Versatile Cutting Method for Producing Fluorescent Ultrasmall MXene

Subscriber access provided by READING UNIV

Article

A Versatile Cutting Method for Producing Fluorescent Ultrasmall MXene Sheets Zhiqiang Wang, Jin-Nan Xuan, Zhigang Zhao, Qingwen Li, and Fengxia Geng ACS Nano, Just Accepted Manuscript • DOI: 10.1021/acsnano.7b06476 • Publication Date (Web): 07 Nov 2017 Downloaded from http://pubs.acs.org on November 7, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Nano is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 19

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

A Versatile Cutting Method for Producing Fluorescent Ultrasmall MXene Sheets Zhiqiang Wang,1 Jinnan Xuan,1 Zhigang Zhao,2 Qingwen Li,2 Fengxia Geng1,* 1

College of Chemistry, Chemical Engineering and Materials Science, Soochow University, 199 Renai Road, Suzhou 215123, China 2

Suzhou Institute of Nanotech and Nanobionics, Chinese Academy of Sciences, 398 Ruoshui Road, Suzhou Industry Park, Suzhou 215123, China

E-mail: [email protected]

Abstract: As a recently created inorganic nanosheet material, MXene has received growing attention and has become a hotspot of intensive research. The efficient morphology control of this class of material would bring enormous possibilities for creating marvelous properties and functions; however, this type of research is very scarce. In this work, we demonstrated a general and mild approach for creating ultrasmall MXenes by simultaneous intralayer cutting and interlayer delamination. Taking the most commonly studied Ti3C2 as an illustrative example, the resulting product possessed monolayer thickness with a lateral dimension of 2-8 nm and exhibited bright and tunable fluorescence. Further, the method could also be employed to synthesizing ultrasmall sheets of other MXene phases, for example, Nb2C, Ti2C. Importantly, although the strong covalent M–C bond was to some extent broken, all the characterizations suggested that the chemical structure was composed of well-maintained host layers without observation of any serious damages, demonstrating the superior reaction efficiencies and safeties of our methods. This work may provide a facile and general approach to modulate various nanoscale materials and could further stimulate the vast applications of MXene materials in many optical-related fields.

KEYWORDS: MXene, two-dimensional materials, intercalation, delamination, ultrasmall sheets, fluorescence

The morphology control of nanoscale structures, especially dimensionality modulation, 1

ACS Paragon Plus Environment

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 19

provides tremendous and exciting opportunities for creating materials with marvelous properties and functions. These materials can be utilized as important building components for the assembly of a wide variety of practical devices.1-3 Two main directions for reducing the dimensionality of inorganic lattices are available: 1) lowering the thickness down to the molecular or atomic level and 2) decreasing the lateral dimensions, even down to the quantum confinement range in some extreme cases. For the former, a number of unilamellar sheets have been produced by delamination from layered host compounds and have attracted considerable interest in the materials research community. The sheets possess ultimate two-dimensional anisotropy with a lateral size on the micrometer scale, while the thickness is on the nanometer level, endowing the material with a wealth of interesting physical phenomena and applications.4-6 For the latter, nanoparticles that reduce at least one effective dimension from three-dimensional bulk materials to a tiny size of several nanometers have been synthesized by a variety of methods.7-9 The quantum confinement effects in these systems with reduced space dimensions would modify electronic and optical properties of these structures, which is important for advancement in both fundamental science and industrial technology fields.10,11 Although it is recognized that efficient cleavage of inorganic lamellar compounds into individual layers and simultaneously reducing the lateral size of monolayered sheets would offer unexpected opportunities,12,13 the related studies are rather limited because the bonds within host layers are usually very strong covalent bonds. An intensive reaction may yield breakage of unit layers into smaller parts, but in most cases, damage to the intrinsic chemical structure of the materials would also unavoidably happen to some extent.14,15 In the rich pool of two-dimensional materials, the so-called MXene’s family is one of the youngest, and these materials are receiving an explosion of interest due to their diverse and intriguing structural, mechanical, physical, and chemical properties.16-22 The multilayered MXenes are produced by selectively etching out A from a parent MAX phase with the general formula of Mn+1AXn, where M denotes an early transition metal, A represents a main group 3 or main group 4 element, and X is either C or N. All known MAX structures are crystallized in a layered hexagonal structure with P63/mmc symmetry with the A element interleaving between regularly stacked Mn+1Xn layers, where the M layers are nearly close packed and X 2


