Article

Two-Dimensional Tantalum Carbide (MXenes) Composite Nanosheets for Multiple Imaging-Guided Photothermal Tumor Ablation Chen Dai, Yu Chen, Xiangxiang Jing, Lihua Xiang, Dayang Yang, Han Lin, Zhuang Liu, Xiaoxia Han, and Rong Wu ACS Nano, Just Accepted Manuscript • DOI: 10.1021/acsnano.7b07241 • Publication Date (Web): 20 Nov 2017 Downloaded from http://pubs.acs.org on November 21, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Nano is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 55

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Two-Dimensional Tantalum Carbide (MXenes) Composite Nanosheets for Multiple Imaging-Guided Photothermal Tumor Ablation Chen Dai1, Yu Chen3*, Xiangxiang Jing2*, Lihua Xiang1, Dayang Yang2, Han Lin3, Zhuang Liu4, Xiaoxia Han5 and Rong Wu1* 1

Department of Ultrasound in Medicine, Shanghai Tenth People’s Hospital, Tongji University School of Medicine, Shanghai 200072, P. R. China. E-mail: [email protected]. 2

Department of Ultrasound, Hainan General Hospital, Haikou, 570311, P. R. China. Email: [email protected].

3

State Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai

Institute of Ceramics, Chinese Academy of Sciences, Shanghai, 200050, P. R. China. E-mail: [email protected]. 4

Department of Radiology, Fudan University Shanghai Cancer Center, Shanghai, 200032, P. R. China. 5

Second Affiliated Hospital, Institute of Ultrasound Imaging, Chongqing Medical University, Chongqing, 400010, P. R. China.

ACS Paragon Plus Environment

1

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 55

Abstract MXenes, an emerging family of graphene-analogues two-dimensional (2D) materials, have attracted continuous and tremendous attentions in many application fields because of their intrinsic physiochemical properties and high performance in versatile applications. In this work, we report on the construction of tantalum carbide (Ta4C3) MXene-based composite nanosheets for multiple imaging-guided photothermal tumor ablation, which has been achieved by rational choice of the composition of MXenes and their surface functionalization. A redox reaction was activated on the surface of tantalum carbide (Ta4C3) MXene for in-situ growth of manganese oxide nanoparticles (MnOx/Ta4C3) based on the reducing surface of the nanosheets. The tantalum components of MnOx/Ta4C3 acted as the high-performance contrast agents for contrast-enhanced computed tomography, and the integrated MnOx component functionalized as the tumor microenvironment-responsive contrast agents for T1-weighted magnetic resonance imaging. The photothermal-conversion performance of MnOx/Ta4C3 composite nanosheets not only has achieved contrast-enhanced photoacoustic imaging, but also realized the significant tumorgrowth suppression by photothermal hyperthermia. This work broadens the biomedical applications of MXenes, not only by the fabrication of family members of biocompatible MXenes, but also by the development of functionalization strategies of MXenes for cancertheranostic applications.

Keywords: MXene, tantalum carbide, theranostic, nanomedicine, cancer

ACS Paragon Plus Environment

2

Page 3 of 55

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Engineering and tailoring materials at an atomic or molecular level have vastly propelled the development of scenarios for efficient cancer therapy.1-5 Due to sparse knowledge of the tumorigenesis metastasis and angiogenesis, and limitation of current diagnostic techniques and therapeutic modalities, cancer is still a major public health problem worldwide.6 Photothermal therapy (PTT), as an emerging protocol for tumor ablation by hyperthermia, is now developing fast.7-9 Typically, PTT generates heat by transforming near infrared (NIR) light into thermal energy at a minimally invasive manner, which is regarded as the potential treatment substitution for conventional clinical cancer-therapeutic modalities.10,

11

On this ground, abundant

nanoplatforms with varied compositions and nanostructure have been developed as the photothermal-conversion nanoagents to enhance the therapeutic effects of PTT, including the well-known Au nanoparticles,12-14 graphene and its derivatives,15-17 black phosphorous,18, transition-metal dichalcogenides,20-22 some organic nanosystems,23,

24

19

etc. In addition, the

accurate pre-determination of tumor location is of high significance for improving the therapeutic accuracy and mitigating the damage of PTT to the surrounding normal cells/tissues, which can be achieved by the imaging guidance and monitoring before and during the PTT hyperthermia.25, 26 It has been well-demonstrated that each diagnostic-imaging modality is featured with individual advantages. For instance, computed tomography is regarded as the powerful means for medical diagnosis because of its high spatial resolution and valuable tomography information of anatomical structure.21,

