Crystal Cox B (x = 1−3) Synthesized by a Ball ... - ACS Publications

Oct 2, 2017 - Key Laboratory of In-Fiber Integrated Optics, Ministry of Education and College of Science, Harbin Engineering University, Harbin. 15000...
1 downloads 3 Views 4MB Size
Subscriber access provided by LONDON METROPOLITAN UNIV

Article

Crystal CoxB (x=1, 2, 3) Synthesized by Ball-Milling Method as High-Performance Electrocatalysts for Oxygen Evolution Reaction Xinzhi Ma, Jing Wen, Shen Zhang, Haoran Yuan, Kaiyue Li, Feng Yan, Xitian Zhang, and Yujin Chen ACS Sustainable Chem. Eng., Just Accepted Manuscript • DOI: 10.1021/ acssuschemeng.7b02281 • Publication Date (Web): 02 Oct 2017 Downloaded from http://pubs.acs.org on October 3, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Sustainable Chemistry & Engineering is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Crystal CoxB (x=1, 2, 3) Synthesized by BallMilling

Method

as

High-Performance

Electrocatalysts for Oxygen Evolution Reaction Xinzhi Ma,†, ‡ Jing Wen,‡ ShenZhang,† Haoran Yuan,† Kaiyue Li,† Feng Yan,† Xitian Zhang*,‡ and Yujin Chen*,† †Key Laboratory of In-Fiber Integrated Optics, Ministry of Education and College of Science, Harbin Engineering University, Harbin 150001, China. ‡Key Laboratory for Photonic and Electronic Bandgap Materials, Ministry of Education and School of Physics and Electronic Engineering, Harbin Normal University, Harbin 150025, China.

AUTHOR INFORMATION Corresponding Authors: *E-mail: [email protected] *E-mail: [email protected] Notes The authors declare no competing financial interest.

ACS Paragon Plus Environment

1

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 29

ABSTRACT: Development of noble metal-free and active electrocatalysts is crucial for the oxygen evolution reaction (OER) in water splitting process. Herein, crystal CoxB catalysts (x=1, 2 and 3) toward OER are fabricated by a ball-milling method. Among these CoxB catalysts, Co2B exhibits the best OER activity with a current density of 10 mA cm-2 at overpotential of 287 mV in 1 M KOH solution. Such OER activity of Co2B is favorably comparable to the commercial IrO2 and most recently reported OER catalysts. Furthermore, the Co2B catalyst exhibit excellent stability with a stable current density of 50 mA cm-2 over 12 h continuous electrolysis operation. X-ray photoelectron spectroscopy and the cyclic voltammetry demonstrate that the B in CoxB make oxidation more easily, leading to their enhanced OER activities in comparison to metal Co. In addition, the Co2B electrocatalyst also exhibit high activity toward hydrogen evolution reaction and thus the catalyst can be used as bifunctional catalyst for full water splitting.

KEYWORDS: oxygen evolution reaction, electrocatalysts, CoxB, ball-milling method

ACS Paragon Plus Environment

2

Page 3 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Introduction The current rapid increased energy demand and the huge depletion of fossil fuels have promoted intense researches on the low cost and environmental friendly energy conversion and storage system with high efficiency. Photoelectrochemical or electrochemical water splitting system provides a promising route to overcome the excessive reliance on fossil fuels.1-3 However, a bottleneck for water splitting involved in oxygen evolution reaction (OER) is a kinetically sluggish process, which proceeds through a complex four-electron redox process and generally requires a high overpotential.4 IrO2 and RuO2 have been considered as the most active OER electrocatalys. However, their low abundance and high cost hamper their practical application for large-scale water splitting.5, 6 Thus, extensive efforts have been undertaken to exploit low-cost OER catalysts with high efficiency. Among OER catalysts, cobalt-based materials have gained considerable attentions due to earth-abundant and moderate activities.7-21 Cobalt oxides exhibited good OER performances over a broad range of PH values,7-11 however, their instinct poor conductivities result in high overpotentials towards OER.22, 23 To overcome the issue more attentions were focused on cobalt chalcogenides, phosphates and nitrides with higher conductivities than that of cobalt oxides. For example, Xie et al. reported that Co4N nanowires possessed high OER activity with a current density of 10 mA cm–2 at an overpotential of 257 mV, which is due to their metallic characters originating from the N atom incorporation.12 Ultrathin CoSe2 nanosheets showed outstanding catalytic activity toward OER owing to enriched cobalt vacancies and enhanced conductivity of the nanosheets in comparison to bulk CoSe2.15, 16 Co/Co9S8 core-shell structures with S and N codoping exhibited excellent OER activity with a current density of 10 mA cm–2 at an overpotential of 290 mV (0.1M KOH). The excellent OER performance was attributed to the synergistic effect

ACS Paragon Plus Environment

3

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 29

between Co and Co9S8 as well as good electrical conductivity of the core-shell structures.19 The covalent coupling and tuned electronic properties due to heteroatom doping were also found in other cobalt sulfide catalysts. 24-26 Recently, CoxP nanomaterials have also reported to catalyze OER efficiently, and the reason for their excellent OER activities was relative to the high conductivities of those cobalt phosphides and large electronegativity of phosphorus.20, 21, 27-29 In terms of the above reports, it can be concluded that the types of non-metals in the cobalt compounds have an important effect on the OER catalytic activities of Co-based electrocatalysts. 30-33

. However, the electrochemical activities of cobalt borides have been studied scarcely to

date. 34-39 Furthermore, the effect of the atomic ratio of metal Co to non-metal in the cobalt compounds on the OER activity has not been identified. One major reason is in that it is difficult to fabricate metal borides through common methods such as solvothermal/hydrothermal method, chemical vapor deposition, and electrochemical deposition, etc. Herein we develop a ball-milling method to fabricate a series of cobalt borides (CoxB, x = 1, 2, 3) and their OER activities are investigated. Among these cobalt borides, Co2B can drive a current density of 10 mA cm–2 at an overpotential of 287 mV in 1.0 M KOH solution, superior to CoB (340 mV) and Co3B (312 mV). Furthermore, compared to most of other OER catalysts reported previously, Co2B also exhibits favorably comparable OER catalytic activity. In addition, Co2B in alkaline media has a good stability as OER catalyst, showing a very stable current density at 50 mA cm–2 over 12 hours continuous electrolysis operation. Furthermore, the effect of B in the CoxB catalysts and the reason for the best OER activity of Co2B are also discussed in terms of X-ray photoelectron spectroscopy and the cyclic voltammetry measurements.

