Understanding the Seed-Mediated Growth of Gold Nanorods through

Dec 5, 2016 - This statistical experimental design and analysis method, besides determining which experimental variables are important and which are n...
0 downloads 9 Views 4MB Size
Subscriber access provided by NEW YORK UNIV

Article

Understanding the Seed-Mediated Growth of Gold Nanorods through a Fractional Factorial Design of Experiments Nathan D. Burrows, Samantha Harvey, Fred A. Idesis, and Catherine J. Murphy Langmuir, Just Accepted Manuscript • DOI: 10.1021/acs.langmuir.6b03606 • Publication Date (Web): 05 Dec 2016 Downloaded from http://pubs.acs.org on December 10, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Langmuir is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

Understanding the Seed-Mediated Growth of Gold Nanorods through a Fractional Factorial Design of Experiments Nathan D. Burrows*, Samantha Harvey, Fred A. Idesis, and Catherine J. Murphy* Department of Chemistry, 600 S. Mathews Ave., University of Illinois at Urbana-Champaign, Urbana, IL, 61801 Abstract Since the development of simple, aqueous protocols for the synthesis of anisotropic metal nanoparticles, research into many promising, valuable applications of gold nanorods has grown considerably; but, a number of challenges remain including gold-particle yield, robustness to minor impurities, and precise control over gold nanorod surface chemistry. Here in we present the results of a composite fractional factorial series of experiments designed to screen seven additional potential avenues of control over and understanding the seedmediated silver-assisted synthesis of gold nanorod. These synthetic variables are the amount of sodium borohydride used and the rate of stirring when producing seed nanoparticles, the age of and the amount of seeds added, the reaction temperature, the amounts of silver nitrate and ascorbic acid added, and the age of the reduced growth solution before seed nanoparticles are added to initiate rod formation. This statistical experimental design and analysis method, besides determining which experimental variables are important and which are not when synthesizing gold nanorods (and quantifying their effects), give further insight into the mechanism of growth by measuring the degree to which variables interact with each other mapping out their mechanistic connections. This work demonstrates that when forming gold ACS Paragon Plus Environment

1 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 53

nanorods by the reduction of auric ions by ascorbic acid onto seed nanoparticles, ascorbic acid determines how much gold is reduced and the amount of seeds determine how it is divided up, yet both influence intrinsic growth rates, in both width and length, of the forming nanorods. Furthermore, this work shows that the reduction of gold proceeds via direct reduction on the surface of seeds and not through a disproportionation reaction. Further control over the length of gold nanorods can be achieved by tuning the amount of a silver nitrate or the reaction temperature. This work shows that silver does not directly influence rod length or width and a new primary role for silver is proposed as a catalyst promoting the reduction of gold on the ends of forming nanorods. Furthermore, this silver catalyst is removed from the reaction by adsorption onto the surface of the growing nanorod. Additionally, this work demonstrates the importance of freshly prepared silver nitrate and ascorbic acid solutions, free from even a few hours of photodegradation, in preparing gold nanorods with high shape purity and gold yield.

2 of 52

ACS Paragon Plus Environment

Page 3 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

Introduction Research has exponentially exploded in the past two decades concerning the study of gold nanoparticles. Over 17,000+ published research articles on gold nanorods alone have appeared since 2005. This level of research activity can be attributed to two primary developments. First is the development of simple, aqueous protocols for anisotropic metal nanoparticle synthesis that have enabled unprecedented access to these nanomaterials for research.1-15 Second is the promise of valuable applications in sensing and plasmon-enhanced spectroscopies,9,16 biomedical imaging,8,17,18 drug/gene delivery,8,16,18-20 and photothermal therapy8,16,18,19,21,22 due to their shape-dependent optical and physical properties. Gold nanorods are also applied in non-biologic applications including: optical power limiters,23 solar cells,24,25 light emitting diodes,26 stress/strain sensors,27,28 and catalysis.29 It is the tunability of these properties through changes in particle dimensions that makes these potential applications possible. For example, the optical extinction spectrum for a suspension of gold nanorods that are strongly influenced by the aspect ratio of the gold nanorods. Gold nanorods were initially prepared using electrochemical methods in a hard template of porous alumina or polycarbonate membranes.30,31 This was followed by development of a more accessible three-step seeded growth synthesis that results in rods with aspect ratios (length/width) between 8 and 20 with absolute dimensions of 150 – 1800 nm × 25 nm.13-15 In the decade following this development, the method of seeded growth has been extended to other anisotropic shapes and materials and has been improved upon resulting in many modifications.32-35 These include the development a one-step silver-assisted seeded growth, 3,36,37

the addition of small organic additives,38-40 a “seedless” version,38,41,42 co-surfactants,43

alternative reducing agents,44-46 as well as several gram-scale syntheses of gold nanorods.38,39,47-49 A more detailed accounting of the history of gold nanorod synthesis and recent developments can be found in numerous review articles.5,7,9,10 ACS Paragon Plus Environment

3 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 53

The result of this decade of intense research is that the seeded growth approach to synthesizing many inorganic nanomaterials dominates the literature.50-57 Yet, a number of challenges remain. These include an improved gold-particle yield, robustness to minor impurities, and precise control over gold nanorod surface chemistry. Here in we present the results of a composite fractional factorial series of experiments designed to screen seven potential avenues of controlling gold nanorod synthesis. Besides determining which factors are important and which are not when synthesizing gold nanorods, these experiments also give further insight into the mechanism of growth by measuring the degree to which variables interact with each other. Results and Discussion This work focuses on the one-step silver-assisted seeded growth synthesis of gold nanorods.36

The

current

standard

protocol

in

the

Murphy

group

for

preparing

cetyltrimethylammonium bromide (CTAB) capped gold nanoparticle seeds and their subsequent growth into CTAB capped gold nanorods on a 10-mL scale resulting in approximately 100 mg of nanoparticles (assuming 100% yield) is as follows. First, 250 µL of 0.0100 M chloroauric acid is diluted with 9.75 mL of 0.100 M CTAB and set stirring with a magnetic bar. Second, a fresh, cold solution of 0.0100 M sodium borohydride is prepared by massing 0.0378 g of sodium borohydride, dissolving this in 10 mL of ice-cold nanopure water, and diluting 1 mL of this solution to 10 mL with ice-cold nanopure water. 600 µL of this solution is then immediately injected into the stirring gold solution and continued to stir for 10 minutes. This results in a honey colored suspension of gold nanoparticle seeds that is aged for an hour so that any excess sodium borohydride may decompose. Third, a nanorod growth solution is prepared by adding varying amounts of 0.0100 M silver nitrate (20 – 150 µL) to 9.5 mL of 0.100 M CTAB followed by 500 µL of 0.0100 M chloroauric acid and 55 µL of 0.100 M ascorbic

4 of 52

ACS Paragon Plus Environment

Page 5 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

acid. At these concentrations, the weak reducing agent ascorbic acid is the limiting reagent. To this growth solution, 12 µL of the prepared seed suspension is added. The formation of color is observed after about 10 minutes, which grows in intensity over the next hour, as gold nanorods form. The product is then collected by centrifugation at 11,000 rcf for 15 minutes into a pellet, the supernatant is siphoned off, and the pellet is resuspended in nanopure water. This suspension of gold nanorods is typically characterized by optical absorption / scattering techniques (e.g. ultraviolet visible infrared spectroscopy (UV-Vis-NIR), dynamic and phase analysis light scattering techniques) and microscopies (e.g. optical, transmission electron, and scanning electron microscopy).

ACS Paragon Plus Environment

5 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 53

Figure 1. Vis-NIR spectroscopic analysis of gold nanorods produced following the standard Murphy protocol. A) Vis-NIR extinction spectra as a function of silver nitrate concentration used in the synthesis of a series of gold nanorod suspensions with all other synthetic variables being held constant. Inset images are of the corresponding nanorod suspensions. B) A plot of the longitudinal surface plasmon resonance extinction peak wavelength as a function of silver nitrate concentration employed for the same set of suspensions presented in part A, for experiments done by one experienced person. C) A plot similar to part B showing the synthetic variation by different individuals produced in the Murphy group over the last half-decade when attempting to control the longitudinal absorption peak wavelength by varying only the concentration of silver nitrate. The blue line in C is the best fitting power equation by least-squares and the red line is a horizontal line at 785 nm for illustrative purposes (see text for details).

6 of 52

ACS Paragon Plus Environment

Page 7 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

Figure 1 presents a typical set of shape-controlled gold nanorod suspensions produced in an afternoon and characterized by Vis-NIR spectroscopy following the standard Murphy protocol. Analysis of the longitudinal localized surface plasmon resonance (LSPR) absorption band as a function of silver nitrate concentration (Figure 1B), from experiments done by one experienced person, shows that although there is a positive correlation between the amount of silver nitrate and the resultant longitudinal LSPR peak wavelength (black fitted line) small incremental increases in silver nitrate does not always correspond to an increase in the peak wavelength and suggests additional, unintentionally varied, factors influence the longitudinal LSPR peak wavelength. Comparing many product suspensions from over ten different researchers within our group over the last five years (Figure 1C), including students with different degrees of experience, shows a large degree of variability, but still displays a trend of increasing longitudinal LSPR as a function of silver nitrate concentration (blue fitted line). Yet, the red horizontal line illustrates the difficulty of preparing rods that have an extinction at 785 nm, a typical laser wavelength used in biomedical research due to the low absorption coefficient of water in this region of the electromagnetic spectrum allowing for deep tissue penetration. For example, an individual researcher could find that a wide range of silver nitrate concentrations, 50 µM to about 200 µM, would lead to gold nanorods that exhibited a longitudinal plasmon band maximum at 785 nm, for all other concentrations being the same. Many possible sources of variation across researchers were found to occur when executing the standard protocol (in addition to intentionally varying the silver nitrate concentration) that theoretically could contribute to the observed scatter of LSPR wavelength as a function of silver nitrate concentration (Figure 1C). Variation involving the preparation of seed nanoparticles includes: 1) the accuracy of the mass of sodium borohydride used due to the adsorption of atmospheric water vapor, 2) the rate of stirring during sodium borohydride addition, and 3) the age of the seed suspension unintentionally varied anywhere from 1 to 48 ACS Paragon Plus Environment

7 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 53

hours when used to prepare gold nanorods. When growing the gold nanorods from seeds, plausible sources of variation includes: 1) the amount of seeds added, 2) the temperature in the laboratory, 3) the amount / concentration of ascorbic acid added, and 4) the amount of time that passed between adding the ascorbic to reduce the auric ions to aurous ions and adding the seed nanoparticles to initiate rod growth unintentionally varied over a 30 minute period (i.e., the age of the reduced growth solution). Other possible sources of variation also include changes in vendors and lots of reagents used and the experience of the scientist conducting the synthesis; however, the variation in LSPR peak wavelength can also be observed when conducted by the same person three days in a row using the same chemical stock. Many of these variables have been systematically studied, though not simultaneously, including: [AgNO3],38,41,42,45,46,58-61 [reductant],36,45,46,58,60, [seeds]36,38,41,45,46,60-62 and temperature.38,46,60 Presented with all these possible variables to test, an efficient experimental design of minimal effort (and resources) to screen these variables can be found in a factorial design of experiments. Such a design consists of a set number of levels or versions for each factor (i.e., variable) to be studied and experiments are conducted for each possible combination. Although this statistical method of experimentation and analysis was developed in the 1920s and brought into the chemical sciences after World War II,63 a search of the literature finds few examples of factorial experimental design that involves nanoparticles. This method has been applied in optimizing analytical methods involving nanoparticles,64-66 and in preparing pharmaceutical nanoparticle therapies,67-71 nanoparticle composites,72,73 and nanoparticles of various compositions.74-78 Changing one factor at a time while the remaining factors are held constant, the one-factor-at-a-time method of experimentation, is standard practice in chemistry. However, the one-factor-at-a-time experimental design only provides an estimate of an effect for a single factor at selected and fixed levels for all other factors. It is then necessary to assume that the effect would behave similarly at all other levels of the remaining factors to 8 of 52

ACS Paragon Plus Environment

Page 9 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

have a more general relevance; in other words an assumption that these remaining factors only affect the response additively. Factorial experiments have a two-fold advantage over the one-factor-at-a-time method. First, if factors do act additively, a factorial design can measure this primary effect for each factor, but with much more precision and fewer experiments per factor studied. Second, if one factor influences how another factor affects a response on top of its primary effect, a factorial design can detect, identify, and estimate this nonadditive, synergistic, secondary interaction effect. Table 1 presents the factors studied here, their level in the standard synthetic protocol, and the levels used for each factor in these factorial experiments. Further details on the selection of these levels can be found in Materials and Methods. Table 1. The experimental levels used for each factor of study compared with the standard protocol on a 10-mL synthesis scale.