27

In addition, magnetic resonance imaging (MRI) can offer higher

anatomical structure information of soft tissue at a non-invasive and non-ionizing manner as compared to other imaging modalities.28,

29

As an emerging diagnostic-imaging modality,

photoacoustic (PA) imaging can break the penetration limit of optical imaging by detecting the

ACS Paragon Plus Environment

3

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 55

induced pressure waves of laser-irradiated tissues, which is based on its low tissue-attenuation coefficient, affording real-time detections of biological structure and functional information.30-35 It is highly expected to integrate different imaging modalities together to acquire comprehensive and synergetic information of living subjects for further enhancing the diagnosis accuracy.36-39 However, the rational integration of two or more different theranostic functional components into one nanoplatform generally suffers from complicated synthetic procedures, high cost, low production yield and instability, thus significantly hindering their further possible clinic translation. Recently, layer-structured two-dimensional (2D) transition metal carbides and nitrides (MXenes) have attracted considerable attention and interest due to their rich elemental compositions and 2D topologies as compared to graphene,40,

41

endowing them with

abundant/tunable physiochemical properties and high performance in versatile applications, ranging from mostly explored electrochemical energy storage materials36,

42-44

to recently

developed biomedical applications.45-47 Typically, MXenes are synthesized by exfoliation of their corresponding layer-structured 3D MAX-phase ceramics, which represent a large material family with over seventy members.48 The general formula of the MAX phase is Mn+1AXn (n = 1, 2, 3) where M is an early transition metal, A is a mainly A-group element and X is carbon or nitrogen.41, 49, 50 The A layer can be selectively removed to exfoliate the MAX-phase ceramics to produce 2D MXenes. The surface of MXene is typically terminated by -OH, -O, and/or -F, offering the possibility for engineering and functionalization of MXene’s 2D topological surface.49, 51 Recently, we have demonstrated that 2D Ti3C2 MXenes have the high photothermalconversion capability for cancer hyperthermia,45 but these MXenes cannot exert the specific functionality for diagnostic imaging because of the simple titanium and carbon compositions.

ACS Paragon Plus Environment

4

Page 5 of 55

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

In this work, we have successfully developed a MXene-based composite nanoplatform for multiple imaging-guided photothermal hyperthermia of cancer. 2D tantalum carbide (Ta4C3) MXene has been constructed based on its high photothermal-conversion performance for photothermal cancer ablation and tantalum-based composition with high atomic number (Z = 73) for contrast-enhanced CT imaging.52, 53 Furthermore, a surface-engineering strategy has been proposed to in-situ grow manganese oxide nanoparticles onto the surface of Ta4C3 MXene by triggering the redox reaction between reducing MXene’s surface and strongly oxidative MnO4(MnOx/Ta4C3). The integrated MnOx component endows the composite MXene nanosheets with tumor microenvironment (TME)-responsive T1-weighted MR imaging capability. Especially, the photothermal-conversion performance of Ta4C3 in MnOx/Ta4C3 composite nanosheets makes the as-synthesized MnOx/Ta4C3 become the desirable contrast agents for PA imaging. After the further surface organic modification by soybean phospholipid (SP), these biocompatible MnOx/Ta4C3-SP composite nanosheets have been systematically evaluated on their biosafety and theranostic performance on combating cancer.

Results and discussion Design, Synthesis and Characterization of MnOx/Ta4C3 Composite Nanosheets. As a MXene family member, 2D Ta4C3 nanosheets have been rarely explored because of the relatively high synthetic difficulty for the fabrication of Ta4C3 nanosheets with desirable 2D topology and nanostructures as compared to mostly explored 2D Ti3C2 MXene. Especially, the biomedical applications of nanoparticles typically require the strict controlling of their composition and structure at nanoscale. To satisfy the biomedical requirements, a two-step exfoliation strategy has been developed to fabricate nanosized 2D Ta4C3 nanosheets. The bulk MAX-phase Ta4AlC3

