J. Phys. Chem. C 2010, 114, 3287–3291

3287

Diketopyrrolopyrrole-Based Donor-Acceptor Copolymers as Organic Sensitizers for Dye Sensitized Solar Cells Catherine Kanimozhi,† P. Balraju,‡ G. D. Sharma,*,‡,§ and Satish Patil*,† Solid State and Structural Chemistry Unit, Indian Institute of Science, Bangalore, India, 560012, Molecular Electronic and Optoelectronic DeVice Laboratory, Physics Department, JNV UniVersity, Jodhpur 342005, India, and Jaipur Engineering College, Kukas, Jaipur, India ReceiVed: September 29, 2009; ReVised Manuscript ReceiVed: December 25, 2009

In this work diketopyrrolopyrrole based copolymers (PDPP-BBT and TDPP-BBT) containing a donor-acceptor structural unit have been explored as organic sensitizers for quasi-solid state dye sensitized solar cells. Polymersensitized solar cells (PSSC) fabricated utilizing PDPP-BBT and TDPP-BBT as the active layer resulted in a typical power conversion efficiency of 1.43% and 2.41%, respectively. The power conversion efficiency of PSSCs based on TDPP-BBT with use of TiCl4-modified TiO2 photoanode was about 3.06%, attributed to the reduced back recombination reaction and more charge carriers in the external circuit. Introduction In recent years, dye-sensitized solar cells (DSSCs) based on inorganic/organic hybrid materials gained significant attention as an alternative to conventional silicon-based solar cells.1 These cells are very promising because of their low cost and high power conversion efficiency. The most widely used device architecture of conventional DSSCs typically contains the following key components: (i) a photoanode (mesoporous TiO2 film), (ii) a sensitizer (dye), (iii) an electrolyte/hole transporter, and (iv) a counter electrode. The overall power conversion efficiency of DSSC is affected by many factors including the nanostructure organization of TiO2.2 The ordered assembly of TiO2 provides percolating pathways for efficient electron transport to the electrode.3 In this context one-dimensional nanostructure was proven to be an effective way to increase the electron mobility by providing a large electron diffusion coefficient as compare to a TiO2 nanoparticle thin film.4 The Ru(4,4′-dicarboxylic acid-2,2′-bipyridine)2(NCS)2 complex is frequently used as a sensitizer, which is anchored to the surface of semiconducting TiO2 nanocrystals.5 In combination with mesoporous TiO2 thin film and various dyes as a sensitizer, power conversion efficiencies up to 11% have been achieved.1,6,7 But still there is a lot of room to explore new materials to overcome the drawbacks of existing sensitizers. For example, Gratzel and co-workers8-13 have explored a large variety of ruthenium complexes for the application in DSSCs and observed that thiocyanate-containing ruthenium(II) complexes perform well in nanocrystalline TiO2 DSSCs. These expensive and source limited ruthenium dyes can be replaced with environmentally friendly metal free organic sensitizers. As demonstrated by many research groups, the metal free organic sensitizers have many advantages such as lower cost, easier processing, and higher molar extinction coefficient.14-22 Most of the metal free organic sensitizers used for DSSCs show the character of both electron donor (D) and electron acceptor (A) linked with a π conjugation * To whom correspondence should be addressed. Tel: +91-80- 22932651. Fax: +91-80-23601310. E-mail: [email protected] and sharmagd_in@ yahoo.com. † Indian Institute of Science. ‡ JNV University. § Jaipur Engineering College.

