Vanadium as a potential membrane material for ... - ACS Publications

Toney,ǁ Jennifer Wilcox*,†,‡. 4. †Department of ... Park, California 94025, United States. 11 ...... (6) Wilcox, J. Nitrogen-permeable membrane...
0 downloads 0 Views 677KB Size
Subscriber access provided by UNIVERSITY OF ADELAIDE LIBRARIES

Article

Vanadium as a potential membrane material for carbon capture: Effects of minor flue gas species Mengyao Yuan, Simona Liguori, Kyoungjin Lee, Douglas G. Van Campen, Michael F. Toney, and Jennifer Wilcox Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.7b02974 • Publication Date (Web): 14 Sep 2017 Downloaded from http://pubs.acs.org on September 18, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 30

Environmental Science & Technology

1

Vanadium as a potential membrane material for

2

carbon capture: Effects of minor flue gas species

3

Mengyao Yuan,† Simona Liguori,†,‡ Kyoungjin Lee,†,§ Douglas G. Van Campen,ǁ Michael F.

4

Toney,ǁ Jennifer Wilcox*,†,‡

5

†Department of Energy Resources Engineering, Stanford University, 367 Panama Street,

6

Stanford, California 94305, United States

7

‡Department of Chemical and Biological Engineering, Colorado School of Mines, 1613 Illinois

8

Street, Golden, Colorado 80401, United States

9

§Applied Materials, 974 E. Arques Avenue, Sunnyvale, California 94085, United States

10

ǁStanford Synchrotron Radiation Lightsource, SLAC National Accelerator Laboratory, Menlo

11

Park, California 94025, United States

ACS Paragon Plus Environment

1

Environmental Science & Technology

12

Page 2 of 30

ABSTRACT

13 14

Vanadium and its surface oxides were studied as a potential nitrogen-selective membrane

15

material for indirect carbon capture from coal or natural gas power plants. The effects of minor

16

flue gas components (SO2, NO, NO2, H2O, and O2) on vanadium at 500–600 °C were

17

investigated by thermochemical exposure in combination with x-ray photoelectron spectroscopy

18

(XPS), scanning electron microscopy (SEM), and in situ x-ray diffraction (XRD). The results

19

showed that SO2, NO, and NO2 are unlikely to have adsorbed on the surface vanadium oxides at

20

600 °C after exposure for up to 10 hours, although NO and NO2 may have exhibited oxidizing

21

effects (e.g., exposure to 250 ppmv NO/N2 resulted in an 2.4 times increase in surface V2O5

22

compared to exposure to just N2). We hypothesize that decomposition of surface vanadium

23

oxides and diffusion of surface oxygen into the metal bulk are both important mechanisms

24

affecting the composition and morphology of the vanadium membrane. The results and

25

hypothesis suggest that the carbon capture performance of the vanadium membrane can

26

potentially be strengthened by material and process improvements such as alloying, operating

27

temperature reduction, and flue gas treatment.

28 29

1. Introduction

ACS Paragon Plus Environment

2

Page 3 of 30

Environmental Science & Technology

30

Vanadium and vanadium oxides are widely studied for a suite of environmental and energy

31

applications, e.g., selective catalytic reaction (SCR) catalysts, electrodes for lithium-ion batteries,

32

hydrogen storage, and fusion systems.1-3 In recent years, vanadium has been investigated as a

33

potential membrane material for carbon capture,4-8 the process of separating carbon dioxide

34

(CO2) from the flue gas of fossil fuel power generation as a climate change mitigation method. It

35

is therefore important to understand the effects of flue gas pollutants and minor components on

36

vanadium at realistic power plant operating conditions. In this paper, we aim to investigate the

37

effects of selected flue gas species, including sulfur dioxide (SO2), nitric oxide (NO), nitrogen

38

dioxide (NO2), water vapor (H2O), and oxygen (O2) on vanadium and its surface oxides using x-

39

ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), and in situ x-ray

40

diffraction (XRD).

41

Membrane separation is considered a competitive separation technology along with solvent-

42

based absorption and physical adsorption. Recent modeling studies have shown that membrane

43

separation can achieve comparable or lower energy consumption than amine absorption,9 one of

44

the more mature technologies proposed for carbon capture. In addition, membrane separation has

45

unique advantages such as ease of scale-up, smaller footprints, and requiring little chemicals in

46

the separation process.10-11 Currently, the most-studied carbon capture membranes are polymeric

47

membranes that selectively separate CO2 from flue gas (known as “CO2-selective” membranes).

48

Recently, there has been an emerging research interest in the development of nitrogen-selective

49

membranes, which is primarily motivated by their potential for reducing the energy use of CO2

50

separation.7 In a typical flue gas from coal or natural gas combustion, nitrogen (N2) is the

51

dominant species, with concentrations above 70 vol%. The high N2 concentration in flue gas is

52

able to provide a higher driving force for separation (i.e., higher partial pressure difference

ACS Paragon Plus Environment

3

Environmental Science & Technology

Page 4 of 30

53

across the membrane), whereas the low CO2 concentration (as low as 3–5 vol% from a natural

54

gas power plant12) can pose design limitations to CO2-selective membranes. For example, it has

55

been shown a CO2-selective membrane with experimentally achievable material properties

56

cannot simultaneously achieve 90% capture and 95% CO2 purity, a common separation target for

57

carbon capture, within single-stage separation for an inlet CO2 concentration typical of a coal-

58

fired flue gas (e.g., 10–12 vol% CO2).13-14 Unlike in CO2-selective membranes, concentrated

59

CO2 product stream exits on the high-pressure side of a nitrogen-selective membrane, which

60

could reduce the energy use for compression to high pressures (e.g., 110 bar12) for long-term

61

geologic storage.

62

A few studies on polymer-based nitrogen-selective membranes can be found in the

63

literature.15-19 While these membranes have successfully demonstrated N2 selectivity over CO2,

64

the reported N2/CO2 selectivities are often fairly low, e.g., below 20, despite a few outliners. In

65

contrast, the focus of this study is a vanadium membrane that falls under the category of metallic

66

nitrogen-selective membranes. Unlike its polymeric counterparts, the vanadium membrane

67

provides nitrogen selectivity via a solution-diffusion mechanism similar to that found in

68

palladium-based membranes for hydrogen separation. The key steps in this mechanism include

69

catalytic dissociation of N2 into nitrogen atoms on the membrane surface and diffusion of

70

nitrogen atoms across the membrane bulk.5 The solution-diffusion mechanism has been validated

71

for vanadium by experiments as well as density functional theory (DFT) calculations4-5 and

72

enables the membrane to have N2/CO2 selectivities orders-of-magnitude higher than those

73

typically found in polymer-based membranes, and ongoing effort is dedicated to improving the

74

N2 permeability of the membrane (e.g., currently, at 400 °C and a pressure difference of 2–5 bar,

75

N2 fluxes on the order of 0.03–0.05 mol/m2-h have been measured4, 8) for large-scale

ACS Paragon Plus Environment

4

Page 5 of 30

Environmental Science & Technology

76

applications. A recent process modeling and optimization study has shown that the metallic

77

nitrogen-selective membrane concept based on vanadium has the potential of achieving energy

78

consumption comparable to CO2-selective membranes while reducing process design

79

complexities.7

80

One common uncertainty in the application of membrane technologies for carbon capture is

81

the effects of minor flue gas species on the membrane materials, yet this topic is little explored

82

even for polymeric membranes.20 This paper represents the first attempt to the authors’

83

knowledge that investigates the effects of SO2, NO, NO2, H2O, and O2 on vanadium as a

84

candidate membrane material for carbon capture. Specifically, we focused on typical conditions

85

found at the exit of the economizer and prior to the emissions controls in a coal-fired power

86

plant, where the flue gas temperature is 370–650 °C,21 and the pollutant concentrations are

87

higher than those found at the stack (see SI Section S1). Previous experimental studies have

88

shown that a suitable operating temperature range for the vanadium nitrogen-selective membrane

89

is 400–800 °C.4, 8 A potential location for installing the vanadium membrane, therefore, is at the

90

exit of the economizer in a coal-fired power plant, where the high-temperature flue gas can be

91

fed to the membrane with minimal heating.

