A Cationic Silver Pyrazine Coordination Polymer with High Capacity

Subscriber access provided by Bethel University

Remediation and Control Technologies

A Cationic Silver Pyrazine Coordination Polymer with High Capacity Anion Uptake from Water Eaindar Soe, Beatriz Ehlke, and Scott R. J. Oliver Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.9b01633 • Publication Date (Web): 07 Jun 2019 Downloaded from http://pubs.acs.org on June 9, 2019

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 30

Environmental Science & Technology

1

A Cationic Silver Pyrazine Coordination Polymer

2

with High Capacity Anion Uptake from Water

3

Eaindar Soe, Beatriz Ehlke and Scott R. J. Oliver*

4

University of California, Santa Cruz, Department of Chemistry and Biochemistry, 1156 High

5

Street, Santa Cruz, California 95064

6

Keywords: silver pyrazine, anion exchange, coordination polymers, perrhenate,

7

alkanedicarboxylates

8 9

Abstract

10

We report the first example of linker modification for an N-donor Ag-based cationic material

11

while maintaining and in some cases increasing the anion exchange capacity. Cationic silver(I)

12

pyrazine nitrate selectively traps harmful oxo-anions from water such as permanganate,

13

perrhenate and a variety of α,ω-alkanedicarboxylates. We chose these anions as initial examples

14

of exchange for potential water purification. The host-guest interaction between the cationic

15

layers of -stacked silver pyrazine polymers and the incoming/outgoing interlamellar anions

16

allows for the exchange. The exchange capacity over 24 h reached 435 and 818 mg/g for

17

permanganate and perrhenate, respectively, a record for a crystalline metal-organic material and

18

over five times the exchange capacity compared to commercial resin. The material also

19

undergoes organic exchange as an analog for pharmaceutical waste, some of which have a

ACS Paragon Plus Environment

1


20

carboxylate functionality at the neutral pH range typical of natural water sources. Both the as-

21

synthesized and exchanged materials are characterized by a variety of analytical techniques.

Page 2 of 30

22 23

Introduction

24

Open-framework metal-organic polymers, derived from a combination of selected

25

transition metal and bridging ligands, have attracted much attention owing to their various

26

potential applications including electrocatalysis,1 magnetism,2 luminescence,3 gas storage,4 ion

27

exchange5 and heterogeneous catalysis.6,7 Coordination polymers (CPs) based on Ag(I) cations

28

are attracting a great deal of attention, in part because they are structurally versatile.8,9 The

29

coordination sphere of the d10 metal, Ag(I), is very flexible and can adopt coordination numbers

30

two to six and various geometries from linear to trigonal, tetrahedral, trigonal pyramidal and

31

octahedral.10 The structural flexibility of these complexes is essential for the investigation of

32

non-covalent host-guest interactions. Weak intermolecular forces significantly affect the

33

geometry and topology of the Ag(I) coordination polymers in the solid state and in turn the anion

34

exchange.11

35

There has been much recent interest in the study of linear 1-D silver coordination

36

polymers involving bridging N-heterocyclic ligands.12,13 The simplest such ligand is pyrazine,

37

which has two nitrogen donors in its six-ring. Using a 1:1 ratio with silver nitrate, silver(I)

38

pyrazine structures can be synthesized.14,15 The first silver pyrazine structures, [Ag(NC4H4N)+]n

39

and [Ag(NC4H4N)2+]n, were first reported in the 1960s16 and have since been the subject of

40

various studies including measurements of stability constants,16 infrared spectroscopy17 and mass

41

spectroscopy.18 Both structures displayed a high melting point (250 °C), which led the authors to

42

suggest polymeric structures because pyrazine can act as bidentate bridging group. In a 1966


2

Page 3 of 30


43

report, the silver pyrazine crystals were inherently twinned and the structure consisted of kinked

44

chains of the type [-Ag-NC4H4N-]n.19 Due to the lability of the Ag-donor atom bond,20 the

45

process of coordination polymer formation is highly reversible. As a result, the Ag(I)

46

coordination polymers can readily be crystallized with various counter-anions, allowing

47

investigation by single crystal X-ray diffraction. Anion exchange was not studied; our group is

48

thus interested in developing new anion exchange chemistry using silver pyrazine CPs.

49

Many of the priority pollutants in wastewater listed by the U.S. Environmental Protection

50

Agency (EPA) are in their oxo-anionic form, for example, pertechnetate (TcO4–), chromate

51

(CrO42–) and arsenate (AsO43–).21 These toxic, harmful anions are problematic in the vitrification

52

of low activity radioactive waste, weakening the integrity of the waste glass by forming

53

spinels.2{Citation}2 Another class of water-borne toxic anion pollutants are organic, generated

54

through both industrial processes and personal use. EPA classifies many of these pollutants as

55

pharmaceutical and personal care products (PPCPs).23 Many pharmaceuticals are sold in their

56

acid or chloride form and consequently form anions when dissolved in water. Pharmaceutical

57

anions and their metabolites are a growing problem because of ineffective removal or

58

chlorination to toxic derivatives in wastewater treatment facilities.24

59

Resins with cationic side groups and exchangeable counter anions are still considered the

60

standard ion exchanger.25,26 Due to their organic polymer nature, these resins are of limited

61

thermal and chemical stability.27 One alternative to possibly replace resins is layered double

62

hydroxides (LDHs), an isostructural group of materials containing cationic brucite type layers

63

that are charged balanced by interlayer anions with general formula [M2+1−xM3+x(OH)2][An–

64

x/n]·xH2O

where M2+ and M3+ are a range of metals, An− is the intercalated anion, and x is ratio


3


65

of M3+/( M2+ + M3+). LDHs generally suffer, however, from low selectivity and re-intercalation

66

of common anions such as carbonate or sulfate due to the memory effect.28,29

Page 4 of 30

67

Owing to the structural diversity and weak host-guest interaction, cationic coordination

68

polymers are gaining considerable attention for anion exchange. Silver-based CPs in particular

69

have been previously studied for their ability to selectively trap anions via a crystal-to-crystal

70

transition.30,31 We reported silver(I) with 4,4-bipyridine polymers and ethanedisulfonate [EDS, –

71

O3S(CH2)2SO3–] as a charge balance anion.32 We also reported oxo-anion pollutants exchange

72

materials such as [Cu4(OH)62+][EDS2–]·2H2O33 and [M(H2O)n(4,4’-bipyridine)22+][EDS2–] [M =

73

Cu(I), Ag(I), Co(II) or Zn(II)].32,34,35 We subsequently described silver-4,4’-bipyridine nitrate

74

(SBN)36,37 and acetate (SBA)38 materials. Both circumvent the need for EDS anions and have

75

even higher capacity, rate, selectivity and reversibility for trapping of perchlorate from water.

