Trap-Door Like Irreversible Photo Induced Charge Transfer In A Donor

Trap-Door Like Irreversible Photo Induced. Charge Transfer In A Donor-Acceptor Complex. Carlos R. Medrano. †,‡ and Cristián G. Sánchez. ∗,†,...
0 downloads 0 Views 2MB Size
Subscriber access provided by Kaohsiung Medical University

Energy Conversion and Storage; Plasmonics and Optoelectronics

Trap-Door Like Irreversible Photo Induced Charge Transfer in a Donor-Acceptor Complex Carlos Medrano, and Cristian G. Sanchez J. Phys. Chem. Lett., Just Accepted Manuscript • DOI: 10.1021/acs.jpclett.8b01043 • Publication Date (Web): 11 Jun 2018 Downloaded from http://pubs.acs.org on June 11, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

Trap-Door Like Irreversible Photo Induced Charge Transfer In A Donor-Acceptor Complex Carlos R. Medrano†,‡ and Cristi´an G. S´anchez∗,†,‡ †Universidad Nacional de C´ ordoba. Facultad de Ciencias Qu´ımicas. Departamento de Qu´ımica Te´orica y Computacional. Ciudad Universitaria X5000HUA, C´ordoba, Argentina ‡Instituto de Investigaciones Fisicoqu´ımicas de C´ordoba, Consejo Nacional de Investigaciones Cient´ıficas y T´ecnicas (INFIQC - CONICET), Ciudad Universitaria X5000HUA, C´ordoba, Argentina E-mail: [email protected]

1

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Abstract For efficient conversion of light into useful energy sources, is very important to study and describe the first steps of primary charge-transfer process in natural structures and artificial devices. The time-scale of these process in artificial photosynthetic and photovoltaic devices are on the order of femto to picoseconds, and involve vibronic coupling of electrons and nuclei and also nuclear alleviation to enhance charge separation. Here we present an atomistic description of the photoexcited electron dynamics in a noncovalently bonded system formed by an hydrogenated nanodiamond as donor and a perylene diimide as an acceptor. The complex shows extremely fast charge transfer, separation, and stabilization within 90 fs. This stabilization is purely electronic in nature. To the best of our knowledge, these results show for the first time, that it is possible to stabilize charge without polaron formation or nuclear relaxation reaching a steady-state enhanced by a pure electronic reorganization.

Graphical TOC Entry

2

ACS Paragon Plus Environment

Page 2 of 27

Page 3 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

Light-induced charge transfer and subsequent charge separation are fundamental processes for a variety of phenomena including artificial and natural photosynthesis and solar energy conversion in photovoltaic cells. It is well known that the excitation of the ”specialpair” and the primary process in photosynthesis are followed by a series of secondary reactions involving electron transfer. These secondary reactions are faster than charge recombination processes, allowing an efficient charge separation. As a result of this process, photosynthetic organisms can obtain useful chemical redox energy from electronic excitation in the reaction center. 1 Following Nature’s strategy, several dyads and triads based on porphyrin derivatives have been synthesized and studied. From the first dyads, based on porphyrin covalently linked with quinone, C60 , carotenoid or aromatic imides, 2–6 to triads based on carotenoid-porphyrinquinone or carotenoid-porphyrin-C60 . 7,8 The first charge-separation event in these systems occurs within 3 ps to approximately 40 fs. 9–13 This kind of supramolecular structures were used to fabricate single-material organic solar cells (SMOCS) for light to electricity conversion applications 14 but with low power conversion energy (PCE, record of 2.2% 15 ), probably due to the fast charge recombination they present. 16 Another approach to organic solar cells (OSCs) are bilayer heterojunctions and bulk heterojunction architectures, where the active layer is formed by a blend of donor and acceptor materials. The bulk heterojunction is the most popular and efficient architecture due to the higher donor-acceptor interface area, where charge separation occurs. 17 Nowadays, the most common acceptor material used in bulk heterojunction solar cells are fullerene derivatives (like [6,6]-phenyl-C61-butyric acid methyl ester, PC61 BM and [6,6]-phenyl-C71-butyric acid methyl ester PC71 BM), 18 commonly blended with an acceptor conjugated polymer like poly(3-hexylthiophene) (P3HT). Experimental results using transient absorption spectroscopy for the study of the charge transfer process in these blends shows that the charge carriers are generated within the time resolution of the instrument (∼100fs). 19 Brabec et al. have also revealed an ultrafast charge transfer process in a bulk heterojunction with a time

3

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

constant of around 45 fs, using ultrafast spectroscopic techniques. 20 In both cases, the coherent nature of the oscillations are associated with phonon modes coupled with the electronic excitation of the conjugated polymer. Recent experimental and theoretical studies confirm that coherent vibronic coupling between electrons and nuclei is of key importance for the first steps of charge separation in covalent, 21 non-covalently 22 linked organic systems, and also in inorganic materials like vertically stacked transition-metal dichalcogenide. 23,24 Last years, the PCE for this kind of Organic solar cells surpassed 10% by developing novel p-type semiconductors (donors) but maintaining fullerenes as the acceptor material. 25,26 In recent years, there was particular interest in developing new acceptor materials due to limited visible light absorption, difficult functionalization, high production cost and bad mechanical properties of the fullerene derivatives. 18 3,4,9,10-Perylenetetracarboxylic acid diimides (PDI) and their derivatives are promising acceptor materials due to their high visible light absorption, good electron-accepting ability, high electron mobility and strong thermal, chemical and photochemical stabilities. 27 Shuixing Li, et al. reviewed recent progress in non-fullerene acceptors for efficient OSC, 28 showing PCE of 8.3% 29 and 9.15% 30 for blends composed of a widely used polymer donor and PDI derivatives as acceptors. In this work we present a computational study of a supramolecular arrangement composed of a hydrogenated nanodiamond interacting with a PDI molecule. The system shows ultrafast charge transfer in the scale of few tens of fs after photoexcitation of the acceptor. This system belogs therefore to the same class of systems as the dyads and triads mentioned above. After the charge transfer process, the system reaches a stable steady state showing extremely efficient charge separation, avoiding charge recombination processes in the studied time window. Since our method does not take into account nuclear motion, a pure electronic reordering of the of the system after charge separation is the reason for the irreversibility of the ultrafast charge transfer process. A novel component of the system we show is that the hole acceptor is a nanosized diamond particle. Nanodiamonds are outstanding materials with properties like high surface area, surface structure tunability,