bridge.23-31 Generally, organic sensitizers for excellent DSSCs are required to possess broadband intense spectral absorption in the visible light region and also have suited the lowest unoccupied molecular orbital (LUMO) energy level with the energy of the conduction band edge of nanocrystalline metal oxide semiconductor for efficient electron injection. Various groups have explored conjugated polymers as a sensitizer to meet all the above requirements.32-38 We directed our attention toward the synthesis of conjugated polymers containing donor-acceptor-donor structures and explore these materials as a sensitizer in solar cells. The energy levels (HOMO-LUMO) can be controlled by introducing alternating electron-rich and electron-deficient units in the polymer backbone. These materials were reported to have large absorption coefficients and tunable band gaps that cover the whole visible and near-IR spectrum.39,40 These properties are essential for DSSCs since the high efficiency can only be achieved when the excited state charge transfer from the polymer to the photoanode is allowed and the photo-oxidized polymer can be easily reduced by the electrolyte. Up to now, the efficiencies of DSSCs based on conjugated polymers remain low.41-43 In the present work, we have explored diketopyrrolopyrrole-based conjugated copolymers for the first time as a sensitizer in solar cells. Although the COOH group is a prime requisite to anchor on the TiO2 surface, other reactive functional group such as -OH or CdO are also capable of anchoring on the TiO2 surface.44,45 The polymers used in this study exhibit CdO groups in their backbone, hence the polymers can adsorb on the TiO2 surface, as a result electrons can be injected from the excited state of polymers into the conduction band of TiO2 as observed in the case of a carboxylated polythiophene.42 Fabrication of Polymer-Sensitized Solar Cells. TiO2 paste was prepared by slowly adding 1 g of TiO2 powder (P25, Degussa) to 0.2 mL of acetic acid, 1 mL of water, and 60 mL of ethanol, then this mixture was sonicated for 3 h. Finally Triton X-100 was added and the well-dispersed colloidal paste was coated over FTO glass by the doctor blade technique. The TiO2coated FTO electrodes were sintered at 450 °C for 30 min. The polymer was dissolved in chloroform solution and the TiO2 electrode was immersed into the solution for 10 h and after the sensitization, the electrode was washed. Quasi-solid state

10.1021/jp909353s  2010 American Chemical Society Published on Web 02/04/2010

3288

J. Phys. Chem. C, Vol. 114, No. 7, 2010

Kanimozhi et al.

Figure 2. Absorption spectra of thin films of (a) PDPP-BBT and (b) TDPP-BBT, (c) PDPP-BBT, and (d) TDPP-BBT adsorbed on TiO2 films.

Figure 1. Chemical structure of PDPP-BBT and TDPP-BBT.

polymer electrotyte was prepared by adding 0.083 g of P25 TiO2 powder, 0.1 g of LiI, 0.019 g of I2, 0.264 g of PEO, and 44 µL of 4-tert-butylpyridine to a (1:1) acetone/propylene carbonate solution. Finally the electrolyte was spin coated over the polymer-sensitized TiO2 electrode. To prepare the platinum counter electrode, H2PtCl6 solution in isopropanol (2 mg /mL) was deposited onto the FTO glass substrates and sintered at 400 °C for 30 min. The polymersensitized solar cells were fabricated by sandwiching the electrolyte between the polymer-sensitized photoanode and counter electrode. The current-voltage (J-V) characteristics of these devices were measured in the dark and under illumination by a semiconductor parameter analyzer (Keithley 4200-SCS). A xenon light source (Oriel, USA) was used to give an irradiance of 100 mW/cm2 (equivalent to AM1.5) at the surface of the device. The photoaction spectrum of the devices was measured with a monochromator (Spex 500 M, USA) and the resulting photocurrent was measured with a Keithley electrometer (model 6514), which is interfaced to the computer by LABVIEW software. Results and Discussion In the present study, we have used two diketopyrrolopyrrole (DPP)-based copolymers with different donor (phenyl and thiophene in DPP core) segments as organic sensitizers for the quasi-solid state DSSCs and the chemical structures are shown in Figure 1. The synthesis and characterization of these two copolymers, i.e., PDPP-BBT and TDPP-BBT, is reported elsewhere.46 Figure 2 shows the UV-visible spectra of PDPP-BBT and TDPP-BBT thin films deposited from chloroform solution. The absorption spectra of these copolymers cover the entire solar spectrum. The PDPP-BBT and TDPP-BBT exhibit an intramolecular charge transfer (ICT) band at 563 and 655 nm, respectively. Both the copolymers show broad absorption spectra with an extended absorption edge in the solid state. The optical band gaps of these polymers has been estimated from the absorption edge of the film, using Egop ) 1240/λ, and are 1.70