76

Wang and coworkers recently reported a variety of cationic extended materials, denoted as SCU-

77

n (Soochow University, structure No. n) with outstanding performance for TcO4–/ReO4–

78

removal.39–42 These authors also recently reported organic polymers with similar properties.42,43

79

There have also been significant advances with selective crystallization approaches for anion

80

removal44 and very recently Zr6O8-based cationic MOFs, though the latter require ligands with

81

multiple step syntheses and have limited selectivity.45,46

82

In this study, a variety of anionic pollutants including permanganate, perrhenate (as an

83

analog for pertechnetate) and α,ω-alkanedicarboxylates (as analogs for anionic pharmaceutical

84

pollutants) were exchanged into the cationic CP Ag-pyrazine nitrate. The weak interaction

85

between the interlamellar nitrates and the cationic silver pyrazine layers likely allows for the

86

high capacity exchange.

87


4

Page 5 of 30


88

Experimental

89

Reagents: Silver nitrate (AgNO3, Alfa Aesar, 99%) and pyrazine (NC4H4N, Acros Organics,

90

99%) were used as-received for the synthesis. For the exchange studies, the following were used

91

as-purchased: potassium chromate (K2CrO4, Fischer Scientific), potassium permanganate

92

(KMnO4, Acros Organics), sodium tetrafluoroborate (NaBF4, Acros Organics), potassium

93

chloride (KCl, Fischer Scientific), potassium bromide (KBr, Acros Organics), potassium iodide

94

(KI, Spectrum Chemical), sodium perrhenate (NaReO4, Alfa Aesar), disodium malonate ([−O2C-

95

CH2-CO2−]Na2, TCI America), disodium succinate ([−O2C-(CH2)2-CO2−]Na2, TCI America),

96

disodium glutarate ([−O2C-(CH2)3-CO2−]Na2, TCI America), disodium adipate ([−O2C-(CH2)6-

97

CO2−]Na2, TCI America), disodium sebacate ([−O2C-(CH2)8-CO2−]Na2, TCI America), ascorbic

98

acid (C6H8O6, Fischer Scientific), salicylic acid [HOC6H4(CO2H), Fischer Scientific],

99

terephthalic acid [C8H4(CO2H)2, TCI America], 2,6-naphthalene dicarboxylic acid

100

[C10H6(COOH)2, TCI America] and Purolite A530E (Purolite).

101

Instrumental Details: Powder X-ray diffraction (PXRD) data were obtained on a Rigaku

102

Americas Miniflex Plus powder diffractometer, scanning from 2° to 40° (2θ) at a rate of 3°min-1

103

with a 0.02° step size under Cu-Kα radiation (λ = 1.5418 Å). Inductively coupled plasma optical

104

emission spectrometry (ICP-OES) data were acquired on a Perkin Elmer Optima 4300DV, run in

105

radial mode using yttrium as an internal standard. A standard curve for silver(I) was prepared to

106

quantify the amount of free silver in the samples. Fourier Transform Infrared (FT-IR)

107

spectroscopy data was collected on a Perkin Elmer Spectrum One FT-IR spectrometer.

108

Thermogravimetric analysis (TGA) was performed using a TA Instruments Q500 TGA, heating

109

from 25 to 600 °C with a gradient of 10 °C/min and nitrogen flow. In situ variable temperature

110

PXRD (VT-PXRD) was performed on a Rigaku SmartLab X-Ray Diffractometer with Cu-


5


Page 6 of 30

111

K radiation ( = 1.57418 Å) from 2° to 70° (2) at a scan rate of 2°/min and 0.02° step size.

112

The samples were heated at a rate of 10°C/min and held at the set temperature for 5 min before

113

scanning. SEM images were collected with a FEI Quanta 3D Dualbeam microscope.

114

Synthesis: Silver nitrate and pyrazine (1:1 molar ratio) were added together in 10 mL of

115

Millipore water and the mixture was kept at 70 °C for 1 h. The reaction mixture was then cooled

116

in an ice bath and rinsed with cold Millipore water and acetone. The filtration gave rise to white

117

needle-like small crystals (yield: 65.8% based on AgNO3). Direct synthesis of silver malonate

118

was performed by mixing silver nitrate and sodium malonate (1:1 molar ratio) together in 10 mL

119

of Millipore water and the mixture was stirred at room temperature for 1 h. The product was

120

filtered and rinsed with Millipore water and acetone (yield: 63.4% based on AgNO3).

121

Anion Exchange: The exchange reactions were performed by placing [Ag(pyrazine)+][NO3–]

122

(0.2 mmol) and the anion of interest (0.2 mmol) in 10 mL of Millipore water. The resulting

123

systems were kept under 300-400 rpm magnetic stirring rate at room temperature 25 °C for 24 h.

124

Equimolar quantities were used for all anion exchanges but modified if necessary according to

125

the charge of the incoming anion. The selectivity tests were performed by introducing the

126

material into a sealed beaker containing 10 mL Millipore water and the anion mixture of interest

127

(0.2 mmol for each). The reaction was stirred for 24 h under ambient conditions.

128

Silver leaching: To study the leaching of silver ion of exchanged product [Ag(pyrazine)+][ReO4–

129

], the sample was placed in water under dark, static conditions for 24 h and the solution was

130

analyzed by ICP-OES.

131

Results and Discussion

132 133

The Ag(I) pyrazine nitrate (SPN) structure (Scheme 1) was synthesized using a slight modification of the literature method.19 The crystals formed within 1 h under low heat, as


6

Page 7 of 30


134

evidenced by the match of the experimental PXRD pattern to the theoretical pattern simulated

135

from single crystal data (Figure 1). The single crystal data and structure refinement indicate a

136

much better structure solution (4.84%) that the previous publication (9.10%) (Table S1). AgNO3

137 138

+

N

N

H2O

Ag N

N

n

NO3

Ag(pyrazine)+NO3-

Scheme 1: Reaction scheme of SPN.

139

140 141

Figure 1: PXRD pattern of SPN: (a) theoretical; (b) as-synthesized.


