Communication

Deterministic switching of the growth direction of self-catalyzed GaAs nanowires Eero Koivusalo, Teemu Hakkarainen, Helder Vinicius Avanço Galeti, Yara Galvão Gobato, Vladimir G. Dubrovskii, and Mircea D. Guina Nano Lett., Just Accepted Manuscript • DOI: 10.1021/acs.nanolett.8b03365 • Publication Date (Web): 11 Dec 2018 Downloaded from http://pubs.acs.org on December 13, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

1

Deterministic switching of the growth direction of

2

self-catalyzed GaAs nanowires

3

Eero S. Koivusalo* 1, Teemu V. Hakkarainen1, Helder V. A. Galeti2, Yara G. Gobato3,

4

Vladimir G. Dubrovskii4, Mircea D. Guina1

5

1

Optoelectronics Research Centre, Tampere University of Technology, P.O. Box 692,

6 7

FIN-33101 Tampere 2

Electrical Engineering Department, Federal University of São Carlos, 13565-905, São

8 9

Carlos-SP, Brazil 3

Physics Department, Federal University of São Carlos, 13565-905, São Carlos-SP,

10 11

Brazil 4

ITMO University, Kronverkskiy prospekt 49, 197101 St. Petersburg, Russia

12

ABSTRACT: Typical vapor-liquid-solid growth of nanowires is restricted to vertical one-

13

dimensional geometry, while there is a broad interest for more complex structures in the

14

context of electronics and photonics applications. Controllable switching of the nanowire

15

growth direction opens up new horizons in the bottom-up engineering of self-assembled

16

nanostructures, for example, to fabricate interconnected nanowires used for quantum

ACS Paragon Plus Environment

1

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 50

17

transport measurements. In this work, we demonstrate a robust and highly controllable

18

method for deterministic switching of the growth direction of self-catalyzed GaAs

19

nanowires. The method is based on the modification of the droplet-nanowire interface in

20

the annealing stage without any fluxes and subsequent growth in the horizontal direction

21

by a twin-mediated mechanism with indications of a novel type of interface oscillations.

22

A 100% yield of switching the nanowire growth direction from vertical to horizontal is

23

achieved by systematically optimizing the growth parameters. A kinetic model describing

24

the competition of different interface structures is introduced to explain the switching

25

mechanism and the related nanowire geometries. The model also predicts that growth of

26

similar structures is possible for all vapor-liquid-solid nanowires with commonly observed

27

truncated facets at the growth interface.

28

KEYWORDS Self-catalyzed GaAs nanowires, Growth direction, Crystal facets, Surface

29

energetics

30

Precise shaping of III-V semiconductor nanowires (NWs) is paramount for their

31

functionalization into electronic and photonic devices. In particular, GaAs/AlGaAs NW-

ACS Paragon Plus Environment

2

Page 3 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

32

based lasers integrated on silicon waveguides [1], monolithic LEDs [2, 3], and functional

33

NW array solar cells [4] have been the important milestones in this development. All these

34

achievements have relied on the axial or radial heterostructures within one-dimensional

35

(1D) NWs. Extension of the NW growth beyond 1D geometry provides a suitable template

36

for delicate quantum transport measurements [5, 6]. Several approaches have previously

37

been used to form a versatility of three-dimensional NW-based structures. In particular,

38

Au-catalyzed NW crosses have been grown on a (100) substrate producing rather

39

random InAs NW meshes [6], and in a more controllable way on a pre-patterned substrate

40

[7]. A ridged template covered by oxide with pre-determined nucleation sites has provided

41

another approach to grow more regular InAs

42

Interconnected NWs can also be produced by switching the NW growth direction with

43

respect to the typical [or in the case of wurtzite (WZ) NWs] direction of the

44

substrate normal. The most convenient 90° switching of the growth direction has been

45

demonstrated for Au-catalyzed WZ InAs NWs [7] and catalyst-free InAs(Sb) NWs [10]. In

46

optics and photonics, possible applications of such structures include circular dichroism

47

in the optical response of chiral nanostructures [11], exploiting the waveguiding properties

[8, 9] and InSb [5] NW crosses.

ACS Paragon Plus Environment

3

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 50

48

of semiconductor NWs. [12, 13] This effect further increases the interest in controlling the

49

NW growth direction. To date, the yield of bent NWs has always been less than 100 %

50

within the framework of self-catalyzed approach. Furthermore, not all the horizontal

51

growths start in the same horizontal plane, which is unfavorable for further contacting the

52

NWs.

53

The simplest mechanism for switching the NW growth direction is driven by a catalyst

54

droplet wetting one of the NW side facets [7, 10, 14]. After that, more complex growth

55

effects may occur, including the formation of new facets or twin planes separating

56

different facets. Using these effects, even reversible switching of the growth direction has

57

been demonstrated in Au-catalyzed InP NWs [15]. In addition, twinning is known to

58

facilitate the formation of kinks and other kind of structures such as nanomembranes [16],

59

flags [14] and sails [17]. Very important information on the kinetics of kinking in Au-

60

catalyzed NWs is provided by in-situ transmission electron microscopy (TEM), as

61

descried previously [18, 19]. Despite the significant progress in understanding and

62

controlling the NW growth direction by different methods, a simple and robust procedure

63

for achieving 100% yield of horizontal self-catalyzed NW growth in one horizontal plane

ACS Paragon Plus Environment

4

Page 5 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

64

is still lacking. Consequently, this work reports a method to grow very regular ensembles

65

of 90° bent GaAs NWs on silicon in the self-catalyzed approach.

66

By using a lithography-free SiOx patterns as templates for the self-catalyzed vapor-

67

liquid-solid (VLS) growth, we have been able to obtain GaAs NWs with the controllable

68

number density, high quality zincblende (ZB) crystal structure and remarkable sub-

69

Poissonian length uniformity [20–22]. Here, we show that this growth method can be

70

extremely suitable to induce bent NW structures with horizontal growth. The deterministic

71

switching of the growth direction occurs in the same horizontal plane due to the narrow

72

length distribution of the initial NWs. This is highly desirable for fabrication of

73

interconnected NWs. 100% yield of regularly bent NWs is achieved simply by a growth

74

interruption, which determines a transition from vertical to horizontal growth. We

75

investigate in detail the previously unknown growth mechanism in different stages and

76

show that the NW morphology is generally sensitive to the duration of the growth

77

interruption, the local V/III ratio, and the NW diameter. Longer growth interruption is found

78

to deterministically switch the NW growth direction by 90° with a 100% yield. We develop

79

a model, which describes the observed reshaping of the growth interface and shows that

ACS Paragon Plus Environment

5

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 50

80

the deterministic transition from vertical to horizontal growth upon the growth interrupt

81

must be a general phenomenon for all self-catalyzed III-V NWs under the appropriate

82

conditions. Thus, the insights presented here may help to either avoid the unwanted

83

kinking during the NW growth or deterministically switch the NW growth direction when

84

required for particular applications.

