Ti3C2 MXene Composites for

May 17, 2019 - ... of Sciences and Technology (NUST) , Islamabad 44000 , Pakistan ... and Petroleum Engineering, United Arab Emirates University (UAEU...
0 downloads 0 Views 2MB Size
Download PDF
This is an open access article published under an ACS AuthorChoice License, which permits copying and redistribution of the article or any adaptations for non-commercial purposes.

Article Cite This: ACS Omega 2019, 4, 8661−8668

http://pubs.acs.org/journal/acsodf

La- and Mn-Codoped Bismuth Ferrite/Ti3C2 MXene Composites for Efficient Photocatalytic Degradation of Congo Red Dye M. Abdullah Iqbal,† S. Irfan Ali,‡,§ Faheem Amin,† Ayesha Tariq,† Muhammad Z. Iqbal,∥ and Syed Rizwan*,†

ACS Omega 2019.4:8661-8668. Downloaded from pubs.acs.org by 5.101.217.114 on 05/17/19. For personal use only.

†

Physics Characterization and Simulations Lab, Department of Physics, School of Natural Sciences (SNS), National University of Sciences and Technology (NUST), Islamabad 44000, Pakistan ‡ Shenzhen Key Laboratory of Advanced Thin Films and Applications, College of Physics and Energy, and §Key Laboratory of Optoelectronic Devices and Systems of Ministry of Education and Guangdong Province, College of Optoelectronic Engineering, Shenzhen University, Shenzhen 518060, China ∥ Department of Chemical and Petroleum Engineering, United Arab Emirates University (UAEU), P.O. Box 15551, Al-Ain, United Arab Emirates ABSTRACT: Over the years, scarcity of fresh potable water has increased the demand for clean water. Meanwhile, with the advent of nanotechnology, the use of nanomaterials for photocatalytic degradation of pollutants in wastewaters has increased. Herein, a new type of nanohybrids of La- and Mn-codoped bismuth ferrite (BFO) nanoparticles embedded into transitionmetal carbide sheets (MXene−Ti3C2) were prepared by a low-cost doublesolvent sol−gel method and investigated for their catalytic activity in dark and photoinduced conditions. The photoluminescence results showed that pure BFO has the highest electron hole recombination rate as compared to all the codoped BFO/Ti3C2 nanohybrids. The higher electron−hole pair generation rate of the nanohybrids provides a suitable environment for fast degradation of organic dye molecules. The band gap of the prepared nanohybrid was tuned to 1.73 eV. Moreover, the BLFO/Ti3C2 and BLFMO-5/Ti3C2 degraded 92 and 93% of the organic pollutant, respectively, from water in dark and remaining in the light spectrum. Therefore, these synthesized nanohybrids could be a promising candidate for catalytic and photocatalytic applications in future.

1. INTRODUCTION With increasing population and global industrialization, potential risks associated with contaminating potable water streams have increased tremendously. Different coloring industries discharge various kinds of organic dyes into the freshwater streams, consequently generating wastewaters. With the increasing demand of potable water, these organic coloring substances must be treated in order to make water safe to drink. Congo red (CR) is a sodium salt of benzidinediazo-bis1-naphthylamine-4-sulfonic acid.1 In this study, CR has been selected because of its anionic structure and severe environmental issues. A large number of industries such as textiles, printing, dyeing, paper, and plastic produce CR effluents which can contaminate the freshwater supply.1,2 If metabolized, CR can turn into benzide, a well-known human carcinogen.3 The treatment of CR-contaminated wastewater may also be complicated because of the complex aromatic structure, which resists degradation. Several physical, chemical, and biological methods qualify for the treatment of colored waters. These methods include adsorption,4−7 reverse osmosis,8 coagulation,9,10 biological,11 and photochemical degradation12 of organic dyes in water. Photocatalysis (photochemical degradation) is a low-cost treatment method that uses catalysts in order to accelerate degradation of organic dyes using sunlight. A class of © 2019 American Chemical Society

photocatalysts called semiconductor photocatalysts have also been reported for effective degradation of organic compounds in water.12 Over the years, several semiconductor particles such as TiO2 and ZnO2 were reported for photocatalysis.12,13 However, these materials exhibited lower photocatalytic activity attributed to wide band gaps (∼3.2 eV for TiO2 under visible light). Many heterogeneous and hierarchical photocatalysts were reported previously for degradation of different dyes such as CR, methyl orange (MO), cyanide, rhodamine B (RhB), p-chlorophenol, norfloxacin, and phenol. As the UV and visible lights constitute 3−5 and 43% of the solar light spectrum, respectively,13−16 developing new catalysts for visible light photocatalysis are of great interests. In semiconducting materials, bismuth ferrites, BiFeO3 (called BFO hereafter), have shown promising results for photocatalysis using visible light irradiation attributed to their narrow band gap (∼2.2 eV).17−19 The band gap in BFOs can be further improved by doping with other ions,18,20 which alternatively improves its photocatalytic activity under the visible light irradiation. At room temperature, BFOs exhibit rhombohedrally distorted perovskite structure (R3c),21 with Received: February 21, 2019 Accepted: April 16, 2019 Published: May 17, 2019 8661