7


Page 8 of 30

142 143

144

Figure 2: SEM image of a representative needle-shaped crystal of SPN. SPN crystallizes as colorless needle crystals (Figure 2). The crystals are in the Pī space

145

group of the triclinic system. Single crystal XRD revealed that the structure contains one

146

dimensional silver(I) pyrazine chains, -stacked [3.483(2) to 3.975(4) Å] into layers with charge-

147

balancing nitrate anions between the layers (Figure 3). The chains are slightly kinked with Ag-N

148

distance ranging from 2.211(7) to 2.229(7) Å (Table S2). Within the polymeric chain, the N–Ag–

149

N is significantly bent at an angle of 157.4(2)°, likely due to the presence of weakly coordinating

150

oxygen atoms of nearby nitrate anions. The bond length between Ag(I) and the oxygen from

151

nitrate was 2.558(6) Å, creating weak covalent Ag-O bonds47 that play a crucial role in the anion

152

exchangeability (vide infra).


8

Page 9 of 30


153 154

Figure 3: Crystallographic views of SPN: (a) a-projection; (b) b-projection;

155

(c) c-projection (hydrogen atoms are omitted for clarity; silver = gray, nitrogen = blue, oxygen =

156

red, carbon = black).

157

The thermal behavior of SPN was investigated by in-situ variable temperature powder X-

158

ray diffraction (VT-PXRD) and thermogravimetric analysis (TGA), both under nitrogen flow

159

(Figure 4). At 145 °C, an additional unknown crystalline phase appeared [first peak at ~ 12°

160

(2)]. Both the original phase and this new phase are gone by 225 °C, replaced by peaks at ~ 19°,

161

21°, 24° and 29° (2, peaks indicated with asterisks in Figure 4) and correspond to silver nitrate

162

(ICDD PDF #00-043-0649). The TGA trace showed only a single weight loss at ~ 175 °C and is

163

likely due to the partial loss of pyrazine (calculated: 20.8%, observed: 18.1%). At 400 °C, the

164

VT-PXRD shows a mixed phase of silver nitrate, silver oxide (ICDD PDF #03-065-3289, peaks

165

indicated by number signs) and silver metal (ICDD PDF #01-071-5025, peaks indicated by solid

166

diamond).


9


Page 10 of 30

167 168

Figure 4: Thermal analysis of SPN: (left) TGA trace and (right) variable temperature PXRD. (*,

169

# and  denote the most intense peaks of silver nitrate, silver oxide and silver metal,

170

respectively).

171

All of the anion exchange studies of [Ag(pyrazine) +][NO3–] were performed in aqueous

172

conditions and pH 7. The first exchange investigated was organic, using various -

173

alkanedicarboxylate anions. An equimolar ratio of malonate, succinate, glutarate, adipate or

174

sebacate to the CP material was tested in aqueous solution (Figure 5). The principal peak of the

175

as-synthesized nitrate-containing material is at 12.5° (2θ) (Figure 5a), corresponding to a basal

176

spacing of 7.1 Å (Table 1). Based on the relative carbon chain length and size of carbonate end

177

groups [−O2C(CH2)nCO2−], it was expected that succinate (n = 2), glutarate (n = 3), adipate (n =

178

4) and sebacate (n = 8) would shift the principal (200) peak to lower 2θ values as the interlayer

179

distance increases.


10

Page 11 of 30


180 181

Figure 5: PXRD of (a) as-synthesized SPN and after uptake of [−O2C(CH2)nCO2−]: (b) n = 1,

182

malonate; (c) n = 2, succinate; (d) n = 3, glutarate; (e) n = 4, adipate; (f) n = 8, sebacate.

183

Table 1: Principal PXRD peak (2 and d-spacing values) for SPN and the organic-containing

184

materials

Anion

2 (°)

d spacing (Å)

As synthesized

12.5

7.1

Malonate

16.6

5.3

Succinate

11.9

7.4

Glutarate

8.5

10.4

Adipate

8.0

11.0

Sebacate

5.7

15.5

185 186 187

Malonate (n = 1, Figure 5b) shifted to higher 2θ value due to its shortest length. Organic uptake was confirmed by directly synthesizing silver malonate from silver nitrate and disodium


11


Page 12 of 30

188

malonate in a 1:1 ratio. The resultant PXRD pattern was identical to Figure 6c, with slight

189

variation in intensity due to the fine microcrystalline nature of the directly synthesized material.

190 191

Figure 6: PXRD pattern of: (a) as-synthesized SPN (black); (b) after reaction with sodium

192

malonate (red); (c) directly synthesized silver malonate (blue).

193

As expected, longer carbon chains shifted the prominent peak to lower angle, with

194

sebacate being the longest of the dicarboxylates tested (Figure 5d-f). The principal PXRD peak

195

of the [Ag(pyrazine)+][−O2C(CH2)nCO2−] materials and their corresponding d-spacing are

196

reported in Table 1 and plotted in Figure 7.

197


12

Page 13 of 30


198

Figure 7: Principal PXRD peak versus total number of carbons for

199

[Ag(pyrazine)+][−O2C(CH2)nCO2−] (n = 1 to 8).

200

As the number of carbons of the dicarboxylate anion increased, the 2θ value of the 100% peak

201

decreased according to Bragg’s law (Figure 7). Attempts to reverse the exchange have been

202

unsuccessful to date, implying the organic-intercalated materials are of higher stability. The

203

[Ag(pyrazine)+][−O2C(CH2)nCO2−] materials are thermally stable up to 300 °C (Figure S1),

204

which further supports the irreversibility. The appearance of carboxylate peaks in the FTIR

205

spectra also confirms that organic uptake has taken place (Figure 8). The C=O and C-O stretches

206

of carboxylate bands were found at 1570 and 1300 cm−1, respectively.

207 208

Figure 8: FTIR spectra of: (a) as-synthesized SPN; after uptake of [−O2C(CH2)nCO2−]: (b) n = 1,

209

malonate; (c) n = 2, succinate; (d) n = 3, glutarate; (e) n = 4, adipate; (f) n = 8, sebacate.

210

The selectivity amongst the -alkanedicarboxylates was also tested to see if there is a

211

preference between them. The exchange started out with a mixture of even (C2, C4 and C8) or

212

odd (C1, C3 and C8) carbon chain length dicarboxylates (Figure 9). In all tests, sebacate


13


Page 14 of 30

213

[−O2C(CH2)8CO2−] was the only phase observed, likely due to its greater amphiphilicity and thus

214

stability of the n = 8 phase via van der Waals close-packing.

215 216

Figure 9: PXRD pattern of: (a) as-synthesized [Ag(pyrazine)+][NO3−]; (b) the product after

217

malonate, glutarate and sebacate in competition; (c) after succinate, adipate and sebacate in

218

competition; (d) exchange with sebacate only.

