithography, e-beam evaporation of Ni and lift off techniques.

135 136

Figure 2. Electrical characterization of selected NW heterostructures. (a) I/V characteristics of

137

a processed Si NW without NCs (NW1), a Si NW heterostructure with a GaAs NC (NW2) and

138

four Si NWs with Ga/GaAs NCs (NW3–NW6). Axial lengths of the GaAs NCs are for NW2:

7 ACS Paragon Plus Environment

Page 13 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

139

124 nm (□), NW3: 136 nm (∆), NW4: 180 nm (∇), NW5: 245 nm (×) and NW6: 469 nm (○).

140

The inset shows the SEM image of NW6 with electrical contacts and the direction of the bias

141

VSD applied to the source contact next to the Ga segment is depicted. The drain contact as well as

142

the Si substrate is grounded. (b) Scatter diagram of |VSD| values of measured NW

143

heterostructures under reverse bias at |IS| = 200 nA as a function of GaAs NC length with a linear

144

fitting curve.

145 146

The I/V characteristics of a contacted Si NW without a NC exhibits linear behavior (NW1 in

147

Figure 2a) and four-terminal measurements revealed a resistivity of 1.1 mΩcm. Unambiguously

148

n-type doping was confirmed by thermoelectric measurements on individually contacted Si NWs

149

(see Supporting Information 6). Assuming As as the dopant, this corresponds to a bulk impurity

150

concentration of approx. 8.6 × 1019 cm-3 and thus degenerate doping of the Si NWs19. Due to the

151

high doping of the Si NW and the present SiO2 shell, influences of surface states or adsorbates

152

on the electronic structure of the NW core were assumed to be negligible. Furthermore, the low

153

resistivity of the Si NWs impeded the use of capacity-dependent scanning probe microscopy to

154

investigate NW doping.

155

For the NWs with GaAs NCs and Ga/GaAs hybrids, no such direct experimental determination

156

of the doping type could be achieved. However, as GaAs grown from a Si-rich high temperature

157

melt by LPE results in n-type GaAs crystals20, n-type doping was also assumed to be prevailing

158

in the present GaAs NCs. Furthermore, rectifying Ga/GaAs contacts only form with n-type

159

GaAs21, which agrees well with the Schottky-type behavior of the Ga/GaAs heterostructures

160

(NW3–NW6 in Figure 2a). The resistivity of the GaAs NCs was measured to be approx. 6 Ωcm

161

which corresponds to an effective impurity concentration of 1.5 × 1014 cm-3 in n-type GaAs19.

8 ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 27

162

However, Raman investigations (cf. Supporting Information 3) indicate considerably higher Si

163

impurity concentrations of about 5 × 1018 cm-3.22 Thus, we can conclude that, due to the

164

amphoteric nature of Si dopants in GaAs, compensation doping results in overall moderately

165

doped n-type GaAs NCs.

166

The highly n-type doped Si NWs aligned with a 124 nm long GaAs NC (NW2 in Figure 2a)

167

results in a quantum-barrier-like structure with a barrier height for conduction electrons of about

168

67.8 meV (see simulation results in Supporting Information 7). In contrast to the n-type Si NWs

169

for which ohmic behavior was observed (cf. NW1), a strongly nonlinear but symmetric behavior

170

is observed which is typical for field-induced tunneling currents that increase steeply when the

171

effective tunneling barrier narrows for ascending bias voltages. Temperature-dependent I/V

172

measurements, at a small bias voltage of 10 mV to minimize band-bending and tunneling effects,

173

yielded an effective barrier height of approx. 50 meV which is in reasonable agreement with

174

semi-classical device simulations (see Supporting Information 7).

175

For NW heterostructures with a Ga segment adjacent to the GaAs NC, the Ga/GaAs Schottky

176

junction dominates the I/V characteristics, resulting in a distinct rectifying behavior (NW3–NW6

177

in Figure 2a). I/V characteristics are further labelled forward (reverse) for positive (negative)

178

bias VSD applied to the NW end facing the Ga segment. According to the simulated energy band

179

diagram under forward bias (right panel in Figure 3) conduction electrons encounter the small

180

barrier at the Si/GaAs interface with a turn on voltage of around 0.2–0.6 V.

