Thickness Effect of Bulk Heterojunction Layers on the Performance

Aug 11, 2017 - Charging Characteristics of Lithium Ion Battery Using Semi-Solar Modules of Polymer:Fullerene Solar Cells. Myeonghun Song , Sooyong Lee...
0 downloads 10 Views 2MB Size
Subscriber access provided by BOSTON UNIV

Article

Thickness Effect of Bulk Heterojunction Layers on the Performance and Stability of Polymer:Fullerene Solar Cells with Alkylthiothiophene-Containing Polymer Sungho Nam, Myeonghun Song, Hwajeong Kim, Donal D.C. Bradley, and Youngkyoo Kim ACS Sustainable Chem. Eng., Just Accepted Manuscript • DOI: 10.1021/ acssuschemeng.7b02238 • Publication Date (Web): 11 Aug 2017 Downloaded from http://pubs.acs.org on August 11, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Sustainable Chemistry & Engineering is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Thickness Effect of Bulk Heterojunction Layers on the Performance and Stability of Polymer:Fullerene Solar Cells with Alkylthiothiophene-Containing Polymer Sungho Nam†,‡, Myeonghun Song†, Hwajeong Kim†,§, Donal D. C. Bradley*,‡,∥ and Youngkyoo Kim*,† †

Organic Nanoelectronics Laboratory and KNU Institute for Nanophotonics Applications, Department of Chemical Engineering, School of Applied Chemical Engineering, Kyungpook National University, Daegu 41566, Republic of Korea



Departments of Physics, Division of Mathematical, Physical and Life Sciences, University of Oxford, Oxford OX1 3PU, United Kingdom

§

Priority Research Center, Research Institute of Advanced Energy Technology, Kyungpook National University, Daegu 41566, Republic of Korea

∥Departments

of Engineering Science, Division of Mathematical, Physical and Life Sciences,

University of Oxford, Oxford OX1 3PJ, United Kingdom

*Corresponding Authors: Prof. Youngkyoo Kim: Email) [email protected]; Tel) +82-53-950-5616, Fax) +82-53-950-6615 Prof. Donal D. C. Bradley: Email) [email protected] 1

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 31

ABSTRACT: We report a pronounced thickness effect of bulk heterojunction (BHJ) layers on the performance and stability of inverted polymer solar cells with the BHJ layers of poly[(4,8bis(5-(octylthio)thiophen-2-yl)benzo[1,2-b:4,5-b′]dithiophene-co-3-fluorothieno[3,4b]thiophene-2-carboxylate] (PBDT-TS1) and [6,6]-phenyl-C71-butyric acid methyl ester (PC71BM). The thickness of the BHJ layers was varied from 40 to 120 nm by changing solution concentrations and spin-coating speeds. The results showed that the film thickness considerably affected the performance and stability of devices. The power conversion efficiency reached ca. 9 % at the thickness of 80 nm by the optimized nanoscale phase separation between donor and acceptor components. However, the devices with 120 nm-thick BHJ layers showed better device stability under continuous illumination with a simulated solar light due to the well-maintained surface morphology and nanostructure in addition to the improved morphological volume stability.

KEYWORDS: thickness, bulk heterojunction, device stability, morphology, volume stability.

2

ACS Paragon Plus Environment

Page 3 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

INTRODUCTION Polymer solar cells (PSCs) with bulk heterojunction (BHJ) layers consisting of electrondonating and electron-accepting materials have been extensively studied for renewable energy sources because of their intriguing features including flexibility, light weight, and solution-based fabrication.1-6 Recently, power conversion efficiencies (PCEs) of PSCs have reached up to 12% for single-stack cells.7-10 This is attributed to extensive studies on morphology control via thermal/solvent annealing, addition of additives, interface engineering of charge-collecting buffer layers, newly synthesized electron-donating/accepting materials, and a comprehensive understanding of device operation mechanisms in PSCs.11-22 One of the key challenges for improving solar cell efficiency is to find an optimal BHJ layer thickness, which should be limited to enable the separated charges to reach their respective electrodes.23-24 There is a compromise between strong light absorption and efficient charge transport/collection because of the relatively low charge carrier mobilities and short exciton diffusion lengths (~10 nm). Recently, most of the efficient PSCs have had active layer thicknesses ranging from 80–150 nm.18, 25-26 Despite

significant

effort

being

focused

on

PCE

improvement,

the

device

stability/degradation issues have not yet been fully resolved. The degradation stems from thermal instability of the nanostructure/morphology for BHJ layers, photooxidation of polymers, and chemical oxidation at the metal interface.4,

27-30

The PSC degradation

mechanism is rather complicated and multiple factors for degradation are combined. Therefore, critical issues affecting PSC device stability enhancement should be resolved for PSC commercialization. Of various electron-donating polymers for PSCs, poly[(4,8-bis(5-(octylthio)thiophen-2yl)benzo[1,2-b:4,5-b′]dithiophene-co-3-fluorothieno[3,4-b]thiophene-2-carboxylate] (PBDT3

