Article

Highly stretchable DNA/clay hydrogels with self-healing ability Ahmet Talha Uzumcu, Orhan Guney, and Oguz Okay ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.8b00168 • Publication Date (Web): 14 Feb 2018 Downloaded from http://pubs.acs.org on February 19, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 37 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Highly stretchable DNA/clay hydrogels with self-healing ability Ahmet T. Uzumcu, Orhan Guney,* and Oguz Okay*

Istanbul Technical University, Departments of Chemistry and Polymer Science & Technology, 34469 Maslak, Istanbul, Turkey

ABSTRACT: We present mechanically strong and self-healable clay hydrogels containing 2 to 8 w/v% ds-DNA together with a synthetic biocompatible polymer, poly(N,N-dimethylacrylamide). Clay nanoparticles in the hydrogels act like a chemical cross-linker and promote their elastic behavior while DNA contributes to their viscoelastic energy dissipation. The extent of mechanical hysteresis during cyclic tensile tests reveals that the strength of intermolecular bonds in DNA/clay hydrogels is in the range of the strength of hydrogen bonds. The hydrogels exhibit a high stretchability (up to 1500%) and a tensile strength between 20 and 150 kPa. They have the ability to self-heal, induced by heating the damaged gel samples above the melting temperature of ds-DNA. When comparing the mechanical properties of the hydrogels before and after healing, the healing efficiency is greater than 100%. We also demonstrate that ds-DNA molecules entrapped in the gel network undergoes thermal denaturation/renaturation cycles leading to a further improvement in the mechanical properties of the hydrogels.

Keywords: DNA; clay; nanocomposite hydrogels; mechanical properties; self-healing.

1

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 37

INTRODUCTION Deoxyribonucleic acid (DNA) existing in all living cells is a semi-flexible biopolymer with a double-helical conformation in its native state. Heating aqueous double-stranded (ds) DNA solutions breaks the hydrogen bonds keeping the double-strands together and ds-DNA dissociates into flexible single strands.1 The thermal transition from double- to single stranded (ss) DNA is called denaturation or melting which can be reversed by slow cooling dilute DNA solutions.2 DNA as a smart biomaterial has received interest in the past decades due to its programmable base-pairing recognition, designable sequence, and predictable secondary structure.3,4 Hydrogels derived from DNA are 3D networks of DNA strands containing large quantities of water.5,6 DNA hydrogels are excellent candidates to utilize the unique features of DNA molecules such as bioresponsivity,

biocompatibility,

biodegradability,

selective

binding,

and

molecular

recognition.7,8 DNA-based hydrogels can thus be used in a variety of applications including controlled release of biocatalysts,9 chemotherapy drug doxorubicin,10 proteins,11 and cells,12 for constructing three-dimensional tissue-like structures,13 for highly sensitive detection of mercury and lead ions,14-16 cocaine,16 and DNA.17

Several approaches have been developed

to produce physical or chemical DNA

hydrogels.3,4,9,11,18-23 For instance, a chemical network of DNA strands was created by enzymatic ligation of branched DNA,24 while DNA hydrogels with reversible cross-links were produced by cross-linking DNA-polyethylene glycol-DNA triblock copolymers using K+ or Na+ ions.25 Liu and co-workers developed several strategies for the preparation of supramolecular DNA hydrogels with self-healing ability.3,19,21,26 The research group also reported preparation of double-network hydrogels based on DNA that exhibit a storage modulus of around 300 Pa and 2

ACS Paragon Plus Environment

Page 3 of 37 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

reversible gel-sol transition.20 Supramolecular self-healable graphene oxide / DNA hydrogels exhibiting a storage modulus of 4.6 kPa were also prepared via π-π stacking and hydrophobic interactions.18 DNA hydrogels can also be produced by cross-linking DNA in semi-dilute aqueous solutions in the presence of diepoxides as a chemical cross-linker.27,28 Despite many advantages, widespread use of DNA hydrogels is limited due to their poor mechanical properties. Moreover, many applications require mechanically strong DNA hydrogels combined with selfhealing ability to prolong their lifetimes.

Physical gels formed by clay such as Laponite nanoparticles provide a protective environment for biomolecules by enhancing their bioresponsivity and stability against degradation, that may have been important in the origin and sustainability of life on earth.29,30 For instance, ds-DNA without protection of clay hydrogels is easily digested by the DNase, while in the clay environment, it is effectively protected from DNase digestion and preserves its biological function.29 Laponite is a synthetic hectorite clay that forms disk-like particles in water with a thickness of 1 nm and a diameter of about 25 nm stabilized by their surface charges. Haraguchi et al showed that Laponite particles act as a multifunctional cross-linker during the solution polymerization of monomers such as N-isopropylacrylamide (NIPAM) or N,N-dimethylacrylamide (DMAA) and produce synthetic hydrogels with extraordinary mechanical properties.31-34 Taki et al reported a significant increase of the loss factor tan δ after incorporation of DNA in clay hydrogels.35 Recently, we prepared DNA hydrogels containing Laponite particles and poly(NIPAM) chains exhibiting a fracture stress and elongation to break of up to 53 kPa and 544%, respectively.36 However, they lack the ability to self-heal upon damage, and thermal denaturation/renaturation

3

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 37

cycle of ds-DNA in the hydrogel could not be monitored because poly(NIPAM) turns into collapsed state above its lower-critical-solution temperature (34 °C).

To address this problem, we present here DNA/clay hydrogels of high stretchability (up to 1500%) and a tensile strength between 20 - 150 kPa by in situ polymerization of DMAA in aqueous solutions of ds-DNA (2 to 8 w/v%) in the presence of Laponite nanoparticles. The hydrogels thus prepared also contain poly(DMAA), which is a hydrophilic and biocompatible polymer with associative properties.37,38 As will be seen below, DNA entrapped in clay hydrogels undergoes thermal denaturation/renaturation cycle leading to a further improvement in the hydrogel mechanical properties. The hydrogels have the ability to self-heal, induced by heating the damaged gel samples above the melting temperature of ds-DNA. When comparing the mechanical properties of the hydrogels before and after healing, the healing efficiency is greater than 100%.

EXPERIMENTAL PART Materials. The hydrogels were prepared from deoxyribonucleic acid sodium salt from salmon testes (DNA, Sigma-Aldrich) having a melting temperature of 87.5 oC and an average molecular weight of 1.3x106 g/mol corresponding to ~ 2000 base pairs. Laponite XLG clay, [Mg5.34Li0.66Si8O20(OH)4]Na0.66, was purchased from Rockwood Ltd. N,N-dimethylacrylamide (DMAA) provided by Sigma-Aldrich was purified by filtering through activated alumina. Ammonium persulfate (APS), N,N,N’,N'-tetramethylethylenediamine (TEMED), and ethidium bromide (EtBr) were all purchased from Sigma-Aldrich (St Lois, MO) and used without purification. 4

ACS Paragon Plus Environment

Page 5 of 37 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Hydrogel Preparation. The hydrogels were prepared at 25oC by polymerization of 1 M DMAA in aqueous ds-DNA solutions containing Laponite XLG clay in the presence of APS (3.5 mM) TEMED (0.08 v/v%) redox initiator system. Two sets of experiments were carried out. In the 1st set, clay content was varied between 2 and 7 w/v% at 2 w/v% DNA. In the 2nd set, clay content was kept at 5 w/v% while the concentration of DNA was varied between 2 and 8 w/v%, which are much above its critical overlap concentration (0.043 w/v%).27 Laponite clay was first dispersed in deionized water under vigorous stirring for 60 to 90 min to obtain a homogeneous, transparent dispersion. After addition of DMAA and mixing 15 min, ds-DNA was included in the solution and stirred for 24 hours at 35 oC. The initiator APS was then added to the viscous solution and stirred in an ice-water bath for 1h, followed by the addition of the accelerator TEMED to initiate the reaction. The reaction solutions were transferred into plastic syringes of 4.5 mm in internal diameter, as well as between parallel plates of the rheometer to monitor the gelation reactions. To highlight the effect of DNA on the gel properties, the hydrogels were also prepared without addition of ds-DNA.

