Tip-Enhanced Raman Spectromicroscopy on the Angstrom Scale

Subscriber access provided by UNIVERSITY OF ADELAIDE LIBRARIES

Article

Tip-Enhanced Raman Spectromicroscopy On The Å Scale: Bare and CO-Terminated Ag Tips Nicholas Tallarida, Joonhee Lee, and Vartkess Ara Apkarian ACS Nano, Just Accepted Manuscript • DOI: 10.1021/acsnano.7b06022 • Publication Date (Web): 05 Oct 2017 Downloaded from http://pubs.acs.org on October 5, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Nano is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Tip-Enhanced Raman Spectromicroscopy On The Å Scale: Bare and COTerminated Ag Tips Nicholas Tallarida, Joonhee Lee,* Vartkess Ara Apkarian* Department of Chemistry, University of California at Irvine, Irvine, CA 92697-2025 ABSTRACT The tip is key to the successful execution of tip-enhanced Raman scattering (TERS) measurements in the single molecule limit. We show that nanoscopically smooth silver tips, batch produced through field directed sputter sharpening, reliably attain TERS with enhancement factors that reach 1013, as measured by the Raman spectra of single CO molecules attached to the tip apex. We validate the bare tips by demonstrating spectromicroscopy with submolecular spatial resolution; and underscore that TERS is a near-field effect that does not obey simple selection rules. As a more gainful analytical approach, we introduce TERS-relayed molecular force microscopy using CO-terminated tips. By taking advantage of the large Stark tuning rate of the CO stretch, molecular structure and charges can be imaged with atomic resolution. As illustration, we image a single Ag atom adsorbed on Au(111), and show that the adatom carries +0.2e charge. Keywords: tip-enhanced Raman spectroscopy, spectromicroscopy, force microscopy, scanning tunneling microscopy, field-directed sputter sharpening, COterminated tip, silver tip

By now, it is well established that plasmonic nanojunctions allow vibrational spectroscopy with single molecule sensitivity, both in frequency1–3 and time domain,4 through the surface enhanced Raman scattering (SERS) effect discovered nearly four decades ago.5,6 In the intervening period, there has been an explosion of developments and applications of the effect, among which SERS combined with scan-probe microscopy has heralded the ultimate frontier in vibrational spectromicroscopy (sm), under the rubric of tip-enhanced Raman scattering (TERS).7–10 Despite the advances, the fundamentals of the effect remain an active area of research, as summarized in recent expansive reviews.11–13 Most notable in this effort was the demonstration of TER-sm with submolecular spatial resolution, carried out on individual molecules at the junction of a scanning tunneling microscope (STM).14 While enhanced local fields are necessary to boost the single molecule signal to a detectable level, localization of light is essential to limit the observation to just one molecule in TER-sm. This is accomplished in the STM using an atomically terminated silver needle to concentrate light at its apex. The attained submolecular resolution has confirmed that atomistic detail in junction morphology defines the local fields,15–18 and has led to advances in theory to treat plasmonics in this nonclassical limit, through ab initio spectroscopy coupled to atomistic

ACS Paragon Plus Environment

1

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 22

plasmonics,17,19 and photodynamics in nano/pico-cavities by borrowing from the fields of cavity optomechanics20 and quantum electrodynamics.21 Remarkably, the experimental arrangement that yielded TERS with submolecular resolution was not substantively different from others in use;22 and the submolecular spatial resolution of the original demonstration was not reproduced under seemingly similar conditions, using the same molecule as the TERS reporter.23 In the sophisticated instrumentation used for TER-sm, the fabrication of the STM tip is the variant that is not standardized in practice.24 As such, we give it center-stage here: We describe a method for the batch processing of nanoscopically smooth silver tips, which invariably couple far-field radiation to the single cavity mode of the STM junction and enable TER-sm on the Å-scale. We preview the enabled measurements and highlight the fundamental challenge posed by the capability: In contrast with well-defined selection rules of vibrational spectroscopy carried out on ensembles with plane waves, single molecule SERS/TERS is tensorial near-field scattering determined by molecular orientation and light fields sculpted by the junction cavity.19,25 It was recognized early on that, in this limit, field gradients lead to multipolar Raman scattering, and that ultimately even multipolar expansions may fail.26 This was emphatically illustrated in measurements at a fusing plasmonic nanojunction, where it could be shown that field-gradient driven quadrupolar and magnetic Raman transitions, that are otherwise 103-105 times weaker than normal (dipolar) Raman, can dominate single molecule spectra.27 While important new science is accessed, the analytical utility of vibrational microscopy is compromised. A more gainful approach toward analytical spectromicroscopy is suggested through TERS-relayed molecular force microscopy (TERS-mfm) with single molecule functionalized tips, which we introduce here. We demonstrate TERS of COterminated silver tips and use the spectral shift of the CO stretching mode to map out intermolecular forces, therefore structure, with atomic resolution. The approach is closely related to implementations in atomic force microscopy (AFM) and STM using CO-terminated tips,28,29 which have yielded molecular structure with the highest spatial resolution to date. In TERS-mfm, the molecular spring replaces the mesoscopic AFM cantilever. The eight orders of magnitude increase in operating frequency of the transducer allows instantaneous force sensing through the spectral domain, with quality factor enhanced by the multiplexing advantage, as in superresolution microscopy.30 Beside mechanical forces, electric forces and charge distributions within individual molecules can be mapped31 by the large Stark tuning rate of the CO stretch,32 which is magnified on tipped Ag.33 Indeed, the differential Raman scattering cross section of CO is small.34 As such, observation of the single molecule requires dramatic field enhancement,27 of order >1012, which is routinely attained on the tips we describe. The very large enhancement factors, which arise from the combination of electromagnetic and chemical mechanisms,35 distinguish TERS of CO chemisorbed on the tip. At plasmonic junctions, this involves tunneling