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 31

TS1) has attracted keen interest because the two-dimensional structure of benzodithiophene (BDT) and thienothiophene (TT) units in the backbone and the presence of linear alkylthio chains in the BDT unit demonstrated the excellent photovoltaic properties such as broad absorption band, strong intermolecular interaction to facilitate the charge transport, and lower highest occupied molecular orbital (HOMO) energy level resulting in outstanding PCE near 10%.25-26,31-32 To date, the previous works focused on the normal-type PBDT-TS1:fullerene solar cells.25-26, 33-36 However, less attention has been paid to the performance and stability of the inverted-type PBDT-TS1:fullerene solar cells according to the varied thickness of the PBDT-TS1:fullerene layers even though the device performance and stability could be significantly influenced by the thickness of active layers.23, 29, 37-40 In this work, we fabricated the inverted-type PBDT-TS1:[6,6]-phenyl-C71-butyric acid methyl ester (PC71BM) PSCs by varying the thickness of active layers from 40 nm to 120 nm and

investigated

the

correlation

between

active

layer

thickness

and

device

performance/stability. Optimal solar cell performance was obtained with a film thickness of 80 nm because of nanoscale phase-separated percolating pathways between the PBDT-TS1 and PC71BM materials. This led to favourable charge transport and collection. Finally, device stability was tested under continuous illumination with simulated solar light (100 mW cm−2). Devices with film thicknesses of 120 nm exhibited relatively longer lifetimes due to the subtle change in surface morphology and nanostructure and a more stable in the bulk, compared to 40 and 80 nm-thick devices.

Experimental Section Materials and Solutions. PBDT-TS1 polymer (weight-average molecular weight = 28.9 kDa, polydispersity index, PDI = 2.07) and PC71BM (purity > 99%) were purchased from Orgatec 4

ACS Paragon Plus Environment

Page 5 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Materials Inc. and Nano-C, respectively. Zinc acetate dihydrate (purity > 99%) and 1,8diiodooctane (DIO) were supplied from Sigma-Aldrich. Zinc oxide precursor solutions (0.45 M) were prepared by dissolving zinc acetate dihydrate and ethanolamine in 2methoxyethanol with stirring at 60 °C for 3 h and then at room temperature before spincoating. PBDT-TS1:PC71BM (1:1.5 by weight) solutions were prepared at solid concentrations of 20, 25, and 30 mg/mL with a mixture of chlorobenzene and DIO (97:3 v/v). The resulting mixture was subjected to vigorous stirring on a magnetic stirring plate at room temperature prior to spin-coating. Thin Film and Device Fabrication. Patterned ITO-coated glass substrates were cleaned using acetone and isopropanol in an ultrasonic bath, followed by drying with a nitrogen flow. The ZnO layers (~40 nm) were spin-coated onto the ITO-coated glass substrates and baked at 200 °C for 1 h. Next, the PBDT-TS1:PC71BM solutions were spin-coated on top of the ZnO layers and dried at room temperature for 1 h inside a nitrogen-filled glove box. The active layer thickness was varied by changing both solution concentration and spin-coating speed (see Table S1). All samples were transferred into a vacuum chamber inside an argon-filled glove box. MoO3 (~10 nm) and Ag (~80 nm) were sequentially deposited on top of the BHJ layers through a shadow mask at ~3 × 10−6 torr, defining the active area of 0.055 cm2. The hole-only and electron-only devices were fabricated with ITO/PEDOT:PSS/PBDTTS1:PC71BM/MoO3/Ag and ITO/ZnO/PBDT-TS1:PC71BM/Al, respectively. Measurements. Film thicknesses were measured using a surface profiler (Alpha Step 200, Tencor Instruments). Optical absorption and PL spectra of BHJ layers with different thicknesses were measured using a UV-vis spectrophotometer (Optizen 2120, MECASYS) and a PL spectrometer (FluoroMate FS-2, SCINCO), respectively. The solar cells were characterized under calibrated AM 1.5 G illumination (at 100 mW cm−2) using a solar cell 5

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 31

measurement system equipped with a sourcemeter (Model 2400, Keithley) and a solar simulator (92250A-1000, Newport-Oriel). The EQE spectra of the solar cells were measured using an EQE measurement system equipped with a light source (tungsten-halogen lamp (150 W), ASBN-W, Spectral Products) and a monochromator (CM110, Spectral Products) controlled by the Labview program. The nanostructures of the film samples were measured using a field-emission/scanning transmission electron microscope (FE-TEM/STEM, Titan G2 ChemiSTEM Cs Probe, FEI Company). Surface morphologies of the thin films were measured using AFM (Nanoscope V Multimode 8, Bruker), while the nanostructure of the film samples was measured using a synchrotron radiation grazing incidence X-ray diffraction (GIXD) system (X-ray wavelength =1.2807 Å , incidence angle =0.12o, 3C SAXS I beamline, Pohang Accelerator Laboratory). The depth profiles of atomic distribution were measured using TOF-SIMS (TOF-SIMS 5-100, ION-TOF) with a 30 keV ion beam energy (Bi+ primary ions), a 1.07 pA ion beam current, a 100 × 100 μm2 sampling area for the analysis, an energy of 0.5 keV Cs+, and a 36 nA current over a 300 × 300 μm2 area.

RESULTS AND DISCUSSION Inverted-type PBDT-TS1:PC71BM solar cells with different film thicknesses (40, 60, 80, 100, and 120 nm) achieved by varying the solution concentration and spin-coating speed were fabricated (Fig. 1a). Based on the flat energy band diagram in Fig. 1b, we can expect that charge separation occurs at the interfaces between PBDT-TS1 and PC71BM domains. This is supported by the photoluminescence (PL) spectra of PBDT-TS1:PC71BM blend films with different thicknesses (Fig. S1). Discrete p-interfaces (BHJ–MoO3 layers) and ninterfaces (BHJ–ZnO layers) were observed from the cross-sectional focused ion beam (FIB)prepared transmission electron microscope (TEM) image for the device in Fig. 1c. It is 6

ACS Paragon Plus Environment

Page 7 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

expected that separated holes and electrons should be transported to the anode and cathode through MoO3 hole-collecting and ZnO electron-collecting buffer layers, respectively.