181

9 ACS Paragon Plus Environment

Page 15 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

182 183

Figure 3. Simulated energy band diagrams. Band diagrams of a Ga/GaAs/Si heterostructure

184

similar to NW4, calculated with the semi-classical device simulator Minimos-NT under reverse

185

(left panel), zero (center panel) and forward (right panel) bias conditions. EV denotes the valence

186

band maximum and EC the conduction band minimum. The Fermi level as well as the electron

187

and hole quasi Fermi levels are denoted by EF, EF,n and EF,p, respectively. The heterojunctions

188

were assumed to be defect-free and the work function of Ga was fixed to 4.3 eV.23 Under non-

189

zero bias conditions, the main drift component of the current is sketched as electrons (Θ)

190

entering the GaAs NC by tunneling through the Ga/GaAs Schottky junction (reverse bias) or the

191

Si/GaAs heterojunction (forward bias). The cascade process responsible for generating electron-

192

hole (⊕) pairs due to impact ionization of hot charge carriers is shown for the device operated

193

under reverse bias. The inset shows the I/V characteristics of NW4 with marked operating points

194

for the three bias conditions.

195 196

For such Si NW heterostructures containing a Ga/GaAs segment, Schottky barrier heights in

197

the range of 186–330 meV were obtained from temperature-dependent I/V measurements. With 10 ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 27

198

e the elementary charge, χ = 4.07 eV the electron affinity and eφm = 4.3 eV the work function of

199

GaAs23, the Schottky barrier height of an ideal Ga/GaAs junction can be calculated to eφ = eφm

200

− χ ≈ 230 meV. In literature, Schottky barrier heights of Ga/n-GaAs junctions are usually larger

201

than 1 eV, owing to Fermi level pinning caused by defects at the interface21. Thus, a reasonable

202

low number of interface defects due to the absence of Fermi level pinning can be assumed for the

203

obtained Ga/GaAs Schottky junctions within NW heterostructures.

204

Under reverse bias conditions, the voltage is supported across the drift region of the Schottky

205

contact with the maximum electric field located at the Ga/GaAs interface. Due to a weak barrier

206

lowering, the leakage current rises gradually with reverse bias as thermally excited electrons in

207

the metal surmount the barrier. However, as the field increases further, a fraction of high energy

208

carriers fail to lose energy by phonon emission, attaining energies in excess of the material

209

bandgap and lose energy by creating electron-hole pairs – a process generally known as impact

210

ionization24,25. At a crucial breakdown field, these generated carriers gain sufficient energies to

211

induce further impact ionizations cascades leading to avalanche carrier multiplication (left panel

212

in Figure 3).

213

Simulations of the reverse biased NW heterostructure yielded high impact ionization rates in

214

the GaAs NC next to the Schottky interface, proportional to the applied bias (see Supporting

215

Information 8). Since negligible voltage is supported within the metal and the degenerately

216

doped Si NW, the reverse blocking capability of the Schottky rectifier is governed by the GaAs

217

NC and the breakdown voltage thereby appears to be linearly dependent on the length of the NC,

218

as shown in Figure 2b.

219

Operating the Ga/GaAs/Si NW heterostructure devices under reverse bias in the avalanche

220

breakdown regime resulted in broadband light emission, clearly originating from the GaAs NCs.

11 ACS Paragon Plus Environment

Page 17 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

221

In Figure 4 an SEM image of the two-terminal device (Fig. 4a) and an optical microscope image

222

(Fig. 4b) are shown, demonstrating distinct electroluminescence (EL) of NW4 under reverse bias

223

conditions. The associated EL spectrum for the device operated under reverse and forward bias

224

conditions is depicted in Figure 4c. The measured EL spectra were corrected according to

225

transmission data obtained from calibrating the spectroscopy equipment with a calibrated

226

halogen light source.