Fluorescence Measurements. The measurements were carried out using a Varian Cary-Eclipse Luminesce Spectrometer. The gelation solutions containing 10 µM ethidium bromide (EtBr) as a fluorescent probe were transferred into the fluorescence cell of the spectrometer, which is a cylindrical glass tube of 10 mm in internal diameter. The measurements were performed at various reaction times at an excitation wavelength of 530 nm and then, the emission spectra between 550 and 800 nm were recorded. For the measurements on hydrogel samples at various

5

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 37

temperatures between 25 and 90 oC, they were first immersed in a temperature controlled water bath to adjust the temperature prior to the measurements.

Rheological Experiments. Rheological tests were carried out on a Bohlin Gemini 150 Rheometer system (Malvern Instruments, UK) equipped with a Peltier device for temperature control. The gelation solutions were placed between the parallel plates of the instrument. The upper plate (diameter 40 mm) of the rheometer was set at a distance of 500 µm before the onset of the reactions. During all of the rheological tests, a solvent trap was used and the outside of the upper plate was covered with a thin layer of low-viscosity silicone oil to prevent evaporation of water. The dynamic moduli of the reaction system were monitored at a frequency ω = 6.28 rad s−1 and a deformation amplitude γo = 0.01 to ensure that the oscillatory deformation is within the linear regime (Figure S1). After a reaction time of 2 h, frequency-sweep tests at γo = 0.01 were carried out at 25 oC over the frequency range 6.3x10-2 to 3.1x102 rad·s-1. Oscillatory deformation tests on gel samples were also carried out by on-off switching of the applied strain γo. The tests were carried out by application of a high strain and monitoring the dynamic moduli of the sample for a duration of 10 min, followed by immediate reduction of the strain to a low value and monitoring the moduli for 10 min. The gel samples formed between the parallel plates of the rheometer were also subjected to thermal cycles by first heating from 25 to 90 oC at a rate of 3.3 o

C·min-1, keeping at 90 oC for 10 min, and then cooling back to 25 oC at 1.1 oC·min-1, and finally

keeping at 25 oC for at least 10 min. The changes in the dynamic moduli of gels were monitored during the course of the cycle as a function of temperature.

6

ACS Paragon Plus Environment

Page 7 of 37 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

X-ray diffraction measurements. The hydrogel samples were dried at 24±1 °C for 48 hours and then at 80 °C under vacuum for 24 h. X-ray diffraction (XRD) patterns of dried gel samples were collected on a Bruker AXS D8 diffractometer using a Cu-Kα source (λ = 1.54184 Å) operating at 30 kV / 10 mA. The patterns were collected in the 5-15 °, 2θ range with a scan rate of 0.01 °·min1

.

Mechanical Tests. Uniaxial elongation tests were performed on a Zwick Roell Z0.5 TH test machine using a 500 N load cell. The tests were carried out at 24±1 oC using cylindrical gel samples of about 4.5 mm in diameter. The initial sample length between jaws was fixed at 30±2 mm. The nominal stress σnom and strain ε, which is the change in the sample length relative to its initial length, were recorded at a fixed strain rate of 5.6x10-2 s-1. The Young's modulus E was calculated from the slope of stress strain curves between 5 and 15% deformations. Cyclic elongation tests were conducted by first stretching the gel sample to a maximum strain εmax and then unloading. After certain relaxation time which was varied between 3 and 9 min, they were again stretched to a higher εmax that increased stepwise from 200 to 800%. To quantify the selfhealing ability of the hydrogels, gel samples were cut in the middle, and then the two halves were gently connected together within a plastic syringe (having same diameter with the samples) followed by heating to 80 or 90 oC. To quantify the healing efficiency, uniaxial elongation tests were performed on both virgin and healed gel samples.

Swelling tests and DNA release studies. DNA/clay hydrogels of about 4.5 mm in diameter were cut into samples of about 10 mm in length. Each gel sample of mass mo was immersed in an excess of water and the gel mass m in water at 24±0.5 oC was monitored by weighing the samples 7

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 37

every day and refreshing water. The relative degree of swelling mrel = m/mo was monitored until obtaining the equilibrium swelling degree mrel,eq. For accurate results, at least three different samples were measured for each type of gel. The amount of ds-DNA released during swelling was estimated by both UV and fluorescence spectroscopy. For UV measurements, ds-DNA release to water was monitored on a T80 UV–vis spectrometer using the molar extinction coefficient ε260 determined as 6900 M-1 cm-1 at 260 nm. For the fluorescence measurements, water samples were collected from the external solution during the swelling process of the hydrogels. After addition of 10 µM EtBr, the measurements were conducted at an excitation wavelength of 530 nm and then, the emission spectra between 550 and 800 nm were recorded. The amount of ds-DNA released from the hydrogels was estimated from the maximum intensity at 600 nm (Imax). For this purpose, a calibration curve was prepared by measuring Imax of aqueous 10 µM EtBr solutions containing varying amounts of ds-DNA (0-30 mM), and plotting Imax against ds-DNA concentration.

RESULTS AND DISCUSSION Formation and microstructure. DNA/clay hydrogels were prepared by free-radical polymerization of N,N-dimethylacrylamide (DMAA) at a concentration of 1 M in aqueous dsDNA solutions containing Laponite (XLG) nanoparticles. Two sets of gelation experiments were carried out. In the 1st set, the amount of DNA in the feed was set to 2 w/v% while the XLG content was varied between 2 and 7 w/v%. In the 2nd set, XLG content was kept at 5 w/v% and DNA concentration was varied between 2 and 8 w/v%. In the following, the hydrogels are denoted as NC-DNA-x/y where NC means nanocomposite, x and y denote the concentrations of XLG and DNA in w/v%, respectively. For comparison, hydrogels without DNA were also 8

ACS Paragon Plus Environment

Page 9 of 37

prepared and denoted as NC-x. Figure 1a shows the reaction time dependences of the storage modulus G’ and loss factor tan δ (= G’’/G’) during the 1st (upper panel) and 2nd set of experiments (bottom panel). Following an induction period of 14±4 min, the modulus G’ rapidly increases while tan δ decreases and then, they approach plateau values after about 70 min. Figure 1b showing G’ and tan δ values after a reaction time of 70 min reveals opposite effects of DNA and XLG on the viscoelastic properties of NC-DNA hydrogels. XLG acts like a chemical crosslinker and promotes the elastic behavior of the hydrogels by increasing the modulus and decreasing the loss factor. In contrast, DNA contributes to their viscoelasticity and produces hydrogels with a lower modulus and a higher loss factor suggesting weakening of clay – polymer interactions in the presence of DNA. (a) XLG w/v% =

5

2 4 4

100

5

2

XLG w/v% 4 6

(b)

8

12 9 6

7

101

2 G' / kPa

G' / kPa

7

100 tan δ

XLG w/v% =

101

10-1

3

100

DNA w/v% = 0

DNA w/v% =

8 4

8

0.3 tan δ

4

tan δ

2

G' / kPa

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

0.2

2

0.1

100

10-1

0

0.0 0

20

40

Time / min

60 0

20

40

60

Time / min

0

2

4

6

8

DNA w/v%

Figure 1. (a): Variations of the storage modulus G’ and the loss factor tan δ during the formation of NC-DNA hydrogels. The data are from the 1st (upper panel) and 2nd set of experiments (bottom panel). Temperature = 25 °C. ω =6.3 rad s-1. γo = 0.01. (b): G’ and tan δ of 9