Figure 1

The current density-voltage (J–V) curves under illumination with simulated solar light (air mass (AM) 1.5 G, 100 mW cm−2) are shown in Fig. 2a. Open circuit voltage (VOC) values are less relevant to the active layer thickness, while short-circuit current density (JSC) values are significantly dependent on film thickness. Devices with an active layer thickness of ~80 nm exhibit the highest JSC of 17.53 mA/cm2, whereas significantly lower values are observed for 40 and 120 nm-thick devices (14.24 and 16.39 mA/cm2, respectively). For 80 nm-thick devices, the highest JSC is attributed to the relatively fast charge transport and suppressed charge recombination based on not only the lowest leakage J at reverse bias (see from −1 to 0 V for clarity), but also the relatively high forward J at 1 V from the dark J–V curve (Fig. S2). In order to gain more insight into the charge transport properties in the BHJ layers with different thicknesses, the hole and electron mobilities were extracted using the Mott-Gurney law from the space-charge-limited current (SCLC) for corresponding hole-only and electrononly devices with the different film thicknesses (Fig. 2b). The hole and electron mobilities (µ h and µ e) for the 80 nm-thick devices were 1.32 × 10−4 cm2V−1s−1 and 1.28 × 10−4 cm2V−1s−1, respectively. These results indicate that the well-balanced hole and electron transport in the 80 nm-thick devices (µ h / µ e = 1.03) can contribute to the higher JSC because of the minimized charge recombination. However, the devices with the 40 nm-thick layers exhibited relatively slow charge transport (µ h = 1.90 × 10−5 and µ e = 1.79 × 10−5 cm2V−1s−1), while the unbalanced charge transport was measured for the devices with the 120 nm-thick 7

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 31

BHJ layers (µ h / µ e = 0.67). Furthermore, the external quantum efficiency (EQE) spectra (Figs. 2c and S3a) of 80 nm-thick devices exhibit higher EQE values (> 65% at wavelengths 450– 750 nm), while the EQE values for thinner films (< 80 nm) and thicker films (> 80 nm) are relatively low (Fig. S3b) (here we note that the obtained JSC values were almost equivalent to the integration of the EQE spectra). It is noteworthy that the well-balanced charge transport for 80 nm-thick BHJ layers are beneficial to higher EQE values. However, the relatively low EQE values for the thinner films (< 80 nm) are restricted by the relatively low mobility and optical absorption. Moreover, the unbalanced charge transport for thicker films (> 80 nm) could significantly impact the relatively low EQE values despite the higher optical absorption. The JSC value trend is explained by the SCLC mobilities and EQE spectra for devices with different film thicknesses.

Figure 2

The detailed solar cell parameters are summarized in Fig. 3 and Table 1. The JSC values gradually increase with increasing PBDT-TS1:PC71BM film thickness up to 80 nm, followed by a drop with film thicknesses > 80 nm. This observation is in accordance with the inverse trend seen in the series resistance (RS). The VOC values increase with increasing film thickness up to 100 nm. Interestingly, the fill factor (FF) values marginally decrease with increasing film thicknesses up to 80 nm. This is followed by a rapid decline for devices with thicknesses > 80 nm, corresponding to the shunt resistance (RSH) trend. It is noteworthy that efficient charge transport and suppressed charge recombination can be explained by the relatively low RS and high RSH for devices with 80 nm-thick BHJ layers. Thus, the remarkable PCE improvement for devices with 80 nm-thick active layers is a result of the 8

ACS Paragon Plus Environment

Page 9 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

relatively higher JSC, VOC, and FF values (JSC = 17.53 mA/cm2, VOC = 0.768 V, FF = 66.45%, and PCE = 8.88%), which is consistent with the previous report.26, 33, 36, 41 These results show that film thickness is critical in affecting charge transport and collection, thus determining the solar cell performance.

Figure 3

To understand the relatively high PCEs for 80 nm-thick devices, the PBDT-TS1:PC71BM nanostructure was examined by high-resolution transmission electron microscopy (HRTEM) and scanning TEM (STEM). The cross-sectional TEM/STEM images show a well-defined pinterface (BHJ–MoO3 layers) without interface damage during MoO3 thermal deposition as well as the conformal coating of PBDT-TS1:PC71BM BHJ layers at the n-interface (BHJ– ZnO layers) (Fig. 4a,b). These discrete p- and n-interfaces help charge extraction from the BHJ layers to the anode and cathode, respectively. We observed bicontinuous interpenetrating networks of BHJ layers with nanoscale phase segregation, leading to efficient charge separation and transport (Fig. 4c). This observation is further confirmed by the S- and Fmapping of the STEM images (Fig. 4d) (here we note that S and F atoms refer to the PBDTTS1 polymer as seen from the chemical structure (Fig. 1a)).