ACS Paragon Plus Environment

4

Page 5 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Figure 1. XRD patterns of a) CoB, Co2B, Co3B and pure cobalt. Crystal structure models of b) CoB, c) Co2B and d) Co3B. Low-magnification SEM images of e) CoB, f) Co2B and g) Co3B. RESULTS AND DISCUSSION Structural Characterization. The morphologies and the structures of the CoxB catalysts were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and the transition electron microscopy (TEM). Figure 1a shows the XRD patterns of metal cobalt precursor, CoB, Co2B and Co3B. The diffraction peaks of metal cobalt precursor at 2θ 44.2 and 51.5o can be assigned to (111) and (200) crystal planes of cubic Co. After ball-milling with B powder under different conditions, the CoxB catalysts with different crystal structures can be obtained. As the mole ratio of Co and B (RCo/B) was 1: 1 and the rotational speed was set to be 1000 rpm, orthorhombic CoB (JCPDS no. 03-0959) with a unit cell structure shown in Figure 1b could be obtained. When the rotational speed decreased to 900 rpm and RCo/B was kept unchanged, tetragonal Co2B (JCPDS no. 25-0241), with a unit cell structure shown in Figure 1c, would be fabricated. As RCo/B was changed to 2: 1 and the rotational speed was set to be 1000 rpm, orthorhombic Co3B (JCPDS no. 12-0443) with a unit cell structure shown in Figure 1d

ACS Paragon Plus Environment

5

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 29

could be formed. Furthermore, the diffraction peaks from impurities are not detected, suggesting high crystal purities of these CoxB catalysts. SEM images (Figure 1e-g) show that the asprepared CoxB catalysts exhibit particle-like shapes with sizes ranging from several hundreds of nanometers, confirmed by low-magnification TEM images (insets in Figure 2a-c).40

Figure 2. HRTEM images of a) CoB, b) Co2B and c) Co3B. The insets in a), b) and c) show the coresponding low-magnification TEM images. Coresponding EDS elemental mapping images of d) CoB, e) Co2B and f) Co3B.

ACS Paragon Plus Environment

6

Page 7 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

HRTEM images taken from the regions highlighted by the red circles in the low-magnification TEM images display clear lattice fringes, as shown in Figure 2a-c, revealing crystal natures of all the CoxB catalysts. The detailed measurements for the adjacent lattice spacings in these HRTEM images confirm the crystal structures of these CoxB catalysts. For example, the labeled lattice spacings in the HRTEM image of CoB (Figure 2a) are 0.238 and 0.214 nm, corresponding to (101) and (120) planes of orthorhombic CoB, respectively; the labeled lattice spacings in the HRTEM image of Co2B (Figure 2b) are 0.210 and 0.251 nm, which can be assigned to (002) and (200) crystal planes of tetragonal Co2B, respectively; the labeled lattice spacings in the HRTEM image of Co3B (Figure 2c) are 0.236 and 0.199 nm, which can be assigned to the (021) and (103) planes crystal planes of orthorhombic Co3B, respectively. In order to determine the elemental distribution in these CoxB catalysts, the energy dispersive X-ray spectrometry (EDX) elemental mapping images were taken. As shown in Figure 2d-f, the Co and B distribute uniformly across the particles, further confirming successful preparation of CoxB catalysts by the facile ballmilling method. X-ray photoelectron spectroscopy (XPS) was utilized to analyze the chemical surface states and compositions of these CoxB catalysts. The survey XPS spectrum of CoxB catalysts (Figure S1, Supporting Information) indicates that the surfaces of our CoxB catalysts contain B, Co and O elements, in which the existence of the O elements is due to air exposition of the catalysts. According to the XPS spectra, the contents of B and Co can be estimated (the inset in Figure S1). According to the B and Co contents the atomic ratios of Co: B in CoB, Co2B and Co3B calculated from the XPS data about 0.99: 1, 2: 1.25 and 3.00:1. As shown in Figure 3a, the main binding energies of Co 2p 3/2 and Co 2p 1/2 core peaks are at 777.9 and 793.2 eV for CoB, 778.1 and 793.4 eV for Co2B and 777.8 and 792.8 eV for Co3B are assigned to Co species in

ACS Paragon Plus Environment

7

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 29

cobalt borides. 41 The difference of Co species in the binding energies is due to different electronic environments of Co in these CoxB catalysts. Besides, the Co 2p 3/2 and Co 2p 1/2 peaks at around 780.5 and 796.4 eV for all cobalt borates can be ascribed to the Co2+ oxidation state (CoO or Co(OH)2) due to air exposure.42, 43 The corresponding B 1s spectrums, shown in Figure 3b, are all deconvoluted into two distinct peaks. The peaks at 188.4, 188.2 and 188 eV are assigned to the low-valence B in CoB, Co2B and Co3B, respectively, while the peaks at around 191.6 eV correspond to high valence state of B such as boron-oxo species.32

Figure 3. XPS spectra of CoxB. a) Co 2p core level spectras of CoB, Co2B and Co3B, and b) B 1s core level spectra of CoB, Co2B and Co3B. OER Activities of CoxB Catalysts. The results above suggest that homogeneous signal crystal cobalt borates were successfully fabricated by the ball-milling method. To assess the

