Capturing Cadmium(II) Ion from Wastewater Containing Solid Particles

Feb 8, 2017 - Cavities and adsorption sites in adsorption materials can be easily blocked in complex media containing solid particles and floccules, w...
0 downloads 0 Views 5MB Size
Subscriber access provided by University of Newcastle, Australia

Article

Capturing Cadmium (II) Ion from Wastewater Containing Solid Particles and Floccules Using Ion-imprinted Polymers with Broom Effect Xu-Biao Luo, Yu Xi, Haiyan Yu, Xiaocui Yin, and Shenglian Luo Ind. Eng. Chem. Res., Just Accepted Manuscript • DOI: 10.1021/acs.iecr.6b04030 • Publication Date (Web): 08 Feb 2017 Downloaded from http://pubs.acs.org on February 14, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Industrial & Engineering Chemistry Research is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

1 2 3

Capturing Cadmium (II) Ion from Wastewater Containing Solid Particles and Floccules Using Ion-imprinted Polymers with Broom Effect Xubiao Luo†*, Yu Xi†, Haiyan Yu†, Xiaocui Yin†, Shenglian Luo†*

4 5



6

Recycle, Nanchang Hangkong University, Nanchang 330063, P.R. China

Key Laboratory of Jiangxi Province for Persistent Pollutants Control and Resources

7 8

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 29

9

ABSTRACT: Cavities and adsorption sites in adsorption materials can be easily

10

blocked in complex media containing solid particles and floccules, which limit the

11

applicability of these materials. This study demonstrates the synthesis of cadmium (II)

12

ion-imprinted polymers (Cd-IIPs) and non-ion-imprinted polymers (NIPs) via

13

reversible

14

(RAFTPP). Microspheres of IIPs and NIPs were modified by grafting bi-component

15

polymer brushes with different ratios of a hydrophilic component, hydroxyethyl

16

methacrylate (HEMA) and a rigid component, styrene. The maximum adsorption

17

capacities of the IIPs and NIPs in pure water are 65.5 and 24.5 mg/g, respectively.

18

Specifically, the 9:1-IIP exhibits excellent anti-blockage and anti-interference

19

performance, with an adsorption capacity considerably higher than those of IIPs in

20

simulated wastewater, including SiO2 solid particles and floccules. This higher

21

performance suggests that the 9:1-IIP has the rigidity to resist chaff interference from

22

different aqueous media and also possesses good water-compatibility. The 9:1-IIP has

23

a high recognition ability and high selectivity (α > 5.9) to Cd(II) although the surface

24

is grafted with bi-component polymer brushes. Furthermore, the steric hindrance due

25

to the styrene on the bi-component polymer brushes, in addition to van

26

der Waals interactions with the interfering chaff, was confirmed to result in a “broom

27

effect”. The developed sorbents demonstrate the expected adsorption capacities when

28

applied to environmental samples from factories, indicating that IIP microspheres

29

grafted with polymer brushes have significant potential for application in complex

30

wastewater treatment.

31 32 33 34

Keywords: Cd(II), ion-imprinted anti-blockage, anti-interference

addition-fragmentation

chain

transfer

polymer,

precipitation

polymer

ACS Paragon Plus Environment

polymerization

brushes,

adsorption,

Page 3 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

35

INTRODUCTION

36

Ion imprinting polymers (IIPs) have proven to be novel sorbents that are widely

37

used to remove heavy metals from aqueous media. They are easy to synthesize, are

38

environmentally stable and exhibit high selectivity toward target ions due to their

39

tailor-made recognition sites.1,2 The development of IIPs holds significance due to

40

their applicability for the removal of heavy metals from different aqueous media, such

41

as pure water,3 pure milk,4 synthetic nuclear power reactor effluents,5 neutral

42

analytes,6 and steel pickling waste liquor.7 In our research group, the use of

43

copper,8─10 lead,11,12 lithium,13 and cadmium14,15 as template ions for ion-imprinting

44

technology has resulted in considerable advancements in wastewater treatment.

45

However, despite the advantages of water compatibility and multiple applications,

46

previously developed IIPs also present the challenge that their adsorption sites are

47

easily blocked when template ions diffuse to their surface during adsorption from

48

complex aqueous matrices from factories.16─19 Such blockage significantly limits their

49

practical application in wastewater treatment. In fact, special attention must be paid to

50

the development of novel IIPs with anti-interference performance in complex-matrix

51

water samples from the environment, such as those containing solid particles and

52

floccules.

53

Recently, increasing attention has been focused on reversible addition

54

-fragmentation chain transfer (RAFT) polymerization, which is a highly exploited

55

living radical polymerization (LRP) technique, widely studied and utilized for the

56

production of well-defined polymers with controllable molecular weight and

57

composition.20─26 Polymer brushes synthesized by RAFT polymerization have been

58

used to make surfaces with a variety of mechanical and chemical properties.27─31

59

Surface modification using polymeric systems that respond to a variety of stimuli,

60

such as pH, thermal stimuli, cosolvents, and magnetic fields,32 has been applied in the

61

field of molecular imprinted polymers (MIPs).33─35 Grafting of surfaces with the

62

polymer 2-(dimethylamino) ethylmethacrylate (PDMAEMA) can make the material

63

responsive to the pH of aqueous environments;36,37 thermo-responsive poly (N-isopro

64

pylacrylamide) (PNIPAM) can be used to make a material either hydrophilic or

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

65

hydrophobic, depending on the temperature of water;38─43 and polymer hydroxyethyl

66

methacrylate (PHEMA) can improve the hydrophilicity of the material.44─47

67

Herein, we introduce the concept of the “broom effect”. A broom is a well-known

68

cleaning tool typically consisting of rigid fibers attached to a long handle, used for

69

such purposes as sweeping dirt off sidewalks. Similarly, polymers grafted onto the

70

surface of IIP microspheres act as a broom because they can resist chaff interference

71

in IIP cavities during adsorption from complex water samples. The anti-blockage and

72

anti-interference performance of such IIPs grafted with polymer brushes is referred to

73

as the “broom effect” here due to its similarity to the cleaning action of brooms.