DOI: 10.1021/acsomega.9b00493 ACS Omega 2019, 4, 8661−8668

ACS Omega

Article

lattice parameters arh = 3.965Å and rhombohedral angle of αrh = 89.3°−89.4°.22 In hexagonal space, the hexagonal lattice parameters of BFOs are ahex = 5.58 Å and chex = 13.90 Å.23,24 Doping BFOs with other metallic atoms such a lanthanum (La) and manganese (Mn) not only affects the lattice structure of BFOs25,26 but also improves magnetoelectric coupling.27−29 La- and Mn-doped BFO shows a mesoporous network with more internal surface area and higher photocatalytic activity compared to a nonporous pure BFO system. La doping into BFO tuned the band gap from 2.08 to 2.04 eV, whereas Mn doping on Fe sites showed a large band gap tunability: the band gap was tuned up to 1.49 eV and increased the surface area.30−32 The codoped BFOs have revealed improved photocatalytic activity,33,34 which is required to degrade pollutants such as organic dyes in wastewater under UV and visible light irradiation.19,33,34 The nanocomposites of BFOs with graphene derivatives and metal-codoped BFOs have shown improved photocatalytic activity.20,35 With the discovery of graphene in 2004, a twodimensional (2D) sheet of sp2-hybridized carbon atoms, a new era has emerged with the drive to discover unique 2D materials. Several new 2D materials have been proposed to serve for a large number of potential applications.36−38 These 2D materials gained enormous attention because of their very high surface area and electronic properties compared to their bulk counterparts. Largely studied 2D materials include graphene,39,40 boron nitride,41−43 and transition-metal dichalcogenides,44,45 which are essentially derived from 3D layered materials. Recently, a new 2D layered material composed of transition-metal carbides and carbonitrides, also called as MXenes, has attracted considerable attention from the research community.46−49 MXenes are represented by the general formula Mn+1XnTx (n = 1−3), where M stands for an early transition metal such as Ti, Cr, and Mo; X is either carbon or nitrogen; and T represents surface functionality such as −O, −OH, and/or −F. The first reported MXene was Ti3C2Tx, which further led to the synthesis of additional 19 potentially important but different variations in the MXene family. MXenes are considered significant for applications in nanoelectronic devices and catalysis in future.46−49 There have been a few reports on photochemical degradation of organic pollutants using BFOs. For example, Soltani and Lee reported the photocatalytic degradation of aqueous bisphenol A using nanohybrids of BiFeO3/reduced graphene oxide (rGO) nanohybrids.50 A complete degradation of bisphenol A was observed in 70 min under the visible light irradiation. Wang et al. also reported a complete degradation of bisphenol A using Bi25FeO40/rGO nanocomposites in 180 min under similar irradiation.51 Dai et al.52 reported a very low degradation of MO (50% degradation) in 6 h using BiFeO3/ GO nanohybrid. In this study, we reported the synthesis of a highly efficient nanohybrid from lanthanum (La)- and manganese (Mn)-codoped bismuth ferrite (BiFeO3) abbreviated as BFO nanoparticles embedded into transition-metal carbide sheets (MXene−Ti3C2) and investigated for their catalytic activity against CR under dark and visible light conditions. The nanohybrids were synthesized by a low-cost double-solvent sol−gel method. The microstructures, surface morphology, and electronic properties of the nanohybrids were studied using X-ray diffraction (XRD), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS), respectively. The charge carrier recombination rate of nanohybrids was measured using photoluminescence (PL)

technique. The MXene−Ti3C2 attachment and codoping of BFOs provided a suitable environment for fast degradation of CR. A high degradation rate of CR (∼92%) was observed.

2. RESULTS AND DISCUSSIONS 2.1. Structure and Morphology of Nanohybrids. X-ray diffractometer was used to study the phase morphology of the synthesized nanohybrids. The doped BFO nanohybrids defined as, Bi0.9La0.1FeO3 (BLFO), Bi0.9La0.1Fe0.95Mn0.05O3 (BLFMO-5), Bi 0. 9 La 0 . 1 Fe 0 . 90 Mn 0. 1 0 O 3 (BLFMO-10), Bi0.9La0.1Fe0.80Mn0.20O3 (BLFMO-20), and Bi0.9La0.1Fe0.75Mn0.25O3 (BLFMO-25) with Ti3C2−MXene, were synthesized. The microstructure of nanohybrids was studied using XRD (Figure 1). The pure BFO matches the

Figure 1. (a) XRD patterns of Bi1−xLaxFe1−yMnyO3 (x = 0.1, y = 0.0, 0.05, 0.10, 0.20, and 0.25)/Ti3C2−MXene nanohybrids and (b) magnified patterns ranging from 30° to 34°.

JCPDS card no. 20-0169 for BiFeO3 structure. All diffraction peaks were indexed as rhombohedral, corresponding to (012), (104), (110), (006), (202), (024), (116), (112), (018), and (214) reflections. The doublet peak at 32° merged into a single peak showing structural transformation from rhombohedral to orthorhombic. La and Mn doping causes the diffraction peaks to vanish, related to planes (006) and (018). Overall, the peaks shifted toward right for Bi1−xLaxFe1−yMnyO3 compared to that in pure BFO. However, the dual diffraction peaks of planes (104) and (110) occurring at 2θ = 31.6° and 32.01° were reduced in intensity and merged as the concentration of Mn was increased in BLFO as shown in Figure 1b, a similar trend was observed elsewhere.1,30 The average particle sizes were calculated using Scherrer’s formula53 D = kλ/β cos θ, where D = crystallite size, k = Debye constant, λ = wavelength of X-ray, and β = fwhm. For pure BFO, BLFO, BLFMO-5, BLFMO-10, BLFMO-20, and BLFMO-25, the average particle sizes are 46.32, 33.89, 27.68, 26.65, 22.96, and 30.15 nm respectively. There was a reduction in average particle size from pure BFO up to BLFMO-20 as Mn doping increased; however, larger particles were observed for BLFMO-25. The surface morphology of hybrids (Bi1−xLaxFe1−yMyO3/ Ti3C2) was studied using SEM (Figure 2). In BLFO/Ti3C2 nanohybrids (Figure 2a), the only dopant is the La, where the dopants are La and Mn as in BLFMO (Figure 2b−e). MXene (Ti3C2) showed a sheetlike structure observed in all microimages where the sheets were ∼1−1.5 μm wide and 2−3 μm in the lateral dimensions. The nanoparticles (codoped BFO particles (Bi1−xLaxFe1−yMyO3)) were embedded on the surfaces of Ti3C2 sheets. Despite improved catalytic activity (later), there was no regular pattern of the distribution of nanoparticles on Ti3C2 sheets observed in SEM images. Briefly, 8662

