Thermal-Induced Dielectric Switching with 40K Wide Hysteresis Loop

information storages, signal processing and memory devices.7-12 Among these ... application. Control of the polar components assemble and thus the die...
3 downloads 4 Views 1MB Size
Subscriber access provided by UNIV OF DURHAM

Energy Conversion and Storage; Plasmonics and Optoelectronics

Thermal-Induced Dielectric Switching with 40K Wide Hysteresis Loop Near Room Temperature Yang-Hui Luo, Chen Chen, Dan-Li Hong, Xiao-Tong He, Jing-Wen Wang, and Bai-Wang Sun J. Phys. Chem. Lett., Just Accepted Manuscript • DOI: 10.1021/acs.jpclett.8b00597 • Publication Date (Web): 12 Apr 2018 Downloaded from http://pubs.acs.org on April 12, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

Thermal-Induced Dielectric Switching with 40K Wide Hysteresis Loop Near Room Temperature

Yang-Hui Luo, * Chen Chen, Dan-Li Hong, Xiao-Tong He, Jing-Wen Wang, and Bai-Wang Sun*

School of Chemistry and Chemical Engineering, Southeast University, Nanjing, 211189, PR. China. E-mail: [email protected], [email protected].

1

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Abstract A thermal-induced dielectric switching has been realized in two ion-pair crystal [C2H6N5]+—[H2PO4]- (1, C2H6N5 = 3, 5-diamino-1, 2, 4-triazolinium) through single-crystal-to-single-crystal phase transition (SCSC-PT). Upon cooling from room temperature, the one-dimensional cation stripes that composed of [C2H5N5]+ cations have rotated sharply around the c axis with 90 degrees, accompanied by transition of crystal stacking from loose un-paralleled (dynamic state) to compression paralleled (static state), and reorientation of dipoles on [C2H5N5]+ cation, which thus resulted in high-dielectric state (HDS) to low-dielectric state (LDS) transformation. While on the warming run, the reverse process was rather sluggish, resulting a reversible dielectric switching with ultra-large (about 40K wide) hysteresis loop near room temperature. It is thought that the large-sized polar cation stripes play a predominant influence on the switching properties of 1.

TOC

2

ACS Paragon Plus Environment

Page 2 of 21

Page 3 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

Materials showing switchable physical and/or chemical properties continue to draw attention of scientists with respect to not only the doubtlessly interesting fundamental aspects, but also the potential applications.1,2 Usually, switchable properties are highly sensitive to such external stimuli as light, irradiation, temperature, press, guest molecules, electric/magnetic fields, etc.3-6 As have been expected, the bulk physical/chemical properties will be turned between at least two distinct states triggered by multiple stimuli, that is bi-stability. Which has the potential to be developed into sensors, displays, switching devices, information storages, signal processing and memory devices.7-12 Among these switchable properties, magnetization and polarity have occupied a special position. Switchable magnetization refers to the spin-arrangement of respective sites and the coupling interactions between them, that is the so-called “spin crossover” (SCO) which refers to the spin-state transition between a high-spin (HS) and a low-spin (LS) state.13,14 Whereas polarity is related to the redistribution of positive and negative charge centers, and this redistribution will resulted in dielectric switching between high- and low-dielectric states (HDS and LDS) that can be viewed as an electrical counterpart to SCO.15,16 As a consequence, the switchable dielectric compounds have emerged as a promising candidate to act as effective stimuli-responsive materials.

3

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

For practical application, a molecular switch must be required to show a remarkable bi-stability.17-20 More ideally, it should operate under ambient conditions with a wide hysteresis loop at around room temperature (RT).21 From the microscopic viewpoint of molecule-based crystalline structures, the bi-stability is often manifests a reversible structural phase-transition (PT) at molecular level. One thing deserves noting that: in most cases, the degree of thermal hysteresis can be significantly affected by the cooperativity during structural PT, that is the motion resistance of atomic /molecular within the tightly stacked crystalline environment.22 On the one hand, the dielectric switching is originated from the reorientation of polar components (atoms、ions or molecules) between static (frozen) and dynamic (motional) states.23,24 On the other hand, the reorientation of large-sized polar components will be more sluggish than the small-sized ones, which thus can promote the generation of unusual thermal hysteresis loop.25 Hence, the assemble of large-sized polar components into switchable dielectric compounds would make a significant difference. Zhang et, al.26-28 have reported a series of metal-cyanide based perovskite-type metal-organic frameworks, which have shown distinct dielectric constant switching triggered by guest molecules but with negligible thermal hysteresis loop; Wen et, al.29 has prepared two bulky ion-pair compounds which have shown above-room temperature dielectric constant switching with about 10K wide hysteresis loop. More recently, Tang et, al.30