Page 3 of 19

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

atoms fill the octahedral sites. This structure is very strongly held by metallic M–A bond and M–X bond in a mixed covalent/metallic/ionic character. Therefore, the exfoliation of the structure to selectively draw the A layer or further delamination into individual Mn+1Xn layers was not realized until very recently by taking advantage of the relatively weak strength of M– A bond compared with that of M–X. The principle involves selectively etching out the Al layer by a strong corrosive acid, i.e., hydrofluoric acid (HF), to weaken the interlamellar binding forces, which facilitates subsequent bulky guest intercalations and delaminations.13,23 Alternatively, we recently discovered that the Al layer can also be extracted by reacting Al in a base environment, for example, tetramethylammonium hydroxide (TMAOH), in which case TMA ions could be simultaneously intercalated, resulting in delaminations in one single step.19,24 However, the further breakage of primary strong M–X bond to produce ultrasmall sheets of this family remains a critical challenge, which needs to be urgently addressed to further broaden our understanding and widen the applications of this important family. Here, we demonstrate an in-depth study for the fabrication of their ultrasmall sheets by simultaneous layer cutting and stacking cleavage through a mild reaction in aqueous TMAOH. Taking the most widely studied member, Ti3C2, as a representative case, the obtained ultrathin tiny structure was 2-5 nm in lateral width and 0.5-1.5 nm in thickness. The so-obtained ultrasmall Ti3C2 sheets showed strong optical absorption and excitation-dependent emission behavior, endowing the materials with great potential in a variety of important applications. Furthermore, the synthetic method can also be extended to produce ultrasmall sheets of other members in this family, for example, Ti2C and Nb2C, therefore establishing its general applicability.

Results and Discussions The fabrication process of ultrasmall Ti3C2 monolayers involved a simple and mild reaction in aqueous TMAOH followed by an ultrasonic treatment, as schematically demonstrated in Figure 1. The reaction with TMAOH induced both in-plane fragmentation of MXene host layers and gallery intercalation of bulky guests, which facilitated the delamination into monolayers and facile cutting into small pieces after applying ultrasonication, yielding ultrasmall monolayers. We recently reported that TMAOH could 3


ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 19

hydrolyze interlayer Al of Ti3AlC2 crystals into Al(OH)4- by destroying the strong Ti−Al bonds and simultaneously intercalating TMA+ into the gallery, resulting in delamination into unilamellar nanosheets with the aid of a gentle shear force, for example, shaking by hand. It was interesting to find that in some occasions, defects were present on the sheet surfaces (Supporting Information, S1), which may suggest that there was a certain reactivity between TMAOH and surface Ti atoms in the structure. To enhance the reaction efficiency, in this study, we adopted multilayered MXene, i.e., the phase with interlayer Al extracted with concentrated HF, as the starting crystals. TMA ions were intercalated into the gallery space, and in the meantime, the host layers were cut into smaller fragments, after which an ultrasonication treatment led to in-plane fragmentation and perpendicular cleavage of the layers, thus producing the targeted ultrasmall sheets.

Figure 1. Schematic illustration of the synthetic process for preparing ultrasmall Ti3C2 sheets. After the reaction with TMAOH, the host layers fragmented into smaller parts, and at the same time, TMA ions were intercalated into the gallery, in which layer cutting and delamination simultaneously occurred upon ultrasonication, producing the targeted ultrasmall sheets.

The crystal structure, morphology, and chemical composition of the phases were systematically investigated by X-ray powder diffraction (XRD) measurements, scanning electron microscopy (SEM) equipped with energy-dispersive X-ray spectroscopy (EDS), and transmission electron microscopy (TEM) characterizations. The starting MXene crystals were produced according to previously reported procedures, using HF to selectively extract the Al layer located between the regular stacking of Ti3C2 layers, and its characterizations can be 4


Page 5 of 19

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

found in the Supporting Information, S2-3. With the removal of the Al layer, the stacking was to some extent loosened due to the loss of metallic Ti–Al bond binding the neighboring layers, in which the basal spacing shifted from the original value of 9.9 Å at approximately 9.51° to a slightly larger value of 10.8 Å at 8.17°. EDS analysis confirmed the reactions, which showed a significant decrease in the Al content. The occurrence of O and F signals was also detected, which should be explained by their high tendency to terminate the exposed Ti surfaces, in good agreement with previously documented reports.25 The subsequent intercalation of TMA ions when reacting in aqueous TMAOH was evidenced by observation of a further basal lattice expansion to 15.2 Å in the XRD characterizations and detection of an N signal in the EDS analysis, which would facilitate the delamination into monolayers under external shearing forces. Importantly, while most of the nonbasal reflections disappeared due to the loss of layer-to-layer registry, the characteristic in-plane diffraction, i.e., (110) peak, was found to be preserved, suggesting that the structure of the host layer was well-maintained with no appreciable chemical degradation or oxidation. Still, a broadening of the peak was discerned, which indicated shrinkage of the crystalline sizes. Based on Scherrer equation, the average crystallite sizes were 27.0 and 15.8 nm for starting Ti3AlC2 and HF-etched multilayered MXene, respectively, but decreasing to 12.5 nm after reaction in aqueous TMAOH. The lateral size reduction was also verified by SEM morphology observations. All of the results are very suggestive hints that the layers may have fragmented in the treatment in aqueous TMAOH. Combining the aforementioned interlayer expansion with TMAOH intercalation, the structure would be readily broken into monolayers of smaller pieces. As expected, an ultrasonic treatment of the fragmented, TMA-intercalated phase in H2O produced a steady aqueous colloidal emulsion, which showed no noticeable precipitation even after being kept still for weeks at room temperature. The resulting colloid displayed a clear Tyndall scattering effect when irradiated with a laser beam, as indicated in the inset of Figure 2a, suggesting the presence of abundant nanosized crystallites dispersed in the aqueous medium. Information regarding the average hydrodynamic diameter of the ultrasmall sheets was retrieved from dynamic light scattering measurements, which observed a homogeneous Gaussian distribution of the particles sizes centering around 200 nm (Supporting Information, S4). A representative transmission electron microscopy (TEM) image of the freshly obtained 5


ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 19

colloid is presented in Figure 2a, which unambiguously illustrated the formation of fairly uniform ultrasmall pieces with widths ranging from 2-8 nm. The high-resolution TEM (HRTEM) image in Figure 2b manifested clear fringes in each nanocrystal, suggesting the single-crystalline feature of the obtained ultrasmall sheets. The distance between adjacent lattice fringes was elucidated to be 1.5 Å, matching with the (11) lattice spacing of an individual Ti3C2 layer. The single crystallinity was also supported by the selected-area electron diffraction (SAED) pattern acquired from one of the ultrasmall sheets (inset in Figure 2b), which exhibited individual spots instead of diffraction rings. In addition, the spots were in a hexagonal arrangement as expected for the in-plane symmetry intrinsic to Ti3C2 layers. Atomic force microscopy (AFM) images of the product, collected by dip coating a polyethylenimine-pretreated Si wafer in a fresh emulsion, and the corresponding height profile in Figure 2c revealed highly dispersed sheets on the Si substrate with a typical topographic height of ca. 1.0 nm, providing a direct and reliable evidence for the monolayer or bilayer characteristics. The average lateral width and thickness were studied with more detail in several areas and evaluated from a systematic statistical analysis performed on 200 tiny sheets from 5 different spots in the TEM and AFM characterizations (Figure 2d-e and Supporting Information, S5), giving mean values of approximately 4.0 nm and 1.0 nm, respectively. Lateral sizes of the sheets could to some extent be adjusted with synthesis parameters, for example, HF concentration and corrosion period, liquid cascade centrifugation speed, etc. If the starting Ti3AlC2 crystals were only contacted with HF of low concentrations or of limited period, by which the Al layer sandwiching between Ti3C2 sheets was still remained, TMAOH would mainly work to extract Al. In this case, TMAOH could only intercalate into the gallery with almost no fragmentation, sheets of relatively large sizes would be obtained. In contrast, when the Al layer was completely extracted with concentrated HF or extended reaction, TMAOH would fragment the host layer along with intercalation and thus sheets of relatively smaller sizes would be obtained. Meantime, with the liquid cascade centrifugation technique normally applied to colloidal dispersions, sheet sizes could be possibly selected. The detailed data will be reported in a future work. The XRD pattern of ultrasmall sheets collected by high-speed centrifugation manifested no obvious peak except for a broad halo at the low-angle area (Supporting Information, S6), 6


Page 7 of 19

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

further confirming their highly delaminated nature. Zeta-potential measurement on aqueous colloids of the ultrasmall sheets, shown in Figure 2f, gave a negative value reaching -60 mV, which suggested that the sheet surface was terminated with negative moieties, probably inheriting from the parent MXene crystals, for example, OH-, F-. Due to the surface charges and electrostatic repulsions among the nanosized particles, these ultrasmall sheets could be dispersed in a variety of solvents, including ethanol, methanol, dimethylsulfoxide, N,N-dimethylfomamide, formamide, N-methyl-2-pyrrolidone (NMP), and some others, all exhibiting excellent colloidal stability (Supporting Information, S7).

Figure 2. (a) Representative low-magnification, (b) high-resolution TEM images, and (c) tapping-mode AFM image for the as-prepared ultrasmall Ti3C2 sheets. Inset in (a): a photograph of the colloid clearly displaying the Tyndall scattering effect, which confirmed the abundant presence of small sheets; inset in (b): corresponding SAED pattern, showing individual spots in a hexagonal arrangement, as expected from the intrinsic symmetry of Ti3C2 layers; inset in (c): height profile of the ultrasmall Ti3C2 sheets. Statistical distribution of (d) lateral width and (e) thickness of the obtained ultrasmall Ti3C2 sheets. (f) Zeta potential spectrum of the colloid.