DOI: 10.1021/acsomega.9b00493 ACS Omega 2019, 4, 8661−8668

ACS Omega

Article

PL spectrum indicates a lower electron−hole recombination rate and consequently high photocatalytic activity of the material. The opposite is true for the high-intensity peak observed in PL spectra. A very low PL peak was observed for BLFO/Ti3C2 nanohybrids. Also, the electron−hole recombination rate was lower for all BLFMO/Ti3C2 nanohybrids compared to that of pure BFO particles, which is attributed to enhanced surface area and larger active points present on Ti3C2 sheets. Increasing the concentration of Mn doping lowered the recombination rate significantly, bringing it almost similar to that of the BLFO/Ti3C2 nanohybrid level. The radicals produced in BLFMO/Ti3C2 nanohybrids are due to activation of nanoparticles. The generation of electron− hole pairs, as the light falls, at first excites the electrons from valence band to the conduction band (CB). The CB of semiconductors has more than one energy band. Liqiang et al. explained the dependence of photocatalytic activity on the PL spectra of semiconductor materials.54 The working mechanism of hybrid is such that the charge carriers produced are suddenly spread over the Ti3C2 sheets occupying the larger areas of the Ti3C2 sheets. The charge carriers spread on the sheets further significantly enhance the surface redox reactions of the Ti3C2 sheets. The BLFMO/Ti3C2 nanohybrids have higher surface areas compared to neat BFO nanoparticles. Attaching BFO particles on MXene surface along with doping has significantly lowered the recombination rate of charge carriers and a higher surface area of the nanohybrids is expected. These results are in agreement with previous reports on BFO/graphene nanohybrids where higher surface area and higher photogeneration/lower recombination rate were observed, providing the higher photocatalytic activity.50−52,55 2.2. X-ray Photoelectron Spectroscopy. XPS analysis is used to check the chemical composition and binding energies of different elements present in the synthesized hybrid structure. Figure 4 shows the XPS analysis of the prepared nanohybrid (BLFMO-5/Ti3C2). In order to confirm the newly proposed nanohybrids, the XPS survey scans were conducted on a represented sample of BLFMO-5/Ti3C2 containing La and Mn doping. Survey scans (Figure 4a) indicated the presence of Bi, Fe, O, Ti, La, Mn, and C with their respective binding energies in the synthesized BLFMO-5/Ti3C2 nanohybrid. A very small signal attributed to La was detected at about binding energy (BE) 840 eV. Mn peak is attributed to BE 682 eV, while Bi and O shows intense peaks at 159 and 531 eV, respectively, which are explained in the discussion later. The high-resolution scans were also performed for Bi, Fe, O, and C in codoped nanohybrids shown in Figure 4b−e. The high-resolution XPS scan for Bi 4f was in the BE range of 156− 167 eV (Figure 4b). Two sharp peaks were observed: BE ≈ 158.9 and 164.2 eV, representing Bi 4f7/2 and Bi 4f5/2, respectively. Further stating, Bi is in the Bi3+ oxidation state.31 Figure 4c shows the high-resolution spectrum for Fe over BE range of 707−728 eV. Similar to Bi spectrum, two peaks were observed at 710.7 and 724.4 eV, attributed to Fe 2p3/2 and Fe 2p1/2, indicating the formation of Fe2+ ions; in a previous report, Fe 2p3/2 and Fe 2p1/2 peaks of pure BFO were at 714.5 and 728 eV, respectively, and due to La doping Fe 2p3/2 shifted to lower BE near to 710 eV.31,56,57 More oxygen vacancies should be produced because of the presence of Fe ions of such valence states on the surface of BFO, which enhances the surface adsorption of the organic and oxygen species on the BFO surface.58,59 Figure 4d represents high-resolution O1 spectrum. The photocatalytic mechanism is a series of redox

Figure 2. SEM images of (a) BLFO/Ti3C2, (b) BLFMO-5/Ti3C2, (c) BLFMO-10/Ti3C2, (d) BLFMO-20/Ti3C2, and (e) BLFMO-25/ Ti3C2.

the BLFO particles (Figure 1a) formed a coagulated structure on the Ti3C2 sheets with approximately 0.8 μm cluster size. In BLFMO/Ti3C2 nanohybrids, Mn concentration was increased, which further reduced the distribution of BLFMO particles on Ti3C2 sheets, and some sheets had lesser attached particles. In addition, the average nanoparticle size (from XRD) ranged 22−33 nm, whereas SEM showed large clustering of the nanoparticles. There were a few grains which were not nucleated and observed distributed over the sheets. The BLFO/Ti3C2 nanohybrid exhibited a uniform growth of the BFO nanoparticles compared to the BLFMO/Ti3C2 samples with Mn doping (Figure 2b−e). Figure 3 shows the PL spectra of the Bi1−xLaxFe1−yMnyO3/ Ti 3 C 2 nanohybrids. All the samples of pure BFO, Bi1−xLaxFe1−yMyO3/Ti3C2, were tested for the PL spectra. Considering the PL peaks showing the recombination rate of the separated charge carriers, the pure BFO showed the highest electron hole recombination rate as compared to all the codoped BFO/Ti3C2 nanohybrids. A low-intensity peak in the

Figure 3. PL spectra of pure BFO and Bi1−xLaxFe1−yMyO3/Ti3C2− MXene nanohybrids. 8663

DOI: 10.1021/acsomega.9b00493 ACS Omega 2019, 4, 8661−8668

ACS Omega

Article

Figure 5. Tauc plot of BLFMO-20/Ti3C2−MXene from DR-UV spectroscopy.

onset of the decrease, which may be attributed to a small amount of impurity phases.12,35 The narrowing of the band gap in nanohybrids in comparison with bare BFO nanoparticles can be explained through the formation of Fe−O−C bonds at the surface of BLFM, which reduces the charge transfer from oxygen ion to Fe ions.35 Analogous band gap narrowing was observed in literature for graphene/BiFeO3 nanohybrids.65 The superior band gap narrowing of BLFO/Ti3C2 is indicative of better coupling of the BLFO nanoparticles and Ti3C2 sheets, which was illustrated through SEM images. 2.4. Catalytic Degradation. O2 and OH radicals on the organic matter help in the degradation of the organic pollutants. These highly active radicals start degrading the organic pollutants present in the water solution and in turn reduce to harmless byproducts (CO2 and H2O). The general mechanism of combining electrons (e−) with O2 and holes (h+) with OH− produces super oxides and free hydroxyl radicals, respectively, consequently removing dye from the liquid solution.66 Figure 6a shows the catalytic activity (under dark c o n d i t i o n s ) a n d p h o t o c a ta l y t i c a c t i v i t y o f t h e Bi1−xLaxFe1−yMnyO3/Ti3C2 nanohybrids (irradiated). The

Figure 4. XPS analysis of BLFMO-5 sample. Survey scan (a), highresolution scan for Bi (b), Fe 2p (c), O 1s (d), C 1s (e), and deconvolution of the O 1s high-resolution XPS scan (f).

reactions that occur on the surface of the material, and oxygen species is an important part of the process. The O 1s highresolution spectra were deconvoluted and fitted using the Lorentzian−Gaussian curves (Figure 4f). Three peaks were observed from the curve fitting: the peak at BE ≈ 529 eV (because of the lattice oxygen atoms), the peak at BE ≈ 531 eV is attributed to hydroxyl oxygen, and the third peak at BE ≈ 532 eV is attributed to the surface-adsorbed oxygen species.60,61 During photocatalytic reactions, higher content of hydroxyl species is required to produce reactive oxygen species such as hydroxyl radical •OH−.62 Figure 4e represents a high-resolution C1 spectrum. A sharp peak at BE ≈ 284.8 eV was further deconvoluted into two peaks for C−C and C−O bonds (not shown).50,63 2.3. Diffusive Reflectance Spectroscopy of Nanohybrids. The light absorption properties of BLFMO/Ti3C2 nanohybrids were investigated via diffuse reflectance UV (DRUV) spectroscopy. Band gap energies (EBG) were calculated from the extrapolation of the linear range obtained from modified Kubelka−Munk function [F(R)hν]0.5 versus photon energy, hν.64 Significant band gap narrowing was observed for BLFMO/Ti3C2 nanohybrids in comparison to the bare BFO nanoparticles. EBG of bare BFO nanoparticles were given as 2.04 eV, in good agreement with literature values.19,20 BLFMO/Ti3C2 composites showed band gaps between 1.3 and 1.5 eV. In particular, 1.30 eV was calculated for BLFO/ Ti3C2, whereas for BLFMO-20/Ti3C2, the band gap was 1.48 eV (Figure 5). Precise EBG assessment of the rest of BLFMO/Ti3C2 series was not possible because of the difficulty in discerning the

