Transformation and Speciation Analysis of Silver Nanoparticles of

Jul 3, 2018 - Department of Soil and Water Sciences, Hebrew University of Jerusalem ... (7−10) The ingestion of AgNPs could have severe health risks...
0 downloads 0 Views 732KB Size
Subscriber access provided by University of Winnipeg Library

Ecotoxicology and Human Environmental Health

Transformation and Speciation Analysis of Silver Nanoparticles of Dietary Supplement in Simulated Human Gastrointestinal Tract Wenhao Wu, Ruojie Zhang, David Julian McClements, Benny Chefetz, Tamara Polubesova, and Baoshan Xing Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.8b01393 • Publication Date (Web): 03 Jul 2018 Downloaded from http://pubs.acs.org on July 4, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 33

Environmental Science & Technology

1

Transformation and Speciation Analysis of Silver Nanoparticles of

2

Dietary Supplement in Simulated Human Gastrointestinal Tract

3

Wenhao Wu1, Ruojie Zhang2, David Julian McClements2, Benny Chefetz3, Tamara Polubesova3,

4

Baoshan Xing1,*

5 6

1

Stockbridge School of Agriculture, University of Massachusetts, Amherst, MA 01003, USA

7

2

Department of Food Science, University of Massachusetts, Amherst, MA 01003, USA

8

3

Department of Soil and Water Sciences, Hebrew University of Jerusalem, Rehovot 76100, Israel

9 10 11 12

*Corresponding Author: Dr. Baoshan Xing, Phone: 413-545-5212, Email: [email protected]

13

1 ACS Paragon Plus Environment

Environmental Science & Technology

14

Abstract: Knowledge of the physicochemical properties of ingestible silver nanoparticles (AgNPs)

15

in human gastrointestinal tract (GIT) is essential for assessing their bioavailability, bioactivity, and

16

potential health risks. The gastrointestinal fate of AgNPs and silver ions from a commercial dietary

17

supplement was therefore investigated using a simulated human GIT. In the mouth, no dissolution or

18

aggregation of AgNPs occurred, which was attributed to the neutral pH and the formation of

19

biomolecular corona, while the silver ions formed complexes with biomolecules (Ag-biomolecule).

20

In the stomach, aggregation of AgNPs did not occur, but extensive dissolution was observed due to

21

the low pH and the presence of Cl-. In the fed state (after meal), 72% AgNPs (by mass) dissolved,

22

with 74% silver ions forming Ag-biomolecule and 26% forming AgCl. In the fasted state (before

23

meal), 76% AgNPs dissolved, with 82% silver ions forming Ag-biomolecule and 18% forming AgCl.

24

A biomolecular corona around AgNPs, comprised of mucin with multiple sulfhydryl groups,

25

inhibited aggregation and dissolution of AgNPs. In the small intestine, no further dissolution or

26

aggregation of AgNPs occurred, while the silver ions existed only as Ag-biomolecule. These results

27

provide useful information for assessing the bioavailability of ingestible AgNPs and their

28

subsequently potential health risks, and for the safe design and utilization of AgNPs in biomedical

29

applications.

30 31 32 33

2 ACS Paragon Plus Environment

Page 2 of 33

Page 3 of 33

34

Environmental Science & Technology

Abstract Art:

35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 3 ACS Paragon Plus Environment

Environmental Science & Technology

56

Introduction

57

Silver nanoparticles (AgNPs) have been utilized in a number of commercial products due to their

58

strong antimicrobial properties (1-3). The AgNPs present in these products may either intentionally

59

or unintentionally get into the human food chain. AgNPs have been incorporated into commercially

60

available supplements and functional foods intended for oral consumption due to their proposed

61

health benefits (4-5). The AgNPs incorporated into the food containers or packaging materials for

62

protecting foods may leach out into the foods and be consumed with the foods (3). Moreover, the

63

increasingly manufactured AgNPs will be inevitably released into the environment, particularly

64

during their use in agricultural systems, where they may eventually become associated with plants or