ACS Paragon Plus Environment

8

Page 9 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

OER catalytic activity, the electrochemical OER activities of CoxB catalysts, commercial cobalt and IrO2 powers were measured using three-electrode configuration in 1.0 M KOH at a scan rate of 2 mV s-1. The OER activity of the Co3O4, obtained through heating the commercial cobalt powder at 500oC for 5 h under air atmosphere, was also evaluated. The crystal Co3O4 catalyst was confirmed by the XRD measurement (Figure S2a). SEM images indicate that the Co3O4 (Figure S2b) surfaces become rough in compared to the commercial cobalt powers (Figure S2c). These catalysts were loaded on the carbon fiber papers with same loading mass of 2.56 mg. A carbon rod and a Ag/AgCl (KCl saturated) were used as counter and reference electrodes, respectively. The Ohmic potential drop (iR) losses caused by electrolyte resistance were compensated for the measurements. As shown in Figure 4a and Figure S3, typical LSV curves indicate that these CoxB catalysts exhibit higher OER activity than the pure cobalt and Co3O4. For example, to drive a current density of 10 mA cm-2, metal cobalt and Co3O4 require overpotentials of 373 and 377 mV, whereas CoB, Co2B and Co3B only need 340, 287 and 312 mV, respectively; to drive a current density of 100 mA cm-2, metal cobalt and Co3O4 require overpotentials of 507 and 493 mV, whereas CoB, Co2B and Co3B only need 464, 389 and 428 mV, respectively. Furthermore, it can be found that Co2B shows the best OER activity in the tested potential range among these CoxB catalysts. Remarkably, the OER activity of Co2B is superior to that of IrO2 at the overpotential larger than 289 mV (Figure 4a). For example, to deliver current density of 100 mA cm-2, IrO2 requires overpotential of 400 mV, while Co2B needs 389 mV. Even in 0.1 M KOH solution, the Co2B can drive 10 mA cm-2 at 292 mV overpotential (Figure S4). The OER activity of Co2B in both 1 M KOH and 0.1 M KOH solutions show favorably comparable to the-state-of-the-art OER catalysts recently reported such as CoSe/Ti, CoP films, CoP3 nanoneedle arrays and other borate-based catalysts measured in 0.1

ACS Paragon Plus Environment

9

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 29

M potassium borate (KBi) solution (Table S1). Additionally, the electrochemical OER properties of those catalysts were also measured in 0.1 M KOH solutions using a rotating disk electrode (RDE) made of glassy carbon, Pt foil and AgCl/Ag/KCl (3 M) as working electrode, counter electrode and reference electrode, respectively. The scan rate was set to 10 mV s-1 and a rotation rate was 1600 rpm. The loading weight for all the catalysts is about 0.2 mg cm-2. LSV curves show that the Co2B exhibit the best OER activity among these catalysts (Figure S5). To drive a current density of 10 mA cm-2 the Co2B only needs 371 mV overpotential, lower than that of IrO2 (378 mV), CoB (405 mV), Co3B (378 mV) and Co (466 mV). Compared to the reported catalysts previously, the Co2B also exhibits favorably comparable or superior OER activity under the similar measured conditions (Table S2).

Figure 4 a) Polarization curves and b) Tafel plots of Co and CoxB elctrodes. The OER kinetics of these catalysts were evaluated by the Tafel plots according to the Tafel equation, η = a + b log|j|, where b is the Tafel slope. As shown in Figure 4b, the Tafel slope of Co2B is 50.7 mV dec-1, lower than that of Co (56 mV dec-1), CoB (63 mV dec-1) and Co3B (53 mV dec-1). The Tafel slope of Co2B is lower than that of IrO2 (51.5 mV dec-1) and those of the-

ACS Paragon Plus Environment

10

Page 11 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

state-of-the-art OER catalysts recently reported (Table S1), suggesting more favorable OER kinetics of Co2B. Thus, Co2B has very promising application in large-scale water splitting. Those slopes near 60 mV dec-1 suggest that a chemical step subsequent to the first electron transfer step is the rate-determining step for these CoxB catalysts.44 The Reasons for the Difference of CoxB Catalysts in the OER Activities and the Stability of Co2B towards OER. To further study the intrinsic catalytic activity of these CoxB catalysts, turnover frequency (TOF) reflecting all the active sites involved in the electrochemical reaction was determined by previously reported method. 45-47 The number of active sites (n) was first determined by the cyclic voltammetry cycling in pH = 7 phosphate buffer with a scan rate of 50 mV s-1. The voltammetric charges (Q) values were determined by deducting their corresponding blank values (Figure S6), and about 0.0309, 0.0444, 0.0343, 0.0430 and 0.1259 C for Co, CoB, Co2B, Co3B and IrO2, respectively. Figure 5a shows the TOF data of the Co-based catalysts. It can be found that the Co2B catalyst has the largest TOF values at all tested potential range among the Co-based catalysts and IrO2. Typically, for the given TOF = 0.5 s-1 the cobalt, CoB, Co3B and IrO2 catalysts require overpotentials of 422, 413, 370 and 375 mV, respectively, significantly higher than Co2B catalyst (328 mV). Thus, the trend in intrinsic catalytic activity of these Co-based catalysts is identified as Co2B > Co3B > CoB, consistent with the result determined by LSV curves. To understand the difference of these CoxB catalysts in the OER activities, the effective active areas of catalysts were estimated by measuring the electrochemical double-layer capacitances (Cdl) using a simple CV method.48-50 Figure S7 shows the CV curves of these CoxB catalysts at different scan rates. As shown in Figure 5b, the Cdl is 1.17, 3.7 and 1.52 mF cm-2 for CoB, Co2B, Co3B, respectively. The trend of CoxB catalysts in Cdl value is consistent with their trend in OER activity. Therefore, high OER activity of Co2B is attributed to

ACS Paragon Plus Environment

11

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 29

its high effective active area. The transfer resistance (Rct) has an important effect on the catalytic activity of the catalyst. Thus, the electrochemical impendence spectroscopy (EIS) was measured to Rct for these CoxB catalysts. Figure 5c shows the Nyquist plots of these catalysts at 356 mV overpotential. According to the equivalent circuits (the inset in Figure 5c), Rct is 1.09 Ω cm-2 for Co2B, smaller than Co (1.52 Ω cm-2), CoB (1.44 Ω cm-2) and Co3B (1.16 Ω cm-2). The small Rct facilitates charge transport during OER process, and thus improves the OER activity of Co2B.

Figure 5 a) The TOF data, b) the differences in current density (∆J = Ja-Jc) at potential range of 0.86-0.96 V vs. RHE plotted against scan rate fitted to a linear regression allows for the estimation of Cdl for CoB, Co2B and Co3B, respectively, and c) Nyquist plots at 1.586 V vs. RHE. The inset in c) showing the corresponding equivalent circuit. d) Comparisons of the 10th and the 1000th CV curves for Co2B and IrO2 catalysts with the scan rate at 50 mVs-1 and the inset

ACS Paragon Plus Environment

12

Page 13 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

showing the time-dependent current density curves for Co2B and IrO2 catalysts at an overpotential of 345 mV. Besides the catalytic activity, the stability of the catalysts is also an important criterion for their practical application. The stability of Co2B and IrO2 were evaluated by CV sweeping in N2saturated 1.0 M KOH solution at a high scan rate of 50 mV s−1. A negligible difference in the CV curve profiles before and after 1000 cycles (Figure 5d) was observed for Co2B, in contrast, a macroscopic larger potential shift occurred for IrO2 electrode. The long-term durability of Co2B toward OER was further assessed by potentiostatic measurements at a given overpotential of 345 mV. As shown in the inset in Figure 5d, the initial current density was around 50 mA cm−2, and there was negligible decrease in the current density over 12 h electrolysis for Co2B, however, a 24.4% current density loss was happened on the IrO2 electrode. Thus, the Co2B catalyst not only exhibit high activity toward OER, but also excellent long-term durability toward OER.