Figure 6. (a) Photocatalytic degradation of CR by BLFO/Ti3C2− MXene, and BLFMO/Ti3C2−MXene nanohybrids against the time taken and (b) BLFO−Ti3C2 dye degradation curves for four cycles. 8664

DOI: 10.1021/acsomega.9b00493 ACS Omega 2019, 4, 8661−8668

ACS Omega

Article

radicals can be produced by the reaction of OH− with holes.12,16,20,30,66,72,73,78−80 As the electrons react with the catalyst, the H2O molecules are converted into OH. The radicals produced in the process, that is, •O2− and •OH−, being highly reactive for the organic pollutants such as CR, degrade it to the harmless byproducts that are CO2 and H2O. The mechanism of degradation is given by the equations below

relative concentration of the CR dye versus the irradiation time for various nanohybrids is represented. All the nanohybrids showed improved dye degradation as compared to the neat BFO nanoparticles. Neat BFO nanoparticles exhibited 10% dye degradation under dark conditions, which reached to a maximum of 40% at 90 min of irradiation after which no change in dye concentration was observed. Pure MXene− Ti3C2 exhibited 12% dye degradation in 120 min reported previously.67 In Bi1−xLaxFe1−yMnyO3 nanoparticles, BLFMO5/MXene showed the best degradation under dark conditions, which did not change much when irradiated.30 Here, the best catalytic activity was observed for BLFO/Ti3C2 and BLFMO5/Ti3C2 where BLFO/Ti3C2 reduced the CR concentration to ∼92% in dark whereas an ∼93% reduction in CR concentration was observed for BLFMO-5/Ti3C2 in dark. Both nanohybrids reached to almost 100% degradation when irradiated within 30 min of irradiation. Both of these nanohybrids proved to be the best reducing catalysts of CR. Most of the dye degradation was achieved under dark conditions, which might be attributed to the adsorption effect of CR on BLFMO/Ti3C2 nanohybrids. The enhanced catalytic effect was exhibited by the combined structure of the codoped BFO with MXene−Ti3C2 sheets. As stated earlier in the XPS discussion, the nanohybrid is enriched with oxygen species such as hydroxyl ions and adsorbed oxygen, which consequently enhances the photocatalytic activity on the surface of the material. Exfoliated MXene−Ti3C2 as reported earlier with a surface area of 39 m2 g−1 might have increased the active sites on the nanohybrid for reactive species for the adsorption effect68,69 as larger surface area provides more space to dye molecules to get adsorbed and degraded easily and quickly.35,70,71 The produced nanohybrids showed better catalytic activity compared to previously reported hybrid systems. Previous research reported the BLFMO/GNP nanohybrids for CR removal in which the best catalyst in their report is BLFO/ GNP graphene nanoplatelet, which took 30 min to degrade the CR completely and another BLFMO-20/GNP nanohybrid degraded 76% CR dye in dark with complete degradation in about 120 min. Another report showed BLFMO/GO nanohybrids for the CR dye degradation; the best catalyst BLFMO15/GO degraded 96% CR dye in 30 min. In another report, researchers showed the photocatalysts for the degradation of RhB. Their best produced catalyst Au−CdS degraded the RhB in 90 min. Graphene-wrapped TiO2 (graphene-w-TiO2) was reported as the best photocatalyst for the degradation of methylene blue (MB) in 90 min. A system of MoS2/rGO aerogel was produced to photodegrade chromium(VI) in about 120 min. A Ag−CdS−TiO2 nanotube system was produced to degrade MB under ultra violet (UV) light, which degraded MB in 120 min.20,72−77 Under photocatalytic conditions, the generation of electron−hole pairs by visible light irradiation produces O2 and OH radicals. These highly active radicals start degrading the organic pollutants present in the water solution and in turn reduce to harmless byproducts (CO2 and H2O). In the general mechanism, photoexcited BLFO/Ti3C2 produces electron− hole paired charge carriers as in eq 1. Large surfaces may possibly have many active sites, which might increase the possibility of maximum interactions between the dye molecules and the nanohybrid. Once the process starts, the superoxide anion radicals •O2− can be produced, and meanwhile, •OH−

hν + Bi1 − xLaxFe1 − yMn yO3−Ti3C2 → e− + h+ −

−

Ti3C2 + e → e (trap sites Ti3C2) −

•

e (trap sites Ti3C2) + O2 → O2

(2)

−

(3)

H 2O + h+ →• OH− •

(1)

(4)

−

CR + OH → CO2 + H 2O (degradation byproducts) (5) •

−

CR + O2 → CO2 + H 2O (degradation byproducts) (6)

The recyclability of the nanohybrids was also investigated for one nanohybrid structure (BLFO/MXene) as shown in Figure 6b. The nanohybrid was removed from the dye solution, washed, and reused in four consecutive cycles in order to show its potential regeneration in continuous applications. During each cycle, there was negligible reduction in the catalytic efficiency. This result further proves that the synthesized catalyst does not degrade itself, and it can be regenerated efficiently for extended applications. However, further experiments will be conducted later in order to understand the recyclability of these catalysts (a separate manuscript will be submitted later).

3. MATERIALS AND METHODS Salts of bismuth nitrate pentahydrate (Bi(NO3)3.5H2O, 99% pure), iron nitrate (Fe(NO3)3.9H2O, 98.5% pure), ethylene glycol (C2H6O2, 99%), acetic acid (C2H4O2, 99.5%), and hydrofluoric acid (HF, 39 wt %) were used as received. 3.1. Synthesis of MXene−Ti3C2 Sheets. Multilayered sheets of Ti3C2Tx were fabricated from pure Ti3AlC2 (MAX phase) using the following procedure: approximately 3 g of Ti3AlC2 powder was dissolved in 70 mL of HF (39 wt %) in a closed Teflon bottle and stirred magnetically for 60 h at room temperature. Solids were removed from the Teflon bottle, filtered under vacuum, and subsequently washed with deionized (DI) water and ethanol until a pH ≈ 6 was reached. Finally, the washed residue was dried in a convection oven at 60 °C for 6 h. The residue obtained was MXene−Ti3C2 sheets with formula Ti3C2. 3.2. Synthesis of Doped BFO Nanoparticles. The Bi1−xLaxFe1−yMnyO3 (abbreviated as BLFMO, x = 0.1, y = 0.0, 0.05, 0.10, 0.20, and 0.25), named here in as BLFO, BLFMO5, BLFMO-10, BLFMO-20, and BLFMO-25, nanoparticles were synthesized using a double-solvent sol−gel method. Bismuth nitrate pentahydrate and lanthanum nitrate hexahydrate were stoichiometrically were dissolved in equimolar acetic acid and ethylene glycol and magnetically stirred for 90 m at 40 °C. A mixture of iron nitrate nonhydrate powder and manganous nitrate solution (50%) was also dissolved in acetic acid under constant stirring for 90 m at 40 °C. Both solutions were mixed in a single flask and stirred for another 180 m at 40 °C until a uniform, reddish brown precursor solution (0.4 M) 8665

