Anisotropic Self-Oscillating Reaction in Liquid Crystalline Nanosheet

Feb 17, 2018 - Research Institute for Sustainable Chemistry, National Institute of Advanced Industrial Science and Technology (AIST), Tsukuba Central ...
0 downloads 11 Views 690KB Size
Subscriber access provided by UNIV OF NEW ENGLAND ARMIDALE

Article

Anisotropic Self-Oscillating Reaction in Liquid Crystalline Nanosheets Hydrogels Morio Shintate, Takumi Inadomi, Shinya Yamamoto, Yusuke Kuboyama, Yutaka Ohsedo, Takashi Arimura, Tomoka Nakazumi, Yusuke Hara, and Nobuyoshi Miyamoto J. Phys. Chem. B, Just Accepted Manuscript • DOI: 10.1021/acs.jpcb.7b11631 • Publication Date (Web): 17 Feb 2018 Downloaded from http://pubs.acs.org on February 17, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

The Journal of Physical Chemistry B is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Anisotropic Self-Oscillating Reaction in Liquid Crystalline Nanosheets Hydrogels

Morio Shintate,1 Takumi Inadomi,1 Shinya Yamamoto,1 Yusuke Kuboyama,1 Yutaka Ohsedo,1 Takashi Arimura,2 Tomoka Nakazumi,2 Yusuke Hara,2* and Nobuyoshi Miyamoto1*

1

Department of Life, Environment and Materials Science, Fukuoka Institute of

Technology, 3-30-1, Wajirohigashi, Higashiku, Fukuoka 811-0295, Japan 2

National Institute of Advanced Industrial Science and Technology (AIST), AIST

Central 5–2, Tsukuba 305-8565, Japn

*

corresponding authors: [email protected], [email protected]

1 ACS Paragon Plus Environment

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ABSTRACT.

Anisotropic

Belouzov-Zhabozinsky

chemical

(BZ)

wave

reaction

Page 2 of 24

propagation was

of

self-oscillating

demonstrated

in

the

poly(N-isopropylacrylamide gel films embedded with macroscopically aligned liquid crystalline inorganic nanosheets. While the average propagation rate of chemical wave ̅ was 3.56 mm min-1 in the gels without nanosheets, the propagation was retarded in the gels with 1 wt% of nanosheets: ∥ = 1.89 mm min-1 and   

= 1.33 mm min-1

along the direction parallel and perpendicular to the nanosheet planes, respectively. Thus, the wave propagation is anisotropic with the anisotropy ratio  ∥ / = 1.42 in these gels and the periodic patterns formed by the BZ-reaction were concentric ellipses, different from circles seen in isotropic gels. Furthermore, the propagation rate and degree of anisotropy were controllable by nanosheet concentration. These phenomena can be explained that the diffusion of molecules inside the gel is effectively hindered along the direction perpendicular to the nanosheet planes due to very large aspect ratio of the aligned nanosheets. The present systems will be applicable for anisotropic self-oscillating soft actuators with one-dimensional motions as well as for ideal model system of BZ reactions.

2 ACS Paragon Plus Environment

Page 3 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

INTRODUCTION

Soft and wet structures with anisotropy and hierarchy are regarded as key for various intriguing functions and properties of living organisms. Liquid crystal (LC) materials are often utilized to artificially fabricate such sophisticated structures like living organisms.1-2 For this purpose, lyotropic LC phases of inorganic nanosheets are emerging as a new type of LC materials due to many fascinating characteristics.3-4 Actually, inorganic nanosheet LCs have been utilized as unusual anisotropic reaction media,5-6 the materials to fabricate tough fibers 10

7-8

and inorganic-polymer composites.9

The most distinctive feature of inorganic nanosheet LCs is that they can effectively

barrier the diffusion of molecules. Since the nanosheets are two dimensional objects with huge aspect ratio (the lateral dimension of several micrometer and the thickness of ~1 nm), aligned nanosheets can effectively retard molecular diffusion compared to the materials made with conventional LC molecules.11 We recently communicated that dye ions anisotropically diffuse into the polymer gel embedded with macroscopically aligned LC nanosheets.10 Meanwhile, combining artificial soft and wet structures with particular