Figure 3. IPCE spectra of the quasi-solid state DSSCs based on PDDPBBT and TDDP-BBT as sensitizers.

and 1.43 eV for PDPP-BBT and TDPP-BBT, respectively. Figure 2 also shows the normalized absorption spectra of copolymers adsorbed on TiO2 film. In comparison to the absorption spectra of copolymer films, the absorption on the TiO2 film was broadened and slightly red-shifted in both cases, indicating that both copolymers were assembled on the TiO2 film in a monolayer state. The CdO groups at the backbone of the polymers are capable of anchoring on the surface of TiO2.53 Figure 3 shows the IPCE spectra obtained from DSSCs with use of PDPP-BBT and TDPP-BBT as sensitizers. The IPCE value (∼54%) for the TDPP-BBT based cell is higher than that of the PDPP-BBT based cell. The IPCE spectra of the TDPPBBT based device confirm the analysis for the absorption spectra of TDPP-BBT has a red-shifted and broadened light response as compared to that of PDPP-BBT. As the relatively narrowed absorption peak is one of the main drawbacks of organic dyes, this result indicates that the polymers could be potentially more effective sensitizers for DSSCs. The current-voltage characteristics of the quasi-solid state polymer-sensitized solar cells under illumination intensity of 100 mW/cm2 are shown in Figure 4. Both the devices were fabricated under identical conditions. The photovoltaic param-

Organic Sensitizers for Dye Sensitized Solar Cells

J. Phys. Chem. C, Vol. 114, No. 7, 2010 3289

Voc )

Figure 4. Current-voltage characteristics of the quasi-solid state DSSCs based on PDDP-BBT and TDDP-BBT sensitizers.

TABLE 1: Photovoltaic ParaMeters of the Quasi-Solid State Polymer-Sensitized Solar Cells sensitizer

Jsc,a mA/cm2

Voc,b V

FFc

η,d %

PDPP-BBT TDPP-BBT

4.5 6.3

0.59 0.66

0.54 0.58

1.43 2.41

a Short circuit current. conversion efficency.

b

Open circuit voltage. c Fill factor.

d

Power

eters estimated from these curves are summarized in Table 1. The power conversion efficiency of the solar cells with TDPPBBT as sensitizer is higher than that of PDPP-BBT. It has been attributed to the improved light harvesting ability of TDPPBBT as sensitizer due to excellent overlap with the solar spectrum and low band gap. The IPCE at a wavelength is the production of three efficiencies,47,48 i.e., IPCE (λ) ) LHE(λ)φinjηc, in which LHE (λ) is the light harvesting efficiency at a wavelength λ, φinj is the electron injection efficiency, and ηc is the collection efficiency of the injected electrons at the photoanode. ηc is associated with (i) the electron transport within the TiO2 network, (ii) the recombination of the injected electrons with the electrolyte (I3-), and (iii) the recombination of the injected electrons with the oxidized dye, and therefore should be independent of excitation wavelength. Since in both devices the photoanode, counter electrode, and polymer gel electrolyte are the same, the higher value of IPCE and power conversion efficiency are attributed to the improved light harvesting and the electron injection efficiency of the DSSCs based on TDPPBBT rather than PDPP-BBT. For both PDPP-BBT and TDPP-BBT, the LUMO energy level is energetically higher than the conduction band of TiO2 (-4.2 eV), and consequently, electron injection from the single excited state of PDPP-BBT and TDPP-BBT into TiO2 is energetically feasible. In addition, the oxidation potential of PDPP-BBT and TDPP-BBT is sufficiently more positive that the standard redox potential of iodine/iodide couple (0.34 V vs. Ag/AgCl), therefore, the photo-oxidized polymers could be efficiently reduced by the iodide ions. Moreover, the LUMO level of TDPP-BBT is higher than that of PDPP-BBT, resulting in more electron injection from TDPP-BBT into the conduction band of TiO2 as compared to PDPP-BBT. The open circuit voltage in the DSSCs can be expressed by following expression

