Temperature-Controlled Synthesis of Porous CuO Particles with

Mar 13, 2017 - Xiao-Juan LeiXiang-Yang HouShu-Ni LiYu-Cheng JiangGuo-Xin SunMan-Cheng HuQuan-Guo Zhai. Inorganic Chemistry 2018 57 (22), ...
0 downloads 0 Views 3MB Size
Subscriber access provided by HACETTEPE UNIVERSITESI KUTUPHANESI

Article

Temperature-controlled synthesis of porous CuO particles with different morphologies for highly sensitive detection of triethylamine Ya-Pan Wu, Wei Zhou, Wen-Wen Dong, Jun Zhao, Xiu-Qing Qiao, Dong-Fang Hou, Dongsheng Li, Qichun Zhang, and Pingyun Feng Cryst. Growth Des., Just Accepted Manuscript • DOI: 10.1021/acs.cgd.7b00102 • Publication Date (Web): 13 Mar 2017 Downloaded from http://pubs.acs.org on March 14, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Crystal Growth & Design is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

Temperature-controlled synthesis of porous CuO particles with different morphologies for highly sensitive detection of triethylamine Ya-Pan Wu†, Wei Zhou†, Wen-Wen Dong†, Jun Zhao†, Xiu-Qing Qiao†, Dong-Fang Hou†, Dong-Sheng Li†,*, Qichun Zhang‡,* and Pingyun Feng§,* †

College of Materials and Chemical Engineering, Hubei Provincial Collaborative Innovation Center for New

Energy Microgrid, Key Laboratory of Inorganic Nonmetallic Crystalline and Energy Conversion Materials, China Three Gorges University, Yichang, Hubei,443002, China ‡

School of Materials Science and Engineering, Nanyang Technological University, Singapore 639798,

Singapore §

Department of Chemistry, University of California, Riverside, California, 92521, United States

KEYWORDS:

CuO,

morphology-controllable

synthesis,

MOFs

precursors,

thermal

decomposition, triethylamine, sensing ABSTRACT: Because porous metal oxides with controllable morphologies have been attracting much attention for their potential applications in the fields of adsorption/separation, sensing, energy storage, and conversion, it is highly desirable to prepare new morphology of metal oxides and investigate their performance. In this work, CuO particles with different shapes such as octahedron, sponge-like octahedron, and sphere have been synthesized through thermal decomposition of crystalline Cu(II)-organic frameworks (HKUST-1). The structure and morphology of as-prepared CuO particles have been fully characterized by the usage of XRD, XPS, SEM, and TEM. The gas-sensing behaviors of these CuO samples have been investigated and our results show that CuO-400 with spherical shape displays unprecedentedly high response

ACS Paragon Plus Environment

1

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 23

(maximum value, 102) for triethylamine (TEA) at 100 ppm with a low detection limit of 5ppm, a lower working temperature (230°C), excellent reproducibility, and long-term stability. The highly-sensing behavior of CuO-400 sphere might be due to its special structural factor with many open active sites for oxygen adsorption, which could react with TEA molecules more efficiently. Our results clearly suggest that porous CuO particles should be promising candidates for future practical application to detect TEA vapor at relatively low temperature. INTRODUCTION Triethylamine (TEA) not only has been considered as an important raw material for industrial organic synthesis, but also it has been widely used as preservatives, catalysts, synthetic dyes and energy fuels.1,2 Besides these, TEA can also generate from microbial degradation of triethylamine N-oxide during the deteriorating of dead fish and marine organisms. As such, TEA has been widely employed as one of effective indicators to assess the freshness of fish and seafood. Furthermore, TEA has also been known for a long time to irritate the eyes and skins, which further result in acute diseases such as pulmonary edema or even death.3-5 Due to its potential hazards to human body, the threshold limit of TEA concentration is 10ppm on volumetric basis decided by National Institute for Occupational Safety and Health (NIOSH).6 Although high efficiency methods such as colorimetric and chromatography have been used to detect TEA gas in environmental field, the complex process and expensive cost restrict their practical application on a large scale. Thus, developing new TEA sensing materials and techniques with low working-temperature, high sensitivity and low limit of detection, is still a major challenge. It is well-known that many metal oxide semiconductors sensors such as SnO2, TiO2 and their composites show response to TEA (Table S1). However, relatively high working temperature and

