Subscriber access provided by YORK UNIV

Article

X-Ray Lithography on Perovskite Nanocrystals Films: From Patterning with Anion-Exchange Reactions to Enhanced Stability in Air and Water Francisco Palazon, Quinten A Akkerman, Mirko Prato, and Liberato Manna ACS Nano, Just Accepted Manuscript • DOI: 10.1021/acsnano.5b06536 • Publication Date (Web): 30 Nov 2015 Downloaded from http://pubs.acs.org on November 30, 2015

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Nano is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 20

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

X-Ray Lithography on Perovskite Nanocrystals Films: From Patterning with Anion-Exchange Reactions to Enhanced Stability in Air and Water Francisco Palazon, Quinten A. Akkerman, Mirko Prato,* and Liberato Manna* Nanochemistry Department, Istituto Italiano di Tecnologia, Via Morego 30, 16163 Genova, Italy * Address correspondence to [email protected] [email protected]

ABSTRACT. Films of colloidal CsPbX3 (X=I, Br or Cl) nanocrystals, prepared by solution drop-casting or spin coating on a silicon substrate, were exposed to low flux X-rays from an Xray photoelectron spectrometer source, causing inter-molecular C=C bonding of the organic ligands that coat the surface of the nanocrystals. This transformation of the ligand shell resulted in a greater stability of the film, which translated into the following features: (i) insolubility of the exposed regions in organic solvents which caused instead complete dissolution of the unexposed regions. This enabled the fabrication of stable and strongly fluorescent patterns over millimeter scale areas; (ii) inhibition of the irradiated regions towards halide anion exchange reactions, when the films were exposed either to halide anions in solution or to hydrohalic

ACS Paragon Plus Environment

1

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 20

vapors. This feature was exploited to create patterned regions of different CsPbIxBryClz compositions, starting from a film with homogenous CsPbX3 composition; (iii) resistance of the films to degradation caused by exposure to air and moisture, which represents one of the major drawbacks for the integration of these materials in devices; (iv) stability of the film in water and biological buffer, which can open interesting perspectives for applications of halide perovskite nanocrystals in aqueous environments.

KEYWORDS: Perovskite, nanocrystals, X-ray, anion-exchange, patterning

Lead halide perovskites are currently the focus of a considerable research effort, owing to their important optoelectronic and photovoltaic properties.1-16 Also, various colloidal synthesis routes towards nanocrystals (NCs) of these materials have been recently demonstrated, with control over size, shape, mixed halide composition and consequently over emission wavelength.17 Furthermore, it has been shown that these materials, both in bulk and in nanocrystalline form, can undergo fast anion-exchange, with a fine tuning of the chemical composition and therefore of their photoluminescence properties.18-24 In principle, these perovskite NCs may find applications in light emitting devices and as labeling agents, provided that issues with stability and toxicity are solved, whereas applications in solar cells in general require organic-free perovskite films in order to achieve electrical conductivity.25-26 Recent reports nonetheless suggest that even for bulk perovskite films the incorporation of organic molecules can help cross-linking the crystal grains and hence enhance film stability.27-28 The reactivity of halide perovskites (both as bulk films and as NCs) towards agents such as air/moisture, their rapid dissolution in aqueous solutions, and the change in their optical

ACS Paragon Plus Environment

2

Page 3 of 20

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

properties in the presence of external halogen species (due to fast anion exchange), severely limit both their applications and the study of their properties under conditions that would degrade them. Colloidally synthesized NCs come equipped with a ligand shell of organic surfactants that, if properly transformed by irradiation by electrons or by X-rays from a synchrotron light source (as we demonstrated recently)29 can potentially represent an effective barrier towards degradation by a diverse range of agents. We demonstrate here that irradiation by a low flux of X-rays (1011 photons/mm2·s), which can be easily provided by a common laboratory X-ray photoelectron spectrometer source, can also induce a change in the hybridization state of carbon (sp3 to sp2) of the ligand shell in films of halide perovskite NCs deposited on a substrate, with the formation of intermolecular C=C bonding between adjacent ligands (see Scheme 1).

Scheme 1: Schematic representation of the irradiation-induced graphitization process. Perovskite NCs (green cubes) deposited on a silicon substrate are capped with oleylamine (red dot = NH2) and oleic acid (red dot = COOH) ligands. Intermolecular C=C bonding appears as a consequence of irradiation, linking adjacent NCs in the film.