4

ACS Paragon Plus Environment

Page 4 of 27

Page 5 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

excellent mechanical and optical properties, biocompatibility and chemical stability. 31 The surface chemistry of nanodiamonds allows to attach many different functional groups to their surface when compared with other carbon-based materials like nanotubes. For example, hydrogenated nanodiamonds can be obtained 32 as well as reactive C-F and C-Cl surfaces for wet chemistry functionalization. 33 This chemical versatility would allow to further elaborate on the basic structure we show in order to ensure efficient and time stable charge separation. Within light capture, nanodiamonds have attracted considerable interest as material for solar cells 34 including applications as anodes, 35 p-type semiconductor 36 in OSC and light scattering material 37 in Dye-Sensitized Solar Cells (DSSCs). The ireversibility of the light induced charge-separation process is given by a three stage mechanism. First, an electron hole pair is formed in the PDI molecule within the first 20fs. This is then followed by electron transfer from a manifold of nanodiamond states (with energy tuned within the optical gap of the acceptor) within the next 20fs. Then, purely electronic stabilization of the charge separated state is caused by energy detuning between donor and acceptor states. Given the very large chemical hardness of diamond, its charging induces a large change in the relative energies between the donor states, whereas the acceptor state is only slightly modified in energy upon hole annihilation. These relative change in energy is the cause of rapid detuning of donor and acceptor states, stabilizing the charge separated state. The mechanism works in a trap-door like fashion, in which an electron is transfered from the ND to the PDI but Rabi oscillations of the electron back to the nanodiamond is prevented by electrostatic detuning. Diamond surface energies were calculated using a slab structure periodically repeated of 16 carbon layers at least and allowing 6 layers on each side of the the slab to relax. This method was used by G. Kern and J. Hafner who presented ab initio local-density-functional calculations of the electronic structure of clean and hydrogenated diamond (110) surfaces. 38 Here, we performed the same calculations for 3 clean diamond low-index surfaces within the density functional tight-binding approach. Table 1 shows the diamond surfaces energies in

5

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

comparison with the values obtained by G. Kern and J. Hafner. The results shows good agreement with ab initio results. Hence, our tight-binding approach can reproduce the structures and energies obtained with DFT. Table 1: Surface energies of low-index diamond surfaces (in eV per surface site) calculated with dftb model. The values obtained are compared with those presented in reference.

a

Diamond surface Present result Referencea 100 2dbb 3.46 3.63 b 110 1db 1.68 1.66 111 3dbb 4.03 4.63 38 b G. Kern and J. Hafner , db: dangling bonds.

It could be observed that the smallest surface energy corresponds to the 110 diamond face (1.68 eV per surface site). Taking this fact into account, we built nanodiamond structures of 80

15 C26H30 C44H42 C140H90 C190H110

Abs / a.u.

60

12

n states

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 27

40

C26H30 C44H42 C140H90 C190H110

9

6

20 3

0 -15

-10

-5

0

5

10

15

Energy / eV

(a)

(b)

0 6

8

10

12

14

16

Energy / eV

(c)

Figure 1: (a) Irregular octahedral Nanodiamons of different sizes.(b) Density of states for the ND structures.(c) Calculated spectra of the NDs. different sizes in a shape that maximizes the 110 surface exposed. We observe previously that structures with multiple faces exposed show instability, probably due to a high edge energy between different faces for crystals of this size. The structures were hydrogen-passivated obtaining stable nanodiamonds of irregular octahedral shape (similar to structures previously reported in literature 39,40 ). These structures are shown in figure 1a. In order to study the electronic properties, we calculated the density of states of the nanodiamonds (see figure 6

ACS Paragon Plus Environment

Page 7 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

1b). The DOS shows a typical “insulator” material with a large band gap. The quantum confinement effect is observed which in accordance with the trend observed by Fokin, Andrey A and Schreiner, Peter R in ab initio band gap calculations of hydrogen-terminated nanodiamonds. 40 The larger the size, the smaller the band gap. From 10.9 eV for the smallest ND (C26 H30 ) to 8.7 eV for the biggest ND (C190 H110 ) studied here. In order to study the optical properties, absorption spectra of the NDs were calculated and are displayed in figure 1c. A decrease in the energy of the lowest energy excitation is observed as the nanodiamond size decreases. This agrees with the quantum confinement effect at the nanometer scale and the lowering of the band gap observed in figure 1c (b). Next, we build a donor + acceptor complex composed of a Perylene tetracarboxilic diimide interacting with a hydrogen-terminated ND by London dispersion forces (see figure 2a). Figure 2b displays the evolution of the Mulliken charge distributions in the ND (donor) and the PDI (acceptor), upon photo-excitation of the complex with time-dependent electric field pulse perturbation at 2.2 eV in resonance with the HOMO-LUMO transition of the PDI ˚-1 . (as it can be seen in the absorption spectra in figure S2) and with an intensity of 0.1 V A From figure 2b we observe that the acceptor molecule (PDI) becomes increasingly negatively charged as a function of time during the duration of the pulse, this charge transfer continues for a shot time after the pulse reaching a steady state after 90 fs. The opposite process occurs in the donor. A net charge is transferred from the ND to the PDI molecule. A similar process can be observed in an analogous covalently-linked system (see figures S1a and S1b). As can be seen from figure S2 the lowest energy band that appears in the absorption spectrum is the PDI HOMO-LUMO transition, furthermore, no new bands appear upon formation of the complex. This evidence suggest the absence of spurious charge transfer excitations in this particular system and that the calculated excited state structure is correct. We must stress that the described charge transfer process occurs once a significant population has been transfered from the HOMO to the LUMO of the PDI. It does not correspond to a charge transfer excitation but to a dynamic process of energy reorganization that happens after the