ACS Paragon Plus Environment

2

Page 3 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

lower sensitivity are required to be improved. Generally, the microstructures and morphologies of metal oxides are crucial factors for gas sensing selectivity, sensitivity and working temperature. Typically, CuO is a p-type semiconducting material (bandgap 1.2eV) and have many potential applications including magnetic storage media, solar cells, catalyst, gas sensor and supercapacitors.7-9 Many excellent methods have been established for the fabrication of CuO nanostructures with various morphologies including nano-sheet, nano-fibers, nano-spheres, nano-flowers, nano-flakes and nano-wires.7-10 Prior works have already reported that CuO nanostructures with different morphologies display efficient sensing behaviors to detect different types of toxic or combustible gases, including hydrogen sulfide, acetone, carbon monoxide, ethanol, ammonia, and so on (Table 1). However, no any exploration has been reported on pure CuO nano-materials for the detection of TEA, although only one case11 mentioned that CuO/ZnO hybrid nanorods could show a good response to TEA at 50ppm level under 40oC. Recently, MOFs (metal-organic frameworks) have been widely employed as important precursors to fabricate many different types of porous carbon/metal/ metal oxide nanostructures (M/MONs) via thermal decomposition under controlled atmospheres,12-16 because these asobtained materials have several important factors including different compositions, morphologies, and diverse structures, which make them desirable for potential applications in lithium-ion batteries, gas sensor, solar cells, hydrogen production, supercapacitors, super adsorbent material.17-20 For example, Lu et al.19 fabricated high purity porous Co3O4 concave nanocubes for the detection of ethanol through calcining ZIF-67 at a curtain temperature. Li et al16 obtained an unique hierarchical ZnO nanocages for the detection of acetone by direct temperature-programmed decomposition of MOF-5. On other hand, diverse Cu2O/CuO nanoparticles derived from Cu–MOFs have been observed15,

21

ACS Paragon Plus Environment

and the as-prepared materials

3

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 23

displayed some promising properties such as CO oxidation, lithium-ion batteries and sensing properties. Unfortunately, till now, a systematic study on the morphology control of these materials under calcination conditions is lacking. Such gap strongly motivates us to systematically investigate this type of materials. Here by controlling calcination conditions, octahedral, sponge-like or spherical CuO materials were readily obtained through thermal decomposition of octahedra Cu-MOF (HKUST-1). Remarkably, the as-synthesized CuO-400 sphere nanomaterial exhibits high sensitivity to TEA with a very low detection limit, a lower working temperature, high reproducibility, and steady stability. To the best of our knowledge, this is first CuO sensor derived from MOFs template, which shows high sensitivity to TEA. RESULTS AND DISCUSSION TGA measurements. The TGA was conducted to investigate the thermal stabilities and decide the calcination temperature for HKUST-1 materials. As shown in Figure 1b, a weight loss of 70% was observed before 370oC suggesting that large amounts of CO2 or H2O were released during the thermal decomposition process of MOFs. Three stages of mass loss can be seen in Figure 1b: one occurs at temperature below 320oC, which is attributed to the loss of physically absorbed H2O and DMF molecules. Selecting 300oC as calcining temperature for 5h, CuO-300 sample with octahedron shape can be obtained in this stage. The next stage for mass loss (about 40% weight loss) appears from 320 to 370oC. Employing 350oC as calcining temperature for 5h, the sponge-liked CuO-350 sample can be ready obtained. Since the weight loss in last stage (starting at 370oC) is not obvious, we tried different calcining temperatures such as 400, 450 and 500oC to complete the decomposition of HKUST-1 precursors. As shown in Figure 1a, if system temperature reaches or overpasses the decomposition temperature of HKUST-1, the guest

ACS Paragon Plus Environment

4

Page 5 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

molecules or organic ligands in HKUST-1 are released or burned away in air to generate CO2, H2O, or NOx, while Cu(II) ions will be converted into CuO with different morphology through reacting with O2.

Figure 1. (a) Schematic illustration of the formation of CuO products via the HKUST-1 template; (b) TGA curves of the HKUST-1 precursor.

Figure 2. (a) SEM images of HKUST-1 precursors; (b, c) SEM images of the as-prepared CuO-300; (d-f) SEM images of the as-prepared CuO-350; (g-i) SEM images of the as-prepared CuO-400.