4

ACS Paragon Plus Environment

Page 4 of 21

Page 5 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

have demonstrated an approximately 15K wide hysteresis loop of dielectric relaxation at around 228K, in an succinimide lithium(I) hybrids. However, none of these above-mentioned results meet the requirements for practical application. Control of the polar components assemble and thus the dielectric switching operate at around room temperature with ultra-large hysteresis loop remains a main challenge for the fabricating of functioning dielectric devices. Here in this context, we report a crystalline two ion-pair compound composed of 3, 5-diamino-1, 2, 4-triazolinium cation (1+) and phosphate ion (1-), that is crystal [C2H6N5]+—[H2PO4]- (1). Upon cooling and heating, 1 shown reversible dielectric switching between distinct HDS and LDS with an approximately 40K wide thermal hysteresis loop near the room temperature. Interestingly, this dielectric switching was accompanied by a SCSC-PT, which was originated from the reorientation of the large-sized polar 3, 5-diamino-1, 2, 4-triazolinium cation stripes. Where, the polar cation stripes undergo a 90 degrees rotation around the c axis, accompanied by a dynamic change between the paralleled and un-paralleled stacking models that switched by temperature. More importantly, this SCSC-PT has induced exchange of the positive and negative charge centers on each [C2H6N5]+ cations, which primary responsible for the dielectric switching properties of 1. Crystal 1 was precipitated from an aqueous solution of 3, 5-diamino-1, 2, 4-triazole and phosphate (Supporting Information) with large white block habit.

5

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Firstly, we solved its structure at room temperature (293 K), it has shown orthorhombic space group Fdd2 with a = 13.481(3) Å, b = 36.938(8) Å, c =

Figure 1. Crystal structure of compound 1 under different temperature. (a) The formation of 1D ladder-like 3, 5-diamino-1, 2, 4-triazolinium cations stripe and (b) the connecting motif of 3D framework; The height of “steps” in the stripe undergo a decrease from HDS (c) to LDS (d); The dihedral angle and plane-plane distances between adjacent stripes for HDS (e) and LDS (f) have been presented.

6

ACS Paragon Plus Environment

Page 6 of 21

Page 7 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

6.0738(12) Å (Supporting Information, Tables S1). In the crystal, each cation of 3, 5-diamino-1, 2, 4-triazolinium connects to two other one through N-HON hydrogen bonding contacts (NON distance of 3.036 Å) along the crystallography c axis, and four different phosphate ions through N-HOO hydrogen bonding contacts (NOO distances 2.766-2.988 Å) along the crystallography b axis (Figure S1a and Table S2). While for each phosphate ion, its connects to three other ions and four 3, 5-diamino-1, 2, 4-triazolinium cations, through O-HOO (OOO distances of 2.535 and 2.585 Å) and N-HOO (NOO distances of 2.754-2.988 Å) hydrogen bonding contacts, along the crystallography a and b axis, respectively (Figure S1b and Table S2). Interestingly, the adjacent 3, 5-diamino-1, 2, 4-triazolinium cations were connected

into

crystallography

one-dimensional

c

direction

(1D)

(Figure

ladder-like 1a).

