2,5-Furandicarboxylic Acid- and Itaconic Acid ... - ACS Publications

Feb 22, 2017 - The thermal and mechanical characterizations of the cured bio-UPs were evaluated using thermogravimetric analysis, 3-point bending test...
0 downloads 0 Views 723KB Size
Subscriber access provided by UB + Fachbibliothek Chemie | (FU-Bibliothekssystem)

Article

2, 5-Furandicarboxylic acid and Itaconic acid Derived Fully Biobased Unsaturated Polyesters and their Cross-linked Networks Jinyue Dai, Songqi Ma, Na Teng, Xinyan Dai, Xiaobin Shen, Sheng Wang, Xiaoqing Liu, and Jin Zhu Ind. Eng. Chem. Res., Just Accepted Manuscript • DOI: 10.1021/acs.iecr.7b00049 • Publication Date (Web): 22 Feb 2017 Downloaded from http://pubs.acs.org on February 26, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Industrial & Engineering Chemistry Research is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 26

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

2, 5-Furandicarboxylic acid and Itaconic acid Derived Fully Biobased Unsaturated Polyesters and their Cross-linked Networks

†‡







†‡

†‡

Jinyue Dai, , Songqi Ma,*, Na Teng, Xinyan Dai, Xiaobin Shen, , Sheng Wang, , Xiaoqing †

Liu, *, Jin Zhu





Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, P.R.China ‡

University of Chinese Academy of Sciences, Beijing 100049, China

*Corresponding

author:E-mail: [email protected] (Songqi Ma); [email protected] (Xiaoqing Liu)

ABSTRACT: A range of fully bio-based unsaturated polyesters (bio-UPs) derived from 2, 5-furandicarboxylic (FDCA), itaconic acid (IA), succinic acid (SA), and 1, 3propanediol (PD) were obtained via the direct polycondensation. The chemical structures of the bio-UPs were identified by FT-IR and 1H-NMR before they were cured together with a bio-based, non-volatile reactive diluent-guaiacol methacrylate (GM). The thermal and mechanical characterizations of the cured bio-UPs were evaluated using thermogravimetric analysis (TGA), 3-point bending tests, and dynamic mechanical analysis (DMA). Results showed that the thermal properties, flexural strength and modulus of the cured bio-UPs were greatly improved after introducing FDCA. The temperature of 5% thermal weight loss (Td5%) reached up to 330 °C, and the flexural strength and modulus reached up to 122.8 MPa and 3521 MPa, respectively. These results indicate that the bio-UPs have potential to replace the petroleum-based UPs.

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 26

1. INTRODUCTION Over the past few years, along with the increasing concern about environmental protection and continuous consumption of fossil oil reserves, exploring and utilizing the renewable resource has received much attention by both academia and industry around the world.

1-5

As the majorities of polymeric materials are derived from fossil

resources accounting for about 7% of crude oil and natural gas annual consumption in the world, using bio-based resources to synthesize novel polymers is important both from ecological and sustainability considerations. 6 Unsaturated polyester (UP) has wide applications in transportation, construction, aerospace, marine, and auto industries because of excellent thermal, mechanical, and corrosion resistant performances, and has a growing global market forecast to reach USD 10.48 billion in 2019. 7 Commercially available UPs are currently obtained from petroleum-based monomers (e.g. phthalic acids, phthalic fumaric acid and maleic anhydrides, and glycols). In recent years, increasing attention has been captured to explore various bio-based monomers for developing bio-based UPs.

8-11

Plant oils

primarily consisting of unsaturated triglycerides are potential alternatives due to their similar structures to UPs. Acrylated epoxidized soybean oil (AESO) is one of the most common used and commercially available plant oil-based UP analogs. However, their thermal and mechanical properties were not satisfactory because of the flexible long aliphatic chains of AESO, as a result, over 50 % non-renewable rigid monomers, like styrene, 12-13 acrylate, 14 and divinylbenzene, 15-16 were often used together with AESO. In recent years, a great deal of bio-based compounds from sucrose,

ACS Paragon Plus Environment

17

betulin,

18

Page 3 of 26

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

isosorbide, 19 tannic acid, 20 and myrcene 21 and galic acid, 22 etc. have also been utilized to enhance performance of AESO-based polymers. At the same time, for the purpose of preparing higher performance bio-UPs, growing bio-based dicarboxylic acids and dialcohols 23-27 have been exploited directly to be as the substitutes for the petroleumbased monomers for synthesizing bio-based UPs in recent decades. As an example, Sadler et al.

23

reported several bio-based UPs synthesized from isosorbide, maleic

anhydride and other diacids, and the polymers exhibited good thermodynamic properties with Tg of 53~107 °C and storage modulus of 430-1650 MPa. Rorrer et al. 27

prepared bio-based UPs from muconic acid, succinic acid and 1, 4-butanediol via

bulk polycondensation, and bio-based fiberglass panel with excellent properties was achieved after loading woven fiber glass mat followed by chemical cross-linking. Itaconic acid is one of the top 12 value added bio-based platform chemicals reported by the U.S. Department of Energy, 28 and it has similar structure (two carboxyl groups and one exo-double bond) to maleic acid and maleic anhydride. Thus, as a probable substitute for maleic acid or maleic anhydride, itaconic acid has been employed to prepare bio-based UPs.

