Theoretical Investigations into Defected Graphene for Electrochemical

Oct 10, 2017 - Electrochemical reduction of CO2 coupled with a renewable energy source (such as wind or solar) is an emerging reaction of interest for...
0 downloads 10 Views 1MB Size
Subscriber access provided by UNIVERSITY OF ADELAIDE LIBRARIES

Article

Theoretical Investigations into Defected Graphene for electrochemical Reduction of CO2 Samira Siahrostami, Kun Jiang, Mohammadreza Karamad, Karen Chan, Haotian Wang, and Jens K. Norskov ACS Sustainable Chem. Eng., Just Accepted Manuscript • DOI: 10.1021/ acssuschemeng.7b03031 • Publication Date (Web): 10 Oct 2017 Downloaded from http://pubs.acs.org on October 12, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Sustainable Chemistry & Engineering is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 18

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Theoretical Investigations into Defected Graphene for electrochemical Reduction of CO2 Samira Siahrostami,[1]* Kun Jiang, [2] Mohammadreza Karamad,[1] Karen Chan, [3] Haotian Wang, [2] Jens Nørskov[1],[3] [1] SUNCAT Center for Interface Science and Catalysis, Department of Chemical Engineering, Stanford University, 443 Via Ortega, Stanford, California 94305, United States [2] Rowland Institute, Harvard University, Cambridge, MA 02142, United States [3] SUNCAT Center for Interface Science and Catalysis, SLAC National Accelerator Laboratory, 2575 Sand Hill Road, Menlo Park, California 94025, United States

* email: [email protected]

Abstract Despite numerous experimental efforts have been dedicated to studying carbonbased materials for electrochemical reduction of CO2, a rationalization of the associated trends in the intrinsic activity of different active motifs has so far been elusive. In the present work, we employ density functional theory calculations to examine a variety of different active sites in N-doped graphene, to give a comprehensive outline of the trends in activity. We find that adsorption energies of COOH* and CO* do not follow the linear scaling relationships observed for the pure transition metals, and this unique scaling is rationalized through differences in electronic structure between transition metals and defected graphene. This finding rationalizes most of the experimental observations on the carbon-based materials which present promising catalysts for the two-electron reduction of CO2 to CO. With this simple thermodynamic analysis, we identify several active sites that are expected to exhibit a comparable or even better activity to the state-of-the-art gold catalyst, and several configurations are suggested to be selective for CO2RR over HER.

1

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Key words: Density functional theory (DFT), Calculated limiting potential, hydrogen evolution reaction (HER), scaling relation, free energy diagram.

2

ACS Paragon Plus Environment

Page 2 of 18

Page 3 of 18

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Main text Global average carbon dioxide (CO2) concentration at the surface—the main driver of recent climate change—has reached 400 parts per million (ppm) for the first time in recorded history. In recent years, several strategies have been proposed to mitigate atmospheric CO2 concentration, including CO2 capture, storage, and conversion into valuable products. Among these, electrochemical conversion and reduction of CO2 coupled with a renewable energy source (such as wind or solar) has attracted much attention as an approach to generate carbon-neutral fuels or industrial chemicals. Many potential electrocatalysts have been suggested, including transition metals (e.g. Cu,1–4 Au, and Ag), transition metal oxides (e.g. RuO2, oxidederived copper)5–11, transition metal dichalcogenides (e.g. MoS2, MoSe2),12,13 metalfunctionalized porphyrin like structures14–17 and metal organic frameworks.18,19 Carbon-based materials are particularly interesting potential catalysts for the CO2 reduction reaction (CO2RR) due to their low cost and ability to form a wide range of nanostructures. 20,21,22–24 They are chemically inactive at negative potential ranges and present high overpotentials for the hydrogen evolution reaction compared to metal surfaces.25 Pristine graphene does not exhibit any activity. However, introducing dopants20,26,27 and defects28 during the synthesis tailors the electronic structure and catalytic properties of nanostructured carbon materials.28 N-doping has been shown to significantly enhance the CO2 reduction activity.29–33 Different types of naturally occurred defects can also modulate the catalytic activity.28,34,35 It is interesting to note that there is an interplay between N-doping and the number of generated defects.36 N-doping is energetically more favorable near the defects especially around the pentagons and represents the important role of defect-induced strain in the stability of the N-dopant.36 Figure 1 displays the performance of several carbon-based materials that have been tested and reported for the electrochemical reduction of CO2.29,30,37–41 The reported overpotentials and Faradic efficiencies in Figure 1a correspond to the maximum collected CO in each report. The partial current densities at the same potential are displayed in Figure 1b. We also report an in-house made N-doped reduced graphene oxide (N-rGO) as a representative CO2RR catalyst (details are in 3

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 18

Supplementary Information (SI)). Among them, nitrogen-doped carbon nanotubes (NCNT) have shown great promise in the electrochemical reduction of CO2 to CO at very low overpotentials.29–33 Apart from CO, other products such as acetate41, methane30 and formic acid38,42 have also been reported on different N-doped carbon-based materials.