Where,

stripe the

along height

the and

centroids-centroids distances of the adjacent “steps” within one stripe were found to be 0.590 (Figure 1c) and 6.074 Å (Figure S2a), respectively. These 1D ladder-like stripes were further stacked along both the a and b direction, supported by the two-dimensional (2-D) phosphate ion ([H2PO4]-) arrays, into three-dimensional (3D) framework (Figure 1b). It is notable that, in the 2-D arrays, the [H2PO4]- ions were formed a dimer unit through double O-HOO (OOO distances of 2.585 Å) hydrogen bonding interactions, and each dimer unit was further connected to other fours through single O-HOO (OOO

7

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

distances of 2.535 Å) hydrogen bonding interactions (Figure S3a). For the 3-D framework, the cation stripes stacked un-paralleled along the crystallography a direction in OABABO fashion and fixed in the both sides of the 2-D arrays, with the dihedral angle and centroids-centroids distances between adjacent stripes of 0.76° (Figure 1e) and 3.700 Å (Figure S2b), respectively. Thermal analysis revealed that crystal 1 can maintained to 200 °C upon heating (Figure S4).

Figure 2. Rotation of cation stripes around the c axis with variation of temperature (a and b); Insert: DSC curves of 1 as measured in cooling-heating cycles (c). Upon cooling to 100K, the space group of 1 is still Fdd2, however, the unit cell a and b have exchanged with a = 37.1049(10) Å, b = 13.3329(3) Å, c =

8

ACS Paragon Plus Environment

Page 8 of 21

Page 9 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

6.07102(16) Å (Table S1), which can be attribute to the rotation and reorientation of the large-sized polar 3, 5-diamino-1, 2, 4-triazolinium cation stripes. To understand the microscopic rotation and reorientation process of the cation stripes, a detailed comparison between the crystal structures at 293 and 100K have been performed. Results shown that the most striking changes in the crystal structure were the rotation about 90 degrees of the cation stripes around the c axis, from perpendicular to the a axis to perpendicular to b axis (Figure 2a and b) and the strengthening of intermolecular hydrogen bonding contacts (Table S3). Note that, this rotation was accompanied by a reorientation of the individual cation in the stripes: e.g. for the reoriented stripes, the height and centroids-centroids distances of the adjacent “steps” within one stripe were shorter to be 0.550 (Figure 1d) and 6.071Å (Figure S2c), respectively. More importantly, after reorientation, the cation stripes stacked paralleled along the b direction, with plane-plane distances of 3.456 Å (Figure 1f) and the centroids-centroids distances between 3, 5-diamino-1, 2, 4-triazolinium cation in adjacent stripes was shorter to 3.667 Å (Figure S2d). This dramatic rotation of the cation stripes is responsible primary for the SCSC-PT and dielectric switching for crystal 1 as described below. While for the 2-D arrays, the OOO distances for the dimer unit have shown a slight increase to 2.587 Å, which can be attributed to the pulling effect provided by transformation of the 1-D polar 3, 5-diamino-1, 2, 4-triazolinium

9

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 21

cation stripes from un-paralleled to paralleled stacking. This pulling effect was accompanied by a decrease in the OOO distances (2.529 Å) between adjacent dimer units as sacrifices (Figure S3b).

Figure 3. Comparison between the (a) Hirshfeld dnorm surfaces, (b) Crystal Voids, and (c) Electron Density of polar 3, 5-diamino-1, 2, 4-triazolinium cations at HDS (left) and LDS (right), respectively. 3D Hirshfeld surfaces and 2D fingerprint plots analysis

31,32

(Figure 3 and

Figure S5-S6) were performed to compare the polar 3, 5-diamino-1, 2, 4-triazolinium cations at different dielectric states. Shown in Figure 3 were the