219

In addition to α,ω-alkanedicarboxylates, the material displays high capacity inorganic

220

anion exchange for water-borne metal oxo-anion pollutants. Permanganate, perrhenate and

221

tetrafluoroborate were studied as initial examples. The latter was chosen as a comparitive

222

tetrahedral anion whereas permanganate and perrhenate were selected as group 7 surrogates for

223

pertechnetate, which is a problematic radioactive pollutant during the vitrification of nuclear

224

waste.48 An equimolar amount of permanganate and as-synthesized SPN were introduced into

225

aqueous solution under mild stirring. As monitored by UV-Vis spectroscopy, the permanganate

226

concentration rapidly decreased by 32% to 57% with reaction intervals of 0.5 h to 3 h,

227

respectively (Figure 10). The uptake of permanganate was confirmed by PXRD (Figure S2) and

228

was 92% after 24 h with an adsorption capacity of 435 mg/g (0.91 mol/mol). This uptake


14

Page 15 of 30


229

performance is better than SLUG-21 (292 mg/g)32 and Ag[4,4’-bis(1,2,4-

230

triazole)]PF6·0.5CH3CN (342 mg/g).49

231 232

Figure 10: (a) UV-Vis spectra of permanganate solution during anion exchange with SPN at

233

increasing time interval; (b) relative intensity of the 524 nm MnO4– maximum versus time.

234

Similarly, perrhenate exchanged successfully according to PXRD, with the powder

235

pattern corresponding to the directly synthesized [Ag(pyrazine)+][ReO4–] (Figure 11). ICP-OES

236

was used to quantitatively monitor the Re uptake, reaching over 82% removal from solution in

237

8 h (Table 2, Figure 12).


15


Page 16 of 30

238 239

Figure 11: PXRD pattern of: (a) as-synthesized SPN (black); (b) exchanged with ReO4−; (c)

240

directly synthesized [Ag(pyrazine)+][ReO4–].

241 242

Figure 12: Concentration of perrhenate vs. time based on ICP-OES for anion exchange by

243

[Ag(pyrazine)+] [NO3–] (black) and Purolite A530E (red).


16

Page 17 of 30


244

To understand the change in morphology of SPN during anion exchange with perrhenate,

245

in-situ optical microscopy was performed to monitor the transformation between the two

246

crystalline phases (Figure 13). As-synthesized SPN crystals were immersed in an aqueous

247

solution of sodium perrhenate under ambient conditions, yielding the highly crystalline phase

248

[Ag(pyrazine)+][ReO4–]. The formation of [Ag(pyrazine)+][ReO4–] was observed on the surface

249

of the SPN crystals after 40 min. The competitive crystallization allows [Ag(pyrazine)+][ReO4–]

250

to gradually grow in expense of the original SPN crystal to form the distinct new phase and

251

crystal morphology after 60 min. Unlike solid-state equilibrium-driven anion exchange process

252

for LDHs, this crystal-to-crystal transition process indicates that our material undergoes a

253

solvent-mediated recrystallization mechanism typical of this type of material, including SBN.36,37

254 255

Figure 13: In-situ optical micrographs of a single crystal of SPN in sodium perrhenate solution

256

for 10 min (a), 20 min (b), 30 min (c), 40 min (d), 50 min (e) and 60 min (f). Scale bar is 500

257

m.


17


Page 18 of 30

258

Table 2: Adsorption capacity of SPN and Purolite A530E with an equimolar ratio of perrhenate

259

in 50 mL aqueous solution over a 24 h interval, as monitored by ICP-OES

Time (h)

SPN

Purolite A530E

Adsorption (mg/g)

Removal (%)

Adsorption (mg/g)

Removal (%)

1

476.6

47.8

85.6

8.6

2

355.2

35.6

120.4

12.0

4

764.7

76.6

125.5

12.6

8

812.6

81.4

167.7

16.8

24

818.0

82.0

175.0

17.5

260 261

The adsorption capacity of SPN is 818 mg ReO4−/g of material, higher than that of SBN (786

262

mg/g),43 NDTB (720 mg/g),50 , SCU-COF-1 (702.4 mg/g),55 SLUG-21 (602 mg/g),32 SCU-8

263

(540 mg/g),39 SCU-100 (541 mg/g)40, SCU-102 (291 mg/g),56 SCU-101 (217 mg/g)42, UiO-66-

264

NH3+ (159 mg/g)51. The rate of uptake is slower than that of SBN, SCU-8, SCU-100, SCU-101

265

and SCU-COF-1 nor did it reach as high capacity as the recently reported organic polymer, SCU-

266

CPN-1 (999 mg/g).41 Our material is extremely easy to synthesize using water, commerically

267

available reagents and ambient conditions. The higher specific uptake of SPN versus the other

268

CP/MOF type materials is likely due to the shorter and thus lighter organic linker, coupled with a

269

higher cationic charge density and thus anion density. PXRD before and after anion exchange

270

confirmed that SPN retains its crystalline layered character after intercalation, with the d-spacing

271

slightly increasing from 7.0 to 7.4 Å due to the larger anion (Figure 14). The exchange for both

272

permanganate and perrhenate were irreversible after all attempts. Reusability is, in fact,

273

undesirable for a highly problematic pollutant such as the radionuclide pertechnetate.


18

Page 19 of 30


274 275

Figure 14: PXRD spectra of as-synthesized SPN (a) and after exchange with MnO4− (b), ReO4−

276

(c) and BF4− (d).

277

Since BF4−, MnO4− and ReO4− are all tetrahedral geometry, we were interested in the

278

selectivity. According to PXRD data, perrhenate outperformed the other anions (Figure 15).

279


19


280

Figure 15: PXRD spectra of SPN after exchange with: (a) ReO4− only; (b) BF4− and ReO4− in

281

competition; (c) BF4−, MnO4− and ReO4− in competition.

Page 20 of 30

282

Given the high adsorption capacity of [Ag(pyrazine)+][ReO4–], we also performed the

283

competition study with chloride (Cl–) which is commonly present in water (Figure 16). The

284

selectivity of SPN for perrhenate over chloride was demonstrated by performing two lower

285

chloride concentration tests containing 100 ppm and 200 ppm, as evidenced by PXRD (Figure

286

16b,c). In both tests it was observed that the chloride did not interfere with the uptake of

287

perrhenate. When SPN is exposed to an equimolar ratio of ReO4– and Cl–, the resulting mixture

288

gave rise to pure-phase AgCl (Figure 16d).