ACS Paragon Plus Environment

3

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 20

This enhances the film stability in several manners. First, such “graphitization” creates a network of NCs interconnected with each other and renders the exposed regions insoluble in solvents that are able to disperse the starting “as synthesized” NCs. It is therefore easy to “lift-off” the nonexposed regions, as they remain soluble, such that luminescent patterns extending over millimetric areas can be fabricated easily. Second, the irradiated regions become refractory to anion exchange reactions when exposed to either liquid or gaseous halide precursors, whereas the non-irradiated regions exchange rapidly the anions, as reported by various groups (including ours).18-21 This makes it possible to “draw” regions of CsPbIxBryClz with varying x, y and z stoichiometries starting from a single CsPbX3 film, which may be exploited to elicit broadband photoluminescence from a suitably patterned film. Furthermore, the irradiated regions exhibit good resistance towards ageing in air, water and even in a biological buffer (phosphate buffer saline, PBS 1X). Such stability is currently one of the most sought-after aspects concerning these materials.25,30-33

RESULTS AND DISCUSSION In the present work, cesium lead halide NCs, synthesized as previously described18 (procedure adapted from Protesescu et al.)17, were deposited on a silicon substrate either by drop casting or spin-coating and were then inserted in a X-ray photoelectron spectrometer, where they were irradiated with X-rays from the monochromatic Al Kα source of the spectrometer (photon energy = 1486.6 eV). At the same time, we monitored the chemical changes in the ligand shell that took place while irradiating the film by in-situ X-ray photoelectron spectroscopy (XPS). As can be seen from Figure 1a, upon irradiation over several hours (up to 2 days) the C1s peak shifted to lower binding energies (BE) and broadened, while the so-called D-parameter,34 which

ACS Paragon Plus Environment

4

Page 5 of 20

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

is extracted from the derivative curve of the C KLL peak, increased to 16.4 eV from 12.3 eV of the starting, non-irradiated film (Figure 1b). This parameter is sensible to the sp2/sp3 carbon hybridization ratio, with higher values of the D-parameter corresponding to a higher fraction of sp2 carbon.34 According to published calibration curves,34 this change corresponds to the transformation from roughly all-sp3 hybridization (consistent with a layer of oleylamine/oleic acid molecules capping the pristine particles) to a 50% sp2 hybridization. This partial graphitization can be assigned to the loss of hydrogen and the formation of intra- and intermolecular C=C bonds, induced by X-ray irradiation (see Scheme 1 for a schematic view of the graphitization process). It is reasonable to think that the electrons generated by the interaction of the primary X-ray beam with the sample are causing the transformation rather than (or in combination with) the X-rays themselves. Indeed, primary and secondary electrons have already been reported to induce transformations in thin organic self-assembled monolayers.35-36 Furthermore we observed a similar effect upon exposure to electron beams on these NCs (see Figure S1 of the supporting information) as well as on NCs of other inorganic materials but coated with the same ligand shell as the one studied here.29

ACS Paragon Plus Environment

5

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 20

Figure 1. XPS (a-c) and XRD (d) characterization of pristine and irradiated CsPbBr3 NC films. C 1s (a) and first derivative of C KLL (b) XPS spectra corroborating the partial transformation from sp3 to sp2 hybridization state of carbon. These changes can be ascribed to the breaking of C-H bonds and formation of C=C bonds, with consequent cross-linking of the ligands at the surface of the NCs. Wide XPS scans (c; see Table S1 in supporting information for a more complete assignment of XPS peaks) and XRD patterns (d) show that the chemical composition and the crystallinity of the particles are maintained.

Partial ligand transformation was observed already after 30 min of irradiation with a 2.4 × 1011 photons/mm2·s X-ray flux. Therefore, in the experiments that follow, typical irradiation times were between 30 min and 5 h. It must be noted that, since the X-ray intensity profile on the sample has a Gaussian distribution,37 the area affected by the irradiation becomes larger with

ACS Paragon Plus Environment

6

Page 7 of 20

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

increasing irradiation time, as regions far from the spot center (> 1-2 mm) may receive a high enough dose even at low flux. This range of irradiation times proved enough for the stabilization of the film. At the same time, X-ray irradiation under vacuum did not lead to noticeable changes in the chemical composition of the film (see Figure 1c) or in the crystalline structure of the particles’ cores, as demonstrated by X-ray diffraction (XRD, see Figure 1d). Also, irradiation with X-rays under the higher vacuum conditions of the XPS setup does not lead to the deposition of any additional carbon layer, which may be the case when the irradiation is performed with electron beam lithography. Interestingly, the regions of the NCs films irradiated by X-rays became insoluble in toluene, while the non-exposed regions could be easily lifted-off from the substrate in a process similar to that presented by Nandwana et al.38 and by others.39-41 We used this property to demonstrate large-scale patterning of a CsPbBr3 NCs film. A 3 mm copper grid with a honeycomb network of 150 µm hexagonal apertures was used as stencil mask during the irradiation of the film. The mask was then removed and the whole film was rinsed in toluene (see Figure 2a for a schematic representation of the process). Scanning electron microscopy (SEM), confocal photoluminescence (PL) imaging and XPS chemical mapping of the bromine 3d peak corroborated the selective etching of the film only at the non-irradiated regions between the hexagons (see Figure 2b-d). Similar results could be obtained with an e-beam (see Figure S1), although for the reasons mentioned above e-beam lithography was not investigated further in this work.