92

In this work, we performed thermochemical exposure experiments for vanadium foils using

93

various gas mixtures and studied the chemical and morphological changes on the vanadium

94

oxide surface using XPS and SEM. Surface studies were the focus of this work because they can

95

reveal the first signs of potential chemical reactions or gas permeation and are indicative of bulk

96

changes. In addition, we will briefly discuss a set of in situ transmission XRD experiments aimed

97

at investigating potential phase changes in the bulk of vanadium during thermochemical

98

exposure. While the purpose of this work is to facilitate the understanding of the chemical

ACS Paragon Plus Environment

5

Environmental Science & Technology

Page 6 of 30

99

resistance and potential failure mechanism of vanadium in an actual flue gas environment, the

100

methodology and results presented here have broader implications in other environmental and

101

energy applications where vanadium and vanadium oxides play a key role.

102 103

2. Experimental

104

The experiments in this work can be divided into two parts. The first part consists of

105

thermochemical exposure tests and ex situ XPS and SEM characterization. The second part is a

106

series of in situ XRD measurements performed during gas exposure. The materials and

107

experimental procedures are briefly described below.

108

Materials. Commercial vanadium foils (Goodfellow Cambridge Limited, cold-rolled, 99.8%

109

purity, 0.040 mm thickness) were used in all of the tests. These foils were cut into small pieces

110

for gas exposure and characterization (approximately 25 mm2 for ex situ analyses and 85 mm2

111

for in situ XRD measurements). Test gases were single gases or gas mixtures prepared from

112

argon (Ar, 99.999%), N2 (99.998%), helium (He, 99.999%), SO2 (4.97 vol%, N2 balance), NO

113

(1.97 vol%, N2 balance), NO2 (1018 ppmv, N2 balance), H2O (10 vol%, N2 balance), and O2 (10

114

vol%, He balance). To simulate the flue gas concentrations in a coal-fired power plant, the

115

following gas mixtures were tested: 2500 ppmv SO2/N2, 250 ppmv NO/N2, 50 ppmv NO2/N2, 10

116

vol% H2O/N2, and 5 vol% O2/He. These gas concentrations were chosen based on the data in the

117

Integrated Environmental Control Model (IECM) software program.22 The chosen gas

118

concentrations are comparable to or higher than the gas concentrations exiting the economizer in

119

a pulverized coal plant for typical coal types found in IECM (see SI Table S1).

ACS Paragon Plus Environment

6

Page 7 of 30

Environmental Science & Technology

120

Thermochemical exposure experiments. Each vanadium sample was supported by quartz

121

wool in a glass tube reactor, and the reactor was connected to continuous gas flow by Teflon

122

fittings. The tube reactor was placed in a tube furnace (Carbolite) with a heating zone of

123

approximately 30 cm. The total gas flow rate in all exposure tests was set to 120 ml/min by mass

124

flow controllers. The test temperature was chosen to be 600 °C to represent the flue gas

125

temperature exiting the economizer. Each sample was heated in Ar from room temperature

126

(approximately 20 °C) to 600 °C at 3 °C/min. The temperature was then held constant at 600 °C

127

for 5 or 10 hours, during which the sample was exposed to a gas mixture containing one of the

128

minor flue gas species. At the end of the exposure, the reactor was quenched to room

129

temperature at 2 °C/min while Ar was used to purge the system. In both the 5-hour and 10-hour

130

exposure experiments, SO2/N2, NO/N2, and NO2/N2 were tested. In addition, N2 was tested in

131

both 5-hour and 10-hour experiments to rule out possible effects of the balance gas, and H2O/N2

132

was tested in 5-hour experiments. The samples are referred to in the following sections by the

133

gas used in the test and exposure duration, e.g., “N2-5h” refers to the sample exposed to N2 for 5

134

hours, and “NO-10h” refers to the sample exposed to NO/N2 for 10 hours.

135

Ex situ XPS and SEM characterization. All XPS analyses were performed on a PHI 5000

136

Versaprobe using a monochromatic Al Kα radiation source (1486.6 eV). The x-ray beam was

137

200 µm in diameter with a beam power of 49.9 W and an operating potential of 16 kV. A

138

vacuum of ~6 × 10−8 Pa was maintained in the main chamber. The angle between the analyzer

139

and sample surface was 45°. Survey scans were recorded over a binding energy (BE) range of 0–

140

600 eV using a pass energy of 117.4 eV. Region scans were recorded for V 2p, C 1s, O 1s, N 1s,

141

and S 2p with a pass energy of 23.5 eV. All photoemission spectra were referenced to C 1s =

142

284.8 eV. The spectra were fitted using CasaXPS 2.3.17 assuming Gaussian-Lorentzian

ACS Paragon Plus Environment

7

Environmental Science & Technology

Page 8 of 30

143

lineshapes and a Shirley background. High-resolution SEM images were obtained using an FEI

144

XL30 Sirion SEM with a beam intensity of 5 keV and a spot size of 3.

145

Exposure and in situ XRD experiments. Thermochemical exposure experiments and in situ

146

transmission XRD measurements were performed on Beamline 10-2 (BL10-2) at the Stanford

147

Synchrotron Radiation Lightsource (SSRL). Gas exposure was conducted using a hermetic

148

annealing chamber (see SI Section S2). The energy of the incident x-ray beam was 20 keV. The

149

scattering intensity was detected by a two-dimensional image detector (Dectris Pilatus 300W)

150

with a pixel size of 172 µm (1475 × 195 pixels). This combination of beam energy and detector

151

gave a detectable q-space of up to 10 Å−1, or 10 lines for vanadium. SO2/N2, NO/N2, NO2/N2,

152

H2O/N2, O2/He as well as N2 and He were tested. The total gas flow rate was 120 ml/min in all of

153

the exposure tests. Several experimental conditions were different from those in the exposure

154

experiments with ex situ characterization due to the setup at the beamline. A gas exposure

155

temperature of 500 °C was used, which was set by the annealing chamber material but is still

156

within the temperature range at the economizer exit. Each sample was heated from room

157

temperature to 500 °C at 5 °C/min, during which the respective gas or gas mixture for testing

158

was supplied to the chamber as purge gas. The temperature was held at 500 °C for 4 hours for

159

each gas or gas mixture with the exception of O2/He, which was tested for 3.5 hours due to the

160

availability of the beamline equipment. Cooling was not programmed. Transmission XRD data

161

were collected with an exposure time (time during which the sample was exposed to x-ray) of 2

162

seconds every 2 minutes during temperature ramp-up and every 5 minutes while the temperature

163

was stabilized at 500 °C.

164

ACS Paragon Plus Environment

8

Page 9 of 30

Environmental Science & Technology

165

3. Results and Discussion

166

Since the results from the 5-hour and 10-hour exposure tests share many similarities, the

167

discussion in this section will be focused on the latter, and the differences between the two sets

168

of data will be highlighted. The results from the 5-hour exposure tests are shown in the

169

Supporting Information (SI Section S4).

170

Ex situ XPS characterization: Survey scans. Surface elemental compositions of the

171

vanadium samples before and after gas exposure were determined by XPS survey scans. It was

172

found that all of the as-received vanadium foils analyzed (see SI Table S2) had consistent surface

173

compositions with the following average (± standard deviation) atomic percentages: 10.0 ± 1.7%

174

vanadium, 35.5 ± 3.4% oxygen, 49.6 ± 5.2% carbon, 2.7 ± 0.9% nitrogen, and 2.1 ± 0.7%

175

calcium. In addition to the expected V and O, the as-received foil surfaces all contained about

176

50% carbon and small amounts of nitrogen and calcium. As will be shown by XPS region scans,

177

the surface vanadium on the as-received foils mostly existed as V2O5. Since direct studies on the

178

interactions of vanadium foils with similar gases are rare in the literature, studies of V2O5

179

catalysts will be used to compare with the results obtained from our experiments.

