Visual Understanding of Light Absorption and ... - ACS Publications

Aug 21, 2017 - Bio-Nanotechnology and Nanomedicine Laboratory, Department of Chemistry & Nano-Science Center, University of Copenhagen,. Universitetsp...
2 downloads 8 Views 1MB Size
Subscriber access provided by UNIVERSITY OF ADELAIDE LIBRARIES

Article

Visual Understanding of Light Absorption and Waveguiding in Standing Nanowires with 3D fluorescence confocal microscopy Rune Frederiksen, Gözde Tütüncüoglu, Federico Matteini, Karen L. Martinez, Anna Fontcuberta i Morral, and Esther Alarcon Llado ACS Photonics, Just Accepted Manuscript • DOI: 10.1021/acsphotonics.7b00434 • Publication Date (Web): 21 Aug 2017 Downloaded from http://pubs.acs.org on August 23, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Photonics is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 18

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Photonics

1

Visual Understanding of Light Absorption and Waveguiding in

2

Standing Nanowires with 3D fluorescence confocal microscopy

3 4 5 6 7 8 9 10 11

Rune Frederiksen,1 Gozde Tutuncuoglu,2 Federico Matteini,2 Karen L. Martinez,1 Anna Fontcuberta i Morral,2

12

Abstract

13

Semiconductor nanowires are promising building blocks for next generation photonics. Indirect proofs of

14

large absorption cross-sections have been reported in nano-structures with sub-wavelength diameters, an

15

effect that is even more prominent in vertically standing nanowires. In this work we provide a 3-

16

dimensional map of the light around vertical GaAs nanowires standing on a substrate by using

17

fluorescence confocal microscopy, where the strong long-range disruption of the light path along the

18

nanowire is illustrated. We find that the actual long distance perturbation is much larger in size than

19

calculated extinction cross-sections. While the size of the perturbation remains similar, the intensity of the

20

interaction changes dramatically over the visible spectrum. Numerical simulations allow us to distinguish

21

the effects of scattering and absorption in the nanowire leading to these phenomena. This work provides a

22

visual understanding of light absorption in semiconductor nanowire structures, which is of high interest

23

for solar energy conversion applications.

Esther Alarcon-Llado2,3* 1

Bio-Nanotechnology and Nanomedicine Laboratory, Department of Chemistry & Nano-Science Center, University of Copenhagen, Universitetsparken 5, DK-2100 Copenhagen, Denmark

2

Laboratory of Semiconductor Materials, Institute of Materials, School of Engineering, EPFL, 1015 Lausanne,

Switzerland 3

Center for Nanophotonics, AMOLF, Science Park 104, 1098XG Amsterdam, Netherlands

*Corresponding Author: [email protected]

24 25 26

Keywords: semiconductor nanowire, optical properties, solar energy, confocal microscopy

1 ACS Paragon Plus Environment

ACS Photonics

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

Page 2 of 18

TOC Graphic

2 3

2 ACS Paragon Plus Environment

Page 3 of 18

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Photonics

1

Since the discovery of photonic properties of dielectric nanostructures,1–7 their great potential for solar

2

applications at lower cost has been unravelled.8–18 Nanowire (NW) ensembles constitute a new class of

3

metamaterial, where the optical properties cannot be directly deduced from individual parts.19–22 Optical

4

properties of NW arrays are tuned by the individual NW type, geometry and collective arrangement,

5

which provide a new playground in solar energy conversion and the solid-state lighting arenas.23–32 The

6

effective absorption cross-section in vertically standing nanowires can be much larger than the

7

geometrical one.6,8,33 This large absorption cannot be explained by standard Mie-like resonance

8

formulism, as in the case of horizontally lying structures.34,35 Assessing the absorption cross-section in

9

vertical structures is not straightforward and it is important to understand how light is interacting with

10

nanostructures and essential for the accurate quantum efficiency determination in photodevices. Many

11

approaches have been shown to measure the optical local density of states in and around photonic and

12

plasmonic structures, which include cathodoluminescence tomography,36 near-field optical probe

13

techniques, single molecules attached to an AFM tip37,38 or fluorescent solutions probed with super-

14

resolution microscopes39–41, among others. Although complex computational work has shown that super-

15

resolution microscopy can be used to scan in all three dimensions,42 no studies have shown 3D imaging of

16

local density of states at microscale surroundings of photonic nano-structures.