ACS Paragon Plus Environment

7

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 20

Figure 2. (a) Schematic representation of X-ray lithography for perovskite NC film patterning (see Scheme 1 for additional details). The stencil mask is a 3 mm honeycomb copper grid. Confocal PL microscopy (b; 515 nm emission), SEM (c), and XPS (d; Br 3d intensity mapping at BE = 68 eV) demonstrating selective stabilization of the CsPbBr3 NCs in the exposed regions corresponding to the hexagonal apertures of the stencil mask. Scale bars are 300 µm.

The dose of X-ray irradiation on the NC films regulated the extent to which the films could engage in anion exchange reactions. As an example, a “mild” dose (i.e. 30 min at 1011 photons/mm2·s) was enough to modify the ligand shell so that the irradiated regions could not be dissolved by dipping the whole sample in toluene, while at the same time the ligand shell remained permeable enough to enable anion exchange. Higher doses (achieved by a few hours

ACS Paragon Plus Environment

8

Page 9 of 20

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

exposure at same photon flux) could then block the exchange. Starting from a CsPbBr3 NC film, using a long masked irradiation followed by a short “flood” (maskless) exposure of the whole film and then by immersion of the sample in a iodine precursor (I-OLAM) solution in toluene,18 we could fabricate patterns of bromide-rich (unexchanged) and iodide-rich (exchanged) regions, as shown in Figure 3a-b. This methodology has two drawbacks: it requires two irradiation steps (masked and unmasked), which makes the process elaborate, and additionally the flood irradiation can cause some undesired anion exchange inhibition.

Figure 3. Photoluminescence (PL) microscopy image (a) and XPS chemical mapping of iodine (orange) and bromine (green) (b) on a CsPbBr3/CsPbI3 NC patterned film, prepared from an initial CsPbBr3 NC film by a sequence of two irradiation sessions (masked irradiation at high

ACS Paragon Plus Environment

9

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 20

dose to inhibit anion-exchange on selected regions followed by unmasked irradiation at low dose to prevent dissolution of the film in toluene). The hexagonal areas remained indeed Br rich, while the stripe regions between the hexagons became I rich. (c-d)PL microscopy images recorded by integrating in a wavelength range from 410 to 500 nm (c) and from 500 to 600 nm (d) on a patterned CsPbBr3/CsPbCl3 NC film by single masked irradiation and followed by anion-exchange (Br  Cl) using HCl vapors as source of Cl- ions. PL microscopy image (e) and emission spectra of different regions of interest (f) on a film of CsPbI3 NCs after having undergone sequential irradiations and anion-exchange with HBr and HCl. Due to the deposition technique (drop-casting) the film had high roughness. Since the image was acquired with a confocal microscope, the appearance of dark spots on the image is due to out-of-focus regions that were cut-out by the pinhole setup. Scale bars are 300 µm.

In order to circumvent these issues, we carried out anion exchange by exposing the NC films to hydrohalic vapors, as this procedure avoids the intermediate unmasked irradiation step. Films of CsPbBr3 could be converted to CsPbCl3 and then converted back to their original composition simply by placing the film a few mm above a vial of HCl or HBr for less than a minute (see Figure S2 and supporting video). Thus, as the stability of the film was no more an issue in this case, we could easily fabricate patterns of different compositions after a single masked irradiation, followed by anion exchange with gaseous reagents (see Figure 3c-d). Eventually, starting from a red-emitting CsPbI3 film it was also possible to obtain a gradient of different colors after subsequent irradiations and anion-exchanges with HBr and HCl, resulting in a film with broadband photoluminescence between 500 and 700 nm (see Figure 3e-f). In this case, no stencil mask was applied. However, as the X-ray spot on the surface has an uneven intensity