DOI: 10.1021/acsomega.9b00493 ACS Omega 2019, 4, 8661−8668

ACS Omega

Article

wavelength of 496 nm.30 The efficiency of the degradation can be measured using the formula

was produced. In order to compensate for Bi loss during the heating process, solutions containing 3% excess Bi were prepared. Ethylene glycol was used to maintain constant electronegativities of iron and bismuth during the chemical reaction, whereas acetic acid acted as a catalyst to maintain the solution concentration and for controlled chemical reaction during the synthesis process. The as-prepared solution was dried in a convection oven at 80 °C for 12 h to obtain a gel which was calcined in a furnace at 600 °C for 3 h. After calcination was completed, the powder was crushed to obtain a homogeneous fine powder. 3.3. Synthesis of MXene-Based Nanohybrids. The nanohybrids were fabricated using a double-solvent sol−gel technique. MXene−Ti3C2 solution was made in DI water with the molarity of 0.5 mg/mL, followed by ultrasonication for 10 min. The codoped BFO nanoparticles (Bi1−xLaxFe1−yMnyO3) were dissolved in a mixture of ethylene glycol and acetic acid with a 1:1 ratio and 0.01 M molarity. The Bi1−xLaxFe1−yMnyO3 solutions were ultrasonicated for 1 h at 60 °C; then, the solutions of Bi1−xLaxFe1−yMnyO3 were mixed with Ti3C2 solutions separately for all hybrids, and then the Bi1−xLaxFe1−yMnyO3/MXene−Ti3C2 solutions were stirred magnetically for 2 h at 80 °C for coprecipitation synthesis. The products were washed with DI water several times and dried at 60 °C for 3 h.

Degradation (%) =

Co − C t × 100 Co

Here, Co shows the initial concentration of the dye and Ct shows the concentration of the dye at specific times.81

5. CONCLUSIONS La- and Mn-codoped BFO nanohybrids with various doping concentrations were successfully synthesized using a doublesolvent sol−gel method. The 2D MXene−Ti3C2 sheets were synthesized from their pure MAX phase via selective etching of aluminum. The Bi1−xLaxFe1−yMnyO3/Ti3C2 nanohybrids were fabricated using the double-solvent sol−gel technique. Nanohybrids showed large electron−hole pair generation and low recombination time compared to pure BFO nanoparticles. The nanohybrids were further tested for catalytic and photocatalytic degradation of CR. The best catalytic activity was observed under dark conditions where >90% CR degradation was observed; BLFO/Ti3C2 and BLFMO-5/Ti3C2 degraded the 92 and 93% dye in dark, respectively, and further complete (100%) degradation within 20 min of irradiation. Furthermore, these nanohybrid catalysts are regenerative and work efficiently without losing their catalytic activity up to four cycles. The hybrids reported are novel and best candidates for catalytic activities, which makes them potential candidates for commercial applications owing to its low-cost synthesis route.

4. CHARACTERIZATION Samples were analyzed for their structure using the XRD, Cu Kα radiation source (Rigaku 2500, Japan). The samples were analyzed for a range of 10°−70°. Surface and morphology of hybrids were investigated using field-emission SEM (FESEM, JEOL7001F). To avoid the charging effect, platinum was sputter-coated on the nanohybrid before FESEM exposure. PL spectroscopy was performed to calculate the generation/ recombination rate of the carrier. Binding energies of elements present in the hybrid were checked using XPS. The solid-state diffuse reflectance UV/vis spectra of the La-, Mn-codoped BFO nanoparticles were recorded with a double-beam UV/ vis−NIR spectrophotometer (Cary 5000, Varian) equipped with a diffuse reflection accessory (Praying Mantis, Harrick). Baseline correction was achieved using a BaSO4 standard. Approximately, 50 mg of each sample was dispersed in 150 mg of BaSO4 for the measurement. The reflectance was converted to the Kubelka Munk function F(R) with Cary WinUV software. 4.1. Photocatalytic Characterization. The codoped nanohybrids were tested for their photocatalytic dye degradation application. The apparatus detailed as Hitachi (UV-3310) UV−vis spectrophotometer is used to test the photocatalytic property of the nanohybrids. An amount of 100 mg of nanohybrids was used to be tested in the prepared solution of 100 mL of CR so that the concentration of the dye solution is taken as 100 mg L−1 and the solution is put into stirring in dark condition for about 120 min. As to ignore the thermal degradation activity, the solution is put in the ice bath under constant stirring.12,30 Visible light is taken from the xenon lamp (300 W), a 5 W light-emitting diode was used for UV (ultraviolet) source. Every 30 min, an amount of 3 mL of the solution is taken out from the main solution during the complete process; the taken amount was centrifuged at 7000 rpm to get the supernatant. The supernatant is then used to check the concentration of CR using the Hitachi UV-3310 UV−vis spectroscope, and the curve is measured at a specific

■

AUTHOR INFORMATION

Corresponding Author

*E-mail: [email protected]. Phone: +92-51-90855599. ORCID

S. Irfan Ali: 0000-0002-6015-2415 Syed Rizwan: 0000-0002-6934-0949 Author Contributions

M.A.I., S.I.A., and A.T. carried out the experimentation; F.A. and M.Z.I. assisted in manuscript writing and data analysis; and S.R. designed and supervised the project. Notes

The authors declare no competing financial interest.

■

ACKNOWLEDGMENTS The authors are thankful to the Higher Education Commission (HEC) of Pakistan for providing research funding under the project no. 6040/Federal/NRPU/R&D/HEC/2016 and HEC/USAID and financial support under the project no. HEC/R&D/PAKUS/2017/783. The author also thanks the School of Natural Sciences (SNS) at the National University of Science & Technology (NUST), Islamabad, Pakistan, for partial financial support. Special thanks to DAAD, Germany, for providing financial assistance under the project no. 57345771.