29-33

In our previous works,

34-36

a range of fully

bio-based UPs were synthesized successfully based on itaconic acid and other bio-based diols, and the resulting polymers showed high performance due to the compact chemical structure of itaconic acid. However, compared with the commonly used UPs, the thermodynamic properties of previous reported bio-UPs still need to be improved further due to the lack of rigid structure. 2, 5-Furandicarboxylic acid (FDCA), which can be derived from sugars or polysaccharides via oxidizing hydroxymethylfurfural

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(HMF), 37-38 is a potential platform chemical in the synthesis of bio-based polyesters with excellent properties. For example, poly (ethylene 2, 5-furandicarboxylate) (PEF) exhibited better barrier properties to carbon dioxide and oxygen permeability in addition to the comparable or even better thermomechanical properties relative to poly (ethylene terephthalate) (PET).

39-41

Although FDCA-based UPs have been seldom

studied so far, previous work has demonstrated that FDCA-based UPs could achieve comparable thermal and mechanical performances with petroleum-based ones. 26 In this work, a range of fully bio-based UPs were prepared based on itaconic acid, 2, 5-furandicarboxylic acid, succinic acid and 1, 3-propanediol via melt polycondensation for the first time. As far as we know, almost all the UPs have extremely high viscosities that reactive diluent-styrene-which is identified as volatile organic compounds (VOCs) and hazardous air pollutants (HAPs)

42

is utilized together to achieve indispensable

processability. Thus, in this paper, guaiacol methacrylate (GM) from softwood lignin 43-44

as the green and non-volatile reactive diluent was cured together with the

synthesized bio-UPs. The relationships between chemical structures and mechanical, thermo-mechanical and thermal properties were investigated. The aim of this work is to develop a potential cured-UP with superior performance and high bio-based content via a facile and eco-friendly approach.

2. EXPERIMENTAL SECTION 2.1. Materials. 2, 5-Furandicarboxylic acid (FDCA) was bought from Sichuan Dagaote Technology Co., Ltd, China. Itaconic acid (IA) was supplied by Zhejiang Guoguang Biochemistry Co., Ltd, China. 1, 3-Propandiol (PD), succinic acid (SA),

ACS Paragon Plus Environment

Page 4 of 26

Page 5 of 26

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

dichloromethane (DCM), guaiacol, methacryloyl chloride, dibutyltin dilaurate (DBTDL),

triethylamine,

4-methoxyphenol

(MEHQ),

p-toluenesulfonic

acid

monohydrate and tert-Butyl peroxybenzoate (TBPT) were purchased from Aladdin Reagent, China. All of the chemicals were used as received. Guaiacol methacrylate (GM) (Scheme 1) was synthesized from methacrylic anhydride esterified guaiacol as reported previously. 43-44

Scheme 1. The chemical structure of guaiacol methacrylate (GM) 2.2 Characterization. The 1H-NMR characterization was conducted on a 400MHz AVANCE III Bruker NMR spectrometer (Bruker, Switzerland) using chloroform-d as a solvent. The FT-IR spectra determination was carried out on a NICOLET 6700 FT-IR (NICOLET, America). Gel contents of the cured bio-UPs were measured by extracting the samples in acetone (the polymer could swell in acetone). 0.5 g of specimens were cut from the cured bio-UPs and extracted with acetone for 48 h by a Soxhlet extractor, then they were dried at 60 °C in a vacuum oven for 24 hours. According to the weight difference of the samples before and after extraction, gel contents were calculated. To achieve high accuracy, the data of all the gel contents in this work were obtained by averaging three repeated samples. Gel permeation chromatography (GPC, HLC-8320, Tosoh Corporation, Japan) was applied to measure the number-average molecular

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

weight and polydispersity index of the bio-UPs. Monodisperse polystyrene was used as the standard sample, and THF was used as the mobile phase at a flow rate of 1 mL/min. Mettler-Toledo MET DSC (METTLER TOLEDO, Switzerland) was utilized to monitor the non-isothermal curing reaction under nitrogen atmosphere at a heating rate of 10 °C/min. Flexural properties were conducted on a Instron 5569A Universal Mechanical Testing Machine with a three-point bending mode at a speed of 1 mm/min, and each data was calculated by averaging the results of the five repeated samples. Dynamic mechanical analysis (DMA) was conducted on a Mettler-Toledo DMA/SDTA861e coupled under a tension mode. All the specimens with sizes of 70 mm ×10 mm ×3 mm were measured from 0 °C to 200 °C at a heating rate of 3 °C/min and a frequency of 1 Hz. Thermogravimetric analysis (TGA) was conducted on a Mettler-Toledo TGA/DSC1 Thermogravimetric Analyzer (METTLER TOLEDO, Switzerland) was used to determine the thermal stability of the cured bio-UPs with highly pure nitrogen or air as purge gas at a scanning rate of 20 °C/min from 50 °C to 600 °C. 5~10 mg of each sample was utilized. 2.3. Preparation of the fully bio-UPs. Table 1 presents the specific formulations of bio-UPs. Herein, p-toluenesulfonic acid monohydrate (0.5 mol% relative to diacid) and MEHQ (0.5 wt.% relative to the total weight of mixtures) were used as the prepolymerization catalyst and the free radical polymerization inhibitor, respectively. The mixtures of IA, PD, SA, FDCA, catalyst and inhibitor were placed in a four-necked flask with a reflux condenser, a thermometer, a mechanical stirrer, and a nitrogen inlet. After pre-polymerizing at 140 °C for 2 h, DBTDL (0.5 wt.% relative to the total weight