65

animals intended for human consumption. Indeed, Frohlich et al. (6) estimated that the daily intake

66

of AgNPs by humans is about 20-80 µg based on food consumption. The daily intake dose could be

67

even higher when the silver supplements were involved (7-10). The ingestion of AgNPs could have

68

severe health risks (7-10). For example, Asharani et al. (8) linked increased concentrations of

69

ingested AgNPs to increased mortality and developmental defects such as cardiac arrhythmia and

70

spinal deformation. Other researchers have reported that ingestion of AgNPs can cause argyria in

71

humans (4,9,10). For these reasons, there has been increasing concern about the potential

72

environmental and health risks associated with AgNPs.

73

After being ingested, AgNPs will first pass through the gastrointestinal tract (GIT), which

74

consists of mouth, esophagus, stomach, small intestine and large intestine regions, and ultimately

75

either be directly excreted from the body within feces or urine, or be absorbed through the small

76

intestinal epithelium and enter the circulatory system where they can cause toxic effects (11-12). The

77

bioavailability of AgNPs depends on their initial physicochemical properties (e.g., concentration, 4 ACS Paragon Plus Environment

Page 4 of 33

Page 5 of 33

Environmental Science & Technology

78

particle size distribution, surface properties and chemical species), as well as any changes in these

79

properties as they pass through the GIT (11-12). Therefore, knowledge of the fate of AgNPs within

80

the human GIT is of great importance, because the AgNPs properties before, during, and after

81

passing through the GIT could be significantly different (11-15). To date, only a few studies have

82

investigated the fate of AgNPs in a simulated human GIT (13-15). Walczak et al. (13) showed that

83

AgNPs dissolved and formed AgCl in the simulated gastric fluid and subsequently AgNPs

84

concentration recovered in the simulated small intestinal fluid, but the AgNPs size distribution was

85

not altered in simulated GIT. Kastner et al. (14) and Bohmert et al. (15) both observed that AgNPs

86

partially aggregated when exposed to simulated GIT, but the size of the formed aggregates was still

87

in the nanoscale. A number of other studies focused on the aggregation, dissolution, and

88

transformation of AgNPs only under simulated gastric conditions (16-19). These previous

89

investigations provide important information; however, knowledge of the fate of AgNPs in human

90

GIT is still limited due to the following reasons. First, the AgNPs investigated in these studies (13-19)

91

are all laboratory-synthesized; no ingestible AgNPs or commercial products actually from the market

92

were used. The structural and physicochemical properties of commercial AgNPs, such as

93

concentration, particle size distribution, interfacial properties and chemical species, may be

94

appreciably different from those of laboratory-synthesized AgNPs. Thus, the results from previous

95

studies may not accurately predict the fate of ingestible AgNPs in the human GIT. Second, it was

96

reported that AgNPs could be oxidized into Ag+ and then combine with Cl- in the gastrointestinal

97

fluids to form AgCl (13,18). Alternatively, Ag+ ions can also combine with the various types of

98

biomolecules (e.g., mucin and digestive enzymes) in the gastrointestinal fluids and form

99

Ag-biomolecule complexes, because most biomolecules contain sulfhydryl, carboxyl and hydroxyl 5 ACS Paragon Plus Environment

Environmental Science & Technology

100

groups that can strongly interact with Ag+ ions through complexation or electrostatic attraction (20).

101

Thus, the chemical species of silver in human GIT could be AgNPs, AgCl, Ag-biomolecule and free

102

Ag+ ions. However, the formation of Ag-biomolecule complexes was not examined in previous

103

studies (13-19), and no comprehensive and quantitative speciation analysis of the silver in human

104

GIT has previously been conducted. Third, the applicability of the results from previous studies

105

(16-19) is rather limited in predicting the gastrointestinal fate of AgNPs because the effects of the

106

saliva and small intestinal fluid were neglected. Therefore, further investigations are needed to more

107

accurately predict the gastrointestinal fate of ingestible AgNPs under simulated human GIT

108

conditions and their bioavailability.