■

REFERENCES

(1) Walker, G. M.; Hansen, L.; Hanna, J.-A.; Allen, S. J. Kinetics of a reactive dye adsorption onto dolomitic sorbents. Water Res. 2003, 37, 2081−2089. (2) Pavan, F. A.; Dias, S. L. P.; Lima, E. C.; Benvenutti, E. V. Removal of Congo red from aqueous solution by anilinepropylsilica xerogel. Dyes Pigm. 2008, 76, 64−69. 8666

DOI: 10.1021/acsomega.9b00493 ACS Omega 2019, 4, 8661−8668

ACS Omega

Article

(24) Wood, S. A. The aqueous geochemistry of the rare-earth elements and yttrium. Chem. Geol. 1990, 82, 159−186. (25) Kothari, D.; Reddy, V. R.; Gupta, A.; Phase, D. M.; Lakshmi, N.; Deshpande, S. K.; Awasthi, A. M. Study of the effect of Mn doping on the BiFeO3 system. J. Phys.: Condens. Matter 2007, 19, 136202. (26) Zheng, X.; Xu, Q.; Wen, Z.; Lang, X.; Wu, D.; Qiu, T.; Xu, M. X. The magnetic properties of La doped and codoped BiFeO3. J. Alloys Compd. 2010, 499, 108−112. (27) Li, M.; Ning, M.; Ma, Y.; Wu, Q.; Ong, C. K. Room temperature ferroelectric, ferromagnetic and magnetoelectric properties of Ba-doped BiFeO3 thin films. J. Phys. D: Appl. Phys. 2007, 40, 1603. (28) Bartkowska, J. A. Dynamical magnetoelectric coupling in multiferroic BiFeO3. Int. J. Thermophys. 2011, 32, 739−745. (29) Arya, G. S.; Negi, N. S. Effect of In and Mn co-doping on structural, magnetic and dielectric properties of BiFeO3 nanoparticles. J. Phys. D: Appl. Phys. 2013, 46, 095004. (30) Irfan, S.; Rizwan, S.; Shen, Y.; Tomovska, R.; Zulfiqar, S.; Sarwar, M. I.; Nan, C.-W. Mesoporous template-free gyroid-like nanostructures based on La and Mn co-doped bismuth ferrites with improved photocatalytic activity. RSC Adv. 2016, 6, 114183−114189. (31) Meng, W.; Hu, R.; Yang, J.; Du, Y.; Li, J.; Wang, H. Influence of lanthanum-doping on photocatalytic properties of BiFeO3 for phenol degradation. Chin. J. Catal. 2016, 37, 1283−1292. (32) Wang, H.-C.; Lin, Y.-H.; Feng, Y.-N.; Shen, Y. Photocatalytic behaviors observed in Ba and Mn doped BiFeO3 nanofibers. J. Electroceramics 2013, 31, 271−274. (33) Zhang, Z.; Liu, H.; Lin, Y.; Wei, Y.; Nan, C.-W.; Deng, X. Influence of La doping on magnetic and optical properties of bismuth ferrite nanofibers. J. Nanomater. 2012, 2012, 238605. (34) Kanhere, P.; Chen, Z. A review on visible light active perovskite-based photocatalysts. Molecules 2014, 19, 19995−20022. (35) Li, Z.; Shen, Y.; Yang, C.; Lei, Y.; Guan, Y.; Lin, Y.; Liu, D.; Nan, C.-W. Significant enhancement in the visible light photocatalytic properties of BiFeO3−graphene nanohybrids. J. Mater. Chem. A 2013, 1, 823−829. (36) Gupta, A.; Sakthivel, T.; Seal, S. Recent development in 2D materials beyond graphene. Prog. Mater. Sci. 2015, 73, 44−126. (37) Mas-Ballesté, R.; Gómez-Navarro, C.; Gómez-Herrero, J.; Zamora, F. 2D materials: to graphene and beyond. Nanoscale 2011, 3, 20−30. (38) Novoselov, K. S.; Jiang, D.; Schedin, F.; Booth, T. J.; Khotkevich, V. V.; Morozov, S. V.; Geim, A. K. Two-dimensional atomic crystals. Proc. Natl. Acad. Sci. U.S.A. 2005, 102, 10451−10453. (39) Zhu, Y.; Murali, S.; Cai, W.; Li, X.; Suk, J. W.; Potts, J. R.; Ruoff, R. S. Graphene and graphene oxide: synthesis, properties, and applications. Adv. Mater. 2010, 22, 3906−3924. (40) Geim, A. K. Graphene: status and prospects. Science 2009, 324, 1530−1534. (41) Song, L.; Ci, L.; Lu, H.; Sorokin, P. B.; Jin, C.; Ni, J.; Kvashnin, A. G.; Kvashnin, D. G.; Lou, J.; Yakobson, B. I.; Ajayan, P. M. Large scale growth and characterization of atomic hexagonal boron nitride layers. Nano Lett. 2010, 10, 3209−3215. (42) Watanabe, K.; Taniguchi, T.; Kanda, H. Direct-bandgap properties and evidence for ultraviolet lasing of hexagonal boron nitride single crystal. Nat. Mater. 2004, 3, 404. (43) Chopra, N. G.; Luyken, R. J.; Cherrey, K.; Crespi, V. H.; Cohen, M. L.; Louie, S. G.; Zettl, A. Boron nitride nanotubes. Science 1995, 269, 966−967. (44) Jariwala, D.; Sangwan, V. K.; Lauhon, L. J.; Marks, T. J.; Hersam, M. C. Emerging device applications for semiconducting twodimensional transition metal dichalcogenides. ACS Nano 2014, 8, 1102−1120. (45) Wang, Q. H.; Kalantar-Zadeh, K.; Kis, A.; Coleman, J. N.; Strano, M. S. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nat. Nanotechnol. 2012, 7, 699. (46) Anasori, B.; Xie, Y.; Beidaghi, M.; Lu, J.; Hosler, B. C.; Hultman, L.; Kent, P. R. C.; Gogotsi, Y.; Barsoum, M. W. Two-