227 228

Figure 4. Room temperature EL of a Ga/GaAs/Si NW heterostructure device. (a) SEM image,

229

showing the two-terminal device (NW4) with a Ga segment next to a 180 nm long GaAs NC. (b)

230

Optical microscope image (1 minute exposure time) of the same device under reverse bias

231

conditions (VSD = -9.4 V, IS = -4 µA) with visible EL originating from the GaAs NC. Spectral

232

decomposition of the EL spot is due to artefacts of the imaging system. (c) Corrected EL spectra

233

acquired from NW4 under forward bias (VSD = 4.85 V, IS = 8.3 µA) and reverse bias (VSD = -9.4

234

V, IS = -4 µA). Black curves are fittings according to Equation (1), representing luminescence

235

ascribed to Bremsstrahlung. Under reverse bias, band-to-band EL is superimposed, whereas

236

under forward bias only Bremsstrahlung can be seen at high field conditions.

237 12 ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 27

238

Pronounced features were observed in the EL spectra above the GaAs band gap energy EG =

239

1.42 eV, which are assigned to radiative band-to-band (b-b) recombinations. A continuous

240

background in the EL spectrum extending to the near-infrared is ascribed to intraband transitions,

241

or Bremsstrahlung26,27.

242

Under high forward biases, the weak EL appears to be consisting of Bremsstrahlung only.

243

Assuming a Maxwellian distribution for electrons and a bulk density of states with simple

244

parabolic energy bands, the rate R for light emission ascribed to Bremsstrahlung at an energy E

245

is proportional to27 R ∝ √E exp −

246







(1)

247

with kB the Boltzmann constant, and Te the electron temperature. Values for Te, obtained by

248

fitting Equation (1) to EL spectra, assuming the electron energy distribution to be reproduced by

249

the photon energy distribution, are in good agreement with temperatures of hot electrons in GaAs

250

high-electron-mobility transistors26.

251

In general, considerably higher EL intensities were observed under reverse bias conditions.

252

Bremsstrahlung corresponding to Te = 2256 K and superimposed b-b recombinations constitute

253

the EL spectra, as shown in Figure 4c for such a reverse biased device. For a more detailed

254

analysis of the b-b recombination related EL, Ga/GaAs/Si NW heterostructures with increasing

255

GaAs NC lengths and thus increasing breakdown voltages were investigated. Figure 5a shows

256

EL spectra of three NW heterostructures, exemplarily selected out of 30 investigated devices

257

which all exhibited similar EL characteristics.

13 ACS Paragon Plus Environment

Page 19 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

258 259

Figure 5. EL spectra with designated transition energies. (a) Room temperature EL spectra

260

obtained from NW3, NW5 and NW6 and the respective bias parameters. Vertical lines denote

261

transition energies for the radiative b-b recombinations correlating with maxima in the presented

262

EL spectra. (b) Sketch of the GaAs energy band structure between the Brillouin zone symmetry

263

points L, Γ, X with the lowest conduction band , heavy-hole, light-hole as well as the split-off

264

valence bands with the relevant energies obtained from ref. 28: EG = 1.42 eV, EL = 1.72 eV, EX =

265

1.91 eV, ESO = 0.34 eV. Radiative b-b recombinations identified by energy values of maxima in

266

EL spectra of investigated NW devices are shown with colored arrows. Solid and dashed lines

267

denote indirect (phonon-assisted) and direct transitions, respectively.

268 269

Operated under reverse bias conditions (cf. Fig. 2a), these devices exhibited a broad visible EL

270

extending to the near-infrared. Notably, there is no distinct emission peak which may be assigned

271

to the band gap energy EG = 1.42 eV of GaAs (cf. Figure 5b). Under reverse bias, the voltage is

272

supported across the drift region of the Schottky contact. As the moderately doped GaAs NC is

273

embedded between a metallic and a degenerately doped (i.e. highly conducting) Si NW, the

274

maximum electric field, exceeding 2 × 105 V/cm, is supposed to be located in the GaAs NC. At 14 ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 27

275

such high electric fields, the conduction band Γ valley population is approaching zero with high

276

populations of the X and L valleys25, diminishing direct Γ valley transitions (i.e. EL at the GaAs

277

band gap energy).