ACS Paragon Plus Environment

5

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 55

ceramics were initially sintered at high temperature, followed by chemical etching in 40% HF solution for four days to remove the middle Al layer. Subsequently, the delaminated Ta4C3 MXenes were treated by sonication for 12 h to fabricate nanosized 2D Ta4C3 ultrathin MXene nanosheets (Figure 1a and 1b). To integrate manganese oxide (MnOx) components onto the surface of 2D Ta4C3 MXene, we introduced highly oxidative KMnO4 into the Ta4C3 solution, which could react with the surface-exposed -OH groups (reducing sites) for in-situ producing and growing MnOx nanoparticles (Figure 1b, MnOx/Ta4C3). To improve the stability of assynthesized MnOx/Ta4C3 composite nanosheets, soybean phospholipid (SP), as a biocompatible natural organic component, was further introduced to modify the surface of MnOx/Ta4C3 nanosheets (designated as MnOx/Ta4C3-SP), which could guarantee the possible in vivo evaluation and application. Each component in MnOx/Ta4C3 composite nanosheets has its own functionality for cancer theranostics, including MnOx component for tumor microenvironmentresponsive MR imaging, Ta component for contrast-enhanced CT imaging and Ta4C3 component with high photothermal-conversion capability for simultaneous contrast-enhanced PA imaging and photothermal ablation of tumor (Figure 1c). The bulk MAX-phase Ta4AlC3 ceramics were initially sintered by solid-phase reaction at 1500 °C for 2 h (Figure 2a). After 40% HF etching for 96 h to remove the Al layer sandwiched between two Ta4C3 MXene layers, the exfoliated multilayer nanostructure of Ta4C3 MXene could be fabricated, which was clearly observed in SEM (Figure 2b) and TEM (Figure 2c) images, indicating the expanded interlayer space after the removal of Al layer. The high-resolution TEM (HRTEM) image and corresponding selected area electron diffraction (SAED) pattern clearly exhibited the crystalline lattice and hexagonal structure of as-prepared multilayered Ta4C3 MXenes, indicating that the crystallinity of the Ta4AlC3 MAX phase could be well preserved

ACS Paragon Plus Environment

6

Page 7 of 55

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

after long-term HF treatment (Figure 2d). To satisfy the strict biomedical application where the small nanoparticulate sizes is required, the as-prepared multilayer-structured Ta4C3 nanosheets were further treated by sonication for 12 h, which could reduce the planar size of Ta4C3 nanosheets. The SEM and TEM images of the obtained samples (Figure 2e and 2f, Figure S1) showed the successful fabrication of ultrathin Ta4C3 nanosheets with nanosizes in planar direction. X-ray diffraction (XRD) pattern of the synthesized Ta4C3 nanosheets is shown in Figure 2g. After 40% HF etching of MAX-phase Ta4AlC3 ceramics for 96 h, the (0002) peaks broadened and downshifted to lower angles due to its higher c value. In addition, more peaks in XRD pattern vanished or shrunk, especially over the range of 30-40 degree. These results suggested the successful removal of Al layer and desirable topological transformation from three 3D to 2D. The 2D topology of Ta4C3 MXenes endows it with large surface area, and the HF etching could bring with the special surface terminations such as -OH groups,40, 54, 55 which provides the possibility for further surface modification and functionalization. Herein, highly oxidative KMnO4 was introduced into Ta4C3 aqueous solution to generate in-situ MnOx species onto the surface of the Ta4C3 nanosheets via a simple redox reaction between MnO4- ions and reducing -OH groups. The TEM images of MnOx/Ta4C3 composite nanosheets documented that the as-formed MnOx component in sheet-like morphology was firmly attached onto the surface of Ta4C3 nanosheets (Figure 2h and Figure S2a, b). The Bright-field SEM image (Figure S2c) of MnOx/Ta4C3 composite nanosheets evidenced the formation of a thin MnOx layer on the surface of Ta4C3 MXene. The Dark-field SEM image (Figure 2i), corresponding the high-angle annular detector dark-field (HAADF) image (Figure S2d) and the TEM image at high magnification (Figure S2e) of MnOx/Ta4C3 composite nanosheets showed the sheet-like

ACS Paragon Plus Environment

7

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 55

morphology of MnOx species anchored on the surface of Ta4C3, which was further demonstrated by the corresponding secondary electron SEM image (Figure 2j). The elemental distribution mappings of Ta, Mn and O in MnOx/Ta4C3 composite nanosheets (Figure 3a-c) confirmed the coexistence of the Ta and Mn elements and high uniformity of MnOx distribution on the surface of Ta4C3 nanosheets. X-ray energy dispersive spectroscopy (EDS) of MnOx/Ta4C3 composite nanosheets (Figure 3d) exhibit the presence of Ta and Mn elements, indicating the successful functionalization of the MnOx on the surface of Ta4C3 nanosheets. The atomic ratio of Mn and Ta was nearly 1:5. The electron energy loss spectrum (EELS) of MnOx/Ta4C3 (Figure 3e) shows the presence of typical Mn signal, further indicating the MnOx-functionalized Ta4C3 composition. X-ray photoelectron spectroscopy (XPS) was adopted to investigate the chemical nature of Ta4AlC3, Ta4C3, and MnOx/Ta4C3 composite nanosheets. As shown in Figure 3f, after HF etching, Al-indexed peaks in the XPS spectrum of Ta4C3 nanosheets disappeared as compared to that of Ta4AlC3 MAX-phase ceramic. The obvious Mn-indexed peaks in XPS demonstrated the presence of MnOx components on the surface of Ta4C3 nanosheets. The fitted peaks were at 642.7 eV and 655.7 eV, respectively. The relative contents of bivalent, trivalent and quadrivalent Mn in MnOx/Ta4C3 composite nanosheets were determined to be 18.5% 65.4%, and 16.1%, respectively (Figure 3g).