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

the hydrogels after a reaction time of 70 min plotted against their DNA (circles) and XLG contents (triangles). Figures 2 shows the frequency dependences of G’ (blue circles) and tan δ (solid curves) for NC-DNA hydrogels after a reaction time of 2 h. For comparison, G’ and tan δ of the corresponding NC-hydrogels prepared without DNA are also shown by gray triangles and dashed curves, respectively. The general trend is that at low frequencies, NC-DNA’s exhibit a lower modulus and a higher loss factor as compared to the NC’s revealing energy dissipation. We attribute this energy dissipation at long experimental time scales to the weak clay-DNA interactions. ds-DNA molecules in the hydrogel could follow the slow oscillation and slip on the surface of the nanoparticles by dissipating energy. At high frequencies, tan δ of NC-DNA’s is similar to that of NC’s, likely because the semi-flexible ds-DNA with a persistence length of 50 nm could not move with a high frequency in the gel network. NC-DNA 4/2

NC-DNA 2/2

100

NC-DNA 5/8

NC-DNA 6/2

tan δ

101 G' / kPa

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 37

10-1

100 10-1

100

101

ω / rad.s-1

102 10-1

100

101

ω / rad.s-1

102 10-1

100

101

ω / rad.s-1

102 10-1

100

101

102

ω / rad.s-1

Figure 2. G’ (blue circles) and tan d (solid curves) of NC-DNA hydrogels shown as a function of the frequency ω measured after 2 h of reaction time. The hydrogel codes are indicated. G’ and tan δ of the corresponding NC-hydrogels are shown by gray triangles and dashed curves, respectively. Temperature = 25 °C. γo = 0.01. 10

ACS Paragon Plus Environment

Page 11 of 37 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

The results can be explained by considering the extent of intermolecular interactions between the gel components. XLG nanoparticles suspended in water carry strongly negative charge on the surface and weakly positive charge on the rim.39,40 Previous work shows that non-ionic monomers such as DMAA surround the surface of XLG particles in aqueous solutions, which prevent formation of clay hydrogels with a house-of-cards structure via face-rim associations.31,33,41-43 After polymerization of DMAA in aqueous XLG dispersion, a large number of poly(DMAA) chains are aggregated on the surface of clay particles that form multiple hydrogen bonding with the particles leading to hydrogels with extraordinary mechanical properties.31 However, DNA cannot surround the particles due to its repulsive interactions with the negatively charged particle surfaces, which prevent hydrogen bonding between DNA and clay so that DNA strands can slip between the particles by dissipating energy. Thus, increasing amount of DNA in the hydrogel also increases the loss factor due to the weak DNA-clay interactions.

The surface charge of XLG clay used in the hydrogel preparation provides homogeneous distribution of clay nanoparticles in deionized water as well as in DMAA solutions with an exfoliated structure.31-34 To demonstrate the exfoliation of XLG in the viscous gelation solution containing ds-DNA of 2000 base pairs long, XRD measurements were carried out on dried gel samples. Figure 3a shows XRD patterns of dried NC-DNA-5/4 and NC-5 hydrogels together with XLG clay as a reference. The clay shows a strong diffraction peak at 2θ = 7.2° corresponding to a layer spacing of 1.23 nm between regularly stacked clay sheets. This peak is absent in both NCDNA-5/4 and NC-5 hydrogels indicating that the clay particles are dispersed uniformly

11

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 37

throughout the poly(DMAA) / DNA network, similar to the ordinary NC hydrogels prepared without DNA.

Another question regarding the microstructure of NC-DNA hydrogels is whether the native double-stranded (ds) conformation of DNA remains intact after the gelation reaction or, ds-DNA dissociates into single strands? To monitor the conformation of DNA during gelation, fluorescence measurements were conducted using ethidium bromide (EtBr) as a fluorescent probe. EtBr is known to bind ds-DNA by intercalation of its planar phenanthridium ring between the DNA base pairs and results in an increase of EtBr fluorescence.28,44 Due to the intercalation mechanism, ds-DNA leads to a higher increase in EtBr intensity than single-stranded (ss) DNA. Figure 3b shows the fluorescence spectra of 10 µM EtBr in a gelation solution containing 1 M DMAA, 2 w/v% DNA and APS/TEMED redox initiator system. Because XLG nanoparticles interact with EtBr and results in an enhancement of EtBr fluorescence intensity,36 XLG was not included in the gelation solution. The spectra were recorded before and just after addition of APS/TEMED initiator system, and after reaction times of 10 and 60 min, indicated in Figure 3b by 1, 2, 3, and 4, respectively. The inset to the figure shows the emission intensity of EtBr at 600 nm plotted against the reaction time up to 90 min.

The emission intensity of EtBr rapidly decreases after the addition of APS/TEMED system as well as during the induction period of the reaction (Figure 1a), while it again increases with increasing reaction time up to 40 min and then levels off. We attribute the initial decrease of fluorescence intensity to the interactions between negatively charged sulfate groups of APS and the positively charged phenanthridium ring nitrogen of EtBr.45 However, after gel formation, 12

ACS Paragon Plus Environment

Page 13 of 37

ionic interactions between EtBr and APS become weaker due to intercalation of EtBr between the base pairs of DNA within the gel network so that the intensity again increases.46 (a)

Intensity / a.u.

NC-DNA-5/4

600

400

NC-5

200

6

8

10

12

14

2θ θ / ° Imax 400

6

400

1 2

Co

oli

2 3 600

ng

Imax 800

1 4 2

750

3 0

400

30 60 90 Time / min

200

550

(c)

1

4

800

600

650

700

Wavelength / nm

(d)

25 °C

1

3

300

6

(b) Fluorescence intensity / a.u.

XLG

800

Fluoresence intensity / a.u.

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

300

5 4

200

He a

2 tin g

5

3 4

90 °C

30 45 60 75 90 Temperature / °C

25 °C

100

600

650

700

Wavelength / nm

Figure 3. (a): XRD patterns of XLG, dried NC-DNA-5/4, and NC-5 hydrogels in 5 − 15° 2θ ranges. Scan rate = 0.01 °·min-1. (b): Fluorescence spectra of 10 µM EtBr in gelation solution containing 1 M DMAA, 2 w/v% DNA and APS/TEMED redox initiator system. The spectra were recorded before and after addition of APS/TEMED initiator system, and after a reaction time of 10 and 60 min, indicated by 1, 2, 3, and 4, respectively. The inset shows the emission intensity of EtBr at 600 nm plotted against the reaction time. (c): Fluorescence spectra of EtBr in NC-DNA-5/4 hydrogel at 25 (1), 40 (2), 55 (3), 75 (4), and 90 °C (5), and after cooling back to 25 °C (6). The inset shows emission intensity of EtBr at 600 nm plotted against the temperature. 13