Figure 4

PBDT-TS1:PC71BM solar cells with three different thicknesses (40, 80, and 120 nm) were subjected to continuous illumination with simulated solar light (100 mW cm−2) in the presence of a UV-cut filter for 6 h (as reported previously, a UV-cut filter attached to the 9

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 31

illuminating side improves device lifetime).31 The light J–V curves gradually degrade with illumination time, irrespective of film thickness (Fig. 5a). This degradation is mainly attributable to the photodegradation of the PBDT-TS1 polymer (as previously reported for poly(benzodithiophene-co-thieno[3,4-b]thiophene) (PBDTTT)-based materials in PSCs).42-46 All devices exhibited a gradual decrease in both JSC and VOC with increasing illumination time (Figs. 5b and S4). The JSC and VOC values were reduced by 10% and 5%, respectively after 6 h of illumination. However, it is interesting that the FF is more stable for 120 nm-thick devices than for 40 and 80 nm-thick devices. Here we note that after 6 h of illumination, the FF values decreased by 15, 12, and 1.5% for 40, 80, and 120 nm-thick devices, respectively. As a result, the overall PCE stability of the 120 nm-thick device is better than the 40 and 80 nm-thick devices. The different device lifetimes are presumably due to the lateral and vertical distributions of the polymer donor and fullerene acceptor components within BHJ layers because degradation occurs at the surface of the thin films and/or in the bulk layers as discussed below.

Figure 5

We first investigated the surface morphology before and after solar light illumination by employing atomic force microscopy (AFM) in order to understand the device stability trend (Fig. 6). In the case of the surface morphology of blend films before solar light illumination, the relatively large domains for the 40 nm-thick BHJ layers are shown in the phase mode AFM image, while laterally phase-separated surface morphology of the 80 and 120 nm-thick BHJ layers was observed (here we note that the lateral phase separation can be significantly influenced by the solvent drying rate and high solution concentration and low spin-coating 10

ACS Paragon Plus Environment

Page 11 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

speed can provide the sufficient time for the phase separation). Interestingly, the thin film surface for the 40 and 80-nm thick BHJ layers became smoother after 6 h illumination, based on the different root-mean-square roughness (RRMS) change (from 1.00 nm to 0.86 nm and from 0.91 nm to 0.74 nm for 40 and 80 nm-thick BHJ layers, respectively). This is evident from the relatively larger domains after illumination in the phase mode AFM images for the 40 and 80 nm-thick BHJ layers, compared with those before illumination. However, interestingly, the 120 nm-thick BHJ layers was almost marginally changed after illumination when it comes to the well-kept uniform film surface (RRMS=0.79 to 0.74 nm) and the relatively finer domains in the phase mode AFM image. Here it is noteworthy that the surface of the 120 nm-thick BHJ layers became already much smoother than that of the 40 and 80 nm-thick BHJ layers before solar light illumination.

Figure 6

However, the surface morphology itself cannot account for the device stability, so we performed the synchrotron radiation grazing incidence X-ray diffraction (GIXD) measurements for the pristine PBDT-TS1 and PTBT-TS1:PC71BM BHJ layers with different film thicknesses. The (010) peak in the out-of-plane (OOP) direction and (100) peak in the inplane (IP) direction for the PBDT-TS1 chains in the pristine PBDT-TS1 and BHJ layers were clearly observed from the 2D GIXD images (Fig. 7a) before and after illumination. Taking a closer look at the 1D profiles (Fig. 7b), the (010) peak in the OOP direction and the (100) peak in the IP direction for the 40 and 80-nm thick BHJ layers became less intense after illumination. However, the intensity of the (010) and (100) peaks after illumination for the 120-nm thick BHJ layers became comparable to that before illumination. These results 11

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 31

indicate that the nanostructure of the relatively thicker film (~120 nm) could be wellmaintained even after illumination, which is in good agreement with the relatively less change in the surface morphology for the thicker film (>80 nm) as disclosed from the AFM images. Comparing the surface morphology/nanostructure change of the BHJ layers with the device stability, the relatively thicker film (~120 nm) was more morphologically stable than the relatively thinner film (≤80nm). Hence, on the basis of the present results, it is shortly concluded that the active layer thickness can play a critical role in improving the device stability.

Figure 7

We further investigated in-depth compositional distributions of the PBDT-TS1:PC71BM films using a time-of-flight secondary ion mass spectrometry (TOF-SIMS) depth profiler. As shown in Fig. 8 and Fig. S5, sharp S− and F− peaks at the p-interface (BHJ–MoO3 layers) indicate enrichment of the PBDT-TS1 polymer formed at the film surface (p-interface) irrespective of film thickness (irrespective of solution concentration/spin-coating speed) due to the lower surface energy of the PBDT-TS1 polymer compared to PC71BM, whereas it seems that the PC71BM molecules are evenly distributed without any aggregation (note that the S− and F− signals as a function of depth refer to the PBDT-TS1 polymer). This result implies that the accumulated PBDT-TS1 polymer near the p-interface rather than in the bulk film could be inevitably photooxidised upon illumination, leading to a decrease in J SC and VOC values irrespective of film thickness. However, the relatively stable FF values for 120 nm-thick devices might be attributed to the homogeneous vertical distribution of PBDT-TS1 polymer and PC71BM for 120 nm-thick BHJ layers, compared to 40 nm-thick and 80 nm12

ACS Paragon Plus Environment

Page 13 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

thick BHJ layers. Hence, based on above characterization results, the device stability can be considerably governed by the homogeneous vertical distribution of two components in the BHJ layers.