*Reagent concentrations at beginning of rod growth for standard protocol: 94.0 mM CTAB, 0.495 mM HAuCl4, 0.544 mM Ascorbic acid, 0.040 mM AgNO3, 0.672 µM NaBH4, and [Seeds]syn×0.00119. The results and discussion presented here are focused on the presentation and discussion of the best-fitting, refined response-surface models that explain trends in the experimental response data. These models are summarized and presented as perspective plots; however, topographic versions of the perspective plots are available in the supporting information along with the results of a t-test and tabulated and graphical ANOVAs (SI Section ACS Paragon Plus Environment

9 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 53

7). For each synthetic run, the product was characterized by Vis-NIR extinction, TEM, and ICPMS (details described in Materials and Methods). An example of this raw data for an experimental run is presented in Figure 2. Additional plots of Vis-NIR extinction spectra, rod width as a function of rod length, and aspect ratio distribution are available for each of the 42 synthetic runs conducted in SI Sections 3 and 4. This raw characterization data has been analyzed, as described in Materials and Methods, resulting in longitudinal LSPR peak wavelength, extinction, yield, purity, and descriptive statistics of nanoparticle distributions for each run. These results are tabulated in SI Section 5. By themselves, these data do not offer insight easily as to where trends are located and to which factors are important in influencing these trends. Their value comes from the composite fractional factorial experimental design and its analysis. The screening response-surface models considering all eight factors and their two-factor interactions for each response are tabulated in SI Section 6 with the results of a ttest, tabulated and graphical ANOVAs (i.e., residual analysis), Daniel plot, and Bayes plot for each response. Further details on the statistical methods employed here may be found in Materials and Methods.

10 of 52

ACS Paragon Plus Environment

Page 11 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

Figure 2. An example of the raw data collected for one of 42 synthetic runs including: A) a VisNIR extinction spectrum, B) transmission electron microscopy images, and graphical representations of the distribution of the nanoparticles’ C) lengths, widths, and D) aspect ratios.

ACS Paragon Plus Environment

11 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 53

Longitudinal Peak Wavelength

Figure 3. A graphical summary of the significant primary and secondary interaction effects on the longitudinal surface plasmon resonance extinction peak wavelength. See Table 1 for the code for each letter condition. Black spectra illustrate the average extinction peak wavelength response. Blue|red spectra illustrate the average blue|red shift in the extinction peak wavelength response. Effects are reported as a response to increasing factor levels as reported in Table 1. P-values: ∗∗∗  0.001  ∗∗  0.01  ∗  0.05  .   0.1     1 It is known that the amount of trace silver ion in gold nanorod synthesis influences the aspect ratio and hence their longitudinal surface plasmon resonance extinction peak wavelength.59 However, the best, refined response-surface model shows four active factors, and their significant primary and secondary interaction effects tune the longitudinal peak wavelength (Figure 3). In addition to the amount of silver nitrate added, the amount of seeds added, the temperature, and the amount of ascorbic acid added have significant primary effects on the longitudinal peak wavelength as seen in the tabulated results of the t-tests (SI Section 7.A.i). Also, five of the six possible secondary interaction effects appear to be significant as well. Perspective plots of the refined model are presented in Figure 4. Tabulated and graphical ANOVA and lack-of-fit test (SI Section 7.A.i) show that the model has an excellent fit with an adjusted R2 value of 0.7238.

12 of 52

ACS Paragon Plus Environment

Page 13 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

Figure 4. Perspective plots showing the longitudinal extinction peak wavelength in response to changing the amount of seeds, temperature, amount of silver nitrate, and amount of ascorbic acid. Each plot shows a slice of the longitudinal peak wavelength response with one of the possible pairs of factors on each axis with the other two factors at the center point. A) Slice at 65 µL of AgNO3 & 62.5 µL of ascorbic acid, B) slice at 38 ˚C & 62.5 µL of ascorbic acid, C) slice at 38 ˚C & 65 µL of AgNO3, D) slice at 36 µL of seeds & 62.5 µL of ascorbic acid, E) 36 µL of seeds & 65 µL of AgNO3, and F) slice at 36 µL of seeds & 38 ˚C. From these figures, it is quite apparent that changing the amount of silver nitrate added produces the largest effect, specifically red-shifting the longitudinal peak by an average 85 ± 12 nm when increasing the silver nitrate added from 40 µL to 90 µL. The remaining primary and secondary interaction effects are approximately on the same order of magnitude; namely red or blue shifts ranging from about 20 to 50 nm when increasing from the low to high factor level. In order of decreasing absolute average shift, increasing the amount of seeds produces a red shift of 50 ± 12 nm; whereas, both increasing the temperature or the amount of ascorbic acid results in a blue shift of 37 ± 12 or 20 ± 12 nm, respectively. These quantified primary ACS Paragon Plus Environment

13 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 53

effects agree with previously published qualitative observations regarding the influence of the silver nitrate concentration;36,45,46,59 the amount of seeds;36,45,46,62 the temperature;46 and the amount of the reducing agent; whether ascorbic acid,36 dopamine,46 or hydroquinone.45 Similar qualitative results in the “seedless” or in situ seed generated synthesis of gold nanorods has been observed when increasing the silver nitrate concentration,38,60,61 the amount of seeds generated by increasing the amount of strong reductant,38,60,61 the temperature,38 and the amount of weak reducing agent.60 To our knowledge, no one has previously studied the nonadditive, secondary interaction effects of the amount of silver nitrate added, the amount of seeds added, the temperature, and the amount of reducing agent added either qualitatively or quantitatively. Increasing the ascorbic acid with increasing the amount of silver nitrate produces a blue shift of 28 ± 12 nm whereas increasing the temperature with increased ascorbic acid produces a red shift of 43 ± 12 nm. Increasing the amount of silver nitrate and the temperature results in a red shift of 24 ± 12 nm and increasing the amount of ascorbic acid and the amount of seeds added produces a red shift of 21 ± 12 nm. Increasing the amount of silver nitrate and the amount of seeds added results in a red shift of 27 ± 12 nm. If all four of these primary effects had been independent, nothing new would have been gained through these experiments as these four variables have been previously studied independently. However, the existence of these secondary interaction effects show that these factors are connected mechanistically (see Mechanistic Implications of Secondary Effects for discussion). What is surprising is the sheer number of secondary effects on the LSPR peak wavelength and that the amount of silver nitrate connects with all three of the other active factors.

14 of 52

ACS Paragon Plus Environment

Page 15 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

Metallic Gold Yield

Figure 5. A graphical summary of the significant primary and secondary interaction effects on the percent yield of gold. See Table 1 for the code for each letter condition. Each pie represents 100% metallic gold yield, where the gold wedge illustrates the average gold yield and the green|red wedge represents an average increase|decrease of the reported percentage. Effects are reported as a response to increasing factor levels as reported in Table 1. P-values: ∗∗∗  0.001  ∗∗  0.01  ∗  0.05  .   0.1     1 The best, refined response-surface model describing metallic gold yield, based on ICPMS measurements, has two factors and their significant primary and secondary interaction effects are summarized in Figure 5. The temperature and amount of ascorbic acid have significant primary effects and a secondary interaction effect as seen in the tabulated results of the t-tests (SI Section 7.B). Increasing the temperature results in a metallic yield decrease of about 7.3 ± 2.1 % on average, and increasing the amount of ascorbic acid results in a metallic yield increase of about 6.2 ± 2.1 % on average. Blocking effects also appear to be significant and indicate that freshly prepared ascorbic acid solutions are ideal for higher yields. In the statistical theory of the design of experiments, blocking is the arranging of experiments in groups (i.e., blocks) that are similar to one another. Usually a block of experiments is

ACS Paragon Plus Environment

15 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 53

conducted together to minimize unintentional differences within a block and allows for the statistical accounting of both intentional (e.g., stock reagent solution age) and unintentional (e.g., new reagent lots) differences between blocks. Tabulated and graphical ANOVA and lackof-fit test (SI Section 7.B) show that the model has an adequate fit with an adjusted R2 value of 0.4277.

Figure 6. Perspective plots showing A) the percent Au yield and B) the extinction, at the longitudinal LSPR peak wavelength, in response to changing the temperature and amount of ascorbic acid added. An alternative and experimentally expeditious way to approximate a semi-quantitative metallic gold yield is to use the extinction at the longitudinal peak wavelength as a proxy 16 of 52

ACS Paragon Plus Environment

Page 17 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

measurement for yield, assuming that the particles produced are of similar size with similar absorption coefficients and scattering cross-sections, and are suspended in similar volumes. Spectroscopic methods have previously been employed to measure metallic gold yield with semi-quantitative success; although, when compared to ICP measurements of digested gold nanorods, spectroscopic methods can have a 20-30% error.58,79 Perspective plots of both models are presented in Figure 6. The best, refined response-surface model of extinction also has only temperature and the amount of ascorbic acid added as active factors and similarly show that increasing only the ascorbic acid and keeping a lower temperature can achieve a higher yield or extinction. Significant primary and secondary interaction effects as seen in the tabulated t-tests (SI Section 7.A.ii). Tabulated and graphical ANOVA and lack-of-fit test (SI Section 7.A.ii) show that the model has an adequate fit with an adjusted R2 value of 0.7832. Very few published studies have examined the metallic gold yield when preparing gold nanorods.45,46,58,59 Historically59 (and in this work), the gold yield has always been low in an absolute sense; however, near quantitative conversion of gold ions to metallic gold can be achieved by using a large stoichiometric excess of reducing agent.45,46,58 Under both experimental conditions in this work (i.e., 55 vs. 70 µL of 0.100 M), ascorbic acid is the stoichiometrically limiting reagent in the reduction of auric ions with 20 and 80% theoretic gold yields, respectively; and therefore, allows for the identification of additional factors that influence metallic yield. Operating in an experimental space where theoretical gold yields are less then 100% permit the discovery of additional factors that improve the reduction of aurous ions, not only through a primary effect, but even a secondary effect that only operates at the higher ascorbic acid concentration. However, the model shows that actual gold yields tend to be about 5 and 20%, respectively, at the standard temperature condition of 26 ˚C (Figure 6). One idea for the cause of this large discrepancy between stoichiometric and actual yield is that the reaction is limited by the number of available nucleation points for growth (i.e., seeds). ACS Paragon Plus Environment

17 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 53

However, this work demonstrates that this is not the case, as the amount of seeds added does not appear to play an active role in determining the gold yield. Systematically, it appears that yields tend to be about 25% of the theoretical yield, and we propose that a portion of the ascorbic acid is sequestered within the hydrophobic phase of the surfactant micelles and is unavailable for aurous reduction to metallic gold on the surface of the seeds. In support of this notion is the fact that although near 100% metallic gold yield can be achieved with a significant stoichiometric excess of ascorbic acid,58 hydroquinone45 and other phenols,60 or dopamine46 as the reducing agent; a greater stoichiometric excess is needed in the case of phenols and dopamine to achieve that yield. These reducing agents are expected to have a higher hydrophobic partition coefficient than ascorbic acid due to their aromatic rings. Furthermore, increasing the temperature appears to negate any benefit from increasing the amount of ascorbic acid and may be due to changes in the hydrophobic partition coefficient of the reducing agent. Shape Purity Shape purity, (i.e. the fraction of nanoparticles that have the desired shape), is an important parameter to control because it is the morphology of the nanoparticles that leads to their interesting and useful properties. And although morphological impurities can be removed,80-84 this is done at considerable effort and expense. Shape purity can be semiquantitatively measured by determining the extinction ratio of the longitudinal and transverse LSPR peaks due to the overlap of the transverse LSPR of rods with the LSPR of spheres.62 However, a more quantitative measure of purity is the fraction of particles that have a rod-like morphology determined by counting particles in TEM micrographs, which is the method of measuring purity employed here.