Figure 6. HRTEM images of a) CoB, b) Co2B and c) Co3B after OER process at the current density of 50 mA cm-2 for 12 h. The insets in a), b) and c) show the coresponding lowmagnification TEM images. The Mechanism of CoxB Catalysts towards OER. To further analyze the OER mechanism and study the structural changes of the CoxB catalysts, XRD and SEM measurements for the

ACS Paragon Plus Environment

13

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 29

CoB, Co2B and Co3B catalysts after OER process for 12 h at the current density of 50 mA cm-2 were carried out. XRD patterns (Figure S8) show that there are almost no obvious changes in the crystal phases of these CoxB catalysts after the long-term OER operation, while the diffraction peaks at 2θ 42.4, 44.5 and 54.5o in all CoxB patterns come from the carbon paper substrates (JCPDS no. 08-0415). However, SEM images (Figure S9) indicate that thin films with nanosheet-like shapes are formed on the surfaces of these catalysts, which further confirmed by low-magnification TEM images (the insets in Figure 5).41, 51, 52 HRTEM images (Figure 6) show the outmost nanosheets are polycrystalline and enriched in defects. In Figure 6a, the labeled lattice distances are 0.309, 0.261 and 0.176 nm, corresponding to (120), (130) and (150) planes of CoOOH, respectively; in Figure 6b, the labeled lattice distances are 0.31, 0.201 and 0.223 nm, corresponding to (120), (140) and (200) planes of CoOOH, respectively; in Figure 6c, the labeled lattice distances are 0.229, 0.224 and 0.258 nm, corresponding to (111), (200) and (130) crystal planes of CoOOH, respectively. Based on the HRTEM analyses, the outmost nanosheets of the CoxB catalysts after OER processes are mainly composed of CoOOH species. Notably, the outmost nanosheets are preferentially contacted with the electrolyte, and thus they are real active sites for OER. In order to further determine the chemical composition of the nanosheets, XPS analyses for these CoxB catalysts after the long-term OER operation were carried out. As shown in Figure 7a, all the fitted XPS spectra show that the CoxB surfaces are composed of Co3O4 and CoOOH, which dominate the catalyst surfaces.43 On the other hand, B in all the CoxB catalysts is oxidized, evidenced by the enlarged peaks of boron-oxo species and the disappearance of the boron species (Figure S10). Thus, real active sites of these CoxB catalysts are CoOOH species, consistent with previous reports.32 Based on the discussion above, we can conclude that the following reactions occur during oxygen evolution process of these CoxB catalysts:53, 12

ACS Paragon Plus Environment

14

Page 15 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Co + 2OH− → Co(OH)2 + 2e-

(1)

3Co(OH)2 + 2OH− → Co3O4 + 4H2O + 2e-

(2)

Co3O4 + H2O + OH− → 3CoOOH + e-

(3)

CoOOH + OH− → CoO2 + H2O + e-

(4)

CoO2 → Co* + O2

(5)

Summary: 4OH− → 2H2O + O2 +4e-

(6)

Figure 7. a) XPS spectra of Co 2p core level for CoxB electrodes after OER process at the current density of 50 mA cm-2 for 12 h, and b) CV curves of CoxB and cobalt electrodes measured in N2-saturated 1.0 M KOH solution at the scan rate of 2 mV s-1. In short, CoO or Co(OH)2 on the catalyst surfaces undergoes oxidation and then Co3O4 and/or CoOOH appear gradually depending on the electrode potential in basic solutions.54, 55 During the reaction, Co3O4 might favor the oxidation from Co2+ to Co3+ by the typical cationic occupancies

ACS Paragon Plus Environment

15

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 29

of Co2+ and Co3+ on the tetrahedral and octahedral site, and this facilitate the further oxidation to CoOOH and CoO2,56 CoO2 was more efficient for the OER and constructed by the oxidization of CoOOH.57 In addition, the effect of B on the OER activities of the CoxB catalysts is studied by the CV measurements at a scanning rate of 2 mV s-1. As shown in Figure 7b, there is an oxidation peak at about 1.45 V for metal Co before oxygen evolution. However, upon B introduction, the oxidation peaks positions for the CoxB catalysts shift toward low potential region, suggesting that the oxidation of Co in the CoxB catalysts become more easily than metal Co. As a result, the CoxB catalysts show lower onset potentials (corresponding current density: 1 mA cm−2) toward OER in comparison to metal Co. For example, the onset potentials for CoB, Co2B, and Co3B are 1.51, 1.46 and 1.49 V, respectively, 30, 80, and 50 mV lower than that of metal Co (1.54 V). Thus, B elements in CoxB catalysts have positive effects on the OER activities.

Figure 8. a) Polarization curve of Co2B on carbon paper for HER in 1.0 KOH solution at a scan rate of 2 mV s−1 and b) long-term stability of the alkaline water electrolyzer assembled with Co2B powder as bifunctional catalyst.