180

Surface elemental compositions of the samples after 10-hour gas exposure are shown in

181

Table 1. The surface composition of the as-received foil used for this set of experiments is also

182

shown. Atomic concentrations below 0.5% are shown in brackets and are considered negligible.

183 184

Table 1. Surface elemental compositions of the vanadium samples from the 10-hour exposure

185

experiments.

ACS Paragon Plus Environment

9

Environmental Science & Technology

O 1s

V 2p3/2

C 1s

Page 10 of 30

N 1s

Ca 2p

Si 2p

9.0%

34.5%

52.0%

1.5%

3.2%

-

N2

23.5%

58.9%

17.6%

-

[0.4%]

-

2500 ppmv SO2

22.0%

59.3%

16.9%

-

-

1.8%

250 ppmv NO

25.2%

59.9%

14.9%

[0.4%]

-

-

50 ppmv NO2

22.1%

59.0%

18.9%

[0.2%]

-

-

as-received (Foil #4)

186 187

10-hour gas exposure removed about 60–70% carbon and almost all nitrogen originally

188

present on the vanadium foil. C 1s region scans (see SI Figure S6) show that the carbon

189

contamination is from both inorganic (e.g., deposition from air) and organic (e.g., solvent used in

190

foil manufacturing) sources, and that most of the organic carbon species has been removed by

191

gas exposure. The small amount of silicon content found on the SO2-10h sample is most likely

192

from the quartz wool support used in the exposure test.

193

The nitrogen content on the NO-10h and NO2-10h samples is negligible, while small

194

amounts of nitrogen were found on the NO-5h and NO2-5h samples (see SI Table S3). Based on

195

literature evidence, the most probable explanation is that native nitrogen species on the as-

196

received foils were not fully desorbed or decomposed during the 5-hour tests, and NO or NO2

197

did not adsorb on the vanadium surface. Barbaray et al. studied NO2 adsorption on V2O5 at 10−2

ACS Paragon Plus Environment

10

Page 11 of 30

Environmental Science & Technology

198

Torr (1.3 Pa) and 25–450 °C and found that the adsorbed NO2 had an XPS N 1s BE close to

199

406.5 eV (reference: C 1s = 285 eV), and that the N 1s signal decreased with temperature and

200

disappeared above 250 °C.23 In contrast, the N 1s peaks of the NO-5h and NO2-5h samples from

201

our experiments are in the range of 400–402 eV (shown in SI Figure S4), and the exposure

202

temperature was much higher than 250 °C, so the detected nitrogen is unlikely to be associated

203

with NO or NO2. Several groups studied V2O5 or V2O5/TiO2 for SCR reactions and concluded

204

that NO did not strongly adsorb on the catalyst surface at the temperature investigated, i.e., 150–

205

400 °C.24-27 Yu et al. exposed V2O5-WO3/TiO2 to 2% NO/N2 at 350 °C and concluded that the

206

adsorption of NO on the catalyst was unstable at high temperatures.28 Inomata et al. found that

207

instead of adsorbing onto the catalyst, gaseous NO reacted with strongly adsorbed NH3 during

208

NO reduction, and this has been confirmed by Gruber and Hermann using cluster models and

209

DFT calculations.25, 29 Guo et al. performed NO adsorption on V2O5/TiO2 at room temperature

210

and concluded that nitrates only formed on titania.30

211

No sulfur species was detected by XPS on the samples exposed to SO2/N2, suggesting that

212

SO2 did not physically or chemically adsorb onto the surface vanadium oxides. This observation

213

can be corroborated by previous studies. Barbaray et al. studied SO2 adsorption on V2O5 powder

214

at 25–400 °C and 0.01 Torr (1.3 Pa) using XPS and found that chemisorption of SO2 onto V2O5

215

did not occur below 150 °C, and that the intensity of the S 2p line for the adsorbed SO2 peaked at

216

300 °C and decreased afterwards.31 Le Bars and Auroux studied SO2 adsorption on V2O5-based

217

catalysts at 353 K (80 °C) and found that SO2 did not adsorb on bulk V2O5 or V2O5/SiO2 and was

218

instead selective for uncovered alumina on V2O5/γ-Al2O3.32 They also concluded that the surface

219

of V2O5 shows a weakly acidic character.32 Guo et al. exposed V2O5/TiO2 catalysts to a mixture

220

of 2700 ppm SO2, 5% O2, 0 or 4% water vapor in He at 380 °C for 24 hours and concluded that

ACS Paragon Plus Environment

11

Environmental Science & Technology

Page 12 of 30

221

stable sulfate species formed on titania instead of vanadia.30 Yu et al. exposed V2O5-WO3/TiO2

222

to 2% SO2 and 5% O2 in N2 at 350 °C and concluded that sulfate was formed with titanium in the

223

catalyst.28 Similar observations can also be found in sulfate impregnation studies.24, 33 In addition

224

to SCR reactions, V2O5 is also used as a catalyst for SO2 oxidation.3 Several studies on

225

V2O5/activated carbon found that in SO2 oxidation reactions, SO2 reacts with surface V2O5 to

226

form a VOSO4-like structure, and O2 is necessary for SO3 formation and catalyst regeneration

227

via reactions with the VOSO4 intermediate.34-38 Since sulfur species were not detected by XPS

228

survey scans, and no O2 was used with SO2 in the exposure tests, it is not very likely that SO2

229

reacted with the vanadium foil surface to form SO3.

230

Overall, the survey scans showed that adsorption of SO2, NO, and NO2 as well as the

231

presence of thermally unstable species are not likely to be a concern for the purpose of carbon

232

capture in high-temperature flue gas for extended time periods. Nevertheless, coal-derived flue

233

gas is a complex mixture containing fly ash, O2, moisture, carbon monoxide (CO), hydrocarbons,

234

mercury (Hg), and many acid gases, such as sulfur trioxide (SO3) and hydrogen chloride

235

(HCl).39-40 Deposition of solid carbon species such as fly ash particles would be a problem for

236

membranes in general, as observed by Eiberger et al. in their study on ceramic membranes.41 The

237

testing described in this work also does not include species such as CO, SO3, or HCl. There can

238

be potential impacts of both CO and acid gases on the membrane, and this could be a fruitful

239

area for future research on vanadium and other metallic membranes for carbon capture.

240

Ex situ XPS characterization: Region scans. This section focuses on the changes in

241

vanadium oxidation state, which can be indicative of possible reactions on the surface as well as

242

potential permeation of these gases into the bulk of the vanadium foil. The V 2p3/2 photoemission

243

spectra of the samples from the 10-hour exposure tests are shown in Figure 1. The region scan

ACS Paragon Plus Environment

12

Page 13 of 30

Environmental Science & Technology

244

for the corresponding as-received foil and the reference BEs are also shown. The V 2p3/2

245

reference BEs are taken from the Handbook of X-ray Photoelectron Spectroscopy:42 metallic V

246

(“V met.”) at 512.4 eV, V2O3 at 515.7 eV, VO2 at 516.3 eV, and V2O5 at 517.6 eV.

247

The spectrum for the as-received foil in Figure 1 is representative of the spectra for all the as-

248

received foils analyzed (see SI Figure S3). These spectra are asymmetric towards the high BE

249

side, indicating that V2O5 is likely to be the dominant surface oxide on these foils. It has been

250

shown that V2O5 is the most stable phase in the V–O system,43-46 especially at room temperature

251

in dry air.47-48 This explains the consistency of surface oxide compositions across the as-received

252

vanadium foils, since the foils had been exposed to dry air at room temperature, and the surface

253

compositions would have reached equilibrium with air prior to XPS characterization.