The surface compositions and chemical structure of the as-obtained ultrasmall Ti3C2 sheets were examined by X-ray photoelectron spectroscopy (XPS) and Fourier transform 7


ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 19

infrared spectroscopy (FT-IR). The survey spectrum revealed the existence of F and O in addition to Ti and C (Supporting Information, S8). In the high-resolution Ti 2p spectrum displayed in Figure 3a, no obvious trace of Ti–Al at lower energies of approximately 452 eV was observed, evidencing the removal of the Al layer while showing evident signals corresponding to Ti–C and Ti–O/F.26 The former should originate from the intrinsic nature of Ti3C2 layers, and the latter confirmed the surface termination with –O(H) and/or F. Correspondingly, the O 1s spectrum in Figure 3b could be fitted by components corresponding to O–Ti, OH–Ti, and H2O–Ti at 530.0, 531.5, and 532.8 eV, respectively,27 additionally evidencing the surface terminations of –O(H) along with strongly absorbed H2O molecules. In good consistencies, the FT-IR analysis also detected signals corresponding to – OH and Ti–O, along with Ti–C (Figure 3c).28 The conspicuous feature of Ti–C in all of the characterizations verified that the internal atomic structure of the Ti3C2 layers was almost perfectly retained from the pristine multilayered MXene crystals, and these ultrasmall sheets did not experience any chemical change or oxidization during the mild delamination and fragmentation process. It should be noticed that when the MXenes were hydrothermally treated to induce the preparation of quantum dots, it was reported that oxidation was unavoidable, and the oxidizing degree was more severe with increasing temperature.14,15 Therefore, the present approach of fragmenting host layers and weakening the interlamellar forces with TMAOH provided a mild and facile synthetic route to produce ultrasmall sheets. Stability of the obtained ultrasmall sheets against oxidizing media, for example ambient air, H2O2 etc., was studied and compared with large sheets including those prepared with milder etchants HCl+LiF25 and HF-dimethyl sulfoxide,23 from which it was surprising to see that the ultrasmall sheets manifested the highest stability (Supporting Information, S9). A recent report studied in-depth the oxidation behavior of titanium carbide sheets obtained via directly sonicating multilayered MXene,29 which found that the oxidation process was basically edge-driven and smaller sheets would be less stable. The seemingly different results may be explained by their different sheet thicknesses. The ultrasmall sheets in the present work may contain higher percentage of unilamellar materials because the synthesis process included an additional step of TMA intercalation to further weaken the inter-lamellar forces. Considering the oxidation reaction from Ti3C2O2 to TiO2 involves a structural recrystallization, 8


Page 9 of 19

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

atomic diffusion in thinner sheets is supposed to be more difficult, which may account for the unusual high stability of the ultrasmall sheets. This was also proved by the final oxidized phases, anatase/rutile TiO2 for the sheets from milder etchants, HCl+LiF and HF-dimethyl sulfoxide, but stacking aggregates for the ultrasmall unilamellar sheets. Similar phenomenon was also ever reported for titania sheets, single layer sheets exhibiting the highest stability in the diffusion rate-limiting process of thermal transformation from Ti0.87O2 to TiO2.30

Figure 3. High-resolution XPS spectra of (a) Ti 2p, (b) O 1s, and (c) FT-IR spectrum for the obtained ultrasmall Ti3C2 sheets, displaying that the intrinsic chemical structure of Ti3C2 was well maintained.

It is well-known that MAX phases have a quite large family of members with the general composition of Mn+1AXn, we following attempted to cut and delaminate some other Al-containing phases to demonstrate the general applicability of this method. Nb2AlC and Ti2AlC were chosen as examples. Possibly due to the different stability or reactivity of their in-plane bonds, the synthesis parameters, including concentration of HF or TMAOH, reaction period, etc., have to be carefully adjusted before success. The reaction intensity should be tuned to be stronger and weaker for Nb2AlC and Ti2AlC, respectively. Figures 4a-b show the representative TEM images for the finally obtained Nb2C and Ti2C. The in-plane dimensions were found to be cut into sizes of 60-75 nm and 2-5 nm for Nb2C and Ti2C, respectively. The Nb2C materials possessed relatively larger lateral sizes. Additionally reminiscent of the fact that normally more severe conditions, higher HF concentrations and extended reaction times, were required to exfoliate Nb2AlC, this should be related with the higher chemical stability for Nb-C bonds. The broad applicability of the present approach to synthesize ultrasmall sheets of diverse materials underlined the excellent general applicability and advantages of 9


ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 19

this synthesis protocol for cutting MAX phases.

Figure 4. TEM images for the product of (a) Nb2C and (b) Ti2C ultrasmall sheets, demonstrating the general applicability of this synthesis procedure.