ACS Paragon Plus Environment

5

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 23

Formation mechanism of CuO products. The morphologies of the as-obtained materials at various calcination temperatures are shown in Figure 1a, which are confirmed by SEM images (Figure 2 and Figure S1). According to TGA results, below 320 oC, different types of solvents in the pores almost have no effect on the decomposition temperature and the as-synthesized HKSUT-1 crystalline sample could maintain its framework at this stage, 22 which can explain why the octahedron CuO-300 has similar morphology to that of the precursor HKUST-1. During heating stage at 300 oC in air, some carbon formed to protect frameworks from the further contraction. Note that these carbons can be removed through oxidation to generate porous CuO materials during the annealing step. Such precise control of the shape, size, and chemical composition of nanocrystal structure not only allows to study their unique properties, but also is helpful to finely tune their physical and chemical properties.23 When the calcination temperature increased, the frameworks of HKUST-1 collapse to form sponge-like CuO materials (Figure 2d and Figure S1). Such formation might be owing to the existence of different facets and pose sizes of HKUST-1 as well as the faster releasing rates of decomposed gas composing stage I. Interestingly, when the calcination temperature reaches ~400oC, the morphology of CuO products evolved from sponge to sphere. Further gradually increasing temperature leads to the collapse of sphere CuO structure and form an irregular morphology. The SEM images of CuO450 and CuO-500 are shown in Figure S1g-Figure S1i. The general reaction process can be described through the following equation: [C18H6Cu3O12]n+O2→ CuO+ CO2↑+ H2O↑ Morphological and structural characteristics. Figure 2 shows the typical morphologies and microstructures of CuO particles derived from HKUST-1 precursors. The uniform HKUST-1 octahedron particles were synthesized at room temperature according to the reported

ACS Paragon Plus Environment

6

Page 7 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

procedure.24A subsequent thermal transformation process was introduced to convert Cu-MOFs into CuO particles with different shapes. Generally, the size of CuO-300 (4µm) is smaller than that of CuO-350 (12µm).The size of sphere CuO-400 is only 1µm as shown in Figure 2h. High-resolution TEM suggests that the lattice interplane distances of CuO-300 sample are −



0.267, 0.31, 0.255 and 0.215nm, which can be assigned to the ( 20 2 ) , (202), (11 2) and (111) interplane spacing of monoclinic crystal phase of CuO (Figure 3a). The selected electron diffraction (SAED) confirms that monocrystalline CuO particles have octahedra structure and the −

discrete diffraction cycles can be assigned to

( 20 2)

and (111) crystal planes of CuO (Figure 3d).

The selected area electronic diffraction and high-resolution TEM of other two CuO samples are shown in Figure 3b-3f. The phase composition and the purity of the as-prepared CuO samples have been characterized by powder X-ray diffraction (XRD). Figure S2 shows the XRD patterns of HKUST-1 crystallite while the diffraction peaks of the five as-synthesized CuO samples could be perfectly indexed as CuO (JCPDS card No.48-1548), which is not only in agreement with the above-mentioned assignments in SAED cycles, but also indicates their high purity(Figure 4).

ACS Paragon Plus Environment

7

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 23

Figure 3. (a, d) HRTEM image, lattice distance and SAED pattern of CuO-300; (b, e) HRTEM image, lattice distance and SAED pattern of CuO-350; (c, f) HRTEM image and lattice distance and SAED pattern of CuO400, respectively.

Figure 4. Powder X- ray diffraction patterns of the five porous CuO products prepared at different temperatures.

ACS Paragon Plus Environment

8

Page 9 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

Table 1 Gas sensing properties of various CuO nanostructures at different concentration of target gas.

morphologies

Gases

Concentrat ion

cloud-like

CO

400ppm

Working temperatur e(oC) 300

nanoparticles

NH3

100ppm

cages

ethanol

nanowires

sensitivity

response time/s

recovery time/s

Ref.