18 of 52

ACS Paragon Plus Environment

Page 19 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

The best, refined response-surface model describing the fraction of rods has two active factors (Figure 7). Increasing either the temperature, or the amount of silver, or both, results in a decrease of 3.6 ± 2.1, 7.9 ± 2.1, or 7.3 ± 2.1%, respectively, in the fraction of rods. Tabulated t-tests demonstrate the significance of temperature and the amount of silver nitrate (SI Section 7.C.i). Blocking effects also appear to be significant and may be more important than these factors as their effect, an increased rod yield of about 17 ± 12.7 %, is two to three times larger. The active blocking effect suggests that freshly prepared silver nitrate is needed to ensure a low shape impurity and that even solutions wrapped in aluminum foil to prevent photodegradation are no longer ideal after a few hours. Tabulated and graphical ANOVA and lack-of-fit test (SI Section 7.C.i) show that the model has an adequate fit for identifying active factors with an adjusted R2 value of 0.4719.

ACS Paragon Plus Environment

19 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 53

Figure 7. A) A perspective plot showing the fraction of rods in response to changing the temperature and amount of silver nitrate added. B) A graphical summary of the significant primary and secondary interaction effects on the fraction of rods. See Table 1 for the code for each letter condition. Each pie represents 100% purity, where the gold wedge illustrates the average fraction of rods, the blue wedge illustrates the average fraction of shape impurities (usually spheres), and the red wedge represents the average decrease of the reported percentage. Effects are reported as a response to increasing factor levels as reported in Table 1. P-value: ∗∗∗  0.001  ∗∗  0.01  ∗  0.05  .   0.1     1 Frequently in the published literature, yield has been mistakenly synonymous with shape purity,36,38,42,62 which has been characterized both qualitatively38,45,46,60,62,85 and 20 of 52

ACS Paragon Plus Environment

Page 21 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

quantitatively.36,42,62 The primary effects observed here agree with previously published results on the effects of silver nitrate38,45,46 and temperature.38 Similar results have also been observed with the “seedless” in situ seed generated synthesis of gold nanorods.38,42,60 Though some have noted a much lower fraction of nanorods than reported in this work due to increased silver nitrate or temperature, this lower purity may actually be due to the age of their silver nitrate stock solution which has not been previously monitored or reported before this work. Also, to the best of our knowledge, no one has previously reported the synergistic effect of increasing both silver nitrate and temperature on decreasing shape purity. Rod Length and Width

Figure 8. A graphical summary of the significant primary and secondary interaction effects on the median nanorod length. See Table 1 for the code for each letter condition. The black nanorods illustrate the average median dimensions of the nanorods, where the red|green represents the average decrease|increase in median nanorod length. Effects are reported as a response to increasing factor levels as reported in Table 1. P-values: ∗∗∗  0.001  ∗∗  0.01  ∗  0.05  .   0.1     1 Measurements of the individual members of a population of nanoparticles will have a distribution where there are multiple statistical measurements to describe that distribution. Three descriptions of rod length include mode (the most common length), median (the middle length when sorted by size), and mean (the average length). The best, refined response-

ACS Paragon Plus Environment

21 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 53

surface model for each of these responses have the same four active factors and present similar trends (SI Sections 7.D.i-iii). Using median rod length for illustration, significant primary and secondary interaction effects are summarized in Figure 8. Tabulated t-tests demonstrate the significance of the amount of seeds, temperature, the amount of silver nitrate, and the amount of ascorbic acid (SI Section 7.D.ii). Perspective plots of the refined model are presented in Figure 9 in which it is apparent that changing the amount of seeds produced the largest effect, an average median length decrease of 11.2 ± 1.3 nm. Interestingly, there is only three primary and two secondary interaction effects. Increasing the amount of ascorbic acid results in an average median length increase of 5.3 ± 1.3 nm; whereas, increasing the temperature results in an average median length decrease of 3.2 ± 1.3 nm. The amount of silver nitrate only has a secondary, synergistic effect with the amount of ascorbic acid further increasing the average median length by 2.8 ± 1.2 nm and no primary effect. Tabulated and graphical ANOVA and lack-of-fit test (SI Section 7.D.ii) show that the model has an excellent fit with an adjust R2 value of 0.8241.

22 of 52

ACS Paragon Plus Environment

Page 23 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

Figure 9. Perspective plots showing the median rod length in response to changing the amount of seeds, temperature, amount of silver nitrate, and amount of ascorbic acid. Each plot shows a slice of the average median rod length response with one of the possible pairs of factors on each axis with the other two factors at the center point. The mode, median, and mean of the rod width is similar to length in that all three response-surface models have the same two active factors which have similar effects (SI Sections 7.E.i-iii). Using median again for illustration, increasing the amount of ascorbic acid results in thicker rods (increase of 4.07 ± 0.63 nm); whereas, increasing the amount of seeds added results in thinner rods (decrease of 7.07 ± 0.66 nm, Figure 10). Increasing both the amount of ascorbic acid and the seeds results in an additional average decrease of 2.66 ± 0.62 nm in width. Tabulated t-tests demonstrate the significance of the amount of ascorbic acid and the amount of seeds added (SI Section 7.E.ii). Blocking effects appear to be significant and suggest that fresher ascorbic acid solutions result in rods thinner by 4.19 ± 1.62 nm on average. Tabulated and graphical ANOVA and lack-of-fit test (SI Section 7.E.ii) show that the model has an excellent fit with an adjust R2 value of 0.7827.

ACS Paragon Plus Environment

23 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 53

Figure 10. A) A perspective plot showing median rod width in response to changing the amount of seeds and the amount of ascorbic acid added. B) A graphical summary of the significant primary and secondary interaction effects on the median rod width. See Table 1 for the code for each letter condition. The black nanorods illustrate the average median dimensions of the nanorods, where the red|green represents the average decrease|increase in median nanorod width. Effects are reported as a response to increasing factor levels as reported in Table 1. P-values: ∗∗∗  0.001  ∗∗  0.01  ∗  0.05  .   0.1     1

24 of 52

ACS Paragon Plus Environment

Page 25 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

As the amount of seeds was increased five-fold, it produced the largest effect on rod length and width. The dominant role of the amount of seeds is easier to understand because the amount of seeds does not play a determinative role in the amount of gold that is reduced in forming particles. By increasing the amount of seeds, there is less gold being added to each seed on average. This results in shorter, thinner rods (Figure 8 and Figure 10) as the amount of seeds added increases. We see the combined effect of this in the LSPR peak wavelength, which according to Gans theory1,86-88 is dominated by particle aspect ratio and changes in local medium dielectric constant. As the decrease in nanorod width is a larger percent change (48%) in that dimension compared to decreasing length (33%), this results in an increase of the particle’s aspect ratio and a corresponding red-shift of the LSPR peak wavelength (Figure 3). Similar results have been observed previously regarding rod dimensions, longitudinal LSPR peak wavelength, and the amount of seeds added.36,45,46,62 Comparatively, increasing the amount of sodium borohydride in the “seedless” in situ seed generated synthesis of gold nanorods produces more nucleation points (i.e., in situ seeds) and has a similar effect on rod dimensions and LSPR peak wavelength.41,60,61 As increasing the amount of ascorbic acid increases the yield of metallic gold, there is more gold available for each growing seed particle. This results longer, thicker rods as the amount of ascorbic acid is increased (Figure 8 and Figure 10). The LSPR peak blue-shifts when the amount of ascorbic acid is increased because the aspect ratio is decreasing (Figure 3). This decrease is because the percent increase to the width (28 %) is larger than that of the length (16 %) when increasing the ascorbic acid. Analogous results have been observed when increasing the amount of reductant, regardless of the specific reductant (e.g., ascorbic acid,36 hydroquinone,45 dopamine,46 or other phenol derivatives60). Both temperature and the amount of silver nitrate seem to only have an influence on nanorod length and not the width. Increasing the temperature results in shorter nanorods ACS Paragon Plus Environment

25 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 26 of 53

(Figure 8), decreased aspect ratios, and therefore a blue-shifted LSPR peak wavelength (Figure 3). In contrast to this, increasing the silver nitrate contributes to longer rods and therefore an increased aspect ratio and a red-shifted LSPR peak wavelength. These results are consistent with previously published results regarding the effects of silver nitrate42,45,46,59-61 and temperature.46,60 Other statistical descriptors of rod length and width describing the dispersion, such as standard deviation, skewness, and kurtosis, are poorly modeled by these response-surface models with adjusted R2 values typically well below 0.5 but still have significant p-values. This shows that these responses are not well modeled as a linear relationship between the primary and secondary interaction effects of these factors, but that the models do capture all the linear information in the data that exists (albeit that is not much). Furthermore, this suggests that there are additional, unknown and uncontrolled factors (in these experiments) that influence the dispersion of rod dimensions. This data suggests that the amount of seeds play a role in the standard deviation and kurtosis of rod length (SI Section 7.D.iv & 7.D.vi) and the temperature and amount of silver nitrate influence the skewness of rod length (SI Section 7.D.iv). Whereas, the standard deviation, skewness, and kurtosis of rod width (SI Section 7.E.iv-vi) appear to be affected by the amount of seeds and ascorbic acid, the amount of seeds, and the amount of sodium borohydride, respectively. Aspect Ratio and Multivariate Dimensional Characterization Aspect ratio is a difficult response to model as a linear relationship between the primary and secondary interaction effects. The models for mode, median, and mean aspect ratio suggest that the amount of seeds and the amount of silver nitrate influence the aspect ratio (SI Section 7.G.i-iii). Despite significant p-values, adjusted R2 values are below 0.4 for mode, median, and mean aspect ratio. Changing the amount of ascorbic acid does not show an

26 of 52

ACS Paragon Plus Environment

Page 27 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

appreciable effect on aspect ratio despite being important in influencing both length and width. This may be due to that the proportional influence of ascorbic acid between length and width nearly maintains constant average aspect ratio within statistical error over the range studied and therefore does not measure as a major influential factor. Models for the standard deviation and skewness of aspect ratio also have low R2 values, but show significant effects from changing the amount of seeds and the temperature, respectively (SI Section 7.G.iv-v). The model for aspect ratio kurtosis, a measure of distribution spread, shows significant primary effects in the amount of seeds added and the amount of silver nitrate causing an decrease or increase, respectively, with an adjusted R2 value above 0.50 (SI Section 7.G.vi). An alternative approach to considering both length and width simultaneously is to use multivariate descriptive statistics. The coordinate-wise mean is identical to the mean obtained when considering length and width simultaneously and is susceptible to outliers. Alternatively, median is resistant to outliers and the multivariate median employed here is a spatial median that minimizes the sum of the Euclidean distances between the spatial median and the data. The best, refined response-surface models for spatial median length and width have the same active factors and trends as their coordinate-wise counterparts with equally adequate model fit and adjust R2 values (SI Section 7.F.i-ii). Multivariate descriptive statistics can also be used describe the dispersion in the data (i.e., multivariate mean and median deviation, total variation), as well as, the shape (i.e. multivariate skewness and kurtosis). Like the coordinatewise dispersion statistics, multivariate dispersion statistics are poorly modeled as a linear relationship between the primary and secondary interaction effects of these factors, but the data does suggest that the amount of seeds and temperature may play a role in the dispersion of their dimensions (SI Section 7.F.iii-vii). With more data at additional factor levels, fully quadratic models may be better abled to determine significant dispersion effects for these