ACS Paragon Plus Environment

Page 6 of 26

Page 7 of 26

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

of reactants) as the polycondensation catalyst was introduced. The reaction proceeded at 160 °C under the vacuum of 0.09-0.095 MPa for 5 h, and then the systems were cooled down and discharged prior to storing at a dry environment. The bio-UPs at room temperature were light yellow and viscous liquids. Scheme 2 presents the synthetic route. Table 1. Feed compositions, synthetic conditions and Mn of the bio-UPs

a

Bio-UPs

IA/FDCA / PD/ SA (molar ratio)

Prepoly.

Polycondensation

Mna (g/mol)

PPI PPIF5 PPIF10 PPIF15 PPIF20 PPIF25 PPIF15S20 PPIF15S40 PPIF15S60

1/0/1.2/0 0.95/0.05/1.2/0 0.9/0.1/1.2/0 0.85/0.15/1.2/0 0.8/0.2/1.2/0 0.75/0.25/1.2/0 0.65/0.15/1.2/0.2 0.45/0.15/1.2/0.4 0.25/0.15/1.2/0.6

2 2 2 2 2 2 2 2 2

5 5 5 5 5 5 5 5 5

1.1 ×103 0.9 ×103 1.1 ×103 1.0 ×103 1.1 ×103 1.0 ×103 1.1×103 1.2×103 1.1×103

Reaction time (h)

Number-average molecular weight

Scheme 2. Synthesis of the fully bio-based UPs (bio-UPs)

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 26

2.4. Preparation of the cured bio-UPs. A predetermined content of bio-UPs, GM (shown in Table 2) and TBPT (2 wt.% of the total weight of bio-UPs and GM) were placed in a 100 mL bottle. After being stirred and degassed under vacuum, the mixtures were poured into a preheated stainless mold coated with mold release agent. The curing reaction was carried out at 80 °C for 2 h, 120 °C for 2 h, and 160 °C for 3 h based on the previously demonstrated conditions for curing itaconic acid-based UPs.

35

Cured

samples were carefully taken out from the mold after being cooled down.

Table 2. Feed compositions, bio-based content and gel content for different cured bio-UPs Weight ratio (%) sample cured-PPI cured-PPIF5 cured-PPIF10 cured-PPIF15 cured-PPIF20 cured-PPIF25 cured-PPIF15S20 cured-PPIF15S40 cured-PPIF15S60

UP

GM

Bio-based content (wt.%)

60 60 60 60 60 60 60 60 60

40 40 40 40 40 40 40 40 40

85.6 85.6 85.6 85.6 85.6 85.6 85.6 85.6 85.6

Bio-UP PPI PPIF5 PPIF10 PPIF15 PPIF20 PPIF25 PPIF15S20 PPIF15S40 PPIF15S60

Gel content (wt.%) 99.7 99.7 99.0 98.3 98.0 97.9 98.5 95.9 93.1

3. RESULTS AND DISCUSSION 3.1. Preparation and characterization of the bio-UPs. In the present work, the bio-UPs were synthesized from diacids and diols via the direct melt polycondensation with negligible VOC emission. Meanwhile, it should be pointed out that all monomers in this study came from renewable resources.

10

So far, some international standards

have been established for determining the bio-based content in order to standardize the

ACS Paragon Plus Environment

Page 9 of 26

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

development of bio-based polymeric materials. The concept of bio-based content is referred to as “the amount of bio-based carbon in the material or product as a percent of the weight (mass) of the total organic carbon in the product” by United States Department of Agriculture (USDA).

45

The bio-based content of the synthesized bio-

UPs in our study reached 100% because all of the monomers used can be from biomass. The bio-based content of the cured bio-UPs was also calculated and summarized in Table 2. All the cured bio-UPs exhibited a high bio-based content of 85.6%. Therefore, the synthesis procedure of UPs and final cured-UPs kept in line with the rules of Green Chemistry. The chemical compositions and structures of the bio-UPs were confirmed by FT-IR and 1H-NMR. The FT-IR spectra of the bio-UPs (PPI/ PPIF5/PPIF15S20) shown in Figure 1 are quite similar to each other. The broad adsorption peak at around 3540 cm1

corresponds to the -OH stretching. The peak at 1732 and the peaks at 817 and 1639

cm-1 are attributed to the C=O stretching of ester units and the C=CH2 stretching vibration of itaconic acid unit, respectively. The spectra of the bio-UPs (except PPI) also display characteristic C-H stretching (3122 cm-1) and C=C skeletal-in-plane vibration (1582 cm-1and 767 cm-1) peaks of furan unit. 46 The spectra of the others bioUPs are shown in supporting information (Figure S1). The structures of bio-UPs could be confirmed preliminary from the aforementioned FT-IR results. 1H NMR spectra are given to further confirm the chemical structures as shown in Figure 2. As shown, all of the peaks match well the protons of bio-UPs. The compositions of the bio-UPs were calculated from the integral area of different protons in the bio-UPs’ 1H NMR spectra.