3 ACS Paragon Plus Environment

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 24

chemical reactions that have characteristic features of biological systems is fascinating because such combinations will lead us to fabrication of artificial living organisms or molecular robots.12 Yoshida et al. reported the hydrogel of poly(N-isopropylacrylamide) (pNIPA) copolymerized with ruthenium trisbipyridine (Ru(bpy)3) units, which is a catalyst of self-oscillating Belouzov-Zhabozinsky reaction (BZ-reaction).13 Not only BZ reaction proceeded in this gel, but also the gel showed self-oscillating motion. After this pioneering work, many kinds of self-oscillating gels with improved properties such as faster and larger oscillation, were reported14-17 in view of applications for micro-robotics and micro electro mechanical systems (MEMS). The concentric circles18 or rotating spiral 19 waves that appear during BZ reaction is also interesting phenomena as a model of chemical waves in biological systems19 such as embryo, neural networks, and heart muscles. In this context, controlling and modifying the wave patterns in anisotropic, heterogeneous, or patterned media are interested. The BZ-reactions under electric field,

20

in the lamellar phase of surfactant solution

21

and in a porous glass22

were investigated to control the reaction. However, anisotropic BZ reaction has not been investigated so far.

4 ACS Paragon Plus Environment

Page 5 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Herein, we demonstrate the anisotropic propagation of chemical waves of BZ reaction for the first time in anisotropic composite gel comprising aligned LC nanosheets. To realize this, we successfully synthesized very large anisotropic gel sheet in which fully aligned nanosheets are embedded.

EXPERIMENTAL

N-isopropylacrylamide (NIPA; monomer) and N,N’-methylenbisacrylamide (chemical cross-linker) were used after recrystallization from hexane/acetone mixture. The photo-initiator 2-hydroxy-2-methylpropiophenon was used without purification. The LC layered clay mineral, fluorohectorite (FHT), was supplied from Topy Industries Inc. and purified by centrifugation before use. The nanosheet/water colloid is very stable and no aggregation nor precipitation is observed for years. The average lateral size of the nanosheets is 2.2 µm as confirmed by transmission electron microscopy, while the size distributes broadly from ~100 nm to ~10 µm.23 The synthesis of the gel sheets was conducted as follows by slightly modifying the process we recently published24. First, 6.5 mmol of the monomer, 0.065 mmol of the chemical cross-linker, and 0.061 µmol of

5 ACS Paragon Plus Environment

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 24

the photo-initiator were dissolved in 10 ml of the FHT aqueous dispersion (1 or 0.5 wt%). This solution was sealed in a 1 mm-thick cell constructed with a silicon rubber sheet, two glass plates and aluminum electrodes, followed by applying AC electric field (10 kHz and 2 V mm-1) for 1 h (Figure 1a). Thereafter, by irradiating ultraviolet light for 5 min, photo-polymerization was carried out. After polymerization, the nanosheets are immobilized in the polymer network, of which mesh size is much smaller than the lateral size of the nanosheets, so that the orientation of the nanosheets is retained even after removing the electric field. The structure of the anisotropic composite gel was characterized by observation with crossed-polarizers and the optical waveplate with retardation R of 530 nm. Small angle X - ray scattering measurements (SAXS; Rigaku NANO-PIX) were also performed. For the BZ reaction, the aqueous solution containing sodium bromate (0.24 M), sodium bromide (0.12 mM), malonic acid (0.069 mM), sulfuric acid (0.043 mM), and ferroin (0.043 mM) was prepared in a glass dish. After immersing the composite gel in the solution for 10 minutes, the gel was taken out from the dish and observed in air with a digital camera (CASIO EX-ZR 1000). The reaction was conducted in a room air-conditioned at around 23ºC to avoid the influences of