109

In this study, a commercially available silver nanoparticle dietary supplement (AgDS) was

110

selected to investigate the fate of ingestible AgNPs in a simulated human GIT. According to the

111

product specification provided by the commercial supplier, the AgDS is designed to support and

112

boost a healthy human immune system through the antimicrobial function of AgNPs. It is a pure

113

silver solution with about 75% of silver in nanoparticle form (AgNPs) and 25% in ionic form (Ag+),

114

and the total silver concentration is around 20 mg/L. A simulated human GIT model containing

115

mouth, stomach and small intestine phases was used in this study to examine the potential

116

gastrointestinal fate of the AgDS. The specific objectives of this study were to: (i) investigate the

117

gastrointestinal fate including aggregation, dissolution and transformation of AgNPs from the AgDS

118

in the simulated GIT; (ii) quantitatively analyze the distribution of different silver species from

119

AgDS in the simulated GIT; (iii) understand the transformation pathways and mechanisms of AgNPs

120

from AgDS in the simulated GIT. The obtained results in this study will be useful for understanding

121

the human exposure to AgNPs through ingestion and assessing the bioavailability of ingestible 6 ACS Paragon Plus Environment

Page 6 of 33

Page 7 of 33

Environmental Science & Technology

122

AgNPs in better-understood forms and their potential health risks, because the physicochemical

123

properties of AgNPs can be significantly changed as they passed through the GIT.

124 125

Materials and Methods

126

Materials. The AgDS (a dietary supplement) was purchased online (Amazon). Gastrointestinal

127

components, including mucin from porcine stomach, α-amylase from porcine pancreas (≥10

128

units/mg), pepsin from porcine gastric mucosa (≥250 units/mg), pancreatin (4×USP) and bile salts

129

from porcine pancreas, were purchased from the Sigma-Aldrich Co. (St. Louis, MO). Sodium

130

chloride (>99.0%), sodium nitrate (>99.0%), sodium hydroxide (>97.0%), hydrochloric acid

131

(36.5%-38.0%), nitric acid (68.0%-70.0%) were purchased from Fisher Scientific Co. (Fair Lawn,

132

NJ). Ultrapure deionized water was used in the experiment.

133

Simulated Gastrointestinal Tract Model. The AgDS was passed through a simulated GIT to

134

mimic the passage through human mouth, stomach and small intestine. This simulated GIT model

135

(Table S1) was based on the one used in previous studies (21-23) with some slight modifications as

136

described below. (i) Mouth phase: Simulated saliva, containing mucin (3.0 g/L), α-amylase (0.5 g/L)

137

and NaCl (2.0 g/L) was preheated to 37 °C, and then the pH was adjusted to 6.8 using NaOH or HCl

138

solutions. Fifteen mL of AgDS (suggested daily dosage) were mixed with 15 mL of simulated saliva

139

in a 100 mL glass beaker, and then placed in an incubator shaker at 37 °C for 2 minutes to mimic the

140

mouth phase. (ii) Stomach phase: both fed state (i.e., after meal) and fasted state (i.e., before meal)

141

were considered in this study. Fifteen mL “bolus” sample resulting from the mouth phase was mixed

142

with 15 mL fed gastric fluid (3.2 g/L pepsin, 3.0 g/L mucin and 2.0 g/L NaCl) or fasted gastric fluid

143

(0.4 g/L pepsin, 3.0 g/L mucin and 2.0 g/L NaCl) in a 100 mL glass beaker, and the pH of the 7 ACS Paragon Plus Environment

Environmental Science & Technology

144

mixture was adjusted to 2.5. Then, the mixture was placed in an incubator shaker at 37 °C for 2 hours

145

to mimic the stomach phase. (iii) Small intestine phase: Twenty-five mL “chyme” sample from the

146

fed or fasted stomach phase was adjusted to pH 7.0, and then mixed with 5 mL fed small intestinal

147

fluid (30.0 g/L bile salts, 14.4 g/L pancreatin, and 52.6 g/L NaCl) or fasted small intestinal fluid (3.0

148

g/L bile salts, 2.4 g/L pancreatin, and 52.6 g/L NaCl) in a 100 mL glass beaker. The pH of the

149

mixture was adjusted to 7.0. Then, the mixture was placed in the incubator shaker at 37 °C for 2

150

hours to mimic the small intestine phase. All the incubations in the simulated GIT model were

151

conducted in the dark.