ACS Paragon Plus Environment

27 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 28 of 53

factors or the larger data set could suggest appropriate transformations so that it may be more easily modeled. Mechanistic Implications of Secondary Effects Secondary effects are manifested when one factor synergistically influences how another factor affects a response in addition to their primary effect. Interestingly, more significant secondary effects are observed in the LSPR data than in either the length and width data. This is most likely due to the increased sensitivity that LSPR peak wavelength has to changes in aspect ratio or local medium dielectric and the level of error in the models for determining which secondary interaction effects are significant. In the case of LSPR peak, the standard error is about 11 nm and corresponds to an exceedingly small change in the aspect ratio. In the case of length and especially width, the standard error is about 1.2 and 0.7 nm, respectively, and is a larger percent error than observed for LSPR peak wavelength (SI Sections 7.A.i, 7.D.i-iii, & 7.E.i-iii). Therefore, a factor has to be of greater importance to appear significant in the nanoparticle dimensional data, and conversely the LSPR data is better at measuring smaller yet still significant effects. Secondary interaction effects that appear in the dimensional data show a mechanistic connection between these factors. Auric Reduction The net redox reaction for the reduction of AuIII to Au0 in this synthesis is presented in Scheme 1A. AuBr4- 1 has been identified as the main gold species present in a solution of CTAB micelles;58,89 and, at the acidic conditions of the synthesis, L-ascorbic acid is mostly in the form of L-ascorbate 2.90,91 The reduction of AuIII however occurs in two steps: reduction to AuI when ascorbic acid is added (Scheme 1B), followed by reduction to Au0 once the seeds are added (Scheme 1C or D) as ascorbate is not a strong enough reductant to reduce AuI to Au0 without a gold surface. The two-electron oxidation of L-ascorbic acid 7 is presented in 28 of 52

ACS Paragon Plus Environment

Page 29 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

Scheme 1E with the dominant secondary reducing species, radical anionic ascorbate 6, which is the strongest reductant of the possible radical ascorbates.91 As L-ascorbate 2 is the limiting reagent in Scheme 1B and complete reduction to AuI is observed, the product radical anionic ascorbate 6 must also participate in the reduction of AuIII (Scheme 1B). Two mechanisms for the second reduction of AuI to Au0 have been proposed; namely, the disproportionation of AuI to Au0 and AuIII (Scheme 1C) and the direct reduction of AuI (Scheme 1D). It has been observed that the production of metallic gold as a function of time has a sigmoidal shape consistent with an autocatalytic reaction;58 however, this cannot distinguish between the two mechanisms as both mechanisms are catalyzed by metallic gold and would be autocatalytic as metallic gold is produced.

ACS Paragon Plus Environment

29 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 30 of 53

Scheme 1. Various reactions involved in the reduction of AuIII to Au0. A) net reaction, B) primary reduction of AuIII to AuI, C) disproportionation reaction of AuI to AuIII and Au0, D) direct reduction of AuI to Au0, and E) oxidation of L-ascorbic acid to L-dehydroascorbic acid. Note that only Au is shown balanced; bromide ions are not shown.

30 of 52

ACS Paragon Plus Environment

Page 31 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

In the results presented here, the amount of seeds and the amount of ascorbic acid added has an additional secondary interaction effect that when both are increased: rods are shorter and thinner (Figure 8 and Figure 10) than the sum of either factor alone. Because the decrease in width is a larger percent change (8% vs. 18%), the aspect ratio increases, resulting in a red-shift of the LSPR peak wavelength (Figure 3). The existence of this secondary effect suggests that the seeds and the ascorbic acid are physically interacting and supports the direct reduction of aurous ions on the surface of the seed by ascorbic acid (Scheme 1D) over a disproportionation reaction of three aurous ions on the seed (Scheme 1C). Furthermore, with the range of concentrations employed, there is only one or two AuBr4- 1 solubilized with the surface of each micelle;58 and this reduces the likelihood of three aurous ions meeting for disproportionation. Only at temperatures higher then employed here (100˚C), the two-electron oxidized product of ascorbic acid, dehydroascorbic acid 3, and its easily hydrolyzed form 2,3-diketo-1gulonic acid can reduced gold ions due to the presence of mild reducing alcohol groups.92 However, the results presented here on the effects of temperature on metallic gold yield (Figure 5) indicate that increasing the temperature results in a deceased yield and that 50 ˚C is insufficient to cause appreciable reduction of gold by dehydroascorbic acid or 2,3-diketo-1gulonic acid. At the temperatures employed here, ascorbic acid is limited to providing two electrons per molecule for the reduction of gold. The Role of Silver Three differing mechanisms have been proposed on the role of silver in the growth of gold nanorods. The first mechanism is that silver is selectively reduced from Ag+ to Ag0 on specific faces due to the reduction potential of the growth solution, blocking isotropic growth, and resulting in nanorods.7,10,33,93 The underpotential deposition of silver on gold is expected to

ACS Paragon Plus Environment

31 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 32 of 53

prefer the high-energy side facets of gold nanorods.33,93-95 A second, yet similar, alternative mechanism is the preferential deposition of silver bromide complexes blocking gold addition to these side facets.7,10 The third mechanism, is a soft template mechanism based on the rod-like micelle structure that CTAB forms above its critical micelle concentration (~1mM).10,38,96 The addition of silver to CTAB micelles may alter their shape and subsequently the nanorods.38,97 There is evidence that silver is incorporated into the gold nanorods (2.5 to 9%) and that it is preferentially at or near the surface using a combination of XPS, SERS, and ICP-MS.59,98 Furthermore, ICP-AES and XPS studies on a variety of gold nanoparticle shapes (i.e., octahedral, rhombic dodecahedra, truncated ditetragonal prisms, and concave cubes) produced by varying the trace silver concentration, shows a correlation between silver coverage on gold facets and what was predicted, if silver serves as a blocking agent.99 However, it is unclear if a similar mechanism is at play in nanorods as the shapes studied in these experiments did not included nanorods. Further evidence also shows the presence of bromide at the surface of gold nanorods. The bromide ion is an important synthetic component as replacement of bromide completely with chloride does not result in nanorods; however, with bromide still on the seeds it can be replaced with sodium oleate in the growth solution.100 Au-Br and Ag-Br species have been identified by XPS and SERS, and the disappearance of the Au-Br stretch has been observed by Raman spectroscopy upon addition of thiols.42,98,101 Furthermore, multiple groups have identified the presence of AgBr and AuBr by mass spectrometry.102,103 However, recent work employing HR-TEM and STEM-EDS elemental maps suggests that silver is present on all surfaces of gold nanorods contradicting these first two mechanisms.104 Little experimental evidence exists besides the correlation between elongated CTAB micelles and nanorod shape in support of the third mechanism.38,105 The preferential adsorption of CTAB to specific facets of the growing nanorod is usually invoked as 32 of 52

ACS Paragon Plus Environment

Page 33 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

thermodynamic arguments for the anisotropic growth. However, the adsorption of CTA+ on different crystallographic planes of flat gold, in electrochemical experiments, demonstrate little thermodynamic preference between crystal faces.106,107 These electrochemical experiments do show differing levels of bromide adsorption on different crystallographic planes. This suggests that there may be a sufficiently different electronic states between crystal facets so that the diffusion of charged species (i.e., reagents) to these faces would be different impacting their reactivity and rate of growth.97 The surfactant still may be critical in the symmetry breaking event required to go from a symmetrical seed to an anisotropic nanorod. In this work, the amount of silver shows neither a primary effect in length nor width; but does have a secondary interaction effect with the amount of ascorbic acid resulting in longer rods (Figure 8), an increased aspect ratio, and a red-shifted LSPR peak (Figure 3). As there is neither a primary effect in length nor width, the corollary is that silver does not directly influence the length or width despite being eventually deposited on the surface of the growing nanorod. We propose that the deposition of silver on the gold surface is not the driving force for an anisotropic particle and propose, as others have before, that the high levels of bromide is responsible for promoting and stabilizing nanoparticle anisotropy.106-108 Our current results suggest that the primary role of silver is to modify the rate of reduction of aurous ions by a radical ascorbate anion. This reduction is kinetically suppressed by CTA+ compared to the synthesis of CTA+-free gold spheres and this work shows that the growth is finely tuned further to a slightly faster rate on the ends of the rods due to silver synergistically assisting ascorbic acid in the reduction of gold. This may be achieved mechanistically by the silver cation shielding the aurous bromide anion or the radical ascorbate anion allowing it to more readily approach the negatively charged, bromide coated, gold surface. Furthermore, we propose that the loss of silver to the surface of the nanorod operates as a sink for silver, removing it from the reaction. This silver sink is responsible for the cessation of growth once the silver cations ACS Paragon Plus Environment

33 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 34 of 53

are no longer available in sufficient quantities to shield anionic reagents. This notion agrees with why higher concentrations of silver nitrate are needed when producing gold mininanorods,62 or larger nanorods via reduction with hydroquinone45 or a co-surfactant sodium oleate.109 Due to an increased production of surface area, which serves as a larger silver sink, higher concentrations of silver nitrate are needed to compensate for the increase of silver lost to a larger silver sink. Silver nitrate having a relatively minor role in determining the absolute dimensions of the nanorods (Figure 8 and Figure 10) begs the question as to why changes in silver nitrate produces the largest effect on the longitudinal LSPR wavelength (Figure 3). According to extended Mie theory by Gans,1,86-88 the longitudinal LSPR wavelength is mainly dependent on two properties: 1) the dimensions of the nanorod (specifically its aspect ratio) which effects the polarizability of the LSPR, and 2) the effective medium dielectric surrounding the nanorod, which includes adsorbed species. Therefore we propose, if silver is not the dominating factor controlling the dimensions of the nanorods, it must be influencing the effective medium dielectric that the nanorod experiences through the adsorption of silver complexing with bromide on the surface. Inactive Factors Four of the eight factors studied here (age of seeds; increasing borohydride concentration for seed formation; rate of stirring during growth; age of growth solution) do not appear to have any appreciable effect on any of the responses; however, when taken to an extreme value outside these experimental ranges, an effect would be expected for all factors. For example, using seed particles that are weeks old that may have ripened into much larger particles or dissolved into a colorless solution would not be expected to successfully produce nanorods. Yet, the lack of difference between one-hour old seeds and five-hour old seeds

34 of 52

ACS Paragon Plus Environment

Page 35 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

indicates that the structure, surface chemistry, and reactivity of the seeds are relatively stable over this timeframe and that any excess sodium borohydride has sufficiently decomposed within one hour and does not appreciably affect the nanorod synthesis. A lack of an effect when increasing the amount of sodium borohydride used in the synthesis of the seeds demonstrates that the byproducts of borohydride oxidation does not influence the subsequent nanorod synthesis. It shows that it is an increase in the number of seed particles that is responsible for the observed effects of increasing the volume of the seed suspension added and not borohydride oxidation byproducts. The rate of stirring when preparing the seed nanoparticles does not have any appreciable effect despite laboratory lore to the contrary. And finally, the lack of an effect of varying the age of the reduced growth solution shows that the reduction of auric ions to aurous ions is a thermodynamically controlled process, and not kinetically controlled under these conditions, where equilibrium is rapidly reached. This includes the distribution of remaining ascorbic acid molecules that are available (or not available, i.e., sequestered) for the subsequent reduction of aurous ions to metallic gold. Conclusion Combined, these results show that the basic process of forming gold nanorods is the reduction of auric ions by ascorbic acid onto seed nanoparticles. The amount of ascorbic acid, mainly, influences how much metallic gold will be produced and the amount of seeds determines how it is divided up. The particles grow with intrinsic, yet different rates of growth on the ends vs. the sides, forming rods, where the growth in these directions is either decreased or increased as a function of increasing the amount of seeds or ascorbic acid, respectively. Furthermore, the proportional change of length and width can result in an increased or decreased aspect ratio, respectively, and a corresponding shift in LSPR peak wavelength. The growth on the ends of the rods can be further tuned by changing the amount