85

The self-catalyzed GaAs NWs were grown by solid source molecular beam epitaxy

86

(MBE) on lithography-free oxide pattern templates fabricated on p-Si(111) substrates via

87

droplet epitaxy. The lithography-free templates are fabricated on HF etched, oxide-free

88

Si substrates, by depositing Ga droplets on the substrate and crystallizing the droplets

89

into GaAs under the As flux. After that, the templates are oxidized in air and loaded back

90

into the MBE chamber, where the GaAs mounds are evaporated to form the lithography-

91

free oxide patterns, on which the NWs are in-situ grown, as described in [20, 22]. The

92

NWs were grown on four different templates with the nucleation site densities varying

93

from 5×107 cm-2 to 5×108 cm-2. The vertical NW growth was initiated with a 40 s pre-

94

deposition of Ga droplets, re-evaporation of the droplets and simultaneously opening the

95

Ga and As2 fluxes. The NW growth was conducted at 640 °C, as determined by

ACS Paragon Plus Environment

6

Page 7 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

96

pyrometer, the Ga deposition rate was 0.3 µm/h, as calibrated for (100) GaAs growth,

97

and the V/III beam equivalent pressure (BEP) ratio was 9. The vertical NW growth time

98

was 20 min, except for three samples with variable diameters for which the growth

99

durations from 20 to 30 min were used. More details on the template fabrication and the

100

NW growth method can be found in Refs. [20–22]. After growth of the vertical part, the

101

NWs were annealed for 20 to 70 s at the growth temperature without any fluxes in order

102

to reshape the droplet-NW interface. After the annealing, the NW growth was resumed

103

by simultaneously providing the Ga and As fluxes. The V/III BEP ratio for the horizontal

104

growth was varied from 7 to 11. After growth, the samples were rapidly cooled down.

105

Additional samples with vertical NWs grown for 20 min and rapidly cooled down (template

106

density 5×108 cm-2), and NWs gone through 45 s annealing (template densities 2×108 cm-

107

2,

108

fabricated as the references to study the droplet-NW interface and the NW dimensions

109

before the growth continuation.

5×108 cm-2 and 5×107 cm-2, and growth durations from 20 to 30 min) were also

110

The NW morphologies were studied using scanning electron microscopy (SEM). A

111

typical NW sample after 20 min of vertical growth and immediate cool down without any

ACS Paragon Plus Environment

7

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 50

112

fluxes is shown in Figures 1 (a) and (d). It is clearly seen that the Ga droplets remain

113

stationary on the NW tips just after growth. In contrast, the sample that was annealed for

114

45 s at the growth temperature prior to cool down [Figure 1 (b) and (e)] exhibits 100%

115

yield of droplets falling toward one of the (110) side facets. When the growth is resumed

116

after annealing by simultaneously opening the Ga shutter and As valve, the NWs continue

117

their growth perpendicular to their initial growth direction [Figures 1 (c) and (f)], or slightly

118

downward [Figures 1 (c) and (g)]. Perpendicularly grown horizontal sections are referred

119

to as type 1 and downward pointing sections as type 2. The azimuthal direction of the

120

bent NW part is toward one of the directions associated with the corners of the

121

(110) sidewalls, in contrast to the droplet position after the annealing [see the top-view

122

images in Figures 1 (e) to (g)].

ACS Paragon Plus Environment

8

Page 9 of 50

(a) Self-catalyzed NW growth

(e)

Annealing

(c) Continued growth nm

1 µm

(d)

(b)

20

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

1 µm

(f)

1 µm Type 1

(g)

Type 2

123 124

Figure 1. Growth of bent GaAs NWs: (a) and (d) Vertical NWs grown for 20 min and rapidly cooled

125

down; (b) and (e) NWs annealed at the growth temperature for 45 s prior to cool down; (c) NWs

126

grown for 5 min after 45 s annealing; Side- and top-view images of (f) type 1 horizontal and (g)

127

type 2 downward growth. Scale bars in low magnification 30° tilted images are 1 µm in (a) to (c)

128

and 100 nm in (d) to (g).

129

To further understand the formation mechanism of these structures, the post-annealing

130

droplet-NW interfaces were analyzed by SEM and high-resolution transmission electron

ACS Paragon Plus Environment

9

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 50

131

microscopy (HR-TEM) [JEOL JEM-2200FS operated at 200 kV and FEI Tecnai G2-F20

132

operated at 200 kV for Figure 4 (b)]. Two different droplet–NW interface shapes with

133

respect to the [110] zone axis (ZA) were found by TEM, as shown in Figures 2 (a) and

134

(b). The first shape is dominated by the A-polar (1-1-1) facet and the second type by the

135

(0-10) facet. The third low index facet is the B-polar (-111) facet forming below the (0-10)

136

one, as shown in Figure 2(b). Otherwise, the structures compose of minor higher index

137

facets. The facets are identified based on the assumption that the NW top facet is (-1-1-

138

1) and the NW sidewalls are (110). The growth direction is identified as B because

139

it is the common growth direction of self-catalyzed GaAs NWs [23, 24], while A-polar GaAs

140

NWs are rarely achieved and mainly using Au-catalyzed VLS growth [25, 26]. It should also be

141

noted that the radial symmetry of the NW is three-fold. This symmetry yields three

142

possible sets of [110] ZA that give equivalent results for the facet identification. The one

143

presented here is an arbitrarily chosen example showing the droplet-NW interface of a

144

particular NW.

ACS Paragon Plus Environment

10

Page 11 of 50

(a)

(b)

---

(111)

20 nm

(111)

20 nm

- -

---

(111)

(010)

-

-

(101)

--

(811)

-

(110)

-

(111)

(d) - 0) (1-0 1) (11

(- 110) 101) (

(e)

---

(111) (010) -(111)

(f)

---

--

(111)

(111) (011)

145

20 nm

(101)

(011)

50 nm

(111)

-

--

(c)

---

(100)

(011)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

-

(010)

(g) 109.5°

-

(011)

(h) 125.3°

-

(101)

146

Figure 2. (a)–(c) TEM micrographs of three NWs annealed for 45 s at the growth temperature

147

prior to cool down. The ZAs marked in the micrographs are also marked in the SEM image of

148

droplet-free NW top facet in (d) and sketches (e), (g) and (h). SEM image (d) and top-view sketch

149

(e) are aligned with respect to each other. Complementary SEM analysis of (d) is presented in

150

the SI.

151

Both dominating reshaped facets are inclined toward one of the corner directions

152

of the NW sidewalls, perpendicular to the [110] ZA used for imaging. However, back-view

153

TEM [Figure 2 (c)] and top-view SEM [Figure 1 (e)] show that the droplets are tilted

154

symmetrically toward one of the (110) side facets. The shape of the NW growth interface

ACS Paragon Plus Environment

11

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 50

155

was imaged by SEM after removing the Ga droplets by HCl etching. SEM analysis

156

revealed the pentagonal shape of the top facet marked by the dashed line in Figure 2 (d),

157

and that two of the sidewall corners are hidden under the reshaped facets. Based on

158

these results, the interface configurations shown in Figures 2 (a) and (b) are interpreted

159

as different views of similar structure, illustrated in the sketches in Figures 2 (e)–(h). More

160

details on the SEM analysis of the droplet-NW interface are given in the supporting

161

information (SI).

162

Results of the TEM analysis of a type 1 NW structure, shown in Figures 3 (a) and (b),

163

reveal pure ZB structure throughout the whole NW, with a single twin plane extending

164

along the horizontal section HR-TEM images in Figures 3 (c) to (e) are aligned in such a

165

way that the top side of the horizontal section is facing upward. These images show two

166

different interface configurations existing during growth of type 1 horizontal sections. Both

167

configurations are dominated by a flat (111) plane on one side of the twin plane, and

168

feature a combination of smaller facets on the other. For the NW imaged in Figure 3 (c),

169

the dominating flat (111) plane is B-polar as it is situated above the twin plane. For the

170

NW in Figure 3 (d), the dominating (111) plane is A-polar, and lies below the twin plane.

