Copper Oxide and Zinc Oxide Nanomaterials Act as Inhibitors of

Apr 7, 2015 - Bing Wu†‡, Cristina Torres-Duarte‡, Bryan J. Cole‡, and Gary N. Cherr‡§. † State Key Laboratory of Pollution Control and Re...
0 downloads 0 Views 1MB Size
Article

Subscriber access provided by SUNY DOWNSTATE

Copper Oxide and Zinc Oxide Nanomaterials Act as Inhibitors of Multidrug Resistance Transport in Sea Urchin Embryos: Their Role as Chemosensitizers Bing Wu, Cristina Torres Duarte, Bryan J. Cole, and Gary Cherr Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.5b00345 • Publication Date (Web): 07 Apr 2015 Downloaded from http://pubs.acs.org on April 12, 2015

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 36

Environmental Science & Technology

1

Copper Oxide and Zinc Oxide Nanomaterials Act as

2

Inhibitors of Multidrug Resistance Transport in Sea

3

Urchin Embryos: Their Role as Chemosensitizers

4

Bing Wu, †,‡ Cristina Torres-Duarte, ‡ Bryan J. Cole, ‡ Gary N. Cherr‡,§,

5



6

Environment, Nanjing University, Nanjing, 210023, P.R. China

7



Bodega Marine Laboratory, University of California, Davis, California, USA

8

§

Departments of Environmental Toxicology and Nutrition, University of California,

9

Davis, California, USA

State Key Laboratory of Pollution Control and Resource Reuse, School of the

10



11

Gary N. Cherr

12

Bodega Marine Laboratory

13

University of California Davis

14

PO Box 247

15

2099, Westside Road,

16

Bodega Bay, CA 94951 USA

17

Bodega Bay, CA 94923 USA

18

Phone: 001-707-875-2051

19

FAX: 001-707-875-2009

20

E-mail:[email protected]

Corresponding Author

21 22

Notes

23

The authors declare no competing financial interest.

24 1

ACS Paragon Plus Environment

Environmental Science & Technology

25

ABSTRACT

26

The ability of engineered nanomaterials (NMs) to act as inhibitors of ATP-binding

27

cassette (ABC) efflux transporters in embryos of white sea urchin (Lytechinus pictus)

28

was studied. Nano-copper oxide (nano-CuO), nano-zinc oxide (nano-ZnO), and their

29

corresponding metal ions (CuSO4 and ZnSO4) were used as target chemicals. The

30

results showed that nano-CuO, nano-ZnO, CuSO4 and ZnSO4, even at relatively low

31

concentrations (0.5ppm), significantly increased calcein-AM (CAM, an indicator of

32

ABC transporter activity) accumulation in sea urchin embryos at different stages of

33

development. Exposure to nano-CuO, a very low solubility NM, at increasing times

34

after fertilization (>30min) decreased CAM accumulation, but nano-ZnO (much more

35

soluble NM) did not, indicating that metal ions could cross the hardened fertilization

36

envelope, but not undissolved metal oxide NMs. Moreover, non-toxic levels (0.5ppm)

37

of nano-CuO and nano-ZnO significantly increased developmental toxicity of

38

vinblastine (an established ABC transporter substrate) and functioned as

39

chemosensitizers. The multidrug resistance associated protein (MRP, one of ABC

40

transporters) inhibitor MK571 significantly increased copper concentrations in

41

embryos, indicating ABC transporters are important in maintaining low intracellular

42

copper levels. We show that low concentrations of nano-CuO and nano-ZnO can

43

make embryos more susceptible to other contaminants, representing a potent

44

amplification of nanomaterial-related developmental toxicity.

45

KEYWORDS: Sea

46

Nano-ZnO, Developmental toxicity

urchin,

ABC transporter, Chemosensitizer, Nano-CuO,

47

2

ACS Paragon Plus Environment

Page 2 of 36

Page 3 of 36

Environmental Science & Technology

48

TOC Art

49

3

ACS Paragon Plus Environment

Environmental Science & Technology

50

INTRODUCTION

51

Large-scale production and application of metal oxide nanomaterials (NMs) in

52

several industries has led to environmental concern in estuarine and marine

53

environments1, 2. Nano-zinc oxide (nano-ZnO) and nano-copper oxide (nano-CuO) are

54

two common metal oxide NMs. Nano-ZnO is used as an ultraviolet light scattering

55

additive in cosmetics such as sunscreens, toothpastes and beauty products, and is

56

widely used in rubber manufacturing, production of solar cells and liquid crystal

57

displays, pigments, chemical fibers, and textiles3, 4. The most important and unique

58

application of nano-CuO is in electronics and technology (semiconductors, electronic

59

chips, heat transfer nanofluids), as nano-CuO has excellent thermophysical properties5.