Figure 8

CONCLUSIONS We fabricated the inverted PBDT-TS1:PC71BM solar cells with different active layer thicknesses from 40 ~ 120 nm to investigate the effect of film thickness on the device performance and stability. The highest PCE was achieved at 80 nm due to the well-balanced hole/electron transport and reduced charge recombination, as supported by the higher rectification ratio (low leakage and high forward current) and EQE values over the visible region, which are attributable to the formation of well-connected percolated pathways for each (PBDT-TS1 and PC71BM) component as evidenced by the TEM/STEM analysis. The devices with thinner BHJ layers (< 80 nm) exhibited relatively slow charge transport because of the less uniform surface morphology and the presence of pinholes, whereas unbalanced charge transport was observed for the devices with thicker films (> 120 nm). However, better device stability under continuous solar light illumination was measured for the 120 nm-thick devices with higher FF values, which can be attributed to the relatively well-maintained surface morphology/nanostructure and better morphological volume stability. Therefore, the present study highlights the importance of active layer thickness control to optimize both device performance and stability, which is of crucial for the commercialization of polymer solar cells.

13

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 31

ASSOCIATED CONTENT Supporting Information Available: Summary of solution concentration and spin-coating speed, PL spectra, dark J–V curves, EQE spectra, optical absorption spectra, changes in solar cell parameters under continuous illumination, and TOF-SIMS depth profiles accor ding to atom concentration. This material is available free of charge via the Internet at h ttp://pubs.acs.org.

ACKNOWLEDGMENTS This work was financially supported by grants from the Korean Government (NRF_2015R1A2A2A01003743, NRF_2016H1D5A1910319, NRF_2014R1A1A3051165, Human

Resource

Training

Project

for

Regional

Innovation,

MOE

and

NRF-

2014H1C1A1066748, and Basic Science Research Program_2009-0093819).

REFERENCES (1)

Angmo, D.; Larsen-Olsen, T. T.; Jørgensen, M.; Søndergaard, R. R.; Krebs, F. C., Rollto-roll inkjet printing and photonic sintering of electrodes for ITO free polymer solar cell modules and facile product integration. Adv. Energy Mater. 2013, 3, 172-175, DOI: 10.1002/aenm.201200520.

(2)

Lu, L.; Zheng, T.; Wu, Q.; Schneider, A. M.; Zhao, D.; Yu, L., Recent advances in bulk heterojunction polymer solar cells. Chem. Rev. 2015, 115, 12666-12731, DOI: 10.1021/acs.chemrev.5b00098.

(3)

Zhou, H.; Yang, L.; You, W., Rational design of high performance conjugated polymers 14

ACS Paragon Plus Environment

Page 15 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

for organic solar cells. Macromolecules 2012, 45, 607-632, DOI: 10.1021/ma201648t. (4)

Gevorgyan, S. A.; Madsen, M. V.; Roth, B.; Corazza, M.; Hösel, M.; Søndergaard, R. R.; Jørgensen, M.; Krebs, F. C., Lifetime of organic photovoltaics: Status and predictions. Adv. Energy Mater. 2016, 6, 1501208, DOI: 10.1002/aenm.201501208.

(5)

Facchetti, A., Polymer donor–polymer acceptor (all-polymer) solar cells. Mater. Today 2013, 16, 123-132, DOI: 10.1016/j.mattod.2013.04.005.

(6)

Hong, S.; Kang, H.; Kim, G.; Lee, S.; Kim, S.; Lee, J. H.; Lee, J.; Yi, M.; Kim, J.; Back, H.; Kim, J. R.; Lee, K., A series connection architecture for large-area organic photovoltaic modules with a 7.5% module efficiency. Nat. Commun. 2016, 7, 10279, DOI: 10.1038/ncomms10279.

(7)

Li, S.; Ye, L.; Zhao, W.; Zhang, S.; Mukherjee, S.; Ade, H.; Hou, J., Energy-level modulation of small-molecule electron acceptors to achieve over 12% efficiency in polymer solar cells. Adv. Mater. 2016, 28, 9423-9429, DOI: 10.1002/adma.201602776.

(8)

Zhao, J.; Li, Y.; Yang, G.; Jiang, K.; Lin, H.; Ade, H.; Ma, W.; Yan, H., Efficient organic solar cells processed from hydrocarbon solvents. Nat. Energy 2016, 1, 15027, DOI: 10.1038/nenergy.2015.27.

(9)

Wan, Q.; Guo, X.; Wang, Z.; Li, W.; Guo, B.; Ma, W.; Zhang, M.; Li, Y., 10.8% efficiency polymer solar cells based on PTB7-Th and PC71BM via binary solvent additives

treatment.

Adv.

Funct.

Mater.

2016,

26,

6635-6640,

DOI:

10.1002/adfm.201602181. (10) Baran, D.; Ashraf, R. S.; Hanifi, D. A.; Abdelsamie, M.; Gasparini, N.; Rohr, J. A.; Holliday, S.; Wadsworth, A.; Lockett, S.; Neophytou, M.; Emmott, C. J.; Nelson, J.; Brabec, C. J.; Amassian, A.; Salleo, A.; Kirchartz, T.; Durrant, J. R.; McCulloch, I., Reducing the efficiency-stability-cost gap of organic photovoltaics with highly efficient 15