ACS Paragon Plus Environment

10

Page 11 of 20

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

distribution, a “gradient of anion-exchange inhibition” could be obtained from a single exposure (see Figure S3 for more details on the dose-dependent anion exchange inhibition from a single irradiation). It must be noted that long exposures to X-rays (5 hours with a flux of 2.4 × 1011 photons/mm2·s in case of the sample shown in Figure 4) could lead to a loss of photoluminescence on the central region of the irradiated spot (maximum dose). This deleterious effect does not appear to be related to any specific lability of halide perovskites, since we observed the same behavior on giant shell CdSe/CdS NCs,42 which are systems that have a documented photostability (see Figure S4). Furthermore, we could not detect any changes in chemical composition, crystallinity (Figure 1 and S5) or film morphology (Figure S5 and S6) in the regions that suffered such loss in photoluminescence. Therefore, we can only speculate that the prolonged exposure to “high” X-ray flux is likely inducing the formation of trap states which lead to non-radiative recombination. On the other hand, it is clear that at lower doses (which is the case either for regions further away from the center of irradiation – see Figure 4 - or for samples at shorter irradiation times – see Figures S4 and S7) the photoluminescence was preserved. From a practical point of view, it is plausible that a less-focused X-ray source could lead to a more homogeneous stabilization (i.e., prevention from redispersion or anion-exchange, while conserving the photoluminescence properties) over larger areas. While recent reports have stressed the instability of lead triiodide perovskites, especially towards moisture,25,30-32 we demonstrate here that the same sample of irradiated NCs remained stable after several weeks in air (room temperature, ambient humidity), then after one day in ultrapure MilliQ water and then finally after three days in a biological buffer (PBS 1X). This is striking contrast to the rapid degradation of the same crystals deposited on the same conditions,

ACS Paragon Plus Environment

11

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 20

but not irradiated (or irradiated at lower dose, see Figure 4). At the end of the ageing procedure, the irradiated sample was rinsed with ultrapure water to remove deposited salts from the PBS solution and the PL spectrum was recorded (see Figure S7): the emission peak from this sample was still at around 670 nm, consistent with the spectral position of the pristine CsPbI3 NC sample.

Figure 4. Photographs of CsPbI3 NC films (ca. 5x5 mm) under UV lamp. Films irradiated at low dose (1h or less) are completely degraded after 5 days exposed to air (room temperature and ambient humidity) and were therefore not immersed in water or biological buffer. Instead, sample irradiated for 5h retains its PL properties in air, water and PBS 1X

CONCLUSION We have demonstrated how low flux X-ray irradiation can greatly enhance the stability of cesium lead halide NC films by inducing the formation of C=C bonds between the organic

ACS Paragon Plus Environment

12

Page 13 of 20

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

ligands present at the NC surfaces. This enhanced stability can be useful for a number of applications. It was shown that PL patterns of one or several colors could be easily obtained either by redispersion of non-irradiated areas or by selective anion-exchange using either liquid or gaseous reagents. Furthermore, we demonstrated that irradiated cesium lead triiodide films could be remarkably protected from degradation when exposed to air, moisture, pure water and even biologic buffers. This stability is especially promising for further exploitation of these NCs to different fields, including applications in aqueous environments. Although these films may not be suitable as such for applications where electrical conductivity is needed (due to their high organic content), great promise is coming from hybrid approaches incorporating organic molecules to organic-free films.27-28 X-ray induced stabilization could also play a key role in the development of these approaches.

METHODS Materials. Lead(II) bromide (PbBr2, 99.999% trace metals basis), lead(II) Iodide (PbI2, 99.999% trace metals basis), cesium carbonate (Cs2CO3, reagentPlus, 99%), iodine (I2, 99.99%), hydrochloric acid (HCl, ACS reagent, ≥ 37%), hydriodic acid (HI, 57wt.% in H2O), hydrobromic acid (HBr, 48 wt. % in H2O, ≥99.99%), octadecene (ODE, technical grade, 90%), oleylamine (OLAM, 70%) and oleic acid (OA, 90%), were purchased from Sigma-Aldrich. Toluene (TOL, anhydrous, 99.8%) was bought from Carlo Erba reagents. All chemicals were used without any further purification, except for OLAM, OA, and ODE, which were degassed at 100 °C for 2 h in vacuum. CsPbX3 nanocrystals and OLAM-I synthesis. CsPbBr3 and CsPbI3 NCs were synthesized as described by Protesescu et al.,17 with some minor adaptations. In a typical synthesis, 69 mg of