In Vitro Photothermal-Conversion Property of MnOx/Ta4C3 Composite Nanosheets. It has been found that the as-synthesized Ta4C3 MXene was featured with high photothermalconversion capability. Therefore, it was expected that the MnOx/Ta4C3 composite nanosheet was also featured with similar photothermal-conversion performance for potential photothermal hyperthermia due to the presence of Ta4C3 component in the composite nanosheets. UV-vis

ACS Paragon Plus Environment

8

Page 9 of 55

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

spectra of MnOx/Ta4C3 composite nanosheet displayed the specific concentration-dependent light absorption in the NIR region (Figure 4a). The extinction coefficient MnOx/Ta4C3 composite nanosheet at 808 nm was tested and calculated to be 8.67 Lg−1cm−1 (Figure 5a inset), which was much higher than that of mostly explored graphene oxide (3.6 Lg-1cm-1).16 Then, we evaluated the in vitro photothermal performance of MnOx/Ta4C3 composite nanosheets after exposing to an NIR laser (808 nm) at various concentrations under the laser power density of 1.5 and 2.0 W cm1

(Figure 4b and Figure S3). The maximum temperature of the aqueous solution containing

MnOx/Ta4C3 composite nanosheets could reach up to 49 °C at the power density of 1.5 W cm−2 after 300 s irradiation, and to nearly 65°C at a power density of 2.0 W cm−2 under the same irradiation duration, which also exhibited a concentration-/laser power-dependent photothermal features. Such a high photothermal-conversion capability of MnOx/Ta4C3 composite nanosheets could guarantee the further in vivo tumor ablation. In contrast, the temperature increase of only 1 °C in pure water was recorded after 300 s irradiation at the same conditions, indirectly indicating the functionality of MnOx/Ta4C3 composite nanosheets for elevating the aqueous temperature. The photothermal stability of MnOx/Ta4C3 composite nanosheets was further tested. Insignificant changes were observed in elevating temperature after 5 cycles of NIR laser irradiation (1.5 W cm−2) for nearly one hour (Figure 4c). Especially, the photothermalconversion efficiency η of MnOx/Ta4C3 composite nanosheets was measured to be nearly 34.9% (Figure 4d, and 4e), much higher than that of Au nanorods (21%)56 and Cu2-xSe NCs (22%).57 Although the Ta4C3 nanosheets show high hydrophilicity and dispersity in water solution, MnOx/Ta4C3 is easily aggregated in physiological solutions. In order to address this issue, soybean phospholipid (noted as SP) was further used to modify the surface of MnOx/Ta4C3 composite nanosheets (Figure 4f) to endow the MnOx/Ta4C3 composite nanosheets with

ACS Paragon Plus Environment

9

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 55

excellent stability and high dispersity in various solvents such as H2O, saline, phosphate buffer saline (PBS), simulated body fluid (SBF), and Dulbecco’s Modified Eagle’s Medium (DMEM) (Figure 4g). The hydrodynamic size of MnOx/Ta4C3 by means of SP surface modification was measured to be around 190 nm by dynamic light scattering (DLS, Figure 4h). The series changes on Zeta potential of each modification step further indicated the successful grafting of SP on the surface of MnOx/Ta4C3 composite nanosheets (Figure 4i).

In Vitro PTT against Tumor Cells by MnOx/Ta4C3-SP Composite Nanosheets. The in vitro cytotoxicity of MnOx/Ta4C3-SP nanosheets as photothermal agents was initially evaluated. Nanosized MnOx/Ta4C3-SP could efficiently enter the cancer cells, trigger the intracellular hyperpyrexia and subsequently induce the death of cancer cells after 808 nm laser irradiation (Figure 5a). The confocal laser scanning microscopic (CLSM) images exhibited that MnOx/Ta4C3-SP composite nanosheets could be efficiently endocytosed into the cancer cells as evidenced by the presence of obvious intracellular green fluorescence originated from fluorescein isothiocyanate (FITC)-labeled MnOx/Ta4C3-SP composite nanosheets after 1 h coincubation. The fluorescence intensity was substantially enhanced with the prolonged coincubation duration for 4 h (Figure 5b). Then, confocal fluorescence images of calcine AM (green) and PI (red) co-stained cancer cells confirmed the effective photothermal ablation of 4T1 cells in the presence of MnOx/Ta4C3-SP composite nanosheets after exposing to NIR irradiation. The majority of 4T1 cells after the incubation with MnOx/Ta4C3-SP composite nanosheets was destructed under the NIR laser irradiation as demonstrated by the presence of strong red fluorescence (PI staining). In contrast, the viability of 4T1 cells treated without MnOx/Ta4C3-SP