6 ACS Paragon Plus Environment

Page 7 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

temperature difference on the BZ reaction.15, 25-26

RESULTS AND DISCUSSION

Uniform macroscopic alignment of LC nanosheets in the pNIPA gel was assured by crossed polarizer observation and SAXS (Figure 1). In the observation of the gel with the crossed polarizers (Figure 1b), uniformly blue and yellow interference colors, which correspond to the retardation R of >530 nm and < 530 nm, are observed when the waveplate (R = 530 nm) was set with its slow axis parallel and perpendicular to the electric field direction, respectively. It is known that the total R is the sum of R for the sample and waveplate when the slow axis of the waveplate are parallel to each other, while total R is the difference between them when the axes are perpendicular to each other. Thus we assure that the nanosheets are preferentially aligned along the electric field, considering that the slow axis of the nanosheet LC domain is parallel to the nanosheet plains inside the domain.24 It is known that electric-field-induced polarization of counter cation cloud around the negatively charged nanosheet cause the nanosheet orientation.27

7 ACS Paragon Plus Environment

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 24

SAXS measurements (Figure 1c-f) further confirm the preferential orientation of the nanosheets on macroscopic scale as well as good dispersion and well-regulated super-structure formed by the nanosheets on mesoscopic scale. The anisotropic 2D scattering pattern (Figure 1c) and the sharp peaks in the I vs χ profile (Figure 1d) indicate the strong alignment of the nanosheets. From the I vs χ profile, nematic order parameter S = 0.93 was estimated. In the I(q) vs q profile (Figure 1e), the overall profile with the power law of q-2 and q-3 are observed at χ = 0º, and 90 º, respectively. These are ascribable to the form factor of oriented nanosheets.28 In addition, the peak at q = 0.11 nm-1 (d = 2π/q = 57 nm) is observable in the I•q2 vs q plot (Figure 1f), showing the presence of a weak short-range structural order of the nanosheets. Because the structural order is low, the nanosheets are regarded as in nematic state. It is noticeable that the oriented mono-domain as large as 30 mm × 30 mm is obtained, which is suitable for the investigation of anisotropic BZ reactions. While the mono-domain of 5 mm × 30 mm was already obtained in the previous study,24 we optimized the synthetic condition to realize this larger mono-domain gel sheet.

8 ACS Paragon Plus Environment

Page 9 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

An important point in the present study is that the composite gel for BZ-reaction is synthesized by the very simple synthetic procedure, electric field-assisted alignment of the nanosheets, photo-polymerization, and adsorption of the catalyst by post-process, in contrast with rather complicated processes of previous BZ-gels.13 Visible absorption spectroscopy confirms that most of the ferroin cations, that are the catalyst for BZ reaction, are strongly adsorbed on the surface of the nanosheets in the gel. In the spectrum (Figure 2a) of the aqueous ferroin solution, the absorption maximum due to ferroin is observed at 510nm. In contrast, the composite gel after BZ reaction (Figure 2c) and the nanosheet colloid (1 wt%) added with ferroin (3 x 10-5 M) (Figure 2b) show the absorption maxima at the 520 nm. The 10 nm shift of the maximum is ascribed to strong adsorption of the chromophore onto nanosheet surface which cause modification of HOMO and/or LUMO level of the dye.29 Even after immersing the ferroin-adsorbed composite gel in pure water or in the acidic solution for BZ reaction, no desorption of the dye was observed; this stability allows us to use this ferroin-adsorbed gel repeatedly for BZ reactions. It is supposed that electrostatic interaction between divalent ferroin

9 ACS Paragon Plus Environment

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 24

and negatively charged nanosheets is strong enough to keep the ferroin dications on the nanosheets although they are not fixed in the gel by covalent bond. The anisotropic propagation of BZ reaction wave in the present anisotropic gels was clearly confirmed by eye observations. Figure 3a shows the images clipped from the real-time movie (Movie S1) of the anisotropic gel in which BZ reaction is progressing. The patterns formed by the BZ-reaction are anisotropic ellipses, in contrast with the isotropic circles in the isotropic gel (Figure 3b, Movie S2). The ellipses diffuse with time, keeping their aspect ratio. We picked up one ellipse and measured the time-course of the semi-minor and semi-major axes to evaluate the propagating distance of the wave from the center (Figures 4a). With 1 wt% nanosheet (Figures 4a and a'), we find large difference in propagation rate along the two directions. From the slope, the propagation rates v// and v⊥ along the directions perpendicular and parallel to the nanosheet planes are estimated as 1.10 and 1.61 mm min-1, respectively, while anisotropy v///v⊥ = 1.46. In contrast, the wave propagation is much faster and isotropic in the gel without nanosheets (Figures 4b and b'). To confirm the validity of our experiments, we picked up 11 ellipses formed during the BZ reaction runs performed on