10

ACS Paragon Plus Environment

Page 11 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

Hirshfeld dnorm surfaces, Crystal Voids, and Electron Density of the polar 3, 5-diamino-1, 2, 4-triazolinium cation at HDS and LDS respectively. Where, the proportion of the significant hydrogen bonding contacts (Figure 3a, represented by the large deep red circular depressions on the dnorm surfaces) has shown an increased with the decrease of temperature, from 58.6% contribution to the total Hirshfeld surfaces at 293K to 62.5% at 100K (Table S4). On the contrary, the crystal voids have undergone a decrease with temperature, from V = 345.32 Å3, A = 1178.21 Å2 at 293K to V = 319.54 Å3, A = 1132.30 Å2 at 100K (Figure 3b), demonstrating a compressed crystal stacking at lower temperature that similar with the results of crystal structure analysis, and this compressed crystal stacking can be viewed as a static (frozen) state. More importantly, the SCSC-PT has accompanied by an exchange of the positive and negative charge centers on the polar 3, 5-diamino-1, 2, 4-triazolinium cations (Figure 3c), that is the reorientation of dipoles, thus, a dielectric switching with large relaxation can be expected with 1. The whole process of the SCSC-PT of 1 from 293 to 100K was also demonstrated by DSC (differential scanning calorimetry) analysis (Figure 2c). During the cooling-warming cycles, a sharp exothermic peak occurred at approximately 213 K with enthalpy change of 0.67 Jg-1 was observed on the cooling DSC curves, corresponding to the rotation and change of the stacking model of the polar 3, 5-diamino-1, 2, 4-triazolinium cation stripes from

11

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

un-paralleled to paralleled stacking. While on the warming procedure, a broad endothermic peak appears in temperature range 223-240K with enthalpy change of 0.46 Jg-1. These results indicated that: one the one hand, the SCSC-PT of 1 from HDS to LDS can occurred reversibly in the solid-state; on the other hand, the un-paralleled to paralleled stacking transformation was more sharply than its reverse process, which will certainly result in ultra-large thermal hysteresis loop. From the above single-crystal structure analysis, the polar 3, 5-diamino-1, 2, 4-triazolinium cation stripes in 1 undergo approximately 90 degrees rotation along the c axis, accompanied by an un-paralleled to paralleled stacking model transformation at around the transition point. More importantly, within this rotational geometry, the dipoles within the 3, 5-diamino-1, 2, 4-triazolinium cation have undergone reorientation, that is the violently oscillation of the dipole moments within [C2H6N5]+ cation,33 A phenomenon that usually accompanied by large dielectric constant and reversible dielectric switching with ultra-large thermal hysteresis loop, as described below. Dielectric switching properties of crystal 1 were measured in temperature range 330-120 K and frequency range 0.5-1000 kHz with the powdered crystalline samples on cooling-warming cycles (Figure 4). At the room temperature, the real part (ε’) value at 1000 kHz indicates the HDS, and this value has undergone an increase to reach a peak value of about 6.4 at 293 K

12

ACS Paragon Plus Environment

Page 12 of 21

Page 13 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

upon cooling. This short-range increase of ε’ value with decrease of temperature can be interpreted as the fight between random thermal motion of the polar 3, 5-diamino-1, 2, 4-triazolinium cation stripes and the orientational polarization that induced by electric field.34 Then, a rapid decrease of this ε’ value was observed to reach a platform with value of about 2.9 at 264K upon further cooling, indicating a transformation from the HDS to the LDS, that is dielectric switching. Note that, this dielectric switching can be attribute to the transitions of the polar cation stripes from un-paralleled-to-paralleled stacking in the crystal. Interestingly, a typical dielectric relaxation has occurred as expected, with the peak value of ε’ decreases from 48 to 6.4, and the peaking temperature moves from 288 to 293K, as the frequency increases from 0.5 kHz to 1000 kHz, demonstrating the slows down of dipolar reorientation process with the decrease of the temperature.35 It is thought that the motion of polar cation stripes in the crystal 1 is more slowly than 0.5 kHz because the SCSC-PT temperature (213K, determined by DSC measurements) is much lower than the peaking temperature (288K) of ε’ at 0.5 kHz.

13

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 21

Figure 4. The real part of the dielectric constant of 1 dependent on temperature at 1 MHz (left) and comparison of thermal hysteresis loop under different frequency (right). While on the warming runs, the ε’ value has undergone a gradual increase in the temperature range 210-250K below the transition point of 278K, indicating a much slower transition from LDS to HDS than its reverse process. As a consquences, an approximate 40K wide dielectric hysteresis loop (ε’-T) has appeared, i.e., dielectric bi-stability, which can be attribute to the motion resistance that derived from the rotation and reorientation of the polar 3, 5-diamino-1,