The optical properties of the colloid containing ultrasmall Ti3C2 sheets were studied by ultraviolet-visible (UV-Vis) absorption and photoluminescence (PL) spectroscopy. The recorded UV-Vis absorption spectrum for the colloid is provided in Figure 5a, exhibiting an abrupt increasing absorption below 320 nm, which almost reached the maximum at approximately 250 nm. This spectral feature remarkably differed from that of parent MXenes or TMA-intercalated phase, in which the diffuse reflectance spectrum revealed an almost constant and featureless absorption over a wide wavelength range of 200–800 nm. Although their different detection modes made a simple and quantitative comparison difficult, the significant spectral change before and after delamination was most likely associated with the cleavage of three-dimensional stacked crystals into individual layers with a sub-nanometer thickness. Similar optical behaviors were also reported for MnO2 sheets delaminating from bulk layered manganese oxide, H0.13MnO2·H2O.31,32 The position of the absorption edge may be closely related to the lateral dimensions of the sheets due to the ubiquitous size effect, which still needs more elaborate experiments. Compared with normal-size sheets, obviously the absorption edge exhibited a slight blue shift, which has been commonly observed in many dimensionally reduced materials due to size effect (Supporting Information, S10). To exclude the possibility of the presence of carbon dots that would strongly interfere with fluorescence behavior of samples, we characterized the sample with Raman technique, which is a powerful tool to detect carbon traces. In the Raman spectrum of the ultrasmall sheets, no G or D band 10


Page 11 of 19

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

characteristic of carbonaceous materials was detected, excluding the possibility of carbon production and interference with fluorescence behaviors (Supporting Information, S11). Figure 5b depicts the dependence of absorbance at 250 nm on sheet concentrations, showing a nearly linearly function, which suggested that no possible association among the ultrasmall sheets occurred in this concentration range. Noticeably, the characteristic features in various solvents were almost the same (Supporting Information, S12), suggesting that the optical behavior originated from the ultrasmall sheet structure rather than any solvation effects. The excitation spectrum of the colloid showed a maximal luminescence at ca. 405 nm, and on excitation near 405 nm the PL spectrum manifested a broad and symmetric fluorescence peak at 509 nm, as depicted in Figure 5c. Interestingly, similar to the hydrothermally synthesized carbon or graphene quantum dots,33,34 the colloid of the so-obtained ultrasmall Ti3C2 sheets exhibited an excitation-dependent emission behavior. The phenomenon has been attributed to the optical selection of differently sized or surface defects within the sample ensemble. With the increased excitation wavelength from 340 to 500 nm, the fluorescence peaks correspondingly redshifted from 460 to 580 nm, as shown in Figure 5d (the inset displays the normalized emission spectra). While the origin of luminescence and excitation dependent PL behaviors is still under controversy and awaiting discovery,35,36 these results indicated the distinctiveness of the as-prepared ultrasmall Ti3C2 sheets, and the multiple PL colors under different excitation wavelengths are important for certain practical applications. The emission quantum yield of the ultrasmall Ti3C2 sheets was determined according to the comparative method, yielding a high value of 8.9%. Furthermore, the photoluminescence under different pH values was examined, which showed no significant change in either wavelength or intensity with increasing pH close to neutral and alkaline values beyond 6, while the intensity decreased at low pH values (pH = 2~5) (Supporting Information, S13). The possible reason for this phenomenon may be the passivation of surface terminating groups (OH- or F-) in strong acid media, providing additional evidence for the surface capping of the ultrasmall sheets.

11


ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 19

Figure 5. (a) UV-Vis spectra for colloid of ultrasmall Ti3C2 sheets at various concentrations of 0.111, 0.056, 0.037, 0.028, and 0.022 mg ml-1. The diffuse scattering spectra for MXene and TMA-reacted phase are also shown for comparison. (b) The absorbance at 245 nm plotting against concentration, showing a nearly linear manner. (c) UV-Vis absorption, excitation, and emission spectra of as-prepared ultrasmall Ti3C2 sheets. (d) The emission spectra under different excitation wavelengths from 340 to 500 nm. Inset in (d) shows the corresponding normalized emission spectra.

Conclusion In summary, a generic and mild approach for producing ultrasmall MXene sheets was developed by simultaneous intralayer cutting and interlayer delamination. Owing to the efficient but mild reactions, the intrinsic chemical structure of parent phases was well maintained in the ultrasmall sheets. For the mostly studied Ti3C2, the product was 4 nm in lateral dimensions and 1 nm in thickness on average. The attempts on extending the method to MXenes of other compositions, Nb2C and Ti2C, were also successful, although the lateral dimensions of final products seemed to be highly related with the chemical stability of MAX phases. Importantly and interestingly, the ultrasmall sheets manifested optical behavior quite similar to carbon dots, displaying strong photoluminescence and excitation-dependent 12


Page 13 of 19

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

behavior. We believe that this work can provide a versatile approach for creating diverse nanoscale materials and additionally broaden the applications of MXene materials in optical and display fields.