8

20

150

7

25

9.83

100

500

8

200ppm

150

6.6

-

-

21

H 2S

100ppb

180

0.237

2520

1200

26

nanowire

H 2S

100ppm

160

3

500

250

29

spheres

H 2S

1ppm

190

2

9

10

30

nanosheets

H 2S

1ppm

240

2.5

200

10

31

boat-like

HCN

50ppm

25

0.8

25

200

32

octahedra

20

10

80

sponge-liked

17

34

103

102

21

150

spheres

7.7

38

200

sheets

5.6

30

256

spheres

TEA

100ppm

230

this work

XPS was applied to identify the surface chemical compositions and element analysis of CuO400.25 In the survey area (0 – 1200 eV), elements C, O, and Cu are investigated to coexist in the same material (Figure 5a). The peaks at 933.9 eV (Cu2p3/2) and 953.6 eV(Cu2p1/2) are contributed from Cu. This result is higher than the peak positions for Cu (0) metal, which suggests that Cu has been oxidized (Figure 5b). The oxidation state of CuO can be further confirmed by two satellite peaks at 943.8 eV and 962.4 eV. Additionally, the C(1s) spectrum displays three peaks at 284.5, 285.5, and 288.2 eV in CuO sample, which can be assigned to C−C, C−O, and C=O, respectively (Figure 5c). Although CuO-300 and CuO-350 samples give the high peak intensities of C−O and C=O as shown in Figure S3 and Figure S4, these peak intensities in XPS spectra tremendously decrease with the increase of calcination temperature. All these results reveal that most of the oxygen-containing functional groups are successfully removed after calcination. Finally, The O1s peak at 530.5 eV matches the oxygen species in CuO

ACS Paragon Plus Environment

9

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 23

(Figure 5d). The O1s peaks at 531.4eV and 532.6eV can be identified as oxygen vacancy (OV) and adsorbed oxygen. Hence, the as-synthesized CuO products should be CuO compounds.26 N2 adsorption-desorption isothermal was used to evaluate surface factors of the as-prepared CuO particles (Figure 6). The as-measured surface areas of five CuO products (octahedral, sponge-like, spherical CuO, CuO-450, and CuO-500) are 6.644, 9.640, 20.912, 10.304, and 7.1889 m2/g, respectively. The BJH method has been used to determine pore size distributions from the desorption branch of the isotherm (Figure 6, the inset). The octahedral CuO-400 has two pore size distributions with the maximum peaks at 2nm and 20nm, which favors mass transportation. In addition, the maximum peak of pore size distributions for the sponge-liked CuO-350 is at 12nm, while the peak for the spherical CuO-400 is at 20nm. By comparison, CuO400 has a larger surface area than other samples, which may contribute positively to the sharp leap as gas sensors.

Figure 5. XPS spectra of as-obtained CuO-400 spheres: (a) survey, (b) Cu(2p) spectrum, (c) C

(1S)

spectrum,

(d) O1s spectrum.

ACS Paragon Plus Environment

10

Page 11 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

Figure 6. N2 adsorption-desorption isotherms and pore size distributions of the porous CuO products obtained at different calcinations temperatures.

The gas sensing properties of CuO products. CuO has been widely used in humidity-sensing,24 lithium-ion batteries,25,33 CO2 photoreduction,27 gas sensor (Table 1).26, 29-32 Key factors to be considered in optimizing the performance and utility of chemical sensors are response time, sensitivity, selectivity, reusability, and stability. In order to prove the possibility of CuO particles as gas sensors, different CuO samples abstained from different calcination temperature have been tested for comparison. It is well-known that the response of a chemiresistor-type gas sensor strongly depends on the working temperature.34 Thus, the responses to diverse gases (formaldehyde, acetone, ether, or triethylamine) at 200ppm as the function of temperature have been investigated to obtain the optimized operational temperature. As shown in Figure 7a, the responses of all sensors remarkably changed with the variation of the working temperature, and generally, higher working temperature gave poor responses. Taking CuO-300 as an example, the optimized operating temperatures for sensing formaldehyde, ether, acetone, and trimethylamine are 230, 240, 240, and 230, respectively. Although high temperature could lead to the short response/recovery time due to the higher diffusion and adsorbed rate of gas molecules as well as quick reactions between TEA vapor and oxygen adsorbed on the surface, the low concentration of the adsorbed O2 will result in the decreased responsivity. Thus, from Figure 7a, it is easy to

ACS Paragon Plus Environment

11

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 23

conclude that all responses of CuO-300 samples arise with the increasing temperature at the first stage and will approach its peak (about 20) at ~ 230oC. After passing this temperature, a little bit decrease can be seen, suggesting that there exists an optimized working temperature.

Figure 7. (a) Gas sensing responses of the CuO-300 products to 200 ppm of ether, formaldehyde, acetone, triethylamine at different temperatures. (b) Sensitivity reproducibility of the CuO-300 sample to 100ppm at 230 oC.