2

Page 3 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

of charge transfer plasmons through the molecular bond.36 A formal treatment of the process37 and explicit time-dependent density functional simulations of the field driven tunneling current have been presented.33

RESULTS and DISCUSSION Silver Tips The dielectric properties of silver make it the material of choice for fashioning bright plasmonic tips. Although electrochemically etched silver tips serve well for STM purposes,38 in contrast to gold and tungsten, silver surfaces roughen in the process. Both electrochemically etched and vapor deposited silver tips are plagued by nanoscopic asperities, nanocrystalites, and surface irregularities due to redeposition of ions during etching and corrosion.39 To simplify, standardize and optimize tip fabrication, we have previously developed an automated two-stage electrochemical etching and electropolishing procedure.40 The technique produces relatively sharp Ag tips (r < 100 nm) with improved microscopic smoothness. However, the surface remains rough on the nanoscopic scale, as seen in the SEM images of Figure 1. Hot spots on nanoscopic asperities can be sufficiently bright to produce single molecule SERS.41 While focused ion beam milling can be used to superficially polish and shape individual silver tips, the process is laborious, and implanted ions degrade the surface conductivity of silver and scatter surface plasmons.42 Instead, we have adapted the field-directed sputter sharpening (FDSS) technique43 for batch processing silver tips. The result is depicted in Fig. 1. Despite variations in gross shapes and cone radii, these optically smooth tips invariably concentrate visible light to a single nanometric spot, as will be validated below.

Figure 1. Scanning electron micrographs of two-stage electrochemically etched tips, before (a, c, e) and after (b, d, f) batch processing via field directed sputter sharpening (FDSS). The process eliminates nanoscopic surface roughness and sharpens the apex, with memory of the original gross structure. (g) The reduction in tip length is due to head-on sputtering.

Field Directed Sputter Sharpening


3

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 22

The concept of FDSS, which was introduced and implemented by Schmucker et al. to produce PtIr, W, and HfB2 tips with nanometric sharpness,43 is illustrated in Figure 2. The tip is showered head-on with 2 keV Ar+-ions while positively-biased at 100500 V. The positive surface charge density of the tip provides a retardation field that conforms to the taper by the lightning rod effect. Explicitly, the retarding potential on a cone can be described by the fractional-order Legendre polynomial: (, ) ≃ ( ) (1) with ν = 0.247 for the exemplary half-cone angle of α = 16.2°, and coefficient A determined by the boundary condition at large r .44 The associated electric field, in spherical coordinates, 1 = − ≃ − ( ), = − ≃ − ( ), (2) determines the trajectory of an ion subject to the force: F=qE. For a given cone angle and impinging ion energy, the counter bias can be adjusted to produce ion trajectories that graze the taper, to produce ion-streaming on the inclined surface for optimal polishing without dulling the apex. For the cone in Fig. 2, this is accomplished at a counter bias ratio of Vcone/Vion = 0.1 ~ 0.3. In practice, the asperity decorated surface dictates the intricate local fields and FDSS retains memory of the initial morphology. As such, the procedure greatly benefits from starting with uniform, electrochemically polished tips. The key consideration in the design of a batch processor is the maintenance of the symmetry of ion streamlines on tips held in close proximity. The schematic of our design to batch-process seven tips, is shown in Figure 3. Its operating conditions and simulations of its computer-aided design are provided in the supplement. The outcome is illustrated by the scanning electron micrographs in Fig. 1: The finished surface is smooth on the nm-scale, the tips are sharpened subject to memory of initial shape, and the sharpest tip has a cone radius of 16 nm.


4

Page 5 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Figure 2. Ion trajectories overlaid on the electric field map of a positively biased tip modeled as a cone: incident Ar+-ion energy = 2 keV, counter bias = + 500 V, cone semi angle α= 16.2°, initial lateral displacements of the incoming ions from the principal axis are 5 and 50 nm. Scale bar = 500 nm.


5

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 22

Figure 3: Assembly for field directed sputter sharpening. (a) 3-dimensional view of the setup used to perform batch FDSS on up to 7 tips. (b) Sectional view of the setup: Grounded sections are in white while biased sections are in dark grey. The GND structure (aluminum) is connected to the grounded vacuum chamber (flange) via the metallic standoffs. The tips are biased through their contact with the holder, which, in turn, is connected to a setscrew and a bias feedthrough (shown in (a)). Ions are shot through narrow holes in the GND structure to sputter the tips. Inset: the GND structure with holes providing individual tips with separate ground surfaces and ion channels. (c) The assembly, made of molybdenum and tantalum, used to perform FDSS in the UHV TERS-STM chamber using existing sputtering housing (blue).

Highly polished Ag surfaces are highly reactive. Tips tarnish upon exposure to air during transfer to the UHV chamber of the STM. The formation of an adventitious diamond-like carbon (DLC) film can be recognized by the broad Raman band in the range from 1200 to 1700 cm-1 seen in Figure 4a (red trace).45 This surface contamination is completely removed by additional FDSS cycles inside the STM chamber, as illustrated by the spectrum in Fig. 4a (black trace). The design of the tip holder for in-situ FDSS is illustrated in Fig. 3c, and operating conditions are given in the supplement. Cavity Plasmons


6

Page 7 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

The cavity plasmon resonance can be observed through electroluminescence (EL) and electronic Raman scattering on the empty junction. EL arises from inelastic scattering of tunneling electrons at the protruding atom of the tip apex, with far field radiation colored by the junction plasmon.46,47 Raman is driven by intraband scattering on Fermi electrons of the metal, which generates a gap independent background that decays exponentially as a function of Stokes shift,48 and a gap sensitive resonance, which is shown in Fig. 4b. The close agreement between EL and Raman spectra and the gap dependence of the resonances (Fig. 4b and 4c), indicate that the cavity mode is being seen.49 The red shift of the resonance as the gap is reduced identifies the binding dipolar plasmon formed by the coupling of the tip plasmon with its mirror image in the metallic substrate.47 The spectral shift of the optically detected resonance upon an atomic scale variation in the junction gap validates the TERS utility of a tip, since it establishes that the nanocavity mode is coupled to the far-field and is the sole source of the observed Raman scattering. FDSS processed tips show this signature, which is absent in unprocessed electrochemically etched silver tips. Although resonances of tips with different cone radii vary, they can be tuned to some extent by reshaping the apex by applying voltage pulses (100 ms, 3-10 V) in the tunneling regime. The resulting shape of the apex in use is unknown beyond its atomic protrusion, which is deduced from the sharpness of topographic STM images. Indeed, cavity modes evolve and tips deteriorate over time and dull after crashing with the substrate. Nevertheless, tip performance can be restored by voltage pulsing.