7

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

excitation and therefore outside the scope of a linear response description. Monitoring the

∆q(t) / a.u.

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 27

1 0.8 0.6 0.4 0.2 0 -0.2 -0.4 -0.6 -0.8 -1 0

pulse sin C190H110 PDI

25

50

2

75 100 125 150 175 200

t / fs (a)

(b)

Figure 2: (a) Donor-acceptor complex, hydrogenated-ND + PDI. (b) Charge as a function of time for donor (black) and acceptor (blue). The squared-sinusoidal pulse perturbation in tune with the HOMO-LUMO transition of the acceptor is represented in red. dipole moments of the donor and the acceptor, we see that the steady state is a dynamic state since the dipole moment of the acceptor keeps oscillating after charge transfer process is complete (see figure S3). Three things are remarkable in this process. The first one is the amount of charge transferred, one full electron. The second is the time-scale of the process, less than 90 fs are needed to complete the transference and 80% of the charge is transfered within less than 50 fs. Third, the system reaches a stable steady state after the pulse perturbation ends which last for the whole simulation time. In other words, the charge separation seems to be extremely efficient in the system proposed, avoiding any charge recombination process in these time scales. The evidence discards a charge transfer excitation since at the excitation energy at which the pulse is tuned the only active excitation is the HOMO-LUMO excitation of the acceptor (and the time-scale of a charge transfer excitation would be in the order of a few femtoseconds). The time-scale of the process and the fact that nuclear motion is not taken into account point to a new photo induced charge transfer mechanism. All these data leads us to believe that there must be a pure electronic reordering of the electronic structure 8

ACS Paragon Plus Environment

Page 9 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

of the system that enhances charge separation preventing charge recombination and leading to a stable steady-state in a trap-door like mechanism. We also have studied the process dependence with the field intensity and pulse duration. As the field intensity increases, the positive charge reached for the donor at the steady-state increases (see figure S4). As the pulse width increases, the positive charge reached for the donor at the steady-state increases as well but it takes more time to achieve the charge separated state (see figure S5). The amount of transfered charge depends exponentially on the distance between donor and acceptor as can be expected from the decrease in electronic coupling between the two, see figure S6. We additionally investigate the dependence of the process with the nanodiamond size, observing a decrease of the steady-state charge as the nanodiamond size decreases (see figure S7). This decrease in steady state charge with size is related to the lower density of ND donor states within the optical gap for smaller structures. To discard the possibility that a particular arrangement causes this unusual process we studied the configuration space of the smallest complex (C26 H30 +PDI). We performed Born-Oppenheimer molecular dynamics at 500K, take random configurations from this trajectory, and perform the corresponding electron dynamics (for further details of the molecular dynamics see section S2.6 in supporting information). We find that the charge transfer process is not a characteristic of a particular configuration, it is geometry independent to the extent explored by the performed sampling (see figure S8). In order to further investigate the charge transfer mechanism, we studied the evolution of the density matrix in the molecular orbital basis set. This study provides a more detailed understanding of the nature of the excitation. We have used this method in previous works for a complete characterization of the type of injection mechanism in DSSC, 41 and for a deeper understanding of the molecular orbitals involved in the excitation of photosynthetic pigments outside the scope of the Fermi golden rule. 42 Figure 3 (lower graph) shows the time-dependent molecular orbital populations for the donor + acceptor complex (figure 2a left) when a pulse perturbation in tune with the exci-

9

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

t / fs

∆q(t) / a.u.

0 10 20 30 40 50 60 70 80 90 100 1 0.8 0.6 0.4 0.2 1 0.8

ρmol

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

0.6 0.4 0.2 0 0 10 20 30 40 50 60 70 80 90 100

t / fs Figure 3: (upper graph) Donor charge as a function of time. (lower graph), GS orbital population as a function of time for the donor-acceptor complex. The basis used is constructed from the molecular orbitals of the ground state. tation energy of the acceptor is applied. The upper graph in figure 3 shows the evolution of the donor charge (ND). From figure 3 we can divide the process in 3 stages. The first stage is a preparation step (from 0 to 20 fs), the charge of the donor remains close to zero during this stage but population transfer can be observed from the HOMO to the LUMO of the acceptor (black and red curves). After that, we can see a whole re-organization of several states in the charge transfer stage (from 20 to 50 fs). Many states are involved in this process. Finally, we found the stabilization stage, where the charge of the donor reach a steady-state (see figure 2b) over 100fs with an accompanying change in a broad manifold of the molecular orbitals. After the steady state is reached, molecular orbital populations remain steady around an average value, with fast oscillations that correspond to the carrier frequency of the pulse (not shown in the figure). In order to gain insight into the electronic nature of the process, we calculated the Projected Density of States (PDOS) of the ground state and the corresponding cationic and anionic states of the system. Figure 4a and 4b shows the evolution of the PDOS as the