ACS Paragon Plus Environment

13

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 20

PbBr2 (0.188 mmol) or 87 mg of PbI2, 5 mL ODE, 0.5 ml OA and 0.5 mL OLAM were loaded in a 25 mL 3-neck flask and dried under vacuum for 1 h at 120 °C. After degassing, the temperature was raised to 165 °C and a 0.6 mL ODE with 0.4 mL of previously synthesized Cs-Oleate (0.4 g Cs2CO3 degassed in 15 mL ODE and 1.75 mL OA at 150 °C) mixture was swiftly injected. Immediately after the injection, the NC solution was quickly cooled down to room temperature with an ice bath, and the NCs were transferred to a glovebox. The OLAM-I precursor was prepared by reacting 0.5 mmol of I2 (1 mmol I-) with 0.250 mL OLAM overnight. The solid OLAM-I was dissolved in 5.75 mL TOL. Film deposition. Nanocrystals were deposited either by spin-coating or drop-casting onto piranha-cleaned silicon wafers. Typically 1 mL of CsPbX3 solution in ODE was centrifuged for 10 min at 14000 rpm, the supernatant was removed and the particles were redispersed in 100 µL toluene. For spin-coating, 20 µL of solution was dropped on the substrate which was then spinned at 2500 rpm for 40 seconds. X-ray irradiation. Nanocrystal films were irradiated in vacuum with the AlKα monochromatic source of the X-ray Photoelectron Spectrometer (photon energy = 1486.6 eV) with an emission current of 10 mA or 20 mA, corresponding to photon fluxes of 1.2 x 1011 photons/mm2·s or 2.4 x 1011 photons/mm2·s. E-beam lithography. CsPbBr3 nanocrystal films were irradiated by an electron beam from a Raith 150-two lithography system with an acceleration voltage of 10kV and exposure dose of 1 mC/cm2. Anion-exchange. Br I anion-exchange was performed in toluene by immersing the sample film in a 0.17 M solution of OLAM-I precursor for 5 min, followed by rinsing with fresh toluene and drying under a stream of nitrogen. Br  Cl, I Br, and I  Br  Cl exchanges were

ACS Paragon Plus Environment

14

Page 15 of 20

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

performed from the gas phase simply by holding the sample (film) a few mm on top of a vial of hydrobromic or hydrochloric acid for ca. 30 seconds. XPS characterization. XPS characterization was performed using a Kratos Axis Ultra DLD spectrometer with a monochromatic Al Kα source (15 kV, 20 mA). Wide scans were acquired at an analyzer pass energy of 160 eV. High resolution narrow scans were performed at a pass energy of 20 eV and steps of 0.1 eV. The photoelectrons were detected at a takeoff angle Φ =0° with respect to the surface normal. The pressure in the analysis chamber was maintained below 5 × 10−9 Torr for data acquisition. The data were converted to VAMAS format and processed using CasaXPS software. For the monitoring of the carbon graphitization, films were deposited on a gold substrate and the binding energy scale was referenced to the Au 4f7/2 peak (BE = 84.0 eV). SEM characterization. SEM images were recorded using a JEOL JSM- 7500F (JEOL, Tokyo, Japan) equipped with a cold field emission gun (FEG), operating at 10 kV acceleration voltage. PL microscopy. Confocal PL microscopy images and spectra were recorded with a Nikon A1 microscope with a laser excitation of 405 nm or 488 nm. XRD. XRD analysis was performed on a PANalytical Empyrean X-ray diffractometer equipped with a 1.8 kW Cu Kα ceramic X-ray tube and PIXcel3D 2 × 2 area detector, and operating at 45 kV and 40mA. The diffraction patterns were collected in air at room temperature using parallel-beam (PB) geometry and symmetric reflection mode. XRD data analysis was carried out using HighScore 4.1 software from PANalytical Conflict of interest: The authors declare no competing financial interest.

Acknowledgement: The research leading to these results has received funding from the 7th European Community Framework Programme under grant agreement no. 614897 (ERC

ACS Paragon Plus Environment

15

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 20

Consolidator Grant “TRANS-NANO”). We thank A. Toma for help with e-beam lithography, S. Marras for XRD measurements, S. Dogan and A. Scarpellini for SEM characterization.

Supporting information available: Table of main XPS peaks found on CsPbX3 nanocrystals wide spectra, PL microscopy image of e-beam patterned CsPbBr3 film, high-resolution XPS spectra of nanocrystals during irradiation and after anion-exchange from gas phase, XPS semiquantitative analysis of dose-dependent stabilization, photograph and SEM images of stabilized chalcogenide nanocrystal films, high-resolution SEM images of CsPbI3 film before and after irradiation, photographs of irradiated CsPbI3 films under various ageing conditions, PL spectra of aged CsPbI3 films and pristine solution, and video showing sequential BrCl exchanges from hydrohalic vapors.