ACS Paragon Plus Environment

12

Page 13 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

171

This (111) A facet corresponds to the (1-1-1) plane marked in Figure 2 (a). The HR

172

magnification shown in Figure 3 (e) confirms that the (111) planes exist on both sides of

173

the twin plane. It should be noted that defect-free ZB structure without twin planes was

174

observed at the tip of all investigated NWs before and after the annealing step, as shown

175

in the SI and Figure 2, respectively. Based on these observations, we conclude that type

176

1 growth is initiated by nucleation of the twin plane which forms the (111)B plane to

177

oppose the initial (1-1-1) plane seen in Figure 2 (a). The two (111)B and (111)A opposing

178

facets pin the droplet to sustain the horizontal growth.

ACS Paragon Plus Environment

13

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 50

179 180

Figure 3. HR-TEM analysis of type 1 bent GaAs NWs. The low magnification image in (a) and

181

selective area diffraction (SAED) patterns in (b) reveal the excellent crystal purity in the ZB phase,

182

and a single twin plane present in the horizontal section. Two different droplet-NW interfaces are

183

dominated by a flat (111)B plane in (c) and (111)A plane in (d). Periodic faceting of the top of the

ACS Paragon Plus Environment

14

Page 15 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

184

horizontal NW section can clearly be seen in (c) and (d). (e) HR magnification of the twin section

185

that features both (111)A and (111)B facets.

186

TEM analysis conducted on a type 2 NW structure reveals some similarities with type

187

1 growth. In particular, Figure 4 (a) shows that type 2 downward growth occurs on a NW

188

where a single twin is present, as we saw earlier for type 1. However, in this case the twin

189

is found in the vertical part, above the downward type 2 growth [Figure 4 (a), SAED

190

pattern 1] and is most likely formed when the growth is resumed. The downward growth

191

continues directly along the B direction [Figure 4 (b)] pointing 109° away from the

192

original NW growth direction. This is the direction of the (-111) facet marked in Figure

193

2(b). Thus, type 2 downward growth is interpreted to start with nucleation of a single twin

194

plane and the droplet sliding down from the (0-10) facet wetting the (-111) facet marked

195

in Figure 2(b), where the growth continues. During the downward growth, the (-111) facet

196

remains flat and no microfacetting in the droplet-NW interface is witnessed [Figure 4 (b)

197

and SI].

198

The NW shown in Figure 4 (a) is aligned to a [110] ZA, which is rotated by 60° around

199

the NW axis from the direct side-view [Figure 1(g)]. In this case, possible twinning of the

ACS Paragon Plus Environment

15

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 50

200

downward part cannot be seen because a twin in that growth direction rotates the zone

201

axis away from the [110]. Hence, only one set of the diffraction points would be seen in

202

the SAED pattern even if the downward section were twinned. Therefore, additional TEM

203

analysis in side-view configuration aligned to [117] ZA is shown in Figure 4 (b),

204

demonstrating that the downward section is dominated by periodic twinning. The twinning

205

is clearly seen as a contrast difference in Figure 4 (b), and is also observable as

206

roughness of the downward section in Figure 4 (a).

ACS Paragon Plus Environment

16

Page 17 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

207 208

Figure 4. Type 2 downward growth of a GaAs NW. (a) [110] ZA image of a type 2 structure with

209

downward section grown for 20 min shows the defect-free vertical section, with a single twin in

210

the tip of the NW (SAED 1). (b) In [117] ZA image of a structure with 20 min downward growth,

ACS Paragon Plus Environment

17

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 50

211

periodic twinning of the horizontal section is witnessed, corresponding to SAED 4. The evolution

212

of type 2 structures during the downward growth is described in more detail in the SI.

213

As type 1 structures grow precisely in the same horizontal plane (see the SI) and exhibit

214

only a single twin plane, whereas type 2 structures consist of a periodic twinning

215

superlattice, we carefully optimized the yield of higher quality type 1 structures. We

216

studied the effects of the NW density, annealing time, V/III BEP ratio during the resumed

217

growth and NW diameter on the populations of type 1 and 2 NWs. For the annealing time,

218

V/III BEP ratio and NW density, all horizontal sections were grown on similar vertical NWs.

219

The effect of each growth parameter was studied independently using the intermediate

220

values of the other two parameters (the NW density = 3×107 cm-2, the annealing time =

221

45 s, the V/III BEP ratio = 9). For the diameter series, the vertical growth time was varied

222

in order to tune the size of the initial NWs (at a fixed V/III BEP ratio). The populations

223

were characterized by analyzing top-view SEM images as described in more detail in the

224

SI.

ACS Paragon Plus Environment

18

Page 19 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

225

According to Figure 5 (a), increasing the NW surface density from 2.4×107 cm-2 to

226

2.5×108 cm-2 allowed us to increase the yield of type 1 structures from 20 to 100% . The

227

effect of the annealing time is shown in Figure 5 (b). Very importantly, 99% yield of type

228

1 structures was obtained with the longest annealing time of 70 s. For the shortest

229

annealing time of 20 s, the horizontal growth was mostly suppressed by the formation of

230

arbitrarily shaped bulges, showing that 20 s is not an adequate time for the deterministic

231

switching of the NW growth direction. Figure 5 (c) shows that altering the V/III ratio as the

232

growth is resumed after the annealing step also had a significant effect on the yield of

233

type 1 structures. For the lowest V/III ratio, all horizontal sections nucleated as type 1

234

structures. However, for 35% of these structures the droplets wetted the horizontal NW

235

sidewalls, terminating the original type 1 growth. Formation of these structures, referred

236

to as type 1b in the Figure 5 (e), is explained in the SI, where the top facets of such

237

structures are analyzed in more detail based on SEM images. A higher V/III ratio of 11

238

produced up to 70% yield of type 1 structures. However, many droplets started shrinking

239

during the subsequent horizontal growth, implying that such growth would eventually be

240

terminated due to the droplet consumption. Furthermore, 40% of type 2 structures

ACS Paragon Plus Environment

19

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 50

241

obtained with V/III=11 exhibited growth directly downward along the sidewalls of vertical

242

NWs. These structures have nucleated similarly to type 2 NWs, and are referred to as

243

type 2b in Figure 5 (e). The SEM analysis of these structures is given in the SI. No droplets

244

were observed on top of type 2b structures.

245

Figure 5 (d) shows the effect of the NW diameter on the yield of type 1 structures. For

246

the narrowest NWs with the diameters of 75 nm, more than 99% yield of type 1 structures

247

is achieved. Increasing the NW diameter leads to a rapid decrease of the type 1

248

population. For 84 nm diameter NWs, the type 1 yield becomes only 17.4%, and drops

249

below 10% for 91 nm diameter NWs. The additional data point for 90 nm diameter NWs

250

but with the annealing time increased from 45 s to 70 s demonstrates that type 1 yield

251

increases from less than 10% to 55% despite the large NW diameter. Therefore,

252

increasing the annealing time has a similar effect as decreasing the NW diameter, both

253

leading to higher yield of type 1 structures. This will be important in what follows. Figure

254

5 (f) shows a SEM image of the high density sample with 100% yield of type 1 NWs.

ACS Paragon Plus Environment

20

Page 21 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

255 256

Figure 5. Effect of the growth parameter tuning on the yield of type 1 structures: (a) NW

257

density, (b) annealing time, (c) V/III BEP ratio, and (d) NW diameter. Note that the

258

intermediate data in histograms (a)–(c) are from the same sample. The inset in (b) shows

259

the typical random bulge formed when the annealing time is too short. The 30° tilted view

260

SEM images in (e) show type 1b and 2b structures as described in the text and SI. The

261

scale bars are 100 nm. (f) 30° tilted SEM image of the high density sample with 100%

262

yield of type 1 structures. (g) the NW diameter dependence of the type 1 and 2

263

populations at a fixed annealing time of 45 s (with a lower density of surface structures of

264

1.26  108 cm-2, and a higher density of 1.91  108 cm-2), fitted by the model described

265

below.