Entry

Catalyst

1 2 3

N-doped Ketjenblack Carbon N-doped carbon nanotubes N-doped carbon nanotubes S,N-doped polymer-derived carbon N-doped reduced graphene oxide (N-rGO) ~20-40nm Ag nanoparticles ~800 nm Au powders ~8 nm Au nanoparticle

4 5 6 7 8

Aqueous Electrolyte 0.1 M KHCO3 0.1 M KHCO3 0.1 M KHCO3

References [16] [33] [29]

0.1 M KHCO3

[30]

0.1 M KHCO3

This work

0.1 M KHCO3 0.1 M KHCO3 0.5 M KHCO3

[33] [33] [43]

Figure 1. Performance map for CO2RR over reported N-doped carbon-based materials as well as N-doped reduced graphene oxide (N-rGO) studied in this work (experimental details are in the Supporting Information). Au and Ag are reported for comparison. Representative CO (a) Faradaic efficiencies, (b) current density and their corresponding overpotentials are plotted for each reported catalyst. Data for the plots are listed in the Supporting Information Table S1.

The aforementioned experimental reports show that different carbon catalysts present diverse activities and in most cases the major product of the CO2

4

ACS Paragon Plus Environment

Page 5 of 18

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

reduction is found to be CO. The interplay between N-doping and naturally occurred defects generates a wide range of possible active motifs, contributing to the overall performance of the material. Different types of N-doping can be formed including pyridinic, pyrrolic and graphitic nitrogen. N-doping in different types of defects provides a wide range of diverse graphitic nitrogen with different activities.35 Through a simple thermochemical analysis, Wu et al have suggested pyridinic-N to have the highest activity for the reduction of CO2 to CO.33 In this work, we examine the activity of a wide range of different possible active sites in the carbon-based materials with and without N-doping in pristine and defective carbon structures for the electrochemical reduction of CO2. We use density functional theory calculations (DFT) in conjunction with the computational hydrogen electrode (CHE)44 model to determine the adsorption energies of key intermediates of CO2 reduction reaction, in order to get the trends in activity and draw comparisons with currently known carbon-based materials (details are in the Supporting Information). The CHE model exploits that the chemical potential of a proton-electron pair is equal to that of gasphase H2, at Uelec = 0.0 V vs. the reversible hydrogen electrode (RHE).44 The maximum potential allowed by thermodynamics is obtained by shifting the chemical potential of the electrons at the equilibrium potential of U= -0.12 V. This allows to obtain the theoretical overpotential, which is defined as the maximum difference between each successive step at the equilibrium potential. The potential at which the electrochemical reaction takes place is called limiting potential, which can be obtained by the difference between the equilibrium potential and overpotential. At the limiting potential, all the reaction steps are downhill in free energy.

Results and discussion Taking into account the two-dimensional graphene sheets as a model system, we introduce different types of defects as depicted in Fig. 1a, including, mono vacancies (MV) as well as several double vacancies (DV), such as 555-777, 555-6777 and Stone Wales 55-77. We also consider two different line defects including 558 and 555-777. Here the 5, 6, 7 and 8 refer to the pentagon, hexagon, heptagon and octagon, respectively in the defect configuration. Further details on the relative 5

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 18

stability of different modeled defect configurations are provided in Table S2 in Supporting Information. Our calculations indicate that MV is too reactive to contribute to the CO2 reduction catalysis, while some of the DVs can catalyze CO2RR. Using DFT calculations and computational hydrogen electrode approach (SI) the CO2 reduction reaction mechanism has been explored and reported on transition metal surfaces.45 A simple thermochemical analysis shows the pathway for CO2 reduction to CO to go through COOH* and CO* intermediates,

CO2+ * + (H++ e−) → COOH*

(1)

COOH* + (H++ e−) → CO*+ H2O

(2)

CO* → CO + *

(3)

Total: CO2+ 2(H++ e−) → CO+ H2O

E0 = -0.12 V

(4)

If the surface adsorbs CO weakly, the CO molecule readily desorbs from the surface and the major product will be CO gas. Au and Ag, for example, bind CO weakly and are selective for the two-electron reduction of CO2 to CO.