ACS Paragon Plus Environment

35 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 36 of 53

of silver nitrate or the temperature, providing the main methods of control over the optical properties of the nanoparticles. Careful and intentional control over the amount of ascorbic acid, the temperature, and especially the amount of seeds added leads to the most reproducible and robust nanorod syntheses. Furthermore, slight photodegradation of silver nitrate and ascorbic acid reagents can negatively impact nanoparticle purity and gold yield, respectively. Future work expanding on the ranges examined here in the active factors will allow for better modeling of the data through canonical analysis, error reduction, and the use of fully quadratic models. This will lead to better synthetic control at higher yields where multiple responses could be simultaneously controlled and optimized. Furthermore, having a larger data matrix will potentially allow for an improved understanding of the effects of these factors on aspect ratio, as directly measured, and measures of particle dispersion. Has the problem presented in Figure 1C of less than satisfactory precision and reproducibility, when averaged over many people over long time, been completely solved? No: the chemical community is still struggling to achieve this goal in syntheses. The example of general chemistry laboratory experiments comes to mind: even with explicitly detailed instructions, when thousands of people do an experiment, they do not all achieve the same result. One experienced person can produce the beautiful data of Figure 1B. However, this paper represents progress towards the goal of robust precision and reproducibility – especially for these kinetically-controlled crystal growth processes -

and validates this experimental

approach in general when studying nanomaterial synthesis. Yet, more research needs to be done even on just this synthesis. One set of synthetic parameters were studied here. At the outset of these experiments some were known to be important ([Ag+] and [reductant]) and some thought unlikely to be important (rate of stirring), serving as a negative control. Still many possibly important factors, and more importantly their interactions with each other, remain to be studied in quantitative detail including pH, the time required for halide ligand exchange 36 of 52

ACS Paragon Plus Environment

Page 37 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

between HAuCl4 and CTAB, alternative and mixtures of reducing agents, and various cosurfactants. Even the nitrate counterions, and oxygen in the air, have redox chemistry that has not been explored and might be important in reducing the variability in the synthesis. There are commercial sources of gold nanorods, which, as far as we are aware, are done in batches not dissimilar to our method.

Improved production will likely be done via a programmed and

automated system, perhaps similar to our own millifluidic reactor48 to achieve improved precision and reproducibility. Achieving that goal requires that all of the important synthetic parameters to control be identified, including how they influence each other. Materials and Methods Materials Reagent solutions were prepared with nanopure water (Barnstead NANOpure II) in volumetric flasks that had been cleaned with fresh aqua regia and rinsed five times with nanopure water (as was all equipment used here). The pH of nanopure water can vary, especially over half a decade, and may have contributed to the variability observed in Figure 1C. However, it is not likely to vary significantly over the three days of experiments within each block and is controlled for between blocks, which occurred over a six month period. The following chemicals were employed in this research: cetyltrimethylammonium bromide (Sigma), chloroauric acid (Sigma-Aldrich), silver nitrate (Sigma-Aldrich), ascorbic acid (Acros & Sigma), and sodium borohydride (Aldrich). A table of lot designators is available in the supporting information. Chemicals were used as received without further purification, but some specific care was taken in handling certain reagents. Fresh silver nitrate and ascorbic acid solutions were prepared and wrapped in aluminum foil to minimize photodegradation. These were prepared fresh every three days (block 1) or every day (blocks 2, 3, & 4). Sodium borohydride was opened, weighed, and stored under dry nitrogen in a glove bag and desiccator until use.

ACS Paragon Plus Environment

37 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 38 of 53

This was done to minimize the adsorption of atmospheric water and the associated decomposition to ensure accurate masses. The nitrogen gas was dried using Drierite and a laboratory gas-drying unit (W.A. Hammond Drierite Company). For consistent stirring, all stir bars were a Teflon coated 1/2 in. by 1/8 in. polygon stir bar. Sample Characterization and Analysis In addition to controlling the longitudinal plasmon peak wavelength, there are a few additional parameters that are useful to control when synthesizing gold nanorods. These include the particle dimensions and their distributions (i.e., length, width, and aspect ratio), metallic gold yield, and particle shape purity. Quite often in the scientific literature, yield is used interchangeably to describe how much of the starting material is recovered in the final nanoparticles or how much of the final nanoparticles adopt a specific morphology (e.g., spheres vs. rods). Here yield is used to describe the former (i.e., the percent of gold added that is recovered as nanoparticles), while purity the later (i.e., the percent of particles with a rod morphology). Visible-Near-Infrared Extinction Spectroscopy To determine the longitudinal plasmon peak wavelength as well as its extinction (i.e., a proxy for yield), the visible near-infrared (Vis-NIR) extinction spectrum was measured from 400 nm to 1100 nm using a Cary 5000 Series UV-Vis-NIR spectrophotometer (Agilent Technologies). Spectrums were measured using a 1 cm quartz cuvette with a nanopure water background subtraction and a scan interval of 1 nm at a rate of 30 nm per second. Inductively Coupled Plasma Mass Spectrometry To determine gold yield, samples from each run were digested with freshly prepared metal-free aqua regia (3:1 v:v neat HCl:HNO3) and quantitatively diluted to between 10 and 80

38 of 52

ACS Paragon Plus Environment

Page 39 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

ppb Au. These were then submitted to the UIUC School of Chemical Science’s Microanalysis Laboratory for elemental analysis by Inductively Coupled Plasma Mass Spectrometry (ICPMS). Samples were analyzed in triplicate on a SCIEX ELAN DRCe ICP-MS against appropriate standards to determine yields with standard errors. An alternative spectroscopic method (absorbance at 400 nm, which is indicative of elemental gold) has recently been developed using spherical particles that shows both a size and surface functionalization dependence causing up to 30% uncertainty.79 At the outset of these experiments, ICP-MS was selected as the means employed here to determine gold yield due to established analysis protocols within the research group and the potential of a size dependence (and need for optimization with nanorods); however, since the completion of this work, this method has been demonstrated with nanorods,110 achieving similar levels of uncertainty as ICP-MS, and was found to have little size dependence most likely due to the small size range observed in nanorod width. Transmission Electron Microscopy Transmission electron microscopy (TEM) was employed to characterize the dimensions of the nanoparticles as well as their purity. TEM samples were prepared by drop casting sample suspensions on 200 mesh copper grids that were coated with a holey, amorphous carbon support film (SPI, inc.) and allowed to air dry. Images were collected on two TEM instruments in the UIUC Materials Research Laboratory’s Center for Microanalysis of Materials. Specifically, either a JEOL 2100 Cryo TEM or JEOL 2010 LaB6 TEM were employed at 200 kV to collect images on either a Gatan UltraScan 2kx2k CCD or a Gatan MatScan1kx1k progressive scan CCD with 1 second exposures, respectively. For each sample, 350+ particles were counted and measured with two conditions. Namely, that every particle in an image must be counted and measured and that once 350

ACS Paragon Plus Environment

39 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 40 of 53

particles had been measured that final image had to be finished. This was done to avoid sampling bias in describing the population distribution. Image analysis was performed using ImageJ.111-114 Statistical descriptions of the particle distributions (i.e., mode, median, mean, standard deviation skewness and kurtosis) for length, width, and aspect ratio for each run were calculated using Mathematica.115 Furthermore, multivariate characterization (i.e., spatial median, mean deviation, median deviation, skewness, kurtosis, and total variation) was also performed considering both length and width simultaneously. Calculating the standard error of many of these descriptive statistics is not a trivial matter; however, they can be computationally approximated

using

a

bootstrap

method.116,117

Assuming

each

sampling

of

350+

measurements is representative of the entire TEM sample, one thousand virtual data sets were created by random selection with replacement for which each of the aforementioned descriptive statistics was determined. The standard deviations of these statistics over the virtual data sets are estimates of the standard errors for the statistics determined from the original sample population. Composite Fractional Factorial Design of Experiments A composite fractional factorial design of experiments is a sequential-experimentation process to optimize a response-surface model in determining which factors are active and which are essentially inert. A principal reference in the application of statistical methods, as applied to experimental design, is Statistics for Experimenters: Design, Innovation, and Discovery; to which, the interested reader is directed for a through instruction in the application of these methods.63 The factors employed and their variable levels are presented in Table 1. These levels are carefully selected and their selection is of utmost importance in designing successful factorial experiments.63 The experimental design employed here is presented in Table 2. Blocking was employed to account for differences between stages of sequential-

40 of 52

ACS Paragon Plus Environment

Page 41 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

experimentation, both, intentional differences (i.e., the age of silver nitrate and ascorbic acid solutions) and unintentional differences (i.e., changes between reagent lots). Table 2. The composite fractional factorial design of experiments conducted consisting of a 2  fractional factorial design with center point, a multiple-column foldover (A, C, D, L, & M) factorial design, and additional runs selected through Bayesian Screening analysis listed in randomized order of experimentation.

In these experiments, a full 2 factorial design consisting of the aforementioned eight factors each with two experimental levels results in a possible 256 different experimental sets of conditions to run. As this number of experiments is prohibitively costly and time consuming,

ACS Paragon Plus Environment

41 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 42 of 53

a specific subset of these 256 experiments was selected plus a center point that would still allow the unconfounded approximation of the primary effects of these factors to determine their importance.63,118,119 Further details on the experimental design can be found in SI Section 1. Fractional Factorial Analysis The composite fractional factorial design employed here was analyzed through response-surface methods using the rsm package120 and BsMD package121 for R122,123 with 30 response variables produced from sample characterization and analysis. For each response variable, a response-surface was modeled based on all eight factors and their two-factor interactions through a weighted least-squares approach; where, weights were the inverse of the standard error squared for each data point. An adjusted R-squared, F-statistic, and P-value for each model was calculated. Along with these values, the fit of the model was evaluated through a tabulated and graphical analysis of variance (ANOVA) by plotting the standardized residuals against a normal distribution, order of experimentation, and modeled values. This was done to check for large irregularities (i.e. the lack of independent, normal and identical distributed random errors, model additively, and constant variance) that would suggest a nonrandom nature to the residuals and the need for data transformation (e.g., scaling), new models or correction for systematic errors.63 Based on these analyses, the top ten candidates out of 256 possible models for each response variable were then fit to the data, without essentially inert factors, to find the best, refined model. The removal of essentially inert factors from the design analysis cause some runs to essentially be replicates.63 This is because the inert factors were the only experimental difference between runs and these differences were determined to produce no significant effect in the response parameter. If there are enough inert factors, this results in a fractional factorial design collapsing into a complete factorial design of the active factors due to the

42 of 52

ACS Paragon Plus Environment

Page 43 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

projectivity of fractional factorial designs. This means that the data can be more accurately modeled without confounding interaction effects and smaller standard errors. The best of these models uses the most factors without additional, unnecessary factors resulting in a large adjusted R-squared value and small p-value for the model as a whole. Models with a p-value less than 0.05 for the lack-of-fit test are considered to inadequately describe the response data and are therefore rejected as possible models. Furthermore, each factor in a refined model needs to have a significant effect (i.e., p-value < 0.05) in either a primary effect, two-term interaction effect, or both. If a factor does not have a significant effect, it is only aiding the model in fitting the experimental error (i.e., noise) and is therefore eliminated as a suitable model. In some cases, multiple models remain as statistically viable after this selection process and these models were ranking using a Bayesian information criterion to determine the best refined model. The remaining alternative refined models don’t describe the experimental data as well as the best refined model; however, they describe the data sufficiently to suggest possible additional active factors that require further experiments to conclude if those factors are actually active. Further details on the fractional factorial analysis can be found in SI Section 6 & 8. Associated Content Supporting Information Supporting information is organized into nine sections: 1. Design of Experiment, 2. Reagent Lots, 3. Vis-NIR characterization, 4. TEM characterization, 5. Data from characterization analysis, 6. Fractional Factorial Screening Models, 7. Best Refined SurfaceResponse Models and Analysis, 8. Alternative Refined Surface-Response Models and Analysis, and 9. References. Section one details the design of the experiments employed.