ACS Paragon Plus Environment

21

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 50

266

We now compare these results with the previously published data. The droplet-NW

267

interface reshaping shown in Figure 1 (e) and analyzed in Figure 2 was observed in our

268

previous work [22]. However, as these samples were immediately cooled down after the NW

269

growth, the effect was not reproducible until the annealing step was introduced to achieve the

270

deterministic switching of the NW growth direction as described above. Similar effect of the

271

growth interface reshaping has previously been reported for Be-doped self-catalyzed GaAs NWs

272

in Ref. [27], where Be was thought to lower the droplet surface energy and to cause a partial

273

wetting of the NW sidewalls. In Ref. [28], the Ga flux was provided for 20 to 60 s after termination

274

of the As input in order to inflate the droplet and let it wet the NW side facets. The multiple (111)

275

facets observed in Ref. [27] form a similar structure to the one shown in Figure 2 (a). Similarly in

276

Ref. [28], the (111)A facet dominated the reshaped droplet-NW interface, even though a few twin

277

planes were formed above the droplets, one of which extended to the droplet-NW interface. This

278

extended twin plane is likely to represent the very first steps of nucleation toward type 1 structure.

279

Thus, prior observations support the repeatability and generality of the (111)-dominated droplet-

280

NW interface reshaping upon the growth interruption.

281

In addition to the reshaped (111)A [(1-1-1) in Figure 2 (a)] facet, our NWs comprise a (100)

282

facet, below which we always observe a (111)B facet [such as the (0-10) and (-111) facets in Figure

283

2 (b)]. The reshaped (100) facet and the (111)B facet below it were not observed in Refs. [27, 28].

284

Based on the droplets tilting symmetrically in between the (1-1-1) and (0-10) facets [away from

285

the (-110) NW side facet in Figure 2 (c)], and taking into account the interface configuration

286

observed on the NWs with the droplets removed, we conclude that the reshaped droplet-NW

287

interface consists of a combination of the (111)A and (100) facets, as illustrated in Figure 2 (e)–

ACS Paragon Plus Environment

22

Page 23 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

288

(h). According to this view, type 1 and type 2 structures nucleate from NWs having very similar

289

droplet-NW interfaces. However, higher quality horizontal type 1 structures are dominated by the

290

(111)A facets. Lower quality downward type 2 structures are dominated by the (100) facets and

291

grow perpendicular to the (111)B facet situated below the (100) one. The difference between type

292

1 and 2 structures should then be explained by the fine tuning of the interface geometry, namely

293

the probabilities of forming the (111)A and (100) reshaped facets. The reshaping of the growth

294

interface should be due to an interplay of the surface energetics and kinetics, supported by the fact

295

that the populations of type 1 and 2 structures can be tuned by the growth parameters and the NW

296

diameters as shown in Figure 5.

297

We now present a model to explain and quantify the switching mechanism. According

298

to Refs. [29,30], B-aligned self-catalyzed GaAs NWs and even Au-catalyzed GaAs

299

NWs grown under Ga-rich conditions exhibit a truncated growth interface with an inward

300

tapered facet wetted by a catalyst droplet. Such truncated NWs have pure ZB crystal

301

phase because nucleation occurs away from the triple phase line where solid, liquid and

302

vapor phases meet [29–32]. Unfortunately, in-situ TEM measurements [29,31] cannot

303

identify the exact orientation of the small truncated facet due to the complex structure of

304

the truncation and its fast oscillations. However, it seems reasonable that the low index

305

(111)A and (100) can both be present in the initially truncated vertical NWs as well as in

306

NWs reshaping under annealing.

ACS Paragon Plus Environment

23

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

307

Page 24 of 50

According to the model of Tersoff [31], the free energy change of forming an inclined

308

facet making the angle  i to the vertical, of height y and length L , is given by

309

   tan  i  2   y  Gi  L  ai y   bi   2 35   . 

310

This expression presents the free energy relative to the vertical facet and planar growth

311

interface. Here,  ai is the surface energy change upon forming the inclined facet, which

312

becomes negative at large enough contact angles of the droplet  (   133° in our

313

vertical NWs),  is the chemical potential difference per GaAs pair in liquid and solid,

314

35  0.0452 nm3 is the elementary volume of GaAs pairs in solid, and bi is a positive

315

constant which determines the facet size when   0 . The energetically preferred facet

316

heigth y*( i ) that minimizes Gi is given by y*(i )  ai /[2bi (1   i  )] , with  i  tan  i /(235bi ) .

317

According to our assumption, ai  0 for both (111)A and (100) facets, with the probability

318

of their occurrence detemining the populations of type 1 ( i  1) or 2 ( i  2 ) bent NW

319

structures. We should now compare the probabilities of forming type 1 or 2 facets at

320

varying chemical potential  which decreases in the annealing stage upon the growth

321

interrupt.

(1)

ACS Paragon Plus Environment

24

Page 25 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

322

323 324

325

Nano Letters

The minimum free energy values at y  y*(i ) are given by

G*(i )  

ai L 4bi (1   i  ) .

(2)

The probability p1 of forming type 1 structure can generally be put as

p1 

exp(G1* / k BT ) exp(G1* / k BT )  exp(G2* / k BT ) ,

(3)

326

with T as the growth temperature and k B as the Boltzmann constant. As shown in the SI,

327

chemical potential decreases with the annealing time t approximatelly as



k BT 33 h 1 k35  0 35 f (  ) R R,

328

  0 (1  t )

329

with  0 as the initial chemical potential value at t  0 . The constant  determines the

330

rate of chemical potential decrease, with 3  0.02 nm3 as the elementary volume of liquid

331

Ga,

,

h  0.326

nm

as

the

(4)

height

of

GaAs

monolayer,

332

f (  )  (1  cos  )(2  cos  ) /[(1  cos  ) sin  ] as the geometrical function of the droplet

333

contact angle  , k35 as the crystallization rate of GaAs pairs, and R as the NW radius

334

(which equals the radius of the droplet base). Chemical potential decreases linearly with

335

t , while for a given t it is higher for larger R because larger droplets deplete more slowly

ACS Paragon Plus Environment

25

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 26 of 50

336

with their As. Using equations (2) to (4), the yield of type 1 structures is obtained in the

337

form p1 

338

1    1 u  1  exp     1   2  0 (1  t ) 1   1  0 (1  t )  ,

(5)

339

with   [a22 /(4b2 )]( L / k BT ) and u  a12b2 /(a22b1 ) .

340

Using the plausible parameters of self-catalyzed growth of GaAs NWs ( 0  0.2 eV

341

[33,34], k35 =165 s-1 corresponding to the mean axial growth rate of our vertical NWs of

342

1.06 nm/s [22], and   133o), we obtain the  values on the order of 1 min-1 for R ~ 50

343

nm, showing that chemical potential tends to zero after ~ 1 min of annealing. According

344

to Figures 5 (b) and (d), an almost 100% yield of type 1 NW structures is obtained after

345

70 s annealing and even after 45 s annealing for a smaller NW diameter of 75 nm. Shorter

346

annealing times or larger NW diameters favor type 2 structures, which becomes

347

predominant (more than 90%) for the largest NW diameters of 90–91 nm. According to

348

the above analysis, smaller diameters or longer annealing times bring the VLS system

349

closer to the quasi-equilibrium state at   0 , corresponding to t  1 in equation (5).