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 37

The numbers in the inset correspond to those given on the spectra. Note that the slight increase of the intensity between the points 4 and 5 was not observed in the absence of XLG (Figure S2). (d) Images of NC-DNA-5/4 hydrogel sample swollen in 10 µM EtBr solution. The images were taken under UV light at 25 and 90 °C, and after cooling back to 25 °C. The stability of native DNA conformation in the hydrogels was also verified by subjecting NCDNA gel specimens after a reaction time of 24 h to the heating-cooling cycles between below and above the melting temperature Tm (87.5 °C) of ds-DNA. Sealed hydrogel samples containing 10 µM EtBr were first heated from 25 to 90 °C at a heating rate of 3.25 °C·min-1 and then cooled back at 1.1 °C·min-1 during which the emission spectra were recorded. Figure 3c shows typical fluorescence spectra of EtBr in NC-DNA-5/4 hydrogel at various temperatures while the inset presents the emission intensity of EtBr at 600 nm plotted against the temperature. The numbers on the spectra correspond to the numbers shown in the inset. The maximum intensity decreases as the temperature is increased to 90 °C indicating the conformational transition from double- to single-stranded DNA within the hydrogel and thus confirms that DNA is in its native conformation after gelation. When the gel is cooled back to 25 °C, fluorescence emission intensity of EtBr in the gel again increases and rises above its initial value (Figure 3c). When the experiments were repeated using hydrogel samples prepared without XLG, the fluorescence intensity after the heating-cooling cycle returned back close to the initial value revealing that the clay nanoparticles are responsible for the higher intensity (Figure S2). The conformational transition of ds-DNA in the hydrogels was also visualized by the optical images of the gel samples swollen in 10 µM EtBr solution (Figure 3d). The initial yellow-orange color of the gel specimen under UV light becomes weaker at 90 °C due to the decrease of fluorescence intensity while the initial color is recovered upon cooling to 25 °C. The results thus reveal that upon 14

ACS Paragon Plus Environment

Page 15 of 37

heating above Tm, ds-DNA molecules in NC-DNA hydrogels are dissociated into single strands and this can be reversed by cooling below the melting temperature Tm. NC-DNA-5/4

(a) 0.4

102

0.3 25 °C

tan δ

G' / kPa

NC-DNA-5/6

0.2

101 90 °C

25 °C

0.1 0

3

6

9 30 40 50 60 70 80

Time / min

3

Temperature / oC

6

9

Time / min

before cycle

G', G'' / kPa

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

102

80 70 60 50 40 30 o

Temperature / C

3

6

9

Time / min

after cycle

(b)

NC-DNA-5/2

NC-DNA-5/1

NC-DNA-5/4

101

100

100

101

ω / rad s-1

102100

101

102

ω / rad s-1

100

101

102

ω / rad s-1

Figure 4. (a): G’ (symbols), and tan δ (lines) of NC-DNA-5/4 and -5/6 hydrogels during heatingcooling cycle between 25 and 90 °C. ω = 6.28 rad s-1. γo = 0.01. (b): Frequency dependence of G’ (filled symbols) and G’’ (open symbols) for NC-DNA hydrogels before and after the heatingcooling cycle. Temperature: 25 °C. γo = 0.01. Previous work shows that the storage modulus G’ of aqueous semi-dilute solutions of ds-DNA significantly increases when subjected to the heating – cooling cycles between below and above the melting temperature of DNA.27,28,47 This phenomenon is due to the formation of hydrogen 15

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 37

bonds between strands belonging to different ds-DNA molecules acting as additional physical cross-links. We observed a similar behavior in the present NC-DNA hydrogels as presented in Figure 4a, where the variations of G’ and tan δ of NC-DNA-5/4 and -5/6 hydrogels are shown during the heating – cooling cycle between 25 and 90 °C. Figure 4b shows frequency-sweep results of NC-DNA-5/1, -5/2, and 5/4 hydrogels before (gray circles) and after the heating– cooling cycle (blue triangles). tan δ significantly increases during the heating period reflecting energy dissipation due to the dissociation of semi-flexible ds-DNA to its flexible single strands. Moreover, G’ increases about one-order of magnitude after the cycle indicating formation of additional hydrogen bonds. The final modulus of the hydrogels is in the range of 100 kPa and remained almost unchanged at room temperature. In contrast, NC hydrogels prepared without DNA showed a much lesser extent of modulus increase after the cycle and this increase was reversible, i.e., G’ dropped back close to its initial value after a storage time of 7 h (Figure S3).

Mechanical properties and self-healing behavior. Mechanical properties of NC-DNA hydrogels were investigated at 24±1 oC by uniaxial elongation and compression tests. Because of the significant effect of the heating-cooling cycle between below and above Tm of ds-DNA on the hydrogel properties, the tests were carried out on the gel specimens before and after subjecting to the thermal cycles. Figure 5a shows typical tensile stress-strain curves at a strain rate of 5.6x10-2 s-1 for NC-DNA-5/2, -5/4, and -5/6 hydrogels before (dashed curves) and after subjecting to the heating–cooling cycles (solid curves). For comparison the data obtained from NC-5 hydrogel containing no DNA is also shown. As expected, stress-strain curves of NC-5 hydrogel before and after the cycle are similar. In contrast, all NC-DNA’s after the cycle exhibit a higher initial slope, i.e., Young’s modulus E, and a higher fracture stress σf as compared to the virgin ones. 16

ACS Paragon Plus Environment

Page 17 of 37

before cycle after cycle

NC-DNA-5/2

NC-5

100

(b)

50

E / kPa

σ nom / kPa

(a)

before cycle after cycle

150

40

30

50 20 0 0

500

1000 1500

Elongation %

500

1000

1500

Elongation %

200

NC-DNA-5/6

σ f / kPa

NC-DNA-5/4

σ nom / kPa

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

60

30

150

100

50

0 0

0 0

400

800

1200

Elongation %

200

400

600

2

4

6

800

Elongation %

DNA w/v%

Figure 5. (a): Nominal stress σnom plotted against the elongation ratio ε of NC-DNA and NChydrogels before (dashed curves) and after the heating-cooling cycle (solid curves). Strain rate = 5.6x10-2 s-1. Temperature = 24±1 °C. (b): Young’s modulus E and the fracture stress σf of the hydrogels before (triangles) and after the heating-cooling cycle (circles) plotted against their DNA contents. The modulus E and the fracture stress σf of the hydrogels compiled in Figure 5b reveal that the higher the DNA content, the higher is the increase of both the modulus and fracture stress after the thermal cycle reflecting formation of additional physical cross-links due to the denaturation and renaturation of ds-DNA. Similar results were also obtained from uniaxial compression tests (Figure S4). Moreover, the stretchability of NC-DNA hydrogels is between 140-800% at or above 4 w/v% DNA while it significantly increases with decreasing DNA content. Highly 17

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 37

stretchable hydrogels exhibiting an elongation at break between 1100-1500% could be obtained at 1 - 4 w/v% DNA (Figures 5a and S5).

Because of the supramolecular nature of the hydrogels, they are potential candidate for selfhealing systems. To understand whether the intermolecular non-covalent bonds dissociate and reassociate reversibly under stress, rheological and mechanical tests were conducted on NC-DNA hydrogels. The gel samples in the form of membranes of 0.5 mm in thickness locating between the parallel plates of the rheometer were subjected to oscillatory deformation tests by on-off switching of the applied strain γo. The tests consisted of the application of a high strain γo,h and monitoring the storage G’ and loss moduli G” of the gel sample for a duration of 10 min, followed by immediate reduction of γo,h to a low value γo,l, and monitoring the G’ and G” for 10 min. γo,l was fixed at 1% while γo,h was stepwise increased from 3 to 300%.

The results for NC-DNA-5/4 hydrogel are shown in Figure 6 where the storage modulus G’ (left) and the loss factor tan δ (right) during the repeated on-off strain cycles are plotted against time. The dashed red lines represent the schedule of the stepwise increased γo,h separated with a low strain γo,l of 1%. Upon application of a high strain, the modulus G’ decreases while the loss factor tan δ increases indicating damage in the gel sample and energy dissipation under strain. However, when the strain is reduced to γo,l, G’ again increases and tan δ decreases revealing the recovery of the microstructure. For instance, G’ of the hydrogel under 300% strain is 0.5 kPa while after reducing the strain to 1%, G’ increases to 6.7 kPa which is 84% of the modulus of the virgin gel sample (8 kPa). Figure 6 also shows that the recovery in tan δ is much lower than that in G’ and it increases from 0.16 to 0.35 after the repeated strain cycles. The results thus indicate a 18

ACS Paragon Plus Environment

Page 19 of 37

partial recovery of the initial microstructure of the gel network upon application of a strain up to 300%.