152

Determination of AgNPs and Ag+ in the AgDS. To obtain the total silver concentration of

153

AgDS, 1 mL of AgDS was totally dissolved in 4 mL concentrated HNO3 and then analyzed by

154

Inductively Coupled Plasma Mass Spectrometry (ICPMS-2030, Shimadzu). The AgNPs and Ag+ ion

155

concentrations in AgDS were quantified by ultrafiltration/ICPMS according to a previous study (24).

156

The AgNPs in the AgDS was first removed by centrifugation (4000 g, 20 min) using Amicon Ultra-4

157

3K centrifugal filter devices and then the Ag+ ion concentration was detected using ICPMS. The

158

mass loss of Ag+ on the filter was determined to be negligible (300 nm, thus, the presence of the AgNPs can be

173

detected and quantified. Second, the formation of AgCl in the simulated GIT could not influence the

174

UV-Visible signals of AgNPs, because the AgNPs-AgCl core-shell structure was not formed

175

(Supporting Information, Page S6). Third, the UV-Visible spectroscopy has already been successfully

176

used to quantify the AgNPs in biological media in many previous studies (16,17,28). According to

177

previous studies (16,17,28), the aggregation and dissolution of AgNPs can both be detected using

178

UV-Visible spectroscopy. The dissolution of AgNPs reduces the intensity of the absorption peak at

179

λmax around 400 nm, because there are less AgNPs adsorbing the incident light after dissolution.

180

While the aggregation of AgNPs not only decreases the intensity of the absorption peak at λmax

181

around 400 nm, but also increases the intensity of another much broader absorption peak at

182

λmax >500 nm (16,17,28). This phenomenon occurs because the aggregation of AgNPs reduces its

183

surface energy, resulting in significant reduction in the surface plasmon resonant frequency (ωmax)

184

and significant increase in the λmax of AgNPs (29). Therefore, the absorption peak at λmax around 400

185

nm is characteristic of non-aggregated monodisperse AgNPs, while the absorption peak at λmax >500

186

nm is characteristic of aggregated AgNPs. Furthermore, the absorption peak at λmax >500 nm is much

187

broader due to the random aggregation of AgNPs. Thus, the UV-Visible spectroscopy method 9 ACS Paragon Plus Environment

Environmental Science & Technology

188

(Agilent 8453) applied in this study was able to characterize both the aggregation and dissolution of

189

the AgNPs from the AgDS collected from the simulated GIT.

190

Silver Speciation Analysis. AgDS contains both AgNPs and silver ions. During passage through

191

the GIT, the AgNPs from AgDS could be oxidized and dissolve into silver ions. The silver ions

192

present in the gastrointestinal fluids may therefore come from the original AgDS or from AgNPs

193

dissolution within the GIT, and may be present in three different forms: free Ag+, Ag-biomolecule

194

and AgCl. The AgNPs concentration in the gastrointestinal fluids can be detected by UV-Visible

195

spectroscopy as mentioned above, while the total silver ion concentration can be calculated by mass

196

difference. In order to quantify the concentrations/distributions of different silver ion species in the

197

gastrointestinal fluids, Ag+ (AgNO3) with a series of known concentrations (0, 5, 10, 15, 20 and 25

198

mg/L) were passed through the simulated gastrointestinal tract. 4 mL of the resultant mouth, stomach,

199

and small intestine digesta fluids were respectively added into Amicon Ultra-4 3K centrifugal filter

200

devices and then centrifuged (4000 g, 30 min). The free Ag+ from the digesta was passed through the

201

filter and analyzed by ICPMS, while the Ag-biomolecule and AgCl from the digesta that were