254

The V 2p3/2 spectra of the N2-10h and SO2-10h samples are broadened and shifted to lower

255

BEs, suggesting that VO2 may be the dominant surface oxide on these samples. In contrast, the V

256

2p3/2 spectra of the NO-10h and NO2-10h samples showed a more prominent V2O5 component

257

with BEs at around 517.6 eV, especially the NO-10h sample. In theory, the V 2p3/2 peak at

258

around 517.6 eV could also be associated with NH4VO3, which has a V 2p3/2 BE of 517.8 eV

259

(using adventitious carbon as BE reference).49 However, the presence of NH4VO3 is unlikely, as

260

N 1s peaks would otherwise be detected on the NO-10h and NO2-10h samples by XPS region

261

scans.

262

A general observation in this study was that XPS survey and region scans of different

263

locations on the same sample often yielded very similar spectra. This suggests highly

264

homogeneous surface features. One exception, however, was the NO2-10h sample (see SI Figure

265

S7). The spectrum of the NO2-10h sample shown in Figure 1 was chosen to represent the mixed

ACS Paragon Plus Environment

13

Environmental Science & Technology

Page 14 of 30

266

nature (i.e., both VO2 and V2O5 components are clearly visible) of the surface oxides on this

267

sample. The mixed surface features can be confirmed by SEM, as will be shown in the following

268

section.

269

Peak fitting was performed for the region scan spectra to obtain a more quantitative

270

comparison of the changes in chemical state before and after gas exposure. Like many other

271

transition metals, vanadium has a range of chemical states with overlapping BEs. Since Figure 1

272

showed that multiple vanadium oxidation states are present on the sample surfaces, much work

273

in this paper has been dedicated to establishing a consistent peak fitting procedure suitable for

274

these samples.

275

While general peak fitting procedures and reference fitting parameters are available in the

276

literature, there exist uncertainties in XPS peak fitting for transition metals. Existing studies and

277

standard databases report peak positions (i.e., BEs) but often do not adequately address issues

278

such as peak widths and other complexities found in transition metal 2p spectra.50 In addition,

279

peak fitting is more than a mathematical problem. A common pitfall in XPS peak fitting is to let

280

goodness-of-fit dictate the interpretation of the physics and chemistry of the systems studied. In

281

reality, however, peak fitting should be an iterative process where mathematical parameters and

282

physical interpretations inform each other, and the latter should play a more decisive role than

283

the former in contributing to the understanding of the system.

284

This study does not venture to address the various complexities involved in the XPS analysis

285

of transition metals. Rather, we hope to better understand the samples in our work by drawing

286

insights from existing literature on similar systems. For this purpose, a careful literature review

287

was conducted on XPS studies of vanadium-based catalysts and vanadium oxide films. A

ACS Paragon Plus Environment

14

Page 15 of 30

Environmental Science & Technology

288

summary of the samples, data processing techniques, BE references, and V2p3/2 BEs and full

289

widths at half maximum (FWHMs) are summarized in SI Table S5. Some studies have

290

concluded that for vanadium oxides, the O 1s line associated with vanadium oxides (VOx) serves

291

as a better BE reference than the C 1s line associated with adventitious carbon, and that the BE

292

difference between the O 1s and V 2p3/2 lines is a more reliable parameter for determining the

293

oxidation state of vanadium.51-54 For this reason, the BE differences between the O 1s (VOx) and

294

V 2p3/2 lines (denoted as “∆”), are also included in the summary.

295

The averages (avg.), standard deviations (stdev.), and ranges of the V 2p3/2 BEs, ∆, and V

296

2p3/2 peak FWHMs for selected oxides from Table S5 are summarized in Table 2. It can be seen

297

from Table 2 that there exists a fairly wide spread in the reported BEs, ∆, and FWHMs, which

298

highlights the uncertainties associated with XPS peak fitting for vanadium. Nevertheless, these

299

literature data serve as a useful guide for the peak fitting in this work, with some observations

300

and caveats discussed in the Supporting Information (SI Section S6).

ACS Paragon Plus Environment

15

Environmental Science & Technology

Page 16 of 30

301 302

Figure 1. V 2p3/2 XPS spectra of the as-received vanadium foil and samples from the 10-hour

303

exposure tests.

304 305

Table 2. Summary of selected XPS fitting parameters of V 2p3/2 and O 1s spectra for selected

306

oxides form the literature (full summary in SI Table S5).

V 2p3/2 BE [eV]

∆ [eV]

min.–max. avg. ± stdev.

min.–max. avg. ± stdev.

(range)

V

512.3 ± 0.3

V 2p3/2 FWHM [eV]

511.5–512.9

min.–max. avg. ± stdev.

(range)

-

-

(range)

1.2 ± 0.5

0.7–2.0

ACS Paragon Plus Environment

16

Page 17 of 30

Environmental Science & Technology

(1.4)

(1.3)

514.4–516.8 V 2O 3

VO2

V 2O 5

515.5 ± 0.6

14.2–15.2 14.6 ± 0.4

1.1–4.8 2.7 ± 1.5

(2.4)

(1.0)

(3.7)

514.8–516.8

12.7–15.0

1.0–4.5

515.9 ± 0.5

13.9 ± 0.5

2.5 ± 1.2

(2.0)

(2.3)

(3.5)

516.3–518.3

12.6–13.2

0.9–3.0

517.2 ± 0.4

12.9 ± 0.1 (2.0)

1.5 ± 0.4 (0.6)

(2.1)

307 308

The peak fitting results for the V 2p3/2 and O 1s spectra from the 10-hour exposure tests are

309

shown in Table 3. Three main vanadium oxides—V2O3, VO2, and V2O5—were considered for

310

fitting of the V 2p3/2 lines, but it was found that using just VO2 and V2O5 was adequate to

311

provide reasonably good fits. Previous discussions have ruled out the possibility that vanadium

312

was associated with sulfur- or nitrogen-containing species, e.g., VOSO4 or NH4VO3. These

313

species were therefore not considered in peak fitting. The O 1s spectra were deconvoluted into

314

two components: one at around 530 eV corresponding to VOx, and one at around 531–532 eV

315

corresponding to C=O bonds.42, 54 The ∆ values were calculated from the BEs of the O 1s (VOx)

316

and V 2p3/2 components. The oxide composition is represented by the peak area percentages (%

317

area) of the V 2p3/2 components relative to the entire V 2p3/2 spectra. The average surface

318

oxidation state was calculated from the assigned oxidation states and oxide composition.

ACS Paragon Plus Environment

17

Environmental Science & Technology

Page 18 of 30

319 320

Table 3. XPS fitting parameters for the V 2p3/2 spectra of the vanadium samples after the 10-

321

hour exposure experiments.

oxide

FWHM BE [eV]

assigned

VO2

average % area

∆ [eV]

[eV]

516.1

1.1

oxidation state

16.8%

14.2 4.8

as-received (Foil #4) V 2O 5

517.3

1.4

83.2%

13.0

VO2

516.3

1.6

75.0%

13.8 4.3

N2 V 2O 5

517.8

1.6

25.0%

12.4

VO2

516.3

1.6

69.9%

13.9 4.3

2500 ppmv SO2 V 2O 5

517.7

1.5

30.2%

12.5

VO2

516.2

1.3

14.4%

14.3 4.9

250 ppmv NO

50 ppmv NO2

V 2O 5

517.6

1.2

85.6%

12.9

VO2

516.0

1.5

60.0%

14.0

4.4

ACS Paragon Plus Environment

18

Page 19 of 30

Environmental Science & Technology

V 2O 5

517.4

1.5

40.0%

12.6

322 323

It should be noted that although the results in Table 3 were generated from consistent peak

324

fitting procedures based on literature evidence, uncertainties such as satellite peaks and

325

asymmetry have not been fully accounted for in these fits. Nevertheless, these results provide a

326

quantitative comparison of the changes in surface oxidation state as well as some insights into

327

the physical and chemical processes that induced these changes during the thermochemical

328

exposure.