60

Nano-CuO has also been used in air and liquid filtration, wood preservation, and

61

bioactive coatings, including antifouling paints

62

nano-CuO have been assessed in aquatic organisms

63

have assessed impacts of metal oxide NMs on marine embryos1, 8.

6, 7

. The toxicity of nano-ZnO and 8-16

. However, very few studies

64

Developmental toxicity caused by metal oxide NMs has received some recent

65

attention, although not in marine developing systems. For example, Zhao et al.17

66

found that nano-ZnO and Zn2+ elicited embryonic toxicity in fish by increasing

67

reactive oxidative species (ROS) and/or compromising the cellular oxidative stress

68

response. Nations et al.18 found gastrointestinal, spinal, and other abnormalities in the

69

freshwater amphibian, Xenopus laevis, occurred following nano-CuO and nano-ZnO

70

exposures. The minimum concentration to inhibit growth of tadpoles exposed to

71

nano-CuO or nano-ZnO was very high (10 ppm). Most studies on developmental

72

toxicity induced by metal oxide NMs have focused on morphological abnormalities 8.

73

In general, relatively high levels of NMs were required to observe these effects.

74

One unexamined aspect of metal oxide NMs toxicity is their potential to act as

4

ACS Paragon Plus Environment

Page 4 of 36

Page 5 of 36

Environmental Science & Technology

75

chemosensitizers, which are compounds that increase the toxicity of other chemicals

76

through their interaction with or inhibition of toxicant defense mechanisms19-22. In

77

embryos, ATP-binding cassette (ABC) efflux transporters are responsible for

78

multidrug resistance22-28 and play important roles in protection from contaminants.

79

ABC transporters are known to efflux numerous compounds that include hormones,

80

sterols, lipids, phospholipids, oligopeptides, nucleotides, chloride ions, heavy metals

81

that have been conjugated to metallothionein or glutathione, and a wide range of

82

moderately hydrophobic xenobiotics28-31. This protective role as the first line of

83

defense against xenobiotics32 is similar to the protective functions ascribed to these

84

transporters in somatic cells and consistent with their expression in the adult blood–

85

brain barrier, blood–testis barrier, and in intestinal epithelia33, 34. The inhibition of

86

ABC transporter activities can increase the accumulation of other toxic chemicals that

87

are substrates for efflux transporters, thus rendering embryos susceptible to these

88

chemicals.

89

Aquatic ecosystems, including estuarine and near shore marine environments, are

90

expected to be one of the most heavily impacted by NM pollution 1, 2. Sea urchins are

91

key species in coastal environments and are a major model system in elucidating a

92

variety of classic developmental problems. In this study, the potential of nano-CuO

93

and nano-ZnO to inhibit efflux transporters, and thus act as chemosensitizers, was

94

studied in embryos of the white sea urchin (Lytechinus pictus). This research provides

95

a new endpoint of chemosensitization via indirect NM toxicity.

96

MATERIALS AND METHODS

97 98 99

Reagents

Potassium

chloride

(KCl),

dimethyl

5

ACS Paragon Plus Environment

sulphoxide

(DMSO),

Environmental Science & Technology

Page 6 of 36

100

ethylhexadecyldimethylammonium bromide, 1,10-phenanthroline, hydrogen peroxide

101

and sodium hydroxide were purchased from Sigma-Aldrich (St. Louis, MO). ZnSO4

102

and CuSO4 were obtained from Sigma-Aldrich (St. Louis, MO). Hydrochloric acid

103

trace metal grade was purchased from Fisher Scientific (Fair Lawn, NJ). Cell dyes

104

Calcien-AM

105

mitochondrial membrane potential probe JC1 (5,5′,6,6′-tetrachloro-1,1′,3,3′

106

-tetraethylbenzimidazolylcarbocyanine

107

Technologies (Carlsbad, CA). DMSO was used as a solvent for all cell dye solutions.