7

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 22

Figure 4: Junction plasmon resonances. (a) Raman spectrum of the unprocessed tip (red) shows a carbonaceous residue, which is removed by in-situ FDSS (black). (b) Cavity mode resonances after reshaping the tip apex through voltage pulsing: The EL spectrum (black) is recorded at a sample bias of +2.8 V, and current of 0.1 nA. The Raman spectrum of the junction (red trace) shows the same resonance (excited at 532 nm, 5 µW/µm2, 10 s accumulation time). The resonance blue-shifts (blue trace) by 16 nm (419 cm-1) and its intensity halves upon retracting the tip by 7.8 Å from the tunneling set point (0.1 nA, +0.1 V, gap ~ 6 Å). (c) Gap-dependence of EL spectra: The plasmon resonance blue-shifts by 11 nm as the tip is retracted by 2.6 Å, by lowering the set point current from 2.0 nA (red) to 0.01 nA (blue) at VB = +2.91 V.


8

Page 9 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

TER-sm We carry out TER-sm on a 2D array of Co(II)-tetraphenylporphyrin (Co-TPP) molecules prepared on Au(111), at T = 80 K. The simultaneously recorded constant current STM topography and TER-sm image are shown in Figures 5a and 5b. The latter is a spectral slice of the hyperspectral image, consisting of complete Raman spectra recorded on 1 Å × 1 Å pixels (1 s/pixel, I0 ~ 5 µW/µm2, λ = 634 nm). The Raman spectrum of the flat aromatic molecules, with polarizability dominated by the in-plane modes, is strongly degraded, as seen in Figure 5d. The line spectrum rides over the exponentially decaying Raman response of the metal electrons. It is limited to the cavity resonance window, which cuts off near 1600 cm-1. The integrated intensity under the prominent line at 1280 cm-1, which is a field gradient driven mode localized on the phenyl rings,50 is used to construct the image in Fig. 5b. Inspection of the images and the line cuts shown in Fig. 5c clarifies that the spatial resolution in the STM and TER-sm is nearly identical. Remarkably, the line cuts are anti-correlated and the contrast in the TER-sm (Fig. 5b) is inverted relative to the topography (Fig. 5a). The TERS signal peaks when the tip is placed between molecules, where phenyl groups from four different molecules share the local field gradient. This is consistent with recent explicit simulations of TERS driven by field gradients.19 The dominant effect in the anti-correlation between spectral intensity and tip height is the confinement of the cavity mode. The 2-Å variation in the apparent height of the molecule in Fig. 5c leads ~ 30 % modulation in intensity of both vibrational lines and the background void of vibrational lines. The latter is directly associated with the cavity resonance, which on the Å-scale is defined by both tunneling junction and conductance of the intervening molecule at optical frequencies. In effect, the observed submolecular spatial resolution of TER-sm derives from confinement of the cavity mode localized at the tip apex. We defer the analysis of mode specific vibrational information contained in the images. It should be noted, however, that the signal is more localized than the probed normal modes. Therefore, the mode specific image (Fig. 5b) is at the ultimate spatial resolution of relevance to vibrational spectromicroscopy in molecular matter. This comes at a price. TERS of CoTPP/Au(111) was previously studied under ambient conditions, but without spatial resolution.51 The molecules deposited from the liquid phase appear in ordered and disordered domains. The two domains show very different spectra; and remarkably, neither agrees with the present, 80 K spectrum. In effect, the vibrational fingerprint of the molecule is lost.


9

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 22

Fig 5. TER-sm of a CoTPP monolayer on Au(111). (a) Constant current STM topography showing the CoTPP array (I = 0.1 nA, Vb = 9.8 mV). (b) Simultaneously acquired TER-sm image of the prominent vibrational peak at 1280 cm-1 (integrated between 1244 and 1304 cm-1, 1 s acquisition time per 1 Å × 1 Å pixel, 634 nm excitation with ~ 5 uW/um2 incident intensity). (c) Line profiles along a dashed line in (a) and (b), showing the anti-correlation between the STM (black) and TER-sm (red) maps. (d) Degraded spectrum recorded on one pixel. The images have been low-pass filtered for clarity. Scale bar = 1 nm.

Single molecule TERS Richer vibrational spectra can be observed for molecules that do not freeze in a planar adsorption state. In Fig. 6a, we show TERS of a single 1,2-di(4-pyridyl) ethylene (BPE) molecule adsorbed on Au(111) at 80 K. Although BPE is mobile on gold at this temperature, a molecule can be trapped at the STM junction. The observed vibrational line intensities fall by ~ 50% upon 1 Å retraction of the tip; and the spectrum and cavity mode disappear when the tip is retracted by 17 nm. BPE is a common nonresonant SERS reporter.3 Its surface-enhanced Raman, hyperRaman and IR spectra, have been previously reported along with the normal modes,52 and we have previously relied on BPE as the reporter in our timeresolved4,53 and polarization selected54 SERS studies on nanodumbbells. Although the observed lines in Fig. 6a can be assigned, the line intensities are entirely different from those of the ensemble and the commonly reported stationary SERS spectra presented in Fig. 6b. The most intense Raman lines of C=C stretching modes above 1600 cm-1 seen in Fig. 6b are absent in the TERS spectrum of Fig. 6a. The most intense TERS line at 990 cm-1 is not visible in the normal spectra (Fig. 6b). With field fixed along the tip z-axis, and Raman restricted to dipolar scattering, the 990 cm-1 can be made to dominate (see Fig. 6c) for the molecular orientation shown in Fig. 6d. However, the rest of the intensity pattern does not match. As in partially fused nanojunctions,27 the spectrum is dominated by the odd parity modes driven by field gradients. This is a consequence of spectroscopy with confined light, where the local wavevector qi given by the spatial Fourier components of the field reaches submolecular length scales, | | ! 1.54 Given knowledge of molecular orientation