45

On the other hand, for

the transition metal surfaces that bind CO, further reduced products past CO may be produced, where the activity has been suggested to be limited by the reduction of CO* to CHO*. 1 Figure 2b displays the calculated chemisorption energies of COOH* vs. CO* on the studied active motifs as well as transition metals (111) surfaces. As it can be seen, there is a linear scaling relation between COOH* and CO* adsorption energies in the case of transition metals.45 The orange dashed line shows the chemical potential of CO in the gas phase, separating the region that CO can be bound to the surface and therefore gets further reduced from no adsorption regime. Copper is in the border and weakly binds CO while gold and silver are in the no adsorption regime. We note that most of the examined active sites do not fall on the known scaling line for the transition metals because they do not bind CO. This is the reason that carbon-based materials represent especially interesting alternatives for the two-electron reduction of CO2 to CO.

6

ACS Paragon Plus Environment

Page 7 of 18

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

For the examined active sites in Figure 2a with positive CO* binding energy, the activity towards CO production can be determined exclusively by the COOH* binding strength. An optimal COOH* binding strength, not too weak and not too strong, is desirable in line with the Sabatier principle (Figure 2c). The equilibrium potential for two-electron reduction of CO2 to CO (Eq. 4) is -0.12 V vs. RHE. Using thermodynamic considerations alone, the ideal catalyst should have a COOH* binding energy of 0.12 eV at zero applied potential. The horizontal red line in Figure 2b displays the adsorption energy of the ideal catalyst that effectively catalyzes the two-electron reduction of CO2 to CO. The vertical distance between this line and each point in the graph can be used as a metric for activity. Interestingly many of the examined active sites show higher activity than Au for the two-electron reduction of CO2 to CO. This information can be translated this into a thermodynamic activity volcano (Figure 2c) with COOH binding energy as descriptor and a free energy diagram at the equilibrium potential of -0.12 V vs. RHE (Figure 2d). These plots suggest that the COOH* formation is rather difficult and is the bottleneck step for CO production on Pyrrolic-N (Figure2a (15)) and N-doped at pristine graphene (Figure 2a (1)). Therefore, the overall CO2 reduction activity is severely limited by formation of COOH*. Pyridinic-N (14), on the other hand, has a surmountable *COOH formation energy at relatively low overpotentials and CO desorption is facile. This has been previously reported by Wu et al.33, who assigned the CO2 reduction activity on N-doped carbon nanotube to the pyridinic-N based on a similar thermodynamic analysis. Figure 2b and 2c show that several defects with and without N-doped are as active as pyridinic-N for the CO2RR. For example, the 558-line defect (Figure2a (12)) and N-doped in the 555-6-777 (Figure2a (7)) defective structure show comparable activity to the pyridinic-N. Moreover, there are a number of other sites, such as N-doped 55-77 (Figure2a (5)), 555-6-777 (Figure2a (6)), N-doped 558-line defect (Figure2a (13)) and 555-777 defect (Figure2a (2)), that exhibit lower activity than pyridinic-N, but represent activities close to or higher than Au and Ag. The difference in scaling behavior between transition metals and defective graphene can be rationalized through their differences in electronic structure. CO 7

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 18

binds to transition metals through the interplay between attractive π* and repulsive σ interactions with the metal d-states 46. Pristine graphene is a semiconductor with no states at the Fermi level (Figure 2e)

47

, which does not provide attractive

interactions with CO. Intense electron localization, however, is present around Ndopants and defects in graphene (Figure 2e) 47. Such sites introduce the possibility for covalent bonds to COOH, which is a radical, but not CO, which has a closed shell configuration. This bonding picture is similar to that suggested for transition metal dichalcogenide edges

48,

and p-block dopants in metals

49,

both of which show

similar deviations from transition metal scaling relations.