Corresponding Author * (M.P.) [email protected]; (L.M.) [email protected]

Author Contributions The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript.

ACS Paragon Plus Environment

16

Page 17 of 20

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

REFERENCES AND NOTES (1)

(2) (3) (4)

(5)

(6)

(7) (8)

(9)

(10)

(11)

(12)

(13)

(14) (15)

Yakunin, S.; Sytnyk, M.; Kriegner, D.; Shrestha, S.; Richter, M.; Matt, G. J.; Azimi, H.; Brabec, C. J.; Stangl, J.; Kovalenko, M. V. et al. Detection of X-Ray Photons by SolutionProcessed Lead Halide Perovskites. Nat. Photon. 2015, 9, 444-449. Green, M. A.; Ho-Baillie, A.; Snaith, H. J. The Emergence of Perovskite Solar Cells. Nat. Photon. 2014, 8, 506-514. Liu, M.; Johnston, M. B.; Snaith, H. J. Efficient Planar Heterojunction Perovskite Solar Cells by Vapour Deposition. Nature 2013, 501, 395-398. Yakunin, S.; Protesescu, L.; Krieg, F.; Bodnarchuk, M. I.; Nedelcu, G.; Humer, M.; De Luca, G.; Fiebig, M.; Heiss, W.; Kovalenko, M. V. Low-Threshold Amplified Spontaneous Emission and Lasing from Colloidal Nanocrystals of Caesium Lead Halide Perovskites. Nat. Commun. 2015, 6, 8056. Jeon, N. J.; Noh, J. H.; Yang, W. S.; Kim, Y. C.; Ryu, S.; Seo, J.; Seok, S. I. Compositional Engineering of Perovskite Materials for High-Performance Solar Cells. Nature 2015, 517, 476-480. Woon Seok Yang, J. H. N., Nam Joong Jeon, Young Chan Kim, Seungchan Ryu, Jangwon Seo, Sang Il Seok High-Performance Photovoltaic Perovskite Layers Fabricated through Intramolecular Exchange. Science 2015, 348, 1234-1237. Chin, X. Y.; Cortecchia, D.; Yin, J.; Bruno, A.; Soci, C. Lead Iodide Perovskite LightEmitting Field-Effect Transistor. Nat. Commun. 2015, 6, 7383. Song, Z.; Watthage, S. C.; Phillips, A. B.; Tompkins, B. L.; Ellingson, R. J.; Heben, M. J. Impact of Processing Temperature and Composition on the Formation of Methylammonium Lead Iodide Perovskites. Chem. Mater. 2015, 27, 4612-4619. Dualeh, A.; Gao, P.; Seok, S. I.; Nazeeruddin, M. K.; Grätzel, M. Thermal Behavior of Methylammonium Lead-Trihalide Perovskite Photovoltaic Light Harvesters. Chem. Mater. 2014, 26, 6160-6164. Feng Zhang, H. Z., Cheng Chen, Xian-gang Wu, Xiangmin Hu, Hailong Huang, Junbo Han, Bingsuo Zou, and Yuping Dong Brightly Luminescent and Color-Tunable Colloidal CH3NH3PbX3 (X = Br, I, Cl) Quantum Dots: Potential Alternatives for Display Technology. ACS Nano 2015, 9, 4533-4542. Nevena Marinova, W. T., Robin Humphry-Baker, M. Ibrahim Dar, Vladimir Bojinov, Shaik Mohammed Zakeeruddin, Mohammad Khaja Nazeeruddin, and Michael Gratzel Light Harvesting and Charge Recombination in CH3NH3PbI3 Perovskite Solar Cells Studied by Hole Transport Layer Thickness Variation. ACS Nano 2015, 9, 4200-4209. Leguy, A. M.; Frost, J. M.; McMahon, A. P.; Sakai, V. G.; Kochelmann, W.; Law, C.; Li, X.; Foglia, F.; Walsh, A.; O'Regan, B. C. et al. The Dynamics of Methylammonium Ions in Hybrid Organic-Inorganic Perovskite Solar Cells. Nat. Commun. 2015, 6, 7124. Lee, M. M.; Teuscher, J.; Miyasaka, T.; Murakami, T. N.; Snaith, H. J. Efficient Hybrid Solar Cells Based on Meso-Superstructured Organometal Halide Perovskites. Science 2012, 338, 643-647. Jishi, R. A.; Ta, O. B.; Sharif, A. A. Modeling of Lead Halide Perovskites for Photovoltaic Applications. J. Phys. Chem. C 2014, 118, 28344-28349. Zhang, W.; Anaya, M.; Lozano, G.; Calvo, M. E.; Johnston, M. B.; Miguez, H.; Snaith, H. J. Highly Efficient Perovskite Solar Cells with Tunable Structural Color. Nano Lett. 2015, 15, 1698-1702.