10

ACS Paragon Plus Environment

Page 10 of 27

Page 11 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

negative and positive charge of the system increases respectively. At the neutral state, the PDOS anion -4

-3

-2

-1

PDOS cation 0

-4

Neutral

Optical Gap

Neutral

-0.2 e

C190H110 PDI

+0.2 e

-0.4 e

+0.4 e

-0.6 e

+0.6 e

-0.8 e

+0.8 e

-1.0 e

+1.0 e

-4

-3

-2

-1

0

-4

Energy / eV

-3

-2

-1

0

Optical Gap C190H110 PDI

-3

-2

-1

0

Energy / eV

(a)

(b)

Figure 4: Projected Density of States (PDOS) for the hydrogenated-ND + PDI complex for different partial amounts of charge. (a) Negative partial charge values. (b) Positive partial charge values. Nanodiamond PDOS in red, PDI PDOS in green, total DOS in black. Charges are decremented or incremented in 0.2 e steps. The rectangles in each figure highlight the optical gap of the acceptor molecule (PDI). In all cases the PDOS are referenced to the LUMO energy of the system. nanodiamond has plenty of states to donate charge, located at the optical gap of the acceptor, enhancing the charge transfer process. As the system charges, an electronic reordering takes place, that leads to an energy change of the states. The nanodiamond states change their energies, leaving the optical gap. The number of states that leaves the gap, for the largest system studied, is of 45 for the case of a negatively charged system and 13 for the case of a positively charged system. This reduction in the states within the optical gap avoids the inverse transfer process, reaching rapidly and irreversibly the steady state we have seen in figure 2b. In other words, these states can transfer charge to the acceptor until they detune from the optical gap. The random surface substitution of H atoms by F strongly affect the charge dynamic of the system. We built ND + PDI complexes with different F percentages in the nanodiamond surface(see section S3.1 in supporting information). Then, we calculated the charge transfer

11

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

upon photostimulation and compared the dynamics obtained with the purely hydrogenatedND + PDI complex. The figure 5 shows the evolution of the Mulliken charge distribution in the ND (donor) upon the photo excitation of the fluorinated complexes with a pulse time-dependent electric field perturbation in tune with the acceptor excitation energy. The charge transferred decreases strongly as the F percentage on the surface increases, reaching an order of magnitude difference between the fully hydrogenated-ND and the fully fluorinated-ND. Besides the decrease of the amount of charge transferred, fluorinated-NDs do not reach a steady-state within the 200fs simulation window as the hydrogenated-NDs do.

∆q(t) ND / a.u.

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1.1 1 0.9 0.8 0.7 0.6 0.5 0.4 0.3 0.2 0.1 0 0

0% F 30% F 60% F 100% F

25 50 75 100 125 150 175 200

t / fs Figure 5: Donor charge as a function of time for different fluorination percentages of the nanodiamonds. These results show the effect of the surface fluorination in the electronic properties of the ND. The strong electronegativity of the F moves the NDs surface states energies to more negative values as shown in figure S10 for the PDOS evolution of the anion and cation total fluorinated-ND + PDI complex. It can be observed that for the neutral complex, there are no nanodiamond states in the optical gap of the acceptor. This fact avoid the charge transfer mechanism described above, showing a completely different charge dynamic through the time as it can be seen in the figure 5. In consequence, the system does not reach a steady-state 12

ACS Paragon Plus Environment

Page 12 of 27

Page 13 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

within the simulated time window and significantly decreases the total transferred charge. The evidence allows us to propose a three stage trap-door like irreversible charge transfer in which an electron hole pair is firstly created at the PDI, then the hole is filled by available electrons from a manifold of ND states that are close in energy which then detune. This detuning process upon charge separation is the key for the trap door mechanism. The working principle requires that donor and acceptor have adequate ionization energies and electron affinities in order to ensure the directionality of charge transfer. Furthermore, the chemical hardness of the donor (2.41 eV) and acceptor (5.51 eV) systems differ substantially. Where  I−A ∂µ = 2 , I and A being the ionization energy and the hardness is calculated as 43 η = 21 ∂N electronic affinity respectively. This difference in hardness ensures that charging of the donor produces a large change in relative energies between donor and acceptor, causing a sudden detuning of these states which is the cause for the observed irreversibility of the process. Our simulations do not take into account the possibility of nuclear motion. Given the fact that most of the charge transfer happens over a very short period of time we would expect, based on our experience of how systems react to such sudden changes in electronic structure, coherent breathing oscillations to be launched impulsively in both systems. 44 The effect of these would increase the detuning (given by the sudden nuclear motion) on one side (helping the transfer) but lowering the hardness of the ND on the other side (since a new degree of freedom over which the system can relax would be added). It is very hard to assess the relative importance of these two processes. An estimation on the importance of the second effect can be assessed pertubatively by recalculating the values of hardness by relaxing the geometries of the respective anion and cation. The new values of hardness are 3.12 eV and 4.61 eV for the PDI and ND respectively. This would indicate that incorporating nuclear motion might reduce the amount of transfered charge via a reduction of the effective hardness difference between donor and acceptor. Within the present work we have studied the charge transfer process between irregular octahedral nanodiamond structures (as donor) and an organic common dye like PDI (as