350

On the other hand, higher  favors type 2 structures. While the  i and u parameters

ACS Paragon Plus Environment

26

Page 27 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

351

entering equation (5) are unknown, higher yield of type 2 structures at   0 (and

352

therefore the preference of the (100) truncation in vertical NWs), transitioning to an almost

353

100% yield of type 1 structures at   0 requires that

354

1   2  0 u 1 u  1 , 1   1 0 ,

355

implying that 1   2 . These two inequalities are essential for describing the observed

356

trends in the two competing NW structures under annealing.

(6)

357

Using equation (6), we can quantify the yield of type 1 structures versus the NW

358

diameter at a fixed t of 45 s. The facet length L entering the  parameter should be

359

proportional to R . We can then write   R / R1 and t  R0 / R according to equation (5).

360

This gives p1 ( R) 

361

1 R  1 u  1  exp    R 1     ( 1  R / R ) 1     ( 1  R / R ) 2 0 0 1 0 0  .  1

(7)

362

Figure 5 (g) shows a good fit to the data by equation (7) with R1  1.5 nm, R0  32.5 nm,

363

u  2 ,  2 0  1 and 10  7. It is seen that the transition from less than 10% to almost

ACS Paragon Plus Environment

27

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 28 of 50

364

100% of type 1 structures is very sharp and occurs for a relatively small diameter change

365

from 90 to 75 nm.

366

Very importantly, all the statistical data on type 1 versus type 2 NW structures shown in

367

Figures 5 (a) to (d) are qualitatively explained within our model. As discussed above,

368

longer annealing times and smaller NW sizes decrease chemical potential and hence

369

favor type 1 structures. Higher density NWs are ~ 100 nm longer and thinner (71 nm in

370

diameter) than the sparse ones (82 nm in diameter). Therefore, the NW density effect is

371

the same as for the diameter series. Due to a higher fraction of re-emitted As species

372

[33], the local V/III flux ratio should be higher for denser NWs. Higher As flux is known to

373

increase the axial NW growth rate and simultaneously shrink the Ga droplets, yielding

374

thinner NWs [35–37]. Lower V/III BEP ratios leads to a steeper decrease of chemical

375

potential in the gallium droplets [33, 34] and hence favor a faster formation of type 1

376

structures when the growth is resumed after annealing. The only exception from this trend

377

is the case of the highest V/III BEP ratio of 11 [see Fig. 5 (c)], where the population of

378

type 1 structures increases even though a higher  is expected. This may be associated

379

with shorter incubation times, where more energetically preferred structures are formed

ACS Paragon Plus Environment

28

Page 29 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

380

over a given period of time. It should also be noted that nucleating the horizontal growth

381

with an optimized V/III BEP ratio for each density (for example, V/III=7 for the intermediate

382

NW density) and then tuning the V/III ratio back to 9 could produce 100% yield of type 1

383

structures. This gives additional versatility of the growth parameters that can individually

384

be tuned to maximize the deterministic nucleation of type 1 structures.

385

Based on the structural analysis of the reshaped droplet-NW interfaces and type 1

386

structures shown in Figures 2 and 3, type 1 structures nucleate on the (1-1-1) facet

387

marked in Figure 2 (a). Simultaneously a twin plane forms, creating a (111)B facet to

388

oppose the (1-1-1) one. Because this twin plane is observed in both types of structures,

389

it is most likely initiated by the triple phase line nucleation at the droplet edge opposing

390

the reshaped (1-1-1) and (0-10) facets, where the droplet contact angle is less than 90°

391

[29, 32]. In type 1 structures, the twin plane between the (111)A and (111)B facets pins

392

the droplet, allowing the growth to propagate in the direction. Such mechanism is

393

known as the twin-mediated growth, observed previously for Ge ingots and Au-catalyzed

394

Ge and GaInP NWs. [38–42] However, our growth mode is different from previous

395

observations. In our case, two different interface configurations are observed, where the

ACS Paragon Plus Environment

29

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 30 of 50

396

flat facet dominating the droplet-NW interface may be either the upper B-polar [Figure 3

397

(c)], or the lower A-polar facet [Figure 3 (d)], and the other (111) facet is replaced by

398

several smaller microfacets. These two morphologies present different phases of a novel

399

type of twin-mediated growth where the flat facet dominating the growth varies

400

periodically. Oscillations between the flat (111)A and (111)B facets during growth is

401

supported by the periodically changing morphology of the top parts of horizontal NWs,

402

where one half-period is almost parallel to the twin plane and the other has a downward

403

slope with respect to the twin. This fine structure can readily be seen in SEM images

404

shown in Figure 1 (f) and in the SI, and in more detail in the side-view TEM in Figures 3

405

(c) and (d). The sustainability of this oscillating twin-mediated growth mode for long

406

horizontal sections is demonstrated in the SI by analyzing the horizontal growth rate for

407

a V/III BEP ratio of 9. The growth rate remains constant for at least 20 min and equals the

408

axial growth rate of vertical NWs (1.06 nm/s).

409

As regards the surface energetics of horizontal growth, we speculated that the (111)A

410

facets are energetically preferred to all other types of facets at low enough chemical

411

potentials, which is why they are most representative in the reshaped droplet-NW

ACS Paragon Plus Environment

30

Page 31 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

412

interface. On the other hand, it is known that the (111)B plane of GaAs has a lower energy

413

than the (111)A one (0.69 J/m2 against 0.82 J/m2 in contact with As-rich vapors according

414

to Ref. [43]). The same property should pertain when these facets are in contact with the

415

Ga liquid, consistent with the fact that the usual NW growth direction is B [44]. Our

416

type 1 structures nucleate on a (111)A facet, which is inward tapered for vertical NWs

417

and has a lower effective surface energy with respect to the outward tapered (111)B facet

418

[30]. The situation changes after nucleation of a horizontal NW section, where the

419

energetically preferred facet to introduce is the (111)B one, which allows for the stable

420

horizontal growth of type 1 NWs. This explains the unique growth mode whereby the

421

horizontal growth direction is maintained by alternating the (111)A and (111)B facets, and

422

should work equally well for other III-V NWs.

423

In conclusion, we have demonstrated a high level of control over the growth direction

424

of self-catalyzed GaAs NWs and found a novel type of twin-mediated growth mode, where

425

the growth interface oscillates between the two flat (111) facets with different polarity. By

426

controlling the NW density, annealing time, V/III ratio during the horizontal growth, and

427

the NW diameter, we are able to obtain 100% yield of regular 90° bent NW structures, in

ACS Paragon Plus Environment

31

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 32 of 50

428

which all the horizontal sections start at the pre-determined height. Our model describes

429

an interesting interplay between the surface energetics and growth kinetics, whereby the

430

horizontal growth is preferred at low chemical potentials achieved in the annealing stage.

431

It explains all the observed data and predicts that such morphology should be achievable

432

for any VLS III-V NWs whose growth front is initially truncated. Detailed structural

433

investigations reveal high crystal quality of the obtained structures, which makes them

434

extremely promising for quantum electronic and photonic applications.