ACS Paragon Plus Environment

10

Page 11 of 55

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

composite nanosheets or the only NIR laser irradiation was not obviously affected as evidenced by the strong green fluorescence (calcine AM staining, Figure 5c). It is noted that the as-fabricated MnOx/Ta4C3-SP composite nanosheets exhibited negligible cytotoxicity to 4T1 cells as evaluated by a standard Cell Counting Kit-8 (CCK-8) protocol (Figure 5d). After co-incubation of MnOx/Ta4C3-SP nanosheets with cells at elevated concentrations (25, 50, 100, 200, 400 µg mL-1) for 24 h and 28 h, MnOx/Ta4C3-SP composite nanosheets exhibited no obvious effect on the survival of 4T1 cells, even at a high evaluated concentration of 400 µg mL-1, indicating the excellent cytocompatibility of MnOx/Ta4C3-SP composite nanosheets. The in vitro photothermal-ablation efficiency of MnOx/Ta4C3-SP composite nanosheets as photothermal agents for 4T1 cell ablation at different concentrations from 12.5 to 200 µg mL-1 was assessed after co-incubation with cancer cells for 4 h, followed by 808 nm laser irradiation (2.0 W cm-2) for 5 min (Figure 5e). It has been shown that with the increase of the concentration of MnOx/Ta4C3-SP nanosheets, the viability of 4T1 cells sharply decreased after 808 nm laser irradiation. In addition, the viability of 4T1 cells incubated with the MnOx/Ta4C3-SP composite nanosheets at the concentration of 200 µg mL-1 were investigated after 808 nm laser irradiation at different power densities of 0, 0.5, 1.0, 1.5 and 2 W cm-2. The results showed that the enhanced 4T1 cell ablation was observed with the increased NIR power density, indicating the concentration-dependent and power density-dependent photothermal features of MnOx/Ta4C3-SP composite nanosheets for PTT (Figure 5f). The desirable in vitro PTT efficiency of MnOx/Ta4C3-SP composite nanosheets guarantees their further in vivo photothermal hyperthermia of tumor.

ACS Paragon Plus Environment

11

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 55

Multiple Imaging Performances (CT, MRI and PA) of MnOx/Ta4C3 Composite Nanosheets. X-ray computed tomography (CT) imaging has been widely used in clinic due to its high spatial resolution, deep tissue penetration and excellent high-resolution 3D tomography imaging of anatomical structure and functional information.58 Tantalum, an element with high atomic number (Z = 73) and high X-ray attenuation coefficient (Ta: 4.3 cm2 kg-1, Au: 5.16 cm2 kg-1 at 100 eV)53, has been demonstrated as the desirable CT contrast agents.58-60 On this ground, we initially evaluated the X-ray attenuation ability of as-prepared Ta-containing MnOx/Ta4C3 composite nanosheets as CT contrast agents in vitro. Figure 6a and 6b showed that a significantly improved brightness of CT images and the corresponding enhanced Hounsfield units (HU) values of MnOx/Ta4C3-SP composite nanosheets were observed with the elevation of Ta concentrations, revealing a perfect linear relationship with the Ta concentration. The HU value induced by MnOx/Ta4C3-SP nanosheets was nearly three folds higher than that of clinically used iodine-based Iopromide 300 under the same element concentration (10 mg mL-1), indicating the high contrast-enhanced CT imaging capability of MnOx/Ta4C3-SP nanosheets. Then, we further investigated whether these MnOx/Ta4C3-SP composite nanosheets could be used as in vivo CT contrast agents. Balb/c mice bearing 4T1 tumors were intravenously injected with MnOx/Ta4C3-SP composite nanosheets (dose: 20 mg kg-1, 100 µL) and then scanned by the clinical CT-scanning instrument. Strong contrast in tumor of mice was observed from CT imaging, and the corresponding HU value increased to 132 HU after i.v. injection as compared to 78 HU before i.v. injection (Figure 6c-6e), suggesting that MnOx/Ta4C3-SP composite nanosheets could act as the promising contrast agents for in vivo contrast-enhanced CT imaging of tumors.