108

Vinblastine and MK571 were obtained from Cayman Chemical (Ann Arbor, MI).

109

Paraformaldehyde was purchased from Electron Microscopy Sciences (Hatfield, PA).

110

Nanomaterials

(CAM),

2’,7’-Dichlorofluorescin

iodide)

diacetate

were

(DCFH)

purchased

and

from

the

Life

111

Nano-ZnO was purchased from Meliorum Technologies (Rochester, NY).

112

Nano-CuO was obtained from Sigma-Aldrich (St. Louis, MO). Nano-ZnO and

113

nano-CuO have been previously characterized by Keller et al.9 and Adeleye et al.35,

114

respectively. All chemicals solutions were freshly prepared for each analysis. Their

115

stock solutions were at a concentration of 1000 ppm prepared in ddH2O, sonicated

116

(B-2200R-1, Fisher Scientific, USA) for 30 min, then 10 ppm alginate (final

117

concentration) was added. All stocks were diluted into desired exposure

118

concentrations in filtered seawater (FSW) containing 0.2 ppm alginate (final

119

concentration)36. Six concentrations (0, 0.5, 1, 2, 5 and 10 ppm) for nano metal oxides

120

and soluble metal ions were used for all analyses. To determine the copper

121

concentration in copper oxide nanoparticle suspensions, samples were acidified to pH

122

1.7 with trace metal grade 6N HCl and analyzed with the method described below.

123

Sea urchin embryo culture

124

Adult white sea urchins (Lytechinus pictus) were kept at the University of

6

ACS Paragon Plus Environment

Page 7 of 36

Environmental Science & Technology

125

California Davis Bodega Marine Laboratory (Bodega Bay, CA) in flow-through

126

seawater tanks. Gametes were collected and fertilized as described previously8. Prior

127

to use in experiments, eggs were washed three times in 0.2 µm FSW containing 0.2

128

ppm alginate (final concentration). Sperm was stored dry at 4oC until use.

129

Fertilization success was checked under the microscope and only batches of embryos

130

exhibiting >90% successful fertilization were used for subsequent experiment. All

131

experiments were conducted at 14oC.

132

Cytotoxicity assays

133

Sea urchin embryos at 30min post-fertilization were exposed to target metals in

134

96-well plate (100 embryos per well). To analyze the mitochondrial membrane

135

potential stability after 3.5 h exposure to target metals, 0.2 µg/ml JC1 (final

136

concentration) was added to the each well and incubated for 1h. Then the green

137

(Ex:485nm, Em:535nm) and red (Ex:530nm, Em:630nm) fluorescence values were

138

measured. For analysis of ROS production after 3.75 h exposure of target metals, 1.0

139

µM DCF (final concentration) was added to each well, and incubated for 45 min. The

140

DCF fluorescence values were measured at 485nm (excitation wavelength) and

141

535nm (emission wavelengths). The fluorescence was measured using a TECAN

142

GENios microplate reader (Maennedorf, Switzerland). Each combination of target

143

chemical concentration and probe assay were internally replicated in 8 wells of each

144

plate. Each exposure plate was replicated 3X for each target chemical using a

145

different batch of embryos collected from different sea urchins.

146

Cellular efflux pump inhibition assay

147

Cellular efflux pump inhibition was measured by CAM accumulation. Embryos

148

at cleavage and blastula stages were used. For the cleavage stage, sea urchin embryos

149

(100 embryos per well) were exposed to target metals in 96-well plate. For

7

ACS Paragon Plus Environment

Environmental Science & Technology

150

comparison among different exposure concentrations, the embryos at 30min

151

post-fertilization were used. For analysis on the influence of the fertilization envelope

152

on CAM accumulation, the embryos at 5, 15, 30, 60 and 90 min post-fertilization

153

were used. After 3 h exposure to target metals, 0.5 µM CAM (final concentration) was

154

added into each well. Then the plates were incubated for 1.5 h at 14oC, and measured

155

in plate reader. The excitation wavelength and emission wavelengths for CAM were

156

485nm and 535nm, respectively. For the fluorescence imaging, the same exposure

157

approaches were applied, but 6-well plates were used. Fluorescence imaging was

158

performed using a scanning laser confocal microscope (Fluoview 500, Olympus,

159

Japan).