278

For EL in the visible spectral range, distinct emission peaks can be observed with the overall

279

maximum shifting to higher energies for longer GaAs NCs, i.e. increasing breakdown voltages

280

(cf. Fig. 2b). These distinct EL peaks are assigned to hot carrier luminescence26,27,29 with the

281

respective phonon-assisted radiative b-b recombinations as sketched in the GaAs energy band

282

structure in Figure 5b. Due to the necessity of energy and momentum conservation, light

283

emission arising from b-b recombinations requires electrons to be scattered from the indirect

284

conduction band valleys to the zone center (k ≈ 0). High phonon density of states are related to a

285

large number of phonon states for a certain energy in the phonon dispersion, i.e. parts of phonon

286

dispersion curves with almost zero slope30. In case of GaAs, the phonon dispersion of all kinds of

287

involved phonons exhibit approximately zero slope at the X- and L-symmetry points31. Thus, a

288

high density of states of phonons with the respective wave vectors are available for scattering

289

electrons to the zone center by emission or absorption of such phonons, resulting in the observed

290

EL maxima. The involvement of split-off band holes in radiative b-b recombinations in GaAs

291

was also observed in photoluminescence studies32. However, the respective b-b transitions

292

requires adequate electron population of the L and X valley, as well as holes in the heavy-hole,

293

light-hole and split-off band29. The formation of hot charge carriers in 〈111〉 oriented GaAs NCs

294

further requires electrons to gain energies higher than the impact ionization threshold (1.8–2

295

eV)25,33 through scattering events, changing their k-vector24.

296

The proposed hot charge carrier generation mechanism is sketched in the left panel of Figure 3

297

with electrons tunneling from Ga through the Schottky barrier into the GaAs NC. Under reverse

15 ACS Paragon Plus Environment

Page 21 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

298

bias, a high electric field is present in the GaAs depletion layer adjacent to the Schottky

299

interface, accelerating charge carriers which in turn attain energies in excess of the impact

300

ionization threshold. Such hot carriers, instead of transferring energy to phonons, lose energy by

301

elevating valence band electrons to the conduction band and these generated electron-hole pairs

302

themselves generate carrier pairs and the process enters runaway. Simulations of the actual

303

structures confirmed impact ionization and also high yields of holes adjacent to the Ga/GaAs

304

Schottky junction (see Supporting Information 8). Remarkably, with increasing bias voltages, EL

305

emission extends further into the GaAs NC, which is consistent with the impact ionization

306

generation rate simulations.

307

Radiative recombinations and intraband electron scattering thus result in the characteristic EL

308

spectra with contributions from b-b recombinations and Bremsstrahlung. This confirms the

309

assumed avalanche process with hot electrons injected from Ga into the GaAs NC, generating

310

holes and resulting in the observed EL. Such single-nanowire light emitters yielded external

311

quantum efficiencies of up to EQE = ∫ (Psp/Eλ) (e/I) dλ = 8.9 × 10−7, where the emitted spectral

312

power Psp was obtained from integrating the EL spectral power in the wavelength range λ = 400–

313

1000 nm. Eλ is the energy of a photon with wavelength λ, I the applied NW current and e the

314

elementary charge. However, including the numerical aperture of the spectroscopy system and

315

considering a homogeneously light emitting GaAs segment with a cylindrical shape, this results

316

in a high EL spectral power density of 14.8 mW/cm².

317

In conclusion, we demonstrated effective EL from avalanche light-emitting diodes in self-

318

assembled metal/semiconductor NW heterostructures. The axially aligned Si/Ga/GaAs/Si NW

319

heterostructures were achieved via a novel approach, combining VLS NW growth, ion

320

implantation and millisecond FLA. The visible spectrum of the EL is dominated by hot carrier

16 ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 27

321

luminescence due to impact ionization, revealing distinct maxima which are correlated with

322

GaAs interband transitions. A low broadband exponential component of the EL is ascribed to

323

Bremsstrahlung. A considerable benefit of the presented approach to process heterostructures

324

within Si NWs is the advantageous condition for combining highly mismatched materials,

325

provided by efficient strain relaxation. Recent experiments already supplied evidence for this

326

method to be applicable to other highly mismatched III–V/Si heterostructures, namely InAs or

327

InGaAs. Furthermore, this unique method is suitable for integrating axial metal segments into Si

328

NWs, by only implanting metal ions. In this study, single NW heterostructures were investigated

329

to gain insight into the fundamental properties of the processed light emitting devices. However,

330

this method could readily be applied to process a large scale device consisting of straight Si NW

331

arrays on bulk Si, allowing to significantly increase device performances due to parallel

332

operation of numerous NW heterostructures.