ACS Paragon Plus Environment

12

Page 13 of 55

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Transition metal manganese (Mn), as one of the necessary elements in human bodies, shows relatively high biosafety and low toxicity as compared to clinically used Gd3+-based agents as MRI contrast agents, which is related to the occurrence of nephrogenic systemic fibrosis (NSF).61, 62 The introduced MnOx-functional motifs on the surface of Ta4C3 nanosheets could achieve both pH-responsive and glutathione (GSH)-sensitive T1-weighted MR imaging,29, 63-67 which are the two most representative characteristics (mild acidity and overexpressed GSH level) in the tumor microenvironments. Especially, a great many bioresponsive materials have been recently constructed in view of the lowed pH values of tumor microenvironments as compared to the normal physiological milieus.68-70 The pH-responsive T1-weighted MR imaging capability for tumor imaging was bestowed on the MnOx components-based nanocomposites, attributed to the instability of Mn-O bonds under the mildly acidic and reductive conditions of tumor microenvironments.29, 64, 71, 72 To access the possibility of using the as-synthesized MnOx/Ta4C3-SP composite nanosheets as a tumor microenvironment-triggered T1-weighted MRI contrast agent, in vitro T1 relaxation time of MnOx/Ta4C3-SP composite nanosheets in buffer solutions at different GSH concentrations and different pH values was measured by using a clinical 3.0 T human clinical scanner. We used buffer solutions at different GSH concentrations (5.0 mM L-1 and 10.0 mM L-1) to imitate tumor reducing microenvironments,67, 73 and buffer solutions of lowed pH values (pH = 5.0 and pH = 6.0) to mimic the tumor acidic microenvironments and buffer solutions at pH of 7.4 to mimic the normal blood circulation. The increase of relaxivity r1 and corresponding concentrationdependent brightening effect of T1-weighted MR imaging in the buffer solution at different GSH concentrations and at lowed pH values could be directly observed and calculated (Figure 7a-d). The initial relaxivity r1 of MnOx/Ta4C3-SP composite nanosheets in neutral SBF was calculated

ACS Paragon Plus Environment

13

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 55

to be 3.77 mM-1s-1, which further increased to 4.71 mM−1s−1 and 5.38 mM−1s−1 at GSH concentrations of 5.0 and 10.0 mM, respectively (Figure 7a). Such a contrast-enhanced responsiveness was also observed in lowed pHs condition (pH = 5.0 and 6.0), where r1 value reached up to 4.89 mM−1s−1 and 8.27 mM−1s−1 at lowed pH values of 5.0 and 6.0, respectively (Figure 7b). This pH- and GSH-responsive MRI performance was attributed to the fact that the Mn-O bonds were easily cleaved under mildly acidic and elevated GSH condition of tumor microenvironments. The released Mn2+ could effectively improve the interaction probability of paramagnetic Mn centers to water molecules, further resulting in enhanced T1-weighted MRI performance (Figure 7e). Once recognized that the presence of the released Mn2+ originated from Ta4C3 nanosheets could efficiently enhance the relaxivity of hydrogen protons, MnOx/Ta4C3-SP composite nanosheets were further evaluated for their performance as the in vivo MRI contrast agents. The MR imaging of 4T1 tumor-bearing mice was recorded before and after i.v. injection of MnOx/Ta4C3-SP composite nanosheets (20 mg kg-1, 100 µL). During the tested 60 min period after injection of MnOx/Ta4C3-SP composite nanosheets, the MRI-signal enhancement in tumor tissues and their corresponding increased T1-weighted MR images were clearly observed (Figure 7f and 7g), suggesting that MnOx/Ta4C3-SP composite nanosheets is highly desirable for the subsequent PTT guidance and monitoring. Taking the high photothermal-conversion capability of MnOx/Ta4C3-SP composite nanosheets into account, the MnOx/Ta4C3-SP composite nanosheets were expected to act as the contrastenhanced contrast agents for PA imaging. As shown in Figure 8a, the enhanced PA signals of MnOx/Ta4C3-SP composite nanosheets were observed as the Ta in MnOx/Ta4C3-SP concentration increased, and the PA signals of MnOx/Ta4C3-SP composite nanosheets followed a linear