2,

4-triazolinium

cation

stripes

during

the

reversible

thermally-induced SCSC-PT. It should be noted that, the width of the dielectric hysteresis loop was increased with the decrease of frequency, from 40K wide at 1000 kHz to 50K wide at 0.5 kHz. This kind of bi-stability in dielectric constants with tunable hysteresis loop is somewhat rare, which may have the potential to be integrated into molecular dielectric switching devices. Again, a

14

ACS Paragon Plus Environment

Page 15 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

typical dielectric relaxation has occurred for the warming runs as expected. Interestingly, the gap between the ε’ value for the HDS and LDS have shown significant frequency-dependency. Where, the value for the HDS was near 58 times larger than that for LDS at 0.5 kHz, while this multiple relationship was decreased to be 32, 10, 6.8, 2.4 and 2.2 times, for 1, 5, 10, 100 and 1000 kHz, respectively. Such results suggesting a promising dielectric switch with large frequency application range. In summary, a thermal-induced dielectric switching with ultra-large hysteresis loop near room temperature has been realized in an easy prepared two ion-pair crystal [C2H5N5]+—[H2PO4]- (1, C2H5N5 = 3, 5-diamino-1, 2, 4-triazolinium) through single-crystal-to-single-crystal phase transition. This dielectric bi-stability was originated from the 90 degrees rotation of the one-dimensional polar 3, 5-diamino-1, 2, 4-triazolinium cation stripes around the c axis and the following change of the intermolecular interactions around the [C2H5N5]+ cation, including hydrogen-bonding contacts, crystal stacking and the exchange of positive and negative charge centers. The large-sized polar cation stripes play a predominant influence on the switching properties of 1.

The authors declare no competing financial interest.

Acknowledgements 15

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

This research was supported by the Natural Science Foundation of China (Grant No. 21701023), Natural Science Foundation of Jiangsu Province (Grant No. BK20170660), Fundamental Research Funds for the Central Universities (No.3207047407) and PAPD of Jiangsu Higher Education Institutions.

Supporting Information Materials and physical measurements, Crystal data and structure refinement details for 1-HDS and 1-LDS, Geometrical parameters for hydrogen bonds, additional crystal structures and TGA/DSC profiles of compound 1, Comparison between Curvedness, Fragment Patch, Shape index and 2-D fingerprint plots of 3, 5-diamino-1, 2, 4-triazolinium cation at HDS and LDS, Summary of the percentage contributions to the Hirshfeld surfaces of 3, 5-diamino-1, 2, 4-triazolinium cation at HDS and LDS.

References (1) Urban, M. W. Handbook of Stimuli-Responsive Materials; Wiley-VCH: Weinheim, Germany, 2011. (2) Theato, P.; Sumerlin, B. S.; O’Reilly, R. K.; Epps, T. H. Stimuli Responsive Materials. Chem. Soc. Rev. 2013, 42, 7055-7056. (3) Horiuchi, S.; Tokura, Y. Organic Ferroelectrics. Nat. Mater. 2008, 7, 357-366. (4) Luo, Y. H.; Chen, C.; Hong, D. L.; He, X. T.; Wang, J. W.; Ding, T.; Wang, B.

16

ACS Paragon Plus Environment

Page 16 of 21

Page 17 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

J.; Sun, B. W. Binding CO2 from Air by a Bulky Organometallic Cation Containing Primary Amines. ACS Appl. Mater. Interfaces 2018, 10, 9495-9502. (5) Halcrow,

M.

A.

Structure:Function

Relationships

in

Molecular

Spin-Crossover Complexes. Chem. Soc. Rev. 2011, 40, 4119-4142. (6) Bersuker, I. B. Pseudo-Jahn–Teller Effect-A Two-State Paradigm in Formation, Deformation, and Transformation of Molecular Systems and Solids. Chem. Rev. 2013, 113, 1351-1390. (7) Venkataramani, S.; Jana, U.; Dommaschk, M.; Sçennichsen, F. D.; Tuczek, F.; Herges, R. Magnetic Bistability of Molecules in Homogeneous Solution at Room Temperature. Science 2011, 331, 445-448. (8) Dei, A. Photomagnetic Effects in Polycyanometallate Compounds: An Intriguing Future Chemically Based Technology? Angew. Chem. Int. Ed. 2005, 44, 1160-1163; Angew. Chem. 2005, 117, 1184-1187; (9) Sato, O.; Tao, J.; Zhang, Y. Z. Control of Magnetic Properties Through External Stimuli. Angew. Chem., Int. Ed. 2007, 46, 2152-2187. (10)