202

blocked by the filter, were collected and rinsed three times using deionized water until no free Cl-

203

can be detected by ion chromatography (Dionex, Thermo Scientific). Then, 4 mL of 20 mmol/L

204

Na2S2O3 was added into the mixture of the Ag-biomolecule and AgCl in the centrifugal filter device

205

and shaken (150 rpm, 1 h) to dissolve the AgCl, because the stability of the thiosulfate complexes of

206

Ag+ are much higher than that of AgCl (20,30). The concentration of dissolved Cl- from AgCl can be

207

detected by ion chromatography, and then the silver concentration from AgCl can be calculated

208

correspondingly. According to a control experiment, >87% AgCl can be dissolved by Na2S2O3.

209

Finally, the silver concentration from Ag-biomolecule was calculated by subtracting the silver 10 ACS Paragon Plus Environment

Page 10 of 33

Page 11 of 33

Environmental Science & Technology

210

concentration of free Ag+ and AgCl from the total silver ion concentration. Therefore, the

211

quantitative relationship between the total silver ion concentration in the gastrointestinal fluids and

212

the concentrations/distributions of different silver ion species was established. The method flowchart

213

of the silver speciation analysis is presented in the Page S7 of Supporting Information. As the total

214

silver ion concentration of AgDS in the GIT can be calculated by subtracting the total silver

215

concentration measured as mentioned above from the AgNPs concentration quantified by the UV-vis

216

spectroscopy, the concentrations/distributions of different silver ion species from AgDS in the GIT

217

could be calculated using the established quantitative relationship above.

218 219

Results and Discussion

220

Analysis of Silver Nanoparticle Dietary Supplement. Analysis of the AgDS using

221

ultrafiltration/ICPMS indicated that it contained 17.96±0.09 mg/L of AgNPs and 8.00±0.03 mg/L

222

of silver ions. The particle size distribution of the AgNPs in the supplement were measured by both

223

TEM (Figure 1A) and DLS (Figure 1B). The particle size distribution obtained from the TEM

224

images (Figure S3) reflects the core-size distribution of AgNPs. The mean core diameter and

225

standard deviation was 14.0±2.5 nm. The volume average particle size distribution obtained from

226

DLS analysis reflects the hydrodynamic size distribution of AgNPs, which was 32.6±9.4 nm. The

227

surface charge of the AgNPs was negative at neutral pH and the negative charge decreased in

228

magnitude as the pH decreased, with a point of zero charge around pH 2.5 (Figure 1C). Meanwhile,

229

trace amounts of Na+, Cl-, and NO3- and total organic carbon (TOC) were detected in the AgDS

230

(Table S2). However, the effects of these trace ingredients on the fate of AgNPs in the GIT would be

231

negligible, considering the much higher concentrations of NaCl and organic biomolecules in the 11 ACS Paragon Plus Environment

Environmental Science & Technology

232

simulated GIT (Table S1), and the much stronger interactions between AgNPs and organic

233

biomolecules with sulfhydryl groups (20).

234

UV-Visible Spectra of AgDS in the Simulated Gastrointestinal Tract. The UV-Visible spectra

235

of the AgDS in the simulated GIT with both background and dilution corrections are displayed in

236

Figure 2. The absorbance of AgDS only decreased slightly after exposure to the mouth phase (around

237

2.0%), but there was a redshift of the λmax from 397 nm to 410 nm. In contrast, there was a steep

238

decrease in the absorbance of the AgDS after exposure to the stomach phase (around 72% for the fed

239

state and 76% for the fasted state), and there was a further redshift of λmax (from 410 nm to 420 nm

240

for the fed state and from 410 nm to 416 nm for the fasted state). Finally, the absorbance of the

241

AgDS decreased slightly after exposure to the small intestine phase (around 10% for the fed state and

242

11% for the fasted state), but there was a blueshift of λmax (from 420 nm to 408 nm for the fed state

243

and from 416 nm to 403 nm for the fasted state). However, this was still a net redshift when