ACS Paragon Plus Environment

14

Page 15 of 55

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

relationship with the Ta concentration (Figure 8b), indicating the desirable PA-imaging capability of MnOx/Ta4C3-SP composite nanosheets. Furthermore, the in vivo PA imaging capability of MnOx/Ta4C3-SP composite nanosheets was evaluated on 4T1 tumor bearing mice after the subcutaneous administration into mice (20 mg kg1

, 100 µL). As expected, the PA effect of MnOx/Ta4C3-SP composite nanosheets as induced by a

laser pulse illumination to generate rapid heating and subsequent acoustic emission signals could be clearly observed in tumor tissues with the prolonged observation time window, which could be further used to image the distribution of nanosheets as the contrast agents in tumors (Figure 8c). The PA signals were quickly enhanced, and the signal intensity reached the high value after the short time of subcutaneous administration (Figure 8d). The excellent in vitro and in vivo PAimaging performance demonstrates the possibility of MnOx/Ta4C3-SP composite nanosheets as the contrast agents for PA imaging and detection of tumors.

In Vivo Photothermal Ablation of Tumor by MnOx/Ta4C3-SP Composite Nanosheets. To shed more light on the photothermal effects of MnOx/Ta4C3-SP composite nanosheets on the tumor therapy, 4T1 breast tumor-bearing mouse xenograft was established to further investigate the therapeutic efficiency of MnOx/Ta4C3-SP composite nanosheets as the photothermalconversion nanoagents for tumor hyperthermia. After the tumor volumes reached about ~60 mm3, the 4T1 tumor-bearing mice were randomly separated into four groups to receive different disposes (n = 5 per group): (i) control, (ii) NIR laser only, (iii) intravenously injected with MnOx/Ta4C3-SP composite nanosheets only, (iv) intravenously injected with MnOx/Ta4C3-SP composite nanosheets + NIR laser irradiation. After 4 h of injection, NIR laser (808 nm) irradiation towards 4T1 tumor ablation was performed at the power density of 2 W cm-2 for 10

ACS Paragon Plus Environment

15

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 55

min. The whole-body thermal images of the 4T1 tumor-bearing mice were taken at given time intervals (Figure 9a). The surface temperature of tumors monitored by infrared thermal (IR) imaging instrument increased to ~55 oC for MnOx/Ta4C3-SP-treated mice within 10 min, which was sufficiently high for tumor ablation (Figure 9b). In contrast, the tumor temperature of the mice injected without MnOx/Ta4C3-SP under 808 nm laser irradiation at the same power density only increased by 5 oC. After the different treatments, the mice weights were recorded every two days, which showed on obvious weight changes among these four groups (Figure 9c). The length and width of the tumors were measured by a digital caliper every two days and the corresponding digital photos of tumor regions were taken every two days during the next two weeks (Figure 2g and Figure S4). It is important to find that MnOx/Ta4C3-SP-treated mice with 808 nm laser irradiation experienced a significantly suppressed tumor growth, while the other three groups showed no obvious inhibition effect on the tumor growth (Figure 9d). These MnOx/Ta4C3-SP-treated mice were still healthy after 60 days post treatment (Figure 9e), and no tumor recurrence was observed. Comparatively, the mice death occurred continuously in the other three groups, confirming the high in vivo therapeutic efficiency of photothermal hyperthermia assisted by MnOx/Ta4C3-SP composite nanosheets. Hematoxylin-eosin (H&E) staining, TdT-mediated dUTP Nick-End Labeling (TUNEL) and Ki-67 antibody staining of tumor slices were collected from each group of mice to further reveal the mechanism of photothermal effect at 24 h after NIR laser irradiation. Severe destruction including changed cell shapes and even condensed nuclei of tumor cells was discovered from micrographs of H&E-stained tumor slices of MnOx/Ta4C3-SP + NIR group (Figure 9f). Comparatively, no noticeable abnormal sign was observed in the other three groups. TUNEL results also showed much higher necrosis of tumor cells in MnOx/Ta4C3-SP + NIR laser group as

ACS Paragon Plus Environment

16

Page 17 of 55

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

compared to other three groups, which was in accordance with the result of H&E staining. Ki-67 antibody staining was introduced to evaluate the proliferative activities of cancer cells. The results of MnOx/Ta4C3-SP + NIR laser group exhibited significantly suppressed proliferative activities of cancer cells while no significant change of suppression effect on the cell proliferation was detected in the other three groups, confirming the high photothermal ablation effect of MnOx/Ta4C3-SP as the photothermal-conversion nanoagents for ablating the tumors (Figure 9f). Based on the systematic in vitro and in vivo evaluations, the as-designed MnOx/Ta4C3-SP nanosheets could achieve simultaneous PA/CT/MR multi-modality imaging where the T1weighted MR imaging is TME responsive. Comparatively, traditional photothermal nanoagents (e.g., Au28, graphene and its derivatives15,