74

However, such polymer brushes have not been applied for the modification of IIP

75

microspheres48 but our research group,49 as it is more challenging to graft polymer

76

brushes onto IIP surfaces than onto MIPs for two reasons. First, the removal of metal

77

ions from IIPs requires organic ligands that must have not only strong binding energy

78

but also good coordination ability such that they can complex with the metal ions

79

during polymerization. Second, it is necessary for the organic ligand to have a double

80

bond to be used as a monomer for graft polymerization. Therefore, we chose

81

3-allylrhodanine as the functional monomer due to its good complexing ability with

82

cadmium and because it has not yet been applied before as a complexing agent for the

83

removal of metal ions.50, 51

84

In this study, we also hope to maintain or improve the hydrophilicity of Cd-IIP/NIP

85

microspheres, with the polystyrene (PS) possessing the dual purpose of being a rigid

86

building block for modification and the hydrophobic component. A mixture of HEMA

87

and styrene was used as the bi-component copolymer for grafting onto IIP

88

microspheres, which imparts them good water-compatibility and the rigidity to resist

89

chaff interference from complex water samples. To our knowledge, this is the first

90

study of IIPs grafted with polymer brushes. A series of adsorption experiments were

91

conducted in pure water, simulated wastewater containing solid particles and floccules,

92

and different real wastewater samples from factories to verify the “broom effect” on

93

the adsorption property, anti-blockage and anti-interference performance.

ACS Paragon Plus Environment

Page 4 of 29

Page 5 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

94 95 96

MATERIALS AND METHODS Material and instrumentation. All details regarding the materials and instrumentation are provided in the Supporting Information (SI).

97

Synthesis of Cd-IIP/NIP microspheres with different ratios of surface-grafted

98

bi-component polymer brushes. The IIP microspheres with surface-immobilized

99

dithioester groups52 were synthesized by RAFT precipitation polymerization

100

(RAFTPP), as described in the SI. For comparison, NIP microspheres were prepared

101

and treated under identical conditions without adding the Cd(II).

102

The Cd-IIP/NIP microspheres grafted with bi-component polymer brushes were

103

synthesized by a surface-initiated RAFT polymerization procedure, as shown in the SI.

104

The resulting solid products were then dried at 30 °C under vacuum until they reached

105

a constant weight, leading to light pink Cd-IIP/NIP microspheres grafted with

106

bi-component polymer brushes. The increases in weight due to grafting are listed in

107

Table 1.

108

Batch Adsorption Experiments. The equilibrium adsorption experiments carried

109

at a pH of 7.0 ± 0.2, with initial Cd(II) concentrations ranging from 100 to 600 mg/L

110

in pure water. Competitive adsorption of RAFT-IIP/NIP and Cd-IIP/NIP were also

111

conducted in pure water, Zn(II), Ni(II), Co(II), and Cu(II) were chosen as competitor

112

ions due to their identical charges and similar sizes to Cd(II). The aqueous solutions

113

(pH = 7.0 ± 0.3) of Cd(II), Zn(II), Ni(II), Cu(II), and Co(II) all had an initial

114

concentration of 500 mg/L. All the adsorption experiments in paper were mixed 50

115

mg sorbents and 50 ml adsorbate solution to incubator shaker.

116

The adsorptions of the developed sorbents were first studied in different samples of

117

simulated wastewater to investigate the broom effect, namely, the anti-blockage and

118

anti-interference performance of the bi-component polymer brushes. Here, we have

119

synthesized three kinds of particle sizes range of SiO2 (Figure S1: 1 ~ 3 nm, 20 ~ 60

120

nm, 70 ~ 400 nm), which cover a wide particle sizes in simulated wastewater, so that

121

we can approach to the solid distribution in real wastewater as much as possible. SiO2

122

particles were homogenized in water at a concentration of 1.0 mg/mL. Additionally,

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

123

several industrial-grade pure flocculating agents, common exist in wastewater,

124

including sodium carboxymethyl cellulose (CMC), poly-aluminium chloride (PAC),

125

and polyacrylamide (PAM), were added either single-component or pairwise

126

orthogonal flocculating agents addition was used to form floccules. The concentration

127

of Cd(II) in all aqueous samples was 500 mg/L. used to simulated.

128

All the sorbents have adsorption experiments in real wastewater. Wastewater from

129

the tin-removal process was obtained from Hongtai Tin Industry Co. Ltd. (Shenzhen,

130

China), the wastewater contained suspended white floccules with a Cd(II)

131

concentration of approximately 4.0 g/L and a pH of 1.35 at room temperature.

132

Lithium battery wastewater, obtained from Dingxin Metal Chemical Co. Ltd.

133

(Shangrao, China), contained approximately 2.5 g/L of Cd(II) and 50 mg/L of solids,

134

with a pH of 7.5 at room temperature. The particle sizes of real wastewater are shown

135

in Figure S1, we adjust pH of real wastewater to 7.0 ± 0.2 before adsorption so as to

136

investigated the performance of sorbents in real wastewater.

137

RESULTS AND DISCUSSION

138

Morphology characterization. The morphologies of both IIP and 9:1-IIP

139

microspheres were characterized by SEM. The IIP (Figure 1a) and 9:1-IIP (Figure 1b)

140

both consist of independently dispersed spherical particles with particle size

141

distributions in the range of 5.5-2.7 µm. A comparison of the magnified images of the

142

IIP (Figure 1c) and 9:1-IIP (Figure 1d) shows that the 9:1-IIP surface contains many

143

bumps and is considerably rougher than the surface of IIP, indicating that polymer

144

brushes have been grafted onto the 9:1-IIP surface.

145

Hydrophilicity of IIP/NIP and Cd-IIP/NIP microspheres. After the ultrasonic

146

dispersion of the sorbents in pure water (1 mg/mL), the dispersed mixtures were

147

allowed to settle for different times at 20 °C. Figure S2 shows typical photographs of

148

the resultant solutions, taken after different sedimentation times. These clearly show

149

that all the sorbents take a rather long time (more than 4 h) to settle down, which is

150

attributed to their hydrophilicity, particularly for IIPs and NIPs. A comparison of the

151

details from Figure S2c shows that sedimentation occurs more rapidly in the presence

ACS Paragon Plus Environment

Page 6 of 29

Page 7 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

152

of the IIP and Cd-IIP than in the presence of the NIP and Cd-NIP, which are ascribed

153

to imprinting cavities in IIP and Cd-IIP, result in its densities lower to NIP and Cd-NIP,

154

respectively.