The response of other four CuO products was also investigated (Figure S4b-Figure S4i). Intriguingly, the CuO-400 sensor showed the maximum responsibility (102) at 230oC (Figure S4d), which might be attributed to the particles size, the special surface area, and the porosity of the as-prepared CuO-400 materials. These factors eventually have big effect on the adsorption, the diffusion, and the desorption of gas molecules, and finally affect the optimized working temperature as well as the oxygen state.35 Comparably, the response sensitivity of CuO-400 sensor is almost double comparing with that of TiO2/SnO2 nanosheets for sensing TEA under the same concentration, while, the working temperature for CuO-400 is lower than that of TiO2/SnO2 nanosheets.36 Based on the above considerations, we choose 230oC as our working temperature to compare the selectivity of different gas sensors at a concentration of 200ppm (Figure 8a). Surprisingly, the CuO-400 sensor possesses excellent selectivity to TEA in comparison to other tested gases, which strongly suggest that the mesoporous morphology of CuO-400 sample have

ACS Paragon Plus Environment

12

Page 13 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

great effect on their gas-sensing behaviors. To further study its stability, the as-prepared CuO300 sensor has been performed three successive sensing tests in 100ppm TEA. As is shown in Figure 8b, the original sensitivity and reproducibility of CuO-300 samples have been maintained without an obvious decrease.

Figure 8. (a) Concentration-dependent sensitivity three-dimensional graph of the porous CuO products obtained at 230oC. (b) Response−recovery curve of the CuO-300 sensor at 230 oC.

Figure 9. Response of the CuO-300 sensor to different concentration TEA at 230 oC. The inset presents a linear dependence of response on TEA concentration between 5 and 100 ppm.

Additionally, we systematically investigated the sensing performance of five CuO samples and commercially-available CuO particles. Compared with commercially-available CuO sample, the gas sensor performance of five CuO materials is much better than that of the commerciallyavailable one, not only in the responses to TEA, but also in the reproducibility and stability. In

ACS Paragon Plus Environment

13

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 23

order to further understand the relation between the concentration variation of TEA and the response ability of six CuO samples, dynamic responses at 230oC have been conducted. From Figure 9, one can easily find that the response is nearly close to the baseline level when the CuO300 sensor is exposed to air. However, when it is exposed to TEA vapor, the response reaches a maximum value, which suggests that CuO-300 sensor has an excellent response to TEA vapor. The evidence is that the resistances of the tested CuO samples increased when the analytic gases was reduced. As indicated in the inset curve, a monotonous responsiveness is suggested because the response increases with the increased concentration. Especially in a lower concentration (from 5 to 100 ppm, Figure 9), the relationship between the concentration and the responsibility is almost linear. The responsivity of other six CuO samples to different concentration of TEA at 230oC have also been conducted (Figure S5) and these results clearly suggests that these samples also can be served as sensors to detect TEA. Their sensitivity is five times better than that of pure brick-shaped SnO2 material under same concentration of TEA.37 The response-recovery feature of gas sensors is an essential parameter, which is determined by temperature-dependent reaction kinetics including the amount of the adsorbed gas and the reaction speed between O2 and gases.35 According to literature, the response-recovery time of one sensor to 100 ppm of gas is defined as the time that required to reach 90% of the final equilibrium value).35 As shown in Figure 10, although the response time is very rapid, the recovery time is relatively longer, which need to be further improved in the future. For the comparion with different CuO samples in triethylamine vapor (100ppm), the recovery times are 100, 103, 150, 200, 256, respectively (Table 1). As for the CuO-400, the fast response time might come from the loose surface as well as its uniform sphere structure, which is helpful to the mass transport and gas diffusion.

ACS Paragon Plus Environment

14

Page 15 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

Figure 10. Response/recovery times of CuO-400 sensor at 230oC.

Figure 11. Responses of CuO-400 sensor to 100 ppm TEA in different days.

Because the stability is another crucial property for a gas sensor, we conducted the explosion of CuO-400 samples to 100 ppm TEA atmosphere at 230oC for every 7 days. Strikingly, the gas response (during 30 days) shows a slight decrease from 102 to 86.4 (Figure 11), which indicates its long-term stability and excellent reproducibility. The sensing mechanism. As a typical p-type semiconducting oxide, the sensing mechanism of CuO has been explained in detail through the changes of its conductivity caused by the reaction between the detected gas and the surface-adsorbed oxygen.8, 10, 29,30,33This mechanism can also be applied in our system. As presented in Figure 12a, when the surfaces of p-type CuO mesospheres are exposed in air, O2 will be adsorbed on the surface of CuO gradually. Then, one electron in the conductive band of CuO will be captured by the adsorbed O2, which leads to the changes of O2 into O2- and O2- ionic species through electron transfer; at the same time, one hole will be produced in CuO samples, which results in the variation of the conductivity of CuO sensors.