10 2

10 1

0.4

Strain / %

0.6

tan δ

G'

101 G' / kPa

0.8 tan δ

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

100 0.2

10 0 0

20

40

60

80

100

0

Time / min

20

40

60

80

100

Time / min

Figure 6. G’ (left) and tan δ (right) of NC-DNA-5/4 hydrogel during on-off strain cycles plotted against time. The dashed red lines represent the schedule of the stepwise increased strain γo,h separated with a low strain γo,l. Temperature = 25 °C. For a deeper understanding of the nature of non-covalent bonds, NC-DNA hydrogels were subjected to cyclic tensile tests at a strain rate of 5.6x10-2 s-1. Figures 7a and b show cyclic tensile stress–strain curves of NC-DNA-5/4 hydrogels before and after the thermal cycle, respectively. The mechanical cycles compose of eight successive loading (solid curves) and unloading cycles (thin dashed curves) with a relaxation time of 9 min between cycles. Note that, in the preliminary experiments, the relaxation time between cycles was varied between 3 and 9 min and the highest recovery was observed after 9 min (Figure S6). The gel samples were first stretched to a maximum strain εmax of 100% and then unloaded. After a waiting time of 9 min, they were again stretched to a higher εmax that increased stepwise from 200 to 800%. Each cycle shows a 19

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

mechanical hysteresis that increases with increasing maximum strain εmax. Moreover, the loading curve of each cycle is between the loading and unloading curves of the previous cycle revealing quasi-reversibility of the successive cycles. This finding is in accord with the results of the rheological tests and indicate that the original microstructure can partially be restored by allowing the damaged hydrogel to rest between cycles for 9 min. 1

Cycle Number:

2

3

5

4

6

7

8

(c)

(b)

(a)

60

NC-DNA-5/4 (before cycle) NC-DNA-5/4 (after cycle)

l

40

ng di oa

NC-5

90 Uhys / kJ.m-3

σnom / kPa

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 37

ing load

20

60

30 0 0 0

200

400

600

Elongation (εε ) %

800

200

400

600

800

Elongation (ε ) %

0

2

4

6

8

εmax

Figure 7. (a, b): Nominal stress σnom vs elongation ratio ε curves from cyclic elongation tests of NC-DNA-5/4 hydrogels before (a) and after the heating-cooling cycle (b). The tests were conducted with increasing maximum strain εmax with a waiting time of 9 min between cycles. Temperature = 24±1°C. (c): Hysteresis energies Uhys of NC-DNA-5/4 before (circles) and after the heating-cooling cycle (triangles up), and NC-5 (triangles down) shown as a function of the maximum strain εmax. The lines are best fit to the data. The energy Uhys dissipated during the mechanical cycle was calculated from the area between the loading and unloading curves using the equation:

20

ACS Paragon Plus Environment

Page 21 of 37 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

ε max

U hys =

∫σ

0 nom

dε −

0

∫σ

nom



(1)

ε max

In Fig. 7c, Uhys energies of NC-DNA-5/4 before and after thermal cycle, and the corresponding NC-5 are plotted against the maximum strain εmax. Uhys linearly increases with εmax with a slope that increases from 7.6±0.3 to 14.0±0.2 kJ·m-3 after subjecting NC-DNA-5/4 hydrogel to the thermal cycle (Table 1). We assume that Uhys is the sum of the dissociation energies of intermolecular non-covalent bonds broken down during the cyclic tests, i.e.,48-51

U hys = U xlν e f v

(2)

where Uxl is the average dissociation energy of intermolecular bonds, νe is the total number of such bonds, that is, the cross-link density of the hydrogel, and fv is the fraction of bonds broken during the tensile cycle. The cross-linking density νe of the hydrogels can be estimated from their Young’s moduli E given in Figure 5b using the equation,52,53

E = 3 νe RT

(3)

where R and T are in their usual meanings. Equation (3) assumes affine deformation of the network chains, which is a reasonable assumption for the physical gels under study.42,54 Linearity of Uhys vs εmax plots shown in Figures 7c and S7 reveals that the fraction of broken bonds fv linearly increases with the maximum strain εmax. The slope of Uhys vs εmax curve can thus be written as: 21

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

dU hys dε max

Page 22 of 37

= U xlν e

(4)

Table 1 shows the slope of Uhys vs εmax curves, Young’s modulus E, and the cross-link density νe of the hydrogels calculated using eq (3). By substituting νe and the slope of Uhys vs εmax curves into eq (4), one may estimate the average dissociation energies Uxl of the non-covalent bonds in the hydrogels, as compiled in the last column of Table 1. Uxl is 2.7±0.2 kJ.mol-1 for NC-DNA-5/4 while it slightly increases to 2.9±0.4 kJ.mol-1 after the thermal cycle, as compared to 3.6±0.3 kJ.mol-1 for NC-5 hydrogel. Considering that the strengths of chemical bonds, hydrogen bonds, and van der Waals bonds are 360, 3.2, and 0.64 kJ.mol-1, respectively,48,55 the bond strength in the hydrogels is in the range of the hydrogen bonds, and it slightly decreases after incorporation of ds-DNA into the NC-hydrogel. Table 1. Slope of Uhys vs εmax plots, Young’s modulus E, cross-link density νe, and the average dissociation energy Uxl of non-covalent bonds in NC-DNA-5/4 and NC-5 hydrogels. The numbers in parenthesis are the standard deviations. Hydrogel

dUhys / dεmax kJ·m

-3

E / kPa

νe / mol·m-3

Uxl / kJ·mol-1

NC-DNA-5/4

7.6 (0.3)

20.7 (2.1)

2.8 (0.3)

2.7 (0.2)

NC-DNA-5/4

14.0 (0.2)

36.7 (4.4)

4.9 (0.6)

2.9 (0.4)

10.0 (0.3)

21.1 (1.2)

2.8 (0.2)

3.6 (0.3)

(after cycle) NC-5

The quasi-reversible manner of dissociation of hydrogen bonds in NC-DNA hydrogels under stress suggests their self-healing abilities. Figure 8a shows photographs of two NC-DNA-5/4 gel 22

ACS Paragon Plus Environment

Page 23 of 37 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

specimens where one of them was colored for clarity. When the two gel samples were put into contact and allowed to stand at 90 °C for 30 min followed by cooling to room temperature, it was not possible to separate the two parts by stretching manually. Figure 8b shows images during uniaxial tensile tests of the healed hydrogel sample while Figure 8c shows stress-strain curves of virgin (solid curves) and healed NC-DNA-5/4 hydrogels. After healing at 90 °C, the hydrogel breaks at a stretch ratio of 1130±140 which is close to that of the virgin NC-DNA hydrogel (1350±200). Interesting to note that both the Young’s modulus E and the fracture stress σf of the hydrogel significantly increase after its healing at 90 °C. For instance, E increases from 21±2 to 30±1 kPa while σf increases from 48±6 to 81±5 kPa after healing at 90 °C, corresponding to 140170% healing efficiencies. Healing conducted at 80 °C resulted in 48±6% healing efficiency with respect to both the stretch ratio at break and the fracture stress while the modulus could completely be recovered. This suggests that the enhanced mechanical strength of NC-DNA hydrogels healed at 90 °C is due to the increase of the modulus E and fracture stress σf of DNAcontaining hydrogels as observed during the heating-cooling cycles (Figure 4). Indeed, no such improvement was observed when the healing tests were conducted using NC-5 hydrogel prepared without DNA (Figure 8c). NC-5 hydrogel healed at 90oC exhibited a healing efficiency of 60 ± 5 % with respect to the fracture stress. As shown in Figure 5b, E and σf of virgin NC-5/4 hydrogel increase from 21±2 to 37±4 kPa and from 48±6 to 82±6 kPa, respectively, by simply heating to 90 °C and then cooling back to 25 °C. Thus, as compared to the mechanical properties of the virgin hydrogel subjected to thermal cycle, the actual healing efficiencies with respect to the modulus and fracture stress are 81±10 and 99±6%, respectively.