ACS Paragon Plus Environment

16

Page 17 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

In addition, the catalytic activity of the hydrogen evolution reaction (HER) of Co2B was assessed. The Co2B powder mixed with 10wt% carbon nanotubes was loading on carbon fiber paper with a loading mass of about 2.56 mg, and the HER activity of the Co2B was examined in in 1.0 M KOH solution with a scan rate of 2 mV/s. Figure 8a shows the polarization curve of the Co2B electrode. The current density can be achieved 10 mA cm-2 at an overpotential of -109 mV. Considering the high OER activity of the Co2B catalyst, we assembled an alkaline electrolyer with Co2B as bifunctional catalysts. Figure S11 shows the polarization curve of the Co2B║Co2B couple. The Co2B║Co2B electrolyzer can drive a current density of -10 mA cm−2 at a cell voltage of 1.656 V, lower than those of bifunctional catalysts such as NiFe LDH/Ni foam║NiFe LDH/Ni foam (1.70 V)58 and commercial electrolyzers (above 1.8 V).59 Furthermore, The Co2B║Co2B couple for full water splitting had a good stability. As shown in Figure 8b, the voltage for driving a current density of 10 mA cm-2 keeps no obvious change for 12 h water splitting. Thus, the Co2B as bifunctional catalyst has potential application in the full water splitting. CONCLUSION In summary, crystal CoB, Co2B and Co3B catalysts were successful synthesized by a ballmilling method. All the products showed OER performance and were benefited from the forming of Co3O4 and CoOOH during reaction, also from the good conductivities of alloy CoxB cores. The most optimized catalyst of Co2B achieved a current density of 10 mA cm-2 at overpotential of 287 mV on a carbon paper electrode and a stability over 12 h continuous electrolysis operation at current density of 50 mA cm-2, which was facilitated by a suitable B alloying. In addition, Co2B also exhibited a good HER performance with a current density of -10 mA cm-2 at -109 mV The ingenious design and industrialized strategy would open up new approaches to develop high performance, inexpensive electrocatalysts for large-scale water-splitting.

ACS Paragon Plus Environment

17

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 29

METHODS Chemicals. Cobalt (purity, >99.99%; diameter, ~0.5 µm) and boron power (purity, >99.9%) were purchased from Aladdin Chemical Co., Ltd. It is worth noting that the potassium hydroxide aqueous solution was further purified as the electrolyte. Experimental Sections. All materials were purchased without further treatment. The synthesis of high performance materials was mainly through a ball-milled method. The mixing mole ratio of Co and B (RCo/B) is 1:1 for both CoB and Co2B, and 2: 1 for Co3B. All the samples were ball-milled using a planetary ball mill (Fritsch Pulverisette 4) with the ball-to-power weight ratio of 20:1. Air in the grinding bowls was removed by an Ar (99.99%) inflation-deflation process and the pressure of bowls was vacuumed to 95 KPa. Rotational speeds for CoB, Co2B and Co3B were kept at 1000, 900 and 1000 rpm, respectively. The reaction time was set to be 10 hours for all samples. Structure Characterizations. XRD data were performed on a Rigaku D/max-2600/PC with Cu Kα radiation (λ=1.5418Å).The morphology and size of samples were characterized by scanning electron microscope (Hitachi SU70) and an FEI Tecnai-F20 transmission electron microscope equipped with a Gatan imaging filter (GIF). XPS analyses were carried out by using a spectrometer with Mg Kα radiation (PHI 5700 ESCA System). The binding energy was calibrated with the C 1s position of contaminant carbon in the vacuum chamber of the XPS instrument (284.6 eV). Electrochemical Measurements. Electrochemical measurements of individual electrodes were conducted in a VMP3 electrochemical workstation (Bio Logic, France) with a standard three-electrode electrochemical system using CoxB catalysts on carbon paper as the working

ACS Paragon Plus Environment

18

Page 19 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

electrode, a graphite rod and an Ag/AgCl electrode were used as the counter and the reference electrodes, respectively. Carbon paper electrode: The preparation of the working electrode was described as below: the catalysts were dispersed in N-methyl-2-pyrrolidone solvent containing 7.5 wt % PVDF under sonication, in which the weight ratio (Wcatalyst / WPVDF) is 8/1, without conductive agents employ. Then the slurry was coated onto a piece of carbon paper, on which loading density of the catalyst about 2.56 mg cm-2. The as-prepared catalyst film was performed a vacuum drying at 90 ℃. Electrochemical measurements of the catalysts were measured in 1 M KOH solution after purging the electrolyte with N2 gas for 30 min. For each catalyst, LSVs were first recorded from 0 to 0.8 V vs Ag/AgCl at a scan rate of 2 mV s-1. The activation for catalysts were carried out under a potential range from 0 V to that corresponding to 100 mA cm-2 several cycles until the curves unchanged. Then, the activity of the catalysts toward the OER was evaluated by recording a linear scan voltammogram from 0 to 0.75 V vs Ag/AgCl at a scan rate of 2 mV s-1. Polarization curves were obtained using linear sweep voltammetry (LSV). The long-term stability test was carried out using chronopotentiometric measurements. All potentials measured were calibrated to RHE using the following equation: E(RHE) =E(Ag/AgCl) + 0.21 V + 0.059 × PH. All current densities presented are corrected against Ohmic potential drop. The TOF calculation. The number of active sites (n) was first examined employing cyclic voltammograms with phosphate buffer (pH = 7) at a scan rate of 50 mV s-1. Then the number of the voltammetric charges (Q) could be determined after deduction of the blank value. n (mol) could be determined with the following equation n (mol) = Q/4F, where F is Faraday constant. TOF (s-1) could be

ACS Paragon Plus Environment

19

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 29

calculated with the following equation TOF (s-1) = I/4n A F, where I (A) was the current of the polarization curve obtained by LSV measurements, and A is the geometric area of the electrodes. ASSOCIATED CONTENT Supporting Information: Figure S1–Figure S10 and Table S1-2. This material is available free of charge via the Internet at http://pubs.acs.org ACKNOWLEDGMENTS This work is supported by the National Natural Science Foundation of China (Grant No. 51572051), the Natural Science Foundation of Heilongjiang Province (E2016023), the Fundamental Research Funds for the Central Universities (GK2110260179 and GK2110260188), the 111 project (B13015) of Ministry Education of China to the Harbin Engineering University, the PhD Student Research and Innovation Fund of the Fundamental Research Funds (HEUGIP201714) for the Central Universities and also the Open Project Program (PEBM201508) of Key Laboratory for Photonic and Electric Bandgap Materials, Ministry of Education, Harbin Normal University, China. REFERENCES

(1) Bard, A. J.; Fox, M. A. Artificial Photosynthesis-Solar Splitting of Water to Hydrogen and Oxygen. Acc. Chem. Res. 1995, 28, 141-145. (2) Walter, M. G.; Warren, E. L.; McKone, J. R.; Boettcher, S. W.; Mi, Q.; Santori, E. A.; Lewis, N. S. Solar Water Splitting Cells. Chem. Rev. 2010, 110, 6446-6473. (3) Yang, J. H.; Cooper, J. K.; Toma, F. M.; Walczak, K. A.; Favaro, M.; Beeman, J. W.; Hess, L. H.; Wang, C.; Zhu, C. H.; Gul, S.; Yano, J. K.; Kisielowski, C.; Schwartzberg, A.; Sharp, I. D. A