435

ASSOCIATED CONTENT

436

Supporting Information contains: SEM analysis of NW top faceting; Additional SEM

437

images to support statistical analysis of type 1 and 2 populations; Description of different

438

structures found on the sample; Analysis of horizontal growth rate; Evolution of type 2

439

downward growth; Additional SEM analysis of growth interface during continued growth;

440

Additional SEM images of exceptions from type 1 and 2 growth due to short annealing or

441

non-optimal V/III BEP ratio; TEM analysis of NWs prior to annealing; Illustrative SEM

ACS Paragon Plus Environment

32

Page 33 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

442

images of the horizontal plane on which type 1 growth occurs; and Derivation of the

443

chemical potential decrease under annealing.

444

AUTHOR INFORMATION

445

Corresponding Author

446

* Email: [email protected]

447

Author Contributions

448

The manuscript was written through contributions of all authors. All authors have given

449

approval to the final version of the manuscript.

450

ACKNOWLEDGMENT

451

This work made use of Aalto University Nanomicroscopy Center (Aalto-NMC) and

452

Tampere University of Technology Microscopy center facilities. E.K, T.H and M.G

453

acknowledge financial support from the Academy of Finland projects NESP (decision No.

454

294630), NanoLight (decision 310985) and the Vilho, Yrjö and Kalle Väisälä Foundation

455

of the Finnish Academy of Science and Letters. H.V.A.G and Y.G.G. acknowledge

ACS Paragon Plus Environment

33

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 34 of 50

456

financial support from São Paulo Research Foundation, FAPESP (decisions grant

457

numbers 14/50513-7 and 16/10668-7). V.G.D. acknowledges the Ministry of Education

458

and Science of the Russian Federation for financial support under grant 14.587.21.0040

459

(project ID RFMEFI58717X0040).

460

REFERENCES

461

[1] B. Mayer, L. Janker, B. Loitsch, J. Treu, T. Kostenbader, S. Lichtmannecker, T.

462

Reichert, S. Morkötter, M. Kaniber, G. Abstreiter, C. Gies, G. Koblmüller, J.J. Finley,

463

Monolithically Integrated High-β Nanowire Lasers on Silicon, Nano Letters, Vol. 16, Iss.

464

1, 2016, pp. 152-156, DOI: 10.1021/acs.nanolett.5b03404

465

[2] K. Tomioka, J. Motohisa, S. Hara, K. Hiruma, T. Fukui, GaAs/AlGaAs Core Multishell

466

Manowire-Based Light-Emitting Diodes on Si, Nano Letters, Vol. 10, Iss. 5, 2010, pp.

467

1639-1644, DOI: 10.1021/nl9041774

468

[3] C. Patrik, T. Svensson, T. Mårtensson, J. Trägårdh, C. Larsson, M. Rask, D.

469

Hessman, L. Samuelson, J. Ohlsson, Monolithic GaAs/InGaP nanowire light emitting

ACS Paragon Plus Environment

34

Page 35 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

470

diodes on silicon, Nanotechnology, Vol. 19, Iss. 30, 2008, pp. 305201, DOI:

471

https://doi.org/10.1088/0957-4484/19/30/305201

472

[4] J. Wallentin, N. Anttu, D. Asoli, M. Huffman, I. Åberg, M.H. Magnusson, G. Siefer, P.

473

Fuss-Kailuweit, F. Dimroth, B. Witzigmann, H.Q. Xu, L. Samuelson, K. Deppert, M.T.

474

Borgström, InP nanowire array solar cells achieving 13.8% efficiency by exceeding the

475

ray optics limit, Science, Vol. 339, 2013, https://doi.org/10.1126/science.1230969

476

[5] S. Gazibegovic, D. Car, H. Zhang, S.C. Balk, J.A. Logan, M.W.A. de Moor, M.C.

477

Cassidy, R. Schmits, D. Xu, G. Wang, P. Krogstrup, R.L.M. Op het Veld, K. Zuo, Y. Vos,

478

J. Shen, D. Bouman, B. Shojaei, D. Pennachio, J.S. Lee, P.J. van Veldhoven, S. Koelling,

479

M.A. Verheijen, L.P. Kouwenhoven, C.J. Palmstrøm, E.P.A.M Bakkers, Epitaxy of

480

advanced nanowire quantum devices, Nature, Vol. 548, 2017, pp. 434 , DOI:

481

http://dx.doi.org/10.1038/nature23468

482

[6] J. Kang, Y. Cohen, Y. Ronen, M. Heiblum, R. Buczko, P. Kacman, R. Popovitz-Biro,

483

H. Shtrikman, Crystal Structure and Transport in Merged InAs Nanowires MBE Grown on

ACS Paragon Plus Environment

35

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

484

(001)

InAs,

Nano

Letters,

Vol.

485

http://dx.doi.org/10.1021/nl402571s

13,

Iss.

Page 36 of 50

11,

2013,

pp.

5190-5196,

DOI:

486

[7] F. Krizek, T. Kanne, D. Razmadze, E. Johnson, J. Nygård, C.M. Marcus, P.

487

Krogstrup, Growth of InAs Wurtzite Nanocrosses from Hexagonal and Cubic Basis, Nano

488

Letters,

489

http://dx.doi.org/10.1021/acs.nanolett.7b02604.

Vol.

17,

Iss.

10,

2017,

pp.

6090-6096,

DOI:

490

[8] T. Rieger, D. Rosenbach, D. Vakulov, S. Heedt, T. Schäpers, D. Grützmacher, M.I.

491

Lepsa, Crystal Phase Transformation in Self-Assembled InAs Nanowire Junctions on

492

Patterned Si Substrates, Nano Letters, Vol. 16, Iss. 3, 2016, pp. 1933-1941, DOI:

493

10.1021/acs.nanolett.5b05157

494

[9] D. Dalacu, A. Kam, D.G. Austing, P.J. Poole, Droplet Dynamics in Controlled InAs

495

Nanowire Interconnections, Nano Letters, Vol. 13, Iss. 6, 2013, pp. 2676-2681, DOI:

496

10.1021/nl400820w

497 498

[10] H. Potts, N.P. Morgan, G. Tütüncüoglu, M. Friedl, A. Fontcuberta, i Morral, Tuning growth

direction

of

catalyst-free

InAs(Sb)

nanowires

with

indium

droplets,

ACS Paragon Plus Environment

36

Page 37 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

499

Nanotechnology, Vol. 28, Iss. 5, 2017, pp. 054001, DOI: https://doi.org/10.1088/1361-

500

6528/28/5/054001

501

[11] Y. Luo, C. Chi, M. Jiang, R. Li, S. Zu, Y. Li, Z. Fang, Plasmonic Chiral

502

Nanostructures: Chiroptical Effects and Applications, Advanced Optical Materials, Vol. 5,

503

Iss. 16, 2017, pp. 1700040 DOI: 10.1002/adom.201700040

504

[12] G. Leahu, E. Petronijevic, A. Belardini, M. Centini, C. Sibilia, T. Hakkarainen, E.

505

Koivusalo, M. Rizzo Piton, S. Suomalainen, M. Guina, Evidence of Optical Circular

506

Dichroism in GaAs-Based Nanowires Partially Covered with Gold, Advanced Optical

507

Materials, Vol. 5, 2017, pp. 1601063, DOI: 10.1002/adom.201601063

508

[13] E. Petronijevic, M. Centini, A. Belardini, G. Leahu, T. Hakkarainen, C. Sibilia, Chiral

509

near-field manipulation in Au-GaAs hybrid hexagonal nanowires, Optics Express, Vol. 25,

510

Iss. 13, 2017, pp. 14148-14157, DOI: 10.1364/OE.25.014148

511

[14] A. Kelrich, O. Sorias, Y. Calahorra, Y. Kauffmann, R. Gladstone, S. Cohen, M.