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The results summarized in Table 3 showed that the final molar ratios of different monomer segments of all the bio-UPs were consistent with the molar ratios of the feed monomers. All the results demonstrate that the target compounds were successfully synthesized. As can be seen Table 1, all the synthesized bio-UPs presents similar number-average molecular weight (Mn) ranged from 0.9 × 103 to 1.2 × 103 g/mol.

Figure 1. FT-IR spectra of PPI, PPIF5, PPIF15S20

ACS Paragon Plus Environment

Page 10 of 26

Page 11 of 26

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

Figure 2. NMR spectra of the bio-UPs

Table 3. The relative molar ratios of the monomers in the feed and in the bio-UPs, characterized by 1H NMR sample

IA/FDCA / PD/ SA Molar ratiofeed(%)

IA/FDCA / PD/ SA Molar ratioNMR(%)

PPI PPIF5 PPIF10 PPIF15 PPIF20 PPIF25 PPIF15S20 PPIF15S40 PPIF15S60

45.5/0/54.5/0 43.2/2.3/54.5/0 40.9/4.6/54.5/0 38.7/6.8/54.5/0 36.4/9.1/54.5/0 34.1/11.4/54.5/0 29.6/6.8/54.5/9.1 20.5/6.8/54.5/18.2 11.4/6.8/54.5/27.3

44.2/0/55.8/0 44.1/2.5/53.4/0 41.9/4.6/53.5/0 37.2/6.9/55.9/0 34.6/7.8/57.6/0 33.9/11.4/54.7/0 26.8/6.0/53.6/13.6 20.4/6.6/54.1/18.9 10.8/6.5/55.0/27.7

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 26

3.2. The gel content of the cured bio-UPs. The gel content is one of the critical indicators for evaluating the performance of the cured bio-UPs. As seen in Table 2, all of the cured bio-UPs presented high gel content ranged from 93.1 wt.% to 99.7 wt.%, which suggests that a high degree of cross-linking has occurred. The cured bio-UPs showed decreased gel content with the increase of furan content, which was owing to the decreased cross-link density of the cured bio-UPs after introducing furan unit. 3.3. The flexural properties of the cured bio-UPs. The flexural stress-strain curves of the cured bio-UPs are illustrated in Figure 3 and their corresponding data are included in Table 4. Obviously in Figure 3a, the stress of the cured bio-UPs (from cured-PPI to cured-PPIF25) virtually increased linearly with strain to the peak value without yield, implying the nature of brittle fracture. 47 Moreover, in the Figure 3b, the increasing content of succinic acid (SA) in the UPs significantly altered fracture behavior of the cured bio-UPs. The stress increased linearly first, then yielded and presented a peak value. Afterwards, the stress began to decrease with the strain, and broke in the end. This is a remarkable feature of toughness fracture.

47

As shown in

Table 4, the flexural strength of the cured bio-UPs (from cured-PPI to cured-PPIF25) reveal a slightly increasing tendency from 116.8 MPa to 122.8 MPa with the increase of FDCA content up to 15 mol%, thereafter the flexural strength demonstrate a reducing trend as FDCA content increased. Meanwhile, the flexural strength of the other cured bio-UPs (from cured-PPIF15 to cured-PPIF15S60) exist decreasing trend from 122.8 MPa to 41.9 MPa along with the increase of the SA content.

ACS Paragon Plus Environment

Page 13 of 26

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

Especially, the cured-PPIF15S60 was not suitable for flexural strength test as it was too soft to be tested. These results demonstrate that materials with varied performance could be easily obtained by adjusting the molar ratio of monomers (FDCA or SA).

Figure 3. Flexural stress-strain curves of the cured bio-UPs

Table 4 Flexural and thermal properties of the cured bio-UPs

Cured-URs cured-PPI cured-PPIF5 cured-PPIF10 cured-PPIF15 cured-PPIF20 cured-PPIF25 cured-PPIF15S20 cured-PPIF15S40 cured-PPIF15S60 a

Flexural strength,

b

σa (MPa)

Eb (MPa)

εc (%)

Tgd (oC)

E’e (MP a)

116.8±7.1 122.3±3.7 122.7±5.2 122.8±2.0 114.7±9.3 116.8±3.1 103.1±9.8 41.9±0.8 /

2714±18 2765±32 2825±21 2935±19 3365±34 3521±15 2460±9 955±10 /

5.5±0.7 4.8±0.3 6.1±0.8 4.9±0.1 4.1±0.6 3.8+0.1 5.9±0.3 24.3±3.1 /

141.7 125.8 119.0 127.6 125.4 121.1 117.1 83.9 73.5

1850 2213 2239 2391 2685 2841 1452 527 175

Flexural modulus,

d

νef/103 (mol m−3)

5.84 4.95 4.91 4.24 2.83 2.65 2.82 0.89 0.11

Td5% (oC)

R600 (%)

299 310 319 330 323 318 311 305 299

5.0 5.7 6.4 8.6 8.1 9.0 6.3 6.1 4.0

Glass transition temperature by DMA, cStrain at break

(%), e Storage modulus at 25 °C, f Cross-link density.