13

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

acceptor), performing simulations of the time evolving electronic structure under visible irradiation. The main result shows an ultrafast charge transfer in the hydrogenated-ND + PDI complex. The system reaches a stable steady-state in less than a 90 fs, transferring one electron from the donor to the acceptor after the pulse irradiation. The charge separation is extremely fast and efficient in this system, related to a resonance and the subsequent separation of states. These result show that is possible to obtain an stable charge-separated state enhanced only by a pure electronic reorganization of the system, without polaron formation or/and nuclear relaxation, by a purely electronic Trap-door like mechanism in which donor and acceptor orbitals dynamically respond to the transferred charge, suddenly detuning precluding charge recombination. To the best of our knowledge, this is the very first time that this phenomenon has been described. Our information at present, limited by the time windows of the simulation, does not allow us to reach into longer times and asses the importance of processes such as back-electron transfer that may occur on the ps to ns timescales. We believe that the present system (as is the case of the triads that are described in the first paragraphs of the paper) is just a possible component of a bigger light harvesting structure that stabilizes and further separates the charge via, for example, a chain of redox reactions or other mechanisms such as those that take place in photosynthetic reaction centers, dye sensitized or organic solar cells. A trap-door like mechanism is proposed by which the charge transfer state is stabilized electro-statically in a dynamic fashion by the charge separation induced detuning of donor and acceptor states. The mechanism requires the combination of a donor-acceptor pair with very different chemical hardness. In the case shown here the PDI system is chemically soft and can accommodate charge easily but the nanodiamond system states respond strongly to charging. This difference in response between the two systems provides the driving force for the purely electronic stabilization of the charge transfer state. Another requisite is that the donor has a manifold of states initially in tune with the acceptor optical gap that can transfer charge, this manifold acts as a reservoir that can fill the hole while detuning (a

14

ACS Paragon Plus Environment

Page 14 of 27

Page 15 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

single donor state would immediately detune). The hard system is then also required to be a nanosystem with a large density of states in tune with the acceptor. This phenomenon could be of extremely useful in electronic applications where the efficient irreversible charge separation is critical, like light harvesting devices. We demonstrate that the process depends strongly on the ND-surface-structure, showing that fluorinatedNDs never reach an steady-state within the simulated time window and transfer an order of magnitude less charge than the hydrogenated-ND at the same conditions. Pointing to the fact that the charge transfer efficiency can be tuned using surface modifications with differing electronegativity. Further comprehension of this kind of stabilization is now needed, there are opened questions like: Are there other systems where we can observed this phenomenon? Can we observe the same experimentally? We believe that the presence of nanodiamonds in a PDI solution should cause strong quenching of the PDI fluorescence. This could be a first step towards an experimental verification of the studied phenomenon.

Computational Methods The Self-Consistent-Charge Density-Functional-Tight-Binding (SCC-DFTB) method was used to describe the electronic structure of the ground state (GS) in all studied systems. 45–47 Under the basis of a controlled approximation of Density Functional Theory (DFT), this method has been used with success to describe quantum properties and electronic structures of large organic and bio-inorganic systems. 47,48 We compute the GS Hamiltonian (HGS ) and overlap matrix (S) using the DFTB+ package, 49 which is an implementation of the SCCDFTB method. With the HGS and the S matrix we can obtain the initial GS reduced single-electron density matrix (ρ). The pbc-0-3 DFTB parameter set was employed in order to obtain the electronic structure of the nanodiamonds and organic molecules presented in this work. Starting from the initial ρ we can obtain the excited state properties of a system, applying

15

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

an external perturbation and monitoring the evolution of the density matrix through time. In other words, a real-time propagation of the reduced single-electron density matrix (ρ) under the influence of an time-varying external field allow us to describe electronic dynamics the whole system. This method has been used, and described in the past by us, 41,42,50–59 and others, by propagating molecular orbitals instead of the single-electron density matrix 60 and in a linear response framework. 61 The light matter interaction in the DFTB approach that we use is incorporated in the Hamiltonian in the dipole approximation as:

ˆ ˆ DFTB (ˆ ˆ · E(t) H(t) =H ρ(t)) − µ

ˆ is the operator that, when traced with the density matrix generates the dipole where µ moment of the Mulliken charges:

ˆ ρ] = Tr[µˆ

X

rI δqi

I

In this way the time dependent external electric field enters the dynamics explicitly, in the atomic orbital basis. Particularly, the absorption spectra of the systems presented in this work were obtained after the application of an initial perturbation in the shape of a delta Dirac. The intensity of this perturbation was 0.001 V ˚ A-1 (within the linear response regime). The non-equilibrium properties, as the charge transfer processes, were calculated after the application of an initial perturbation in the shape of a squared-sinusoidal pulse of 50 fs in all cases. The intensity of this perturbation was of 0.1 V˚ A-1 equivalent to 1.35x1011 W/cm2 (out of the linear response regime).

Acknowledgement The authors acknowledge financial support from SeCyT UNC. This work used computa-

16

ACS Paragon Plus Environment

Page 16 of 27

Page 17 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

tional resources from CCAD - Universidad Nacional de C´ordoba (http://ccad.unc.edu.ar/), in particular the Mendieta Cluster, which is part of SNCAD - MinCyT, Rep´ ublica Argentina. CRM is grateful for a studentship from CONICET.

Supporting Information Available Additional data and characterization for the systems studied: This material is available free of charge via the Internet at http://pubs.acs.org/.