155

Characterization of the grafted polymer brushes. The samples for the

156

characterization experiments were chosen to have different polymer brush: Cd-IIP

157

ratios but the same number of graft sites (dithioester groups) to maintain the same

158

quantity of initiators43. The free polymers obtained in our study were characterized by

159

gel permeation chromatography (GPC)53. As shown in Table 1, the evaluated

160

number-average molecular weights (Mn,

161

polymer brushes on the surface of the IIP/NIP microspheres are in the ranges of

162

26,378–17,282 and 1.14–1.00, respectively. In contrast, the number-average

163

molecular weight of polymer brushes for the 9:1-IIP (Mn, GPC = 26,378) is 0.27% and

164

10.21% higher than those for the 8:2-IIP and 7:3-IIP, and the molecular weight of

165

polymer brushes for the 9:1-NIP (Mn, GPC = 25564) is 19.57% and 32.39% higher than

166

those for 8:2-NIP and 7:3-NIP, indicating that 9:1-IIP/NIP possess longer polymer

167

brushes. Additionally, the rates of weight gain (ΔW = (mCd-IIP-mIIP)/mIIP, (%)) of the

168

resultants from the synthetic reaction, listed in Table 1, show that 9:1-IIP/NIP

169

(10.92%/11.52%) microspheres are considerably heavier than 8:2 and 7:3-IIP/NIP

170

microspheres, which confirm that surface-initiated RAFT polymerization has took

171

place and polymer brushes were grafted on the Cd-IIP/NIP microspheres.

172

GPC)

and polydispersity indices (PDIs) of

Cd(II) Adsorption Capacity Experiments.

Figures 2 and S3 show the

173

equilibrium adsorption results of the IIP/Cd-IIP and the NIP/Cd-NIP toward Cd(II),

174

which were used to investigate the adsorption capacities of the developed materials

175

and determine the adsorption performance after the grafting of IIPs/NIPs with

176

polymer brushes containing different ratios of HEMA and styrene. The correlation

177

coefficient (R2) values demonstrate that the Langmuir model is more suitable than the

178

Freundlich model for describing the adsorption process. The adsorption reaches

179

equilibrium at a concentration of 500 mg/L. Both the IIP and Cd-IIP are found to take

180

up more Cd(II) than their corresponding NIP and Cd-NIP (QIIP = 65.5 ± 1.6 mg/g,

181

QNIP = 23.0 ± 0.8 mg/g), as seen from a comparison with the adsorption capacities

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

182

reported in previous studies. As a monomer, 3-allylrhodanine has higher complexing

183

ability with Cd(II) than cadmium ion-imprinted polymers prepared with

184

carboxymethyl chitosan54 (Q = 20.7 mg/g) and polysaccharide55 (Q = 33.4 mg/g) as

185

monomers. IIP exhibits better adsorption than Cd-IIP (Q9:1-IIP = 58.0 ± 1.5 mg/g) in

186

pure water because identical weights of Cd-IIP-grafted polymer brushes have fewer

187

adsorption sites for Cd(II). Further, the 9:1-IIP has a considerably higher adsorption

188

capacity, 1.5 and 1.7 times higher than those of the 8:2-IIP and 7:3-IIP, respectively.

189

These results suggest that the quantity of hydrophobic styrene in bi-component

190

polymer brushes has an effect on the adsorption capacity. The 9:1-IIP has the best

191

adsorption performance among the grafted microspheres due to the following two

192

reasons. First, the polymer brushes bearing more of the hydrophilic component

193

HEMA show good affinity with aqueous media. Second, the less rigid (hydrophobic)

194

component styrene provides steric hindrance, which obstructs chaff interference from

195

accessing imprinted cavities but still allows sufficient space for Cd(II).

196

Competitive experiments. Figures 3 and S4 show the uptake capacity of Cd(II),

197

Zn(II), Ni(II), Cu(II), and Co(II) by IIP/NIPs and Cd-IIP/NIPs. Combined with the

198

data in Tables 2 and S1, the NIP and Cd-NIP sorbents exhibit considerably lower

199

adsorption capacity and selectivity (β > 1.1, Table 2) than the IIP and Cd-IIP,

200

respectively, in competitive experiments, furthermore, IIP and Cd-IIP showed poor

201

adsorption to Zn(II), Ni(II), Cu(II), and Co(II) (α > 1). These contrasts in the

202

adsorptions indicate that imprinted cavities and Cd(II) specific binding sites in a

203

predetermined orientation are formed in the IIP and Cd-IIP. The IIP shows higher

204

selectivity to Cd(II) (minimum α = 3.8) than materials reported in previous studies15

205

(maximum α = 3.05). Thus, the monomer in this study, 3-allylrhodanine, has a higher

206

complexing ability with Cd(II). Additionally, the 9:1-IIP has a rather high selectivity

207

to Cd(II) (minimum αCd/Ni = 5.9 among the metal ions in Table 2) compared with

208

those shown by the 8:2-IIP and 7:3-IIP, which confirms that the 9:1-IIP still retains a

209

high recognition ability compared to other Cd-IIP ratios. The reason is the styrene

210

content in polymer brushes would affects the adsorption performance because of

211

its hydrophobicity and steric hindrance.

ACS Paragon Plus Environment

Page 8 of 29

Page 9 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

212

Adsorption experiments in simulated wastewater. We chose SiO2 as a

213

representative interfering solid particle and three common types of flocculants (CMC,

214

PAM, and PAC) to simulate floccules to ensure that the components of the simulated

215

wastewater were consistent with those of industrial wastewater. Adsorption

216

experiments were first performed in complex aqueous samples (simulated wastewater)

217

to study the “broom effect” of bi-component polymer brushes on the Cd-IIP/NIP. The

218

broom effect is defined as the combination of two actions: anti-blockage performance

219

in solid particle media, prevention of imprinted cavities from being blocked by solid

220

particles and the performance in floccules media, which is to stop the floccules from

221

wrapping the adsorption sites of sorbents.

222

Figures 4 and S5 show the adsorptions in media containing different particle sizes

223

of SiO2 (1~400 nm). Batch adsorption studies reveal that the IIP and Cd-IIP adsorbed

224

more Cd(II) than the corresponding NIP and Cd-NIP in aqueous samples containing

225

different particle sizes of SiO2. The adsorption capacity of the 9:1-IIP (Q 9:1-IIP = 54.2

226

± 1.0 mg/g) is 2.38 times that of the 9:1-NIP, and 2.17 and 2.16 times those of the 8:2

227

and 7:3 sorbents, respectively, in media containing 1~3 nm SiO2. This suggests that

228

tailor-made recognition sites for target ions, such as those present in adsorbents

229

synthesized by imprinting technique, exist in IIP and Cd-IIP microspheres.