333 334

ASSOCIATED CONTENT

335

Supporting Information. SEM investigations of nanowire response on ion implantation and

336

annealing, thin crystallite formation, detailed Raman and TEM-EDX investigations,

337

experimental determination of Si nanowire doping type, simulations of Si/GaAs/Si barrier

338

heights, hole concentrations and impact ionization generation rates. This material is available

339

free of charge via the Internet at http://pubs.acs.org.

340

AUTHOR INFORMATION

341

Corresponding Author

342

* E-mail: [email protected]

17 ACS Paragon Plus Environment

Page 23 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

343

Notes

344

The authors declare no competing financial interest.

345 346

ACKNOWLEDGMENT

347

The authors thank Michael Stöger-Pollach from the USTEM at TU Wien for providing

348

EFTEM analysis of nanowire slices as well as Oskar Baumgartner from Global TCAD Solutions

349

for his support in setting up simulations. We gratefully acknowledge financial support by the

350

Austrian Science Fund (FWF) project No. I 724-N16, the Deutsche Forschungsgemeinschaft

351

(DFG) project No. R01198/14-1 and thank the Swiss National Science Foundation (SNF) for

352

funding through NCCR-QSIT. We would also like to acknowledge the ITN network

353

'NanoEmbrace'. Furthermore we thank the interdisciplinary Centre for Electron Microscopy

354

(CIME) at EPFL for access and training to the electron microscopes. The cleanroom facilities

355

were provided by the Center for Micro- and Nanostructures (ZMNS) at TU Wien.

356 357

ABBREVIATIONS

358

EDX, energy dispersive X-ray spectroscopy; EL, electroluminescence; FLA, flash lamp

359

annealing; HRTEM, high-resolution transmission electron microscopy; LPE, liquid phase

360

epitaxy; NC, nano-crystallite; NW, nanowire; SEM, scanning transmission electron

361

microscopy;TEM, transmission electron microscopy; VB, valence band; VLS, vapor-liquid-

362

solid.

363

18 ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 27

364

REFERENCES

365

(1) Yan, R.; Gargas, D.; Yang, P. Nature Photon. 2009, 3 (10), 569–576.

366

(2) Wallentin, J.; Anttu, N.; Asoli, D.; Huffman, M.; Åberg, I.; Magnusson, M. H.; Siefer, G.;

367

Fuss-Kailuweit, P.; Dimroth, F.; Witzigmann, B.; Xu, H. Q.; Samuelson, L.; Deppert, K.;

368

Borgström, M. T. Science 2013, 339 (6123), 1057–1060.

369 370 371 372 373 374 375 376 377 378

(3) Bryllert, T.; Wernersson, L.-E.; Froberg, L. E.; Samuelson, L. IEEE Electron Device Lett. 2006, 27 (5), 323–325. (4) Lockwood, D. J.; Pavesi, L. In Silicon Photonics; Topics in Applied Physics; Springer Berlin Heidelberg, 2004; pp 1–50. (5) Hocevar, M.; Immink, G.; Verheijen, M.; Akopian, N.; Zwiller, V.; Kouwenhoven, L.; Bakkers, E. Nat. Commun. 2012, 3, 1266. (6) Conesa-Boj, S.; Dunand, S.; Russo-Averchi, E.; Heiss, M.; Ruffer, D.; Wyrsch, N.; Ballif, C.; Fontcuberta i Morral, A. Nanoscale 2013, 5 (20), 9633–9639. (7) Borg, M.; Schmid, H.; Moselund, K. E.; Signorello, G.; Gignac, L.; Bruley, J.; Breslin, C.; Das Kanungo, P.; Werner, P.; Riel, H. Nano Lett. 2014, 14 (4), 1914–1920.

379

(8) Prucnal, S.; Glaser, M.; Lugstein, A.; Bertagnolli, E.; Stöger-Pollach, M.; Zhou, S.; Helm,

380

M.; Reichel, D.; Rebohle, L.; Turek, M.; Zuk, J.; Skorupa, W. Nano Res. 2014, 7 (12),

381

1769–1776.

382

(9) Fiory, A. T. J. Electron. Mater. 2002, 31 (10), 981–987.