23

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

80

σ nom / kPa

a

c

Healed at 90 °C

60

40

20

Healed at 80 °C

b 0 d 160

σ nom / kPa

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 37

120

80

40

Healed at 90 °C

0 0

400

800

1200

Elongation %

Figure 8. (a): Photographs of two NC-DNA-5/4 gel specimens where one of them is colored for clarity. (b): Images of healed NC-DNA-5/4 hydrogel during uniaxial tensile tests. (c, d): Stressstrain curves of virgin (solid curves) and healed NC-DNA-5/4 (c) and NC-5 hydrogels (d). Figure 9 shows self-healing mechanism we propose for NC-DNA hydrogels. At the cut surface of a damaged gel sample at 24 °C, semi-flexible ds-DNA fragments with a persistence length twice the diameter of Laponite nanoparticle behave as rigid segments, as shown in Figure 9a by ladder-like shapes. However, upon heating the joined cut surfaces above Tm, they dissociate and become flexible due to the much smaller persistence length of ss-DNA (Figure 9b).56 Simultaneously, the mobility of the dissociated strands at the cut surface will significantly increase because the critical overlap concentration of DNA with 2000 base pairs 74-fold increases upon denaturation and becomes 3.2 w/v%, corresponding to the critical entanglement 24

ACS Paragon Plus Environment

Page 25 of 37 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

concentration of 6 – 9.3 w/v%.27,28 Thus, the strands can move from one to another surface while cooling back to room temperature enables formation of bridges between the surfaces via base pairing between ss-DNA strands belonging to both surfaces that facilitates healing process (Figure 9c). (a)

KEY: Laponite ds-DNA ss-DNA poly(DMAA)

(b)

Heating above Tm

(c)

Cooling below Tm

Figure 9. Cartoon showing cut surfaces of NC-DNA hydrogels (a), and after pushing them into contact at above (b), and below Tm of ds-DNA (c). As a length scale, ds-DNA fragments behaving as a rigid segment are 50 nm in length, twice the diameter of Laponite nanoparticles. All the features of NC-DNA hydrogels discussed so far are related to their as-prepared states containing 88.5 – 93.5 wt% water. Figure 10a shows typical swelling kinetics of NC-DNA-5/y hydrogels with various DNA contents (y), where the relative swelling ratio mrel is plotted against the time of swelling. Immersion of the hydrogels in water results in a significant increase in their mass within 2 days and after passing a maximum degree of swelling, they start to deswell until attaining an equilibrium degree of swelling. The inset to Figure 10a shows the equilibrium mrel,eq and maximum swelling ratios mmax of the hydrogels plotted against their initial DNA content y. 25

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

The higher the DNA content of the hydrogels, the higher is both the maximum and equilibrium degrees of swelling. For instance, Figure 10b shows optical images of a NC-5/5 gel specimen at three states: as prepared (i), maximum swelling (ii), and equilibrium swelling (iii). The gel mass first 86-fold increases but then decreases to attain an equilibrium swelling ratio of 34. m rel 80

30

90

20

60

10

30

mm ax

a mrel,eq

60 0

0

0

1

2

3

4

5

DNA w/v% DNA % =

20

5 4 3 2 1 0.5 0

0

2

4

6

8

c 30 0.10 15 0.05

10 12 14 16

DNA in gel / w/v%

40

DNA release %

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 26 of 37

0

Time / days

1

2

3

4

DNA w/v%

Figure 10. (a): Relative weight swelling ratio mrel of NC-DNA-5/y hydrogels in water as a function of the swelling time. DNA contents (y) are indicated. The inset shows the equilibrium mrel,eq (filled symbols) and maximum swelling ratios mmax of the hydrogels plotted against DNA

w/v%. (b): Optical images of a NC-5/5 gel specimen just after preparation (i), after maximum (ii) and equilibrium degrees of swelling in water (iii). (c): Released amount of DNA from NC-DNA hydrogels (filled circles) and DNA concentration in swollen hydrogels (open circles) both plotted against their initial DNA content y. The data are the average of the results from UV and fluorescence measurements.

26

ACS Paragon Plus Environment

Page 27 of 37 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

This swelling profile suggests that ds-DNA in the hydrogels partially releases during the initial swelling process. Thus, NC-DNA hydrogel initially behaves as a polyelectrolyte hydrogel because of the osmotic pressure of phosphate counterions of DNA, and attains a large swelling ratio. However, as the DNA is gradually released from the hydrogel, the ionic osmotic pressure reduces so that the hydrogel progressively changes into a less ionic hydrogel with a distinctly reduced swelling ratio. Increasing equilibrium swelling ratio mrel,eq with increasing DNA content y indicates that a larger amount of DNA can be entrapped within the gel network in equilibrium

with water as the DNA concentration at the gel preparation is increased. This was indeed observed. Figure 10c shows the released amount of DNA with respect to its initial amount at the gel preparation (filled symbols) and DNA concentration in swollen NC-DNA-5/y hydrogels (open symbols) plotted against the initial DNA content y. The released amount of DNA from NCDNA-5/y hydrogels is 20±4% which is almost independent on y, while the concentration of DNA in equilibrium swollen hydrogels increases from 0.05 to 0.12 w/v% with increasing DNA content at the gel preparation. This DNA release behavior may provide applications of NC-DNA hydrogels as DNA-carriers in gene therapy methods.

CONCLUSIONS The hydrogels containing DNA in the protective environment of clay nanoparticles are excellent candidates to utilize the characteristics of DNA such as bioresponsivity, biocompatibility, biodegradability, selective binding, and molecular recognition. We presented here novel DNA/clay hydrogels of high stretchability (up to 1500%) and a tensile strength between 20 - 150 kPa prepared by in situ polymerization of DMAA in aqueous solutions of ds-DNA (2 to 8 w/v%) in the presence of Laponite nanoparticles. Fluorescence measurements show that ds-DNA 27

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 28 of 37

molecules in the gel network undergo thermal denaturation/renaturation cycles leading to further improvement in the mechanical properties of the hydrogels. It was found that clay nanoparticles act like a chemical cross-linker and promote the elastic behavior of the hydrogels while DNA contributes to their viscoelastic energy dissipation. The results of cyclic rheological and tensile tests indicate quasi-reversible manner of dissociation and reformation of intermolecular bonds in the hydrogels. The strength of intermolecular bonds in DNA/clay hydrogels calculated from the hysteresis energies is in the range of the bond strength of hydrogen bonds. The hydrogels have the ability to self-heal induced by heating the damaged gel samples above the melting temperature of ds-DNA with a healing efficiency greater than 100%. For instance, after healing at 90 °C, the Young’s modulus E and the fracture stress σf of the hydrogel increase from 21±2 to 30±1 kPa and from 48±6 to 81±5 kPa, respectively, corresponding to 140-170% healing efficiencies. The enhanced mechanical strength of the hydrogels healed at 90 °C is due to the modulus rise in hydrogels as observed during the heating-cooling cycles. Comparing the healed and virgin hydrogels, both heated to 90°C and cooled back to 25 °C, the actual healing efficiencies with respect to the modulus and fracture stress are 81±10 and 99±6%, respectively.