230

For the IIP/NIP, higher adsorption capacities were seen in media with larger

231

particles of SiO2 (Q1~3nm < Q20~60nm < Q70~400nm). In particular, the IIP shows 57.86%

232

lower adsorption in media with 1~3 nm SiO2 than in pure water because the particle

233

size of SiO2 is sufficiently small for it to easily access the pores of sorbents. In

234

contrast, the situation is completely reversed for the Cd-IIP/NIP, which exhibits a

235

higher adsorption capacity as the particle size of SiO2 is decreased. For example, the

236

9:1-IIP shows an adsorption capacity of 54.2 ± 1.1 mg/g in media with 1~3 nm SiO2,

237

and this drops to 49.4 ± 0.9 and 37.0 ± 1.0 mg/g in media with 20~60 nm and 70~400

238

nm SiO2 particles, respectively. This indicates that the adsorption performance

239

decreases as the intensity of interference in the adsorption environment increases.

240

Q9:1-IIP is 1.96 times higher than that of QIIP (27.6 ± 0.7 mg/g) in 1~3 nm SiO2 media,

241

and the following trend is observed in the adsorption performances of Cd-IIP/NIP:

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

242

Q9:1 > Q8:2 > Q7:3. These results demonstrate that the extent of hydrophobicity of

243

styrene in the bi-component polymer brushes influences the adsorption capacity. The

244

9:1-IIP shows outstanding anti-blockage performance because its bi-component

245

polymer brushes have adequate rigidity and hydrophilicity; due to these properties,

246

the corresponding Cd-IIP shows the “broom effect” and prevents solid particles from

247

accessing the imprinted cavities in sorbents.

248

Additionally, the adsorptions of PHEMA-IIP/NIP and PS-IIP/NIP were studied for

249

comparison. In pure water, the adsorption capacity of PHEMA-IIP/NIP is higher than

250

that of the 9:1-IIP/NIP but lower than that of the IIP/NIP because there is no sterically

251

hindered (styrene) to prevent Cd(II) from accessing the imprinted cavities and an

252

identical weight of PHEMA-IIP/NIP grafted with polymer brushes has fewer

253

adsorption sites than an IIP/NIP. However, the following trend is observed when

254

adsorption is carried out in media containing solid SiO2 particles: QIIP/NIP
QCMC > QPAC+CMC)

273

for Cd(II) adsorption onto the IIP/NIP and Cd-IIP/NIP were observed. However, as

274

shown in Figures 5b and S6b, PAM-containing media show only a slight decrease in

275

adsorption capacity because the viscidity of PAM-containing adsorbents hinders

276

uniform dispersal. In general, floccules were separated out of microspheres by

277

polymer brushes such that efficient adsorption sites were maintained for the target ion

278

Cd(II).

279

Analysis of the mechanism. EDX analysis was performed on the 9:1-IIP after the

280

adsorption of Cd(II) in media containing SiO2 particles (Figure S7a) and floccules

281

(Figure S7b). The results confirm that the template Cd(II) was successfully bound to

282

the imprinted cavities of 9:1-IIP microspheres, as shown by the strong cadmium peaks

283

in the EDX spectrum after adsorption in media containing SiO2 particles and floccules.

284

This suggests that ion-imprinted polymer microspheres grafted with bi-component

285

polymer brushes maintain their adsorption ability for Cd(II). Additionally, the

286

elements Si and Al were also detected on the surface of grafted 9:1-IIP microspheres,

287

verifying that Cd(II) adsorption occurs in media with solid particles and floccules.

288

The chemical composition of the IIP/NIP and 9:1-IIP/NIP after the adsorption of

289

Cd(II) was measured by XPS. As shown in Figures 6a and S8a, the peak

290

corresponding to Cd 3d, S 2p, C 1s, and O 1s of sorbents are observed in the

291

high-resolution spectrum. The 9:1-IIP/NIP shows no clear peaks for Cd 3d in wide

292

scans because the XPS probe can test the microsphere surface only down to 10 nm,

293

indicating that the 9:1-IIP/NIP microspheres have been successfully grafted with

294

bi-component polymer brushes. Cd 3d peaks were obtained in the narrow scope

295

sweep, and the two peaks with binding energies of 404.9 eV and 411.6 eV are

296

attributed to Cd 3d5/2 and Cd 3d3/2,56 respectively, on the surface of IIP microspheres,

297

as shown in Figure 6e. The peaks at 405.8 eV and 412.5 eV are assigned to Cd 3d5/2

298

and Cd 3d3/2 of Cd(II) absorbed on 9:1-IIP microspheres, as shown in Figure 6f. These

299

results indicate that both the IIP and 9:1-IIP adsorb Cd(II). The presence of Cd in the

300

product further validates its affinity to the IIP and 9:1-IIP.

301

Adsorption occurring on the IIP/NIP and 9:1-IIP/NIP can be checked by the shifts

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

302

of S. The analysis of results for the IIP shows peaks at approximately 163.6, 164.3 eV

303

before adsorption, corresponding to S-C bonds (S1/2p and S3/2p), whereas the peaks at

304

approximately 164.8 and 165.5 eV correspond to S=C bonds (S1/2p and S3/2p),57 as

305

shown in Figure 6c. The binding energies of S-C sites are shifted to lower values of

306

163.3 and 163.8 eV after Cd(II) adsorption whereas the S=C sites are shifted to lower

307

values of 164.5 and 165.0 eV. Additionally, the S binding energy of the 9:1-IIP/NIP is

308

changed after the adsorption process, as shown in Figure 6d. The shifts in core levels

309

indicate an electron transfer in the valence band involving the reaction between Cd

310

and S. These findings indicate that the S-C and S=C groups play a critical role in

311

Cd(II) adsorption.

312

To elucidate the anti-interference mechanism of the 9:1-IIP polymer brushes, the

313

adsorptions of the IIP and 9:1-IIP were studied in media containing floccules made

314

with PAC. This test was performed in the absence of Cd(II) to determine how the

315

interfering species affect the chemical state of the elements in the sorbent. An IIP with

316

no bi-component polymer brushes was used as the blank control. Figure S9 suggests

317

the coexistence of S 2p, C 1s, O 1s, and Al 2p in the as-prepared sorbents. The O 1s

318

spectrum (Figure S9c) of the IIP can be fitted to three characteristic peaks: the peaks

319

at 531.77 and 532.49 eV are attributable to oxygen in the IIP of O-C=O, whereas the

320

peak at 533.83 eV is associated with the oxygen from CO2 in air58. After grafting with

321

bi-component polymer brushes in the 9:1-IIP, the peak at 531.96 eV is assigned to Al

322

-OH in the polymer brushes. The high intensity of the Al-OH peak verifies the

323

presence of a large quantity of OH in the polymer brushes. The peaks at 532.82 and

324

533.85 eV, associated with oxygen in the O-C=O groups of the 9-1-IIP, indicate that

325

van der Waals forces are an effective way for the bi-component polymer brushes to

326

prevent interfering species from accessing imprinted cavities. The other way is by the

327

“broom effect” produced by the steric hindrance from benzene rings in styrene.