ACS Paragon Plus Environment

15

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(a)

Page 16 of 23

(b)

Figure 12. (a, b) Schematic model for the CuO sensor exposed to air and TEA gas, respectively.

Similarly, when the surfaces of p-type CuO mesospheres is exposed in TEA vapor (Figure 12b), a virtual reaction occurs between O2- and TEA and some holes will be consumed, which results in the change of electrical conductivity of CuO samples; at the same time, the reaction products including N2, CO2, and H2O will be released into the air. Furthermore, more negativelycharged oxygen ions on the surface can result in the formation of hole accumulation layer (HAL), which further decrease the resistance of sensors.38 The overall reaction can be described with following equations: O2 (free state) → O2(adsorbed state) O2 (adsorbed state)→O2-(adsorbed ionic state)+h+ (h+ represents hole) O2-(adsorbed ionic state)→2O2- (final adsorbed ionic state)+3h+ N(C2H5)3+ O2-+ 2h+→ N2+H2O+CO2 Through the above process, one can conclude that the surface reactions play a key role to determine the gas-sensing process. Moreover, oxidation catalytic activity is also strongly determined by the morphologies of metal oxides. Obviously, larger surface area will provide the high sensitivity of metal oxides because these materials can provide large reaction-contacting

ACS Paragon Plus Environment

16

Page 17 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

area.37 Also, the sensitivity can be enhanced by the usage of particles with small mesosphere size. CONCLUSION A series of mesostructure CuO with different morphologies have been successfully synthesized through thermal decomposition of HKUST-1 at different temperatures. The asprepared particles have been innovatively applied as gas sensors. These materials exhibited high sensitivity and selectivity to TEA vapor, good reproducibility, and long-term stability as well as a low working temperature (~230°C). Note that the sensitivity strongly depends on the morphology of materials, proper pore distribution, and surface area. Our research clearly not only provides a promising method to prepare novel porous metal oxides with MOFs as templates, but also demonstrates that porous metal oxides can be acted as a potential platform to detect TEA vapor during industrial processes and fish-processing industries. ASSOCIATED CONTENT Supporting Information. The experimental section, table, PXRD curve, SEM images of the CuO, XPS spectra, response-recovery curve, linear dependence of response curves is available. AUTHOR INFORMATION Corresponding Authors * E-mail:[email protected](D.-S.Li) * E-mail: [email protected](Q.Zhang) * E-mail: [email protected].(P. Feng) Notes The authors declare no competing financial interest.

ACS Paragon Plus Environment

17

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 23

ACKNOWLEDGMENTS This work was financially supported by the NSF of China (Nos: 21373122, 21673127, 21671119, 51572152 and 51502155), the NSF of Hubei Province of China (No. 2014CFB277).

REFERENCES (1) Guo, J.; Zhang, J.; Zhu, M. High-performance gas sensor based on ZnO nanowires functionalized by Au nanoparticles. Sens. Actuators B. 2014, 199,339‒345. (2) Sun, X.; Liu, X.; Deng, X.; Xu, X. Synthesis of Zn-doped In2O3 nano sphere architectures as a triethylamine gas sensor and photocatalytic properties, RSC Adv., 2016, 6, 89847‒89854. (3) Chen, E. X.; Fu, H. R.; Lin, R.; Tan, Y. X.; Zhang, J. Highly selective and sensitive trimethylamine gas sensor based on cobalt imidazolate framework material. ACS Appl. Mater. Interfaces, 2014, 6, 22871‒22875. (4) Bai, S.; Tian, Y.; Sun, J.; Tong, Z.; Luo, R.; Li, D.; Chen, A. Heterostructures of polyaniline@SnO2 loading on flexible PET thin films for triethylamine detection at room temperature, New J. Chem., 2016,40, 4595‒4600. (5) Ju, D. X.; Xu, H.Y.; Qiu, Z. W. Near room-temperature, fast-response and highly sensitive triethylamine sensor assembled with Au-loaded ZnO/SnO2 core-shell nanorods on flat alumina substrates. ACS Appl. Mater. Interfaces, 2015, 7, 19163‒19171. (6) Sui, L.; Song, X.; Cheng, X.; Zhang, X.; Xu, Y.; Gao, S.; Wang, P.; Zhao, H.; Huo,L. An ultraselective and ultrasensitive TEA sensor based on α-MoO3 hierarchical nanostructures and the sensing mechanism, CrystEngComm. 2015, 17, 6493‒6503. (7) Aslanin, A.; Oroojpour, V. CO gas sensing of CuO nanostructures, synthesized by an assisted solvothermal wet chemical route, Physica B. 2011, 406, 144‒149.