ASSOCIATED CONTENT Supporting Information Experimental details including synthesis, sample preparation and characterization. This material is available free of charge via the Internet at http://pubs.acs.org

AUTHOR INFORMATION Corresponding Authors 28

ACS Paragon Plus Environment

Page 29 of 37 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

*(O.O.) E-mail: [email protected] *(O.G.) E-mail: [email protected]

ACKNOWLEDGEMENT. Work was supported by Istanbul Technical University (ITU), BAP 39773. O. O. thanks Turkish Academy of Sciences (TUBA) for the partial support.

29

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 30 of 37

References (1) Xu, J.; La Bean, T. H.; Craig, S. L. DNA Structures and their Applications in Nanotechnology. in: Ciferri, A. (ed.), Supramolecular Polymers; CRC Press, Boca Raton, FL, 2004, pp 445-480. (2) Bloomfield, V. A.; Crothers, D. M.; Tinoco, I. Jr. Nucleic Acids: Structures, Properties, and Functions; University Science Books, Sausalito, 2000.

(3) Shao, Y.; Jia, H.; Cao, T.; Liu, D. Supramolecular Hydrogels Based on DNA Self-Assembly. Acc. Chem. Res. 2017, 50, 659–668

(4) Wang, D.; Hu, Y.; Liu, P.; Luo, D. Bioresponsive DNA Hydrogels: Beyond the Conventional Stimuli Responsiveness. Acc. Chem. Res. 2017, 50, 733–739 (5) Okay, O. DNA Hydrogels: New Functional Soft Materials. J. Polym. Sci. B: Polym. Phys. 2011, 49, 551-556. (6) Alemdaroglu, F. E.; Hermann, A. DNA meets Synthetic Polymers - Highly Versatile Hybrid Materials. Org. Biomol. Chem. 2007, 5, 1311-1320. (7) Murakami, Y.; Maeda, M. DNA-Responsive Hydrogels that can Shrink or Swell. Biomacromolecules 2005, 6, 2927-2929. (8) Ishizuka, N.; Hashimoto, Y.; Matsuo, Y.; Ijiro, K. Highly Expansive DNA Hydrogel Films Prepared with Photocrosslinkable Poly(vinyl alcohol), Colloids Surf. A 2006, 284-285, 440-443. (9) Lilienthal, S.; Shpilt, Z.; Wang, F.; Orbach, R.; Willner, I.

Programmed DNAzyme-

Triggered Dissolution of DNA-Based Hydrogels: Means for Controlled Release of Biocatalysts and for the Activation of Enzyme Cascades. ACS Appl. Mater. Interfaces 2015, 7, 8923–8931. 30

ACS Paragon Plus Environment

Page 31 of 37 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

(10) Kang, H.; Liu, H.; Zhang, X.; Yan, J.; Zhu, Z.; Peng, L.; Yang, H.; Kim, Y.; Tan, W. Photoresponsive DNA-Cross-linked Hydrogels for Controllable Release and Cancer Therapy. Langmuir 2011, 27, 399–408. (11) Xiang, B.; He, K.; Zhu, R.; Liu, Z.; Zeng, S.; Huang, Y.; Nie, Z.; Yao, S. Self-Assembled DNA Hydrogel Based on Enzymatically Polymerized DNA for Protein Encapsulation and Enzyme/DNAzyme Hybrid Cascade Reaction. ACS Appl. Mater. Interfaces 2016, 8, 22801– 22807. (12) Jin, J.; Xing, Y.; Xi, Y.; Liu, X.; Zhou, T.; Ma, X.; Yang, Z.; Wang, S.; Liu, D. A Triggered DNA Hydrogel Cover to Envelop and Release Single Cells. Adv. Mater. 2013, 25, 4714– 4717. (13) Wang, Y.; Shao, Y.; Ma, X.; Zhou, B.; Faulkner-Jones, A.; Shu, W.; Liu, D. Constructing Tissuelike Complex Structures using Cell-Laden DNA Hydrogel Bricks. ACS Appl. Mater. Interfaces 2017, 9, 12311–12315.

(14) Joseph, K. A.; Dave, N.; Liu, J. Electrostatically Directed Visual Fluorescence Response of DNA-Functionalized Monolithic Hydrogels for Highly Sensitive Hg2+ Detection. ACS Appl. Mater. Interfaces 2011, 3, 733–739.

(15) Dave, N.; Chan, M. Y.; Huang, P.-J. J.; Smith, B. D.; Liu, J. Regenerable DNAFunctionalized Hydrogels for Ultrasensitive, Instrument-Free Mercury(II) Detection and Removal in Water. J. Am. Chem. Soc. 2010, 132, 12668–12673. (16) Liu, D.; Jia, S.; Zhang, H.; Ma, Y.; Guan, Z.; Li, J.; Zhu, Z.; Ji, T.; Yang, C. J. Integrating Target-Responsive Hydrogel with Pressuremeter Readout Enables Simple, Sensitive, Userfriendly, Quantitative point-of-care Testing. ACS Appl. Mater. Interfaces 2017, 9, 22252– 22258. 31

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 32 of 37

(17) Baeissa, A.; Dave, N.; Smith, B. D.; Liu, J. DNA-Functionalized Monolithic Hydrogels and Gold Nanoparticles for Colorimetric DNA Detection. ACS Appl. Mater. Interfaces 2010, 2, 3594–3600. (18) Xu, Y.; Wu, Q.; Sun, Y.; Bai, H.; Shi, G. Three-Dimensional Self-Assembly of Graphene Oxide and DNA into Multifunctional Hydrogels. ACS Nano 2010, 4, 7358–7362. (19) Li, C.; Chen, P.; Shao, Y.; Zhou, X.; Wu, Y.; Yang, Z.; Li, Z.; Weil, T.; Liu, D. A Writable Polypeptide–DNA Hydrogel with Rationally Designed Multi-Modification Sites. Small 2015, 9-10, 1138–1143. (20) Li, C.; Rowland, M. J.; Shao, Y.; Cao, T.; Chen, C.; Jia, H.; Zhou, X.; Yang, Z.; Scherman, O. A.; Liu, D. Responsive Double Network Hydrogels of Interpenetrating DNA and CB[8] Host–Guest Supramolecular Systems. Adv. Mater. 2015, 27, 3298–3304. (21) Cheng, E.; Xing, Y.; Chen, P.; Yang, Y.; Sun, Y.; Zhou, D.; Xu, L.; Fan, Q.; Liu, D. A pHTriggered, Fast-Responding DNA Hydrogel. Angew. Chem. Int. Ed. 2009, 48, 7660 –7663. (22) Kahn, J. S.; Hu, Y.; Willner, I. Stimuli-Responsive DNA-Based Hydrogels: From Basic Principles to Applications. Acc. Chem. Res. 2017, 50, 680–690. (23) Lu, C-H.; Guo, W.; Hu, Y.; Qi, X-J.; Willner, I. Multitriggered Shape-Memory Acrylamide– DNA Hydrogels. J. Am. Chem. Soc. 2015, 137, 15723–15731. (24) Um, S. H.; Lee, J. B.; Park, N.; Kwon, S. Y.; Umbach, C. C.; Luo, D. Enzyme-Catalysed Assembly of DNA Hydrogel. Nat Mater. 2006, 5, 797-801. (25) Tanaka, S.; Wakabayashi, K.; Fukushima, K.; Yukami, S.; Maezawa, R.; Takeda, Y.; Tatsumi, K.; Ohya, Y.; Kuzuya, A. Intelligent, Biodegradable, and Self-Healing Hydrogels Utilizing DNA Quadruplexes. Chem. Asian J. 2017, 12, 2388 –2392.