244

compared to the λmax value of the original AgDS (397 nm). Since the λmax of AgNPs depends on the

245

surface plasmon resonant frequency (ωmax) (29), the shift of λmax is likely to reflect changes in the

246

surface properties of AgNPs. The redshifts of the λmax of AgDS after mouth and stomach phases were

247

relatively small (< 23 nm) and the λmax value was still around 400 nm, which suggests that most of

248

the AgNPs were not aggregated (16,17,28). Additionally, the width of the shifted peak did not

249

significantly increase. Thus, the redshifts observed in Figure 2 are probably not due to aggregation of

250

the AgNPs. Alternatively, it has been reported that the binding of biomolecules to monodisperse

251

AgNPs leads to the formation of biomolecular corona that induces a small redshift around the λmax of

252

monodisperse AgNPs, due to the change of ωmax (29,31,32). The ωmax of AgNPs is highly sensitive

253

to the refractive index of the surrounding medium. Proteins and other biomolecules have a higher 12 ACS Paragon Plus Environment

Page 12 of 33

Page 13 of 33

Environmental Science & Technology

254

refractive index than water, and therefore their adsorption to AgNPs surfaces can decrease ωmax and

255

increase λmax, thereby leading to a redshift (29,31,32). Studies have shown that an increase in ionic

256

strength can reduce the refractive index of biomolecules and thus reduce the magnitude of the

257

redshift (33). Therefore, we assume that the binding of biomolecules to AgNPs in the saliva and

258

gastric fluids could be the reason for the redshift of λmax, while the relatively high NaCl

259

concentration in the small intestinal fluids could be responsible for the reduced redshift. The

260

biomolecular corona around the AgNPs can be seen from the TEM images (Figures S3), and more

261

evidence supporting this explanation can be found in the Supporting Information (Pages S9-S10).

262

Aggregation and Dissolution of AgNPs from AgDS in the Simulated Gastrointestinal Tract.

263

Mouth phase: The fact that there was little change in the maximum absorbance measured by

264

UV-Visible spectrophotometry of the AgDS before and after exposure to the mouth phase (Figure 2)

265

suggests that there was no dissolution of the AgNPs. Moreover, no absorption peak was observed at

266

λmax >500 nm, which suggests that there was no aggregation of the AgNPs in the mouth phase. The

267

lack of dissolution and aggregation of the AgNPs under simulated oral conditions is also supported

268

by the SAXS data, i.e., the SAXS intensities and calculated particle size distributions of the original

269

AgDS suspension and the AgDS placed in saliva were almost the same (Figure S1). The main change

270

of the AgNPs observed in the mouth phase was the coating of the nanoparticle surfaces with

271

biomolecules (mucin and α-amlyase), which can be seen from the TEM image (Figure S3). The

272

presence of this biomolecular corona could enhance the stability of the AgNPs to aggregation and

273

dissolution (34,35). Moreover, the neutral pH condition within the simulated saliva was not

274

conducive to AgNPs dissolution (24).

275

Stomach phase: The pronounced decrease in the maximum absorbance for the AgDS after being 13 ACS Paragon Plus Environment

Environmental Science & Technology

276

exposed to both the fed (71.8%) and the fasted (75.9%) stomach phases (Figure 2) indicates that

277

significant dissolution of the AgNPs occurred. Interestingly, the degree of dissolution was not

278

significantly different for the fed and fasted stomach phase conditions. Again, no absorption peak

279

was observed at λmax >500 nm, implying that there was no aggregation of the AgNPs in both the fed

280

and fasted stomach phases. Further insights into the fate of the AgNPs in the stomach phase were

281

obtained by measuring changes in the UV-Visible spectra of the AgDS over time (Figures 3A, 3B).

282

The λmax and peak width of the AgDS remained constant throughout 2 hours of incubation in both the

283

fed and fasted stomach phases, again indicating that particle aggregation did not occur. Experiments

284

were also carried out to determine the role of the biomolecules on the gastric fate of the nanoparticles.