17

In this work, we are interested in the 3D visualization of long-range light-matter interactions in GaAs

18

standing nanowires, in particular within the region of large absorption. To this end, we use a simple

19

confocal microscope set-up. The reconstructed fluorescence image captures the evolution of light

20

extinction around the nanowire and along its length. By combining the experiments with electromagnetic

21

simulations, we elucidate the mechanisms behind self-concentrating light effects and large absorption

22

cross-sections found in semiconductor nanowires and their relation to the nanowire waveguiding

23

properties. While the resolution is diffraction limited, we show that this method provides insightful 3D

24

extinction maps around nanostructures, which can be an asset to characterize more complex

25

morphologies.

26

To demonstrate the power of the technique we probe gallium arsenide (GaAs) nanowires vertically

27

standing on a silicon (Si) substrate. GaAs is a compound semiconductor with a direct bandgap of 1.42 eV,

28

which makes it an excellent candidate for solar energy applications.

29

Figure 1a illustrates the experimental set-up that provides a 3-dimensional mapping of light distribution

30

around nanostructures. The sample is embedded in a liquid solution with suspended fluorescent dye

31

molecules (see supplementary information S1 for more details). The dye fluorescence intensities are

32

mapped around the nanowires with a laser scanning confocal microscope. Dye molecules are excited with

3 ACS Paragon Plus Environment

ACS Photonics

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 18

1

a laser beam focused with a confocal microscope objective and the emitted light is collected through the

2

same objective and detected with a photomultiplier (PMT). The physical principle of this characterization

3

method resides in the fluorescence intensity of the molecules being proportional to the local excitation

4

light intensity. Thus, by scanning the laser beam over an x-y area for a number of z-stacks, a diffraction-

5

limited resolution 3D map of the light intensity is obtained. The x-y and z optical resolution in our

6

experiments are specified in the Supplementary Information.

7

An example of a reconstructed 3D image of light around GaAs nanowires when illuminated with blue

8

laser light is shown in Figure 1b. In this case, two vertical GaAs nanowires (10 µm long, 126 nm in

9

diameter and 2.5 µm apart) stand vertically on a Si substrate. The sample is excited with blue light

10

(λ=488 nm), for which theory predicts that it should not have the strongest interaction with these

11

nanostructures (see Supplementary Information on the absorption spectrum of single nanowire). The

12

represented grey transparency in the image is linked to the amount of detected light, so that the darkest

13

areas in the image indicate positions where no light is detected. As a consequence, the substrate appears

14

dark. Under these conditions, also two dark columns stand at the position of the nanowires and a dark

15

layer where the silicon substrate starts, in accordance to the lack of fluorophores in that volume.

16

Interestingly, a semi-transparent conical region surrounds the nanowires, and widens up to several

17

microns when approaching the nanowires’ bottom. The y-z cross-section intensity contour plot of the

18

same image (Figure 1c) provides a more quantitative representation of the conical “shadow”. These

19

pictures represent a clear visual image of how the nanowire pair is capable of redistributing the

20

electromagnetic field around them at a long-range distance. It is clear from this picture that there is less

21

light arriving at the silicon substrate surface due to the presence of the nanowires. It is interesting to note

22

both the dimension and the magnitude of the shaded silicon surface. A better understanding of how light

23

is redistributed around the nanowires is discussed later on. First, to confirm and proof that our

24

experimental set-up is truly representing the light intensity distribution around the nanowires of the

25

incoming laser, FDTD simulations were performed. The steady-state field energy distribution was

26

simulated by considering an incoming plane wave propagating in the -z direction and same wavelength as

27

in the experiment (λ=488 nm). Due to the asymmetry of the nanowire pair, two sets of simulations were

28

performed for light polarized in the x and y axes, respectively. The resulting intensity maps were averaged

29

to obtain the final distribution map. Figure 1d displays the line profiles of the calculated electric field

30

intensity squared superimposed to the fluorescence light intensity at 1.2 and 7.5um below the nanowires

31

tip. The calculated field energy distributions are in remarkable agreement with the detected light

32

distribution from the confocal images. This result confirms that the observed confocal images are indeed

33

an excellent representation of the interaction between a vertically-impinging plane wave and the 4 ACS Paragon Plus Environment

Page 5 of 18

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Photonics

1

nanostructures, which can span up to several micrometers in distance. Such good agreement also rules out

2

that the confocal image is strongly perturbed by the possible interactions between fluorophore emission

3

and the nanostructures. In fact, light emitted by the fluorophores is only perturbed when very close to the

4

nanowire surface (