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 31

and stable small molecule acceptor ternary solar cells. Nat. Mater. 2017, 16, 363-369, DOI: 10.1038/nmat4797. (11) Kim, Y.; Cook, S.; Tuladhar, S. M.; Choulis, S. A.; Nelson, J.; Durrant, J. R.; Bradley, D. D. C.; Giles, M.; McCulloch, I.; Ha, C.-S.; Ree, M., A strong regioregularity effect in self-organizing conjugated polymer films and high-efficiency polythiophene:fullerene solar cells. Nat. Mater. 2006, 5, 197-203, DOI:10.1038/nmat1574. (12) Li, G.; Shrotriya, V.; Huang, J.; Yao, Y.; Moriarty, T.; Emery, K.; Yang, Y., Highefficiency solution processable polymer photovoltaic cells by self-organization of polymer blends. Nat. Mater. 2005, 4, 864-868, DOI:10.1038/nmat1500. (13) Shin, M.; Kim, H.; Park, J.; Nam, S.; Heo, K.; Ree, M.; Ha, C.-S.; Kim, Y., Abrupt morphology change upon thermal annealing in poly(3-hexylthiophene)/soluble fullerene blend films for polymer solar cells. Adv. Funct. Mater. 2010, 20, 748-754, DOI: 10.1002/adfm.200901655. (14) Dang, M. T.; Hirsch, L.; Wantz, G.; Wuest, J. D., Controlling the morphology and performance of bulk heterojunctions in solar cells. Lessons learned from the benchmark poly(3-hexylthiophene):[6,6]-phenyl-c61-butyric acid methyl ester system. Chem. Rev. 2013, 113, 3734-3765, DOI: 10.1021/cr300005u. (15) Peet, J.; Kim, J. Y.; Coates, N. E.; Ma, W. L.; Moses, D.; Heeger, A. J.; Bazan, G. C., Efficiency enhancement in low-bandgap polymer solar cells by processing with alkane dithiols. Nat. Mater. 2007, 6, 497-500, DOI:10.1038/nmat1928. (16) Li, G.; Chu, C. W.; Shrotriya, V.; Huang, J.; Yang, Y., Efficient inverted polymer solar cells. Appl. Phys. Lett. 2006, 88, 253503, DOI: 10.1063/1.2212270. (17) Nam, S.; Seo, J.; Han, H.; Kim, H.; Hahm, S. G.; Ree, M.; Gal, Y.-S.; Anthopoulos, T. D.; Bradley, D. D. C.; Kim, Y., >10% efficiency polymer:Fullerene solar cells with 16

ACS Paragon Plus Environment

Page 17 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

polyacetylene-based polyelectrolyte interlayers. Adv. Mater. Interfaces 2016, 3, 1600415, DOI: 10.1002/admi.201600415. (18) Nam, S.; Seo, J.; Woo, S.; Kim, W. H.; Kim, H.; Bradley, D. D.; Kim, Y., Inverted polymer fullerene solar cells exceeding 10% efficiency with poly(2-ethyl-2-oxazoline) nanodots on electron-collecting buffer layers. Nat. Commun. 2015, 6, 8929, DOI: 10.1038/ncomms9929. (19) Hedley, G. J.; Ruseckas, A.; Samuel, I. D., Light harvesting for organic photovoltaics. Chem. Rev. 2017, 117, 796-837, DOI: 10.1021/acs.chemrev.6b00215. (20) Heeger, A. J., 25th anniversary article: Bulk heterojunction solar cells: Understanding the

mechanism

of

operation.

Adv.

Mater.

2014,

26,

10-27,

DOI:

10.1002/adma.201304373. (21) Stoltzfus, D. M.; Donaghey, J. E.; Armin, A.; Shaw, P. E.; Burn, P. L.; Meredith, P., Charge generation pathways in organic solar cells: Assessing the contribution from the electron

acceptor.

Chem.

Rev.

2016,

116,

12920-12955,

DOI:

10.1021/acs.chemrev.6b00126. (22) Rumer, J. W.; McCulloch, I., Organic photovoltaics: Crosslinking for optimal morphology

and

stability.

Mater.

Today

2015,

18,

425-435,

DOI:

10.1016/j.mattod.2015.04.00. (23) Sievers, D. W.; Shrotriya, V.; Yang, Y., Modeling optical effects and thickness dependent current in polymer bulk-heterojunction solar cells. J. Appl. Phys. 2006, 100, 114509, DOI: 10.1063/1.2388854. (24) Kirchartz, T.; Agostinelli, T.; Campoy-Quiles, M.; Gong, W.; Nelson, J., Understanding the thickness-dependent performance of organic bulk heterojunction solar cells: The influence of mobility, lifetime, and space charge. J. Phys. Chem. Lett. 2012, 3, 347017

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 31

3475, DOI: 10.1021/jz301639y. (25) Yao, H.; Zhao, W.; Zheng, Z.; Cui, Y.; Zhang, J.; Wei, Z.; Hou, J., PBDT-TSR: A highly efficient conjugated polymer for polymer solar cells with a regioregular structure. J. Mater. Chem. A 2016, 4, 1708-1713, DOI: 10.1039/C5TA08614K. (26) Ye, L.; Zhang, S.; Zhao, W.; Yao, H.; Hou, J., Highly efficient 2D-conjugated benzodithiophene-based photovoltaic polymer with linear alkylthio side chain. Chem. Mater. 2014, 26, 3603-3605, DOI: 10.1021/cm501513n. (27) Mateker, W. R.; McGehee, M. D., Progress in understanding degradation mechanisms and improving stability in organic photovoltaics. Adv. Mater. 2017, 29, 1603940, DOI: 10.1002/adma.201603940. (28) Lee, J. U.; Jung, J. W.; Jo, J. W.; Jo, W. H., Degradation and stability of polymer-based solar cells. J. Mater. Chem. 2012, 22, 24265–24283, DOI: 10.1039/C2JM33645F. (29) Tournebize, A.; Seck, M.; Vincze, A.; Distler, A.; Egelhaaf, H.-J.; Brabec, C. J.; Rivaton, A.; Peisert, H.; Chassé, T., Photodegradation of Si-PCPDTBT:PCBM active layer for organic solar cells applications: A surface and bulk investigation. Sol. Energy Mater. Sol. Cells 2016, 155, 323-330, DOI: 10.1016/j.solmat.2016.06.026. (30) Tromholt, T.; Madsen, M. V.; Carlé, J. E.; Helgesen, M.; Krebs, F. C., Photochemical stability of conjugated polymers, electron acceptors and blends for polymer solar cells resolved in terms of film thickness and absorbance. J. Mater. Chem. 2012, 22, 75927601, DOI: 10.1039/C2JM16340C. (31) Ye, L.; Sun, K.; Jiang, W.; Zhang, S.; Zhao, W.; Yao, H.; Wang, Z.; Hou, J., Enhanced efficiency in fullerene-free polymer solar cell by incorporating fine-designed donor and acceptor materials. ACS Appl. Mater. Interfaces 2015, 7, 9274-9280, DOI: 10.1021/acsami.5b02012. 18