329

The surface oxides on the as-received foil shown in Table 3 consist of 83% V2O5 and 17%

330

VO2, which confirms the observation from the corresponding spectrum in Figure 1 that V2O5

331

was the dominant surface oxide. The average surface oxidation states of the N2-10h and SO2-10h

332

samples are both 4.3, close to those of the N2-5h and SO2-5h samples (see SI Table S4). The NO-

333

10h sample has a high average surface oxidation state of 4.9, consistent with the peak position

334

and shape of the corresponding spectrum in Figure 1. This value is also similar to the average

335

surface oxidation state of the NO-5h sample, which is 4.8. It can be concluded that V2O5 is the

336

dominant oxide on both NO samples. The NO2-10h sample has an average surface oxidation

337

state of 4.4, which is lower than that of the NO2-5h sample, 4.6. This can also be inferred by

338

comparing the corresponding spectra (in Figure S5 and Figure 1). This difference highlights the

339

mixed surface features resulting from exposure to NO2. The ∆ values in Table 3 are 14.0 ± 0.2

340

eV for the fitted VO2 peaks and 12.6 ± 0.2 eV for the fitted V2O5 peaks. The V 2p3/2 BE of the

341

fitted VO2 and V2O5 peaks are 516.2 ± 0.1 eV and 517.6 ± 0.2 eV, respectively. These values

342

agree with the literature data in Table 2.

ACS Paragon Plus Environment

19

Environmental Science & Technology

Page 20 of 30

343

The lowered surface oxidation states could have resulted from thermal decomposition of

344

V2O5 to lower oxides at high temperature and low O2 partial pressure conditions. This hypothesis

345

is supported by both experimental and theoretical evidence from the literature. Su and Schlögl

346

observed thermal reduction of V2O5 crystals to V2O3 via VO2 when the crystals were heated up

347

to 600 °C in a high vacuum of 10−7 Torr (1.3 × 10−5 Pa).55 Based on thermodynamic calculations,

348

Zhang et al. predicted that V2O5 decomposes at 808 K (535 °C) in an inert atmosphere, while

349

Gulbransen and Andrew predicted that V2O5 decomposes to VO2 and O2 below an oxygen partial

350

pressure of 10−6 mbar above 500 °C.48, 56-57 The phase diagram simulated from computational

351

thermodynamics by de Castro et al. indicates that VO2 is the most stable phase at high

352

temperatures and low pressures. In particular, at 873 K (600 °C), O2 partial pressure would need

353

to be on the order of 1 Pa (10−5 bar) for V2O5 to be stable.47 From in situ XRD measurements of

354

controlled oxidation of vanadium thin films, Rampelberg et al. observed that VO2 was present

355

throughout the temperature and O2 partial pressure ranges investigated (430–615 °C, 0.2–200

356

mbar), whereas V2O5 only appeared at higher O2 partial pressures (20–200 mbar).58 Since N2

357

fluxes through vanadium foils were only detected at above a pressure difference of 2 bar in

358

previous permeation experiments, and the detected fluxes were comparatively small,4, 8 N2 can be

359

considered chemically inert to the vanadium foils in the current experimental setup, where the

360

foil was not sealed or pressurized. The purge gas Ar is also considered chemically inert,

361

independent of the pressure difference across the foils. Therefore, thermal decomposition is

362

likely to be a mechanism that resulted in the lowering of oxidation states after exposure to N2.

363

Thermal decomposition is also thought to have contributed to the lowered oxidation states on the

364

SO2 samples for two reasons. First, the lineshapes and peak fitting results for the SO2 samples

365

are similar to those for the N2 samples. Second, since sulfur-containing species were not detected

ACS Paragon Plus Environment

20

Page 21 of 30

Environmental Science & Technology

366

by XPS after exposure to SO2/N2, it is less likely that SO2 has adsorbed to the vanadium surface

367

and reduced the surface oxides. This conclusion may change depending on the SO2 concentration

368

used in gas exposure as well as the sample condition prior to exposure, as shown by a recent

369

study using deposited vanadium films and 50% SO2/N2.59

370

Exposure to NO/N2 and NO2/N2, especially the former, has resulted in higher surface

371

oxidation states compared to exposure to N2 and SO2/N2. Here, oxidation by NO or NO2 may

372

have been a more competitive mechanism than thermal decomposition, resulting in overall

373

higher surface oxidation states. The oxidizing nature of NO can be indirectly verified by several

374

studies in the literature. Catalysis studies of V2O5/TiO2 by Topsøe et al. in the temperature range

375

of 375–625 K (202–352 °C) concluded that vanadium surface pre-adsorbed with NH3 was more

376

readily regenerated in NO than in O2, with the former providing a more oxidizing atmosphere.27,

377

60

378

(1.3–1333.2 Pa) and found that NO adsorbed on Fe3O4 caused oxidation of the metal oxide

379

surface via back donation of electrons.61 Dianis and Lester studied NO adsorption on NiO,

380

Co3O4, and graphite at −100 °C and 2 × 10−5 Torr (0.003 Pa) and concluded that back donation

381

occurred from the metal oxides to the adsorbed NO.62 An adsorption study of NO and N2O on

382

Al(100) single crystals at 80 K by Pashutski and Folman found that there was a negative charge

383

transfer from the metal to the adsorbed gases, and that NO was more reactive on Al(100) than O2

384

or N2O.63 A caveat is that the experimental conditions in these studies as well as the metals or

385

metal oxides used are quite different from the current study. Future work should include more

386

focused studies on NO and NO2 to further test and refine the hypothesis in this work.

Contour and Mouvier conducted adsorption experiments at −100–200 °C and 10−2–10 Torr

387

Ex situ SEM analyses. The surface SEM images of the samples from the 10-hour exposure

388

experiments and the corresponding as-received foil are shown in Figure 2 (see SI Section S7 for

ACS Paragon Plus Environment

21

Environmental Science & Technology

Page 22 of 30

389

selected cross-sectional SEM images). Two surface features are common among the annealed

390

samples. The N2-10h and SO2-10h samples have dense, irregularly shaped grains with lateral

391

sizes of 1–2 µm. Similar features have also been observed for VO2 films and crystals in the

392

literature.58, 64-67 The NO-10h samples have plate-like crystals with widths below 1 µm. Similar

393

features can also be found for V2O5 films or features associated with V2O5 in the literature.44-45,

394

68-70

395

crystals, as shown in Figure 2(e). This confirms the observation from the XPS scans that the

396

surface oxide composition on this sample is rather inhomogeneous. In general, one can see that

397

the SEM images consistently confirm the XPS results discussed in the previous section.

The NO2-10h sample has mixed features of both the irregularly shaped grains and plate-like

398 399

Figure 2. SEM images of (a) an as-received vanadium foil (Foil #4) and the samples exposed to

400

(b) N2, (c) 2500 ppmv SO2/N2, (d) 250 ppmv NO/N2, and (e) 50 ppmv NO2/N2 in the 10-hour

401

exposure experiments.

402

ACS Paragon Plus Environment

22

Page 23 of 30

Environmental Science & Technology

403

It can be inferred from the XPS region scans and SEM results that while vanadium and its

404

surface oxides showed certain chemical resistance to flue gas components such as SO2 and H2O,

405

an oxidizing environment could be a concern for the long-term structural integrity and

406

performance of the vanadium membrane as well as other metallic membranes. For metallic

407

membrane systems to be implemented for carbon capture in high-temperature flue gas, future

408

research should investigate potential process modifications to reduce the oxidant levels in flue

409

gas and material improvements such alloying to enhance the resistance of membranes to

410

oxidation.

