Carbon Nanotube Composites Synthesized by

Zunxian Yang , Qing Meng , Wenhuan Yan , Jun Lv , Zaiping Guo , Xuebin Yu , Zhixin Chen , Tailiang Guo .... Journal of Solid State Chemistry 2013 197,...
13 downloads 0 Views 528KB Size
2406

Chem. Mater. 2007, 19, 2406-2410

Nanostructured SnSb/Carbon Nanotube Composites Synthesized by Reductive Precipitation for Lithium-Ion Batteries Min-Sik Park,† Scott A. Needham,† Guo-Xiu Wang,†,‡ Yong-Mook Kang,*,§ Jin-Soo Park,† Shi-Xue Dou,† and Hua-Kun Liu† Institute for Superconducting and Electronic Materials and ARC Centre of Excellence for Electromaterials Science and School of Mechanical, Materials and Mechatronic Engineering, UniVersity of Wollongong, NSW 2522, Australia, and Energy Lab, Samsung SDI Company, 428-5 Gongse-ri, Giheung-eup, Yongin-si, Gyeonggi-do, Republic of Korea ReceiVed January 19, 2007. ReVised Manuscript ReceiVed March 15, 2007

Nanosized particles of SnSb alloy were coated on the surface of multiwalled carbon nanotubes (CNTs) by reductive precipitation of metal chloride salts within a CNT suspension. The SnSb-CNT nanocomposite showed a high reversible capacity of 480 mAh g-1 and stable cyclic retention until the 50th cycle. The improvement of reversible capacity and cyclic performance of the SnSb-CNT composite is attributed to the nanoscale dimension of the SnSb alloy particles (480 mAh g-1), and high coulombic efficiency (>95%) up to the 50th cycle, as shown in panels a and b of Figure 6. This indicates that the nanosized SnSb alloy contributed to the increases in Li+ storage, whereas randomly distributed CNTs contrib-

uted to maintaining the electronic conduction around the SnSb alloy particles, as well as accommodating the volume variation that was mainly induced by the reaction between Li+ and SnSb. From the viewpoint of electrochemical properties, CNT is apparently superior to other carbonaceous materials such as graphite,9 MCMB,10 and amorphous carbon.12 Because the structure of CNT is more adaptable to the homogeneous dispersion of SnSb nanoparticles than other carbonaceous materials, loading a large amount of SnSb particles into the composite can achieve a higher capacity. There is evidence to believe that CNTs more effectively prevent the agglomeration of nanosized SnSb particles and therefore retain the enhanced electrical properties of the SnSb alloy in nanoscale form. On the basis of this result and discussion, it could be concluded that the reversible capacity loss or electrical disconnection induced by the agglomeration of nanosized SnSb alloy could be effectively reduced in the SnSb-CNT nanocomposite prepared by the reductive precipitation process. In summary, we have fabricated SnSb-CNT nanocomposite by means of reductive precipitation of metal chloride salts. The CNTs were a sort of framework used to pin nanosized SnSb particles on the surface and, as a result, hinder the agglomeration of SnSb nanoparticles. Several structural analyses clearly showed that SnSb particles were homogeneously precipitated on CNT with the help of Sn-C bonding between SnSb and CNT. SnSb-CNT nanocomposite showed an enhanced reversible capacity (>480 mAh g-1) and stable cyclic retention because the drastic volume variation due to the agglomeration of SnSb alloy particles was effectively reduced during the electrochemical reaction. It could be clearly seen that CNTs were suitable for pinning nanosized SnSb particles and preventing their agglomeration, as well as maintaining the electrical connection around the SbSb particles. However, there was a unique drawback, that the increased initial irreversible capacity caused by the trapped Li+ in the inner holes or defects of CNT. Finally, careful attention to the design and fabrication of these types of complex nanocomposites may lead to their full potential being exploited in commercial lithium ion batteries. Acknowledgment. Financial support provided by the Australian Research Council (ARC) through an ARC Centre of Excellence project (CE0561616) and an ARC Discovery project (DP0559891) are gratefully acknowledged. The authors thank Dr. T. Silver at the University of Wollongong (Australia) and Dr. H.S. Kim at the Universty of Pennsylvania for their contributions. Supporting Information Available: Experimental details and Figures 7 and 8. This material is available free of charge via the Internet at http://pubs.acs.org. CM0701761