3.4. Dynamic mechanical analysis of the cured bio-UPs. Figure 4 presents the DMA curves of the changes of storage modulus and tan δ with temperature for the cured bio-UPs, the values of modulus at 25 °C and glass transition temperature (Tg) are listed

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 26

in Table 4. The Tgs of the cured bio-UPs were determined from the peak temperatures of the temperature dependent curves of tan δ shown in Figure 4a and Figure 4b. The Tg of cross-linked polymer is mainly dependent on its chain segment’s chemical structure and cross-link density.48 It can be seen that all the cured bio-UPs displayed Tgs ranging from 73.5 oC to 141.7 oC, covering most applications’ requirement. The cured-PPI exhibited the highest Tg (147.1 oC) because of the higher cross-link density (Table 3) induced by higher functionality of C=C bond than other cured bio-UPs. Meanwhile, it’s quite clear that Tg declined after the introduction of FCDA in bio-UPs. This is because the introduction of FDCA decreased the number of C=C bonds of the bio-UPs, resulting in the decreased cross-link density for the cured bio-UPs. More interestingly, the Tg of the cured bio-UPs (from cured-PPIF5 to cured-PPIF25) did not further decrease with the FDCA content increasing. This is due to the fact that furan ring of FDCA made great contribution to the rigidity and intermolecular force of molecular chains, and then decreased the mobility of chain segment of the cured bio-UPs. 49 In other cured bio-UPs

(from

cured-PPIF15

to

cured-PPIF15S60),

the

Tg

reduced linearly with increasing the SA content. As shown in Figure 4c and Figure 4d, it is quite clear that the storage modulus (25 o

C) of the cured bio-UPs (from cured-PPI to cured-PPIF25) increased as the FDCA

content increased, which is due to the increased stiffness of the cured bio-UPs after introducing FCDA. And, in other cured bio-UPs (from cured-PPIF15 to curedPPIF15S60), the storage modulus (25 oC) reduced sharply with the increase of SA content. This is due to the reason that the introduction of SA decreased the number of

ACS Paragon Plus Environment

Page 15 of 26

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

C=C bonds of the bio-UPs, resulting in the decreased cross-link density for the cured bio-UPs. The following equation is employed to calculate the cross-link density (νe) of the cured bio-UPs: 35 ve 

E' 3RT

(1)

where E’ is the elastic modulus of the cured bio-UPs in its rubbery plateau region (E’ at the temperature of Tg+40 K at which all the cured bio-UPs were in a rubbery state was selected in this work), T is the absolute temperature and R is the universal gas constant. The calculated cross-link density for the cured bio-UPs is summarized in Table 4. As shown, the cross-link density of the cured bio-UPs (from cured-PPI to cured-PPIF25) was decreased with the addition of FDCA. Meanwhile, for the other cured bio-UPs (from cured-PPIF15S20 to cured-PPIF15S60), the increasing SA content also led to the further reduced cross-link density. The cause of this phenomenon was that FDCA or SA introduction decreased the number of C=C bonds of the bio-UPs, generating the cured bio-UPs with decreased cross-linking density.

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 4. DMA curves of the cured bio-UPs 3.4. Thermal properties of the cured bio-UPs. TGA was carried out for measuring thermal stability and degradation behaviors of the cured bio-UPs under N2 atmosphere. Figure 5 and Table 4 show the non-isothermal TGA curves and the data of the cured bio-UPs The degradation temperature for 5% weight loss (Td5%) and the residue at 600 ºC (R600) were regarded as the indicators to appraise the thermal stabilities of the cured bio-UPs. All the samples showed high thermal stability with Td5% of above 299 ºC. It can be also seen that the cured bio-UPs (from cured-PPIF5 to cured-PPIF15S40 ) containing furan unit are more thermally stable in comparison with the cured-PPI (without furan unit), confirming that the introduction of FDCA well strengthened the thermal stability of these cured bio-UPs, which is in agreement with the previously reported work. 50

ACS Paragon Plus Environment

Page 16 of 26

Page 17 of 26

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

Figure 5. TGA curves of the cured bio-UPs under N2 atmosphere

4. CONCLUSIONS A series of fully bio-based UPs (bio-UPs) were successfully synthesized from renewable monomers (itaconic acid, 2, 5-furandicarboxylic, succinic acid and 1, 3propanediol) via direct polycondensation. Together with a bio-based, non-volatile reactive diluent GM, the cured bio-UPs with high bio-based content were achieved. Meanwhile, the cured bio-UPs exhibited high and varied thermal and mechanical properties. They are thermally stable up to 330 °C, and have Tg of 73.5-141.7 °C and flexural strength of 41.9-116.8 MPa. These properties are comparable or even better than those of petroleum-based UPs. 51-54 Thus, these bio-UPs showed great potential to be as green alternatives to the fossil-derived UPs.