10

Page 11 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

and scattering tensor, the spectra can, in principle, be inverted to reconstruct the local field.27 In practice, this is not a trivial task. Moreover, in this limit, multipolar expansion of the polarizability tensor becomes suspect,19,26 and quantum treatments of the plasmon and molecule on an equal footing will be necessary. This detracts from the aim of vibrational spectromicroscopy, since a given molecule no longer has a single vibrational fingerprint.

Fig 6: Tensorial nature of a single BPE Raman spectrum. (a) TER spectra of a single BPE molecule trapped at the STM junction. The intensity of the vibrational lines and background of the cavity resonance decay upon 1 Å tip retraction, by dropping the STM current from 0.8 nA (red) to 0.1 nA (black), and completely disappear upon retracting by 17 nm (gray). (b) Comparison between simulated Raman spectrum (blue) and SERS of BPE on a gold nanodumbbell (red).55 The molecule, incident and scattered optical fields are aligned along the x-axis. (c) Comparison between a simulated spectrum of BPE oriented in Euler angles (α=78°, β=235°, γ=187°) (blue) and the TERS in (a) (red). (d) Junction geometry of the simulated spectrum in (c), with incident and scattered fields assumed to be along the tip zaxis. The simulation is performed at the B3LYP/6-31G(d) level using Gaussian 09.56


11

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 22

Figure 7. Chemical speciation of a single Ag atom and CO molecule using a CO-terminated Tip. (a) Decay of the integrated intensity of the CO vibrational line (inset) as a function of gap distance is fitted to an exponential decay (red, τ = 3.55 ± 0.14 Å) and power law (blue, n = 2.07 ± 0.06). Inset: A CO spectrum recorded at 1.2 V. (b) Schematic of the measurement. (c) Topographic image (1.2 V, 0.1 nA) of a Ag atom and CO molecule. (d - g) TERS relayed molecular force microscopy (0.37 V. 1.0 nA): (d) Map of CO stretch frequency obtained via a Gaussian fit. The frequency red-shifts over the Ag atom and blue-shifts over the CO molecule with respect to the Au(111) surface. When integrating the Raman intensity, the silver atom appears in the spectral window (e) 2042 - 2055 cm-1 while the CO molecule is best mapped in the window (f) 2072 - 2077 cm-1. (g) A composite image of (e) and (f). Images are low pass filtered and low intensity background noise is masked for clarity. Scale bar = 1 nm.

CO-terminated tips A great deal of structural uncertainty is eliminated in TERS of CO-terminated Ag tips. Now, a single diatomic reporter is aligned along the maximal z-component of the local E-field, with its signal localized to the 1.1 Å bond length of the molecule placed at 2.6 Å from the apex atom.33 In measurements carried out at 5 K on a Au(111) surface, we transfer a single CO molecule to the Ag tip through voltage pulsing. CO is weakly bound on Ag, preferentially attaching to the vertex atom on Ag tips.33 The TERS of the stretching mode of an attached 12C18O molecule is shown in


12

Page 13 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

the inset of Fig. 7a. The line width is instrument limited (FWHM = 2.6 cm-1) and the integrated line intensity, which reaches count rates R = 103 photons/s, decays as a function of gap distance. The data can be represented by an exponential decay of 3.6 Å (Fig. 7a, red), consistent with TERS determined by the tunneling current of Fermi electrons through the " ∗ -orbital of CO.33 In this limited range of measurement, between 5.5 Å and 11.5 Å, the decay of the signal can also be fit to a power law, $ ∝ & '., as shown by the blue fit in the log-log plot in Fig. 7a. Under the quartic law of TERS, the implied local field scales as ) ∝ $/+ ∝ & ,.-'-, in agreement with the recently derived law of enhancement in junction gaps, beyond the classical limit of the original derivation.57 The field experienced by the molecule can be obtained from the effective enhancement factor, . : /

. = = 106 01234/32

(3)

assuming the gas phase scattering cross section, 7/Ω = 3.3 x 10-31 cm2/sr,34 incident photon flux N determined by the softly focused 634 nm laser to 5 µW/µm2, collection angle Ω = 2.7 sr, and efficiency < = 0.1 .41 Accordingly, the field localized /+

on the molecule is ) = , =. > = 0.01 V/Å and the signal is confined to a volume of ≤ 100 Å3, as measured by its vertical decay length of 3.6 Å and lateral resolution in the TER-sm map of ~ 5 Å. TERS-mfm is illustrated in Fig. 7b. Rather than the near-field TER-sm of targeted molecules (Fig. 5), TERS of the CO terminus on the scanning tip is used to map out intermolecular forces. To illustrate the principles, we consider a single Ag atom evaporated onto the Au(111) substrate (Fig. 7b). As seen in the STM topography (Fig. 7c), an additional CO molecule is bound to the atom and locked in orientation. This can be more clearly seen in the TERS-mfm image of Fig. 7g, which is a composite constructed by mapping the CO vibrational line intensity in two different spectral windows. At the applied junction bias of 0.37 V, the 12C18O frequency on Au peaks at 2068 cm-1; the red shifted window (2042-2055 cm-1) yields the image of the Ag atom (Fig. 7e), while the blue edge of the CO peak (2072-2077) cm-1 images the CO molecule (Fig. 7f). Chemically speciated images with atomic resolution are obtained in the different spectral windows. At the 5.5 Å gap fixed by the STM set point, electrostatic forces dominate the interaction. Ascribing the spectral shifts entirely to the first order Stark effect with a tuning rate of 150 cm-1/V/Å,33 and assuming fields due to point charges, () = @A/ ' , the spectral shifts identify a positively polarized Ag atom with a net charge of +0.2e relative to Au, and a negatively charged CO molecule with a net charge of -0.1e relative to Au. The unusual binding geometry of the CO suggests that it is dominated by the interfacial dipole at the adatom-Au junction and the quadrupole of CO. In addition, the polarization of the surface electrons of Au in response to the Ag adatom can be seen. This is illustrated by the discretely sampled spectra as a function of distance from the Ag atom, recorded 10 Å apart (see Fig. 8a) with an integration time of 30 s. The