160

For the embryos at blastula stage, 50 embryos per well at 20 h post-fertilization

161

were added to a 96-well plate. The exposure procedures and CAM measurement were

162

performed as described above. The embryos were fixed with 1% paraformaldehyde in

163

FSW immediately before plate reader measurements were made such that blastulae

164

were in a monolayer on the bottom of the wells.

165

Vinblastine assay

166

The vinblastine (0-0.75µM dose response) assay was performed in 24-well plates

167

at a density of 100 embryos/ml. Embryos at 30min post-fertilization were exposed to

168

0.5 ppm nano-CuO, nano-ZnO and ZnSO4, and 0.2ppm CuSO4. When embryos in the

169

control group developed to the 4-cell stage, vinblastine (0-0.75µM) with or without

170

5µM MK571 (positive control) were added. When embryos in the control group

171

developed to the 8-cell stage (>90%), the embryos in all groups were fixed using 1%

172

paraformaldehyde. Then the percentage of 8-cell embryos in treated groups was

173

counted. Each combination of target chemical and vinblastine concentration was

174

internally replicated in 2 wells of each plate. Each exposure was replicated 3X for

8

ACS Paragon Plus Environment

Page 8 of 36

Page 9 of 36

Environmental Science & Technology

175

each target chemical using different batches of embryos collected from sea urchins.

176

Copper measurement in sea urchin embryos

177

Embryos (200 embryos/ml) at the blastula stage were exposed to CuSO4 and

178

nano-CuO at 1ppm, with or without 10µM MK571, in 6-well plates. After 4.5h

179

exposure, embryos were collected from the plates and washed three times with

180

Ca2+-Mg2+-free artificial seawater (10 mM EDTA, pH 5.0), and then once with FSW,

181

all at 14oC. Embryos were then homogenized in FSW using a probe sonicator. The pH

182

was adjusted to 1.7 using 6 M copper-free HCl. Samples were incubated overnight at

183

4°C, and centrifuged at 14,000 g for 10 min. The copper concentration in the

184

supernatant was measured using a modified method by Durand et al. 37. The method is

185

based on the light-emitting catalytic decomposition of hydrogen peroxide by

186

copper(II)-1,10-phenanthroline complex. Standard solutions were prepared by

187

diluting Certified Copper Standard solution (Sigma-Aldrich, St. Luis MO) in FSW

188

acidified to pH 1.7 with copper-free 6N HCl. Standard solutions and samples are

189

placed in a 96-well plate, and a freshly made solution of reagents was added. Final

190

mixture contains 7.7mM ethylhexadecyldimethylammonium bromide, 0.43 µM

191

tetraethylenepentamine, 29mM NaOH, 2.9mM 1,10-phenanthroline and 4% hydrogen

192

peroxide. Light emission was detected using a TECAN GENios microplate reader

193

(Maennedorf, Switzerland) in the luminescence mode. Concentration was determined

194

by comparison with a standard curve conducted for each plate.

195

Localization of nano-CuO in blastula stage embryos was conducted according to

196

the method of Jose et al.38. Briefly, hatched blastula embryos were incubated in

197

nano-CuO or CuSO4 (1ppm) for 4.5h, washed as described above with

198

Ca2+-Mg2+-free artificial seawater (10 mM EDTA, pH 5), and fixed in 3%

199

paraformaldehyde in FSW for 18 h at 40C.

After washing, blastula were incubated

9

ACS Paragon Plus Environment

Environmental Science & Technology

Page 10 of 36

200

in 10µM Hoechst 33342 (Sigma-Aldrich, St. Luis MO), mounted on slides and

201

compressed under coverglass, then viewed using scanning laser confocal microscopy

202

using both interference contrast optics (transmitted light) and excitation at 405nm

203

(blue diode laser) with a 60X water immersion lens on an Olympus BX61WI fixed

204

stage upright microscope.