289 290

Figure 16: PXRD pattern of SPN exchange with (a) ReO4– only in nanopore water; (b) ReO4–

291

and 200 ppm Cl– in tap water; (c) ReO4– and 100 ppm Cl– in tap water; (d) ReO4– and Cl– in

292

equimolar ratio.


20

Page 21 of 30

293


We attempted to prepare crystals suitable for single crystal X-ray diffraction in order to

294

have a deeper understanding of the specific binding. Among them, only [Ag(pyrazine)+][ReO4–]

295

successfully yielded colorless needle-type crystals, matching the theoretical pattern based on the

296

crystal data reported by Maggard et. al.52 The ReO4− tetrahedra, which reside in the space

297

between the silver pyrazine layers, are separated from each other by 4.61 Å (O1-O1’). Each

298

ReO4− tetrahedron bonds via three O vertices to three different Ag+ in the layer [Ag–O distance

299

2.603(3) to 2.686(5) Å], creating stronger silver to oxygen bonds than BF4– and MnO4– anions

300

(Figure 17). Indeed, Wang et al. reported density functional theory (DFT) analysis for the

301

bonding of a similar silver(I) polymer, [Ag(4,4’-bipyridine)+][ReO4–], where ReO4– has a

302

stronger electrostatic interaction with the polymers that creates a better match of coordinating

303

environment compared to other anions such as BF4– and MnO4– .43

304 305

Figure 17: Crystallographic views of the [Ag(pyrazine)+][ReO4–] structure (hydrogen atoms

306

omitted for clarity; silver = gray, nitrogen = blue, oxygen = red, carbon = black).

307 308 309

A silver leaching measurement was carried out to verify the stability of the SPN material and to confirm the heterogenous nature of the CP. The material was placed in solution and the


21


Page 22 of 30

310

latter was analyzed after 24 h using ICP-OES in order to measure the leached silver. The

311

concentration of the leached silver in the solution was found to be less than 2% for all the

312

samples (Table 3). This may be due to the strong interaction of silver with nitrogen from

313

pyrazine groups which prevents the leaching of silver from the polymer matrix. Table 3: The

314

concentration of leached silver from SPN was measured by ICP-OES. The data was collected at

315

328.06 wavelength (nm) for silver Silver concentration (ppm)

% silver loss

0.54

0.05

25.54

0.24

48.13

0.45

100.80

0.93

158.22

1.46

316 317

Figure 18: PXRD spectra: (a) after reaction of SPN with salicylic acid; (a-i) directly synthesized

318

silver salicylate; (b) after reaction of SPN with p-terephthalate; (b-i) directly synthesized silver


22

Page 23 of 30


319

terephthalate; (c) after reaction of SPN with 2,6-naphthalene dicarboxylate; (c-i) directly

320

synthesized silver 2,6-naphthalene dicarboxylate.

321

Attempts to intercalate other aromatic dicarboxylates such as salicylic acid, p-

322

terephthalate, and 2,6-naphthalene dicarboxylate were not successful, likely due to the limited

323

aqueous solubility of these analytes at neutral pH. Other reports of the intercalation of

324

terephthalate derivatives into cationic materials occurred in basic aqueous solutions.53,54 PXRD

325

data revealed that the exchange products turned out to be identical to the directly synthesized

326

silver dicarboxylates (Figure 18), confirming that pyrazine in this case had been lost upon the

327

exchange attempt.

328

The ability to modify the N-donor linker for these Ag-based cationic CP materials may

329

allow tuning of the anion propensity for water purification and pollution abatement. The cationic

330

material silver(I) pyrazine shows the highest group 7 oxo-anion uptake (435 and 818 mg/g for

331

permanganate and perrhenate, respectively) to date for a metal-organic extended structure,

332

making it potentially useful to trap pertechnetate. The capacity and kinetics far outperform the

333

anion exchange resin Purolite 530E.57 Unlike some of the recently reported cationic MOFs, all of

334

the synthesis and exchange occur aqueously with commercially available reagents. With the

335

formation of a new crystal structure driving the reaction, the anions become incorporated into a

336

structure. Reuse of the material would, in fact, be undesirable for a highly problematic

337

radionuclide. The material also displays uptake toward organic water-borne pollutants through a

338

series of α,ω-alkanedicarboxylates.

339 340

ASSOCIATED CONTENT


23


Page 24 of 30

341

Supporting Information. Crystal data tables of [Ag(pyrazine)+][NO3–] (SPN), TGA of

342

[Ag(pyrazine)+][−O2C(CH2)nCO2−] exchange products and PXRD of the kinetic studies for

343

[Ag(pyrazine)+][MnO4–]. This material is available free of charge via the Internet at

344

http://pubs.acs.org.

345

AUTHOR INFORMATION

346

Corresponding Author

347

*Email: [email protected]

348

Author Contributions

349

The manuscript was written through contributions of all authors. All authors have given approval

350

to the final version of the manuscript.

351

Funding Sources

352

This work was supported by the National Science Foundation under Grant No. 1603754 from the

353

CBET Environmental Engineering GOALI Program.

354

Notes

355

ACKNOWLEDGMENTS

356

This work was supported by the National Science Foundation under Grant No. 1603754 from the

357

CBET Environmental Engineering GOALI Program. We thank Professor Timothy C. Johnstone,

358

University of California, Santa Cruz, Department of Chemistry and Biochemistry for solving the

359

twinned data set. We also thank Professor Allen Oliver of the University of Notre Dame,

360

Department of Chemistry and Biochemistry and the American Crystallographic Association

361

2018 Summer Course for data collection.


24

Page 25 of 30


362

REFERENCES

363 364 365 366 367 368 369 370 371 372 373 374 375 376 377 378 379 380 381 382 383 384 385 386 387 388 389 390 391 392 393 394 395 396 397 398 399 400 401 402 403 404 405

(1) (2) (3)

(4) (5) (6)

(7) (8) (9)

(10) (11)

(12) (13)

(14)