( kTq ) ln[ n k [I ] ] Iinj

cb et 3

where k is Boltzmann’s constant, T is the absolute temperature, q is the electronic charge, Iinj is the injected electron flux from the sensitizers excited state into the conduction band of the TiO2, ncb is the density of the electron in the dark, ket is the electron recombination rate in the back reaction, and [I3-] is the concentration of iodide ions in the polymer gel electrolyte. Since more electrons are injected from the LUMO level of TDPPBBT into the conduction band of the TiO2, a higher open circuit voltage (Voc) for the quasi-solid state DSSCs based on TDPPBBT as compared to PDPP-BBT is observed. Effect of Modified Anode on the Performance of DSSCs Based on TDPP-BBT. Post treatment with TiCl4 was carried out according to the procedure reported in the literature.49 A 0.05 M TiCl4 aqueous solution was prepared in 2 M HCl solution. The sintered TiO2 films were immersed into this solution and stored in an oven at 70 °C for 30 min. After being rinsed with distilled water and dried, the electrode was again sintered at 450 °C in an oven for 30 min. The resulting TiO2 film was represented as TiCl4 modified films. The back electron transfer, i.e., electron leakage, which is the origin of the dark current, plays an important role in the photovoltaic performance of DSSCs.50 The reduction of electron leakage is necessary to enhance the power conversion efficiency of DSSCs. The existence of uncovered TiO2 sites in FTO, due to the porous nature of the TiO2 film, mainly originates in the dark current. The porous structure provides pathways for commonly used redox electrolyte (i.e., I3- species) to penetrate through the porous film and contact the uncovered FTO surface. At these uncovered TiO2 sites in FTO, the potential is thermodynamically favorable for the reduction of oxidative species, mainly I3-. This causes electron recombination and results in the loss of photocurrent. A comparison between the dark currents obtained from DSSCs with and without modified TiO2 electrode can provide a qualitative measure for the current leakage due to the back electron transfer.50-52 Figure 5 shows the onset potential of the dark current for the unmodified TiO2 film at 0.38 V, while for the modified TiO2 film, the onset potential shifted to 0.44 V. Furthermore, the dark current of the modified film increased much slower than that of the unmodified TiO2 film. The increase in the onset potential and reduction in the dark current demonstrated that the modification of TiO2 films reduces the uncovered surface area of the FTO surface forming a blocking layer and reduces the back electron transfer. Consequently, the suppression of electron leakage in the DSSCs with modified TiO2 films led to an enhancement in the photovoltaic performance. The performance of the quasi-solid state DSSCs with controlled film and modified films was characterized under the illumination intensity of 100 mW/cm2. The photocurrentvoltage (J-V) characteristics for the DSSC with modified films are shown in Figure 6. The photovoltaic parameters, i.e., short circuit photocurrent (Jsc), open circuit voltage (Voc), fill factor (FF), and power conversion efficiency (η) derived from the J-V characteristics are 7.16 mA/cm2, 0.68 V, 0.63, and 3.06%, respectively. The Jsc of the DSSC is mainly influenced by the dye loading amount and the electron transfer efficiency in the TiO2 film.50 We have estimated the amount of dye loading by desorbing the adsorbed dye from the photoelectrodes into a NaOH ethanolic solution and then measured the absorbance of the

3290

J. Phys. Chem. C, Vol. 114, No. 7, 2010

Figure 5. Dark current-voltage characteristics of quasi-solid state DSSCs based on TDPP-BBT as sensitizer with unmodified and modified TiO2 electrode.

Kanimozhi et al.

