Synthesis of Reflective Polyimide Films via in Situ Silver (I) Reduction

Aug 18, 2017 - D. Scott Thompson,1" David W. Thompson,*1. Maggie L. Caplan,* and Anne K. St. Clair§. Department of Chemistry and Department of Applie...
0 downloads 0 Views 2MB Size
Chem. Mater. 1996, 7, 2171-2180

2171

Synthesis of Reflective Polyimide Films via in Situ Silver(1) Reduction Robin E. Southward,? D. Scott Thompson,? David W. Thompson,*>+ Maggie L. Caplan,s and Anne K. St. Clair$ Department of Chemistry and Department o f Applied Science, College of William and Mary, Williamsburg, Virginia 23185, and the Materials Division, National Aeronautics and Space Administration, Langley Research Center, Hampton, Virginia 23681 Received J u n e 9, 1995. Revised Manuscript Received A u g u s t 18, 1995@

Optically reflective polyimide films have been prepared by the incorporation of silver(1) acetate and hexafluoroacetylacetone into a dimethylacetamide solution of the poly(amic acid) formed from 3,3‘,4,4‘-benzophenonetetracarboxylic acid dianhydride (BTDA) and 4,4‘oxydianiline (4,4’-ODA). Thermal curing of the silver(1)-containing poly(amic acid) leads to imidization with concomitant silver(1) reduction, yielding a reflective silver surface. The metallized BTDA/4,4’-ODA films retain the essential mechanical properties of undoped films and have good thermal stability particularly in nitrogen atmospheres. The surface and bulk are not electrically conducting. Several additional soluble silver(1) additive systems were examined, all of which underwent thermal reduction to metallic silver but gave widely varying degrees of reflectivity.

Introduction Because of its singularly high reflection coefficient (0.93)and low coefficient of solar absorption (0.071, silver is a metal of choice for a reflecting material. The specular reflectance of silvered mirrors is unexcelled, and the hemispherical reflectance of a clean silver film is greater than 97% weighted over 250-2500 nm, the range of the solar spectrum.l Thus, silvered polymer films have been proposed and investigated for use in solar energy concentrationlconversion devices for both space2 and terrestial application^.^ Metallized polymeric films are fabricated most often in two stages. First, the polymeric film is prepared, and second, the metal is deposited onto the film surface by external processes including sputtering, thermal and electron beam induced metal vapor deposition, thermal and photochemical induced chemical vapor deposition, electrodeposition, or electroless chemical reduction from solution. Unfortunately, adhesion of the more passive metals such as copper, silver, and gold to the polymer is a common problem even with polymer surface modification (plasma, ion beam, and chemical treatments) prior to metal d e p o ~ t i t i o n . ~In - ~this paper we report the preparation of silvered polymeric films via a convenient and efficacious in situ, self-metallization pro+

College of William and Mary.

2 Lockheed Engineering and Sciences Co., Hampton, 5 NASA-Langley Research Center.

VA 23681.

Abstract published in Advance ACS Abstracts, October 1, 1995. (1) Jorgensen, G.; Schissel, P. In Metallized Plastics; Mittal, K. L., Susko, J. R., Eds., Plenum: New York, 1989, Vol. 2, pp 79-92. (2) Gulino, D. A,; Egger, R. A,;Bauholzer, W. F. Oxidation-Resistant Reflective Surfaces for Solar Dynamic Power Generation in Near Earth Orbit. N A S A Technical Memorandum 88865, 1986. (3) (a) Neidlinger, H. H.; Schissel, P. Soc. of Photo-Opt. Znstrum. Eng., Proc. 1987,823,181. (b) Schissel, P.; Goggin, R. M.; Shintion, Y. D. Ibid. 190. (4)Green, P. F.; Berger, L. L. Thin Solid Films 1993,224,209. (5) (a)Gerenser, L. J.; J. Vuc. Sci. Technol., A 1988,6,2897; 1990, 8,3682. (b) Gerenser, L. J.; Goppert-Berarducci, K. E.; Baetzold, R. C.; Pochan, J. M. J. Chem. Phys. 1991, 95, 4641. (6) Mittal, K. L. J . Vac. Sci. Technol. 1976,13,19.

0897-4756/95/2807-2171$09.00/0

cedure involving thermal-initiated reduction of polymersoluble silver(1)complexes to metallic silver. This single stage route to silvered polymeric reflectors has the potential to give improved adhesion at the metalpolymer interface as well as a highly reflecting surface over the visible and infrared regions of the electromagmetic spectrum. Polyimides have outstanding thermal oxidative and chemical ~ t a b i l i t y . ~Thus, - ~ we chose to investigate the fabrication of reflective silvered surfaces on the polyimide film derived from 3,3‘,4,4‘-benzophenonetetracarboxylic acid dianhydride and 4,4’-oxydianiline (BDTM 4,4’-ODA). Solutions of BTDA/4,4’-ODA in dimethylacetamide (DMAc) were doped with silver(1)acetate and 1,1,1,5,5,5-hexafluoro-2,4-pentanedione (hexafluoroacetylacetone or HFAH). Silver(1) acetate is insoluble in DMAc but readily dissolves upon the addition of HFAH with formation of the silver-hexafluoroacetylacetonate, [AgHFAl, coordination compound. A homogeneous single phase polymer-metal solution is essential for formation of a silver mirror. Thermal curing of the silver(1)-dopedresins leads to metallized films which are strikingly reflective. We report the characterization of these silvered films with respect to reflectivity, composition, thermal properties, and conductivity. Our silver(1) acetate-HFAH system represents an improvement in efficiency and simplicity with enhanced reflectivity relative to the (1,5-cyclooctadiene)(hexafluoroacetylacetonato)silver(I)-polyimide systems recently reported by Rubira et al.1° Metallization results using several additional soluble silver(1) additives in BTDM 4,4’-ODA are also reported. A preliminary account of a portion of this work has been reported.ll ~

~~

(7) Bower, G. M.; Frost, L. W. J . Polym Sci., A 1963,1, 3135. ( 8 ) Sroog, C. E.; Endrey, A. L.; Abramo, S. V.; Berr, C. E.; Edwards, W. M.; Olivier, K. L. J. Polym. Sci., A 1965,3,1373. (9) Dine-Hart, R. A,; Wright, W. W. J. Appl. Polym. Sci. 1967,11,

609. (10) (a) Rubira, A. F.; Rancourt, J. D.; Caplan, M. L.; St. Clair, A. K.; Taylor, L. T. Proc. Am. Chem. Soc., Diu. Polym. Mater.: Sci. Eng. 1994,71, 509; (b) Chem. Muter. 1994,6,2351.

0 1995 American Chemical Society

2172

Chem. Mater., Vol. 7, No. 11, 1995

Southward et al.

Experimental Section

Table 1. Reflectivity Data as a Function of Concentration for Silver AcetateK3exafluoroacetylacetone-Doped BTDA/4,4'-ODAFilmsa

Materials. 4,4'-ODA and "ultrapure" BTDA were obtained from Wakayama Seika Kogyo Co., Ltd. (via Kennedy and Klim, Inc.) and Alleo Chemical Corp., respectively. The 4,4'-ODA was used as received. BTDA was dried under vacuum at 150 "C for 5 h prior to use. The melting points of the monomers as determined by differential thermal analysis were 218 and 188 "C, respectively. DMAc (HPLC grade