TiO-Based Nanomaterials for the Production of Hydrogen and the Development of Lithium-Ion Batteries Sergio Pinilla, Abniel Machin, Sang Hoon Park, Juan Camilo Arango, Valeria Nicolosi, Francisco M. Marquez-Linares, and Carmen Morant J. Phys. Chem. B, Just Accepted Manuscript • DOI: 10.1021/acs.jpcb.7b07130 • Publication Date (Web): 23 Oct 2017 Downloaded from http://pubs.acs.org on October 24, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

The Journal of Physical Chemistry B is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 44

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

TiO2-Based Nanomaterials for the Production of Hydrogen and the Development of Lithium-ion Batteries Sergio Pinilla1, Abniel Machín2, Sang-Hoon Park3, Juan C. Arango2, Valeria Nicolosi3, Francisco Márquez -Linares2*, and Carmen Morant1* 1

Department of Applied Physics and Instituto Nicolás Cabrera, Universidad Autónoma de Madrid, 28049 Madrid, Spain

2

School of Natural Sciences and Technology, Universidad del Turabo, Gurabo, PR00778, USA 3

CRANN and AMBER research centers, Trinity College Dublin, Dublin 2, Ireland

ABSTRACT

The photocatalytic activity of different titanium oxide nanowires containing gold (Au@TiO2NWs), and gold-graphene (Au@TiO2NWs-graphene), was evaluated by studying the reaction of hydrogen production by water splitting under UV-vis light. The composites showed high surface areas, with values above 300 m2 per gram, even after the incorporation of gold and graphene on the surface of titanium oxide nanowires. The highest hydrogen production of Au@TiO2NWs was 1,436 µmol h-1 g-1, under irradiation at 400 nm, and with a gold loading of

ACS Paragon Plus Environment

1

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 44

10 wt.%. This photocatalytic activity was 11.5 times greater than that shown by the unmodified TiO2NWs. For the Au@TiO2NWs-graphene composites, the highest hydrogen amount obtained was 1,689 µmol h-1 g-1, at loadings of 10 wt.% and 1 wt.% of gold and graphene, respectively. The photocatalytic activity of the gold-graphene compounds was 1.2 times greater than that shown by the titanium oxide catalysts and 13.5 times higher than the bare TiO2NWs. Even at wavelengths greater than 500 nm, the compounds exhibited yields of hydrogen above 1000 µmol h-1 g-1, demonstrating the high catalytic activity of the compounds.

In addition, TiO2-based materials are of great interest for energy storage and conversion devices, in particular for rechargeable lithium ion batteries. TiO2 has a significant advantage due to its low volume change (