ACS Paragon Plus Environment

43 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 44 of 53

Section two contains a table of reagent lot numbers. Section three presents the raw Vis-NIR extinction spectra for each of the 42 experimental runs. Section four includes the paired TEM characterization of nanorod length and width as scatter plots and the distribution of nanorod aspect ratio. Section five contains tabulated results of the analysis of this data for each run providing LSPR peak wavelengths, their extinction, purity, yield, and descriptive statistics of nanoparticle size and aspect ratio distribution along with standard error values. Section six contains the tabulated screening response-surface models consisting of all eight factors and their two-factor interactions for each response with the results of the t-test. In addition to these tables, the tabulated and graphical ANOVA (i.e., residual analysis), Daniel plot, and Bayes plot are provided for each response. Section seven contains larger perspective and topographic plots of each of the refined response-surface models that best explain the observations in the experimental data for ease of viewing. With these plots are the tabulated results of the t-test and the tabulated and graphical ANOVA (i.e., residual analysis) for each response. Section eight contains topographic plots of each of the alternative refined response-surface models. With these plots are the tabulated results of the t-test and the tabulated and graphical ANOVA (i.e., residual analysis) for each response. This material is available free of charge via the Internet at http://pubs.acs.org. Author Information Corresponding Authors Nathan Burrows: [email protected]; Catherine J. Murphy, [email protected]. Acknowledgements This work was carried out in part in the Frederick Seitz Materials Research Laboratory Central Research Facilities, University of Illinois at Urbana - Champaign. We acknowledge the National Science Foundation for financial support of this work through grant CHE-1306596 and 44 of 52

ACS Paragon Plus Environment

Page 45 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

CBET 1336411. S.H. thanks the UIUC Department of Chemistry for the opportunity to participate in the Research Experience for Undergraduates program funded by the National Science Foundation and the 3M Foundation. We thank Dr. Rudiger Laufhutte at the UIUC School of Chemical Science’s Microanalysis Laboratory for conducting elemental analysis by ICP-MS. We thank the rest of the Murphy group for thoughtful discussions about synthetic protocols and lab practices. References (1)

(2) (3)

(4)

(5) (6)

(7)

(8) (9) (10) (11) (12)

Link, S.; Mohamed, M. B.; El-Sayed, M. A. Simulation of the Optical Absorption Spectra of Gold Nanorods as a Function of Their Aspect Ratio and the Effect of the Medium Dielectric Constant. J. Phys. Chem. B 1999, 103 (16), 3073–3077. Nikoobakht, B.; El-Sayed, M. A. Evidence for Bilayer Assembly of Cationic Surfactants on the Surface of Gold Nanorods. Langmuir 2001, 17 (20), 6368–6374. Nikoobakht, B.; El-Sayed, M. A. Preparation and Growth Mechanism of Gold Nanorods (NRs) Using Seed-Mediated Growth Method. Chem. Mater. 2003, 15 (10), 1957–1962. Eustis, S.; El-Sayed, M. A. Why Gold Nanoparticles Are More Precious Than Pretty Gold: Noble Metal Surface Plasmon Resonance and Its Enhancement of the Radiative and Nonradiative Properties of Nanocrystals of Different Shapes. Chem. Soc. Rev. 2006, 35 (3), 209–217. Huang, X.; Neretina, S.; El-Sayed, M. A. Gold Nanorods: From Synthesis and Properties to Biological and Biomedical Applications. Adv. Mater. 2009, 21 (48), 4880–4910. Murphy, C. J.; Thompson, L. B.; Alkilany, A. M.; Sisco, P. N.; Boulos, S. P.; Sivapalan, S. T.; Yang, J. A.; Chernak, D. J.; Huang, J. The Many Faces of Gold Nanorods. J. Phys. Chem. Lett. 2010, 1 (19), 2867–2875. Murphy, C. J.; Thompson, L. B.; Chernak, D. J.; Yang, J. A.; Sivapalan, S. T.; Boulos, S. P.; Huang, J.; Alkilany, A. M.; Sisco, P. N. Gold Nanorod Crystal Growth: From Seed-Mediated Synthesis to Nanoscale Sculpting. Curr. Opin. Colloid Interface Sci. 2011, 16 (2), 128–134. Murphy, C. J.; Dreaden, E. C.; Alkilany, A. M.; Huang, X.; El-Sayed, M. A. The Golden Age: Gold Nanoparticles for Biomedicine. Chem. Soc. Rev. 2012, 41 (7), 2740–2779. Vigderman, L.; Khanal, B. P.; Zubarev, E. R. Functional Gold Nanorods: Synthesis, Self-Assembly, and Sensing Applications. Adv. Mater. 2012, 24 (36), 4811–4841. Lohse, S. E.; Murphy, C. J. The Quest for Shape Control: a History of Gold Nanorod Synthesis. Chem. Mater. 2013, 25 (8), 1250–1261. Jana, N. R.; Gearheart, L. A.; Murphy, C. J. Seed-Mediated Growth Approach for Shape-Controlled Synthesis of Spheroidal and Rod-Like Gold Nanoparticles Using a Surfactant Template. Adv. Mater. 2001, 13 (18), 1389–1393. Jana, N. R.; Gearheart, L. A.; Murphy, C. J. Wet Chemical Synthesis of High Aspect Ratio Cylindrical Gold Nanorods. J. Phys. Chem. B 2001, 105 (19), 4065–4067. ACS Paragon Plus Environment

45 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(13) (14) (15) (16)

(17)

(18) (19)

(20)

(21) (22)

(23)

(24) (25) (26) (27) (28) (29) 46 of 52

Page 46 of 53

Johnson, C. J.; Murphy, C. J.; Dujardin, E.; Davis, S. A.; Mann, S. Growth and Form of Gold Nanorods Prepared by Seed-Mediated, Surfactant-Directed Synthesis. J. Mater. Chem. 2002, 12 (6), 1765–1770. Busbee, B. D.; Obare, S. O.; Murphy, C. J. An Improved Synthesis of High-AspectRatio Gold Nanorods. Adv. Mater. 2003, 15 (5), 414–416. Gao, J.; Bender, C. M.; Murphy, C. J. Dependence of the Gold Nanorod Aspect Ratio on the Nature of the Directing Surfactant in Aqueous Solution. Langmuir 2003, 19 (21), 9065–9070. Chen, H.; Di, Y.; Chen, D.; Madrid, K.; Zhang, M.; Tian, C.; Tang, L.; Gu, Y. Combined Chemo- and Photo-Thermal Therapy Delivered by Multifunctional Theranostic Gold Nanorod-Loaded Microcapsules. Nanoscale 2015, 7 (19), 8884– 8897. Liu, J.; Detrembleur, C.; De Pauw-Gillet, M.-C.; Mornet, S.; Jérôme, C.; Duguet, E. Gold Nanorods Coated with Mesoporous Silica Shell as Drug Delivery System for Remote Near Infrared Light-Activated Release and Potential Phototherapy. Small 2015, 11 (19), 2323–2332. Pissuwan, D.; Niidome, T. Polyelectrolyte-Coated Gold Nanorods and Their Biomedical Applications. Nanoscale 2015, 7 (1), 59–65. Alkilany, A. M.; Murphy, C. J.; Thompson, L. B.; Boulos, S. P.; Sisco, P. N. Gold Nanorods: Their Potential for Photothermal Therapeutics and Drug Delivery, Tempered by the Complexity of Their Biological Interactions. Advanced Drug Delivery Reviews 2012, 64 (2), 190–199. Fratoddi, I.; Venditti, I.; Cametti, C.; Russo, M. V. Gold Nanoparticles and Gold Nanoparticle-Conjugates for Delivery of Therapeutic Molecules. Progress and Challenges. J. Mater. Chem. B 2014, 2 (27), 4204–4217. Abadeer, N. S.; Murphy, C. J. Recent Progress in Cancer Thermal Therapy Using Gold Nanoparticles. J. Phys. Chem. C 2016, 120 (9), 4691–4716. Kennedy, L. C.; Bickford, L. R.; Lewinski, N. A.; Coughlin, A. J.; Hu, Y.; Day, E. S.; West, J. L.; Drezek, R. A. A New Era for Cancer Treatment: Gold-NanoparticleMediated Thermal Therapies. Small 2010, 7 (2), 169–183. Lundén, H.; Liotta, A.; Chateau, D.; Lerouge, F.; Chaput, F.; Parola, S.; Brännlund, C.; Ghadyani, Z.; Kildemo, M.; Lindgren, M.; Lopes, C. Dispersion and SelfOrientation of Gold Nanoparticles in Sol–Gel Hybrid Silica – Optical Transmission Properties. J. Mater. Chem. C 2015, 3, 1026–1034. Xu, X.; Du, Q.; Peng, B.; Xiong, Q.; Hong, L.; Demir, H. V.; Wong, T. K. S.; Ko Kyaw, A. K.; Sun, X. W. Effect of Shell Thickness on Small-Molecule Solar Cells Enhanced by Dual Plasmonic Gold-Silica Nanorods. Appl. Phys. Lett. 2014, 105 (11), 113306. Mubeen, S.; Lee, J.; Lee, W.-R.; Singh, N.; Stucky, G. D.; Moskovits, M. On the Plasmonic Photovoltaic. ACS Nano 2014, 8 (6), 6066–6073. Wu, X.; Liu, L.; Deng, Z.; Nian, L.; Zhang, W.; Hu, D.; Xie, Z.; Mo, Y.; Ma, Y. Efficiency Improvement in Polymer Light-Emitting Diodes by “Far-Field” Effect of Gold Nanoparticles. Part. Part. Syst. Charact. 2015, 32, 686–692. Murphy, C. J.; Orendorff, C. J.; Baxter, S. C.; Goldsmith, E. C. Light Scattering From Gold Nanorods: Tracking Material Deformation. Nanotechnology 2005, 16 (11), 2601–2605. Stone, J. W.; Murphy, C. J.; Sisco, P. N.; Goldsmith, E. C.; Baxter, S. C. Using Gold Nanorods to Probe Cell-Induced Collagen Deformation. Nano Lett. 2007, 7 (1), 116– 119. Jing, C.; Rawson, F. J.; Zhou, H.; Shi, X.; Li, W.-H.; Li, D.-W.; Long, Y.-T. New ACS Paragon Plus Environment

Page 47 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(30) (31) (32) (33) (34) (35) (36) (37)

(38) (39)

(40) (41)

(42)

(43) (44) (45) (46) (47)