10 ACS Paragon Plus Environment

Page 11 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

two different gels with 1wt% of nanosheets synthesized in different batches (Table S1). The average propagation rates and anisotropy are evaluated as ∥ = 1.89 ± 0.77 mm -1  min-1,    = 1.33 ± 0.50 mm min , and ∥ /  = 1.42 ± 0.18 (the values after

± denote the standard deviation), ensuring the validity of our data. The propagation rate and the anisotropy both strongly depended on the nanosheet concentration as shown in Figure 5. In the gel with 1 wt% of nanosheets, the wave propagation rate is 47% and 73% retarded along the direction parallel and perpendicular to the nanosheet planes compared to the gel without nanosheets (̅ = 356 mm min-1). The gel with 0.5 wt% nanosheets showed the intermediate values. It is also ensured that  the averaged anisotropy  ∥ /  increases with increasing nanosheet concentration. Anisotropic propagation of the chemical wave is explained by the difference in diffusion rate of the molecules in the gel along the two directions,10 caused by the barrier effect of the 2D nanosheets with huge aspect ratio (> 2 x 103). The formation of rotating spiral patterns is also a noticeable feature in the present anisotropic gels. The spirals rotated clockwise or anti-clockwise at many points (Figure 3a), which were not found in the isotropic gel (Figure 3b). It has been reported that

11 ACS Paragon Plus Environment

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 24

rotating spirals appears in the BZ reactions in inhomogeneous media.19 Although the present composite gels have uniform monodomain on macroscopic scale, it is considered that the inhomogeneous structures on mesoscopic and nanoscopic scales causes the spirals.

CONCLUSION

Unusual anisotropic Belouzov-Zhabozinsky (BZ) reactions was demonstrated in the anisotropic mono-domain gel films of nanosheet LC/pNIPA composites, in which molecular diffusion is effectively retarded along the direction perpendicular to the nanosheets planes. Due to the easy preparation and controllable anisotropy, the present system will be an ideal model system for fundamental studies of self-oscillating BZ-reactions that are related to curious pattern formations in natures such as embryo and neural networks. The present system is also applicable to develop self-oscillating soft actuators with uniaxial motion.

Acknowledgement

12 ACS Paragon Plus Environment

Page 13 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

This research was supported by: Research Center for Materials and Energy Devices of Fukuoka Institute of Technology (FIT-ME) (Strategic Research Foundation Grant-Aided Project for Private University from MEXT; #S1511036L); KAKENHI (#24104005, #15K05657, and #17H03209); Canon Foundation; Network Joint Research Center for Materials and Devices (#201507 and #20166009); and Electronics Research Laboratory of Fukuoka Institute of Technology.

Supporting Information Available: Movies S1 and S2 of the anisotropic and isotropic gel films in which BZ reaction is running. Table S1 that show the propagation rate and anisotropy of each experimental runs. This material is available free of charge via the Internet at http://pubs.acs.org.

13 ACS Paragon Plus Environment

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 24

REFERENCES

1.

Kato, T.; Hirai, Y.; Nakaso, S.; Moriyama, M. Liquid-crystalline physical gels.

Chem Soc Rev 2007, 36 (12), 1857-67. 2.

Urayama, K. Selected issues in liquid crystal elastomers and gels.

Macromolecules 2007, 40, 2277-2288. 3.

Liu, Y.; Xu, Z.; Gao, W.; Cheng, Z.; Gao, C. Graphene and other 2D colloids:

liquid crystals and macroscopic fibers. Adv Mater 2017. 4.

Miyamoto, N.; Nakato, T. Colloidal nanosheets. In Inorganic Nanosheets and

Nanosheet-Based Materials, Nakato, T.; Kawamata, J.; Takagi, S., Eds. Springer: 2017; pp 201-260. 5.