(a)

(1) Pristine

(2) 555-777

(3) N-555-777

(4) 55-77

(5) N-55-77

(6) 555-6-777

(7) N-555-6-777

(8) MV

(9) 555-777 LD

(10) N-555-777 LD

(11) N-555-777 LD

(12) 558 LD

(13) N-558 LD

(14) Pyridinc-N

(15) Pyrrolic-N

8

ACS Paragon Plus Environment

Page 9 of 18

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(b)

(c)

(d)

(e)

Figure 2. (a) The optimized structures of different examined carbon structures with and without N-doped, where LD stands for line defect. Here the 5, 6, 7 and 8 refer to the pentagon, hexagon, heptagon and octagon in the defect configuration. Color code; C: gray, N: blue. (b) Calculated chemisorption energies of COOH* vs. CO* intermediates for examined carbon-based materials. Numbers refer to the structures shown in (a). Transition metals (111) are depicted in black, adapted from Ref. [45] for comparison. Energies for CO* are relative to gas-phase CO and H2, and for COOH* are relative to gas-phase CO2 and H2. The vertical dashed line corresponds to the chemical potential of CO in the gas phase. (c) the activity volcano for two-electron reduction of CO2 to CO. (d) The free energy diagram of CO2 to CO conversion on different examined active sites displayed in (a) at equilibrium potential of –0.12 V vs. RHE. (e) The p-projected density of states for pure graphene and N-doped defective carbon labeled as number (5) in (a) as an example.

HER analysis In general the carbon-based materials represent high overpotentials for hydrogen evolution reaction (HER) compared to metal surfaces.25 Herein, we analyze the competition between HER and CO2RR using the thermodynamic limiting potentials UL. It was shown that the difference between the thermodynamic limiting potentials for CO2RR and HER, UL(CO2) - UL(H2), follows trends in selectivity on transition

9

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

metals, and the magnitude of this difference for the metals is less than 0.5 V on the metals that reduce CO2 with significant Faradaic efficiency (FE)45. For metals binding CO* weaker than Cu, UL(CO2) is determined by the COOH* formation from CO2. For Cu and metals binding CO* stronger than Cu, protonation of CO* to CHO* determines the limiting potential. Assuming that the corresponding electrochemical barriers scale similarly in both carbon based and transition metal catalysts, we can apply the same analysis in the present work to obtain an estimate of the selectivity. This analysis does not apply for the catalysts with strong CO* binding energy, where the CO desorption process is slow and the Faradaic efficiency is negligible. Figure 3a and 3b display the UL(CO2), UL(H2) and (UL(CO2) - UL(H2)) for the configurations shown in the free energy diagram (Figure 2d) with respect to gold. The more positive UL(CO2) - UL(H2) corresponds to higher selectivity toward CO2 reduction. This analysis therefore suggests that of the configurations with surmountable COOH* formation energies shown in the Figure 2(d) configurations (7), (12) and (14) should be selective for CO2RR over HER. Pyridinic-N (configuration (14) has the most positive UL(CO2) - UL(H2) and therefore is suggested to be the most selective site for the CO2RR over HER.

10

ACS Paragon Plus Environment

Page 10 of 18

Page 11 of 18

1

2

7

12

14

15

Au

15

Au

0

(a)

-0.3

UL (V)

-0.6 -0.9 -1.2 -1.5 -1.8

U L(CO2) UL(CO2)

UL(H2) UL(H2)

-2.1

(b)

1

2

7

12

14

0.4 0.2

UL(CO2) ⎯UL(H2) (V)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

0 -0.2 -0.4 -0.6 -0.8 -1 -1.2

Figure 3. (a) The calculated limiting potentials for HER and CO2RR and (b) the calculated UL(CO2) - UL(H2) on the active sites studied in Figure (2d) compare to Au(111).

Conclusion In summary, we have studied a diverse range of possible active sites in N-doped carbon-based materials and showed that the calculated adsorption energies do not follow the scaling relations established for transition metal surfaces. This difference in scaling is rationalized by the presence of electron localization in the defected sites of graphene which binds COOH but not CO. This unique scaling rationalizes the numerous experimental reports of low overpotentials for CO2 reduction to CO on carbon based materials. We used the calculated COOH* adsorption energy as an activity metric to map out the trends in activity of different active site motifs. COOH*

11

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

adsorption energies vary significantly depending on the type of active site, allowing for a wide range of possible activities. Based on this simple thermodynamic picture, several configurations are suggested to be selective for CO2RR over HER, and Pyridinic-N is suggested to be the most selective site for the CO2RR over HER. Future work will investigate activation energies and kinetics in order to fully evaluate the efficiency and selectivity of candidate active site motifs.