Langmuir

Insights Into Electrocatalysis Based on Plasmon Resonance for the Real-Time Monitoring of Catalytic Events on Single Gold Nanorods. Anal. Chem. 2014, 86 (11), 5513–5518. Pan, S. L.; Chen, M.; Li, H. L. Aqueous Gold Sols of Rod-Shaped Particles Prepared by the Template Method. Colloids Surf., A 2001, 180 (1-2), 55–62. Yu, Y.-Y.; Chang, S.-S.; Lee, C.-L.; Wang, C. R. C. Gold Nanorods: Electrochemical Synthesis and Optical Properties. J. Phys. Chem. B 1997, 101 (34), 6661–6664. Kundu, S.; Peng, L.; Liang, H. A New Route to Obtain High-Yield Multiple-Shaped Gold Nanoparticles in Aqueous Solution Using Microwave Irradiation. Inorg. Chem. 2008, 47 (14), 6344–6352. Grzelczak, M.; Pérez-Juste, J.; Mulvaney, P.; Liz-Marzán, L. M. Shape Control in Gold Nanoparticle Synthesis. Chem. Soc. Rev. 2008, 37 (9), 1783–1791. Tao, A. R.; Habas, S.; Yang, P. Shape Control of Colloidal Metal Nanocrystals. Small 2008, 4 (3), 310–325. Senthil Kumar, P.; Pastoriza-Santos, I.; Rodríguez-González, B.; Javier García de Abajo, F.; Liz-Marzán, L. M. High-Yield Synthesis and Optical Response of Gold Nanostars. Nanotechnology 2007, 19 (1), 015606. Murphy, C. J.; Sau, T. K. Seeded High Yield Synthesis of Short Au Nanorods in Aqueous Solution. Langmuir 2004, 20 (15), 6414–6420. Murphy, C. J.; Sau, T. K.; Gole, A. M.; Orendorff, C. J. Surfactant-Directed Synthesis and Optical Properties of One-Dimensional Plasmonic Metallic Nanostructures. MRS Bull. 2005, 30 (5), 349–355. Jana, N. R. Gram-Scale Synthesis of Soluble, Near-Monodisperse Gold Nanorods and Other Anisotropic Nanoparticles. Small 2005, 1 (8-9), 875–882. Ye, X.; Jin, L.; Caglayan, H.; Chen, J.; Xing, G.; Zheng, C.; Doan-Nguyen, V.; Kang, Y.; Engheta, N.; Kagan, C. R.; Murray, C. B. Improved Size-Tunable Synthesis of Monodisperse Gold Nanorods Through the Use of Aromatic Additives. ACS Nano 2012, 6 (3), 2804–2817. Scarabelli, L.; Grzelczak, M.; Liz-Marzán, L. M. Tuning Gold Nanorod Synthesis Through Prereduction with Salicylic Acid. Chem. Mater. 2013, 25 (21), 4232–4238. Hubert, F.; Testard, F.; Rizza, G.; Spalla, O. Nanorods Versus Nanospheres: a Bifurcation Mechanism Revealed by Principal Component TEM Analysis. Langmuir 2010, 26 (10), 6887–6891. Hubert, F.; Testard, F.; Spalla, O. Cetyltrimethylammonium Bromide Silver Bromide Complex as the Capping Agent of Gold Nanorods. Langmuir 2008, 24 (17), 9219– 9222. Wadams, R. C.; Fabris, L.; Vaia, R. A.; Park, K. Time-Dependent Susceptibility of the Growth of Gold Nanorods to the Addition of a Cosurfactant. Chem. Mater. 2013, 25 (23), 4772–4780. Koeppl, S.; Ghielmetti, N.; Caseri, W.; Spolenak, R. Seed-Mediated Synthesis of Gold Nanorods: Control of the Aspect Ratio by Variation of the Reducing Agent. J Nanopart Res 2013, 15 (3), 1471. Vigderman, L.; Zubarev, E. R. High-Yield Synthesis of Gold Nanorods with Longitudinal SPR Peak Greater Than 1200 Nm Using Hydroquinone as a Reducing Agent. Chem. Mater. 2013, 25 (8), 1450–1457. Su, G.; Yang, C.; Zhu, J.-J. Fabrication of Gold Nanorods with Tunable Longitudinal Surface Plasmon Resonance Peaks by Reductive Dopamine. Langmuir 2015, 31 (2), 817–823. Jana, N. R.; Peng, X. Single-Phase and Gram-Scale Routes Toward Nearly ACS Paragon Plus Environment

47 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(48)

(49)

(50)

(51) (52)

(53)

(54)

(55) (56)

(57)

(58) (59) (60) (61) (62) (63) 48 of 52

Page 48 of 53

Monodisperse Au and Other Noble Metal Nanocrystals. J. Am. Chem. Soc. 2003, 125 (47), 14280–14281. Lohse, S. E.; Murphy, C. J.; Eller, J. R.; Sivapalan, S. T.; Plews, M. R. A Simple Millifluidic Benchtop Reactor System for the High-Throughput Synthesis and Functionalization of Gold Nanoparticles with Different Sizes and Shapes. ACS Nano 2013, 7 (5), 4135–4150. Alvarez-Puebla, R. A.; Agarwal, A.; Manna, P.; Khanal, B. P.; Aldeanueva-Potel, P.; Carbo-Argibay, E.; Pazos-Perez, N.; Vigderman, L.; Zubarev, E. R.; Kotov, N. A.; LizMarzán, L. M. Gold Nanorods 3D-Supercrystals as Surface Enhanced Raman Scattering Spectroscopy Substrates for the Rapid Detection of Scrambled Prions. Proc. Natl. Acad. Sci. USA 2011, 108 (20), 8157–8161. Rice, K. P.; Saunders, A. E.; Stoykovich, M. P. Seed-Mediated Growth of ShapeControlled Wurtzite CdSe Nanocrystals: Platelets, Cubes, and Rods. J. Am. Chem. Soc. 2013, 135 (17), 6669–6676. Diroll, B. T.; Koschitzky, A.; Murray, C. B. Tunable Optical Anisotropy of Seeded CdSe/CdS Nanorods. J. Phys. Chem. Lett. 2014, 5 (1), 85–91. Xia, X.; Figueroa-Cosme, L.; Tao, J.; Peng, H.-C.; Niu, G.; Zhu, Y.; Xia, Y. Facile Synthesis of Iridium Nanocrystals with Well-Controlled Facets Using Seed-Mediated Growth. J. Am. Chem. Soc. 2014, 136 (31), 10878–10881. Weiner, R. G.; Skrabalak, S. E. Metal Dendrimers: Synthesis of Hierarchically Stellated Nanocrystals by Sequential Seed-Directed Overgrowth. Angew. Chem. Int. Ed. 2014, 54 (4), 1181–1184. Wang, Z.; Chen, Z.; Zhang, H.; Zhang, Z.; Wu, H.; Jin, M.; Wu, C.; Yang, D.; Yin, Y. Lattice-Mismatch-Induced Twinning for Seeded Growth of Anisotropic Nanostructures. ACS Nano 2015, 9 (3), 3307–3313. Peng, H.-C.; Park, J.; Zhang, L.; Xia, Y. Toward a Quantitative Understanding of Symmetry Reduction Involved in the Seed-Mediated Growth of Pd Nanocrystals. J. Am. Chem. Soc. 2015, 137 (20), 6643–6652. DeSantis, C. J.; Sue, A. C.; Bower, M. M.; Skrabalak, S. E. Seed-Mediated CoReduction: a Versatile Route to Architecturally Controlled Bimetallic Nanostructures. ACS Nano 2012, 6 (3), 2617–2628. Weiner, R. G.; Smith, A. F.; Skrabalak, S. E. Synthesis of Hollow and Trimetallic Nanostructures by Seed-Mediated Co-Reduction. Chem. Commun. 2015, 51, 8872– 8875. Edgar, J. A.; McDonagh, A. M.; Cortie, M. B. Formation of Gold Nanorods by a Stochastic “Popcorn” Mechanism. ACS Nano 2012, 6 (2), 1116–1125. Orendorff, C. J.; Murphy, C. J. Quantitation of Metal Content in the Silver-Assisted Growth of Gold Nanorods. J. Phys. Chem. B 2006, 110 (9), 3990–3994. Zhang, L.; Xia, K.; Lu, Z.; Li, G.; Chen, J.; Deng, Y.; Li, S.; Zhou, F.; He, N. Efficient and Facile Synthesis of Gold Nanorods with Finely Tunable Plasmonic Peaks From Visible to Near-IR Range. Chem. Mater. 2014, 26 (5), 1794–1798. Ali, M. R. K.; Snyder, B.; El-Sayed, M. A. Synthesis and Optical Properties of Small Au Nanorods Using a Seedless Growth Technique. Langmuir 2012, 28 (25), 9807– 9815. Jia, H.; Fang, C.; Zhu, X.-M.; Ruan, Q.; Wang, Y.-X. J.; Wang, J. Synthesis of Absorption-Dominant Small Gold Nanorods and Their Plasmonic Properties. Langmuir 2015, 31 (26), 7418–7426. Box, G. E. P.; Hunter, J. S.; Hunter, W. G. Statistics for Experimenters, 2nd ed.; John Wiley & Sons Inc.: Hoboken NJ, 2005. ACS Paragon Plus Environment

Page 49 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(64)

(65)

(66)

(67) (68) (69)

(70)

(71) (72) (73)

(74) (75)

(76) (77) (78)

Langmuir

Wang, L.; Kariuki, N. N.; Schadt, M.; Mott, D.; Luo, J.; Zhong, C.-J.; Shi, X.; Zhang, C.; Hao, W.; Lu, S.; Kim, N.; Wang, J.-Q. Sensing Arrays Constructed From Nanoparticle Thin Films and Interdigitated Microelectrodes. Sensors 2006, 6 (6), 667– 679. Ghoreishi, S. M.; Behpour, M.; Khoobi, A. Central Composite Rotatable Design in the Development of a New Method for Optimization, Voltammetric Determination and Electrochemical Behavior of Betaxolol in the Presence of Acetaminophen Based on a Gold Nanoparticle Modified Electrode. Anal. Methods 2012, 4, 2475–2485. Mabbott, S.; Correa, E.; Cowcher, D. P.; Allwood, J. W.; Goodacre, R. Optimization of Parameters for the Quantitative Surface-Enhanced Raman Scattering Detection of Mephedrone Using a Fractional Factorial Design and a Portable Raman Spectrometer. Anal. Chem. 2013, 85 (2), 923–931. Beck, R. C. R.; Haas, S. E.; Guterres, S. S.; Ré, M. I.; Benvenutti, E. V.; Pohlmann, A. R. Nanoparticle-Coated Organic-Inorganic Microparticles: Experimental Design and Gastrointestinal Tolerance Evaluation. Quím. Nova 2006, 29 (5), 990–996. Bothiraja, C.; Pawar, A. P.; Shaikh, K. S.; Sher, P. Eudragit® EPO Based Nanoparticle Suspension of Andrographolide: In Vitro And In Vivo. Nanosci. Nanotechnol. Lett. 2009, 1 (3), 156–164. Beirowski, J.; Inghelbrecht, S.; Arien, A.; Gieseler, H. Freeze-Drying of Nanosuspensions, 1: Freezing Rate Versus Formulation Design as Critical Factors to Preserve the Original Particle Size Distribution. J. Pharm. Sci. 2010, 100 (5), 1958– 1968. Beck-Broichsitter, M.; Schmehl, T.; Gessler, T.; Seeger, W.; Kissel, T. Development of a Biodegradable Nanoparticle Platform for Sildenafil: Formulation Optimization by Factorial Design Analysis Combined with Application of Charge-Modified Branched Polyesters. J. Control. Release 2012, 157 (3), 469–477. Bhavsar, M. D.; Tiwari, S. B.; Amiji, M. M. Formulation Optimization for the Nanoparticles-in-Microsphere Hybrid Oral Delivery System Using Factorial Design. J. Control. Release 2006, 110 (2), 422–430. Yong, V.; Hahn, H. T. Dispersant Optimization Using Design of Experiments for SiC/Vinyl Ester Nanocomposites. Nanotechnology 2005, 16 (4), 354–360. Ahmed, E. S.; Fouad, O. A.; El-Midany, A. A.; El-Sabbagh, E. A.; Abd El-Rahman, A.; Ibrahim, I. A. Silver Nanostructures via Cementation on Copper: a Comparison Between Experimental Data and Statistical Design Model. Surf. Interface Anal. 2010, 42 (6-7), 730–734. Rondinone, A. J.; Samia, A. C. S.; Zhang, Z. J. A Chemometric Approach for Predicting the Size of Magnetic Spinel Ferrite Nanoparticles From the Synthesis Conditions. J. Phys. Chem. B 2000, 104 (33), 7919–7922. Jia, W.; Douglas, E. P. Characterization and Size Control of Cadmium Sulfide/Cadmium Disulfide Nanoparticles Within Random Ionomer Solutions. J. Mater. Chem. 2004, 14 (4), 744–748. Davies, G.-L.; Barry, A.; Gun’ko, Y. K. Preparation and Size Optimisation of Silica Nanoparticles Using Statistical Analyses. Chem. Phys. Lett. 2009, 468 (4-6), 239–244. Edrissi, M.; Hosseinabadi, H. A. Sythhesis of Coral-Like and Spherical Nanoparticles of Barium Titanate Using Factorial and Taguchi Experimental Design. Mat.-wiss. u. Werkstofftech. 2010, 41 (3), 154–160. Casanova, H.; Higuita, L. P. Synthesis of Calcium Carbonate Nanoparticles by Reactive Precipitation Using a High Pressure Jet Homogenizer. Chem. Eng. J. 2011, 175, 569–578. ACS Paragon Plus Environment

