Letter

The Effect of Adjacent Materials on the Propagation of Phonon Polaritons in Hexagonal Boron Nitride Kris S Kim, Daniel Trajanoski, Kevin Ho, Leonid Gilburd, Aniket Maiti, Luuk van der Velden, Sissi de Beer, and Gilbert C Walker J. Phys. Chem. Lett., Just Accepted Manuscript • Publication Date (Web): 12 Jun 2017 Downloaded from http://pubs.acs.org on June 12, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

The Journal of Physical Chemistry Letters is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

The Effect of Adjacent Materials on the

1

2

Propagation of Phonon Polaritons in Hexagonal

3

Boron Nitride

4

Kris S. Kim1, Daniel Trajanoski1, Kevin Ho1, Leonid Gilburd1, Aniket Maiti1,2, Luuk van der

5

Velden1,3, Sissi de Beer1,3, Gilbert C. Walker1*

6 7

1

Department of Chemistry, University of Toronto, 80 St. George Street Toronto, Ontario M5S

8

3H6, Canada 2

9 10 11 12

3

Department of Physics, Indian Institution of Technology, Kanpur, 208016, India

Materials Science and Technology of Polymers, MESA+ Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500 AE Enschede, the Netherlands

*E-mail: [email protected]

13 14 15 16 17

1 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 25

18

ABSTRACT

19

In order to apply the ability of hexagonal boron nitride (hBN) to confine energy in the form of

20

hyperbolic phonon polariton (HPhP) modes in photonic-electronic devices, approaches to finely

21

control and leverage the sensitivity of these propagating waves must be investigated. Here, we

22

show that by surrounding hBN with materials of lower/higher dielectric responses, such as air

23

and silicon, lower/higher surface momenta of HPhPs can be achieved.

24

alternative method for preparing thin hBN crystals with minimum contamination is presented,

25

which provides opportunities to study the sensitivity of the damping mechanism of HPhPs on

26

adsorbed materials. Infrared scanning near field optical microscopy (IR-SNOM) results suggest

27

that the reflections at the upper and lower hBN interfaces are primary causes of the damping of

28

HPhPs and that the damping coefficients of propagating waves are highly sensitive to adjacent

29

layers, suggesting opportunities for sensor applications.

Furthermore, an

30

31

32

33

34

35 36 2 ACS Paragon Plus Environment

Page 3 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

37

The Journal of Physical Chemistry Letters

TOC GRAPHICS

38 39

KEYWORDS

40

2D materials, hBN, phonon-polaritons, SNOM, near-field

41 42 43 44 45 46 47 48 49 50 51 52

3 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 25

53

When electromagnetic waves are exposed to an interface, they can interact and couple with

54

elementary excitations at the surface of the underlying material. Among these coupled states are

55

surface plasmon polaritons (SPPs) and surface phonon polaritons (SPhPs), and the extent of each

56

coupling is dependent on the intrinsic degrees of freedom of the electrons and lattice vibrations of

57

the material, respectively1–3. In contrast to the widely studied SPPs, SPhPs occur when

58

electromagnetic waves couple with the lattice vibrations in polar dielectrics, between the

59

longitudinal and transverse optical (LO and TO) phonon frequencies, commonly known as the

60

Reststrahlen bands2,4,5.

61

momentum and field densities, but SPPs commonly rely on interactions in the visible to near-

62

infrared frequencies6–8 while SPhPs are found at infrared to terahertz frequencies4,9.

SPPs and SPhPs share similar properties, including high surface

63

Heterogeneous and anisotropic 2D materials, such as boron nitride, can exhibit different types

64

of vibrational coupling events within and between layers, opening opportunities to volume

65

confined photonic applications3,5,10. In particular, hexagonal boron nitride (hBN) has drawn

66

interest due its ability to strongly confine hyperbolic phonon-polariton (HPhP) modes within the

67

volume of the material.

68

hyperbolicity within the Reststrahlen bands2,5,11. Positive and negative (in- and out-of-plane)

69

principle components of the dielectric functions within these bands allows for this strong

70

confinement of HPhPs5,10,12. Additionally, HPhPs experience low optical losses, which arise

71

from the scattering of optical phonons that typically occur on the order of picoseconds4,10,13. Due

72

to these properties, hBN has been suggested for various applications, such as control of energy

73

transfer14, super-resolution imaging10, construction of superlenses15, and biosensors16–19.

While hBN is optically anisotropic, the material exhibits natural

74

Numerous reports have shown that HPhPs can be launched through different mechanisms. For

75

instance, studies15,20 have shown that metal-coated atomic force microscopy (AFM) probes can

76

launch HPhPs in hBN and form volumetric standing waves within the bulk of the material in the 4 ACS Paragon Plus Environment

Page 5 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

77

proximity of a reflective edge21. On the other hand, Li et al.10 showed that a gold overlayer edge

78

can serve as a platform to launch propagating HPhPs in thin sheets of hBN. Gilburd et al22

79

showed the launching of phonon polaritons in hBN using intrinsic folds of the crystal, and

80

Caldwell and coworkers5 showed that dots of hBN could admit phonon polaritons. In order to

81

exploit these mechanisms of launching and propagating HPhPs in small photonic-electronic

82

devices, approaches to finely controlling these waves must be considered. To address this

83

limitation and to better understand the subsequent dissipation of these waves as they propagate,

84

this paper examines the effect of adjacent materials on HPhP of hBN.