Experimental Section Materials and chemicals: High-purity powders of Ti3AlC2 (99.8%, 400 mesh) were purchased from Forsman Scientific (Beijing) Co., Ltd., China. HF (48-51.0%) and TMAOH (25% solution) were purchased from J&K Scientific Co., Ltd., China. KOH was supplied from Sinopharm Chemical Reagent Beijing Co., Ltd. All chemical reagents in this study were of analytical grade and were used as received without further purification. All solutions were prepared using distilled water with resistivity not less than 18.2 MΩ cm (Direct-Q UV, Millipore). Producing ultrasmall sheets: The starting crystals of multilayered MXenes were prepared following a modified previously reported procedure by treating Ti3AlC2 powder with particle size less than 38 µm in 50% aqueous HF solution for 24 h at room temperature. To remove the excess HF, the resulting suspension was thoroughly washed with deionized water until the pH of the liquid reached 5-6. The wet sediment was then reacted in 25% aqueous TMAOH for another 24 h to induce guest intercalation and host layer fragmentation, which was separated by centrifugation at 3500 rpm for 15 min. The obtained powder was dispersed in deaerated water with a sample:water weight ratio of 1:300 and then sonicated in a water bath under flowing Ar for approximately 10 h. To remove the presence of any big particles, the system was centrifuged at 5000 rpm for 30 min, and the supernatant colloid was obtained for characterization and further uses. Morphology and structural characterization: The crystallographic phases of the samples were characterized by powder X-ray diffraction technique and the patterns were recorded on a Rigaku Ultima IV diffractometer with Cu Kα radiation (λ = 0.15405 nm). The sample morphologies and dimensions were studied with a FEI/S-4700 scanning electron microscope at an accelerating voltage of 10 kV equipped with an energy dispersive X-ray spectroscopy module for elemental analyses. TEM investigations were conducted on an FEI G20 microscope with a field emission gun operated at 200 keV. The samples were prepared by 13


ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 19

dropping a diluted suspension of the sheet colloid in water on a carbon-coated copper grid. AFM images were collected on an atomic force microscope (Bruker instrument Dimension Icon) in tapping mode. Zeta-potential surface measurements of the obtained ultrasmall sheets were carried out on a ZetaPlus Zeta-potential analyzer. XPS spectra were obtained from Axis Ultra DLD equipped with an Al anode X-ray tube and helium lamp. Infrared spectra of the samples were recorded on a Varian 3100 FTIR spectrometer in the 4000-400 cm-1 range with a nominal resolution of 0.4 cm-1 using powdered samples diluted in KBr pellets. Raman spectra were measured using an excitation wavelength of 514 nm provided by a Ar laser on an XploRA laser Raman spectrometer. UV-Vis absorption measurement was carried out on a Shimadzu UV-3600 UV-VIS-NIR Spectrophotometer, and PL emission spectra were recorded on a FluoroLog-3 fluorescence spectrophotometer. The confocal imaging was conducted on a LeciaSP5 laser scanning confocal microscope. Calculation of quantum yield: The quantum yield (Φ) of the ultrasmall MXene sheets was calculated by the comparative method using rhodamine 6G dissolved in water as a reference Φs = Φr ×

based on the following equation:

Is η s 2 Ar × × Ir η r 2 As , where I, η, and A represent the

measured integrated emission intensity, refractive index of solvent, and absorption of the reference (r) and ultrasmall MXene sheets sample (s), respectively.

Acknowledgement. The authors acknowledge financial support from the National Natural Science Foundation of China (51402204 and 51772201), Thousand Young Talents Program, Jiangsu Specially-Appointed Professor Program, and a project funded by the Priority Academic Program Development (PAPD) of Jiangsu Higher Education Institutions.

Supporting Information. The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acsnano.··· TEM image of Ti3C2 sheets in aqueous TMAOH, XRD, SEM, and EDS data for as-received Ti3AlC2 crystals, starting MXene crystals, and TMA-reacted phase, XRD, DLS distribution, survey XPS spectrum, oxidation stability for the ultrasmall sheets, more TEM and AFM images, digital photos showing dispersity in other solvents and optical absorption in the 14


Page 15 of 19

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

solvents, optical absorption comparison with large sheets, and photoluminescence at various pHs

References [1] Xiao, F. X.; Pagliaro, M.; Xu, Y. J.; Liu, B. Layer-by-layer Assembly of Versatile Nanoarchitectures with Diverse Dimensionality: A New Perspective for Rational Construction of Multilayer Assemblies. Chem. Soc. Rev. 2016, 45, 3088–3121. [2] Alivisatos, A. P. Semiconductor Clusters, Nanocrystals, and Quantum Dots. Science 1996, 271, 933–937. [3] Liu, Y. H.; Zhao, J. B.; Li, Z. K.; Mu, C.; Ma, W.; Hu, H. W.; Jiang, K.; Lin, H. R.; Ade, H.; Yan, H. Aggregation and Morphology Control Enables Multiple Cases of High-efficiency Polymer Solar Cells. Nat. Commun. 2014, 5, 5293. [4] Collman, J. P. Patterns of Organometallic Reactions Related to Homogeneous Catalysis. Acc. Chem. Res. 1968, 1, 136–143.