References (1) Blankenship, R. E. Molecular Mechanisms of Photosynthesis; 2008; pp 1–321. (2) Tabushi, I.; Yanagita, M. Efficient Intramolecular Quenching and Electron Transfer in Tetraphenylporphyrin Attached with Benzoquinone or Hydroquinone as a Photosystem Model. Tetrahedron Letters 1979, 257–260. (3) Kong, J. L. Y.; Loach, P. A. Syntheses of covalently-linked porphyrin-quinone complexes. Journal of Heterocyclic Chemistry 1980, 17, 737–744. (4) Liddell, P. a.; Sumida, J. P.; Macpherson, A. N.; Noss, L.; Seely, G. R.; Clark, K. N.; Moore, A. L.; Moore, T. a.; Gust, D. Preparation and Photophysical Studies of Porphyrin-C 60 Dyads. Photochemistry and Photobiology 1994, 60, 537–541. (5) Hermant, R. M.; Liddell, P. A.; Lin, S.; Alden, R. G.; Kang, H. K.; Moore, A. L.; Moore, T. A.; Gust, D. Mimicking Carotenoid Quenching of Chlorophyll Fluorescence. Journal of the American Chemical Society 1993, 115, 2080–2081. (6) Cowan, J. A.; Sanders, J. K. M. Pyromellitimide-bridged porphyrins as model photosynthetic systems. 1. Synthesis and steady state fluorescence properties. J. Chem. Soc., Perkin Trans. 1 1985, 2435–2437. 17

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(7) Moore, T. A.; Gust, D.; Mathis, P.; Mialocq, J. C.; Chachaty, C.; Bensasson, R. V.; Land, E. J.; Doizi, D.; Liddell, P. A.; Lehman, W. R. et al. Photodriven charge separation in a carotenoporphyrin-quinone triad. Nature 1984, 307, 630–632. (8) Carbonera, D.; Di Valentin, M.; Corvaja, C.; Agostini, G.; Giacometti, G.; Liddell, P. A.; Kuciauskas, D.; Moore, A. L.; Moore, T. A.; Gust, D. EPR investigation of photoinduced radical pair formation and decay to a triple state in a carotene-porphyrinfullerene triad. Journal of the American Chemical Society 1998, 120, 4398–4405. (9) Gust, D.; Moore, T. A.; Moore, A. L. Mimicking photosynthetic solar energy transduction. Accounts of Chemical Research 2001, 34, 40–48. (10) Kodis, G.; Liddell, P. a.; Moore, A. L.; Moore, T. a.; Gust, D. Synthesis and photochemistry of a carotene–porphyrin–fullerene model photosynthetic reaction center. Journal of Physical Organic Chemistry 2004, 17, 724–734. (11) Kuciauskas, D.; Liddell, P. A.; Lin, S.; Johnson, T. E.; Weghorn, S. J.; Lindsey, J. S.; Moore, A. L.; Moore, T. A.; Gust, D. An artificial photosynthetic antenna-reaction center complex. Journal of the American Chemical Society 1999, 121, 8604–8614. (12) DSouza, F.; Chitta, R.; Ohkubo, K.; Fukuzumi, S. Corrole- Fullerene Dyads: Formation of Long- Lived charge- Separated States in Nonpolar Solvents. J. Am. Chem. Soc. 2008, 130, 14263. (13) Kuciauskas, D.; Liddell, P.; Lin, S.; Stone, S.; Moore, A.; Moore, T.; Gust, D. Photoinduced Electron Transfer in Carotenoporphyrin-Fullerene Triads: Temperature and Solvent Effects. The Journal of Physical Chemistry B 2000, 104, 4307–4321. (14) Roncali, J. Single material solar cells: The next frontier for organic photovoltaics? Advanced Energy Materials 2011, 1, 147–160.

18

ACS Paragon Plus Environment

Page 18 of 27

Page 19 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

(15) Narayanaswamy, K.; Venkateswararao, A.; Nagarjuna, P.; Bishnoi, S.; Gupta, V.; Chand, S.; Singh, S. P. An Organic Dyad Composed of Diathiafulvalene-Functionalized Diketopyrrolopyrrole–Fullerene for Single-Component High-Efficiency Organic Solar Cells. Angewandte Chemie - International Edition 2016, 55, 12334–12337. (16) Lin, Y.; Li, Y.; Zhan, X. Small molecule semiconductors for high-efficiency organic photovoltaics. Chemical Society Reviews 2012, 41, 4245. (17) Hoppe, H.; Sariciftci, N. S. Organic solar cells: An overview. Journal of Materials Research 2004, 19, 1924–1945. (18) Chen, W.; Zhang, Q. Recent progress in non-fullerene small molecule acceptors in organic solar cells (OSCs). J. Mater. Chem. C 2017, 5, 1275–1302. (19) Kaake, L. G.; Moses, D.; Heeger, A. J. Coherence and uncertainty in nanostructured organic photovoltaics. Journal of Physical Chemistry Letters 2013, 4, 2264–2268. (20) Brabec, C. J.; Zerza, G.; Cerullo, G.; De Silvestri, S.; Luzzati, S.; Hummelen, J. C.; Sariciftci, S. Tracing photoinduced electron transfer process in conjugated polymer/fullerene bulk heterojunctions in real time. Chemical Physics Letters 2001, 340, 232–236. (21) Rozzi, C. A.; Falke, S. M.; Spallanzani, N.; Rubio, A.; Molinari, E.; Brida, D.; Maiuri, M.; Cerullo, G.; Schramm, H.; Christoffers, J. et al. Quantum coherence controls the charge separation in a prototypical artificial light-harvesting system. Nature communications 2013, 4, 1602. (22) Falke, S. M.; Rozzi, C. A.; Brida, D.; Maiuri, M.; Amato, M.; Sommer, E.; De Sio, A.; Rubio, A.; Cerullo, G.; Molinari, E. et al. Coherent ultrafast charge transfer in an organic photovoltaic blend. Science 2014, 344, 1001–1005.