Figure 7. Variation of photocurrent with illumination intensity for quasi-solid state DSSCs based on TDPP-BBT as sensitizer with modified TiO2 electrode under illumination.

DSSCs with porous TiO2 and the modified TiO2 were directly proportional to Pin. This indicates that the current density for both DSSC’s was limited by the Pin, rather than the electron transfer processes, such as mass transport of I3- or electron transfer at the counter electrode. The slope for the modified TiO2 (i.e., 0.12) is 25% higher than that for the unmodified TiO2 (0.096) electrode, which indicates that 33% more electrons are collected from the same amount of photogenerated electrons at the FTO surface. This confirms that the use of the modified TiO2 electrode in DSSCs facilitates the electron transfer at the porous TiO2/FTO interface, resulting in an increase in collection efficiency. Conclusions

Figure 6. Current-voltage characteristics of quasi-solid state DSSCs based on TDPP-BBT as sensitizer with modified TiO2 electrode under illumination.

solution. The calculated amounts of TDPP-BBT loading from the unmodified film and modified film were 5.25 × 10-7and 5.30 × 10-7 mol/cm2, respectively. This shows that the modification of the TiO2 film does not significantly affect the adsorbed amount of TDPP-BBT. The similar dye loading amount implies that under the same illumination conditions, the concentration of photoinjected electron from the dye to the TiO2 conduction band will be the same. Therefore, the main factor influencing the Jsc of the DSSC investigated should be the charge recombination at FTO/electrolyte interfaces. In DSSCs with modified TiO2 film, the recombination sites (uncovered TiO2 sites in FTO) are reduced and subsequently the charge recombination in the DSSCs is effectively suppressed as seen in the dark current measurements (Figure 5). Therefore, the increase in the Jsc for the modified film may be associated with the improved electron transfer efficiency in the TiO2 film. As a result, more electrons are transferred to the external circuit. Since the amount of the photogenerated electrons is directly proportional to the incident illumination intensity, the variation of short circuit photocurrent (Jsc) with the illumination intensity (Pin) can be used to obtain information about the amount of photogenerated electrons contributing to the photocurrent and also electron transfer kinetics. Figure 7 shows that Jsc of the

Diketopyrrolopyrrole-based copolymers PDPP-BBT and TDPP-BBT, containing a donor-acceptor structural unit, were synthesized and used as organic sensitizer to fabricate the quasisolid state DSSCs. The DSSCs yield an overall power conversion efficiency about 1.43% and 2.41% for PDPP-BBT and TDBBT-BBT, respectively. Better power conversion efficiency of TDPP-BBT based DSSCs comes form the red-shifted and broadened absorption spectrum for the TDPP-BBT relative to PDPP-BBT and also more electron injection from the LUMO level of TDPP-BBT into the conduction band of TiO2 as it lies more positive as compared to that of PDPP-BBT. The overall power conversion efficiency has been further increased when the TiCl4-modified TiO2 electrode photoanode is used to fabricate the DSSCs. This increase has been attributed to the reduction in the back recombination of injected electrons with I3- in the electrolyte. Acknowledgment. The authors acknowledge the Department of Science and Technology, New Delhi, India for financial support. References and Notes (1) O’Regan, B.; Gratzel, M. Nature 1991, 353, 737. (2) Paronyan, T. M.; Kechiantz, A. M.; Lin, M. C. Nanotechnology 2008, 19, 115201. (3) O’Regan, B.; Durrant, J.; Sommeling, P.; Bakker, N. J. J. Phys. Chem. C 2007, 111, 14001. (4) Schmidt-Mende, L.; Bach, U.; Humphrey-Baker, R.; Horiuchi, T.; Miura, H.; Ito, S.; Uchida, S.; Gratzel, M. AdV. Mater. 2005, 17, 813. (5) Wang, P.; Klein, C.; Humphrey-Baker, R.; Zakeeruddin, S. M.; Gratzel, M. J. Am. Chem. Soc. 2005, 127, 808.