Miyamoto, N.; Yamada, Y.; Koizumi, S.; Nakato, T. Extremely stable

photoinduced charge separation in a colloidal system composed of semiconducting niobate and clay nanosheets. Angew. Chem. Int. Ed. 2007, 46, 4123-4127. 6.

Gabriel, J.-C. P.; Camerel, F.; Lemaire, B. J.; Desvaux, H.; Davidson, P.;

Batail, P. Swollen liquid-crystalline lamellar phase based on extended solid-like sheet. Nature 2001, 413, 504-508.

14 ACS Paragon Plus Environment

Page 15 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

7.

Xu, Z.; Gao, C. Graphene chiral liquid crystals and macroscopic assembled

fibres. Nat. Commun. 2011, 2, 571. 8.

Kou, L.; Huang, T.; Zheng, B.; Han, Y.; Zhao, X.; Gopalsamy, K.; Sun, H.;

Gao, C. Coaxial wet-spun yarn supercapacitors for high-energy density and safe wearable electronics. Nature Commun. 2013, 4754. 9.

Wong, M.; Ishige, R.; White, K. L.; Li, P.; Kim, D.; Krishnamoorti, R.;

Gunther, R.; Higuchi, T.; Jinnai, H.; Takahara, A.; Nishimura, R.; Sue, H. J. Large-scale self-assembled zirconium phosphate smectic layers via a simple spray-coating process. Nature Communications 2014, 5, 3589. 10.

Miyamoto, N.; Shintate, M.; Ikeda, S.; Hoshida, Y.; Yamauchi, Y.; Motokawa,

R.; Annaka, M. Liquid crystalline inorganic nanosheets for facile synthesis of polymer hydrogels with anisotropies in optical property, structure, swelling/deswelling, and ion transport/fixation. Chem. Commun. 2013, 49, 1082-1084. 11.

Choudalakis, G.; Gotsis, A. D. Permeability of polymer/clay nanocomposites:

A review. European Polymer Journal 2009, 45 (4), 967-984. 12.

Murata, S.; Konagaya, A.; Kobayashi, S.; Saito, H.; Hagiiya, M. Molecular

15 ACS Paragon Plus Environment

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 24

robotics: A new paradigm for artifacts. New Generation Computing 2013, 31, 27-45. 13.

Yoshida, R.; Takahashi, T.; Yamaguchi, T.; Ichijo, H. Self-oscillating gel. J.

Am. Chem. Soc. 1996, 118, 5134-5135. 14.

Maeda, S.; Hara, Y.; Yoshida, R.; Hashimoto, S. Peristaltic motion of polymer

gels. Angew. Chem. Int. Ed. 2008, 120, 6792–6795. 15.

Nakamaru, S.; Maeda, S.; Hara, Y.; Hashimoto, S. Control of autonomous

swelling− Deswelling behavior for a polymer gel. J. Phys. Chem. B 2009, 113, 4609– 4613. 16.

Hara, Y.; Mayama, H.; Morishima, K. Generative force of self-oscillating gel.

J. Phys. Chem. B 2014, 118, 2576–2581. 17.

Hara, Y.; Yamaguchi, Y.; Mayama, H. Switching the BZ reaction with a

strong-acid-free gel. j. Phys. Chem. B 2014, 118, 634–638. 18.

Zaikin, A. N.; Zhabotinsky, A. M. Concentration wave propagation in

two-dimensional liquid-phase self-oscillating system. Nature 1970, 225, 535-537. 19.

Winfree, A. T. Spiral waves of chemical activity. Science 1972, 175, 634-636.

20.

Agladze, K. I.; Kepper, P. D. Influence of electric field on rotating spiral

16 ACS Paragon Plus Environment

Page 17 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

waves in the Belousov-Zhabotinsky Reacton. J. Phys. Chem. 1992, 96, 5239-5242. 21.

Magnani, A.; Marchettini, N.; Ristori, S.; Rossi, C.; Rossi, F.; Rustici, M.;

Spalla,

O.;

Tiezzi,

E.

Chemical

waves

and

pattern

formation

in

the

1,2-Dipalmitoyl-sn-glycero-3-phosphocholine/Water Lamellar System. J. Am. Chem. Soc. 2004, 126, 11406-11407. 22.