ACS Paragon Plus Environment

17

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 20

(16) Anaya, M.; Lozano, G.; Calvo, M. E.; Zhang, W.; Johnston, M. B.; Snaith, H. J.; Miguez, H. Optical Description of Mesostructured Organic-Inorganic Halide Perovskite Solar Cells. J. Phys. Chem. Lett. 2015, 6, 48-53. (17) Protesescu, L.; Yakunin, S.; Bodnarchuk, M. I.; Krieg, F.; Caputo, R.; Hendon, C. H.; Yang, R. X.; Walsh, A.; Kovalenko, M. V. Nanocrystals of Cesium Lead Halide Perovskites (CsPbX, X = Cl, Br, and I): Novel Optoelectronic Materials Showing Bright Emission with Wide Color Gamut. Nano Lett. 2015, 15, 3692−3696. (18) Akkerman, Q. A.; D'Innocenzo, V.; Accornero, S.; Scarpellini, A.; Petrozza, A.; Prato, M.; Manna, L. Tuning the Optical Properties of Cesium Lead Halide Perovskite Nanocrystals by Anion Exchange Reactions. J. Am. Chem. Soc. 2015, 137, 10276-10281. (19) Nedelcu, G.; Protesescu, L.; Yakunin, S.; Bodnarchuk, M. I.; Grotevent, M. J.; Kovalenko, M. V. Fast Anion-Exchange in Highly Luminescent Nanocrystals of Cesium Lead Halide Perovskites (CsPbX3, X = Cl, Br, I). Nano Lett. 2015, 15, 5635-5640. (20) Wong, A. B.; Lai, M.; Eaton, S. W.; Yu, Y.; Lin, E.; Dou, L.; Fu, A.; Yang, P. Growth and Anion Exchange Conversion of CH3NH3PbX3 Nanorod Arrays for Light-Emitting Diodes. Nano Lett. 2015, 15, 5519-5524. (21) Jang, D. M.; Park, K.; Kim, D. H.; Park, J.; Shojaei, F.; Kang, H. S.; Ahn, J. P.; Lee, J. W.; Song, J. K. Reversible Halide Exchange Reaction of Organometal Trihalide Perovskite Colloidal Nanocrystals for Full-Range Band Gap Tuning. Nano Lett. 2015, 15, 5191-5199. (22) Sadhanala, A.; Ahmad, S.; Zhao, B.; Giesbrecht, N.; Pearce, P. M.; Deschler, F.; Hoye, R. L.; Godel, K. C.; Bein, T.; Docampo, P. et al. Blue-Green Color Tunable Solution Processable Organolead Chloride-Bromide Mixed Halide Perovskites for Optoelectronic Applications. Nano Lett. 2015, 15, 6095-6101. (23) Solis-Ibarra, D.; Smith, I. C.; Karunadasa, H. I. Post-Synthetic Halide Conversion and Selective Halogen Capture in Hybrid Perovskites. Chem. Sci. 2015, 6, 4054-4059. (24) Pellet, N.; Teuscher, J.; Maier, J.; Grätzel, M. Transforming Hybrid Organic Inorganic Perovskites by Rapid Halide Exchange. Chem. Mater. 2015, 27, 2181-2188. (25) Tomas Leijtens, E. T. H., Giulia Grancini, Daniel J. Slotcavage, Giles E. Eperon, James M. Ball, Michele De Bastiani, Andrea R. Bowring, Nicola Martino, Konrad Wojciechowski, Michael D. McGehee, Henry J. Snaith, Annamaria Petrozza Mapping Electric Field – Induced Switchable Poling and Structural Degradation in Hybrid Lead Halide Perovskite Thin Films. Adv. Energy Mater. 2015, doi:10.1002/aenm.201500962. (26) Leijtens, T.; Lauber, B.; Eperon, G. E.; Stranks, S. D.; Snaith, H. J. The Importance of Perovskite Pore Filling in Organometal Mixed Halide Sensitized Tio2-Based Solar Cells. J. Phys. Chem. Lett. 2014, 5, 1096-1102. (27) Sun, L. Perovskite Solar Cells: Crystal Crosslinking. Nat. Chem. 2015, 7, 684-685. (28) Li, X.; Ibrahim Dar, M.; Yi, C.; Luo, J.; Tschumi, M.; Zakeeruddin, S. M.; Nazeeruddin, M. K.; Han, H.; Gratzel, M. Improved Performance and Stability of Perovskite Solar Cells by Crystal Crosslinking with Alkylphosphonic Acid Omega-Ammonium Chlorides. Nat. Chem. 2015, 7, 703-711. (29) Miszta, K.; Greullet, F.; Marras, S.; Prato, M.; Toma, A.; Arciniegas, M.; Manna, L.; Krahne, R. Nanocrystal Film Patterning by Inhibiting Cation Exchange Via ElectronBeam or X-Ray Lithography. Nano Lett. 2014, 14, 2116-2122. (30) Hwang, I.; Jeong, I.; Lee, J.; Ko, M. J.; Yong, K. Enhancing Stability of Perovskite Solar Cells to Moisture by the Facile Hydrophobic Passivation. ACS Appl. Mater. Interfaces 2015, 7, 17330-17336.