Jasinski, R. A New Fuel Cell Cathode Catalyst. Nature 1964, 201 (4925), 1212–1213. https://doi.org/10.1038/2011212a0. Humphrey, S. M.; Wood, P. T. Multiple Areas of Magnetic Bistability in the Topological Ferrimagnet [Co3(NC5H3(CO2)2-2,5)2(Μ3-OH)2(OH2)2]. J. Am. Chem. Soc. 2004, 126 (41), 13236–13237. https://doi.org/10.1021/ja046351l. Dong, Y.-B.; Jin, G.-X.; Smith, M. D.; Huang, R.-Q.; Tang, B.; zur Loye, H.-C. [Ag2(C33H26N2O2)(H2O)2(SO3CF3)2]·0.5C6H6: A Luminescent Supramolecular Silver(I) Complex Based on Metal−Carbon and Metal−Heteroatom Interactions. Inorg. Chem. 2002, 41 (19), 4909–4914. https://doi.org/10.1021/ic020228i. Furukawa, H.; Cordova, K. E.; O’Keeffe, M.; Yaghi, O. M. The Chemistry and Applications of Metal-Organic Frameworks. Science 2013, 341 (6149), 1230444-11230444-12. https://doi.org/10.1126/science.1230444. Oliver, S. R. J. Cationic Inorganic Materials for Anionic Pollutant Trapping and Catalysis. Chem. Soc. Rev. 2009, 38 (7), 1868–1881. https://doi.org/10.1039/B710339P. Fujita, M.; Kwon, Y. J.; Washizu, S.; Ogura, K. Preparation, Clathration Ability, and Catalysis of a Two-Dimensional Square Network Material Composed of Cadmium(II) and 4,4’-Bipyridine. J. Am. Chem. Soc. 1994, 116 (3), 1151–1152. https://doi.org/10.1021/ja00082a055. Seo, J. S.; Whang, D.; Lee, H.; Jun, S. I.; Oh, J.; Jeon, Y. J.; Kim, K. A Homochiral Metal–Organic Porous Material for Enantioselective Separation and Catalysis. Nature 2000, 404 (6781), 982–986. https://doi.org/10.1038/35010088. Batten, S. R.; Robson, R. Interpenetrating Nets: Ordered, Periodic Entanglement. Angew. Chem. Int. Ed. 1998, 37 (11), 1460–1494. https://doi.org/10.1002/(SICI)15213773(19980619)37. Blake, A. J.; Champness, N. R.; Hubberstey, P.; Li, W.-S.; Withersby, M. A.; Schröder, M. Inorganic Crystal Engineering Using Self-Assembly of Tailored Building-Blocks. Coord. Chem. Rev. 1999, 183 (1), 117–138. https://doi.org/10.1016/S00108545(98)00173-8. Hong, M.-C.; Chen, L. Design and Construction of Coordination Polymers. In Silver(I) Coordination Polymers; Su, C-Y.; John Wiley & Sons, Inc.: New Jersey, 2009; 111–144. Khlobystov, A. N.; Blake, A. J.; Champness, N. R.; Lemenovskii, D. A.; Majouga, A. G.; Zyk, N. V.; Schröder, M. Supramolecular Design of One-Dimensional Coordination Polymers Based on Silver(I) Complexes of Aromatic Nitrogen-Donor Ligands. Coord. Chem. Rev. 2001, 222 (1), 155–192. https://doi.org/10.1016/S0010-8545(01)00370-8. Chen, C.-L.; Kang, B.-S.; Su, C.-Y. Recent Advances in Supramolecular Design and Assembly of Silver(i) Coordination Polymers. Aust. J. Chem. 2006, 59 (1), 3–18. https://doi.org/10.1071/CH05225. Munakata, M.; Wu, L. P.; Kuroda-Sowa, T. Toward the Construction of Functional SolidState Supramolecular Metal Complexes Containing Copper(I) And Silver(I). In Advances in Inorganic Chemistry; Sykes, A. G., Ed.; Academic Press, 1998; 46, 173–303. https://doi.org/10.1016/S0898-8838(08)60151-8. Stoehr, C. Ueber Pyrazine. J. Für Prakt. Chem. 1893, 48 (1), 18–23. https://doi.org/10.1002/prac.18930480103.


25


406 407 408 409 410 411 412 413 414 415 416 417 418 419 420 421 422 423 424 425 426 427 428 429 430 431 432 433 434 435 436 437 438 439 440 441 442 443 444 445 446 447 448 449 450 451

Page 26 of 30

(15) Wolff, L. Synthese Des Pyrazins. Berichte Dtsch. Chem. Ges. 1893, 26 (2), 1830–1833. https://doi.org/10.1002/cber.189302602132. (16) Schmidt, J. G.; Trimble, R. F. The Stability Constants of the Mono- and Dipyrazine Silver Complexes. J. Phys. Chem. 1962, 66 (6), 1063–1065. https://doi.org/10.1021/j100812a022. (17) Stidham, H. D.; Chandler, J. A. Chemical and Infra-Red Spectroscopic Studies of Metal(II) Halide Complexes of Pyrazine. J. Inorg. Nucl. Chem. 1965, 27 (2), 397–403. https://doi.org/10.1016/0022-1902(65)80358-X. (18) Pierce, J. L.; Busch, K. L.; Cooks, R. G.; Walton, R. A. Secondary-Ion Mass Spectra of Nonvolatile Silver Complexes. Inorg. Chem. 1983, 22 (18), 2492–2494. https://doi.org/10.1021/ic00160a005. (19) Vranka, R. G.; Amma, E. L. Metal Ion-Aromatic Complexes. II. The Crystal Structure of the 1:1 Silver Nitrate-Pyrazine Complex. Inorg. Chem. 1966, 5 (6), 1020–1025. https://doi.org/10.1021/ic50040a016. (20) Che, C.-M.; Lau, T.-C. Ruthenium and Osmium: High Oxidation States. In Comprehensive Coordination Chemistry II; McCleverty, J. A., Meyer, T. J., Eds.; Pergamon: Oxford, 2003; 733–847. https://doi.org/10.1016/B0-08-043748-6/04215-8. (21) Keith, L.; Telliard, W. ES&T Special Report: Priority Pollutants: I-a Perspective View. Environ. Sci. Technol. 1979, 13 (4), 416–423. https://doi.org/10.1021/es60152a601. (22) Izak, P.; Hrma, P.; Arey, B. W.; Plaisted, T. J. Effect of Feed Melting, Temperature History, and Minor Component Addition on Spinel Crystallization in High-Level Waste Glass. J. Non-Crystalline Solids 2001, 28 (1), 17 – 29. https://doi.org/10.1016/S00223093(01)00705-0. (23) Daughton, C. G. PPCPs in the Environment: Future Research — Beginning with the End Always in Mind. In Pharmaceuticals in the Environment; Springer, Berlin, Heidelberg, 2004; 463–495. https://doi.org/10.1007/978-3-662-09259-0_33. (24) Castiglioni, S.; Bagnati, R.; Fanelli, R.; Pomati, F.; Calamari, D.; Zuccato, E. Removal of Pharmaceuticals in Sewage Treatment Plants in Italy. Environ. Sci. Technol. 2006, 40 (1), 357–363. https://doi.org/10.1021/es050991m. (25) Jana, S.; Praharaj, S.; Panigrahi, S.; Basu, S.; Pande, S.; Chang, C.-H.; Pal, T. LightInduced Hydrolysis of Nitriles by Photoproduced α-MnO2 Nanorods on Polystyrene Beads. Org. Lett. 2007, 9 (11), 2191–2193. https://doi.org/10.1021/ol070750e. (26) Praharaj, S.; Nath, S.; Panigrahi, S.; Ghosh, S. K.; Basu, S.; Pande, S.; Jana, S.; Pal, T. Layer-by-Layer Deposition of Bimetallic Nanoshells on Functionalized Polystyrene Beads. Inorg. Chem. 2006, 45 (4), 1439–1441. https://doi.org/10.1021/ic051915n. (27) Mark, R.; Findley, W. N. Thermal Expansion Instability and Creep in Amine-Cured Epoxy Resins. Polym. Eng. Sci. 1978, 18 (1), 6–15. https://doi.org/10.1002/pen.760180103. (28) Chibwe, K.; Jones, W. Intercalation of Organic and Inorganic Anions into Layered Double Hydroxides. J. Chem. Soc. Chem. Commun. 1989, 0 (14), 926–927. https://doi.org/10.1039/C39890000926. (29) Hibino, T.; Tsunashima, A. Characterization of Repeatedly Reconstructed Mg−Al Hydrotalcite-like Compounds: Gradual Segregation of Aluminum from the Structure. Chem. Mater. 1998, 10 (12), 4055–4061. https://doi.org/10.1021/cm980478q. (30) Li, C.-P.; Chen, J.; Guo, W.; Du, M. Anion-Directed Assembly and Crystal Transformation of Ag(I) Coordination Polymers with a Versatile Tripyridyltriazole Ligand