49 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(79) (80) (81) (82) (83) (84) (85) (86) (87) (88) (89)

(90) (91)

(92) (93) (94) (95) (96) (97) 50 of 52

Page 50 of 53

Hendel, T.; Wuithschick, M.; Kettemann, F.; Birnbaum, A.; Rademann, K.; Polte, J. In Situ Determination of Colloidal Gold Concentrations with UV-Vis Spectroscopy: Limitations and Perspectives. Anal. Chem. 2014, 86 (22), 11115–11124. Park, K.; Koerner, H.; Vaia, R. A. Depletion-Induced Shape and Size Selection of Gold Nanoparticles. Nano Lett. 2010, 10 (4), 1433–1439. Thai, T.; Zheng, Y.; Ng, S. H.; OHSHIMA, H.; Altissimo, M.; Bach, U. Facile Gold Nanorod Purification by Fractionated Precipitation. Nanoscale 2014, 6 (12), 6515– 6520. Ahmad, I.; Zandvliet, H. J. W.; Kooij, E. S. Shape-Induced Separation of Nanospheres and Aligned Nanorods. Langmuir 2014, 30 (27), 7953–7961. Akbulut, O.; Mace, C. R.; Martinez, R. V.; Kumar, A. A.; Nie, Z.; Patton, M. R.; Whitesides, G. M. Separation of Nanoparticles in Aqueous Multiphase Systems Through Centrifugation. Nano Lett. 2012, 12 (8), 4060–4064. Hao, M.; Liu, C.; Peng, L.; Li, J.; Lu, W.; Jiang, L. Shape Separation of Gold Nanoparticles Using a pH-Responsive Amphiphilic Dendrimer According to Their Shape Anisotropy Distinction. J. Colloid Interface Sci. 2015, 437 (C), 311–315. Garg, N.; Scholl, C.; Mohanty, A.; Jin, R. The Role of Bromide Ions in Seeding Growth of Au Nanorods. Langmuir 2010, 26 (12), 10271–10276. Mie, G. Beiträge Zur Optik Trüber Medien, Speziell Kolloidaler Metallösungen. Ann. Physik 1908, 330 (3), 377–445. Gans, R. Über Die Form Ultramikroskopischer Silberteilchen. Ann. Physik 1915, 352 (10), 270–284. Papavassiliou, G. C. Optical-Properties of Small Inorganic and Organic Metal Particles. Progress in Solid State Chemistry 1979, 12 (3-4), 185–271. Placido, T.; Comparelli, R.; Giannici, F.; Cozzoli, P. D.; Capitani, G.; Striccoli, M.; Agostiano, A.; Curri, M. L. Photochemical Synthesis of Water-Soluble Gold Nanorods: the Role of Silver in Assisting Anisotropic Growth. Chem. Mater. 2009, 21 (18), 4192– 4202. Rani N Gupta, S. Development of Calibration and Standard Addition Polarographic Determination of Ascorbic Acid. IJCEA 2015, 6 (2), 86–90. Schmittel, M.; Lal, M.; Lal, R.; ROck, M.; Langels, A.; Rappoport, Z.; Basheer, A.; Schlirf, J.; Deiseroth, H.-J.; FlOrke, U.; Gescheidt, G. A Comprehensive Picture of the One-Electron Oxidation Chemistry of Enols, Enolates and Α-Carbonyl Radicals: Oxidation Potentials and Characterization of Radical Intermediates. Tetrahedron 2009, 65 (52), 10842–10855. Gou, L.; Murphy, C. J. Fine-Tuning the Shape of Gold Nanorods. Chem. Mater. 2005, 17 (14), 3668–3672. Liu, M.; Guyot-Sionnest, P. Mechanism of Silver(I)-Assisted Growth of Gold Nanorods and Bipyramids. J. Phys. Chem. B 2005, 109 (47), 22192–22200. Wang, Z. L.; Mohamed, M. B.; Link, S.; El-Sayed, M. A. Crystallographic Facets and Shapes of Gold Nanorods of Different Aspect Ratios. Surface Science 1999, 440 (12), L809–L814. Goris, B.; Bals, S.; Van den Broek, W.; Carbó-Argibay, E.; Gómez-Graña, S.; LizMarzán, L. M.; Van Tendeloo, G. Atomic-Scale Determination of Surface Facets in Gold Nanorods. Nature Materials 2012, 11 (11), 930–935. Pileni, M.-P. The Role of Soft Colloidal Templates in Controlling the Size and Shape of Inorganic Nanocrystals. Nature Materials 2003, 2 (3), 145–150. Pérez-Juste, J.; Liz-Marzán, L. M.; Carnie, S. L.; Chan, D. Y. C.; Mulvaney, P. Electric-Field-Directed Growth of Gold Nanorods in Aqueous Surfactant Solutions. ACS Paragon Plus Environment

Page 51 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(98)

(99) (100) (101) (102) (103)

(104)

(105) (106)

(107) (108)

(109) (110) (111) (112) (113) (114) (115) (116)

Langmuir

Adv. Funct. Mater. 2004, 14 (6), 571–579. Grzelczak, M.; Sánchez-Iglesias, A.; Rodríguez-González, B.; Alvarez-Puebla, R.; Pérez-Juste, J.; Liz-Marzán, L. M. Influence of Iodide Ions on the Growth of Gold Nanorods: Tuning Tip Curvature and Surface Plasmon Resonance. Adv. Funct. Mater. 2008, 18 (23), 3780–3786. Personick, M. L.; Langille, M. R.; Zhang, J.; Mirkin, C. A. Shape Control of Gold Nanoparticles by Silver Underpotential Deposition. Nano Lett. 2011, 11 (8), 3394– 3398. Ye, X.; Gao, Y.; Chen, J.; Reifsnyder, D. C.; Zheng, C.; Murray, C. B. Seeded Growth of Monodisperse Gold Nanorods Using Bromide-Free Surfactant Mixtures. Nano Lett. 2013, 13 (5), 2163–2171. Liao, H. W.; Hafner, J. H. Gold Nanorod Bioconjugates. Chem. Mater. 2005, 17 (18), 4636–4641. Liu, X.-H.; Luo, X.-H.; Lu, S.-X.; Zhang, J.-C.; Cao, W.-L. A Novel Cetyltrimethyl Ammonium Silver Bromide Complex and Silver Bromide Nanoparticles Obtained by the Surfactant Counterion. J. Colloid Interface Sci. 2007, 307 (1), 94–100. Niidome, Y.; Nakamura, Y.; Honda, K.; Akiyama, Y.; Nishioka, K.; Kawasaki, H.; Nakashima, N. Characterization of Silver Ions Adsorbed on Gold Nanorods: Surface Analysis by Using Surface-Assisted Laser Desorption/Ionization Time-of-Flight Mass Spectrometry. Chem. Commun. 2009, 1754–1756. Jackson, S. R.; McBride, J. R.; Rosenthal, S. J.; Wright, D. W. Where’s the Silver? Imaging Trace Silver Coverage on the Surface of Gold Nanorods. J. Am. Chem. Soc. 2014, 136 (14), 5261–5263. Ekwall, P.; Mandell, L.; Solyom, P. The Aqueous Cetyl Trimethylammonium Bromide Solutions. J. Colloid Interface Sci. 1971, 35 (4), 519–528. Vivek, J. P.; Burgess, I. J. Quaternary Ammonium Bromide Surfactant Adsorption on Low-Index Surfaces of Gold. 2. Au(100) and the Role of Crystallographic-Dependent Adsorption in the Formation of Anisotropic Nanoparticles. Langmuir 2012, 28 (11), 5040–5047. Vivek, J. P.; Burgess, I. J. Quaternary Ammonium Bromide Surfactant Adsorption on Low-Index Surfaces of Gold. 1. Au(111). Langmuir 2012, 28 (11), 5031–5039. Lohse, S. E.; Burrows, N. D.; Scarabelli, L.; Liz-Marzán, L. M.; Murphy, C. J. Anisotropic Noble Metal Nanocrystal Growth: the Role of Halides. Chem. Mater. 2014, 26 (1), 34–43. Ye, X.; Zheng, C.; Chen, J.; Gao, Y.; Murray, C. B. Using Binary Surfactant Mixtures to Simultaneously Improve the Dimensional Tunability and Monodispersity in the Seeded Growth of Gold Nanorods. Nano Lett. 2013, 13 (2), 765–771. Scarabelli, L.; Sánchez-Iglesias, A.; Pérez-Juste, J.; Liz-Marzán, L. M. A “Tips and Tricks” Practical Guide to the Synthesis of Gold Nanorods. J. Phys. Chem. Lett. 2015, 6 (21), 4270–4279. Rasband, W. S. ImageJ. 1st ed. U.S. National Institutes of Health: Bethesda, Maryland 1997. Abramoff, M. D.; Magalhaes, P. J.; Ram, S. J. Image Processing with ImageJ. Biophotonics International 2004, 11 (7), 36–42. Collins, T. ImageJ for Microscopy. Biotech. 2007, 43 (S1), S25–S30. Schneider, C. A.; Rasband, W. S.; Eliceiri, K. W. NIH Image to ImageJ: 25 Years of Image Analysis. Nat Meth 2012, 9 (7), 671–675. Wolfram Research, Inc. Mathematica. 10 ed. Wolfram Research, Inc.: Champaign, IL. Gatz, D. F.; Smith, L. The Standard Error of a Weighted Mean Concentration .1. ACS Paragon Plus Environment

51 of 52

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(117) (118) (119) (120) (121) (122) (123)

52 of 52

Page 52 of 53

Bootstrapping vs Other Methods. Atmospheric Environment 1995, 29 (11), 1185– 1193. Efron, B. Bootstrap Methods: Another Look at the Jackknife. The Annals of Statistics 1979, 7 (1), 1–26. Box, G. E. P.; Meyer, R. D. Finding the Active Factors in Fractionated Screening Experiments. Journal of Quality Technology 1993, 25 (2), 94–105. Box, G. E. P.; Meyer, R. D. An Analysis for Unreplicated Fractional Factorials. Technometrics 1986, 28 (1), 11–18. Lenth, R. V. Response-Surface Methods in R, Using Rsm. J. Stat. Softw. 2009, 32 (7), 1–17. Barrios, E. BsMD: Bayes Screening and Model Discrimination. 2013 ed. R Foundation for Statistical Computing: Vienna, Austria 2013. R Core Team. R: a Language and Environment for Statistical Computing. 3rd ed. R Foundation for Statistical Computing: Vienna, Austria. http://www.R-project.org/ October 31, 2014. Crawley, M. J. The R Book; John Wiley & Sons: Chichester, UK, 2012.

ACS Paragon Plus Environment

Page 53 of 53

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48

Langmuir

ACS Paragon Plus Environment