NOTES The authors declare no competing financial interest. *Corresponding authors: [email protected] (Songqi Ma); [email protected] (Xiaoqing Liu)

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACKNOWLEDGMENTS The authors are grateful for the financial support from National Natural Science Foundation of China (Grant No. 51473180, 51373194), National Key Technology Support Program (2015BAD15B08) and Youth Innovation Promotion Association of the Chinese Academy of Sciences (Grant No. 2012229). ASSOCIATED CONTENT Supporting Information FT-IR spectra of bio-based UPs (PPIF10, PPIF15, PPIF20, PPIF25, PPIF15S40, PPIF15S60). REFERENCES (1) Corma, A.; Iborra, S.; Velty, A., Chemical routes for the transformation of biomass into chemicals. Chem. Rev. 2007, 107, 2411-2502. (2) Takami, S.; Okuda, K.; Man, X.; Umetsu, M.; Ohara, S.; Adschiri, T., Kinetic Study on the Selective Production of 2-(Hydroxybenzyl)-4-methylphenol from Organosolv Lignin in a Mixture of Supercritical Water and p-Cresol. Ind. Eng. Chem. Res. 2012, 51, 4804-4808. (3) Kupiainen, L.; Ahola, J.; Tanskanen, J., Comparison of formic and sulfuric acids as a glucose decomposition catalyst. Ind. Eng. Chem. Res. 2010, 49, 8444-8449. (4) Williams, C. K.; Hillmyer, M. A., Polymers from renewable resources: a perspective for a special issue of polymer reviews. Polym. Rev. 2008, 48, 1-10.

ACS Paragon Plus Environment

Page 18 of 26

Page 19 of 26

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

(5) Yu, Y.; Wu, H., Kinetics and Mechanism of Glucose Decomposition in HotCompressed Water: Effect of Initial Glucose Concentration. Ind. Eng. Chem. Res. 2011, 50, 10500-10508. (6) Eissen, M.; Metzger, J. O.; Schmidt, E.; Schneidewind, U., 10 years after Rio— concepts on the contribution of chemistry to a sustainable development. Angew. Chem. Int. Edit. 2002, 41, 414-436. (7) Biswas, B.; Chabri, S.; Mitra, B. C.; Bandyopadhyay, N. R.; Sinha, A., Mechanical Behaviour of Aluminium Dispersed Unsaturated Polyester/Jute Composites for Structural Applications. J. In. Eng. (India): Series C 2016, 1-6. (8) Farmer, T. J.; Castle, R. L.; Clark, J. H.; Macquarrie, D. J., Synthesis of unsaturated polyester resins from various bio-derived platform molecules. Int. J. Mol. Sci. 2015, 16, 14912-14932. (9) Gandini, A.; Lacerda, T. M., From monomers to polymers from renewable resources: Recent advances. Prog. Polym. Sci. 2015, 48, 1-39. (10) Vilela, C.; Sousa, A. F.; Fonseca, A. C.; Serra, A. C.; Coelho, J. F.; Freire, C. S.; Silvestre, A. J., The quest for sustainable polyesters-insights into the future. Polym. Chem. 2014, 5, 3119-3141. (11) Belgacem, M. N.; Gandini, A., Monomers, polymers and composites from renewable resources. Elsevier: 2011. (12) Lu, J.; Khot, S.; Wool, R. P., New sheet molding compound resins from soybean oil. I. Synthesis and characterization. Polymer 2005, 46, 71-80.

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(13) Can, E.; Wool, R. P.; Küsefoğlu, S., Soybean- and castor-oil-based thermosetting polymers: Mechanical properties. J. Appl. Polym. Sci. 2006, 102, 1497-1504. (14) Patel, K. I.; Parmar, R. J.; Parmar, J. S., Novel binder system for ultraviolet‐ curable coatings based on tobacco seed (Nicotiana rustica) oil derivatives as a renewable resource. J. Appl. Polym. Sci. 2008, 107, 71-81. (15) Li, F.; Hanson, M.; Larock, R., Soybean oil-divinylbenzene thermosetting polymers: synthesis, structure, properties and their relationships. Polymer 2001, 42, 1567-1579. (16) Li, F.; Larock, R. C., New soybean oil-styrene-divinylbenzene thermosetting copolymers. I. Synthesis and characterization. J. Appl. Polym. Sci. 2001, 80, 658-670. (17) Chen, Z.; Wu, J. F.; Fernando, S.; Jagodzinski, K., Soy-based, high biorenewable content UV curable coatings. Prog. Org. Coat. 2011, 71, 98-109. (18) Auclair, N.; Kaboorani, A.; Riedl, B.; Landry, V., Acrylated betulin as a comonomer for bio-based coatings. Part II: Mechanical and optical properties. Ind. Crop. Prod. 2016, 82, 118-126. (19) Liu, W.; Xie, T.; Qiu, R., Biobased Thermosets Prepared from Rigid Isosorbide and Flexible Soybean Oil Derivatives. ACS Sustain. Chem. Eng 2016, DOI: 10.1021/acssuschemeng.6b02117 (20) Liu, R.; Zhu, J.; Luo, J.; Liu, X., Synthesis and application of novel UV-curable hyperbranched methacrylates from renewable natural tannic acid. Prog. Org. Coat. 2014, 77, 30-37.