19

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(23) Long, R.; Prezhdo, O. V. Quantum Coherence Facilitates Efficient Charge Separation at a MoS2 /MoSe2 van der Waals Junction. Nano Letters 2016, 16, 1996–2003. (24) Zheng, Q.; Saidi, W. A.; Xie, Y.; Lan, Z.; Prezhdo, O. V.; Petek, H.; Zhao, J. PhononAssisted Ultrafast Charge Transfer at van der Waals Heterostructure Interface. Nano Letters 2017, 17, 6435–6442. (25) He, Z.; Xiao, B.; Liu, F.; Wu, H.; Yang, Y.; Xiao, S.; Wang, C.; Russell, T. P.; Cao, Y. Single-junction polymer solar cells with high efficiency and photovoltage. Nature Photonics 2015, 9, 174–179. (26) Liao, S. H.; Jhuo, H. J.; Yeh, P. N.; Cheng, Y. S.; Li, Y. L.; Lee, Y. H.; Sharma, S.; Chen, S. A. Single junction inverted polymer solar cell reaching power conversion efficiency 10.31% by employing dual-doped zinc oxide nano-film as cathode interlayer. Scientific Reports 2014, 4, 4–10. (27) Zhang, X.; Lu, Z.; Ye, L.; Zhan, C.; Hou, J.; Zhang, S.; Jiang, B.; Zhao, Y.; Huang, J.; Zhang, S. et al. A potential perylene diimide dimer-based acceptor material for highly efficient solution-processed non-fullerene organic solar cells with 4.03% efficiency. Advanced Materials 2013, 25, 5791–5797. (28) Li, S.; Liu, W.; Li, C.-Z.; Shi, M.; Chen, H. Efficient Organic Solar Cells with NonFullerene Acceptors. Small 2017, 1701120, 1701120. (29) Meng, D.; Fu, H.; Xiao, C.; Meng, X.; Winands, T.; Ma, W.; Wei, W.; Fan, B.; Huo, L.; Doltsinis, N. L. et al. Three-Bladed Rylene Propellers with Three-Dimensional Network Assembly for Organic Electronics. Journal of the American Chemical Society 2016, 138, 10184–10190. (30) Duan, Y.; Xu, X.; Yan, H.; Wu, W.; Li, Z.; Peng, Q. Pronounced Effects of a Triazine Core on Photovoltaic Performance–Efficient Organic Solar Cells Enabled by a PDI Trimer-Based Small Molecular Acceptor. Advanced Materials 2017, 29 . 20

ACS Paragon Plus Environment

Page 20 of 27

Page 21 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

(31) Mochalin, V. N.; Shenderova, O.; Ho, D.; Gogotsi, Y. The properties and applications of nanodiamonds. Nature nanotechnology 2012, 7, 11–23. (32) Arnault, J.-C.; Petit, T.; Girard, H.; Chavanne, A.; Gesset, C.; Sennour, M.; Chaigneau, M. Surface chemical modifications and surface reactivity of nanodiamonds hydrogenated by CVD plasma. Phys. Chem. Chem. Phys. 2011, 13, 11481–11487. (33) Liu, Y.; Gu, Z.; Margrave, J. L.; Khabashesku, V. N. Functionalization of Nanoscale Diamond Powder: Fluoro-, Alkyl-, Amino-, and Amino Acid-Nanodiamond Derivatives. 2004, 3924–3930. (34) Kausar, A. Nanodiamond: a multitalented material for cutting edge solar cell application. Materials Research Innovations 2017, 8917, 1–13. (35) Lim, C. H. Y. X.; Zhong, Y. L.; Janssens, S.; Nesladek, M.; Loh, K. P. Oxygenterminated nanocrystalline diamond film as an efficient anode in photovoltaics. Advanced Functional Materials 2010, 20, 1313–1318. (36) Nagata, A.; Oku, T.; Kikuchi, K.; Suzuki, A.; Yamasaki, Y.; Osawa, E. Fabrication, nanostructures and electronic properties of nanodiamond-based solar cells. Progress in Natural Science: Materials International 2010, 20, 38–43. (37) Karimi Tafti, M. H.; Sadeghzadeh, S. M. Novel use of nanodiamonds as light-scattering material in dye-sensitized solar cells. Journal of Materials Science: Materials in Electronics 2016, 27, 5225–5232. (38) Kern, G.; Hafner, J. Ab initio calculations of the atomic and electronic structure of clean and hydrogenated diamond (110) surfaces. Physical Review B 1997, 56, 4203–4210. (39) Areshkin, D. A.; Shenderova, O. A.; Adiga, S. P.; Brenner, D. W. Electronic properties of diamond clusters: Self-consistent tight binding simulation. Diamond and Related Materials 2004, 13, 1826–1833. 21

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(40) Fokin, A. A.; Schreiner, P. R. Band gap tuning in nanodiamonds: first principle computational studies. Molecular Physics 2009, 107, 823–830. (41) Oviedo, M. B.; Zarate, X.; Negre, C. F. A.; Schott, E.; Arratia-P´erez, R.; S´anchez, C. G. Quantum Dynamical Simulations as a Tool for Predicting Photoinjection Mechanisms in Dye-Sensitized TiO 2 Solar Cells. The Journal of Physical Chemistry Letters 2012, 3, 2548–2555. (42) Oviedo, M. B.; S´anchez, C. G. Transition dipole moments of the Qy band in photosynthetic pigments. Journal of Physical Chemistry A 2011, 115, 12280–12285. (43) Parr, R. G.; Yang, W. Density Functional Theory of Atoms and Molecules; Oxford University Press, 1989. (44) Bonafe, F. P.; Aradi, B.; Guan, M.; Douglas-Gallardo, O. A.; Lian, C.; Meng, S.; Frauenheim, T.; Sanchez, C. G. Plasmon-driven sub-picosecond breathing of metal nanoparticles. Nanoscale 2017, 9, 12391–12397. (45) Elstner, M.; Porezag, D.; Jungnickel, G.; Elsner, J.; Haugk, M.; Frauenheim, T.; Suhai, S.; Seifert, G. Self-consistent-charge density-functional tight-binding method for simulations of complex materials properties. Physical Review B 1998, 58, 7260–7268. (46) Elstner, M.; Seifert, G. Density functional tight binding. 2014, (47) Christensen, A. S.; Kubaˇr, T.; Cui, Q.; Elstner, M. Semiempirical Quantum Mechanical Methods for Noncovalent Interactions for Chemical and Biochemical Applications. Chemical Reviews 2016, 116, 5301–5337. (48) Gaus, M.; Cui, Q.; Elstner, M. Density functional tight binding: Application to organic and biological molecules. Wiley Interdisciplinary Reviews: Computational Molecular Science 2014, 4, 49–61.