26

Page 27 of 30

452 453 454 455 456 457 458 459 460 461 462 463 464 465 466 467 468 469 470 471 472 473 474 475 476 477 478 479 480 481 482 483 484 485 486 487 488 489 490 491 492 493 494 495 496 497


(31)

(32) (33) (34) (35) (36) (37) (38)

(39)

(40)

(41) (42)

(43)

3,4-Bis(2-Pyridyl)-5-(4-Pyridyl)-1,2,4-Triazole. J. Solid State Chem. 2015, 223, 95–103. https://doi.org/10.1016/j.jssc.2014.06.038. Du, M.; Zhao, X.-J.; Guo, J.-H.; R. Batten, S. Direction of Topological Isomers of Silver( i ) Coordination Polymers Induced by Solvent , and Selective Anion-Exchange of a Class of PtS-Type Host Frameworks. Chem. Commun. 2005, 0 (38), 4836–4838. https://doi.org/10.1039/B508479B. Fei, H.; Bresler, M. R.; Oliver, S. R. J. A New Paradigm for Anion Trapping in High Capacity and Selectivity: Crystal-to-Crystal Transformation of Cationic Materials. J. Am. Chem. Soc. 2011, 133 (29), 11110–11113. https://doi.org/10.1021/ja204577p. Fei, H.; Oliver, S. R. J. Copper Hydroxide Ethanedisulfonate: A Cationic Inorganic Layered Material for High-Capacity Anion Exchange. Angew. Chem. Int. Ed. 2011, 50 (39), 9066–9070. https://doi.org/10.1002/anie.201104200. Fei, H.; Rogow, D. L.; Oliver, S. R. J. SLUG 22- Reversible Anion Exchange and Catalytic Properties of Two Cationic Metal−Organic Frameworks Based on Cu(I) and Ag(I). J. Am. Chem. Soc. 2010, 132 (20), 7202–7209. https://doi.org/10.1021/ja102134c. Fei, H.; Han, C. S.; Robins, J. C.; Oliver, S. R. J. SLUG-35 A Cationic Metal–Organic Solid Solution Based on Co(II) and Zn(II) for Chromate Trapping. Chem. Mater. 2013, 25 (5), 647–652. https://doi.org/10.1021/cm302585r. Colinas, I. R.; Silva, R. C.; Oliver, S. R. J. Reversible, Selective Trapping of Perchlorate from Water in Record Capacity by a Cationic Metal–Organic Framework. Environ. Sci. Technol. 2016, 50 (4), 1949–1954. https://doi.org/10.1021/acs.est.5b03455. R. Colinas, I.; K. Inglis, K.; Blanc, F.; J. Oliver, S. R. Anion Exchange Dynamics in the Capture of Perchlorate by a Cationic Ag-Based MOF. Dalton Trans. 2017, 46 (16), 5320– 5325. https://doi.org/10.1039/C7DT00475C. Citrak, S. C.; Popple, D.; Delgado-Cunningham, K.; Tabler, K.; Bdeir, K.; Oliver, A. G.; Kvam, P. B.; Oliver, S. R. J. Extremely Rapid Uptake of Perchlorate with Release of an Environmentally Benign Anion: Silver Bipyridine Acetate. Cryst. Growth Des. 2018, 18 (3), 1891–1895. https://doi.org/10.1021/acs.cgd.7b01797. Li, Y.; Yang, Z.; Wang, Y.; Bai, Z.; Zheng, T.; Dai, X.; Liu, S.; Gui, D.; Liu, W.; Chen, M. A Mesoporous Cationic Thorium-Organic Framework That Rapidly Traps Anionic Persistent Organic Pollutants. Nat. Commun. 2017, 8 (1), 1-11. https://doi.org/10.1038/s41467-017-01208-w. Sheng, D.; Zhu, L.; Xu, C.; Xiao, C.; Wang, Y.; Wang, Y.; Chen, L.; Diwu, J.; Chen, J.; Chai, Z. Efficient and Selective Uptake of TcO4– by a Cationic Metal–Organic Framework Material with Open Ag+ Sites. Environ. Sci. Technol. 2017, 51 (6), 3471– 3479. https://doi.org/10.1021/acs.est.7b00339. Li, J.; Dai, X.; Zhu, L.; Xu, C.; Zhang, D.; Silver, M. A.; Li, P.; Chen, L.; Li, Y.; Zuo, D. 99TcO4− Remediation by a Cationic Polymeric Network. Nat. Commun. 2018, 9 (1), 111. https://doi.org/10.1038/s41467-018-05380-5. Zhu, L.; Sheng, D.; Xu, C.; Dai, X.; Silver, M. A.; Li, J.; Li, P.; Wang, Y.; Wang, Y.; Chen, L.; Identifying the Recognition Site for Selective Trapping of 99TcO4– in a Hydrolytically Stable and Radiation Resistant Cationic Metal–Organic Framework. J. Am. Chem. Soc. 2017, 139 (42), 14873–14876. https://doi.org/10.1021/jacs.7b08632. Zhu, L.; Xiao, C.; Dai, X.; Li, J.; Gui, D.; Sheng, D.; Chen, L.; Zhou, R.; Chai, Z.; Albrecht-Schmitt, T. E. Exceptional Perrhenate/Pertechnetate Uptake and Subsequent Immobilization by a Low-Dimensional Cationic Coordination Polymer: Overcoming the