328

Application in real wastewater. Figures 7 and S10 show the results for

329

applications of IIP/NIP and Cd-IIP/NIP in real wastewater. The results indicated that

330

for IIP/NIP, all the possible sites are not available as effective adsorption sites for

331

Cd(II) because the pores in the microspheres are blocked by chaff interference in real

ACS Paragon Plus Environment

Page 12 of 29

Page 13 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

332

wastewater. The solid particle sizes in lithium battery wastewater were considerably

333

larger than those in the wastewater from tin removal (see Figure S1), 9:1-IIP showed

334

nice adsorption performance in both lithium battery wastewater and wastewater from

335

tin removal, which might due to the intensity of interference in real wastewater lower

336

than simulation wastewater, 9:1-IIP can dispose it although bigger particle size. Other

337

ratios showed different adsorption capacity, these adsorption rules can benefit the

338

application of these materials in industrial wastewater. Additionally, in contrast to the

339

IIP, the 9:1-IIP has a considerably higher adsorption capacity in real wastewater,

340

which proves that the bi-component polymer brushes can still display the “broom

341

effect” in a real wastewater environment.

342

Reusability. The stability and reusability of IIP and 9:1-IIP is key factors for

343

improving the process economics (Fig. S11). The regenerated IIP and 9:1-IIP were

344

reused for five cycles of adsorption-desorption. It can be observed that the adsorption

345

capacity of IIP and 9:1-IIP were stable within the five cycles with little decrease in the

346

adsorption capacity for Cd(II), but their adsorption capacity of were approximately

347

15.42% and 8.96% loss in the fifth cycles, respectively. It can be concluded that IIP

348

and 9:1-IIP exhibits relatively good adsorption efficiency after regeneration, and ion

349

imprinted polymer grafted polymer brushes also can protect material be destroyed

350

from eluent.

351

CONCLUSIONS

352

Cd-IIP adsorbents exhibiting the broom effect were utilized to treat heavy metal

353

wastewater, which can prevent solid particles and chaff interference in wastewater

354

from blocking the imprinting cavities. Appropriately rigid styrene introduced in

355

bi-component polymer brushes can provide moderate steric hindrance and enhance

356

the anti-blockage ability toward solid particles in complex wastewater. HEMA

357

brushes can provide adsorbents with good hydrophilicity and anti-interference ability

358

toward chaff interference, using van der Waals force to ensure that the adsorption

359

capacity is preserved in complex wastewater. This study provides fundamental

360

insights to enhance the anti-blockage and anti-interference ability of IIPs. It is critical

361

for the broad application of IIP technology to recycle valuable metals from complex

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

362

wastewater and reduce the cost of wastewater treatment by obtaining valuable

363

products.

364



365

Supporting Information

366

Material and instrumentation. Synthesis methods of IIP/NIP microspheres and

367

Cd-IIP/NIP. More detailed information on adsorption capacity and competitive

368

adsorption parameters calculation. Additional adsorption chart of non ion imprinting

369

polymers. This material is available free of charge via the internet at

370

http://pubs.acs.org.

371



372

Corresponding author

373

*(L.X.B.) Tel.: +86 791 3953372; Fax: +86 791 395373; E-mail: [email protected],

374

*(L.S.L.) E-mail: [email protected].

375

Notes

376

The authors declare no competing financial interest.

377



378

This study was financially supported by the National Science Fund for Excellent

379

Young Scholars (51422807), the Natural Science Foundation of China (51238002,

380

51678285), the Key Project of Science and Technology Department of Jiangxi

381

Province (20143ACG70006) and the Cultivating Project for Academic and Technical

382

Leader of Key Discipline of Jiangxi Province (20153BCB22005).

383



384 385

ASSOCIATED CONTENT

AUTHOR INFORMATION

ACKNOWLEDGMENTS

REFERENCES

(1) Fu, J.; Chen, L.; Li, J.; Zhang, Z. Current status and challenges of ion imprinting. J. Phys.Chem. A 2015, 3 (26), 13598–13627.

386

(2) Patra, S.; Roy, E.; Madhuri, R.; Sharma, P. K. Fast and Selective

387

preconcentration of europium from wastewater and coal Soil by graphene

388

oxide/Silane@Fe3O4 dendritic nanostructure. Environ. Sci. Technol. 2015, 49 (10),

389

6117–6126.

390

(3) Liu, Y.; Meng, X.; Luo, M.; Meng, M.; Ni, L.; Qiu, J.; Yan, Y. Synthesis of

391

hydrophilic surface ion-imprinted polymer based on graphene oxide for removal of

ACS Paragon Plus Environment

Page 14 of 29

Page 15 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

392

strontium from aqueous solution. J. Phys. Chem. A. 2014, 3 (3), 1287–1297.

393

(4) Liu, Y.; Meng, X.; Liu, Z., Meng, M.; Jiang, F.; Luo, M.; Zhong, G. Preparation

394

of a two-dimensional ion-imprinted polymer based on a graphene oxide/SiO2

395

composite for the selective adsorption of nickel ions. Langmuir 2015, 31 (32), 8841

396

–8851.

397

(5) Preetha, C. R.; Gladis, J. M.; Rao, T. P.; Venkateswaran, G. Removal of toxic

398

uranium from synthetic nuclear power reactor effluents using uranyl ion imprinted

399

polymer particles. Environ. Sci. Technol. 2006, 40 (9), 3070–3074.

400

(6) Latif, U.; Mujahid, A.; Afzal, A.; Lieberzeit, P. A. Dual and tetraelectrode QCMs

401

using imprinted polymers as receptors for ions and neutral analytes. Anal Bioanal

402

Chem 2011, 400 (8), 2507–2515.

403

(7) Cai, Y.; Zheng, L.; Fang, Z. Selective adsorption of Cu (II) from an aqueous

404

solution by ion imprinted magnetic chitosan microspheres prepared from steel

405

pickling waste liquor. RSC Advances 2015, 5 (118), 97435–97445.

406

(8) Luo, X. B.; Luo, S. L.; Zhan, Y. C. Novel Cu (II) magnetic ion imprinted

407

materials prepared by surface imprinted technique combined with a sol-gel process. J.

408

Hazard. Mater. 2011, 192 (3), 949–955.