ACS Paragon Plus Environment

18

Page 19 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

(8) Bedi, R. K.; Singh, I. Room-temperature ammonia sensor based on cationic surfactantassisted nanocrystalline CuO, Appl. Mater. Interfaces, 2010, 2, 1361‒1368. (9) Song, M. J.; Wang, Hwang, S. W.; Whang, D. Non-enzymatic electrochemical CuO nanoflowers sensor for hydrogen peroxide detection, Talanta. 2010, 80, 1648‒1652. (10) Zhang, F.; Zhu, A.; Luo, Y. P.; Tian,Y. CuO Nanosheets for sensitive and selective determination of H2S with high recovery ability, J. Phys. Chem. C, 2010, 114, 19214‒19219. (11) Xu, Q.; Ju, D.; Zhang, Z.; Yuan, S.; Zhang, J.; Xu, H.; Cao, B. Near room-temperature triethylamine sensor constructed with CuO/ZnO P-N heterostructural nanorods directly on flat electrode, Sens. Actuators B, 2016, 225,16‒23. (12) Harjyoti, T.; Ballav, M. B.; Gopal, D. ZnO nanoparticles from a metal-organic framework containing ZnII metallacycles, J. Inorg. Chem. 2007, 9,524‒529. (13) Yang, S. J.; Kim,T.; Im, J. H.; Kim, Y. S.; Lee, K.; Jung, H.; Park, C. R. MOF-derived hierarchically porous carbon with exceptional porosity and hydrogen storage capacity, Chem. Mater. 2012, 24,464‒470. (14) Zhang, L.; Wang, X.; Wang, R.; Hong, M. Structural evolution from metal–organic framework to hybrids of nitrogen-doped porous carbon and carbon nanotubes for enhanced oxygen reduction activity, Chem. Mater. 2015, 27 , 7610‒7618. (15) Song, Y. H.; Li, X.; Sun, L. L. Metal/metal oxide nanostructures derived from metal-organic frameworks, RSC Adv. 2015, 5, 7267‒7269. (16) Li, W. H.; Wu, X. F.; Han, N.; Chen, J. Y. MOF-derived hierarchical hollow ZnO nanocages with enhanced low-concentration VOCs gas-sensing performance. Sens. Actuators B. 2016, 225, 158‒166.

ACS Paragon Plus Environment

19

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 23

(17) Chen, S. R.; Xue, M. Y.; Li,Q. Rational design and synthesis of NixCo3-xO4 nanoparticles derived from multivariate MOF-74 for supercapacitors. J. Mater. Chem. A. 2015, 3, 20145‒20152. (18) Kathryn, E. K.; Wang, C.; Lin, W. B. Metal-organic framework templated synthesis of Fe2O3/TiO2 nano composite for Hydrogen Production, Adv. Mater., 2012, 24, 2014‒2018. (19) Lu, Y. Y.; Zhan, W. W.; He,Y.; Wang, Y. T. MOF-templated synthesis of porous Co3O4 concave nanocubes with high specific surface area and their gas sensing properties, Appl. Mater. Interfaces, 2014, 6, 4186‒4195. (20) Chen, E. X.; Yang, H.; Zhang, J. Zeolitic imidazolate framework as formaldehyde gas sensor, Inorg. Chem., 2014, 53, 5411‒5413. (21) Wang, Y.; Lü, Y. Y.; Zhan, W. W. Synthesis of porous Cu2O/CuO cages using Cu-based metal-organic-framework as templates and their gas-sensing properties. J. Mater. Chem. A. 2015, 3, 12796‒12803. (22) Martin, D.; Kim, J. H.; Mikhael, B.; Vallicari, C.; MOF-based membrane encapsulated ZnO nanowires for enhanced gas sensor selectivity. Appl. Mater. Interfaces, 2016, 8, 8323‒8328. (23) Kyung, M. C.; Jung, H. P.; Jeung, K. K. Nanocrystalline MOFs embedded in the crystals of other MOFs and their multifunctional performance for molecular encapsulation and energycarrier storage. Chem. Mater., 2015, 27, 5088‒5093. (24) Wang, Z. Y.; Xiao,Y.; Cui, X. B.; Lu, G. Y. Humidity-sensing properties of urchinlike CuO nanostructures modified by reduced graphene oxide, Appl. Mater. Interfaces, 2014, 6, 3888‒3895.