ACS Paragon Plus Environment

20

Page 21 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Multifunctional Biphasic Water Splitting Catalyst Tailored for Intergration with High Performance Semiconductor Photoanodes. Nat. Mater. 2017, 16, 335-341. (4) Zhao, Y.; Nakamura, R.; Kamiya, K.; S. Nakanishi, S.; Hashimoto, K. Nitrogen-Doped Carbon Nanomaterials as Non-Metal Electrocatalysts for Water Oxidation. Nat. Commun. 2013, 4, 2390. (5) Gao, M. R.; Xu, Y. F.; Jiang, J.; Zheng, Y. R.; Yu, S. H. Water Oxidation Electrocatalyzed by an Efficient Mn3O4/CoSe2 Nanocomposite. J. Am. Chem. Soc. 2012, 134, 2930-2933. (6) Matsumoto, Y.; Sato, E. Electrocatalytic Properties of Transition Metal Oxides for Oxygen Evolution Reaction. Mater. Chem. Phys. 1986, 14, 397-426. (7) Bergmann, A.; Martinez-Moreno, E.; Teschner, D.; Chernev, P.; Gliech, M.; de Araujo, JF.; Reier, T.; Dau, H.; Strasser, P. Reversible Amorphization and The Catalytically Active State of Crystalline Co3O4 During Oxygen Evolution. Nat. Commun. 2015, 6, 8625. (8) Zhang, M.; de Respinis, M.; Frei, H. Time-Resolved Boservations of Water Oxidation InterMediates On a Cobalt Oxide Nanoparticle Catalyst. Nat. Chem. 2014, 6, 362-367. (9) Risch, M.; Ringleb, F.; Kohlhoff, M.; Bogdanoff, P.; Chernev, P.; Zaharieva, I.; Dau, H. Water Oxidation by Amorphous Cobalt-Based Oxides: In Situ Tracking of Redox Transitions and Mode of Catalysis. Energy Environ. Sci. 2015, 8, 661-674. (10) Friebel, D.; Bajdich, M.; Yeo, B. S.; Louie, M.W.; Miller, D. J.; Casalongue, H. S.; Mbuga, F.; Weng, T. C.; Nordlund, D.; Sokaras, D.; Alonso-Mori, R.; Bell, A. T.; Nilsson, A. On The Chemical State of Co Oxide Electrocatalysts During Alkaline Water Splitting. Phys. Chem. Chem. Phys. 2013, 15, 17460-17467.

ACS Paragon Plus Environment

21

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 29

(11 ) Deng, X. H.; Tüysüz, H. Cobalt-Oxide-Based Materials as Water Oxidation Catalyst: Recent Progress and Challenges. ACS Catal. 2014, 4, 3701-3714. (12) Chen, P. Z.; Xu, K.; Fang, Z. W.; Tong, Y.; Wu, J. C.; Lu, X. L.; Peng, X.; Ding, H.; Wu, C. Z.; Xie, Y. Metallic Co4N Porous Nanowire Arrays Activated by Surface Oxidation as Electrocatalysts for the Oxygen Evolution Reaction. Angew. Chem. Int. Ed. 2015, 54, 1471014714. (13) Liu, T. T.; Liu, Q.; Asiri, AM.; Luo, Y. L.; Sun, X. P. An Amorphous CoSe Film Behaves as An Active and Stable Full Water-Splitting Electrocatalyst Under Strongly Alkaline Conditions. Chem. Commun. 2015, 51, 16683-16686. (14) Liao, M.; Zeng, G. F.; Luo, T. T.; Jin, Z-Y.; Wang, Y. J.; Kou, X. M.; Xiao, D. ThreeDimensional Coral-Like Cobalt Selenide as An Advanced Electrocatalyst for Highly Efficient Oxygen Evolution Reaction. Electrochim. Acta 2016, 194, 59-66. (15) Xu, X. J.; Du, P. Y.; Chen, Z. K.; Huang, M. H. An Electrodeposited Cobalt–SelenideBased Film as An Efficient Bifunctional Electrocatalyst for Full Water Splitting. J. Mater. Chem. A 2016, 4, 10933-10939. (16) Zhou, X. Q.; Wilfong, B.; Vivanco, H.; Paglione, J.; Brown, C. M.; Rodriguez, E. E. Metastable Layered Cobalt Chalcogenides from Topochemical Deintercalation. J. Am. Chem. Soc. 2016, 138, 16432-16442. (17) Liu, Y. W.; Cheng, H. C.; Lyu, M. J.; Fan, S. J. Liu, Q. H.; Zhang, W. S.; Zhi, Y. D.; Wang, C. M.; Xiao, C.; Wei, S. Q.; Ye, B. J.; Xie, Y. Low Overpotential in Vacancy-Rich Ultrathin CoSe2 Nanosheets for Water Oxidation. J. Am. Chem. Soc. 2014, 136, 15670-15675.

ACS Paragon Plus Environment

22

Page 23 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(18) Zheng, Y. R.; Gao, M. R.; Gao, Q.; Li, H. H.; Xu, J.; Wu, Z. Y.; Yu, S .H. An Efficient CeO2/CoSe2 Nanobelt Composite for Electrochemical Water Oxidation. Small 2015, 11, 182-188. (19) Zhang, X.; Liu, S. W.; Zang, Y. P.; Liu, R. R.; Liu, G. Q.; Wang, G. Z.; Zhang, Y. X.; Zhang, H. M.; Zhao, H. Co/Co9S8@S, N-Doped Porous Graphene Sheets Derived from S, N Dual Organic Ligands Assembled Co-MOFs as Superior Electrocatalysts for Full Water Splitting in Alkaline Media. Nano Energy 2016, 30, 93-102. (20) Jiang, N.; You, B.; Sheng, M-L.; Sun, Y. J. Electrodeposited Cobalt-Phosphorous-Derived Films as Competent Bifunctional Catalysts for Overall Water Splitting. Angew. Chem. Int. Ed. 2015, 54, 6251-6254. (21) Wu, T. L.; Pi, M. Y.; Zhang, D. K.; Chen, S. J. 3D Structured Porous CoP3 Nanoneedle Arrays as An Efficient Bifunctional Electrocatalyst for The Evolution Reaction of Hydrogen and Oxygen. J. Mater. Chem. A 2016, 4, 14539-14544. (22) Xu, Y.; Yi, R.; Yuan, B.; Wu, X. F.; Dunwell, M.; Lin, Q. L.; Fei, L.; Deng, S. G.; Andersen, P.; Wang, D. H.; Luo, H-M. High Capacity MoO2/Graphite Oxide Composite Anode for Lithium-Ion Batteries. J. Phys. Chem. Lett. 2012, 3, 309-314. (23) Fan, Y. Q.; Shao, H. B.; Wang, J. M.; Liu, L.; Zhang, J. Q.; Cao, C. N. Synthesis of FoamLike Freestanding Co3O4 Nanosheets with Enhanced Electrochemical Activities. Chem. Commun. 2011, 47, 3469-3471. (24) Cao, X. C.; Zheng, X. J.; Tiana, J. H.; Jina, C.; Keb, K.; Yang, R. Z. Cobalt Sulfide Embedded in Porous Nitrogen-doped Carbon as a Bifunctional Electrocatalyst for Oxygen Reduction and Evolution Reactions. Electrochim. Acta 2016, 191, 776-783.