Computational Details Density functional theory calculations for the carbon based were performed using the QUANTUM ESPRESSO program package

50

and the Atomic Simulation

Environment (ASE).51 The electronic wavefunctions were expanded in plane waves up to a cutoff energy of 500 eV, while the electron density was represented on a grid with an energy cutoff of 5000 eV. Core electrons are approximated with ultrasoft pseudopotentials.52 We use the BEEF-vdW exchange-correlation functional,53 which has been shown to accurately describe chemisorption as well as physisorption properties on graphene. For adsorption studies, a supercell of lateral size of (4x4) for non-defective and (8x8) for defective structures are used and a vacuum region of at least 18 Å is used to decouple the periodic images. The first Brillouin zones are sampled with (4x4x1) and (2x2x1) Monkhorst-Pack54 k-points for the (4x4) and (8x8) supercells, respectively. All the atoms were allowed to relax until the maximum force on each atom was below 0.05 eV/A for each calculation.

Acknowledgement This material is based upon work performed by the Joint Center for Artificial Photosynthesis, a DOE Energy Innovation Hub, as follows: Density functional theory calculations was supported through the Office of Science of the U.S. Department of Energy under Award No. DE-SC0004993.

Analysis of experimental data was

supported by the Rowland Junior Fellows Program at Rowland Institute, Harvard University.

Reference: 12

ACS Paragon Plus Environment

Page 12 of 18

Page 13 of 18

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(1)

Peterson, A. A.; Abild-Pedersen, F.; Studt, F.; Rossmeisl, J.; Nørskov, J. K. How Copper Catalyzes the Electroreduction of Carbon Dioxide into Hydrocarbon Fuels. Energy Environ. Sci. 2010, 3 (9), 1311.

(2)

Schouten, K. J. P.; Kwon, Y.; van der Ham, C. J. M.; Qin, Z.; Koper, M. T. M. A New Mechanism for the Selectivity to C1 and C2 Species in the Electrochemical Reduction of Carbon Dioxide on Copper Electrodes. Chem. Sci. 2011, 2 (10), 1902.

(3)

Manthiram, K.; Beberwyck, B. J.; Alivisatos, A. P. Enhanced Electrochemical Methanation of Carbon Dioxide with a Dispersible Nanoscale Copper Catalyst. J. Am. Chem. Soc. 2014, 136 (38), 13319–13325.

(4)

Kuhl, K. P.; Cave, E. R.; Abram, D. N.; Jaramillo, T. F. New Insights into the Electrochemical Reduction of Carbon Dioxide on Metallic Copper Surfaces. Energy Environ. Sci. 2012, 5, 7050.

(5)

Karamad, M.; Hansen, H. A.; Rossmeisl, J.; Nørskov, J. K. Mechanistic Pathway in the Electrochemical Reduction of CO 2 on RuO 2. ACS Catal. 2015, 5 (7), 4075–4081.

(6)

Kas, R.; Kortlever, R.; Milbrat, A.; Koper, M. T. M.; Mul, G.; Baltrusaitis, J.; D’Alessandro, D. M.; Smit, B.; Long, J. R.; Ritter, S. K.; et al. Electrochemical CO2 Reduction on Cu2O-Derived Copper Nanoparticles: Controlling the Catalytic Selectivity of Hydrocarbons. Phys. Chem. Chem. Phys. 2014, 16 (24), 12194.

(7)

Le, M.; Ren, M.; Zhang, Z.; Sprunger, P. T.; Kurtz, R. L.; Flake, J. C. Electrochemical Reduction of CO2 to CH3OH at Copper Oxide Surfaces. J. Electrochem. Soc. 2011, 158 (5), E45.

(8)

Frese, K. W. Electrochemical Reduction of C02 at Intentionally Oxidized Copper Electrodes. 1991, 138 (11), 3338–3344.

(9)

Liu, L.-M.; Zhang, C.; Thornton, G.; Michaelides, A. Structure and Dynamics of Liquid Water on Rutile TiO_{2}(110). Phys. Rev. B 2010, 82 (16), 161415.

(10) Sen, S.; Liu, D.; Palmore, G. T. R. Electrochemical Reduction of CO 2 at Copper Nanofoams. ACS Catal. 2014, 3091–3095. (11) Chang, T. Y.; Liang, R. M.; Wu, P. W.; Chen, J. Y.; Hsieh, Y. C. Electrochemical Reduction of CO2 by Cu2O-Catalyzed Carbon Clothes. Mater. Lett. 2009, 63 (12), 1001–1003. (12) Asadi, M.; Kumar, B.; Behranginia, A.; Rosen, B. A.; Baskin, A.; Repnin, N.; Pisasale, D.; Phillips, P.; Zhu, W.; Haasch, R.; et al. Robust Carbon Dioxide Reduction on Molybdenum Disulphide Edges. Nat. Commun. 2014, 5, 4470. (13) Asadi, M.; Kim, K.; Liu, C.; Addepalli, A. V.; Abbasi, P.; Yasaei, P.; Phillips, P.; Behranginia, A.; Cerrato, J. M.; Haasch, R.; et al. Nanostructured Transition Metal Dichalcogenide Electrocatalysts for CO2 Reduction in Ionic Liquid. Science 2016, 353 (6298), 467–470. (14) Tripkovic, V.; Vanin, M.; Karamad, M.; Björketun, M. E.; Jacobsen, K. W.; Thygesen, K. S.; Rossmeisl, J. Electrochemical CO 2 and CO Reduction on