13

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 22

intensity of the CO vibration is anticorrelated with the topographic image of herringbone structure (Fig. 8b): it is enhanced on the FCC domain compared to the HCP domain. The frequency shifts monotonically as a function of distance (Fig. 8c), by 1 cm-1 over 40 Å, corresponding to a potential drop of 0.2 mV/Å. The potential drop relative to gold, ∆V, measures the local workfunction, which is affected up to at least 50 Å away from the adatom. While the analysis can be refined along lines presented for molecular force imaging with CO-terminated tips,58 the extracted images of atomic polarization illustrate that in addition to structure, electrostatic potentials can be mapped out as in atomically resolved Kelvin probe force microscopy.31

Figure 8: (a) Line cut across the STM topography (inset) showing the height of the silver adatom and the corrugation of the Au(111) surface reconstruction (0.1 nA, 0.25 V).


14

Page 15 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Integrated Raman intensity (b) and frequency of the CO peak (b) obtained via a Gaussian fit and acquired at specific points along the line cut. (30 s integration, 5 µW/µm2, 634 nm) The y-axis in (c) is broken to highlight the standard errors.

More generally, the vibrational frequency shift is due to the sum of intermolecular forces, B = −CD/C, and force gradients, E = C ' D/C ', acting on the anharmonic CO bond. The different ranges of electrostatic, dispersive, and Pauli exclusion forces determine the dominant interaction probed at a given distance and, hence, determine molecular shapes observed in molecular force microscopy. The advantages of a molecular transducer versus mesoscopic cantilevers derive from the dramatic increase in frequency of operation (1014 Hz vs. 106 Hz) and substantial localization of the measured force, determined by the vibrational amplitude of the molecular oscillator, Δ = |G = 1|| = 0H| = 0.034 Å. Although the anharmonic CO stretching frequency responds to local forces through the Stark effect,59 for the sake of comparison with mechanical harmonic cantilevers, consider the figure of merit for resolvable force: E Δ =

'L |G M

= 1|| = 0H| (4)

determined by the quality factor, Q, which reflects the accuracy with which frequency shifts can be measured. The spectral domain TERS measurement has the multiplexing advantage, where the uncertainty in frequency is determined by the goodness of the spectral fits, and therefore by the signal strength. As indicated by the error bars of the discrete measurements in Fig. 8c, @N̅, ~0.1 Q, giving a quality factor R = N̅, /@N̅, = 2 × 10+ . Using the stiffness of the 12C18O stretching mode, k = 1.7×103 N/m, forces of ~0.5 pN can be measured according to Equation 4. This favorably competes with advanced quartz cantilevers used with functionalized tips.60

CONCLUSIONS TER-sm offers spectromicroscopy on the Å-scale. However, its implementation rests upon the fabrication of tips with reliable performance. FDSS processing of electrochemically etched and polished silver-tips fulfills this requirement. The process self-sharpens, smoothens, and cleans silver tips, and demonstrably limits the far field scattering to the sole nanocavity mode between the atomically terminated tip and substrate. Localization of the field, rather than enhancement, is the crucial consideration in single molecule sensitivity and spectromicroscopy. Tips with reliable performance accelerate discovery, as previewed by the implementations used to validate the FDSS processed tips. We show that finely tuned tips can lead to large field enhancement by confining the signal to picocavities


15

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 22

of ≤ 100 Å3. A consequence of this extreme confinement is that TERS is a near-field effect, where plane-wave selection rules break down, and scattering driven by field gradients dominate the observable spectra. The contrast inversion between the STM and TER-sm images is a consequence, which affects spatial images. True spatial imaging is provided through TERS-mfm using CO-terminated Ag tips, which image molecular structure, forces, and local potentials with atomic resolution. Of particular value is the mapping of local workfunctions through the CO Stark shift, which gives access to charges and energetics of surfaces with atomic resolution. METHODS The instrument used in the present measurements has been described previously. Briefly, it consists of an ultrahigh vacuum (base pressure 4x10-11 Torr) cryogenic STM equipped with a parabolic collector (collection solid angle 2.7 sr), with focus precisely aligned to the tip apex by imaging EL from the tip.41 For Raman measurements, the tip-sample junction is illuminated at 45° with a single-mode 634 nm diode laser and the spectra are acquired with a Princeton Instruments SpectraPro 2300i spectrograph with a LN2-cooled CCD. For the tip preparation, two rounds of FDSS processing are required. First, FDSS processing was done in an external high vacuum chamber with a beam energy of +2 keV (chamber backfilled with Ar gas at ~5×10-5 Torr) and tip bias of +150 V. Second, FDSS processing was done in the main UHV STM chamber with a beam energy of +1 keV (chamber backfilled with Ne gas at ~5×10-5 Torr) and sample bias of +80 V. Tips were sputtered with ~4×1017 ions cm-2 during each treatment. Additional experimental details can be found in the supplement. Acknowledgements This research was supported by the grant of NSF Center for Chemical Innovation dedicated to Chemistry at the Space-Time Limit (CHE-1414466). We gratefully acknowledge Dr. Laura Rios for her contribution to the fabrication of the FDSS system, Kevin T. Crampton for recording SERS spectra of BPE, Angel Nunez for producing electrochemically etched silver tips, and former Managing Director Dr. Andre A. Schirotzek for his support of this project.