ACS Paragon Plus Environment

23

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 29

(25) Ganesan, P.; Prabu, M.; Sanetuntikul, J.; Shanmugam, S. Cobalt Sulfide Nanoparticles Grown on Nitrogen and Sulfur Codoped Graphene Oxide: An Efficient Electrocatalyst for Oxygen Reduction and Evolution Reactions. ACS Catal. 2015, 5, 3625-3637. (26) Dou, S.; Tao, L.; Huo, J.; Wang, S. Y.; Dai, L. M. Etched and Doped Co9S8/Grapheme Hybrid for Oxygen Electrocatalysis. Energy Environ. Sci. 2016, 9, 1320-1326. (27) Hou, C. C.; Cao, S.; Fu, W. F.; Chen, Y. Ultrafine CoP Nanoparticles Supported on Carbon Nanotubes as Highly Active Electrocatalyst for Both Oxygen and Hydrogen Evolution in Basic Media. ACS Appl. Mater. Interfaces 2015, 7, 28412-28419. (28) Chang, J. F.; Xiao, Y.; Xiao, M. L.; Ge, J. J.; Liu, C. P.; Xing, W. Surface Oxidized CobaltPhosphide Nanorods As an Advanced Oxygen Evolution Catalyst in Alkaline Solution. ACS Catal. 2015, 5, 6874-6878. (29) Chang, J. F.; Liang, L.; Li, C. Y.; Wang, M. L.; Ge, J. J.; Liu, C. P.; Xing, W. Ultrathin Cobalt Phosphide Nanosheets as Efficient Bifunctional Catalysts for Water Electrolysis Cell and The Origin for Cell Performance Degradation. Green Chem. 2016, 18, 2287-2295. (30) Schaeffer, G. W.; Roscoe, J. S.; Stewart, A. C. The Reduction of Iron (III) Chloride with Lithium Aluminohydride and Lithium Borohydride- Iron (II) Borohydride. J. Am. Chem. Soc. 1956, 78, 729-733. ( 31 ) Farrow, C. L.; Bediako, D. K.; Surendranath, Y.; Nocera, D. G.; Billinge, S. J. L. Intermediate-Range Structure of Self-Assembled Cobalt-Based Oxygen Evolving Catalyst. J. Am. Chem. Soc. 2013, 135, 6403-6406. (32) Masa, J.; Weide, P.; Peeters, D.; Sinev, I.; Xia, W.; Sun, Z. Y.; Somsen, C.; Muhler, M.; Schuhmann, W. Amorphous Cobalt Boride (Co2B) as a Highly Efficient Nonprecious Catalyst

ACS Paragon Plus Environment

24

Page 25 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

for Electrochemical Water Splitting: Oxygen and Hydrogen Evolution. Adv. Energy Mater. 2016, 6, 1502313. (33) Li, H.; Wen, P.; Li, Q.; Dun, C. C.; Xing, J. H.; Lu, C.; Adhikari, S.; Jiang, L.; Carroll, D. L.; Geyer, S. M. Earth-Abundant Iron Diboride (FeB2) Nanoparticles as Highly Active Bifunctional Electrocatalysts for Overall Water Splitting. Adv. Energy Mater. 2017, 1700513. (34) Cui, L.; Qu, F. L.; Liu, J. Q.; Du, G.; Asiri, A. M.; Sun, X. P. Interconnected Network of Core-Shell CoP@CoBiPi for Efficient Water Oxidation Electrocatalysis under Near Neutral Conditions. ChemSusChem 2017, 10, 1370-1374. (35) Ji, X. Q.; Hao, S.; Qu, F. L.; Liu, J. Q.; Du, G.; Asiri, A. M.; Chen, L.; Sun, X. P. CoreShell CoFe2O4@Co–Fe–Bi Nanoarray: A Surface-Amorphization Water Oxidation Catalyst Operating at Near-Neutral PH. Nanoscale 2017, 9, 7714-7718. (36) Wang, W. Y.; Liu, D.; Hao, S.; Qu, F. L.; Ma, Y. J.; Du, G.; Asiri, A. M.; Yao, Y. D.; Sun, X. P. High-Efficiency and Durable Water Oxidation under Mild pH Conditions: An Iron Phosphate-Borate Nanosheet Array as a Non-Noble-Metal Catalyst Electrode. Inorg. Chem. 2017, 56, 3131–3135. (37) Xie, L. S.; Qu, F. L.; Liu, Z.; Ren, X.; Hao, S.; Ge, R. X.; Du, G.; Asiri, A. M.; Sun, X. P.; Chen, L. In-Situ Formation of a 3D Core/shell Structured Ni3N@Ni-Bi Nanosheet Array: An Efficient Non-Moble-Metal Bifunctional Electrocatalyst toward Full Water Splitting under NearNeutral Conditions. J. Mater. Chem. A 2017, 5, 7806-7810.