Organic Sensitizers for Dye Sensitized Solar Cells (6) Ito, S.; Miura, H.; Uchida, S.; Takata, M.; Sumioka, K.; Liska, P.; Comte, P.; Pe’chy, P.; Gratzel, M. Chem. Commun. 2008, 5194. (7) Karthikeyan, C. S.; Wietasch, H.; Thelakkat, M. AdV. Mater. 2007, 19, 1091. (8) Jang, S. R.; Yum, J. H.; Klein, C.; Kim, K. J.; Wagner, P.; Officer, D.; Gratzel, M.; Nazeeruddin, M. K. J. Phys. Chem. C 2009, 113, 1998. (9) Choi, H.; Baik, C.; Kim, S.; Kang, M. S.; Xu, X.; Kang, H. S.; Kang, S. O.; Ko, J.; Nazeeruddin, M. K.; Gratzel, M. New J. Chem. 2008, 32, 2233. (10) Gao, F. F.; Wang, Y.; Zhang, J.; Shi, D.; Wang, M. K.; HumphryBaker, R.; Wang, P.; Zakeeruddin, S. M.; Gratzel, M. Chem. Commun. 2008, 2635. (11) Wang, M.; Chen, P.; Humphry-Baker, R.; Zakeeruddin, S. M.; Gratzel, M. ChemPhysChem 2009, 10, 290. (12) Lee, C.; Yum, J. H.; Choi, H.; Kang, S. O.; Ko, J.; HumphryBaker, R.; Gratzel, M.; Nazeeruddin, M. K. Inorg. Chem. 2008, 47, 2267. (13) Gratzel, M. Nature 2001, 414, 338. (14) Yao, Q. H.; Shan, L.; Li, F. Y.; Yin, D. D.; Huang, N. H. J. Chem. 2003, 27, 1277. (15) Hara, K.; Sato, T.; Katoh, R.; Furube, A.; Ohga, Y.; Shinpo, A.; Suga, S.; Sayama, K.; Sugihara, H.; Arakawa, H. J. Phys. Chem. B 2003, 107, 597. (16) Wang, Z. S.; Koumura, N.; Cui, Y.; Takahashi, M.; Sekiguchi, H.; Mori, A.; Kubo, T.; Furube, A.; Hara, K. Chem. Mater. 2008, 20, 3993. (17) Hara, K.; Tachibana, Y.; Ohga, Y.; Shinpo, A.; Suga, S.; Sayama, K.; Sugihara, H.; Arakawa, H. Sol. Energy Mater. Sol. Cells 2003, 77, 89. (18) Tian, H. N.; Yang, X. C.; Chen, R. K.; Zhang, R.; Hagfeldt, A.; Sun, L. C. J. Phys. Chem. C 2008, 112, 11023. (19) Zhan, W. H.; Wu, W. J.; Hua, J. L.; Jing, Y. H.; Meng, F. S.; Tian, H. Tetrahedron Lett. 2007, 48, 2461. (20) Qin, H.; Wenger, S.; Xu, M. F.; Gao, F. F.; Jing, X. Y.; Wang, P.; Zakeeruddin, S. M.; Gra¨tzel, M. J. Am. Chem. Soc. 2008, 130, 9202. (21) Chen, Z. G.; Li, F. Y.; Huang, C. H. Curr. Org. Chem. 2007, 11, 1241. (22) Pei, J.; Peng, S.; Shi, J.; Liang, Y.; Tao, Z.; Liang, J.; Chen, J. J. Power Sources 2009, 187, 620. (23) Li, G.; Zhou, Y. F.; Cao, Y. B.; Bao, P.; Jiang, K. J.; Lin, Y.; Yang, L. M. Chem. Commun. 2009, 2201. (24) Baheti, A.; Tyagi, P.; Justin Thomas, K. R.; Hsu, Y. C.; T’suen Lin, J. J. Phys. Chem. C 2009, 113, 8541. (25) Wang, M.; Chen, P.; Humphry-Baker, R.; Zakeeruddin, S. M.; Gra¨ tzel, M. ChemPhysChem 2009, 10, 290. (26) Ito, S.; Miura, H.; Uchida, S.; Takata, M.; Sumioka, K.; Liska, P.; Comte, P.; Pe’chy, P.; Gra¨tzel, M. Chem. Commun. 2008, 5194. (27) Hwang, S.; Lee, J. H.; Park, C.; Lee, H.; Kim, C.; Park, C.; Lee, M. H.; Lee, W.; Park, J.; Kim, K.; Park, N. G.; Kim, C. Chem. Commun. 2007, 4887. (28) Liu, X. Z.; Zhu, R.; Zhang, Y.; Liu, B.; Ramakrishna, S. Chem. Commun. 2008, 3789. (29) Velusamy, M.; Thomas, K. R. J.; Lin, J. T.; Hsu, Y. C.; Ho, K. C. Org. Lett. 2005, 7, 1899.