Supplementary Material: Computer assisted design of the batch production assembly and operating conditions of the ex-situ and in-situ FDSS process.


16

Page 17 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Author Contributions V. A. A. and J. L. conceived the idea and planned the project. N. T. and J. L designed and constructed the FDSS batch production system. N.T and J. L. performed experiments and recorded data. N.T, J.L. and V. A. A. co-wrote the manuscript.

ToC Figure:

REFERENCES (1)

Nie, S. Probing Single Molecules and Single Nanoparticles by SurfaceEnhanced Raman Scattering. Science 1997, 275, 1102–1106.

(2)

Kneipp, K.; Wang, Y.; Kneipp, H.; Perelman, L.; Itzkan, I.; Dasari, R.; Feld, M. Single Molecule Detection Using Surface-Enhanced Raman Scattering (SERS). Phys. Rev. Lett. 1997, 78, 1667–1670.

(3)

Le Ru, E. C.; Etchegoin, P. G. Single-Molecule Surface-Enhanced Raman Spectroscopy. Annu. Rev. Phys. Chem. 2012, 63, 65–87.

(4)

Yampolsky, S.; Fishman, D. A.; Dey, S.; Hulkko, E.; Banik, M.; Potma, E. O.; Apkarian, V. A. Seeing a Single Molecule Vibrate through Time-Resolved Coherent Anti-Stokes Raman Scattering. Nat. Photonics 2014, 8, 650–656.

(5)

Fleischmann, M.; Hendra, P. J.; McQuillan, A. J. Raman Spectra of Pyridine Adsorbed at a Silver Electrode. Chem. Phys. Lett. 1974, 26, 163–166.

(6)

Jeanmaire, D. L.; Van Duyne, R. P. Surface Raman Spectroelectrochemistry. J. Electroanal. Chem. Interfacial Electrochem. 1977, 84, 1–20.

(7)

Hayazawa, N.; Inouye, Y.; Sekkat, Z.; Kawata, S. Metallized Tip Amplification of near-Field Raman Scattering. Opt. Commun. 2000, 183, 333–336.

(8)

Pettinger, B.; Picardi, G.; Schuster, R.; Ertl, G. Surface Enhanced Raman Spectroscopy : Towards Single Molecule Spectroscopy. Electrochemistry 2000, 68, 942.

(9)

Stöckle, R. M.; Suh, Y. D.; Deckert, V.; Zenobi, R. Nanoscale Chemical Analysis by Tip-Enhanced Raman Spectroscopy. Chem. Phys. Lett. 2000, 318, 131–136.


17

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 22

(10) Anderson, M. S. Locally Enhanced Raman Spectroscopy with an Atomic Force Microscope. Appl. Phys. Lett. 2000, 76, 3130–3132. (11) Pozzi, E. A.; Goubert, G.; Chiang, N.; Jiang, N.; Chapman, C. T.; McAnally, M. O.; Henry, A.-I.; Seideman, T.; Schatz, G. C.; Hersam, M. C.; Van Duyne, R. P. Ultrahigh-Vacuum Tip-Enhanced Raman Spectroscopy. Chem. Rev. 2016, 117, 4961-4982. (12) Verma, P. Tip-Enhanced Raman Spectroscopy: Technique and Recent Advances. Chem. Rev. 2017, 117, 6447-6466. (13) Zhang, Z.; Sheng, S.; Wang, R.; Sun, M. Tip-Enhanced Raman Spectroscopy. Anal. Chem. 2016, 88, 9328–9346. (14) Zhang, R.; Zhang, Y.; Dong, Z. C.; Jiang, S.; Zhang, C.; Chen, L. G.; Zhang, L.; Liao, Y.; Aizpurua, J.; Luo, Y.; Yang, J. L.; Hou, J. G. Chemical Mapping of a Single Molecule by Plasmon-Enhanced Raman Scattering. Nature 2013, 498, 82–86. (15) Zhang, P.; Feist, J.; Rubio, A.; García-González, P.; García-Vidal, F. J. Ab Initio Nanoplasmonics: The Impact of Atomic Structure. Phys. Rev. B - Condens. Matter Mater. Phys. 2014, 90, 161407-1-161407-05. (16) Barbry, M.; Koval, P.; Marchesin, F.; Esteban, R.; Borisov, A. G.; Aizpurua, J.; Sánchez-Portal, D. Atomistic near-Field Nanoplasmonics: Reaching AtomicScale Resolution in Nanooptics. Nano Lett. 2015, 15, 3410–3419. (17) Payton, J. L.; Morton, S. M.; Moore, J. E.; Jensen, L. A Hybrid Atomistic Electrodynamics-Quantum Mechanical Approach for Simulating SurfaceEnhanced Raman Scattering. Acc. Chem. Res. 2014, 47, 88–99. (18) Trautmann, S.; Aizpurua, J.; Götz, I.; Undisz, A.; Dellith, J.; Schneidewind, H.; Rettenmayr, M.; Deckert, V. A Classical Description of Subnanometer Resolution by Atomic Features in Metallic Structures. Nanoscale 2017, 9, 391– 401. (19) Liu, P.; Chulhai, D. V.; Jensen, L. Single-Molecule Imaging Using Atomistic Near-Field Tip-Enhanced Raman Spectroscopy. ACS Nano 2017, 11, 5094– 5102. (20) Benz, F.; Schmidt, M. K.; Dreismann, A.; Chikkaraddy, R.; Zhang, Y.; Demetriadou, A.; Carnegie, C.; Ohadi, H.; de Nijs, B.; Esteban, R.; Aizpurua, J.; Baumberg, J. J. Single-Molecule Optomechanics in “picocavities.” Science 2016, 354, 726–729. (21) Roelli, P.; Galland, C.; Piro, N.; Kippenberg, T. J. Molecular Cavity Optomechanics as a Theory of Plasmon-Enhanced Raman Scattering. Nat. Nanotechnol. 2015, 11, 164–169. (22) Pozzi, E. A.; Goubert, G.; Chiang, N.; Jiang, N.; Chapman, C. T.; McAnally, M. O.; Henry, A.-I.; Seideman, T.; Schatz, G. C.; Hersam, M. C.; Van Duyne, R. P. Ultrahigh-Vacuum Tip-Enhanced Raman Spectroscopy. Chem. Rev. 2017, 117,