32

ACS Paragon Plus Environment

Page 33 of 37 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

(26) Xing, Y.; Cheng, E.; Yang, Y.; Chen, P.; Zhang, T.; Sun, Y.; Yang, Z.; Liu, D. SelfAssembled DNA Hydrogels with Designable Thermal and Enzymatic Responsiveness. Adv. Mater. 2011, 23, 1117–1121

(27) Topuz, F.; Okay, O. Rheological Behavior of Responsive DNA Hydrogels. Macromolecules 2008, 41, 8847-8854. (28) Topuz, F.; Okay, O. Formation of Hydrogels by Simultaneous Denaturation and Crosslinking of DNA. Biomacromolecules 2009, 10, 2652-2661. (29) Yang, D.; Peng, S.; Hartman, M. R.; Gupton-Campolongo, T.; Rice, E. J.; Chang, A. K.; Gu, Z.; Lu, G. Q.; Luo, D. Enhanced Transcription and Translation in Clay Hydrogel and Implications for Early Life Evolution. Sci Rep. 2013, 3, 3165. (30) Cai, P.; Huang, Q.-Y.; Zhang, X.-W. Interactions of DNA with Clay Minerals and Soil Colloidal Particles and Protection Against Degradation by DNase. Environ. Sci. Technol. 2006, 40, 2971–2976. (31) Haraguchi, K.; Takehisa, T. Nanocomposite Hydrogels: A Unique Organic–Inorganic Network Structure with Extraordinary Mechanical, Optical, and Swelling/De-swelling Properties. Adv. Mater. 2002, 14, 1120-1124. (32) Haraguchi, K.; Takehisa, T.; Fan, S. Effects of Clay Content on the Properties of Nanocomposite

Hydrogels

Composed

of

Poly(N-isopropylacrylamide)

and

Clay.

Macromolecules 2002, 35, 10162-10171.

(33) Haraguchi, K.; Farnworth, R.; Ohbayashi, A.; Takehisa, T. Compositional Effects on Mechanical

Properties

of

Nanocomposite

Hydrogels

Composed

of

Poly(N,N-

dimethylacrylamide) and Clay. Macromolecules 2003, 36, 5732-5741.

33

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 34 of 37

(34) Haraguchi, K.; Li, H.-J.; Matsuda, K.; Takehisa, T.; Elliott, E. Mechanism of Forming Organic/Inorganic Network Structures During In-situ Free-radical Polymerization in PNIPA−Clay Nanocomposite Hydrogels. Macromolecules 2005, 38, 3482-3490. (35) Taki, A.; John, B.; Arakawa, S.; Okamoto, M. Structure and Rheology of Nanocomposite Hydrogels Composed of DNA and Clay, Eur. Polym. J. 2013, 49, 923-931. (36) Uzumcu, A. T.; Guney, O.; Okay, O. Nanocomposite DNA Hydrogels with Temperature Sensitivity. Polymer 2016, 100, 169-178. (37) Uemura, Y.; McNulty, J.; Macdonald, P. M. Associative Behavior and Diffusion Coefficients of Hydrophobically Modified Poly(N,Ndimethylacrylamides). Macromolecules 1995, 28, 4150−4158. (38) Relogio, P.; Martinho, J. M. G.; Farinha, J. P. S. Effect of Surfactant on the Intra- and Intermolecular Association of Hydrophobically Modified Poly(N,N-dimethylacrylamide). Macromolecules 2005, 38, 10799−10811.

(39) Mongondry, P.; Tassin, J.-F.; Nicolai, T. Revised State Diagram of Laponite Dispersions. J. Colloid Interface Sci. 2005, 283, 397-405.

(40) Mongondry, P.; Nicolai, T.; Tassin, J.-F. Influence of Pyrophosphate or Polyethylene oxide on the Aggregation and Gelation of Aqueous Laponite Dispersions. J. Colloid Interface Sci. 2004, 275, 191-196. (41) Klein, A.; Whitten, P. G.; Resch, K.; Pinter, G. Nanocomposite Hydrogels: Fracture Toughness and Energy Dissipation Mechanisms. J. Polym. Sci., Part B: Polym. Phys. 2015, 53, 1763–1773. (42) Okay, O.; Oppermann, W. Polyacrylamide - Clay Nanocomposite Hydrogels: Rheological and Light Scattering Characterization. Macromolecules 2007, 40, 3378-3387. 34

ACS Paragon Plus Environment

Page 35 of 37 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

(43) Haraguchi, K.; Uyama, K.; Tanimoto, H. Self-Healing in Nanocomposite Hydrogels. Macromol. Rapid Commun. 2011, 32, 1253–1258.

(44) Karacan, P.; Okay, O. Ethidium Bromide Binding to DNA Cryogels, React. Funct. Polym. 2013, 73, 442-450. (45) Cosa, G.; Focsaneanu, K.-S.; McLean, J. R. N.; McNamee, J. P.; Scaiano, J. C. Photophysical Properties of Fluorescent DNA-Dyes Bound to Single- and Double-Stranded DNA in Aqueous Buffered Solution. Photochem. Photobiol. 2001, 73, 585–599. (46) Ma, Y.; Zhang, G.; Pan, J. Spectroscopic Studies of DNA Interactions with Food Colorant Indigo Carmine with the Use of Ethidium Bromide as a Fluorescence Probe. J. Agric. Food Chem. 2012, 60, 10867−10875

(47) Orakdogen, N.; Erman, B.; Okay, O. Evidence of Strain Hardening in DNA Gels. Macromolecules 2010, 43, 1530-1538.

(48) Webber, R. E.; Creton, C.; Brown, H. R.; Gong, J. P. Large Strain Hysteresis and Mullins Effect of Tough Double-Network Hydrogels. Macromolecules 2007, 40, 2919-2999. (49) Lake, G. J.; Thomas, A. G. The Strength of Highly Elastic Materials. Proc. R. Soc. Lond. A 1967, 300, 108-119. (50) Okay, O. Self-Healing Hydrogels Formed via Hydrophobic Interactions. Adv. Polym. Sci. 2015, 268, 101-142. (51) Tang, J.; Chen, X.; Pei, Y.; Fang, D. Pseudoelasticity and Nonideal Mullins Effect of Nanocomposite Hydrogels. J. Appl. Mech. 2016, 83, 111010. (52) Flory, P. J. Principles of Polymer Chemistry; Cornell University Press: Ithaca, NY, 1953. (53) Treloar, L. R. G. The Physics of Rubber Elasticity; University Press: Oxford, 1975.

35

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 36 of 37

(54) Tuncaboylu, D. C.; Sahin, M.; Argun, A.; Oppermann, W.; Okay, O. Dynamics and Large Strain Behavior of Self-Healing Hydrogels with and without Surfactants. Macromolecules 2012, 45, 1991-2000. (55) Dion, M.; Rydberg, H.; Schröder, E.; Langreth, D. C.; Lundqvist, B. I. Van der Waals Density Functional for General Geometries. Phys. Rev. Lett. 2004, 92, 246401. (56) Pan, W.; Wen, H.; Niu, L.; Su, C.; Liu, C.; Zhao, J.; Mao, C.; Liang, D. Effects of Chain Flexibility on the Properties of DNA Hydrogels. Soft Matter 2016, 12, 5537-5541.

36

ACS Paragon Plus Environment

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

For Table of Contents use only

Laponite ds-DNA ss-DNA poly(DMAA)

T > Tm

T < Tm

80 Stress / kPa

Page 37 of 37

Healed

60 40 Virgin 20 0 0

500

1000

1500

Elongation %

37

ACS Paragon Plus Environment