13

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Metal-Functionalized Porphyrin-like Graphene. J. Phys. Chem. C 2013, 117 (18), 9187–9195. (15) Shen, J.; Kortlever, R.; Kas, R.; Birdja, Y. Y.; Diaz-Morales, O.; Kwon, Y.; Ledezma-Yanez, I.; Schouten, K. J. P.; Mul, G.; Koper, M. T. M. Electrocatalytic Reduction of Carbon Dioxide to Carbon Monoxide and Methane at an Immobilized Cobalt Protoporphyrin. Nat. Commun. 2015, 6, 8177. (16) Varela, A. S.; Ranjbar Sahraie, N.; Steinberg, J.; Ju, W.; Oh, H.-S.; Strasser, P. Metal-Doped Nitrogenated Carbon as an Efficient Catalyst for Direct CO 2 Electroreduction to CO and Hydrocarbons. Angew. Chemie 2015, 127 (37), 10908–10912. (17) Cheng, M.-J.; Kwon, Y.; Head-Gordon, M.; Bell, A. T. Tailoring Metal-PorphyrinLike Active Sites on Graphene to Improve the Efficiency and Selectivity of Electrochemical CO 2 Reduction. J. Phys. Chem. C 2015, 119 (37), 21345– 21352. (18) Lin, S.; Diercks, C. S.; Zhang, Y.-B.; Kornienko, N.; Nichols, E. M.; Zhao, Y.; Paris, A. R.; Kim, D.; Yang, P.; Yaghi, O. M.; et al. Covalent Organic Frameworks Comprising Cobalt Porphyrins for Catalytic CO₂ Reduction in Water. Science 2015, 349 (6253), 1208–1213. (19) Hod, I.; Sampson, M. D.; Deria, P.; Kubiak, C. P.; Farha, O. K.; Hupp, J. T. FePorphyrin-Based Metal–Organic Framework Films as High-Surface Concentration, Heterogeneous Catalysts for Electrochemical Reduction of CO2. 2015. (20) Dai, L. Functionalization of Graphene for Efficient Energy Conversion and Storage. Acc. Chem. Res. 2013, 46 (1), 31–42. (21) Wang, H.; Yuan, X.; Zeng, G.; Wu, Y.; Liu, Y.; Jiang, Q.; Gu, S. Three Dimensional Graphene Based Materials: Synthesis and Applications from Energy Storage and Conversion to Electrochemical Sensor and Environmental Remediation. Adv. Colloid Interface Sci. 2015, 221, 41–59. (22) Sun, Y.; Wu, Q.; Shi, G. Graphene Based New Energy Materials. Energy Environ. Sci. 2011, 4 (4), 1113. (23) Brownson, D. A. C.; Kampouris, D. K.; Banks, C. E. An Overview of Graphene in Energy Production and Storage Applications. J. Power Sources 2011, 196 (11), 4873–4885. (24) Pumera, M. Graphene-Based Nanomaterials for Energy Storage. Energy Environ. Sci. 2011, 4 (3), 668–674. (25) Yang, N.; Waldvogel, S. R.; Jiang, X. Electrochemistry of Carbon Dioxide on Carbon Electrodes. ACS Appl. Mater. Interfaces 2016, acsami.5b09825. (26) Liu, J.; Song, P.; Ning, Z.; Xu, W. Recent Advances in Heteroatom-Doped MetalFree Electrocatalysts for Highly Efficient Oxygen Reduction Reaction. Electrocatalysis 2015, 6 (2), 132–147. (27) Wong, W. Y.; Daud, W. R. W.; Mohamad, A. B.; Kadhum, A. A. H.; Loh, K. S.;