ACS Paragon Plus Environment

Page 19 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(32) Li, S.; Zhang, H.; Zhao, W.; Ye, L.; Yao, H.; Yang, B.; Zhang, S.; Hou, J., Greensolvent-processed all-polymer solar cells containing a perylene diimide-based acceptor with an efficiency over 6.5%. Adv. Energy Mater. 2016, 6, 1501991, DOI: 10.1002/aenm.201501991. (33) Xu, B.; Zheng, Z.; Zhao, K.; Hou, J., A bifunctional interlayer material for modifying both the anode and cathode in highly efficient polymer solar cells. Adv. Mater. 2016, 28, 434-439, DOI: 10.1002/adma.201502989. (34) Zhang, H.; Yao, H.; Zhao, W.; Ye, L.; Hou, J., High-efficiency polymer solar cells enabled by environment-friendly single-solvent processing. Adv. Energy Mater. 2016, 6, 1502177, DOI: 10.1002/aenm.201502177. (35) Zhang, S.; Uddin, M. A.; Zhao, W.; Ye, L.; Woo, H. Y.; Liu, D.; Yang, B.; Yao, H.; Cui, Y.; Hou, J., Optimization of side chains in alkylthiothiophene-substituted benzo[1,2b:4,5-b′]dithiophene-based photovoltaic polymers. Polym. Chem. 2015, 6, 2752-2760, DOI: 10.1039/C5PY00071H. (36) Zhang, M.; Zhang, F.; Wang, J.; An, Q.; Sun, Q., Efficient ternary polymer solar cells with a parallel-linkage structure. J. Mater. Chem. C 2015, 3, 11930-11936, DOI: 10.1039/C5TC03019F. (37) Namkoong, G.; Kong, J.; Samson, M.; Hwang, I.-W.; Lee, K., Active layer thickness effect on the recombination process of PCDTBT:PC71bm organic solar cells. Org. Electron. 2013, 14, 74-79, DOI: 10.1016/j.orgel.2012.10.025. (38) Moulé, A. J.; Bonekamp, J. B.; Meerholz, K., The effect of active layer thickness and composition on the performance of bulk-heterojunction solar cells. J. Appl. Phys. 2006, 100, 094503, DOI: 10.1063/1.2360780. 19

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 31

(39) Tromholt, T.; Madsen, M. V.; Carlé, J. E.; Helgesen, M.; Krebs, F. C., Photochemical stability of conjugated polymers, electron acceptors and blends for polymer solar cells resolved in terms of film thickness and absorbance. J. Mater. Chem. 2012, 22, 75927601, DOI: 10.1039/C2JM16340C. (40) Kirchartz, T.; Agostinelli, T.; Campoy-Quiles, M.; Gong, W.; Nelson, J., Understanding the thickness-dependent performance of organic bulk heterojunction solar cells: The influence of mobility, lifetime, and space charge. J. Phys. Chem. Lett. 2012, 3, 34703475, DOI: 10.1021/jz301639y. (41) Zhao, K.; Ye, L.; Zhao, W.; Zhang, S.; Yao, H.; Xu, B.; Sun, M.; Hou, J., Enhanced efficiency of polymer photovoltaic cells via the incorporation of a water-soluble naphthalene diimide derivative as a cathode interlayer. J. Mater. Chem. C 2015, 3, 9565-9571, DOI: 10.1039/C5TC02172C. (42) Alem, S.; Wakim, S.; Lu, J.; Robertson, G.; Ding, J.; Tao, Y., Degradation mechanism of benzodithiophene-based conjugated polymers when exposed to light in air. ACS Appl. Mater. Interfaces 2012, 4, 2993-2998, DOI: 10.1021/am300362b. (43) Jeong, J.; Seo, J.; Nam, S.; Han, H.; Kim, H.; Anthopoulos, T. D.; Bradley, D. D.; Kim, Y., Significant stability enhancement in high-efficiency polymer:fullerene bulk heterojunction solar cells by blocking ultraviolet photons from solar light. Adv. Sci. 2016, 3, 1500269, DOI: 10.1002/advs.201500269. (44) Nam, S.; Woo, S.; Seo, J.; Kim, W. H.; Kim, H.; McNeill, C. R.; Shin, T. J.; Bradley, D. D.; Kim, Y., Pronounced cosolvent effects in polymer:Polymer bulk heterojunction solar cells with sulfur-rich electron-donating and imide-containing electron-accepting polymers.

ACS

Appl.

Mater.