409

(9) Zhan, Y.; Luo, X. B.; Nie, S.; Huang, Y.; Tu, X.; Luo, S. L. Selective separation

410

of Cu (II) from aqueous solution with a novel Cu (II) surface magnetic ion-imprinted

411

polymer. Ind. Eng. Chem. Res. 2011, 50 (10), 6355–6361.

412

(10) Luo, X. B.; Huang, Y.; Deng, F. A magnetic copper (II) -imprinted polymer for

413

the selective enrichment of trace copper (II) ions in environmental water.

414

Microchimica Acta 2012, 179 (3-4), 283–289.

415

(11) Luo, X. B.; Liu, L. L.; Deng, F.; Luo, S. L. Novel ion-imprinted polymer using

416

crown ether as a functional monomer for selective removal of Pb (II) ions in real

417

environmental water samples. J. Phys. Chem. A 2013, 1 (28), 8280–8286.

418

(12) Luo, X. B.; Deng, F.; Min, L. J.; Luo, S.; Guo, B.; Zeng, G. Facile one-step

419

synthesis of inorganic-framework molecularly imprinted TiO2/WO3 nanocomposite

420

and

421

contaminant. Environ. Sci. Technol. 2013, 47 (13), 7404–7412.

its

molecular

recognitive

photocatalytic

degradation

ACS Paragon Plus Environment

of

target

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

422

(13) Luo, X. B.; Guo, B.; Luo, J. M. Recovery of lithium from wastewater using

423

development of Li ion-imprinted polymers. ACS Sustainable Chem. Eng. 2015, 3 (3):

424

460–467.

425

(14) Luo, X.; Guo, B.; Wang, L. Synthesis of magnetic ion-imprinted fluorescent

426

CdTe quantum dots by chemical etching and their visualization application for

427

selective removal of Cd (II) from water. Colloids and Surfaces A: Physicochemical

428

and Engineering Aspects, 2014, 462, 186–193.

429

(15) Xi, Y.; Luo, Y. T.; Luo, J. M.; Luo, X. B. Removal of cadmium (II) from

430

wastewater using novel cadmium ion-imprinted polymers. J. Chem. Eng. Data. 2015,

431

60 (11), 3253–3261.

432 433

(16) Gauczinski, J.; Liu, Z.; Zhang, X.; Schönhoff, M. Surface molecular imprinting in layer-by-layer films on silica particles. Langmuir 2012, 28 (9), 4267–4273.

434

(17) Liu, Y.; Cao, B.; Jia, P.; An, J.; Luo, C.; Ma, L.; Pan, K. Layer-by-layer surface

435

molecular imprinting on polyacrylonitrile nanofiber mats. J. Phys. Chem. A. 2015, 119

436

(25), 6661–6667.

437

(18) Vatanpour, V.; Madaeni, S. S.; Zinadini, S.; Rajabi, H. R. Development of ion

438

imprinted technique for designing nickel ion selective membrane. J. Membr. Sci.

439

2011, 373 (1), 36–42.

440

(19) Younis, M. R.; Bajwa, S. Z.; Lieberzeit, P. A. Molecularly imprinted porous

441

beads for the selective removal of copper ions. J. Sep. Sci. 2016, 39, 793–798.

442

(20) An, Z.; Shi, Q.; Tang, W.; Tsung, C. K.; Hawker, C. J.; Stucky, G. D. Facile

443

RAFT precipitation polymerization for the microwave-assisted synthesis of

444

well-defined, double hydrophilic block copolymers and nanostructured hydrogels. J.

445

Am. Chem. Soc. 2007, 129 (46), 14493–14499.

446

(21) Barbey, R.; Lavanant, L.; Paripovic, D.; Schüwer, N.; Sugnaux, C.; Tugulu, S.;

447

Klok, H. A. Polymer brushes via surface-initiated controlled radical polymerization:

448

synthesis, characterization, properties, and applications. Chem. Rev. 2009, 109 (11),

449

5437–5527.

450 451

(22) Borges, J.; Mano, J. F. Molecular interactions driving the layer–by–layer assembly of multilayers. Chem. Rev. 2014, 114 (18), 8883–8942.

ACS Paragon Plus Environment

Page 16 of 29

Page 17 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

452

(23) Park, C. S.; Lee, H. J.; Jamison, A. C. Robust Thick Polymer Brushes Grafted

453

from

454

Polymerization Initiators. ACS Appl. Mater. Interfaces 2016, 8 (8), 5586–5594.

455 456 457 458 459 460 461 462

Gold

Surfaces

Using

Bidentate

Thiol-Based

Atom-Transfer Radical

(24) Golriz, A. A.; Kaule, T.; Untch, M. B. Redox active polymer brushes with phenothiazine moieties. ACS Appl. Mater. Interfaces 2013, 5 (7), 2485–2494. (25) Ionov, L.; Minko, S. Mixed polymer brushes with locking switching. ACS Appl. Mater. Interfaces 2012, 4 (1), 483–489. (26) Yang, K.; Berg, M. M.; Zhao, C.; Ye, L. One-pot synthesis of hydrophilic molecularly imprinted nanoparticles. Macromolecules 2009, 42 (22), 8739–8746. (27) Zhou, F.; Zheng, Z.; Yu, B.; Liu, W.; Huck, W. T. Multicomponent polymer brushes. J. Am. Chem. Soc. 2006, 128 (50), 16253–16258.

463

(28) Watanabe, H.; Fujimoto, A.; Yamamoto, R. Scaffold for Growing Dense

464

Polymer Brushes from a Versatile Substrate. ACS Appl. Mater. Interfaces 2014, 6 (5),

465

3648–3653.

466

(29) Li, G. L.; Möhwald, H.; Shchukin, D. G. Precipitation polymerization for

467

fabrication of complex core–shell hybrid particles and hollow structures. Chem. Soc.

468

Rev. 2013, 42 (8), 3628–3646.

469

(30) Kroning, A.; Furchner, A.; Aulich, D. In situ infrared ellipsometry for protein

470

adsorption studies on ultrathin smart polymer brushes in aqueous environment. ACS

471

Appl. Mater. Interfaces 2015, 7 (23), 12430–12439.

472

(31) Zhao, M.; Zhang, C.; Zhang, Y.; Guo, X.; Yan, H.; Zhang, H. Efficient synthesis

473

of narrowly dispersed hydrophilic and magnetic molecularly imprinted polymer

474

microspheres with excellent molecular recognition ability in a real biological sample.

475

Chem. Commun. 2014, 50 (17), 2208–2210.