27


498 499 500 501 502 503 504 505 506 507 508 509 510 511 512 513 514 515 516 517 518 519 520 521 522 523 524 525 526 527 528 529 530 531 532 533 534 535 536 537 538 539 540 541 542

(44) (45)

(46)

(47) (48) (49)

(50)

(51)

(52) (53)

(54) (55)

Page 28 of 30

Hofmeister Bias Selectivity. Environ. Sci. Technol. Lett. 2017, 4 (7), 316–322. https://doi.org/10.1021/acs.estlett.7b00165. Custelcean, R. Anions in Crystal Engineering. Chem. Soc. Rev. 2010, 39 (10), 3675–3685. https://doi.org/10.1039/B926221K. Wang, T. C.; Vermeulen, N. A.; Kim, I. S.; Martinson, A. B. F.; Stoddart, J. F.; Hupp, J. T.; Farha, O. K. Scalable Synthesis and Post-Modification of a Mesoporous MetalOrganic Framework Called NU-1000. Nat. Protoc. 2016, 11 (1), 149–162. https://doi.org/10.1038/nprot.2016.001. Drout, R. J.; Otake, K.; Howarth, A. J.; Islamoglu, T.; Zhu, L.; Xiao, C.; Wang, S.; Farha, O. K. Efficient Capture of Perrhenate and Pertechnetate by a Mesoporous Zr Metal– Organic Framework and Examination of Anion Binding Motifs. Chem. Mater. 2018, 30 (4), 1277–1284. https://doi.org/10.1021/acs.chemmater.7b04619. Lindley, P. F.; Woodward, P. An X-Ray Investigation of Silver Nitrate: A Unique Metal Nitrate Structure. J. Chem. Soc. Inorg. Phys. Theor. 1966, 0 (0), 123–126. https://doi.org/10.1039/J19660000123. Braterman, P. S.; Phol, P. I.; Xu, Z.-P.; Brinker, C. J.; Yang, Y.; Bryan, C. R.; Yu, K.; Xu, H.; Wang, Y.; Gao, H. Potential Applications of Nanostructured Materials in Nuclear Waste Management.; SAND2003-3313, 917460; 2003. https://doi.org/10.2172/917460. Li, X.; Gong, Y.; Zhao, H.; Wang, R. Anion-Directed Assemblies of Cationic Metal– Organic Frameworks Based on 4,4′-Bis(1,2,4-Triazole): Syntheses, Structures, Luminescent and Anion Exchange Properties. Inorg. Chem. 2014, 53 (22), 12127–12134. https://doi.org/10.1021/ic501978u. Wang, S.; Alekseev, E. V.; Diwu, J.; Casey, W. H.; Phillips, B. L.; Depmeier, W.; Albrecht‐Schmitt, T. E. NDTB-1: A Supertetrahedral Cationic Framework That Removes TcO4− from Solution. Angew. Chem. Int. Ed. 2010, 49 (6), 1057–1060. https://doi.org/10.1002/anie.200906397. Banerjee, D.; Xu, W.; Nie, Z.; Johnson, L. E. V.; Coghlan, C.; Sushko, M. L.; Kim, D.; Schweiger, M. J.; Kruger, A. A.; Doonan, C. J. Zirconium-Based Metal–Organic Framework for Removal of Perrhenate from Water. Inorg. Chem. 2016, 55 (17), 8241– 8243. https://doi.org/10.1021/acs.inorgchem.6b01004. Lin, H.; Yan, B.; Boyle, P. D.; Maggard, P. A. Synthesis and Properties of PyrazinePillared Ag3Mo2O4F7 and AgReO4 Layered Phases. J. Solid State Chem. 2006, 179 (1), 217–225. https://doi.org/10.1016/j.jssc.2005.10.037. Millange, F.; Walton, R. I.; Lei, L.; O‘Hare, D. Efficient Separation of Terephthalate and Phthalate Anions by Selective Ion-Exchange Intercalation in the Layered Double Hydroxide Ca2Al(OH)6·NO3·2H2O. Chem. Mater. 2000, 12 (7), 1990–1994. https://doi.org/10.1021/cm0002057. Crepaldi, E. L.; Tronto, J.; Cardoso, L. P.; Valim, J. B. Sorption of Terephthalate Anions by Calcined and Uncalcined Hydrotalcite-like Compounds. Colloids Surf. Physicochem. Eng. Asp. 2002, 211 (2), 103–114. https://doi.org/10.1016/S0927-7757(02)00233-9. He, L.; Liu, S.; Chen, L.; Dai, X.; Li, J.; Zhang, M.; Ma, F.; Zhang, C.; Yang, Z.; Zhou, R. Mechanism Unravelling for Ultrafast and Selective 99TcO4− Uptake by a RadiationResistant Cationic Covalent Organic Framework: A Combined Radiological Experiment and Molecular Dynamics Simulation Study. Chem. Sci. 2019, 10 (15), 4293–4305. https://doi.org/10.1039/C9SC00172G.


28

Page 29 of 30

543 544 545 546 547 548 549 550 551


(56) Sheng, D.; Zhu, L.; Dai, X.; Xu, C.; Li, P.; Pearce, C. I.; Xiao, C.; Chen, J.; Zhou, R.; Duan, T. Successful Decontamination of 99TcO4− in Groundwater at Legacy Nuclear Sites by a Cationic Metal-Organic Framework with Hydrophobic Pockets. Angewandte Chemie International Edition 2019, 58 (15), 4968–4972. https://doi.org/10.1002/anie.201814640. (57) Li, J.; Zhu, L.; Xiao, C.; Chen, L.; Chai, Z.; Wang, S. Efficient Uptake of Perrhenate/Pertechnenate from Aqueous Solutions by the Bifunctional Anion-Exchange Resin. Radiochimica Acta 2018, 106 (7), 581–591. https://doi.org/10.1515/ract-2017-2829


29


83x47mm (300 x 300 DPI)


Page 30 of 30