14

ACS Paragon Plus Environment

Page 14 of 18

Page 15 of 18

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Majlan, E. H. Recent Progress in Nitrogen-Doped Carbon and Its Composites as Electrocatalysts for Fuel Cell Applications. Int. J. Hydrogen Energy 2013, 38 (22), 9370–9386. (28) Terrones, H.; Lv, R.; Terrones, M.; Dresselhaus, M. S. The Role of Defects and Doping in 2D Graphene Sheets and 1D Nanoribbons. Rep. Prog. Phys. 2012, 75 (6), 62501. (29) Sharma, P. P.; Wu, J.; Yadav, R. M.; Liu, M.; Wright, C. J.; Tiwary, C. S.; Yakobson, B. I.; Lou, J.; Ajayan, P. M.; Zhou, X.-D. Nitrogen-Doped Carbon Nanotube Arrays for High-Efficiency Electrochemical Reduction of CO2 : On the Understanding of Defects, Defect Density, and Selectivity. Angew. Chem. Int. Ed. Engl. 2015, 54 (46), 13701–13705. (30) Li, W.; Seredych, M.; Rodríguez-Castellón, E.; Bandosz, T. J. Metal-Free Nanoporous Carbon as a Catalyst for Electrochemical Reduction of CO2 to CO and CH4. ChemSusChem 2016, 9 (6), 606–616. (31) Chai, G.-L.; Guo, Z.-X. Highly Effective Sites and Selectivity of Nitrogen-Doped graphene/CNT Catalysts for CO 2 Electrochemical Reduction. Chem. Sci. 2016, 7 (2), 1268–1275. (32) Liu, Y.; Chen, S.; Quan, X.; Yu, H. Efficient Electrochemical Reduction of Carbon Dioxide to Acetate on Nitrogen-Doped Nanodiamond. J. Am. Chem. Soc. 2015, 137 (36), 11631–11636. (33) Wu, J.; Yadav, R. M.; Liu, M.; Sharma, P. P.; Tiwary, C. S.; Ma, L.; Zou, X.; Zhou, X.-D.; Yakobson, B. I.; Lou, J.; et al. Achieving Highly Efficient, Selective, and Stable CO2 Reduction on Nitrogen-Doped Carbon Nanotubes. ACS Nano 2015, 9 (5), 5364–5371. (34) Jiang, Y.; Yang, L.; Sun, T.; Zhao, J.; Lyu, Z.; Zhuo, O.; Wang, X.; Wu, Q.; Ma, J.; Hu, Z. Significant Contribution of Intrinsic Carbon Defects to Oxygen Reduction Activity. ACS Catal. 2015, 5 (11), 6707–6712. (35) To, J. W. F.; Ng, J. W. D.; Siahrostami, S.; Koh, A. L.; Lee, Y.; Chen, Z.; Fong, K. D.; Chen, S.; He, J.; Bae, W.-G.; et al. High-Performance Oxygen Reduction and Evolution Carbon Catalysis: From Mechanistic Studies to Device Integration. Nano Res. 2016, 1–15. (36) Hou, Z.; Wang, X.; Ikeda, T.; Terakura, K.; Oshima, M.; Kakimoto, M.; Miyata, S. Interplay between Nitrogen Dopants and Native Point Defects in Graphene. Phys. Rev. B 2012, 85 (16), 165439. (37) Jhong, H.-R. M.; Tornow, C. E.; Smid, B.; Gewirth, A. A.; Lyth, S. M.; Kenis, P. J. A. A Nitrogen-Doped Carbon Catalyst for Electrochemical CO 2 Conversion to CO with High Selectivity and Current Density. ChemSusChem 2017, 10 (6), 1094– 1099. (38) Zhang, S.; Kang, P.; Ubnoske, S.; Brennaman, M. K.; Song, N.; House, R. L.; Glass, J. T.; Meyer, T. J. Polyethylenimine-Enhanced Electrocatalytic Reduction of CO 2 to Formate at Nitrogen-Doped Carbon Nanomaterials. J. Am. Chem. Soc. 2014, 136 (22), 7845–7848. 15