22

ACS Paragon Plus Environment

Page 22 of 27

Page 23 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

(49) Aradi, B.; Hourahine, B.; Frauenheim, T. DFTB+, a sparse matrix-based implementation of the DFTB method. Journal of Physical Chemistry A 2007, 111, 5678–5684. (50) Oviedo, M. B.; Negre, C. F. a.; S´anchez, C. G. Dynamical simulation of the optical response of photosynthetic pigments. Physical chemistry chemical physics : PCCP 2010, 12, 6706–11. (51) Negre, C. F. a.; Fuertes, V. C.; Oviedo, M. B.; Oliva, F. Y.; S´anchez, C. G. Quantum Dynamics of Light-Induced Charge Injection in a Model Dye–Nanoparticle Complex. The Journal of Physical Chemistry C 2012, 116, 14748–14753. (52) Fuertes, V. C.; Negre, C. F. a.; Oviedo, M. B.; Bonaf´e, F. P.; Oliva, F. Y.; S´anchez, C. G. A theoretical study of the optical properties of nanostructured TiO2. Journal of physics. Condensed matter : an Institute of Physics journal 2013, 25, 115304. (53) Negre, C. F. A.; Perassi, E. M.; Coronado, E. A.; S´anchez, C. G. Quantum dynamical simulations of local field enhancement in metal nanoparticles. Journal of Physics: Condensed Matter 2013, 25, 125304. (54) Primo, E. N.; Oviedo, M. B.; S´anchez, C. G.; Rubianes, M. D.; Rivas, G. A. Bioelectrochemical sensing of promethazine with bamboo-type multiwalled carbon nanotubes dispersed in calf-thymus double stranded DNA. Bioelectrochemistry 2014, 99, 8–16. (55) Negre, C. F. A.; Young, K. J.; Oviedo, M. B.; Allen, L. J.; S´anchez, C. G.; Jarzembska, K. N.; Benedict, J. B.; Crabtree, R. H.; Coppens, P.; Brudvig, G. W. et al. Photoelectrochemical hole injection revealed in polyoxotitanate nanocrystals functionalized with organic adsorbates. Journal of the American Chemical Society 2014, 136, 16420–16429. (56) Medrano, C. R.; Oviedo, M. B.; S´anchez, C. G. Photoinduced charge-transfer dynamics simulations in noncovalently bonded molecular aggregates. Phys. Chem. Chem. Phys. 2016, 18, 14840–14849. 23

ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(57) Mansilla Wettstein, C.; Bonaf´e, F. P.; Oviedo, M. B.; S´anchez, C. G. Optical properties of graphene nanoflakes: Shape matters. Journal of Chemical Physics 2016, 144 . (58) Douglas-Gallardo, O. A.; Berdakin, M.; S´anchez, C. G. Atomistic Insights into Chemical Interface Damping of Surface Plasmon Excitations in Silver Nanoclusters. Journal of Physical Chemistry C 2016, 120, 24389–24399. (59) Berdakin, M.; Taccone, M. I.; Pino, G. A.; S´anchez, C. G. DNA-protected silver emitters: charge dependent switching of fluorescence. Phys. Chem. Chem. Phys. 2017, 19, 5721–5726. (60) Niehaus, T. A.; Heringer, D.; Torralva, B.; Frauenheim, T. Importance of electronic self-consistency in the TDDFT based treatment of nonadiabatic molecular dynamics. European Physical Journal D 2005, 35, 467–477. (61) Niehaus, T. A.; Suhai, S.; Della Sala, F.; Lugli, P.; Elstner, M.; Seifert, G.; Frauenheim, T. Tight-binding approach to time-dependent density-functional response theory. Physical Review B 2001, 63, 085108.

24

ACS Paragon Plus Environment

Page 24 of 27

PDOS anion -4 25 -2 Chemistry -1 Letters 0 Page The Journal of 27-3of Physical Neutral

Optical Gap

-0.2 1 e

C190H110 PDI

2

-0.4 3 e

4 5 6 e -0.8 7 -1.0 8 e ACS Paragon Plus Environment 9 -4 -3 -2 -1 Energy / eV 10 -0.6 e

0

PDOS cation -4 Journal-3of Physical -2 Chemistry -1 The PageLetters 26 of0 27 Neutral +0.2 1 e

Optical Gap C190H110 PDI

2

+0.4 3 e

4 5 6 e +0.8 7 +1.0 8 e ACS Paragon Plus Environment 9 -4 -3 -2 -1 Energy / eV 10 +0.6 e

0

e Journal Page 27ofofPhysical 27 Chemistry Lett 1 2 3 4 5 ACS 6 Paragon Plus Environment 7 8