18

Page 19 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

4961–4982. (23) Chiang, N.; Jiang, N.; Chulhai, D. V.; Pozzi, E. A.; Hersam, M. C.; Jensen, L.; Seideman, T.; Van Duyne, R. P. Molecular-Resolution Interrogation of a Porphyrin Monolayer by Ultrahigh Vacuum Tip-Enhanced Raman and Fluorescence Spectroscopy. Nano Lett. 2015, 15, 4114–4120. (24) Blum, C.; Opilik, L.; Atkin, J. M.; Braun, K.; Kämmer, S. B.; Kravtsov, V.; Kumar, N.; Lemeshko, S.; Li, J. F.; Luszcz, K.; Maleki, T.; Meixner, A. J.; Minne S.; Raschke, M. B.; Ren, B.; Rogalski, J.; Roy, D.; Stephanides, B.; Wang, X.; Zhang, D.; Zhong, J.; Zenobi, R. Tip-Enhanced Raman Spectroscopy - An Interlaboratory Reproducibility and Comparison Study. J. Raman Spectrosc. 2014, 45, 22–31. (25) Chulhai, D. V.; Jensen, L. Determining Molecular Orientation With SurfaceEnhanced Raman Scattering Using Inhomogenous Electric Fields. J. Phys. Chem. C 2013, 117, 19622–19631. (26) Sass, J. K.; Neff, H.; Moskovits, M.; Holloway, S. Electric Field Gradient Effects on the Spectroscopy of Adsorbed Molecules. J. Phys. Chem. 1981, 85, 621–623. (27) Banik, M.; El-Khoury, P. Z.; Nag, A.; Rodriguez-Perez, A.; Guarrottxena, N.; Bazan, G. C.; Apkarian, V. a. Surface-Enhanced Raman Trajectories on a NanoDumbbell: Transition from Field to Charge Transfer Plasmons as the Spheres Fuse. ACS Nano 2012, 6, 10343–10354. (28) Gross, L.; Wang, Z. L.; Ugarte, D.; Mohn, F.; Moll, N.; Heer, W. a; Vincent, P.; Liljeroth, P.; Journet, C.; Meyer, G.; The Chemical Structure of a Molecule Resolved by Atomic Force Microscopy. Science 2009, 325, 1110–1114. (29) Chiang, C. -l.; Xu, C.; Han, Z.; Ho, W. Real-Space Imaging of Molecular Structure and Chemical Bonding by Single-Molecule Inelastic Tunneling Probe. Science 2014, 344, 885–888. (30) Betzig, E.; Trautman, J. K. Near-Field Optics: Microscopy, Spectroscopy, and Surface Modification beyond the Diffraction Limit. Science 1992, 257, 189– 195. (31) Mohn, F.; Gross, L.; Moll, N.; Meyer, G. Imaging the Charge Distribution within a Single Molecule. Nat. Nanotechnol. 2012, 7, 227–231. (32) Lambert, D. K. Observation of the First-Order Stark Effect of Co on Ni(110). Phys. Rev. Lett. 1983, 50, 2106–2109. (33) He, H. Y.; Pi, S. T.; Bai, Z. Q.; Banik, M.; Apkarian, V. A.; Wu, R. Q. Stark Effect and Nonlinear Impedance of the Asymmetric Ag-CO-Ag Junction: An Optical Rectenna. J. Phys. Chem. C 2016, 120, 20914–20921. (34) Oddershede, J.; Svendsen, E. N. Dynamic Polarizabilities and Raman Intensities. Chem. Phys. 1982, 64, 359–369.


19

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 22

(35) Gieseking, R.; Ratner, M. A.; Schatz, G. C. Theoretical Modeling of Voltage Effects and the Chemical Mechanism in Surface-Enhanced Raman Scattering. Faraday Discuss. 2017, 0, 1–23. (36) Banik, M.; Nag, A.; El-Khoury, P. Z.; Rodriguez Perez, A.; Guarrotxena, N.; Bazan, G. C.; Apkarian, V. A. Surface-Enhanced Raman Scattering of a Single Nanodumbbell: Dibenzyldithio-Linked Silver Nanospheres. J. Phys. Chem. C 2012, 116, 10415-10423. (37) Banik, M.; Apkarian, V. a.; Park, T.-H.; Galperin, M. Raman Staircase in Charge Transfer SERS at the Junction of Fusing Nanospheres. J. Phys. Chem. Lett. 2013, 4, 88–92. (38) Dickmann, K.; Demming, F.; Jersch, J. New Etching Procedure for Silver Scanning Tunneling Microscopy Tips. Rev. Sci. Instrum. 1996, 67, 845. (39) Opilik, L.; Dogan, Ü.; Szczerbińki, J.; Zenobi, R. Degradation of Silver near-Field Optical Probes and Its Electrochemical Reversal. Appl. Phys. Lett. 2015, 107, 1–6. (40) Sasaki, S. S.; Perdue, S. M.; Rodriguez Perez, A.; Tallarida, N.; Majors, J. H.; Apkarian, V. A.; Lee, J. Note: Automated Electrochemical Etching and Polishing of Silver Scanning Tunneling Microscope Tips. Rev. Sci. Instrum. 2013, 84, 96109. (41) Tallarida, N.; Rios, L.; Apkarian, V. A.; Lee, J. Isomerization of One Molecule Observed through Tip-Enhanced Raman Spectroscopy. Nano Lett. 2015, 15, 6386–6394. (42) Majors, J. H. Nonlocal Plasmonic Field Emission of Electrons from Focusing by Shrp Probe Tips, UCI, 2015. (43) Schmucker, S. W.; Kumar, N.; Abelson, J. R.; Daly, S. R.; Girolami, G. S.; Bischof, M. R.; Jaeger, D. L.; Reidy, R. F.; Gorman, B. P.; Alexander, J.; Ballard, J. B.; Randall, J. N.; Lydig, J. W. Field-Directed Sputter Sharpening for Tailored Probe Materials and Atomic-Scale Lithography. Nat. Commun. 2012, 3, 935. (44) Jackson, J. D. Classical Electrodynamics Third Edition. John Wiley & Sons, INC., 1999, 75–79. (45) Ferrari, A. C.; Robertson, J. Raman Spectroscopy of Amorphous, Nanostructured, Diamond-like Carbon, and Nanodiamond. Philos. Trans. R. Soc. A Math. Phys. Eng. Sci. 2004, 362, 2477–2512. (46) Hone, D.; Mü hlschlegel, B.; Scalapino, D. J. Theory of Light Emission from Small Particle Tunnel Junctions. Appl. Phys. Lett. 1978, 33, 203. (47) Rendell, R. W.; Scalapino, D. J.; Mü hlschlegel, B. Role of Local Plasmon Modes in Light Emission from Small-Particle Tunnel Junctions. Phys. Rev. Lett. 1978, 41, 1746–1750.