411

In situ transmission XRD. Throughout the exposure experiments at 500 °C, no new phases

412

in the vanadium membranes were detected by in situ transmission XRD measurements,

413

independent of the gas or gas mixture used. The complete results of the in situ XRD experiments

414

are shown in the Supporting Information (SI Section S7). For comparison, the samples from the

415

previously described 10-hour exposure experiments at 600 °C were analyzed using ex situ XRD,

416

and preliminary results (not included here) showed evidence that vanadium oxides were present

417

in the bulk the these samples. Since the main differences between the two sets of samples are

418

exposure temperature and duration, these observations confirmed the findings that vanadium

419

oxide film growth is promoted by increasing temperature and reaction time.1,

420

hypothesize that the bulk vanadium oxides formed due to the diffusion or dissolution of oxygen

421

from the surface oxides to the metal bulk, with the diffusion driven by the difference in the

422

oxygen content between the surface and the bulk. This hypothesis can particularly be supported

423

by the fact that bulk oxidization was observed even when vanadium was only exposed to non-

424

oxidizing gases, e.g., N2. In this case, the oxygen in the surface oxides was the only possible

425

source of oxygen that could have resulted in bulk oxides. The previously discussed reduction of

56, 71-73

We

ACS Paragon Plus Environment

23

Environmental Science & Technology

Page 24 of 30

426

surface V2O5 can also be attributed to oxygen diffusion or dissolution into the bulk, which has

427

been observed in several previous studies on vanadium oxides.71, 74-75 It should be emphasized

428

that the in situ XRD experiments in this study only aimed at examining the vanadium bulk. For

429

investigations of thin films, readers are referred to a recent in situ XRD study by Rampelberg et

430

al. on controlled oxidation of vanadium thin films over a range of O2 partial pressures and

431

temperatures as well as controlled reduction of V2O5 thin films in H2.58

432

If oxygen diffusion or dissolution from the surface oxides has indeed contributed to

433

vanadium oxidation in the membrane bulk, future studies on vanadium membranes for carbon

434

capture should investigate ways to reduce the operating temperature of the membrane system to

435

slow down bulk oxidation. A lower operating temperature can also potentially reduce the carbon

436

capture energy use of the vanadium membrane7 and is therefore also preferred from the process

437

design perspective. In general, mechanical stability and integrity are always an issue with any

438

membrane, as is long-term exposure to high temperatures. These will be investigated in future

439

research. In addition, the actual N2 permeation performance of the vanadium membrane will be

440

examined in simulated gas mixtures and correlated with the analytical work reported in this

441

paper. These permeation experiments can especially be benefited by coupling with in situ or

442

operando XRD characterization, which can effectively track the influences of these gases on the

443

membrane with time and potentially reveal transient structural or phase changes in the

444

membrane.

ACS Paragon Plus Environment

24

Page 25 of 30

Environmental Science & Technology

445

ASSOCIATED CONTENT

446

Supporting Information

447

The Supporting Information is available free of charge on the ACS Publications website at DOI:

448

.

449

Additional descriptions of experimental design, literature summary of XPS peak fitting

450

parameters, and additional results and discussions (PDF)

451 452

AUTHOR INFORMATION

453

Corresponding Author

454

*Address: Chemical and Biological Engineering Department, Colorado School of Mines, 1613

455

Illinois Street, Golden, CO 80401. Email: [email protected].

456

Notes

457

The authors declare no competing financial interest.

458 459

ACKNOWLEDGMENTS

460

This work is supported by the National Science Foundation under Grant No. 1263991. The XPS

461

and SEM analyses were performed at the Stanford Nano Shared Facilities (SNSF), supported by

462

the National Science Foundation under award ECCS-1542152. The XRD experiments were

463

carried out at the Stanford Synchrotron Radiation Lightsource, SLAC National Accelerator

464

Laboratory, which is supported by the US Department of Energy, Office of Science, Office of

465

Basic Energy Sciences under Contract No. DE-AC02-76SF00515. The authors would like to

ACS Paragon Plus Environment

25

Environmental Science & Technology

Page 26 of 30

466

thank Dr. Laura Schelhas at SLAC, Chuck Hitzman, Dr. Juliet Jamtgaard, and Richard Chin at

467

the SNSF for their helpful discussions and insights on XPS and SEM analyses, and Ron Marks

468

and Tim J. Dunn at the SSRL for providing beamline support.

469 470

REFERENCES

471 472 473 474 475 476 477 478 479 480 481 482 483 484 485 486 487 488 489 490 491 492 493 494 495 496 497 498 499 500 501 502 503 504 505

(1) Gilberd, P. W.; Johnson, P. B.; Vickridge, I. C.; Wismayer, A. C. TEM and IBA study of the thermal oxidation of V following high dose He implantation. J. Nucl. Mater. 1997, 244 (1), 51–58. (2) Kim, C.-H.; Yun, Y. J.; Kim, B. H.; Hong, W. G.; Kim, Y. Y.; Jang, W. l.; Lee, N.-E.; Yu, H. Y. The Observation of electrical hysteric behavior in synthesized V2O5 nanoplates by recrystallization. J. Nanomater. 2013, 2013, 85. (3) Weckhuysen, B. M.; Keller, D. E. Chemistry, spectroscopy and the role of supported vanadium oxides in heterogeneous catalysis. Catal. Today 2003, 78 (1), 25–46. (4) Özdoğan, E. Theoretical and experimental investigations of metallic membranes for CO2 capture. Ph.D. Dissertation, Stanford University, Stanford, CA, 2012. (5) Rochana, P.; Lee, K.; Wilcox, J. Nitrogen adsorption, dissociation, and subsurface diffusion on the vanadium (110) surface: A DFT study for the nitrogen-selective catalytic membrane application. J. Phys. Chem. C 2014, 118 (8), 4238–4249. (6) Wilcox, J. Nitrogen-permeable membranes and uses thereof. US8440000 B2, 2013. (7) Yuan, M.; Narakornpijit, K.; Haghpanah, R.; Wilcox, J. Consideration of a nitrogenselective membrane for postcombustion carbon capture through process modeling and optimization. J. Membr. Sci. 2014, 465, 177–184. (8) Lee, K. From modeling to synthesis and characterization of nitrogen-selective metallic membranes. Ph.D. Dissertation, Stanford University, Stanford, CA, 2016. (9) Kundu, P. K.; Chakma, A.; Feng, X. Effectiveness of membranes and hybrid membrane processes in comparison with absorption using amines for post-combustion CO2 capture. Int. J. Greenhouse Gas Control 2014, 28, 248–256. (10) Khalilpour, R.; Mumford, K.; Zhai, H.; Abbas, A.; Stevens, G.; Rubin, E. S. Membranebased carbon capture from flue gas: A review. J. Cleaner Prod. 2015, 103, 286–300. (11) Songolzadeh, M.; Soleimani, M.; Takht Ravanchi, M.; Songolzadeh, R. Carbon dioxide separation from flue gases: A technological review emphasizing reduction in greenhouse gas emissions. Scientific World J. 2014, 2014, 1–34. (12) Wilcox, J. Carbon Capture; Springer: New York, NY, 2012. (13) Bounaceur, R.; Lape, N.; Roizard, D.; Vallieres, C.; Favre, E. Membrane processes for post-combustion carbon dioxide capture: A parametric study. Energy 2006, 31 (14), 2556–2570. (14) Zhai, H.; Rubin, E. S. Techno-economic assessment of polymer membrane systems for postcombustion carbon capture at coal-fired power plants. Environ. Sci. Technol. 2013, 47 (6), 3006–3014. (15) Hussain, A.; Farrukh, S.; Minhas, F. T. Two-stage membrane system for post-combustion CO2 capture application. Energy Fuels 2015, 29 (10), 6664–6669.