285

The maximum absorbance of the AgDS in the simulated gastric fluid without biomolecules (Figure

286

3C) decreased much faster than that in the gastric fluid with biomolecules (Figure 3A). Moreover, in

287

the absence of biomolecules, there was evidence of nanoparticle aggregation, with a broad

288

absorption peak appearing at λmax >500 nm. Thus, the surface-bound biomolecules (Figure S3)

289

played important roles in slowing down the dissolution rate and preventing aggregation of the AgNPs

290

in the gastric fluid. To elucidate the roles of the different biomolecules (mucin, α-amylase, or pepsin)

291

in protecting the AgNPs in the gastric fluids, AgDS was digested in the gastric fluids containing

292

separate biomolecules (fed state) and the spectra are displayed in Figures 3D-3F. In the gastric fluid

293

containing mucin, the λmax and the peak width of AgDS both kept constant during the 2 hours

294

digestion, similar to that in the gastric fluid containing all biomolecules. Moreover, the decreasing

295

rates of absorbance were almost the same (Figures 3A,3D). In the gastric fluid containing α-amylase,

296

an absorption peak associated with aggregated AgNPs (about 500 nm) emerged and the absorbance

297

decreased faster than in the gastric fluid containing all biomolecules (Figures 3A,3E). In the gastric 14 ACS Paragon Plus Environment

Page 14 of 33

Page 15 of 33

Environmental Science & Technology

298

fluid containing pepsin, a redshift of the λmax was observed and the peak width became broader

299

(Figures 3F). Overall, the fairly similar UV-Visible spectra of the AgDS in the gastric fluid

300

containing all biomolecules (Figure 3A) and in gastric fluid containing only mucin (Figure 3D)

301

suggests that mucin played the main role in slowing down the dissolution rate and preventing the

302

aggregation of AgNPs in the stomach phase. Mucin is rich in cysteines and contains plenty of

303

sulfhydryl groups that could strongly interact with AgNPs and silver ions (20,36,37). Pepsin and

304

α-amylase contain much less sulfhydryl groups as compared with mucin (38,39). Hence, the

305

interaction between mucin and AgNPs in the dietary supplements was much stronger than the

306

interaction with pepsin/α-amylase, and mucin primarily protected AgNPs in the stomach phase. The

307

dissolution of AgNPs into silver ions has been reported in acidic solutions through their oxidation by

308

oxygen (20,40). This dissolution could be enhanced by chloride ions in the surrounding solution

309

leading to the formation of insoluble AgCl (20,41). An experiment was then carried out to confirm

310

the role of the chloride ions and pH in the dissolution process. The decrease in the maximum

311

absorbance of AgDS in the gastric fluid occurred much more slowly when nitric acid (NO3-, Figure

312

3G) was used to control the pH (2.5) rather than hydrochloric acid (Cl-, Figure 3A). In addition, the

313

decrease occurred much more slowly when the pH of the gastric fluid was adjusted to 5.0 (Figure 3H)

314

rather than 2.5 (Figure 3A) using HCl. Overall, these results indicate that the dissolution rate of

315

AgNPs was accelerated by H+ and Cl-, but slowed down by biomolecules in the stomach phase.

316

Small intestine phase: The maximum absorbance of AgDS decreased slightly after exposure to

317

both fed and fasted small intestine phases (Figure 2). This effect may have occurred because the

318

AgNPs continued to dissolve during the short operation time (around 3 min) between the stomach

319

and small intestine phases. These results therefore suggest that there was little further dissolution of 15 ACS Paragon Plus Environment

Environmental Science & Technology

320

the AgNPs in both fed and fasted small intestine phases. No absorption peak was observed at

321

λmax >500 nm, which suggested that no aggregation of the AgNPs occurred in both the fed and fasted

322

states. The lack of further dissolution of AgNPs can mainly be attributed to the fact that the pH was

323

changed from 2.5 to 7.0, so that the concentration of H+ that could accelerate the dissolution reaction

324

significantly decreased (20,40). Furthermore, the biomolecular corona around the AgNPs that can

325

prevent AgNPs from aggregation and dissolution could still be the reason for the good stability of the

326

AgNPs in the small intestine phase. The TEM images clearly showed the presence of a biomolecular

327

corona on the AgNPs in the small intestine phase (Figure S3).