ACS Paragon Plus Environment

18

Page 19 of 20

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

(31) Leguy, A. M. A.; Hu, Y.; Campoy-Quiles, M.; Alonso, M. I.; Weber, O. J.; Azarhoosh, P.; van Schilfgaarde, M.; Weller, M. T.; Bein, T.; Nelson, J. et al. Reversible Hydration of CH3NH3PbI3 in Films, Single Crystals, and Solar Cells. Chem. Mater. 2015, 27, 33973407. (32) Eperon, G. E.; Habisreutinger, S. N.; Leijtens, T.; Bruijnaers, B. J.; van Franeker, J. J.; deQuilettes, D. W.; Pathak, S.; Sutton, R. J.; Grancini, G.; Ginger, D. S. et al. The Importance of Moisture in Hybrid Lead Halide Perovskite Thin Film Fabrication. ACS Nano 2015, 9, 9380-9393. (33) Galisteo-Lopez, J. F.; Anaya, M.; Calvo, M. E.; Miguez, H. Environmental Effects on the Photophysics of Organic-Inorganic Halide Perovskites. J. Phys. Chem. Lett. 2015, 6, 22002205. (34) Kaciulis, S. Spectroscopy of Carbon: From Diamond to Nitride Films. Surf. Interface Anal. 2012, 44, 1155-1161. (35) Kankate, L.; Werner, U.; Turchanin, A.; Golzhauser, A.; Grossmann, H.; Tampe, R. Protein Resistant Oligo(Ethylene Glycol) Terminated Self-Assembled Monolayers of Thiols on Gold by Vapor Deposition in Vacuum. Biointerphases 2010, 5, 30-36. (36) Laibinis, P. E.; Graham, R. L.; Biebuyck, H. A.; Whitesides, G. M. X-Ray Damage to CF3CO2-Terminated Organic Monolayers on Si/Au: Principal Effect of Electrons. Science 1991, 254, 981-983. (37) Briggs, D.; Grant, J. T. Surface Analysis by Auger and X-Ray Photoelectron Spectroscopy; IM publications, 2003. (38) Nandwana, V.; Subramani, C.; Yeh, Y.-C.; Yang, B.; Dickert, S.; Barnes, M. D.; Tuominen, M. T.; Rotello, V. M. Direct Patterning of Quantum Dot Nanostructures Via Electron Beam Lithography. J. Mater. Chem. 2011, 21, 16859-16862. (39) Hogg, C. R.; Majetich, S. A.; Bain, J. A. Investigating Pattern Transfer in the Small-Gap Regime Using Electron-Beam Stabilized Nanoparticle Array Etch Masks. Ieee Trans. Magn. 2010, 46, 2307-2310. (40) Plaza, J. L.; Chen, Y.; Jacke, S.; Palmer, R. E. Nanoparticle Arrays Patterned by ElectronBeam Writing: Structure, Composition, and Electrical Properties. Langmuir 2005, 21, 1556-1559. (41) Lin, X. M.; Parthasarathy, R.; Jaeger, H. M. Direct Patterning of Self-Assembled Nanocrystal Monolayers by Electron Beams. Appl. Phys. Lett. 2001, 78, 1915. (42) Christodoulou, S.; Vaccaro, G.; Pinchetti, V.; De Donato, F.; Grim, J. Q.; Casu, A.; Genovese, A.; Vicidomini, G.; Diaspro, A.; Brovelli, S. et al. Synthesis of Highly Luminescent Wurtzite CdSe/CdS Giant-Shell Nanocrystals Using a Fast Continuous Injection Route. J. Mater. Chem. C 2014, 2, 3439-3347.

ACS Paragon Plus Environment

19

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 20

GRAPHICAL ABSTRACT

ACS Paragon Plus Environment

20