ACS Paragon Plus Environment

26

Page 27 of 30

506 507 508 509 510 511 512 513 514 515 516 517 518 519 520 521 522 523 524 525 526 527 528 529 530 531 532 533 534 535 536 537 538 539 540 541 542 543 544 545 546 547 548 549 550 551

Environmental Science & Technology

(16) Kim, H.-J.; Chaikittisilp, W.; Jang, K.-S.; Didas, S. A.; Johnson, J. R.; Koros, W. J.; Nair, S.; Jones, C. W. Aziridine-functionalized mesoporous silica membranes on polymeric hollow fibers: Synthesis and single-component CO2 and N2 permeation properties. Ind. Eng. Chem. Res. 2014, 54 (16), 4407–4413. (17) Kumar, P.; Kim, S.; Ida, J.; Guliants, V. V. Polyethyleneimine-modified MCM-48 membranes: Effect of water vapor and feed concentration on N2/CO2 selectivity. Ind. Eng. Chem. Res. 2008, 47 (1), 201–208. (18) Moon, S.-Y.; Jeon, E.; Bae, J.-S.; Byeon, M.; Park, J.-W. Polyurea networks via organic sol–gel crosslinking polymerization of tetrafunctional amines and diisocyanates and their selective adsorption and filtration of carbon dioxide. Polym. Chem. 2014, 5 (4), 1124–1131. (19) Wang, Y.; Yang, Q.; Zhong, C.; Li, J. Graphene-like poly (triazine imide) as N2-selective ultrathin membrane for postcombustion CO2 capture. J. Phys. Chem. C 2016, 120 (50), 28782– 28788. (20) Scholes, C. A.; Kentish, S. E.; Stevens, G. W. Effects of minor components in carbon dioxide capture using polymeric gas separation membranes. Sep. Purif. Rev. 2009, 38 (1), 1–44. (21) Wilcox, J.; Rupp, E.; Ying, S. C.; Lim, D.-H.; Negreira, A. S.; Kirchofer, A.; Feng, F.; Lee, K. Mercury adsorption and oxidation in coal combustion and gasification processes. Int. J. Coal Geol. 2012, 90, 4–20. (22) Carnegie Mellon University. Integrated Environmental Control Model; https://www.cmu.edu/epp/iecm/index.html. (23) Barbaray, B.; Contour, J.-P.; Mouvier, G. Effects of nitrogen dioxide and water vapor on oxidation of sulfur dioxide over vanadium pentoxide particles. Environ. Sci. Technol. 1978, 12 (12), 1294–1297. (24) Amiridis, M. D.; Wachs, I. E.; Deo, G.; Jehng, J.-M.; Kim, D. S. Reactivity of V2O5 catalysts for the selective catalytic reduction of NO by NH3: Influence of vanadia loading, H2O, and SO2. J. Catal. 1996, 161 (1), 247–253. (25) Inomata, M.; Miyamoto, A.; Murakami, Y. Mechanism of the reaction of NO and NH3 on vanadium oxide catalyst in the presence of oxygen under the dilute gas condition. J. Catal. 1980, 62 (1), 140–148. (26) Miyamoto, A.; Yamazaki, Y.; Hattori, T.; Inomata, M.; Murakami, Y. Study on the pulse reaction technique: VI. Kinetics of the reaction of NO with NH3 on a V2O5 catalyst. J. Catal. 1982, 74 (1), 144–155. (27) Topsøe, N.-Y.; Dumesic, J. A.; Topsøe, H. Vanadia/titania catalysts for selective catalytic reduction of nitric oxide by ammonia: II. Studies of active sites and formulation of catalytic cycles. J. Catal. 1995, 151 (1), 241–252. (28) Yu, Y.; Wang, J.; Chen, J.; Meng, X.; Chen, Y.; He, C. Promotive effect of SO2 on the activity of a deactivated commercial selective catalytic reduction catalyst: An in situ DRIFT study. Ind. Eng. Chem. Res. 2014, 53 (42), 16229–16234. (29) Gruber, M.; Hermann, K. Elementary steps of the catalytic NOx reduction with NH3: Cluster studies on reaction paths and energetics at vanadium oxide substrate. J. Chem. Phys. 2013, 139 (24), 244701. (30) Guo, X.; Bartholomew, C.; Hecker, W.; Baxter, L. L. Effects of sulfate species on V2O5/TiO2 SCR catalysts in coal and biomass-fired systems. Appl. Catal., B 2009, 92 (1), 30–40. (31) Barbaray, B.; Contour, J. P.; Mouvier, G. Sulfur dioxide oxidation over atmospheric aerosol—X-ray photoelectron spectra of sulfur dioxide adsorbed on V2O5 and carbon. Atmos. Environ. 1977, 11 (4), 351–356.

ACS Paragon Plus Environment

27

Environmental Science & Technology

552 553 554 555 556 557 558 559 560 561 562 563 564 565 566 567 568 569 570 571 572 573 574 575 576 577 578 579 580 581 582 583 584 585 586 587 588 589 590 591 592 593 594 595 596

Page 28 of 30

(32) Le Bars, J.; Auroux, A. Microcalorimetric study of the acid-base properties of bulk and silica or γ-alumina-supported vanadium oxides. J. Therm. Anal. Calorim. 1993, 40 (3), 1277– 1284. (33) Dunn, J. P.; Jehng, J.-M.; Kim, D. S.; Briand, L. E.; Stenger, H. G.; Wachs, I. E. Interactions between surface vanadate and surface sulfate species on metal oxide catalysts. J. Phys. Chem. B 1998, 102 (32), 6212–6218. (34) Li, P.; Liu, Z.; Li, Q.; Wu, W.; Liu, Q. Multiple roles of SO2 in selective catalytic reduction of NO by NH3 over V2O5/AC catalyst. Ind. Eng. Chem. Res. 2014, 53 (19), 7910– 7916. (35) Liu, Q.; Liu, Z. Carbon supported vanadia for multi-pollutants removal from flue gas. Fuel 2013, 108, 149–158. (36) Ma, J.; Liu, Z.; Liu, Q.; Guo, S.; Huang, Z.; Xiao, Y. SO2 and NO removal from flue gas over V2O5/AC at lower temperatures—role of V2O5 on SO2 removal. Fuel Process. Technol. 2008, 89 (3), 242–248. (37) Mathieu, Y.; Tzanis, L.; Soulard, M.; Patarin, J.; Vierling, M.; Molière, M. Adsorption of SOx by oxide materials: A review. Fuel Process. Technol. 2013, 114, 81–100. (38) Xiao, Y.; Liu, Q.; Liu, Z.; Huang, Z.; Guo, Y.; Yang, J. Roles of lattice oxygen in V2O5 and activated coke in SO2 removal over coke-supported V2O5 catalysts. Appl. Catal., B 2008, 82 (1), 114–119. (39) Granite, E. J.; Pennline, H. W. Photochemical removal of mercury from flue gas. Ind. Eng. Chem. Res. 2002, 41 (22), 5470–5476. (40) Presto, A. A.; Granite, E. J. Impact of sulfur oxides on mercury capture by activated carbon. Environ. Sci. Technol. 2007, 41 (18), 6579–6584. (41) Eiberger, J.; Wilkner, K.; Reetz, C.; Sebold, D.; Jordan, N.; de Graaff, M.; Meulenberg, W. A.; Stöver, D.; Bram, M. Influence of coal power plant exhaust gas on the structure and performance of ceramic nanostructured gas separation membranes. Int. J. Greenhouse Gas Control 2015, 43, 46–56. (42) Moulder, J. F.; Stickle, W. F.; Sobol, P. E.; Bomben, K. D. Handbook of X-ray Photoelectron Spectroscopy: A Reference Book of Standard Spectra for Identification and Interpretation of XPS Data; Chastain, J., Ed. Physical Electronics Division, Perkin-Elmer Corporation: Eden Prairie, MN, 1992. (43) Cui, J.; Da, D.; Jiang, W. Structure characterization of vanadium oxide thin films prepared by magnetron sputtering methods. Appl. Surf. Sci. 1998, 133 (3), 225–229. (44) Mane, A. A.; Ganbavle, V. V.; Gaikwad, M. A.; Nikam, S. S.; Rajpure, K. Y.; Moholkar, A. V. Physicochemical properties of sprayed V2O5 thin films: Effect of substrate temperature. J. Anal. Appl. Pyrolysis 2015, 115, 57–65. (45) Prześniak-Welenc, M.; Łapiński, M.; Lewandowski, T.; Kościelska, B.; Wicikowski, L.; Sadowski, W. The influence of thermal conditions on V2O5 nanostructures prepared by sol-gel method. J. Nanomater. 2015, 2015, 1–8. (46) Zou, C. W.; Yan, X. D.; Han, J.; Chen, R. Q.; Gao, W. Microstructures and optical properties of β-V2O5 nanorods prepared by magnetron sputtering. J. Phys. D: Appl. Phys. 2009, 42 (14), 145402. (47) de Castro, M. S. B.; Ferreira, C. L.; de Avillez, R. R. Vanadium oxide thin films produced by magnetron sputtering from a V2O5 target at room temperature. Infrared Phys. Technol. 2013, 60, 103–107.