(3) Mall, I. D.; Srivastava, V. C.; Agarwal, N. K.; Mishra, I. M. Removal of congo red from aqueous solution by bagasse fly ash and activated carbon: kinetic study and equilibrium isotherm analyses. Chemosphere 2005, 61, 492−501. (4) Iqbal, M. Z.; Pal, P.; Shoaib, M.; Abdala, A. A. Efficient removal of different basic dyes using graphene. Desalin. Water Treat. 2017, 68, 226−235. (5) Iqbal, M. Z.; Abdala, A. A. Thermally reduced graphene: synthesis, characterization and dye removal applications. RSC Adv. 2013, 3, 24455−24464. (6) Gupta, V. K.; Agarwal, S.; Saleh, T. A. Synthesis and characterization of alumina-coated carbon nanotubes and their application for lead removal. J. Hazard. Mater. 2011, 185, 17−23. (7) Rafatullah, M.; Sulaiman, O.; Hashim, R.; Ahmad, A. Adsorption of methylene blue on low-cost adsorbents: a review. J. Hazard. Mater. 2010, 177, 70−80. (8) Al-Bastaki, N. Removal of methyl orange dye and Na2SO4 salt from synthetic waste water using reverse osmosis. Chem. Eng. Process. Proc. Intens. 2004, 43, 1561−1567. (9) Moghaddam, S. S.; Moghaddam, M. R. A.; Arami, M. Coagulation/flocculation process for dye removal using sludge from water treatment plant: optimization through response surface methodology. J. Hazard. Mater. 2010, 175, 651−657. (10) Lee, J.-W.; Choi, S.-P.; Thiruvenkatachari, R.; Shim, W.-G.; Moon, H. Evaluation of the performance of adsorption and coagulation processes for the maximum removal of reactive dyes. Dyes Pigm. 2006, 69, 196−203. (11) Stolz, A. Basic and applied aspects in the microbial degradation of azo dyes. Appl. Microbiol. Biotechnol. 2001, 56, 69−80. (12) Irfan, S.; Rizwan, S.; Shen, Y.; Li, L.; Asfandiyar, A.; Butt, S.; Nan, C.-W. The Gadolinium (Gd3+) and Tin (Sn4+) Co-doped BiFeO3 Nanoparticles as New Solar Light Active Photocatalyst. Sci. Rep. 2017, 7, 42493. (13) Carenco, S.; Portehault, D.; Boissière, C.; Mézailles, N.; Sanchez, C. Nanoscaled metal borides and phosphides: recent developments and perspectives. Chem. Rev. 2013, 113, 7981−8065. (14) Tachikawa, T.; Yamashita, S.; Majima, T. Evidence for crystalface-dependent TiO2 photocatalysis from single-molecule imaging and kinetic analysis. J. Am. Chem. Soc. 2011, 133, 7197−7204. (15) Sun, K.; Jing, Y.; Park, N.; Li, C.; Bando, Y.; Wang, D. Solution synthesis of large-scale, high-sensitivity ZnO/Si hierarchical nanoheterostructure photodetectors. J. Am. Chem. Soc. 2010, 132, 15465− 15467. (16) Shen, R.; Jiang, C.; Xiang, Q.; Xie, J.; Li, X. Surface and interface engineering of hierarchical photocatalysts. Appl. Surf. Sci. 2019, 471, 43−87. (17) Gore, S. K.; Jadhav, S. S.; Jadhav, V. V.; Patange, S.; Naushad, M.; Mane, R. S.; Kim, K. H. The structural and magnetic properties of dual phase cobalt ferrite. Sci. Rep. 2017, 7, 2524. (18) Chaturvedi, S.; Das, R.; Poddar, P.; Kulkarni, S. Tunable band gap and coercivity of bismuth ferrite-polyaniline core-shell nanoparticles: the role of shell thickness. RSC Adv. 2015, 5, 23563−23568. (19) Gao, F.; Chen, X. Y.; Yin, K. B.; Dong, S.; Ren, Z. F.; Yuan, F.; Yu, T.; Zou, Z. G.; Liu, J.-M. Visible-Light Photocatalytic Properties of Weak Magnetic BiFeO3 Nanoparticles. Adv. Mater. 2007, 19, 2889−2892. (20) Fatima, S.; Ali, S. I.; Iqbal, M. Z.; Rizwan, S. The high photocatalytic activity and reduced band gap energy of La and Mn codoped BiFeO3/graphene nanoplatelet (GNP) nanohybrids. RSC Adv. 2017, 7, 35928−35937. (21) Moreau, J. M.; Michel, C.; Gerson, R.; James, W. J. Ferroelectric BiFeO3 X-ray and neutron diffraction study. J. Phys. Chem. Solids 1971, 32, 1315−1320. (22) Kubel, F.; Schmid, H. Structure of a ferroelectric and ferroelastic monodomain crystal of the perovskite BiFeO3. Acta Crystallogr., Sect. B: Struct. Sci. 1990, 46, 698−702. (23) Bucci, J. D.; Robertson, B. K.; James, W. J. The precision determination of the lattice parameters and the coefficients of thermal expansion of BiFeO3. J. Appl. Crystallogr. 1972, 5, 187−191. 8667

DOI: 10.1021/acsomega.9b00493 ACS Omega 2019, 4, 8661−8668

ACS Omega

Article

(64) Kubelka, P.; Munk, F.; Fur Tekn, Z. Ein Beitrag Zur Optik der Farbanstriche. Zeitschrift Fur Technische Physik 1931, 12, 593−601. (65) Li, Z.; Shen, Y.; Guan, Y.; Hu, Y.; Lin, Y.; Nan, C.-W. Bandgap engineering and enhanced interface coupling of graphene−BiFeO3 nanocomposites as efficient photocatalysts under visible light. J. Mater. Chem. A 2014, 2, 1967−1973. (66) Irfan, S.; Li, L.; Saleemi, A. S.; Nan, C.-W. Enhanced photocatalytic activity of La3+ and Se4+ co-doped bismuth ferrite nanostructures. J. Mater. Chem. A 2017, 5, 11143−11151. (67) Tariq, A.; Ali, S. I.; Akinwande, D.; Rizwan, S. Efficient VisibleLight Photocatalysis of 2D-MXene Nanohybrids with Gd3+ and Sn4+ Codoped Bismuth Ferrite. ACS Omega 2018, 3, 13828−13836. (68) Ran, J.; Gao, G.; Li, F.-T.; Ma, T.-Y.; Du, A.; Qiao, S.-Z. Ti3C2 MXene co-catalyst on metal sulfide photo-absorbers for enhanced visible-light photocatalytic hydrogen production. Nat. Commun. 2017, 8, 13907. (69) Naguib, M.; Come, J.; Dyatkin, B.; Presser, V.; Taberna, P.-L.; Simon, P.; Barsoum, M. W.; Gogotsi, Y. MXene: a promising transition metal carbide anode for lithium-ion batteries. Electrochem. Commun. 2012, 16, 61−64. (70) Sun, B.; Wei, L.; Li, H.; Chen, P. White-light-controlled ferromagnetic and ferroelectric properties of multiferroic singlecrystalline BiFeO3 nanoflowers at room temperature. J. Mater. Chem. C 2014, 2, 7547−7551. (71) Asahi, R.; Morikawa, T.; Ohwaki, T.; Aoki, K.; Taga, Y. Visiblelight photocatalysis in nitrogen-doped titanium oxides. Science 2001, 293, 269−271. (72) Fatima, S.; Ali, S. I.; Younas, D.; Islam, A.; Akinwande, D.; Rizwan, S. Graphene nanohybrids for enhanced catalytic activity and large surface area. MRS Commun. 2019, 9, 27−36. (73) Li, X.; Xie, J.; Jiang, C.; Yu, J.; Zhang, P. Review on design and evaluation of environmental photocatalysts. Front. Environ. Sci. Eng. 2018, 12, 14. (74) Li, X.; Shen, R.; Ma, S.; Chen, X.; Xie, J. Graphene-based heterojunction photocatalysts. Appl. Surf. Sci. 2018, 430, 53−107. (75) Zhang, R.; Wan, W.; Li, D.; Dong, F.; Zhou, Y. Threedimensional MoS2/reduced graphene oxide aerogel as a macroscopic visible-light photocatalyst. Chin. J. Catal. 2017, 38, 313−320. (76) Tang, H.; Fu, Y.; Chang, S.; Xie, S.; Tang, G. Construction of Ag3PO4/Ag2MoO4 Z-scheme heterogeneous photocatalyst for the remediation of organic pollutants. Chin. J. Catal. 2017, 38, 337−347. (77) Qi, K.; Cheng, B.; Yu, J.; Ho, W. A review on TiO2-based Zscheme photocatalysts. Chin. J. Catal. 2017, 38, 1936−1955. (78) Irfan, S.; Shen, Y.; Rizwan, S.; Wang, H. C.; Khan, S. B.; Nan, C. W. Band-Gap Engineering and Enhanced Photocatalytic Activity of Sm and Mn Doped BiFeO3 Nanoparticles. J. Am. Ceram. Soc. 2017, 100, 31. (79) Li, X.; Yu, J.; Jaroniec, M.; Chen, X. Cocatalysts for Selective Photoreduction of CO2 into Solar Fuels. Chem. Rev. 2019, 119, 3962−4179. (80) Low, J.; Yu, J.; Jaroniec, M.; Wageh, S.; Al-Ghamdi, A. A. Heterojunction photocatalysts. Adv. Mater. 2017, 29, 1601694. (81) Cong, Y.; Zhang, J.; Chen, F.; Anpo, M. Synthesis and characterization of nitrogen-doped TiO2 nanophotocatalyst with high visible light activity. J. Phys. Chem. C 2007, 111, 6976−6982.