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(39) Wu, J.; Yadav, R. M.; Liu, M.; Sharma, P. P.; Tiwary, C. S.; Ma, L.; Zou, X.; Zhou, X.-D.; Yakobson, B. I.; Lou, J.; et al. Achieving Highly Efficient, Selective, and Stable CO 2 Reduction on Nitrogen-Doped Carbon Nanotubes. ACS Nano 2015, 9 (5), 5364–5371. (40) Rosen, J.; Hutchings, G. S.; Lu, Q.; Rivera, S.; Zhou, Y.; Vlachos, D. G.; Jiao, F. Mechanistic Insights into the Electrochemical Reduction of CO 2 to CO on Nanostructured Ag Surfaces. ACS Catal. 2015, 5 (7), 4293–4299. (41) Liu, Y.; Chen, S.; Quan, X.; Yu, H. Efficient Electrochemical Reduction of Carbon Dioxide to Acetate on Nitrogen-Doped Nanodiamond. J. Am. Chem. Soc. 2015, 137 (36), 11631–11636. (42) Wang, H.; Jia, J.; Song, P.; Wang, Q.; Li, D.; Min, S.; Qian, C.; Wang, L.; Li, Y. F.; Ma, C.; et al. Efficient Electrocatalytic Reduction of CO2 by Nitrogen-Doped Nanoporous Carbon/Carbon Nanotube Membranes - A Step Towards the Electrochemical CO2 Refinery. Angew. Chemie Int. Ed. 2017. (43) Zhu, W.; Michalsky, R.; Metin, Ö.; Lv, H.; Guo, S.; Wright, C. J.; Sun, X.; Peterson, A. A.; Sun, S. Monodisperse Au Nanoparticles for Selective Electrocatalytic Reduction of CO2 to CO. J. Am. Chem. Soc. 2013, 135 (45), 16833–16836. (44) Nørskov, J. K.; Rossmeisl, J.; Logadottir, A.; Lindqvist, L.; Kitchin, J. R.; Bligaard, T.; Jónsson, H. Origin of the Overpotential for Oxygen Reduction at a Fuel-Cell Cathode. J. Phys. Chem. B 2004, 108 (46), 17886–17892. (45) Shi, C.; Hansen, H. A.; Lausche, A. C.; Nørskov, J. K. Trends in Electrochemical CO2 Reduction Activity for Open and Close-Packed Metal Surfaces. Phys. Chem. Chem. Phys. 2014, 16 (10), 4720–4727. (46) Nilsson, A.; Gunnar, L.; Pettersson, M. Chemical Bonding on Surfaces Probed by X-Ray Emission Spectroscopy and Density Functional Theory. (47) Jing, Y.; Zhou, Z. Computational Insights into Oxygen Reduction Reaction and Initial Li 2 O 2 Nucleation on Pristine and N-Doped Graphene in Li–O 2 Batteries. ACS Catal. 2015, 5 (7), 4309–4317. (48) Hong, X.; Chan, K.; Tsai, C.; Nørskov, J. K. How Doped MoS 2 Breaks TransitionMetal Scaling Relations for CO 2 Electrochemical Reduction. ACS Catal. 2016, 6 (7), 4428–4437. (49) Lim, H.-K.; Shin, H.; Goddard, W. A.; Hwang, Y. J.; Min, B. K.; Kim, H. Embedding Covalency into Metal Catalysts for Efficient Electrochemical Conversion of CO 2. J. Am. Chem. Soc. 2014, 136 (32), 11355–11361. (50) Giannozzi, P.; Baroni, S.; Bonini, N.; Calandra, M.; Car, R.; Cavazzoni, C.; Ceresoli, D.; Chiarotti, G. L.; Cococcioni, M.; Dabo, I.; et al. QUANTUM ESPRESSO: A Modular and Open-Source Software Project for Quantum Simulations of Materials. J. Phys. Condens. Matter 2009, 21 (39), 395502. (51) Atomic Simulation Environment (ASE), URL: https://wiki.fysik.dtu.dk/ase, Center for Atomic Scale Material Design (CAMD), Technical University of Denmark, Lyngby.

16

ACS Paragon Plus Environment

Page 16 of 18

Page 17 of 18

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(52) Adllan, A. A.; Dal Corso, A. Ultrasoft Pseudopotentials and Projector Augmented-Wave Data Sets: Application to Diatomic Molecules. J. Phys. Condens. Matter 2011, 23 (42), 425501. (53) Wellendorff, J.; Lundgaard, K. T.; Møgelhøj, A.; Petzold, V.; Landis, D. D.; Nørskov, J. K.; Bligaard, T.; Jacobsen, K. W. Density Functionals for Surface Science: Exchange-Correlation Model Development with Bayesian Error Estimation. Phys. Rev. B 2012, 85 (23), 235149. (54) Monkhorst, H. J.; Pack, J. D. Special Points for Brillouin-Zone Integrations. Phys. Rev. B 1976, 13 (12), 5188–5192.

17

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

For Table of Contents Use Only:

+2(H++e-)

Electrochemical reduction of CO2 coupled with a renewable energy source (such as wind or solar) is an emerging reaction of interest for producing carbon-neutral fuels or industrial chemicals. Carbon defects are active in two-electron electrochemical reduction of CO2 to CO.