[5] Nicolosi, V.; Chhowalla, M.; Kanatzidis, M. G.; Strano, M. S.; Coleman, J. N. Liquid Exfoliation of Layered Materials. Science 2013, 340, 1226419. [6] Samorì, P.; Palermo, V.; Feng, X. L. Chemical Approaches to 2D Materials. Adv. Mater. 2016, 28, 6027–6029. [7] Lim, S. Y.; Shen, W.; Gao, Z. Q. Carbon Quantum Dots and Their Applications. Chem. Soc. Rev. 2015, 44, 362–381.

[8] Li, X. M.; Rui, M. C.; Song, J. Z.; Shen, Z. H.; Zeng, H. B. Carbon and Graphene Quantum Dots for Optoelectronic and Energy Devices: A Review. Adv. Funct. Mater. 2015, 25, 4929–4947. [9] Carey, G. H.; Abdelhady, A. L.; Ning, Z. J.; Thon, S. M.; Bakr, O. M.; Sargent, E. H. Colloidal Quantum Dot Solar Cells. Chem. Rev. 2015, 115, 12732–12763. [10] Cullis, A. G.; Canham, L. T. Visible Light Emission Due to Quantum Size Effects in Highly Porous Crystalline Silicon. Nature 1991, 353, 335–338. [11] Cong, S.; Tian, Y. Y.; Li, Q. W.; Zhao, Z. G.; Geng, F. X. Single-Crystalline Tungsten Oxide Quantum Dots for Fast Pseudocapacitor and Electrochromic Applications. Adv. 15


ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 19

Mater. 2014, 26, 4260–4267.

[12] Nakamura, K.; Oaki, Y.; Imai, H. Monolayered Nanodots of Transition Metal Oxides. J. Am. Chem. Soc. 2013, 135, 4501–4508.

[13] Chen, Z. G.; Li, L. H.; Cong, S.; Xuan, J. N.; Zhang, D. S.; Geng, F. X.; Zhang, T.; Zhao, Z. G. Rapid Synthesis of Sub-5 nm Sized Cubic Boron Nitride Nanocrystals with High-Piezoelectric Behavior via Electrochemical Shock. Nano Lett. 2016, 17, 335–361. [14] Xue, Q.; Zhang, H. J.; Zhu, M. S.; Pei, Z. X.; Li, H. F.; Wang, Z. F.; Huang, Y.; Deng, Q. H.; Zhou, J.; Du, S. Y.; Huang, Q.; Zhi, C. Y. Photoluminescent Ti3C2 MXene Quantum Dots for Multicolor Cellular Imaging. Adv. Mater. 2017, 29, 1604847. [15] Hu, T.; Wang, J. M.; Zhang, H.; Li, Z. J.; Hu, M. M.; Wang, X. H. Vibrational Properties of Ti3C2 and Ti3C2T2 (T = O, F, OH) Monosheets by First-Principles Calculations: A Comparative Study. Phys. Chem. Chem. Phy. 2015, 17, 9997–10003. [16] Naguib, M.; Kurtoglu, M.; Presser, V.; Lu, J.; Niu, J. J.; Heon, M.; Hultman, L.; Gogotsi, Y.; Barsoum, M. W. Two-Dimensional Nanocrystals Produced by Exfoliation of Ti3AlC2. Adv. Mater. 2011, 23, 4248–4253.

[17] Naguib, M.; Mochalin, V. N.; Barsoum, M. W.; Gogotsi, Y. MXenes: A New Family of Two-Dimensional Materials. Adv. Mater. 2014, 26, 992–1005. [18] Anasori, B.; Lukatskaya, M. R.; Gogotsi, Y. 2D Metal Carbides and Nitrides (MXenes) for Energy Storage. Nat. Rev. Mater. 2017, 2, 16098. [19] Xuan, J. N.; Wang, Z. Q.; Chen, Y. Y.; Liang, D. J.; Cheng, L.; Yang, X. J.; Liu, Z.; Ma, R. Z.; Sasaki, T.; Geng, F. X. Organic-Base-Driven Intercalation and Delamination for the Production of Functionalized Titanium Carbide Nanosheets with Superior Photothermal Therapeutic Performance. Angew. Chem. Int. Ed. 2016, 55, 14569–14574. [20] Zhou, J.; Zha, X. H.; Chen, F. Y.; Ye, Q.; Eklund, P.; Du, S. Y.; Huang, Q. A Two-Dimensional Zirconium Carbide by Selective Etching of Al3C3 from Nanolaminated Zr3Al3C5. Angew. Chem. Int. Ed. 2016, 55, 5008–2013. [21] Lin, H.; Wang, X.; Yu, L.; Chen, Y.; Shi, J. Two-Dimensional Ultrathin MXene Ceramic Nanosheets for Photothermal Conversion. Nano Lett. 2017, 17, 384–391. [22] Dai, C.; Lin, H.; Xu, G.; Liu, Z.; Wu, R.; Chen, Y. Biocompatible 2D Titanium Carbide (MXenes) Composite Nanosheets for pH-Responsive MRI-Guided Tumor Hyperthermia. 16


Page 17 of 19

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Chem. Mater. 2017, 29, 8637–8652.

