Core-Shell Nanostructured Cobalt-Platinum Electrocatalysts with Enhanced Durability Lei Wang, Wenpei Gao, Zhenyu Liu, Zhenhua Zeng, Yifan Liu, Michael Giroux, Miaofang Chi, Guofeng Wang, Jeffrey Greeley, Xiaoqing Pan, and Chao Wang ACS Catal., Just Accepted Manuscript • DOI: 10.1021/acscatal.7b02501 • Publication Date (Web): 09 Nov 2017 Downloaded from http://pubs.acs.org on November 9, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Catalysis is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

Core-Shell Nanostructured Cobalt-Platinum Electrocatalysts with Enhanced Durability Lei Wang1, Wenpei Gao2, Zhenyu Liu3, Zhenhua Zeng4, Yifan Liu1, Michael Giroux1, Miaofang Chi5, Guofeng Wang3, Jeffrey Greeley4, Xiaoqing Pan2,6, Chao Wang1,* 1

Department of Chemical and Biomolecular Engineering, Johns Hopkins University, Baltimore, Maryland 21218,

USA; 2Department of Chemical Engineering and Materials Science, University of California, Irvine, CA 92697, USA; 3Department of Mechanical Engineering & Materials Science, University of Pittsburgh, Pittsburgh, PA 15261, USA; 4Davison School of Chemical Engineering, Purdue University, West Lafayette, IN 47907, USA; 5Center for Nanophase Materials Sciences, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831, USA; 6Department of Physics and Astronomy, University of California, Irvine, CA 92697, USA

ACS Paragon Plus Environment

1

ACS Catalysis

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ABSTRACT:

Page 2 of 24

Pt-bimetallic alloys involving 3d transition metals (Co, Ni, etc.) are promising elec-

trocatalysts for the oxygen reduction reaction (ORR). Despite the enhanced catalytic activity versus Pt, the electrocatalytic performance of Pt-bimetallic catalysts is however limited by the lack of long-term durability, primarily due to the leaching of the non-noble element under harsh electrochemical conditions. Our study shows that the core-shell nanostructure comprising a Pt shell and a cobalt core (denoted as Co@Pt) could overcome this limitation, demonstrating ~10 times of improvement in catalytic activity versus commercial Pt catalysts and no more than 13% of loss after 30,000 potential cycles. The evolutions of nanoscale and surface structures over the course of extensive potential cycling were followed by combining electron microscopic elemental mapping and electrochemical studies of CO stripping. Atomistic simulations and density functional theory calculations suggest that the core-shell nanostructure could protect the nonnoble cobalt from leaching under the “electrochemical annealing” conditions while maintaining the beneficial mechanisms of bimetallic systems for catalytic activity enhancement.

Keywords: cobalt, platinum, core-shell nanoparticles, electrocatalysts, oxygen reduction reaction, fuel cells

ACS Paragon Plus Environment

2

Page 3 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

INTRODUCTION A fuel cell generates electricity from the hydrogen oxidation reaction at the anode and the oxygen reduction reaction (ORR) at the cathode. With hydrogen generated from water electrolysis using renewable electricity (e.g., solar and wind power), fuel cells are promising as an alternative energy technology for stationary and mobile applications.1 The need for large amounts of platinum (Pt) as catalysts for both of the two electrochemical reactions, however, has limited the commercial viability of fuel cells.2, 3 To improve the kinetics of these reactions, especially the cathodic reduction of oxygen, and thereby reduce the usage of noble metals, a common approach is to alloy Pt with another transition metal (Co, Ni, etc.).2-12 Although significant progress has been made in improving the catalytic activity, the Pt-alloy catalysts are still challenged by the limited durability, primarily caused by leaching of the non-noble elements under the harsh electrochemical conditions relevant to fuel cell operations.13-15 Compared to homogeneous alloys, the core-shell nanostructure is potentially more advantageous for electrocatalytic applications.16-21 It could reduce the content of noble metal in the catalysts if a non-noble metal is used as the core, while a complete noble metal shell can protect the inner non-noble metal from corrosion. Such structures may also possess the beneficial mechanisms of bimetallic catalysts (e.g., strain effect8) for surface property modification and catalytic enhancement. We have recently developed the synthesis Co@Pt nanoparticles in organic solutions using seed-mediated growth and demonstrated their high catalytic activity for the ORR.22 These core-shell nanostructures are distinct from those previously reported Pt-bimetallic (e.g., Pt-Co, Ni, Cu) catalysts with Pt-skin surface produced by thermally induced surface segregation20, 23 or Pt-rich shell generated from dealloying (via electrochemical or acid treatments)6, 8. In the latter cases, the core is always an alloy phase comprising Pt and the 3d metal, and the

ACS Paragon Plus Environment

3

ACS Catalysis

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 24

amount of non-precious metal that can be preserved in such nanostructures under electrochemical environments has been found to be limited (e.g.,