Sun, Z. H.; Luo, J. H.; Chen, T. L.; Li, L. N.; Xiong, R. G.; Tong, M. L.;

Hong, M. C. Distinct Molecular Motions in a Switchable Chromophore Dielectric

4‐N,N‐Dimethylamino‐4′‐N′‐methylstilbazolium

Trifluoromethanesulfonate. Adv. Funct. Mater. 2012, 22, 4855-4861. (11)

Kahn, O.; Martinez, C. J. Spin-Transition Polymers: From Molecular

17

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 21

Materials Toward Memory Devices. Science 1998, 279, 44-48. (12) P.;

Rotaru, A.; Dugay, J.; Tan, R. P.; Guralskiy, I. A.; Salmon, L.; Demont, Carrey,

J.;

Molnar,

Nano-Electromanipulation

G.;

of

Spin

Respaud, Crossover

M.;

Bousseksou,

Nanorods:

A.

Towards

Switchable Nanoelectronic Devices. Adv. Mater. 2013, 25, 1745-1749. (13)

Kahn, O. Molecular Magnetism; VCH: New York, 1993.

(14)

Gutlich, P.; Goodwin, H. A. Spin Crossover-An Overall Perspective.

Top. Curr. Chem. 2004, 233, 1-47. (15) Zhang, W.; Cai, Y.; Xiong, R.-G.; Yoshikawa, H.; Awaga, K. Exceptional Dielectric Phase Transitions in A Perovskite-Type Cage Compound.

Angew. Chem. Int. Ed. 2010, 49, 6608-6610. (16) Zhang, W.; Ye, H.-Y.; Graf, R.; Spiess, H. W.; Yao, Y.-F.; Zhu, R.-Q.; Xiong, R.-G. Tunable and Switchable Dielectric Constant in An Amphidynamic Crystal. J. Am. Chem. Soc. 2013, 135, 5230-5233. (17)

Rosner, B.; Milek, M.; Witt, A.; Gobaut, B.; Torelli, P.; Fink, R. H.;

Khusniyarov, M. M. Reversible Photoswitching of a Spin-Crossover Molecular Complex in the Solid State at Room Temperature Angew. Chem.

Int. Ed. 2015, 54, 12976-12980. (18)

Luo, Y. H.; Nihei, M.; Wen, G. J.; Sun, B. W.; Oshio, H.

Ambient-Temperature Spin-State Switching Achieved by Protonation of the Amino Group in [Fe(H2Bpz2)2(bipy-NH2)]. Inorg. Chem. 2016, 55,

18

ACS Paragon Plus Environment

Page 19 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

8147-8152. (19)

Luo, Y.-H.; Liu, Q.-L.; Yang, L.-J.; Sun, Y.; Wang, J.-W.; You, C.-Q.;

Sun, B.-W. Magnetic Observation of Above Room-Temperature Spin Transition in Vesicular Nano-Spheres. J. Mater. Chem. C 2016, 4, 8061-8069. (20)

Luo,

Y.-H.;

Chen,

C.;

Li,

Y.-J.;

Wang,

J.-W.;

Sun,

B.-W.

Protonation-Induced Color Change of an Amino Group Functionalized [Fe4(µ3-O)2]8+ Cluster. Dyes and Pigments 2017, 143, 239-244. (21)

Jay, C.; Groliere, F.; Kahn, O.; Krçber, J. From Spin Transition to

Display and Memory Devices. Mol. Cryst. Liq. Cryst. 1993, 234, 255-262. (22)

Shi, P. P.; Tang, Y. Y.; Li, P. F.; Liao, W. Q.; Wang, Z. X.; Ye, Q.;

Xiong, R. G. Symmetry Breaking in Molecular Ferroelectrics. Chem. Soc.