Interfaces

2015,

7,

15995-16002,

DOI:

10.1021/acsami.5b04224. 20

ACS Paragon Plus Environment

Page 21 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(45) Razzell-Hollis, J.; Wade, J.; Tsoi, W. C.; Soon, Y.; Durrant, J.; Kim, J.-S., Photochemical stability of high efficiency PTB7:PC70BM solar cell blends. J. Mater. Chem. A 2014, 2, 20189-20195, DOI: 10.1039/C4TA05641H. (46) Tremolet de Villers, B. J.; O’Hara, K. A.; Ostrowski, D. P.; Biddle, P. H.; Shaheen, S. E.; Chabinyc, M. L.; Olson, D. C.; Kopidakis, N., Removal of residual diiodooctane improves photostability of high-performance organic solar cell polymers. Chem. Mater. 2016, 28, 876-884, DOI: 10.1021/acs.chemmater.5b04346.

21

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 31

Table 1. Summary of solar cell performances according to the thickness (t) of BHJ layers (all data were extracted from the light J–V curves for > 12 devices). t

JSC

VOC

FF

PCE

RS

RSH

(nm)

(mA/cm2)

(V)

(%)

(%)

(kΩ∙cm2)

(kΩ∙cm2)

40

14.24±0.44

0.755±0.006

67.08±0.49

7.21±0.16

0.095±0.006

14.48±3.26

60

15.80±0.36

0.760±0.005

66.48±0.79

7.98±0.13

0.090±0.005

13.20±1.83

80

17.53±0.23

0.763±0.005

66.45±1.07

8.88±0.09

0.080±0.005

12.71±2.99

100

17.33±0.31

0.768±0.005

60.85±0.68

8.09±0.18

0.123±0.005

10.15±3.10

120

16.39±0.17

0.758±0.005

57.98±0.34

7.20±0.08

0.145±0.006

8.11±1.97

22

ACS Paragon Plus Environment

Page 23 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Figure 1. (a) Chemical structure of materials and device structure for inverted polymer solar cells with the PBDT-TS1:PC71BM BHJ layer. (b) Flat energy band diagram and (c) crosssectional FIB-prepared TEM image for the inverted polymer solar cells with the PBDTTS1:PC71BM layers: note that p-interface between BHJ and MoO3 layers and n-interface between BHJ and ZnO layers can be made in the present devices.

23

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 31

Figure 2. (a) Current density–voltage (J–V) curves for the inverted PBDT-TS1:PC71BM solar cells according to different film thicknesses (40, 60, 80, 100, and 120 nm) under one-sun condition (AM 1.5 G, 100 mW cm−2). (b) Hole and electron mobilities for the BHJ layers with different film thicknesses of 40, 80, and 120 nm, which were extracted from the spacecharge-limited currents of hole-only and electron-only devices. (c) EQE spectra of the inverted PBDT-TS1:PC71BM solar cells and (d) optical absorption spectra of the BHJ layers with different film thicknesses of 40, 80, and 120 nm. The inset shows corresponding photographs for the PBDT-TS1:PC71BM films.

24

ACS Paragon Plus Environment

Page 25 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Figure 3. Solar cell parameters (JSC, VOC, FF, PCE, RS, and RSH) as a function of the BHJ (PBDT-TS1:PC71BM) film thickness (all data were taken from the light J–V curves with error bars for > 12 devices).

25

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 26 of 31

Figure 4. (a) HRTEM and (b) STEM images for the device cross-section parts prepared by the FIB process. (c) HRTEM and (d, e) STEM images for the 80 nm-thick PBDTTS1:PC71BM BHJ layers coated onto glass substrates (S and F atoms refer to the PBDT-TS1 polymer as seen from the chemical structure in Fig. 1a).

26

ACS Paragon Plus Environment

Page 27 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Figure 5. (a) Light J–V curves for the PBDT-TS1:PC71BM solar cells with different film thicknesses of 40, 80, and 120 nm under continuous one-sun condition (AM 1.5 G, 100 mW cm−2) for 6 h with a UV-cut filter. (b) Normalized JSC, VOC, FF, and PCE as a function of the light exposure time under one-sun condition for the PBDT-TS1:PC71BM solar cells with different film thicknesses of 40, 80, and 120 nm (all data were taken from the light J–V curves with error bars for > 4 devices).

27

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 28 of 31

Figure 6. (a) 2D GIXD images and (b) 1D GIXD profiles for the pristine PBDT-TS1 and BHJ layers coated on the ZnO layers with different film thicknesses of 40, 80, and 120 nm before and after continuous solar light illumination with one sun (100 mW/cm2) for 6 h.

28

ACS Paragon Plus Environment

Page 29 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Figure 7. 3D height-mode AFM images (2D phase mode: upper right) for the BHJ layers coated on the ZnO layers with different film thicknesses before and after continuous solar light illumination with one sun (100 mW/cm2) for 6 h: (a) 40 nm, (b) 80 nm, and (c) 120 nm.

29

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 30 of 31

Figure 8. TOF-SIMS depth profiles for the PBDT-TS1:PC71BM BHJ layers with different film thicknesses of 40, 80, and 120 nm (S and F atoms exist solely in the PBDT-TS1 polymer as seen from the chemical structure in Fig. 1).

30

ACS Paragon Plus Environment

Page 31 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

For Table of Contents Use Only:

Brief Synopsis: The 80 nm-thick BHJ layers delivered the highest efficiency of polymer:fullerene solar cells with alkylthiothiophene-containing polymer, while the thicker (120 nm) BHJ layers secured better device stability.