[23] Mashtalir, O.; Naguib, M.; Mochalin, V. N.; Dall'Agnese, Y.; Heon, M.; Barsoum, M. W.; Gogotsi, Y. Intercalation and Delamination of Layered Carbides and Carbonitrides. Nat. Commun. 2013, 4, 1716.

[24] Liu, W. H.; Wang, Z. Q.; Su, Y. L.; Li, Q. W.; Zhao, Z. G.; Geng, F. X. Molecularly Stacking Manganese Dioxide/Titanium Carbide Sheets to Produce Highly Flexible and Conductive Film Electrodes with Improved Pseudocapacitive Performances. Adv. Energy Mater. 2017, DOI: 10.1002/aenm.201602834.

[25] Ghidiu, M.; Lukatskaya, M. R.; Zhao, M. Q.; Gogotsi, Y.; Barsoum, M. W. Conductive Two-Dimensional Titanium Carbide 'Clay' with High Volumetric Capacitance. Nature 2014, 516, 78–81. [26] Halim, J.; Cook, K. M.; Naguib, M.; Eklund, P.; Gogotsi, Y.; Rosen, J.; Barsoum, M. W. X-ray Photoelectron Spectroscopy of Select Multi-layered Transition Metal Carbides (MXenes). Appl. Surf. Sci. 2016, 362, 406–417. [27] Halim, J.; Kota, S.; Lukatskaya, M. R.; Naguib, M.; Zhao, M.Q.; Moon, E. J.; Pitock, J.; Nanda, J.; May, S. J.; Gogotsi, Y.; Barsoum, M. W. Synthesis and Characterization of 2D Molybdenum Carbide (MXene). Adv. Funct. Mater. 2016, 26, 3118–3127. [28] Satheeshkumar, E.; Makaryan, T.;Melikyan, A.; Minassian, H.; Gogotsi, Y.; Yoshimura, M. One-step Solution Processing of Ag, Au and Pd@MXene Hybrids for SERS. Sci. Rep. 2016, 6, 32049. [29] Zhang, C. J.; Pinilla, S.; Mc Evoy, N.; Cullen, C. P.; Anasori, B.; Long, E.; Park, S.-H.; Seral-Ascaso, A.; Shmeliov, A.; Krishnan, D.; Morant, C.; Liu, X.; Duesberg, G. S.; Gogotsi, Y.; Nicolosi V. Oxidation Stability of Colloidal Two-Dimensional Titanium Carbides (MXenes). Chem. Mater. 2017, 29, 4848–4856. [30] Fukuda, K.; Ebina, Y.; Shibata, T.; Aizawa, T.; Nakai, I.; Sasaki, T. Unusual Crystallization Behaviors of Anatase Nanocrystallites from a Molecularly Thin Titania Nanosheet and its Stacked Forms: Increase in Nucleation Temperature and Oriented Growth. J. Am. Chem. Soc. 2007, 129, 202–209. [31] Omomo, Y.; Sasaki, T.; Wang, L. Z.; Watanabe, M. Redoxable Nanosheet Crystallites of MnO2 Derived via Delamination of a Layered Manganese Oxide. J. Am. Chem. Soc. 17


ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 19

2003, 125, 3568–3575. [32] Liu, Z. P.; Ma, R. Z.; Ebina, Y.; Takada, K.; Sasaki, T. Synthesis and Delamination of Layered Manganese Oxide Nanobelts. Chem. Mater. 2007, 19, 6504–6512. [33] Zheng, X. T.; Ananthanarayanan, A.; Luo, K. Q.; Chen, P. Glowing Graphene Quantum Dots and Carbon Dots: Properties, Syntheses, and Biological Applications. Small 2015, 11, 1620–1636.

[34] Hu, S. L.; Trinchi, A.; Atkin, P.; Cole, I. Tunable Photoluminescence Across the Entire Visible Spectrum from Carbon Dots Excited by White Light. Angew. Chem. Int. Ed. 2015, 54, 2970–2974.

[35] Cui, Q. L.; Xu, J. S.; Wang, X. Y.; Li, L. D.; Antonietti, M.; Shalom, M. Phenyl-Modified Carbon Nitride Quantum Dots with Distinct Photoluminescence Behavior. Angew. Chem. Int. Ed. 2016, 55, 3672–3676.

[36] Song, Z. P.; Lin, T. R.; Lin, L. H.; Lin, S.; Fu, F. F.; Wang, X. C.; Guo, L. Q. Invisible Security Ink Based on Water-Soluble Graphitic Carbon Nitride Quantum Dots. Angew. Chem. Int. Ed. 2016, 55, 2773–2777.

18


Page 19 of 19

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Table of Contents Graphic