ACS Paragon Plus Environment

25

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 26 of 29

(38) Yang, L. B.; Liu, D.; Hao, S.; Kong, R. M.; Asiri, A. M.; Zhang C. X.; Sun, X. P. A cobaltBorate Nanosheet Array: An Efficient and Durable Non-Noble-Metal Electrocatalyst for Water Oxidation at Near Neutral PH. J. Mater. Chem. A 2017, 5, 7305-7308. (39) Zhu, W. X., Zhang, R., Qu, F. L., Asiri, A. M., Sun, X. P. Design and Application of Foams for Electrocatalysis. ChemCatChem 2017, 9, 1721-1743. (40) Baris, M.; Simsek, T.; Akkurt, A. Mechanochemical Synthesis and Characterization of Pure Co2B Nanocrystals. Indian Acad. Sci. 2016, 39, 1119-1126. (41) Liu, Y.; Wang, Y. J.; Xiao, L. L.; Song, D. W.; Wang, Y. P.; Jiao, L-F.; Yuan, H. T. Structure and Electrochemical Behaviors of A series of Co–B Alloys. Electrochim. Acta 2008, 53, 2265-2271. (42) Lu, S. F.; Cao, D.; Xu, X.; Wang, H. N.; Xiang, Y. Study of Carbon Black Supported Amorphous Ni-B Nano-Catalyst for Hydrazine Electrooxidation in Alkaline Media. RSC Adv. 2014, 4, 26940-26945. (43) Biesinger, M. C.; Payne, B. P.; Grosvenor, A. P.; Lau, L. W. M.; Gerson, A. R.; Smart, R. S. C. Reslving Surface Chemical States in XPS Analysis of First Row Transition Metals, Oxides and Hydroxides: Cr, Mn, Fe, Co and Ni. Appl. Surf. Sci. 2011, 257, 2717-2730. (44) Doyle, R. L.; Godwin, I. J.; Brandon, M. P.; Lyons, M. E. G. Redox and Electrochemical Water Splitting Catalytic Properties of Hydrated Metal Oxide Modified Electrodes. Phys. Chem. Chem. Phys. 2013, 15, 13737-13783.

ACS Paragon Plus Environment

26

Page 27 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(45) Gao, M. R.; Cao, X.; Gao, Q.; Xu, Y. F.; Zheng, Y. R.; Jiang, J.; Yu, S. H. Nitrogen-Doped Graphene Supported CoSe2 Nanobelt Composite Catalyst for Efficient Water Oxidation. ACS Nano 2014, 8, 3970-3978. (46) Thomas, F. J.; Kristina, P. J.; Jacob, B.; Jane, H. N.; Sebastian, H.; Ib, C. Identification of Active Edge Sites for Electrochemical H2 Evolution from MoS2 Nanocatalysts. Science 2007, 317, 100-102. (47) An, L.; Huang, L.; Zhou, P. P.; Yin, J.; Liu, H. Y.; Xi, P. X. A Self-Standing HighPerformance Hydrogen Evolution Electrode with Nanostructured NiCo2O4/CuS Heterostructures. Adv. Funct. Mater. 2015, 25, 6814-6822. (48) Merki, D.; Vrubel, H.; Rovelli, L.; Fierro, S.; Hu, X. L. Fe, Co, and Ni ions Promote the Catalytic Activity of Amorphous Molybdenum Sulfide Films for Hydrogen Evolution. Chem. Sci. 2012, 3, 2515-2525. (49) Shang, L.; Bian, T.; Zhang, B. H.; Zhang, D. H.; Wu, L. Z.; Tung, C. H.; Yin, Y. D.; Zhang, T-R. Graphene-Supported Ultrafine Metal Nanoparticles Encapsulated by Mesoporous Silica Robust Catalysts for Oxidation and Reduction Reaction. Angew. Chem. Int. Ed. 2014, 53, 250254. (50) Zheng, Y.; Jiao, Y.; Jaroniec, M.; Qiao, S. Z. Advancing the Electrochemistry of the Hydrogen-Evolution Reaction through Combining Experiment and Theory. Angew. Chem. Int. Ed. 2015, 54, 52-65. ( 51 ) Bruke, M. S.; Kast, M. G.; Trotochaud, L.; Smith, A. M.; Boettcher, S.W. Cobalt Iron(oxy)hydroxide Oxygen Evolution Electrocatalysts: The Role of Structure and Composition on Activity, Stability, and Mechanism. J. Am. Chem. Soc. 2015, 137, 3638-3648.

ACS Paragon Plus Environment

27

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 28 of 29

(52) Gerken, J. B.; McAlpin, J. G.; Chen, J. Y. C.; Rigsby, M. L.; Casey, W. H.; Britt, R. D.; Stahl, S. S. Electrochemical Water Oxidation with Cobalt-based Electrocatalysts from 0-14: The Thermodynamic Basis for Catalyst Structure, Stability, and Activity. J. Am. Chem. Soc. 2011, 133, 12-14. ( 53 ) Chou, N. H.; Ross, P. N.; Bell, A. T.; Tilley, T. D. Comparison of Cobalt-Based Nanoparticles as Electrocatalysts for Water Oxidation. ChemSusChem 2011, 4, 1566-1569. (54) Ismail, K. M.; Badawy, W. A. Electrochemical and XPS Investigations of Cobalt in KOH Solutions. J. Appl. Electrochem. 2000, 30, 1303-1311. ( 55 ) Jayaraman, TR.; Venkatesan, VK.; Udupa, HVK. Cyclic Coltammetric Studies of Electroless Cobalt in NaOH. Electrochem. Acta. 1975, 20, 209-213. (56) Wang, Hsin. Y.; Hung, S. F.; Chen, H. Y.; Chan, T. S.; Chen, H. M.; Liu, B. In Operando Identification of Geometrical-Site-Dependent Water Oxidation Activity of Spinel Co3O4. J. Am. Chem. Soc. 2016, 138, 36-39. (57) Jiang, Y. M.; Li, X.; Wang, T. X.; Wang, C. M. Enhanced Electrocatalytic Oxygen Evolution of Alpha-Co(OH)2 Nanosheets on Carbon Nanotube/polyimide Films. Nanoscale 2016, 8, 9667-9675 (58) Zeng, K.; Zhang, D. Recent progress in alkaline water electrolysis for hydrogen production and applications. Prog. Energy Combust. Sci. 2010, 36, 307-326. (59) Luo, J.-H.; Mayer, Im, M. T.; Schreier, M.; Nazeeruddin, M. K.; Park, N.-G.; Tilley, S. D.; Fan, H. J.; Grätzel, M. Water photolysis at 12.3% efficiency via perovskite photovoltaics and Earth-abundant catalysts. Science, 2014, 345, 1593-1596.

ACS Paragon Plus Environment

28

Page 29 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Table of Contents Graphic and Synopsis

A series of CoxB catalysts were prepared by single-step ball-milling methods, showing highly catalytic activities toward full water splitting.

ACS Paragon Plus Environment

29