dimensional, ordered, double transition metals carbides (MXenes). ACS Nano 2015, 9, 9507−9516. (47) Ghidiu, M.; Naguib, M.; Shi, C.; Mashtalir, O.; Pan, L. M.; Zhang, B.; Yang, J.; Gogotsi, Y.; Billinge, S. J. L.; Barsoum, M. W. Synthesis and characterization of two-dimensional Nb4C3 (MXene). Chem. Commun. 2014, 50, 9517−9520. (48) Naguib, M.; Halim, J.; Lu, J.; Cook, K. M.; Hultman, L.; Gogotsi, Y.; Barsoum, M. W. New two-dimensional niobium and vanadium carbides as promising materials for Li-ion batteries. J. Am. Chem. Soc. 2013, 135, 15966−15969. (49) Naguib, M.; Mashtalir, O.; Carle, J.; Presser, V.; Lu, J.; Hultman, L.; Gogotsi, Y.; Barsoum, M. W. Two-dimensional transition metal carbides. ACS Nano 2012, 6, 1322−1331. (50) Soltani, T.; Lee, B.-K. Sono-synthesis of nanocrystallized BiFeO3/reduced graphene oxide composites for visible photocatalytic degradation improvement of bisphenol A. Chem. Eng. J. 2016, 306, 204−213. (51) Wang, X.; Mao, W.; Wang, Q.; Zhu, Y.; Min, Y.; Zhang, J.; Yang, T.; Yang, J.; Li, X. a.; Huang, W. Low-temperature fabrication of Bi25FeO40/rGO nanocomposites with efficient photocatalytic performance under visible light irradiation. RSC Adv. 2017, 7, 10064− 10069. (52) Dai, J. F.; Xian, T.; Di, L. J.; Yang, H. Preparation of BiFeO3graphene nanocomposites and their enhanced photocatalytic activities. J. Nanomater. 2013, 2013, 1. (53) Asuha, S.; Zhou, X. G.; Zhao, S. Adsorption of methyl orange and Cr (VI) on mesoporous TiO2 prepared by hydrothermal method. J. Hazard. Mater. 2010, 181, 204−210. (54) Liqiang, J.; Yichun, Q.; Baiqi, W.; Shudan, L.; Baojiang, J.; Libin, Y.; Wei, F.; Honggang, F.; Jiazhong, S. Review of photoluminescence performance of nano-sized semiconductor materials and its relationships with photocatalytic activity. Sol. Energy Mater. Sol. Cells 2006, 90, 1773−1787. (55) Naguib, M.; Kurtoglu, M.; Presser, V.; Lu, J.; Niu, J.; Heon, M.; Hultman, L.; Gogotsi, Y.; Barsoum, M. W. Two-Dimensional Nanocrystals Produced by Exfoliation of Ti3AlC2. Adv. Mater. 2011, 23, 4248−4253. (56) Ballirano, P.; Pacella, A.; Nardi, E.; Fantauzzi, M.; Atzei, D.; Rossi, A.; Cametti, G. Fe (II) segregation at a specific crystallographic site of fibrous erionite: A first step toward the understanding of the mechanisms inducing its carcinogenicity. Microporous Mesoporous Mater. 2015, 211, 49−63. (57) Mullet, M.; Khare, V.; Ruby, C. XPS study of Fe(II)−Fe(III) (oxy)hydroxycarbonate green rust compounds. Surf. Inter. Anal. 2008, 40, 323−328. (58) Chuai, H.; Zhou, D.; Zhu, X.; Li, Z.; Huang, W. Characterization of V2O5/MoO3 composite photocatalysts prepared via electrospinning and their photodegradation activity for dimethyl phthalate. Chin. J. Catal. 2015, 36, 2194−2202. (59) Ke, S.; Lin, P.; Zeng, X.; Huang, H.; Zhou, L. M.; Mai, Y.-W. Tuning of dielectric and ferroelectric properties in single phase BiFeO3 ceramics with controlled Fe2+/Fe3+ ratio. Ceram. Int. 2014, 40, 5263−5268. (60) Da Silva, L. F.; Lopes, O. F.; Catto, A. C.; Avansi, W.; Bernardi, M. I. B.; Li, M. S.; Ribeiro, C.; Longo, E. Hierarchical growth of ZnO nanorods over SnO2 seed layer: insights into electronic properties from photocatalytic activity. RSC Adv. 2016, 6, 2112−2118. (61) Wang, T.; Lang, J.; Zhao, Y.; Su, Y.; Zhao, Y.; Wang, X. Simultaneous doping and heterojunction of silver on Na2Ta2O6 nanoparticles for visible light driven photocatalysis: the relationship between tunable optical absorption, defect chemistry and photocatalytic activity. CrystEngComm 2015, 17, 6651−6660. (62) Li, H.; Zhou, Y.; Tu, W.; Ye, J.; Zou, Z. State-of-the-Art Progress in Diverse Heterostructured Photocatalysts toward Promoting Photocatalytic Performance. Adv. Funct. Mater. 2015, 25, 998− 1013. (63) Myhra, S.; Crossley, J. A. A.; Barsoum, M. W. Crystal-chemistry of the Ti3AlC2 and Ti4AlN3 layered carbide/nitride phases characterization by XPS. J. Phys. Chem. Solids 2001, 62, 811−817. 8668

DOI: 10.1021/acsomega.9b00493 ACS Omega 2019, 4, 8661−8668