512

Orenstein, D. Ritter, InP Nanoflag Growth from a Nanowire Template by in Situ Catalyst

ACS Paragon Plus Environment

37

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

513

Manipulation,

Nano

Letters,

514

10.1021/acs.nanolett.6b00648

Vol.

16,

Iss.

Page 38 of 50

4,

2016,

pp.

2837-2844,

DOI:

515

[15] J. Wang, S. Plissard, M.A. Verheijen, L. Feiner, A. Cavalli, Bakkers, Erik P. A. M.,

516

Reversible Switching of InP Nanowire Growth Direction by Catalyst Engineering, Nano

517

Letters, Vol. 13, Iss. 8, 2013, pp. 3802-3806, DOI: 10.1021/nl401767b

518

[16] S. Conesa-Boj, E. Russo-Averchi, A. Dalmau-Mallorqui, J. Trevino, E.F. Pecora, C.

519

Forestiere, A. Handin, M. Ek, L. Zweifel, L.R. Wallenberg, D. Rüffer, M. Heiss, D. Troadec,

520

L. Dal Negro, P. Caroff, A. Fontcuberta, i Morral, Vertical “III–V” V-Shaped

521

Nanomembranes Epitaxially Grown on a Patterned Si[001] Substrate and Their

522

Enhanced Light Scattering, ACS Nano, Vol. 6, Iss. 12, 2012, pp. 10982-10991, DOI:

523

10.1021/nn304526k

524

[17] M. de la Mata, R. Leturcq, S. Plissard, C. Rolland, C. Magén, J. Arbiol, P. Caroff,

525

Twin-Induced InSb Nanosails: A Convenient High Mobility Quantum System, Nano

526

Letters, Vol. 16, Iss. 2, 2016, pp. 825-833, DOI: 10.1021/acs.nanolett.5b05125

ACS Paragon Plus Environment

38

Page 39 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

527

[18] F. Lenrick, M. Ek, K. Deppert, L. Samuelson, L.R. Wallenberg, Straight and kinked

528

InAs nanowire growth observed in situ by transmission electron microscopy, Nano

529

Research, Vol. 7, Iss. 8, 2014, pp, DOI: https://doi.org/10.1007/s12274-014-0481-4.

530

[19] K. Hillerich, K.A. Dick, C. Wen, M.C. Reuter, S. Kodambaka, F.M. Ross, Strategies

531

To Control Morphology in Hybrid Group III–V/Group IV Heterostructure Nanowires, Nano

532

Letters, Vol. 13, Iss. 3, 2013, pp. 903-908, DOI: 10.1021/nl303660h

533

[20] T.V. Hakkarainen, A. Schramm, J. Mäkelä, P. Laukkanen, M. Guina, Lithography-

534

free oxide patterns as templates for self-catalyzed growth of highly uniform GaAs

535

nanowires

536

4484/26/27/275301

on

Si(111),

Nanotechnology,

Vol.

26,

2015,

DOI:

10.1088/0957-

537

[21] E. Koivusalo, T. Hakkarainen, M. Guina, Structural Investigation of Uniform

538

Ensembles of Self-Catalyzed GaAs Nanowires Fabricated by a Lithography-Free

539

Technique, Nanoscale Research Letters, Vol. 12, Iss. 1, 2017, pp. 192, DOI:

540

10.1186/s11671-017-1989-9

ACS Paragon Plus Environment

39

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 40 of 50

541

[22] E.S. Koivusalo, T.V. Hakkarainen, M.D. Guina, V.G. Dubrovskii, Sub-Poissonian

542

Narrowing of Length Distributions Realized in Ga-Catalyzed GaAs Nanowires, Nano

543

Letters, Vol. 17, Iss. 9, 2017, pp. 5350-5355, DOI: 10.1021/acs.nanolett.7b01766

544

[23] C. Colombo, D. Spirkoska, M. Frimmer, G. Abstreiter, A. Fontcuberta, i Morral, Ga-

545

assisted catalyst-free growth mechanism of GaAs nanowires by molecular beam epitaxy,

546

Physical Review B. Vol. 77, 2008, pp. 155326 DOI: 10.1103/PhysRevB.77.155326

547

[24] E. Uccelli, J. Arbiol, C. Magen, P. Krogstrup, E. Russo-Averchi, M. Heiss, G.

548

Mugny, F. Morier-Genoud, J. Nygård, J.R. Morante, A. Fontcuberta, i Morral, Three-

549

Dimensional Multiple-Order Twinning of Self-Catalyzed GaAs Nanowires on Si

550

Substrates, Nano Letters, Vol. 11, Iss. 9, 2011, pp. 3827-3832, DOI: 10.1021/nl201902w

551

[25] X. Yuan, P. Caroff, J. Wong-Leung, L. Fu, H.H. Tan, C. Jagadish, Tunable Polarity

552

in a III–V Nanowire by Droplet Wetting and Surface Energy Engineering, Advanced

553

Materials, Vol. 27, Iss. 40, 2015, pp. 6096-6103, DOI: 10.1002/adma.201503540

ACS Paragon Plus Environment

40

Page 41 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

554

[26] B. Wacaser, K. Deppert, L. Karlsson, L. Samuelson and W. Seifert, Growth and

555

characterization of defect free GaAs nanowires, Journal of Crystal Growth, Vol. 27, Iss.

556

2, 2006, pp. 504-508, DOI: //doi.org/10.1016/j.jcrysgro.2005.11.075

557

[27] Y. Zhang, Z. Sun, A.M. Sanchez, M. Ramsteiner, M. Aagesen, J. Wu, D. Kim, P.

558

Jurczak, S. Huo, L.J. Lauhon, H. Liu, Doping of Self-Catalyzed Nanowires under the

559

Influence of Droplets, Nano Letters, Vol. 18, Iss. 1, 2017, pp. 81-87, DOI:

560

10.1021/acs.nanolett.7b03366

561

[28] L. Li, D. Pan, X. Yu, H. So, J. Zhao, Manipulation of morphology and structure of

562

the top of GaAs nanowires grown by molecular-beam epitaxy, Journal of Semiconductors,

563

Vol. 38, Iss. 10, 2017, pp. 103001, DOI: https://doi.org/10.1088/1674-4926/38/10/103001

564

[29] D. Jacobsson, F. Panciera, J. Tersoff, M.C. Reuter, S. Lehmann, S. Hofmann, K.A.

565

Dick, F.M. Ross, Interface dynamics and crystal phase switching in GaAs nanowires,

566

Nature, Vol. 531, 2016, pp. 317 DOI: http://dx.doi.org/10.1038/nature17148

ACS Paragon Plus Environment

41

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 42 of 50

567

[30] V.G. Dubrovskii, Development of Growth Theory for Vapor–Liquid–Solid

568

Nanowires: Contact Angle, Truncated Facets, and Crystal Phase, Crystal Growth &

569

Design, Vol. 17, Iss. 5, 2017, pp. 2544-2548, DOI: 10.1021/acs.cgd.7b00076

570

[31] C.-Y. Wen, J. Tersoff, K. Hillerich, M.C. Reuter, J.H. Park, S. Kodambaka, E.A.