383

(10) Wang, N.; Cai, Y.; Zhang, R. Q. Mater. Sci. Eng. R Rep. 2008, 60 (1-6), 1–51.

384

(11) Borschel, C.; Niepelt, R.; Geburt, S.; Gutsche, C.; Regolin, I.; Prost, W.; Tegude, F.;

385

Stichtenoth, D.; Schwen, D.; Ronning, C. Small 2009, 5 (22), 2576–2580.

19 ACS Paragon Plus Environment

Page 25 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

386 387 388 389 390 391 392 393

Nano Letters

(12) Borschel, C.; Ronning, C. Nucl. Instrum. Methods Phys. Res. Sect. B Beam Interact. Mater. At. 2011, 269 (19), 2133–2138. (13) Johannes, A.; Noack, S.; Wesch, W.; Glaser, M.; Lugstein, A.; Ronning, C. Nano Lett. 2015, 15 (6), 3800–3807. (14) Wutzler, R.; Rebohle, L.; Prucnal, S.; Bregolin, F. L.; Hübner, R.; Voelskow, M.; Helm, M.; Skorupa, W. J. Appl. Phys. 2015, 117 (17), 175307. (15) Watt, M.; Sotomayor Torres, C. M.; Arnot, H. E. G.; Beaumont, S. P. Semicond. Sci. Technol. 1990, 5 (4), 285–290.

394

(16) Newman, R. C. Semicond. Sci. Technol. 1994, 9 (10), 1749–1762.

395

(17) Sutter, E. A.; Sutter, P. W.; Uccelli, E.; Fontcuberta i Morral, A. Phys. Rev. B 2011, 84

396

(19), 193303.

397

(18) Schmidt, V.; Senz, S.; Gösele, U. Nano Lett 2005, 5 (5), 931–935.

398

(19) Sze, S. M.; Irvin, J. C. Solid-State Electron. 1968, 11 (6), 599–602.

399

(20) Ahn, B. H.; Shurtz, R. R.; Trussell, C. W. J. Appl. Phys. 1971, 42 (11), 4512–4513.

400

(21) Spicer, W. E.; Liliental‐Weber, Z.; Weber, E.; Newman, N.; Kendelewicz, T.; Cao, R.;

401

McCants, C.; Mahowald, P.; Miyano, K.; Lindau, I. J. Vac. Sci. Technol. B 1988, 6 (4),

402

1245–1251.

403 404

(22) Ketterer, B.; Mikheev, E.; Uccelli, E.; Fontcuberta i Morral, A. Appl. Phys. Lett. 2010, 97 (22), 223103.

405

(23) Michaelson, H. B. IBM J. Res. Dev. 1978, 22 (1), 72–80.

406

(24) Shichijo, H.; Hess, K. Phys. Rev. B 1981, 23 (8), 4197–4207.

407

(25) Cavassilas, N.; Aniel, F.; Fishman, G.; Adde, R. Solid-State Electron. 2002, 46 (4), 559–

408

566.

20 ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

409 410

Page 26 of 27

(26) Zanoni, E.; Manfredi, M.; Bigliardi, S.; Paccagnella, A.; Pisoni, P.; Tedesco, C.; Canali, C. IEEE Trans. Electron Devices 1992, 39 (8), 1849–1857.

411

(27) Zappe, H. P. Semicond. Sci. Technol. 1992, 7 (3), 391–400.

412

(28) Adachi, S. Handbook on Physical Properties of Semiconductors; Springer Science &

413 414 415

Business Media, 2004; Vol. 2. (29) Onodera, K.; Nishimura, K.; Furuta, T. IEEE Trans. Electron Devices 1999, 46 (11), 2170– 2177.

416

(30) Kittel, C. In Introduction to Solid State Physics; Wiley & Sons: USA, 2005; pp 106–128.

417

(31) Strauch, D.; Dorner, B. J. Phys. Condens. Matter 1990, 2 (6), 1457.

418

(32) Burr, K. C.; Tang, C. L. Appl. Phys. Lett. 1999, 74 (12), 1734–1736.

419

(33) Bude, J.; Hess, K. J. Appl. Phys. 1992, 72 (8), 3554–3561.

420

21 ACS Paragon Plus Environment

Page 27 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

82x44mm (300 x 300 DPI)

ACS Paragon Plus Environment