476

(32) Gonzato, C.; Courty, M.; Pasetto, P.; Haupt, K. Magnetic molecularly imprinted

477

polymer nanocomposites via surface–initiated RAFT polymerization. Adv. Funct.

478

Mater. 2011, 21 (20), 3947–3953.

479

(33) Chen, L.; Xu, S.; Li, J. Recent advances in molecular imprinting technology:

480

current status, challenges and highlighted applications. Chem. Soc. Rev. 2011, 40 (5),

481

2922–2942.

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

482

(34) Xu, S.; Li, J.; Chen, L. Molecularly imprinted core-shell nanoparticles for

483

determination of trace atrazine by reversible addition-fragmentation chain transfer

484

surface imprinting. J. Phys. Chem. 2011, 21 (12), 4346–4351.

485

(35) Chai, S.; Zhao, G.; Zhang, Y. N.; Wang, Y.; Li, M.; Li, D. Selective

486

photoelectrocatalytic degradation of recalcitrant contaminant driven by an n-P

487

heterojunction nanoelectrode with molecular recognition ability. Environ. Sci.

488

Technol. 2012, 46 (18), 10182–10190.

489

(36) Zhao, B.; Brittain, W. J. Synthesis, characterization, and properties of tethered

490

polystyrene-b-polyacrylate brushes on flat silicate substrates. Macromolecules 2000,

491

33 (23), 8813–8820.

492 493

(37) Roy, D.; Knapp, J. S.; Guthrie, J. T.; Perrier, S. Antibacterial cellulose fiber via RAFT surface graft polymerization. Biomacromolecules 2007, 9 (1), 91–99.

494

(38) Psarra, E.; König, U.; Ueda, Y. Nanostructured biointerfaces: nanoarchitectonics

495

of thermoresponsive polymer brushes impact protein adsorption and cell adhesion.

496

ACS Appl. Mater. Interfaces 2015, 7 (23), 12516–12529.

497

(39) Hufendiek, A.; Trouillet, V.; Meier, M. A.; Barner-Kowollik, C. Temperature

498

responsive cellulose-graft-copolymers via cellulose functionalization in an ionic

499

liquid and RAFT polymerization. Biomacromolecules 2014, 15 (7), 2563–2572.

500

(40) De, P.; Li, M.; Gondi, S. R.; Sumerlin, B. S. Temperature-regulated activity of

501

responsive polymer−protein conjugates prepared by grafting-from via RAFT

502

polymerization. J. Am. Chem. Soc. 2008, 130 (34), 11288–11289.

503

(41) Zhao, B.; Li, D.; Hua, F.; Green, D. R. Synthesis of thermosensitive

504

water-soluble polystyrenics with pendant methoxyoligo (ethylene glycol) groups by

505

nitroxide-mediated radical polymerization. Macromolecules 2005, 38 (23), 9509–

506

9517.

507

(42) Huang, N. P.; Michel, R.; Voros, J.; Textor, M.; Hofer, R.; Rossi, A.; Spencer, N.

508

D. Poly (L-lysine)-g-poly (ethylene glycol) layers on metal oxide surfaces:

509

surface-analytical characterization and resistance to serum and fibrinogen adsorption.

510

Langmuir 2001, 17 (2), 489–498.

511

(43) Zhao, M.; Chen, X.; Zhang, H.; Yan, H.; Zhang, H. Well-defined hydrophilic

ACS Paragon Plus Environment

Page 18 of 29

Page 19 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

512

molecularly imprinted polymer microspheres for efficient molecular recognition in

513

real biological samples by facile RAFT coupling chemistry. Biomacromolecules 2014,

514

15 (5), 1663–1675.

515

(44) Ma, Y.; Zhang, Y.; Zhao, M. Efficient synthesis of narrowly dispersed

516

molecularly imprinted polymer microspheres with multiple stimuli-responsive

517

template binding properties in aqueous media. Chem. Commun. 2012, 48 (50),

518

6217–6219.

519

(45) Pan, G.; Ma, Y.; Zhang, Y.; Guo, X.; Li, C.; Zhang, H. Controlled synthesis of

520

water-compatible molecularly imprinted polymer microspheres with ultrathin

521

hydrophilic polymer shells via surface-initiated reversible addition-fragmentation

522

chain transfer polymerization. Soft Matter 2011, 7 (18), 8428–8439.

523

(46) Jiang, J.; Zhang, Y.; Guo, X.; Zhang, H. Narrow or monodisperse, highly

524

cross-linked, and “living” polymer microspheres by atom transfer radical precipitation

525

polymerization. Macromolecules 2011, 44 (15), 5893–5904.

526

(47) Niu, H.; Yang, Y.; Zhang, H. Efficient one-pot synthesis of hydrophilic and

527

fluorescent molecularly imprinted polymer nanoparticles for direct drug quantification

528

in real biological samples. Biosens. Bioelectron. 2015, 74, 440–446.

529

(48) Meng, X.; Liu, Y.; Meng, M.; Gu, Z.; Ni, L.; Zhong, G.; Yan, Y. Synthesis of

530

novel ion-imprinted polymers by two different RAFT polymerization strategies for

531

the removal of Cs from aqueous solutions. RSC Advances 2015, 5 (17), 12517–12529.

532

(49) Luo, X. B.; Zhong, W. P.; Luo, J. M.; Yang, L. X.; Luo, S. L. Lithium

533

ion-imprinted polymers with hydrophilic PHEMA polymer brushes: the role of

534

grafting density in anti-interference and anti-blockage in wastewater. J. Colloid

535

Interface Sci. 2017, 492, 146–156.

536

(50) Takasu, K.; Inouie, H.; Kim, H. S; Suzuki, M.; Ihara, M. Rhodacyanine dyes as

537

antimalarials. 1. Preliminary evaluation of their activity and toxicity. J. Med. Chem.

538

2002, 45 (5), 995–998.

539

(51) Fabretti, A. C.; Peyronel, G. Rhodanine complexes of zinc(II), cadmium(II),

540

mercury(II) and mercury(I). Spectrochimica Acta Part A Molecular Spectroscopy

541

1978, 34 (7), 667–671.

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

542

(52) Ma, Y.; Pan, G.; Zhang, Y.; Guo, X.; Zhang, H. Narrowly dispersed hydrophilic

543

molecularly imprinted polymer nanoparticles for efficient molecular recognition in

544

real aqueous samples including river water, milk, and bovine serum. Angew. Chem.

545

Int. Ed. 2013, 52 (5), 1511–1514.