ACS Paragon Plus Environment

Page 20 of 26

Page 21 of 26

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

(21) Yang, X.; Li, S.; Xia, J.; Song, J.; Huang, K.; Li, M., Renewable Myrcene-based UV-curable Monomer and its Copolymers with Acrylated Epoxidized Soybean Oil: Design, Preparation, and Characterization. BioResources 2015, 10, 2130-2142. (22) Ma, S. Q.; Jiang, Y. H.; Liu, X. Q.; Fan, L. B.; Zhu, J., Bio-based tetrafunctional crosslink agent from gallic acid and its enhanced soybean oil-based UV-cured coatings with high performance. RSC Adv. 2014, 4, 23036-23042. (23) Sadler, J. M.; Toulan, F. R.; Nguyen, A.-P. T.; Kayea, R. V.; Ziaee, S.; Palmese, G. R.; La Scala, J. J., Isosorbide as the structural component of bio-based unsaturated polyesters for use as thermosetting resins. Carbohydr. Polym. 2014, 100, 97-106. (24) Fonseca, A. C.; Lopes, I. M.; Coelho, J. F.; Serra, A. C., Synthesis of unsaturated polyesters based on renewable monomers: Structure/properties relationship and crosslinking with 2-hydroxyethyl methacrylate. React. Funct. Polym. 2015, 97, 1-11. (25) Ma, S.; Li, T.; Liu, X.; Zhu, J., Research progress on bio‐based thermosetting resins. Polym. Int. 2016, 65, 164-173. (26) Sousa, A.; Fonseca, A.; Serra, A.; Freire, C.; Silvestre, A.; Coelho, J., New unsaturated copolyesters based on 2, 5-furandicarboxylic acid and their crosslinked derivatives. Polym. Chem. 2016, 7, 1049-1058. (27) Rorrer, N. A.; Dorgan, J. R.; Vardon, D. R.; Martinez, C. R.; Yang, Y.; Beckham, G. T., Renewable unsaturated polyesters from muconic acid. ACS Sustain. Chem. Eng 2016, DOI: 10.1021/acssuschemeng.6b01820 (28) Werpy, T.; Petersen, G.; Aden, A.; Bozell, J.; Holladay, J.; White, J.; Manheim, A.; Eliot, D.; Lasure, L.; Jones, S. Top value added chemicals from biomass. Volume 1-

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Results of screening for potential candidates from sugars and synthesis gas; DTIC Document: 2004. (29) Teramoto, N.; Ozeki, M.; Fujiwara, I.; Shibata, M., Crosslinking and biodegradation of poly (butylene succinate) prepolymers containing itaconic or maleic acid units in the main chain. J. Appl. Polym. Sci. 2005, 95, 1473-1480. (30) Sakuma, T.; Kumagai, A.; Teramoto, N.; Shibata, M., Thermal and dynamic mechanical properties of organic–inorganic hybrid composites of itaconate‐ containing poly (butylene succinate) and methacrylate‐substituted polysilsesquioxane. J. Appl. Polym. Sci. 2008, 107, 2159-2164. (31) Barrett, D. G.; Merkel, T. J.; Luft, J. C.; Yousaf, M. N., One-step syntheses of photocurable polyesters based on a renewable resource. Macromolecules 2010, 43, 9660-9667. (32) Gowsika, J.; Nanthini, R., Synthesis, characterization and in vitro anticancer evaluation of itaconic acid based random copolyester. J. Chem. 2014, 2014. (33) Lv, A.; Li, Z.-L.; Du, F.-S.; Li, Z.-C., Synthesis, functionalization, and controlled degradation of high molecular weight polyester from itaconic acid via ADMET polymerization. Macromolecules 2014, 47, 7707-7716. (34) Dai, J.; Ma, S.; Liu, X.; Han, L.; Wu, Y.; Dai, X.; Zhu, J., Synthesis of bio-based unsaturated polyester resins and their application in waterborne UV-curable coatings. Prog. Org. Coat. 2015, 78, 49-54.