Amemiya, T.; Nakaiwa, M.; Ohmori, T.; Yamaguchi, T. Chemical waves in

mesoporous media. Physica D 1995, 84, 103-111. 23.

Miyamoto, N.; Iijima, H.; Ohkubo, H.; Yamauchi, Y. Liquid crystal phases in

the aqueous colloids of size-controlled fluorinated layered clay mineral nanosheets. Chem. Commun. 2010, 46, 4166-4168. 24.

Inadomi, T.; Ikeda, S.; Okumura, Y.; Kikuchi, H.; Miyamoto, N. Anomalous

thermo- and photo-responsive anisotropic deformation of poly(N-isopropylacrylamide) gel hybridized with liquid crystalline inorganic nanosheets aligned by electric field. Macromol. Rapid Commun. 2014, 35, 1741-1746. 25.

Hara, Y.; Mayama, H.; Yamaguchi, Y.; Fujimoto, K. Activation energy of the

Belousov–Zhabotinsky Reaction in a gel with [Fe(bpy)3] catalyst. Chemistry Letters

17 ACS Paragon Plus Environment

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 24

2014, 43 (5), 673-675. 26.

Kenichi, Y. Distinct activation energies for temporal and spatial oscillations in

the Belousov-Zhabotinskii Reaction. Bull. Chem. Soc. Jpn. 1982, 55, 2042-2045. 27.

Dozov, I.; Paineau, E.; Davidson, P.; Antonova, K.; Baravian, C.; Bihannic, I.;

Michot, L. J. Electric-field-induced perfect anti-nematic order in isotropic aqueous suspensions of a natural beidellite clay. J. Phys. Chem. B 2011, 115, 7751-7765. 28.

Lemaire, B. J.; Panine, P.; Gabriel, J. C. P.; Davidson, P. The measurement by

SAXS of the nematic order parameter of laponite gels. Europhys. Lett. 2002, 69, 55-61. 29.

Ogawa, M.; Kuroda, K. Photofunctions of intercalation compounds. Chem.

Rev. 1995, 95, 399-438.

18 ACS Paragon Plus Environment

Page 19 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

TABLE OF CONTENTS IMAGE

19 ACS Paragon Plus Environment

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 24

Figure 1. Synthesis and characterization of the nanosheet LC/pNIPA composite gel with

anisotropy: (a) the schematic representation of the cell setup for the synthesis, (b) the

photograph of the gel observed with crossed polarizers and a wave plate, and (c)-(f) small angle

X-ray scattering results. The (d) I vs χ, (e) I vs q and (f) I•q2 vs q profiles were obtained from

the (c) 2D scattering pattern.

20 ACS Paragon Plus Environment

Page 21 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Figure 2. Visible spectra of (a) aqueous ferroin solution (12 mM), (b) the flocculates obtained

by mixing nanosheet colloid (1 wt%, 10mL) and ferroin solution (0.03 M, 10 µL), and (c) the

nanosheet LC/pNIPA composite gel adsorbed with ferroin.

21 ACS Paragon Plus Environment

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 24

Figure 3. Progression of BZ reaction in the anisotropic composite gel sheet with 1 and (b) 0.5

wt% of the nanosheets and (c) chemically crosslinked isotropic gel sheet. The double arrow

shows the direction of aligned nanosheet plane.

22 ACS Paragon Plus Environment

Page 23 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Figure 4. The time-dependence of the distance that the chemical wave progressed along the

direction (a) parallel (//) and (a') perpendicular (⊥) to the nanosheet planes in the anisotropic

gel with 1.0 wt% of nanosheets. The propagation along two orthogonal directions in the

isotropic gel without nanosheets is also shown as (b) and (b'). The solid and dashed lines were

obtained by linear fitting to evaluate the propagation rates from the slope.

23 ACS Paragon Plus Environment

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 24

Figure 5. The nanosheet concentration dependence of the average propagation rates along the

direction parallel (   ∥ ) and perpendicular (  ) to the nanosheet planes and the anisotropy

 ( ∥ /  ).

24 ACS Paragon Plus Environment