20

Page 21 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

(48) Dey, S.; Banik, M.; Hulkko, E.; Rodriguez, K.; Apkarian, V. A.; Galperin, M.; Nitzan, A. Observation and Analysis of Fano-like Lineshapes in the Raman Spectra of Molecules Adsorbed at Metal Interfaces. Phys. Rev. B - Condens. Matter Mater. Phys. 2016, 93, 1–6. (49) Pettinger, B.; Domke, K. F.; Zhang, D.; Schuster, R.; Ertl, G. Direct Monitoring of Plasmon Resonances in a Tip-Surface Gap of Varying Width. Phys. Rev. B Condens. Matter Mater. Phys. 2007, 76. (50) Chulhai, D. V.; Jensen, L. Determining Molecular Orientation With SurfaceEnhanced Raman Scattering Using Inhomogenous Electric Fields. J. Phys. Chem. C 2013, 117, 19622-19631. (51) Domke, K. F.; Pettinger, B. In Situ Discrimination between Axially Complexed and Ligand-Free Co Porphyrin on Au(111) with Tip-Enhanced Raman Spectroscopy. ChemPhysChem 2009, 10, 1794–1798. (52) Yang, W.; Hulteen, J.; Schatz, G. C.; Duyne, R. P. Van. A Surface-Enhanced Hyper-Raman and Surface-Enhanced Raman Scattering Study of Trans-1 , 2Bis ( 4-Pyridyl ) Ethylene Adsorbed onto Silver Film over Nanosphere Electrodes . Vibrational Assignments : Experiment and Theory. J. Chem. Phys. 1996, 104, 4313–4323. (53) Crampton, K. T.; Zeytunyan, A.; Fast, A. S.; Ladani, F. T.; Alfonso-Garcia, A.; Banik, M.; Yampolsky, S.; Fishman, D. A.; Potma, E. O.; Apkarian, V. A. Ultrafast Coherent Raman Scattering at Plasmonic Nanojunctions. J. Phys. Chem. C 2016, 37, 20943-20953. (54) Banik, M.; Rodriguez, K.; Hulkko, E.; Apkarian, V. A. Orientation-Dependent Handedness of Chiral Plasmons on Nanosphere Dimers: How to Turn a Right Hand into a Left Hand. ACS Photonics 2016, 3, 2482–2489. (55) Crampton, K. T.; Zeytunyan, A.; Fast, A. S.; Ladani, F. T.; Alfonso-Garcia, A.; Banik, M.; Yampolsky, S.; Fishman, D. A.; Potma, E. O.; Apkarian, V. A. Ultrafast Coherent Raman Scattering at Plasmonic Nanojunctions. J. Phys. Chem. C 2016, 120, 20943–20953. (56) Frisch, M. J.; Trucks, G. W.; Schlegel, H. B.; Scuseria, G. E.; Robb, M. A.; Cheesman, J. R.; Scalmani, G.; Barone, V.; Mennucci, B.; Petersson, G. A.; Nakatsuji, H.; Caricato, M.; Li, X.; Hratchian, H. P.; Izmaylov, A. F.; Bloino, J.; Zheng, G.; Sonnenberg, J. L.; Hada, M.; Ehara, M.; et al. Gaussian 09, Revision C.01, Gaussian, Inc., Wallingford CT, 2010. (57) McMahon, J. M.; Gray, S. K.; Schatz, G. C. Fundamental Behavior of Electric Field Enhancements in the Gaps between Closely Spaced Nanostructures. Phys. Rev. B - Condens. Matter Mater. Phys. 2011, 83, 115428-1-115428-5. (58) Ellner, M.; Pavliček, N.; Pou, P.; Schuler, B.; Moll, N.; Meyer, G.; Gross, L.; Peréz, R. The Electric Field of CO Tips and Its Relevance for Atomic Force Microscopy. Nano Lett. 2016, 16, 1974–1980.


21

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 22

(59) Hush, N. S.; Williams, M. L. Carbon Monoxide Bond Length, Force Constant and Infrared Intensity Variations in Strong Electric Fields: Valence-Shell Calculations, with Applications to Properties of Adsorbed and Complexed CO. J. Mol. Spectrosc. 1974, 50, 349–368. (60) Giessibl. Advances in Atomic Force Microscopy. 2013, 75, 1–35.


22

Tip-Enhanced Raman Spectromicroscopy on the Angstrom Scale