328

Previous studies (13-15) have explored the aggregation and dissolution of chemically

329

synthesized and surface-coated AgNPs in a simulated human GIT. However, the main differences of

330

those previous studies from this study were observed. First, partial aggregation of AgNPs was

331

reported in the mouth phase by Kastner et al. (14). Second, partial aggregation of AgNPs in the

332

stomach phase was reported by Kastner et al. (14) and Bohmert et al. (15). Third, the particle number

333

of AgNPs was reported to increase to its original value after exposure to the small intestine phase by

334

Walczak et al. (13). The partial aggregation of AgNPs observed in the mouth and stomach phases by

335

other workers may be due to the much higher and unrealistic dose of AgNPs used, i.e., 3 g/L (14) and

336

10% (w/w) (15). As a consequence, more aggregation occurred because of the higher nanoparticle

337

concentration in solution. In our study, the AgNPs concentration in the original dietary supplement

338

was 17.96 mg/L, and became lower when passed through the simulated GIT due to dilution effects

339

(Table S1). Consequently, AgNP aggregation may have been less likely because of the reduction in

340

the particle-particle collision frequency and the increase in entropy of mixing effects. The particle

341

size distribution of the AgNPs also remained constant throughout the whole GIT in the study by 16 ACS Paragon Plus Environment

Page 16 of 33

Page 17 of 33

Environmental Science & Technology

342

Walczak et al. (13), who also used a relatively low initial AgNPs concentration (10 mg/L). Thus, the

343

aggregation state of AgNPs in the GIT appears to be sensitive to its initial concentration, and the lack

344

of aggregation reported in this study would be more practically relevant since the used AgDS was a

345

commercially available product containing AgNPs. Walczak et al. (13) attributed the recovery of

346

AgNPs particle number in the small intestine to the reversible clustering and disassembling of

347

AgNPs in the GIT. However, since there was substantial mass loss of AgNPs in the stomach phase

348

due to the dissolution, only the reversible clustering and disassembling cannot result in the recovery

349

of AgNPs particle number. In this study, recovery of AgNPs was not observed in the small intestine

350

phase. Moreover, no other study has confirmed the AgNPs recovery in the small intestine phase.

351

Besides the aforementioned studies (13-15), several other investigations (16-19) showed the

352

aggregation and rapid dissolution of AgNPs in simulated gastric fluids. However, the lack of

353

biomolecules (such as mucin and digestive enzymes) in their simulated gastric fluids limits the

354

applicability and implication of their results because these biomolecules can inhibit the aggregation

355

and slow down the dissolution rate of AgNPs as observed in this work. Furthermore, the impacts of

356

the mouth and small intestine phases on the fate of the AgNPs in the human GIT were not considered

357

in these earlier studies (16-19). Therefore, in order to explore the realistic fate of ingestible AgNPs in

358

the human digestive system, a comprehensive GIT model needs to be applied.

359

Transformation and Speciation Analysis of AgNPs and Silvers Ions from AgDS in the

360

Simulated Gastrointestinal Tract. The quantitative relationship between the total silver ion

361

concentration in the gastrointestinal fluids and the distributions of different silver ion species (free

362

Ag+, Ag-biomolecule and AgCl) were established as follows. First, no free Ag+ ions were observed in

363

any of the gastrointestinal fluids according to the ultrafiltration/ICPMS results. Second, the 17 ACS Paragon Plus Environment

Environmental Science & Technology

Page 18 of 33

364

quantitative relationship between the percentage of silver ions as AgCl species (PAgCl) and the silver

365

ion concentration (C) in the gastrointestinal fluids are listed below and displayed in Figure 4A.

366

Mouth:

367 368

(0