16

, black phosphorous19, WS221 and MoS274) are

difficult to be designed with multiple-imaging capability where the tedious multiple functionalization steps are typically involved. Especially, the Ta component in MnOx/Ta4C3-SP nanosheets is capable of enhancing the contrast of CT imaging, which takes the composition feature of the MnOx/Ta4C3-SP photothermal nanoagent. Especially, the photothermal-conversion efficiency of MnOx/Ta4C3-SP nanosheets (34.9%) is much higher than that of traditional Au nanorods (21%)56, Cu2-xSe (22%)57, and Ti3C2 nanosheets (30.6%)45, indicating their high photothermal-hyperthermia performance for tumor ablation. Therefore, these MnOx/Ta4C3-SP nanosheets are intrinsically featured with structural, compositional and physiochemical property for efficient cancer theransotics.

In Vivo Biocompatibility Assay of MnOx/Ta4C3-SP Composite Nanosheets. The in vivo biocompatibility and biosafety of MnOx/Ta4C3-SP composite nanosheets were systematically

ACS Paragon Plus Environment

17

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 55

investigated to ensure their safe bio-applications and guarantee further clinical translations. Twenty healthy Kunming mice were randomly divided into four groups, including control group and three other treated groups at three different MnOx/Ta4C3-SP doses of 5 mg kg-1, 10 mg kg-1 and 20 mg kg-1. After another thirty-days feeding, these mice were sacrificed and their major organs including heart, lung, liver, kidney and spleen were collected and fixed in 10% formalin for histological characterization. During thirty-days feeding period, no obvious weight variation or abnormal behavior in the three treated groups were observed as compared to the control group (Figure S5). A series of blood indexes including the white blood cells, red blood cells, platelets, lymphocytes, hemoglobin, mean corpuscular hemoglobin concentration, mean corpuscular hemoglobin, mean corpuscular volume, hematocrit, and liver and kidney function in all four groups were measured at the 30th day post injection. All the indexes in the three MnOx/Ta4C3-SPtreated groups were found to be normal as compared to that of control group, indicating no adverse effects induced by MnOx/Ta4C3-SP composite nanosheets (Figure 10 a-i). H&E staining of the key organs from different groups of mice treated at the elevated doses was carried out to evaluate the pathological change. Each group showed no shrunk malignant cells, loss of contact, or nucleus damage on the examined tissue sections, indicating that no obviously histological abnormalities or lesions were induced in the main organs after the injection of MnOx/Ta4C3-SP composite nanosheets (Figure 10m). Encouraged by these preliminary in vivo biosafety results at tested doses for thirty days, the as-prepared MnOx/Ta4C3-SP-treated MnOx/Ta4C3-SP composite nanonosheets are expected be non-toxic, which favors their further bio-applications and possibly clinical translation.

ACS Paragon Plus Environment

18

Page 19 of 55

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Conclusions In summary, we herein have successfully construct the 2D tantalum carbide (Ta4C3) MXenebased composite nanosheets for efficient multiple imaging-guided photothermal tumor ablation. Especially, a redox reaction was activated on the surface of tantalum carbide (Ta4C3) MXene for in-situ growth of manganese oxide nanoparticles (MnOx/Ta4C3) based on the reducing surface of the nanosheets. By rational selection on the composition of MXene and further functionalization, the as-constructive MnOx/Ta4C3-SP composite nanosheets acted as the high-performance contrast agents for simultaneous computed tomography (tantalum-based component), tumor microenvironment-responsive T1-weighted magnetic resonance imaging (MnOx component) and photoacoustic imaging (photothermal-conversion property). Importantly, the high photothermalconversion performance of MnOx/Ta4C3-SP composite nanosheets has realized the significant tumor-growth suppression by photothermal hyperthermia. Systematic in vivo evaluation has demonstrated the high biocompatibility and biosafety of the as-designed MnOx/Ta4C3-SP composite nanosheets. This work broadens the biomedical applications of 2D MXenes by rational choice of desirable chemical composition (Ta4C3) and surface engineering for functionalization (MnOx integration), which also provides the desirable high-performance theranostic nanoagents for efficiently combating cancer.

Methods Synthesis of Ta4AlC3. Ta4AlC3 MAX-phase ceramics were prepared by ball-milling element Ta (-325 mesh, 99.97%, Alfa Aesar, Ward Hill, USA), Al (-325 mesh, 99.5%, Alfa Aesar, Ward Hill, USA), and C (-300 mesh 99%, particle size