546

(53) Rowe, M. D.; Hammer, B. A. G.; Boyes, S. G. Synthesis of surface-initiated

547

stimuli–responsive diblock copolymer brushes utilizing a combination of ATRP and

548

RAFT polymerization techniques. Macromolecules, 2008, 41 (12), 4147–4157.

549

(54) Lü, H.; An, H.; Xie, Z. Ion-imprinted carboxymethyl chitosan–silica hybrid

550

sorbent for extraction of cadmium from water samples. Int. j. biol. Macromol. 2013,

551

56, 89–93.

552

(55) Li, F.; Jiang, H.; Zhang, S. An ion-imprinted silica-supported organic–inorganic

553

hybrid sorbent prepared by a surface imprinting technique combined with a

554

polysaccharide incorporated sol–gel process for selective separation of cadmium (II)

555

from aqueous solution. Talanta 2007, 71 (4), 1487–1493.

556 557

(56) Han, J. F.; Liao, C.; Cha, L. M.; Jiang, T.; Xie, H. M.; Zhao, K. Tem and xps studies on cds/cigs interfaces. J.Phys.Chem. Solids. 2014, 75 (12), 1279–1283

558

(57) Hintz, H.; Peisert, H.; Egelhaaf, H. J. Reversible and irreversible light-induced

559

p-doping of P3HT by oxygen studied by photoelectron spectroscopy (XPS/UPS). J.

560

Phys. Chem. C 2011, 115 (27), 13373–13376.

561

(58) Kundu, S.; Wang, Y.; Xia, W. Thermal stability and reducibility of

562

oxygen–containing functional groups on multiwalled carbon nanotube surfaces: A

563

quantitative high-resolution XPS and TPD/TPR Study. J. Phys. Chem. C 2008, 112

564

(43), 16869–16878.

565

ACS Paragon Plus Environment

Page 20 of 29

Page 21 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

1 2

3 4 5

TOC

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

6 7 8

Table captions Table 1. Polymerization conditions for synthesis of different ratios of grafted Cd-IIP/NIP via RAFT polymerization and their properties.

9 10

Table 2. Selectivity adsorption experiments parameters for IIP and Cd-IIP.

11 12

ACS Paragon Plus Environment

Page 22 of 29

Page 23 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

13

Table 1. Polymerization conditions for synthesis of different ratios of Cd-IIP/NIP

14

via RAFT polymerization and their properties. Cd-IIP/NIP

Brush reactant (mmol) HEMA Styrene 9 1 9 1 8 2 8 2 7 3 7 3

9:1-IIP 9:1-NIP 8:2-IIP 8:2-NIP 7:3-IIP 7:3-NIP

ΔW(%)

Mn,GPC

PDI

10.92 11.52 9.57 7.05 7.88 6.52

26378 25564 26307 20561 23685 17282

1.14 1.04 1.07 1.06 1.00 1.08

15 16 17 18 19

Table 2. Selectivity adsorption experiments parameters for IIP and Cd-IIP. metal ions

IIP KD

α

9:1-IIP β

KD

α

8:2-IIP β

124.5

KD

α

7:3-IIP β

78.0

KD

α

β

Cd( II )

138.4

Zn( II)

36.4

3.8

1.1

20.0

6.2

1.7

14.3

5.4 2.6

18.0

3.4

1.2

Ni( II )

26.9

5.1

1.8

21.1

5.9

2.6

12.8

6.1 2.8

14.3

4.3

1.2

Cu( II )

21.3

6.5

2.5

13.4

9.3

3.3

25.9

2.7 1.0

13.9

4.5

1.2

Co( II )

13.3

10.4

3.5

17.8

7.0

2.1

10.9

7.2 2.4

17.0

3.6

1.4

20

ACS Paragon Plus Environment

62.0

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

21

Figure captions

22

Figure 1. SEM images of (a) IIP and (c) their magnified detail, (b) 9:1-IIP grafted

23

copolymer brushes and (d) their magnified detail.

24 25

Figure 2. Equilibrium adsorption experiments for IIP and Cd-IIP.

26 27

Figure 3. The selectivity of Cd(II) adsorption among Zn(II), Ni(II), Cu(II), and Co(II)

28

mixture solution by IIP and Cd-IIP.

29 30

Figure 4. Adsorption experiments of IIP and Cd-IIP performed in simulated

31

wastewater which contains three kind different particle sizes of SiO2.

32 33

Figure 5. Adsorption experiments of IIP and Cd-IIP performed in simulated

34

wastewater which contains three kinds of flocculating agents CMC, PAC, and PAM

35

by adding single-component or pairwise orthogonal.

36 37

Figure 6. XPS spectra of (a) IIP and (b) 9:1-IIP survey; (c), (d) S 2p, and (e), (f) Cd 3d

38

for IIP and 9:1-IIP.

39 40 41

Figure 7. Adsorption experiments with IIP and Cd-IIP in real wastewater: Tin removal wastewater and Lithium battery wastewater.

ACS Paragon Plus Environment

Page 24 of 29

Page 25 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

42 43

44 45

Figure 1. SEM images of (a) IIP and (c) their magnified detail, (b) 9:1-IIP grafted

46

copolymer brushes and (d) their magnified detail.

47

48 49

Figure2. Equilibrium adsorption experiments for IIP and Cd-IIP.

50

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

51 52

Figure3. The selectivity of Cd(II) adsorption among Zn(II), Ni(II), Cu(II), and Co(II)

53

mixture solution by IIP and Cd-IIP.

54

55 56

Figure 4. Adsorption experiments of IIP and Cd-IIP performed in simulated

57

wastewater which contains three kind different particle sizes of SiO2.

58 59

ACS Paragon Plus Environment

Page 26 of 29

Page 27 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

60 61

Figure 5. Adsorption experiments of IIP and Cd-IIP performed in simulated

62

wastewater which contains floccules: (a) two kinds flocculating agents CMC, PAC,

63

and the mixture of two (b) PAM, the mixture of PAM and PAC, the mixture of with

64

PAM and CMC.

65

ACS Paragon Plus Environment

Industrial & Engineering Chemistry Research

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

66 67

Figure 6. XPS spectra of (a) IIP and (b) 9:1-IIP survey; (c), (d) S 2p, and (e), (f) Cd

68

3d for IIP and 9:1-IIP.

69

ACS Paragon Plus Environment

Page 28 of 29

Page 29 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

70 71

Figure 7. Adsorption experiments with IIP and Cd-IIP in real wastewater: Tin

72

removal wastewater and Lithium battery wastewater.

73 74

ACS Paragon Plus Environment