ACS Paragon Plus Environment

Page 22 of 26

Page 23 of 26

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

(35) Dai, J.; Ma, S.; Wu, Y.; Han, L.; Zhang, L.; Zhu, J.; Liu, X., Polyesters derived from itaconic acid for the properties and bio-based content enhancement of soybean oil-based thermosets. Green Chem. 2015, 17, 2383-2392. (36) Dai, J.; Ma, S.; Wu, Y.; Zhu, J.; Liu, X., High bio-based content waterborne UVcurable coatings with excellent adhesion and flexibility. Prog. Org. Coat. 2015, 87, 197-203. (37) Davis, S. E.; Zope, B. N.; Davis, R. J., On the mechanism of selective oxidation of 5-hydroxymethylfurfural to 2, 5-furandicarboxylic acid over supported Pt and Au catalysts. Green Chem. 2012, 14, 143-147. (38) Rass, H. A.; Essayem, N.; Besson, M., Selective aqueous phase oxidation of 5hydroxymethylfurfural to 2, 5-furandicarboxylic acid over Pt/C catalysts: influence of the base and effect of bismuth promotion. Green Chem. 2013, 15, 2240-2251. (39) Bozell, J. J.; Petersen, G. R., Technology development for the production of biobased products from biorefinery carbohydrates-the US Department of Energy’s “top 10” revisited. Green Chem. 2010, 12, 539-554. (40) Sousa, A. F.; Matos, M.; Freire, C. S.; Silvestre, A. J.; Coelho, J. F., New copolyesters derived from terephthalic and 2, 5-furandicarboxylic acids: A step forward in the development of biobased polyesters. Polymer 2013, 54, 513-519. (41) van der Waal, J. C.; Mazoyer, E.; Baars, H. J.; Gruter, G.-J. M., From Terephthalic Acid to 2, 5-Furandicarboxylic Acid: An Industrial Perspective. Liquid Phase Aerobic Oxidation Catalysis: Industrial Applications and Academic Perspectives 2016.

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(42) Sexton, K.; Adgate, J. L.; Ramachandran, G.; Pratt, G. C.; Mongin, S. J.; Stock, T. H.; Morandi, M. T., Comparison of personal, indoor, and outdoor exposures to hazardous air pollutants in three urban communities. Environ. Sci. Technol. 2004, 38, 423-430. (43) Stanzione, J. F.; Sadler, J. M.; La Scala, J. J.; Wool, R. P., Lignin Model Compounds as Bio-Based Reactive Diluents for Liquid Molding Resins. ChemSusChem 2012, 5, 1291-1297. (44) Stanzione III, J. F.; Giangiulio, P. A.; Sadler, J. M.; La Scala, J. J.; Wool, R. P., Lignin-based bio-oil mimic as biobased resin for composite applications. ACS Sustain. Chem. Eng. 2013, 1, 419-426. (45) Kunioka, M.; Taguchi, K.; Ninomiya, F.; Nakajima, M.; Saito, A.; Araki, S., Biobased contents of natural rubber model compound and its separated constituents. Polymers 2014, 6, 423-442. (46) Zhang, J.; Li, J.; Tang, Y.; Lin, L.; Long, M., Advances in catalytic production of bio-based polyester monomer 2, 5-furandicarboxylic acid derived from lignocellulosic biomass. Carbohydr. Polym. 2015, 130, 420-428. (47) Ma, S.; Liu, X.; Fan, L.; Jiang, Y.; Cao, L.; Tang, Z.; Zhu, J., Synthesis and Properties of a Bio‐Based Epoxy Resin with High Epoxy Value and Low Viscosity. ChemSusChem 2014, 7, 555-562. (48) Ma, S.; Webster, D. C.; Jabeen, F., Hard and Flexible, Degradable Thermosets from Renewable Bioresources with the Assistance of Water and Ethanol. Macromolecules 2016, 49, 3780-3788.

ACS Paragon Plus Environment

Page 24 of 26

Page 25 of 26

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

(49) Burgess, S. K.; Leisen, J. E.; Kraftschik, B. E.; Mubarak, C. R.; Kriegel, R. M.; Koros, W. J., Chain mobility, thermal, and mechanical properties of poly (ethylene furanoate) compared to poly (ethylene terephthalate). Macromolecules 2014, 47, 13831391. (50) Froimowicz, P.; R Arza, C.; Han, L.; Ishida, H., Smart, Sustainable, and Ecofriendly Chemical Design of Fully Bio-Based Thermally Stable Thermosets Based on Benzoxazine Chemistry. ChemSusChem 2016, 9, 1921-1928. (51) Ghorui, S.; Bandyopadhyay, N.; Ray, D.; Sengupta, S.; Kar, T., Use of maleated castor oil as biomodifier in unsaturated polyester resin/fly ash composites. Ind. Crop. Prod. 2011, 34, 893-899. (52) Mandhakini, M.; Devaraju, S.; Venkatesan, M. R.; Alagar, M., Linseed vinyl ester fatty amide toughened unsaturated polyester-bismaleimide composites. High Perform. Polym. 2012, 24, 237-244. (53) Liu, C.; Yang, X.; Cui, J.; Zhou, Y.; Hu, L.; Zhang, M.; Liu, H., Tung oil based monomer for thermosetting polymers: synthesis, characterization and copolymerization with styrene. Bioresources 2011, 7, 0447-0463. (54) Konwar, U.; Karak, N., Hyperbranched polyether core containing vegetable oilmodified polyester and its clay nanocomposites. Polym. J. 2011, 43, 565-576.

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

For Table of Contents Only 46x26mm (300 x 300 DPI)

ACS Paragon Plus Environment

Page 26 of 26