Thermal Atomic Layer Etching of Silicon Using O2, HF and Al(CH3)3

44 mins ago - In addition, metal oxides can also be ... The thermal ALE of silicon was performed in a warm wall reactor with a ... The reactor walls w...
0 downloads 0 Views 908KB Size
Subscriber access provided by Bibliothèque de l'Université Paris-Sud

Article

Thermal Atomic Layer Etching of Silicon Using O2, HF and Al(CH3)3 as the Reactants Aziz I. Abdulagatov, and Steven M. George Chem. Mater., Just Accepted Manuscript • DOI: 10.1021/acs.chemmater.8b02745 • Publication Date (Web): 05 Nov 2018 Downloaded from http://pubs.acs.org on November 18, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 46 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Chemistry of Materials

3rd Revised Chemistry of Materials Manuscript ID: cm-2018-02745g.R2 November 5, 2018

Thermal Atomic Layer Etching of Silicon Using O2, HF and Al(CH3)3 as the Reactants Aziz I. Abdulagatov1 and Steven M. George1,2 1Department

of Chemistry and Biochemistry, of Mechanical Engineering, University of Colorado, Boulder, CO 80309-0215, U.S.A. 2Department

Abstract The thermal atomic layer etching (ALE) of silicon was performed using O2, HF and Al(CH3)3 as the reactants at temperatures from 225-290°C. This thermal etching process is based on Si oxidation using O2 and conversion of SiO2 to Al2O3 using trimethylaluminum (TMA). Al2O3 is then fluorinated by HF to produce AlF3 prior to removal of AlF3 by a ligandexchange reaction with TMA. Thermal Si ALE was studied using silicon-on-insulator (SOI) wafers. In situ spectroscopic ellipsometry was employed to monitor simultaneously both the thickness of the top SiO2 layer and the underlying silicon film during Si ALE. These studies observed that the silicon film thickness decreased linearly with the number of reaction cycles while the thickness of the SiO2 layer remained constant. Using an O2-HF-TMA exposure sequence, the Si ALE etch rate was 0.4 Å/cycle at 290°C. This etch rate was obtained using static reactant pressures of 250, 1.0 and 1.0 Torr, and exposure times of 10, 5 and 5 s, for O2, HF and TMA, respectively. The SiO2 thickness was 10-11 Å under these reaction conditions at 290°C. The Si ALE etch rate increased with O2 and TMA pressure before reaching a limiting etch rate at higher O2 and TMA pressures. The order of the reactants affected the Si etch rate. Changing the exposure sequence from O2-HF-TMA to O2-TMA-HF reduced the etch rate from 1 ACS Paragon Plus Environment

Chemistry of Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

0.4 to 0.2 Å/cycle at 290°C. Lowering the etch temperature below 290oC also resulted in the reduction of the Si etch rate. Atomic force microscopy (AFM) measurements determined that the root-mean-squared (RMS) roughness of the surface was 2.0 ± 0.2 Å before and after the Si ALE using the optimum reaction conditions. Lowering the static O2 pressures below 250 Torr reduced the etch rate and also increased the RMS surface roughness. There was no evidence for any change in the Si ALE process for ultrathin Si films with thicknesses