205 206

RESULTS

207

Characterization of nano-CuO and nano-ZnO

208

Particles used in this study have been previously characterized9,

35

. Major

209

physicochemical properties are presented in Table 1. Both NMs rapidly aggregate in

210

high ionic strength media, such as seawater, reaching a stable size in 60 min or less of

211

around 400 nm for nano-ZnO and around 600 nm for nano-CuO. Sedimentation rates

212

are concentration and ionic strength dependent. When a 10 ppm solution is made at

213

high ionic strength, 90% of nano-ZnO particles remain in suspension after 6 h, while

214

60% remains in suspension for a 50 ppm solution. Nano-CuO has a higher

215

sedimentation rate, with less than 25% of nanoparticles remaining in suspension after

216

6 h for a 50 ppm solution35.

217

Nano-ZnO undergoes rapid dissolution in FSW, being almost complete within

218

10-20 h for a 1 ppm solution8, 9. On the other hand, Adeleye et al.35 reported very low

219

dissolution rates of less than 4% for a 10 ppm solution of nano-CuO after 90 days at

220

pH 7 (100 mM NaCl).

221

The dispersed copper oxide nanoparticles were analyzed to determine the copper

222

content. The copper concentration was between typically between 69% to 77% of the

223

nominal concentrations used (i.e. 10 ppm of nano-CuO is equivalent to 6.9-7.7 ppm of

224

Cu2+).

10

ACS Paragon Plus Environment

Page 11 of 36

Environmental Science & Technology

225

ROS generation in cleavage stage embryos

226

The cell dye DCFH-DA was used to assess the generation of ROS. Nano-CuO at

227

relatively low concentration (0.5, 1, and 2 ppm) caused a significant increase in DCF

228

fluorescence values (Figure 1A), indicating an increase in intracellular ROS. However,

229

higher concentrations of nano-CuO (5 and 10ppm) and CuSO4 (0.5-10ppm) did not

230

cause an increase in DCF fluorescence values, and in fact, these fluorescence values

231

decreased. For nano-ZnO and ZnSO4, we found that they have similar effects of ROS

232

generation. A significant increase in DCF fluorescence values was found at 0.5, 1, 2,

233

and 5ppm, but not at 10ppm. (Figure 1B).

234 235

NMs induce changes in mitochondrial membrane potential in cleavage stage

236

embryos

237

Mitochondrial membrane potential was determined by cell dye JC1. A decreasing

238

ratio of red/green fluorescence values from JC1 indicates a loss of mitochondrial

239

membrane potential, and can be indicative of apoptosis. Nano-CuO did not cause

240

changes in mitochondrial membrane potential (Figure 1C), but CuSO4 significantly

241

decreased the ratio of red and green fluorescence values of JC1 at 1, 2, and 5ppm. For

242

nano-ZnO, this NM caused a significant decrease in the ratio of red and green

243

fluorescence values at 1, 2, and 5ppm (Figure 1D). ZnSO4 also decreased the ratio at

244

0.5, 1, and 2ppm.

245 246

Increased Calcien-AM (CAM) accumulation in sea urchin embryos treated with

247

NMs

248

Plasma membrane ABC transporter activity was assessed by CAM dye

249

accumulation. CAM is an established indicator of ABC transporter efflux activity39, 40.

11

ACS Paragon Plus Environment

Environmental Science & Technology

250

CAM is not fluorescent and is membrane permeable, but once inside of cells, CAM is

251

cleaved by esterases to calcein, which is fluorescent, is membrane impermeable, and

252

is poorly effluxed from cells41, 42. Thus, the level of CAM accumulation can indicate

253

the relative activity of ABC transporters. Two developmental stages (cleavage and

254

blastula stages) of sea urchin embryos were utilized in this study. Both stages showed

255

two important developmental stages of sea urchin embryos. At the cleavage stage (2-8

256

cell), sea urchin embryos are surrounded by the fertilization envelope and cannot

257

swim, but at the blastula stage, embryos hatch and can swim.

258

At the cleavage stage, sea urchin embryos were exposed to nano-CuO, CuSO4,

259

nano-ZnO and ZnSO4 at 30 min post-fertilization. After a 4.5h exposure, nano-CuO,

260

CuSO4, nano-ZnO and ZnSO4 significantly increased CAM accumulation (p