85

Several types of adjacent materials are probed in this work. Using near-field scattering optical

86

microscopy we compare the momenta of HPhP of hBN placed directly on silicon with the case of

87

an airgap between the materials. Because a common method of exfoliation of hBN leaves a

88

dispersive, oily layer on the crystal surface, we compare HPhP momenta on oil-covered hBN

89

versus those on clean hBN. Finally, we examine the effect of an IR-absorbing overlayer on hBN

90

to evaluate the possibility of detecting small amounts of infrared absorbing materials on hBN via

91

the HPhPs.

92

In order to implement a bottom-up strategy for fabricating photonic-electronic devices, which

93

utilize HPhPs of hBN, the first component to build such a device that must be considered is the

94

substrate.

95

scanning probe microscopy techniques to study these standing waves in boron nitride of different

96

structures, such as thin sheets15,20 and nanotubes3,23–25, with high spatial resolution. Silicon with a

97

thick oxide layer is commonly employed to prepare boron nitride for many of these studies15,20.

98

Dai et al.20 have previously reported the presence of HPhPs in hBN crystals prepared on silicon

99

dioxide and developed a method of obtaining the polariton wavelengths and corresponding

Previous studies have taken advantage of recent advances in near-field optical

5 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 25

100

momentum at a range of IR frequencies. Below is the analytical expression proposed to describe

101

the polariton dispersion relation for hBN crystals of thickness d [Eq. 1] for large momenta.

102





 +  = − arctan   =



 + arctan 





 + 

[Eq. 1]

∥  √!

103

where  +  is the complex momentum as a function of the wavenumber of the

104

incident IR light (ω), l represents the mode of a propagating wave, " , # , ∥ , and

105

!  are the dielectric functions of air, substrate, and hBN (in- and out-of-plane components),

106

respectively. As seen from the expression above, HPhPs are sensitive to the dielectric functions

107

of materials adjacent above and below an hBN crystal, represented as air (" ) and substrate (# ) in

108

this particular expression.

109

materials of differing dielectric properties.

Therefore, HPhPs can be controlled by surrounding hBN with

110

To investigate the effect of a substrate on HPhPs in hBN, thin crystals of hBN were deposited

111

on a silicon grating. Phase-controlled homodyne SNOM26–29 was used to inject and measure the

112

SPhPs in hBN microcrystals. A height and representative normalized out-of-phase near-field IR

113

response collected at an excitation frequency of 1560 cm-1 on a 250 nm thick hBN crystal is

114

shown in Fig.1. The observed patterns in the IR images are evanescent waves detected on the

115

surface of hBN from the volume-confined HPhPs. The standing waves which occur between the

116

metalized AFM probe and a reflective edge of an hBN crystal (schematic in Fig.1) have half the

117

HPhP wavelength, and thus satisfy the following relationship: $%&# =

118

hBN on a silicon grating, the effect of air and silicon as the underlying adjacent material on the

119

λobs can be studied (Fig.S1).

120

simulated and experimentally constructed by measuring the λobs values on top of hBN sitting on

$'()(+ 2. By preparing

Dispersion profiles for an air-hBN-air and air-hBN-Si were

6 ACS Paragon Plus Environment

Page 7 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

121

the alternating regions of the grating (see SI for more details). These results show that by

122

supporting hBN crystals on low (air) or high (silicon) dielectric response material, a lower/higher

123

HPhP surface momentum can be achieved. The experimental data collected from hBN on top of

124

silicon on the grating is fit with a simulated dispersion profile for a Si/SiO2 substrate (see SI).

125

Furthermore, the apparent intensity of HPhPs over the region where hBN is on top of air is higher

126

than the measured intensity of the phonon polaritons propagating in hBN over silicon across

127

various wavenumbers (see Fig.1C and Fig.S4). Previous reports10,15,30 have shown that metallic

128

edges, both above and below hBN, are capable of launching HPhPs. Here, silicon edges from the

129

grating can also launch HPhPs and stripe-like patterns can be seen in the IR images across

130

various wavenumbers (Fig.1C and Fig.S4) which closely resemble the pattern of the silicon

131

grating underneath hBN. The intense brightness over the region where hBN is on top of air can

132

also be attributed to the interference of phonon polaritons from the region over silicon,

133

illustrating a coupling of phonon polariton states over a region of air (150 nm above silicon).

134 135 136 137 138

7 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 25

139 140

Figure 1. (A) Side view schematic of air-hBN-Si system showing volumetric standing waves in

141

hBN which occur between an AFM probe and reflective edge. Top view images of (B) height

142

and (C) IR field magnitude (at 1560 cm-1) of a 250 nm thick hBN crystal on a silicon grating.

143

The HPhPs in hBN when the crystal is on top of silicon have higher momenta, as indicated by the

144

smaller λobs in (D), than those on top of air. (E) The experimentally constructed dispersion

145

profiles (open circles) of 250 nm thick hBN crystal in an air-hBN-air (red) and air-hBN-Si

146

(black) system closely agree with the simulated profiles.

147

Based on [Eq.1], HPhPs are not only sensitive to dielectric properties of the substrate

148

underneath hBN, but also the material adjacent on top of hBN. When preparing samples by a

149

widely-used tape exfoliation method31,32 (Fig.2A), we found that residue from dicing tape was

150

left behind on the substrate and on top of hBN. This residue was identified to consist of

151

dimethylsiloxane-type moieties through surface sensitive analytical techniques and was found to

152

be