ACS Paragon Plus Environment

20

Page 21 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

(25) Liu, Y.; Wang, W.; Gu, L.; Wang, Y. W.; Ying, Y. L. Flexible CuO nanosheets/reducedgraphene oxide composite paper: binder-free anode for high performance lithium-ion batteries, Appl. Mater. Interfaces. 2013, 5, 9850‒9855. (26) Li, X. P.; Wang, Y.; Lei, Y.; Gu, Z. Y. Highly sensitive H2S sensor based on templatesynthesized CuO nanowires, RSC Adv. 2012, 2, 2302‒2307. (27) Wang, W. N.; Wu, F.; Myung,Y.; Dariusz, M. N. Surface engineered CuO nanowires with ZnO Islands for CO2, Appl. Mater. Interfaces, 2015, 7,5685-5692. (28)Barsan, N.; Koziej, D.; Weimar,U.; Metal oxide-based gas sensor research: How to? Sens. Actuators B., 2007, 121,18‒35. (29)Chen, J. J.; Wang,K.; Hartman, L.; Zhou, W. L. H2S detection by vertically aligned CuO nanowire array sensors, J. Phys. Chem. C. 2008, 112,16017‒16021. (30) Qin, Y.; Zhang, F.; Chen,Y.; Zhou, Y. J. Hierarchically porous CuO hollow spheres fabricated via a one-pot, J. Phys. Chem. C. 2012, 116, 11994‒12000. (31) Zhang, F.; Zhu, A. W.; Luo,Y. P.; Tian,Y.; Yang, J. H. CuO nanosheets for sensitive and selective determination of H2S with high recovery ability, J. Phys. Chem. C. 2010, 114, 19214‒19219. (32) Yang, M. Q.; He, J. H.; Hu, X. C. CuO nanostructures as quartz crystal microbalance sensing layers for detection of trace hydrogen cyanide gas, Environ. Sci. Technol., 2011, 45, 6088‒6094. (33) Wu, R. B.; Qian, X. K.; Feng, Y. MOF-templated formation of porous CuO hollow octahedra for lithium-ion battery anode materials, J. Mater. Chem. A, 2013, 1, 11126‒11129. (34) Zhu, G. X.; Xu,H.; Xiao, Y. Y. Facile fabrication and enhanced sensing properties of hierarchically porous CuO architectures, Appl. Mater. Interfaces., 2012, 4,744-751.

ACS Paragon Plus Environment

21

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 23

(35) Xu, H. Y.; Ju, J. D.; Li, W. R.; Cao, B. Q. Superior triethylamine-sensing properties based on TiO2/SnO2 n-nheterojunction nanosheets directly grown on ceramic tubes, Sens. Actuators B. 2016, 228, 634‒642. (36) Wang, C. X.; Yin, L. W.; Zhang, L. Y. Metal oxide gas sensors: Sensitivity and influencing factors, Sensors. 2010, 10, 2088‒2106. (37) Xie,Y. J.; Du ,J. P.; Zhao, R. H. Facile synthesis of hexagonal brick-shaped SnO2 and its gas sensing toward triethylamine, J. Environ. Chem. Eng. 2013, 1, 1380‒1384. (38) Liu, T.; Liu, J.; liu, Q.; Song, D.; Zhang, H.; Wang, J. Synthesis, characterization and enhanced gas sensing performance of porous ZnCo2O4 nano/microspheres, Nanoscale, 2015, 7, 19714‒19721.

ACS Paragon Plus Environment

22

Page 23 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

For Table of Contents Use Only Temperature-controlled synthesis of porous CuO particles with different morphologies for highly sensitive detection of triethylamine Ya-Pan Wu, Wei Zhou, Wen-Wen Dong, Jun Zhao, Xiu-Qing Qiao, Dong-Fang Hou, DongSheng Li, Qichun Zhang and Pingyun Feng

Mesoporous CuO materials with different controllable morphologies have been facilely obtained by thermal decomposition of Cu(II)–organic frameworks cystallline templates.The CuO-400 not only exhibits unprecedentedly high sensitivity(102) for triethylamine at 100ppm, a low detection limit (5ppm) as well as a lower working temperature of 230oC and also shows excellent reproducibility and long-term stability.

ACS Paragon Plus Environment

23