ACS Paragon Plus Environment

28

Page 29 of 30

597 598 599 600 601 602 603 604 605 606 607 608 609 610 611 612 613 614 615 616 617 618 619 620 621 622 623 624 625 626 627 628 629 630 631 632 633 634 635 636 637 638 639 640 641

Environmental Science & Technology

(48) Lindström, R.; Maurice, V.; Zanna, S.; Klein, L.; Groult, H.; Perrigaud, L.; Cohen, C.; Marcus, P. Thin films of vanadium oxide grown on vanadium metal: oxidation conditions to produce V2O5 films for Li‐intercalation applications and characterisation by XPS, AFM, RBS/NRA. Surf. Interface Anal. 2006, 38 (1), 6–18. (49) National Institute of Standards and Technology, NIST X-ray Photoelectron Spectroscopy Database, Version 4.1, Gaithersburg, MD, USA, 2012, http://srdata.nist.gov/xps/. (50) Biesinger, M. C.; Lau, L. W. M.; Gerson, A. R.; Smart, R. S. C. Resolving surface chemical states in XPS analysis of first row transition metals, oxides and hydroxides: Sc, Ti, V, Cu and Zn. Appl. Surf. Sci. 2010, 257 (3), 887–898. (51) Cornaglia, L. M.; Lombardo, E. A. XPS studies of the surface oxidation states on vanadium-phosphorus-oxygen (VPO) equilibrated catalysts. Appl. Catal., A 1995, 127 (1–2), 125–138. (52) Hryha, E.; Rutqvist, E.; Nyborg, L. Stoichiometric vanadium oxides studied by XPS. Surf. Interface Anal. 2012, 44 (8), 1022–1025. (53) Mendialdua, J.; Casanova, R.; Barbaux, Y. XPS studies of V2O5, V6O13, VO2 and V2O3. J. Electron Spectrosc. Relat. Phenom. 1995, 71 (3), 249–261. (54) Silversmit, G.; Depla, D.; Poelman, H.; Marin, G. B.; De Gryse, R. Determination of the V2p XPS binding energies for different vanadium oxidation states (V5+ to V0+). J. Electron Spectrosc. Relat. Phenom. 2004, 135 (2), 167–175. (55) Su, D. S.; Schlögl, R. Thermal decomposition of divanadium pentoxide V2O5: towards a nanocrystalline V2O3 phase. Catal. Lett. 2002, 83 (3), 115–119. (56) Gulbransen, E. A.; Andrew, K. F. The kinetics of the reactions of vanadium with oxygen and nitrogen. J. Electrochem. Soc. 1950, 97 (11), 396–404. (57) Zhang, Z.; Henrich, V. E. Electronic interactions in the vanadium/TiO2(110) and vanadia/TiO2(110) model catalyst systems. Surf. Sci. 1992, 277 (3), 263–272. (58) Rampelberg, G.; De Schutter, B.; Devulder, W.; Martens, K.; Radu, I.; Detavernier, C. In situ X-ray diffraction study of the controlled oxidation and reduction in the V–O system for the synthesis of VO2 and V2O3 thin films. J. Mater. Chem. C 2015, 3 (43), 11357–11365. (59) Ji, Y.-X.; Niklasson, G. A.; Granqvist, C. G.; Boman, M. Thermochromic VO2 films by thermal oxidation of vanadium in SO2. Sol. Energy Mater. Sol. Cells 2016, 144, 713–716. (60) Topsøe, N.-Y.; Topsøe, H.; Dumesic, J. A. Vanadia/titania catalysts for selective catalytic reduction (SCR) of nitric-oxide by ammonia: I. Combined temperature-programmed in-situ FTIR and on-line mass-spectroscopy studies. J. Catal. 1995, 151 (1), 226–240. (61) Contour, J. P.; Mouvier, G. X-ray photoelectron spectroscopy of nitrogen oxides adsorbed on iron oxides. J. Catal. 1975, 40 (3), 342–348. (62) Dianis, W.; Lester, J. E. A study of nitric oxide adsorbed on nickel oxide, cobalt oxide, and graphite by X-ray photoelectron spectroscopy. Surf. Sci. 1974, 43 (2), 602–616. (63) Pashutski, A.; Folman, M. Low temperature XPS studies of NO and N2O adsorption on Al(100). Surf. Sci. 1989, 216 (3), 395–408. (64) Corr, S. A.; Grossman, M.; Shi, Y.; Heier, K. R.; Stucky, G. D.; Seshadri, R. VO2(B) nanorods: solvothermal preparation, electrical properties, and conversion to rutile VO2 and V2O3. J. Mater. Chem. 2009, 19 (25), 4362–4367. (65) Jin, Z.; Hwang, I.-H.; Park, C.-I.; Son, J.-K.; Han, S.-W. Synthesis and temperaturedependent local structural and electrical properties of VO2 films. Curr. Appl. Phys. 2016, 16 (2), 183–190.

ACS Paragon Plus Environment

29

Environmental Science & Technology

642 643 644 645 646 647 648 649 650 651 652 653 654 655 656 657 658 659 660 661 662 663 664 665 666 667

Page 30 of 30

(66) Mian, M. S.; Okimura, K. Effect of conductive TiN buffer layer on the growth of stoichiometric VO2 films and the out-of-plane insulator–metal transition properties. J. Vac. Sci. Technol., A 2014, 32 (4), 041502. (67) Wu, Y.; Fan, L.; Liu, Q.; Chen, S.; Huang, W.; Chen, F.; Liao, G.; Zou, C.; Wu, Z. Decoupling the lattice distortion and charge doping effects on the phase transition behavior of VO2 by titanium (Ti4+) doping. Sci. Rep. 2015, 5, 9328. (68) Beke, S.; Kőrösi, L.; Papp, S.; Oszkó, A.; Nánai, L. XRD and XPS analysis of laser treated vanadium oxide thin films. Appl. Surf. Sci. 2009, 255 (24), 9779–9782. (69) Corr, S. A.; Shoemaker, D. P.; Toberer, E. S.; Seshadri, R. Spontaneously formed porous and composite materials. J. Mater. Chem. 2010, 20 (8), 1413–1422. (70) Liu, X.; Wang, S.-W.; Chen, F.; Yu, L.; Chen, X. Tuning phase transition temperature of VO2 thin films by annealing atmosphere. J. Phys. D: Appl. Phys. 2015, 48 (26), 265104. (71) Lindström, R.; Maurice, V.; Groult, H.; Perrigaud, L.; Zanna, S.; Cohen, C.; Marcus, P. Li-intercalation behaviour of vanadium oxide thin film prepared by thermal oxidation of vanadium metal. Electrochim. Acta 2006, 51 (23), 5001–5011. (72) McAdam, D. J.; Geil, G. W. Rate of oxidation of typical nonferrous metals as determined by interference colors of oxide films. J. Res. Natl. Bur. Stand 1942, 28, 593–615. (73) Mukherjee, A.; Wach, S. P. Kinetics of the oxidation of vanadium in the temperature range 350–950 °C. J. Less-Common Met. 1983, 92 (2), 289–300. (74) Han, Y.-H.; Choi, I.-H.; Kang, H.-K.; Park, J.-Y.; Kim, K.-T.; Shin, H.-J.; Moon, S. Fabrication of vanadium oxide thin film with high-temperature coefficient of resistance using V2O5/V/V2O5 multi-layers for uncooled microbolometers. Thin Solid Films 2003, 425 (1), 260– 264. (75) Schiechl, H.; Winkler, A. Growth of a vanadium oxide layer on V(100) and its reactivity towards atomic hydrogen. Fresenius' J. Anal. Chem. 2001, 371 (3), 342–347.