571

Stach, F.M. Ross, Periodically Changing Morphology of the Growth Interface in Si, Ge,

572

and GaP Nanowires, Physical Review Letters, Vol. 107, Iss. 2, 2011, pp. 025503, DOI:

573

https://doi.org/10.1103/PhysRevLett.107.025503

574

[32] F. Glas, J. Harmand, G. Patriarche, Why does wurtzite form in nanowires of III-V

575

zinc blende semiconductors? Phys Rev Lett, Vol. 99, Iss. 14, 2007, pp. 146101, DOI:

576

10.1103/PhysRevLett.99.146101

577

[33] F. Glas, M.R. Ramdani, G. Patriarche, J. Harmand, Predictive modeling of self-

578

catalyzed III-V nanowire growth, Physical Review B, Vol. 88, Iss. 19, 2013, pp. 195304,

579

DOI: https://doi.org/10.1103/PhysRevB.88.195304

ACS Paragon Plus Environment

42

Page 43 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

580

[34] V.G. Dubrovskii, Group V sensitive vapor–liquid–solid growth of Au-catalyzed and

581

self-catalyzed III–V nanowires, in: Journal of Crystal Growth, Vol. 440, Iss. 15, 2016, pp.

582

62–68, DOI: https://doi.org/10.1016/j.jcrysgro.2016.01.019

583

[35] T. Rieger, S. Heiderich, S. Lenk, M.I. Lepsa, D. Grützmacher, Ga-assisted MBE

584

growth of GaAs nanowires using thin HSQ layer, Journal of Crystal Growth, Vol. 353, Iss.

585

1, 2012, pp. 39-46. DOI: https://doi.org/10.1016/j.jcrysgro.2012.05.006

586

[36] M.R. Ramdani, J.C. Harmand, F. Glas, G. Patriarche, L. Travers, Arsenic Pathways

587

in Self-Catalyzed Growth of GaAs Nanowires, Crystal Growth & Design, Vol. 13, Iss. 1,

588

2013, pp. 91-96, DOI: 10.1021/cg301167g

589

[37] M. Federico, V.G. Dubrovskii, D. Rüffer, G. Tütüncüoğlu, Y. Fontana, A.

590

Fontcuberta, i Morral, Tailoring the diameter and density of self-catalyzed GaAs

591

nanowires on silicon, Nanotechnology, Vol. 26, Iss. 10, 2015, pp. 105603, DOI:

592

https://doi.org/10.1088/0957-4484/26/10/105603

ACS Paragon Plus Environment

43

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 44 of 50

593

[38] E. Billig, Growth of monocrystals of germanium from an undercooled melt,

594

Proceedings of the Royal Society of London.Series A.Mathematical and Physical

595

Sciences, Vol. 229, Iss. 1178, 1955, pp. 346-363, DOI: 10.1098/rspa.1955.0090

596

[39] D.R. Hamilton, R.G. Seidensticker, Propagation Mechanism of Germanium

597

Dendrites, Journal of Applied Physics, Vol. 31, Iss. 7, 1960, pp. 1165-1168 DOI:

598

10.1063/1.1735796

599

[40] A.J. Shahani, P.W. Voorhees, Twin-mediated crystal growth, Journal of Materials

600

Research,

Vol.

31,

Iss.

601

https://doi.org/10.1557/jmr.2016.308

19,

2016,

pp.

2936-2947,

DOI:

602

[41] A.D. Gamalski, P.W. Voorhees, C. Ducati, R. Sharma, S. Hofmann, Twin Plane Re-

603

entrant Mechanism for Catalytic Nanowire Growth, Nano Letters, Vol. 14, Iss. 3, 2014,

604

pp. 1288-1292, DOI: 10.1021/nl404244u

605

[42] D.S. Oliveira, L.H.G. Tizei, A. Li, T.L. Vasconcelos, C.A. Senna, B.S. Archanjo, D.

606

Ugarte, M.A. Cotta, Interaction between lamellar twinning and catalyst dynamics in

ACS Paragon Plus Environment

44

Page 45 of 50 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

607

spontaneous core–shell InGaP nanowires, Nanoscale, Vol. 7, Iss. 29, 2015, pp. 12722-

608

12727, DOI: 10.1039/C5NR02747K

609

[43] N. Moll, A. Kley, E. Pehlke, M. Scheffler, GaAs equilibrium crystal shape from first

610

principles, Physical Review B, Vol. 54, Iss. 12, 1996, pp. 8844-8855, DOI:

611

10.1103/PhysRevB.54.8844

612

[44] W. Kim, V.G. Dubrovskii, J. Vukajlovic-Plestina, G. Tütüncüoglu, L. Francaviglia, L.

613

Güniat, H. Potts, M. Friedl, J. Leran, A. Fontcuberta i Morral, Bistability of Contact Angle

614

and Its Role in Achieving Quantum-Thin Self-Assisted GaAs nanowires, Nano Letters,

615

Vol. 18, Iss. 1, 2018, pp. 49-57, DOI: 10.1021/acs.nanolett.7b03126.

ACS Paragon Plus Environment

45

(a) Self-catalyzed NW

Page 46 of 50 (c) Continued growth nm

1 2 3 4 5 6 7 8 9 10 11 12 13 (d) 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51

Nano Letters

Annealing

20

growth

(b)

1 µm

(e)

1 µm

(f)

1 µm Type 1

ACS Paragon Plus Environment

(g)

Type 2

(a) 47 of 50 Page 20 nm

Nano Letters -- -

(111)

20 nm

(c) 20 nm

- -

-

-- -

(101)

(100)

(111)

(010)

-

(011)

-

(101)

-

(110)

-

(111)

(101

)

(e) ) (101 -110 ) ( ---

(111) (010) -(111)

(011)

(011)

1 2 -3 (111) 4 5 6 -7 (811) 8 9 10 11 ) (d) 12 -110 ( 13 14 15 16 17 50 nm 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51

(b)

-- -

(111)

-- (f) (111) -(010) (111) (g) 109.5°

ACS Paragon Plus Environment

-

(011)

(h) 125.3°

-

(101)

(b)

(a)

Nano Letters

1

Page 48 of 502

3 1 -1 -1 5 nm 5 nm 2 31 4 2 5 6 -1 7 5 nm 8 9200 nm 10 11 (c) 12 13 14 15 16 {111}B 17 18 19 20 21 22 23 24 25 nm 25 26 27 (e) (d) 28 {111}B 29 30 31 32 {111}A {111}A 25 5 nm 33 nm 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 ACS Paragon Plus Environment 49 50 51

3

(a) Page 49 of 150

Nano Letters 1

1[110] 2 3 -1 5 nm 4 5 6 7 2 8 5 1/nm 9 10 11 12 -1 50 nm 2 5 nm 13 14 15 (b) 16 17 18 [117] 19 20 21 100 nm 22 23 24 -1 5 nm 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 ACS Paragon Plus Environment 49 50 51

4

3

3

4

5 nm

-1

(b)

T ype 2

T ype 1

80

80

Yield (%)

Yield (%)

100

1 60 2 40 3 20 4 0 5 6 (c) 7 100 (c) 8 80 9 10 60 11 40 12 20 13 0 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51

T ype 2

T ype 1

100

Nano (e) Letters2b 1b (g)

60 40 20

2.4E7

0

2.5E8

3.2E7

Nanowire density (cm-2) Type 2 Type 2b

Type 1 Type 1b

20

45

70

A nnealing time (s)

(f) (d)

Type 2, 45 s Type 2, 70 s

Type 1, 45 s Type 1, 70 s

100

Yield (%)

Yield (%)

80

7

9

V/III ratio

11

Page 50 of 50

Type 1 and 2 yields (%)

(a)

100 80 Type 1, lower density Type 2, lower density Type 1, higher density Type 2, higher density

60 40 20 0

60

70

40

80

85

90

Nanowire diameter (nm)

1 μm

20 0

75

75

80

85

90

Diameter (nm)

ACS Paragon Plus Environment

95