Rev. 2016, 45, 3811-3827. (23)

a) Garcia-Garibay, M. A. Supramolecular Structure and Dynamics

Special Feature: Molecular Structure As A Blueprint for Supramolecular Structure Chemistry in Confined Spaces. Proc. Natl. Acad. Sci. USA 2005,

102, 10766-10770. (24)

Vogelsberg, C. S.; Garcia-Garibay, M. A. Crystalline Molecular

Machines: Function, Phase Order, Dimensionality, and Composition.

Chem. Soc. Rev. 2012, 43, 1892-1910. (25) Han, S.; Zhang, J.; Teng, B.; Ji, C.; Zhang, W.; Sun, Z.; Luo, J. Inorganic–

19

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 21

Organic Hybrid Switchable Dielectric Materials with the Coexistence of Magnetic Anomalies Induced by Reversible High-Temperature Phase Transition. J. Mater. Chem. C 2017, 5, 8509-8515. (26)

a) Shi, C.; Zhang, X.; Cai, Y.; Yao, Y. F.; Zhang, W. A Chemically

Triggered and Thermally Switched Dielectric Constant Transition in a Metal Cyanide Based Crystal. Angew. Chem. Int. Ed. 2015, 54, 6206-6210. (27)

Shi, C.; Yu, C. H.; Zhang, W. Predicting and Screening Dielectric

Transitions in a Series of Hybrid Organic–Inorganic Double Perovskites via an Extended Tolerance Factor Approach. Angew. Chem. Int. Ed. 2016, 55, 5798-5802. (28)

Liu, Y. L.; Zhang, W. Dual Stimuli-Triggered Dielectric Switching and

Sensing in a Host–Guest Cyanometallate Framework. Chem. Commun. 2017, 53, 6077-6080. (29)

Zhang, S.-Y.; Liao, J.-S.; Xu, W.-J.; Liang, F.-Y.; Peng, G.-H.; Liu, S.-J.;

Wen, H.-R.; Du, Z.-Y. Structural Phase Transitions, Dielectric Bistability and

Luminescence

of

Two

Bulky

Ion-Pair

Crystals

[N(CH)]

[Ln(NO)](Ln=Tb,Dy). New J. Chem. 2017, 41, 9963-9968. (30)

Tang, Y. Z.; Wang, B.; Zhou, H. T.; Chen, S. P.; Tan, Y. H.; Wang, C. F.;

Yang, C. S.; Wen, H. R. Reversible Phase Transition with Ultralarge Dielectric Relaxation Behaviors in Succinimide Lithium(I) Hybrids. Inorg

20

ACS Paragon Plus Environment

Page 21 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

Chem 2018, 57, 1196-1202 (31)

Thomas, S. P.; Shi, M. W.; Koutsantonis, G. A.; Jayatilaka, D.;

Edwards, A. J.; Spackman, M. A. The Elusive Structural Origin of Plastic Bending in Dimethyl Sulfone Crystals with Quasi-isotropic Crystal Packing.

Angew. Chem. Int. Ed. 2017, 56, 8468-8472. (32)

Luo, Y.-H.; Wang, J.-W.; Chen, C.; Li, Y.-J.; Sun, B.-W. Reversibly

Stretching Cocrystals by the Application of a Magnetic Field. Cryst. Growth

Des. 2017, 17, 2576-2583. (33)

Shang, R.; Wang, Z.-M.; Gao, S. A 36-Fold Multiple Unit Cell and

Switchable Anisotropic Dielectric Responses in an Ammonium Magnesium Formate Framework. Angew. Chem. Int. Ed. 2015, 54, 2534-2537. (34)

Zhang, J.; Sun, Z.; Zhang, W.; Ji, C.; Liu, S.; Han, S.; Luo, J.

Hydrogen-Bonded Switchable Dielectric Material Showing the Bistability of Second-Order Nonlinear Optical Properties. Cryst. Growth Des. 2017, 17, 3250-3256. (35)

Shao, X. D.; Zhang, X.; Shi, C.; Yao, Y. F.; Zhang, W. Switching

Dielectric Constant Near Room Temperature in a Molecular Crystal. Adv.

Sci. 2015, 2, 1500029.

21