J. Phys. Chem. C, Vol. 114, No. 7, 2010 3291 (30) Zhao, G.; Wu, G.; He, C.; Bai, F. Q.; Xi, H.; Zhang, H. X.; Li, Y. J. Phys. Chem. C 2009, 113, 2636. (31) Tao, Y.; Wang, Q.; Shang, Y.; Yang, C.; Ao, L.; Qin, J.; Ma, D.; Shuai, Z. Chem. Commun. 2009, 77. (32) Hong, J. S.; Joo, M.; Vittal, R.; Kim, K. J. J. Electrochem. Soc. 2002, 149, E493. (33) Mwaura, J. K.; Zhao, X.; Jiang, H.; Schanze, K. S.; Reynolds, J. R. Chem. Mater. 2006, 18, 6109. (34) Kim, Y. G.; Walker, J.; Samuelson, L. A.; Kumar, J. Nano Lett. 2003, 3, 523. (35) Senadeera, G. K. R.; Kitamura, T.; Wada, Y.; Anagida, S. Y. Sol. Energy Mater. Sol. Cells 2005, 88, 315. (36) Kim, Y. G.; Walker, J.; Samuelson, L. A.; Kumar, J. Appl. Phys. Lett. 2003, 83, 5470. (37) Liu, X.; Zhu, R.; Zhang, Y.; Liu, B.; Ramakrishna, S. Chem. Commun. 2008, 3789. (38) Ohshita, J.; Matsukawa, J.; Hara, M.; Kunai, A.; Kajiwara, S.; Ooyama, Y.; Harima, Y.; Kakimoto, M. Chem. Lett. 2008, 37, 316. (39) Bernius, M. T.; Inbasekaran, M.; O’Brien, J.; Wu, W. S. AdV. Mater. 2000, 12, 1737. (40) Kraft, A.; Grimsdale, A. C.; Holmes, A. B. Angew. Chem., Int. Ed. 1998, 37, 402. (41) Nakamura, K.; Kitamura, T.; Wada, Y.; Yanagida, S. Appl. Phys. Lett. 2003, 83, 5470. (42) Mwaura, J. K.; Zhao, X. Y.; Jiang, H.; Schanze, K. S.; Reynolds, J. R. Chem. Mater. 2006, 18, 6109. (43) Taranekar, P.; Qiao, Q. Q.; Jiang, H.; Ghiviriga, I.; Schanze, K. S.; Reynolds, J. R. J. Am. Chem. Soc. 2007, 129, 8958. (44) Mishra, A.; Fischer, M. K. R.; Bauerle, P. Angew. Chem, Int. Ed. 2009, 48, 2474. (45) Balrajua, P.; Suresh, P.; Manish, K.; Roy, M. S.; Sharma, G. D. J. Photochem. Photobiol. C 2009, 206, 53–63. (46) Kanimozhi, C.; Balraju, P.; Sharma, G. D.; Patil, S. J. Phys. Chem. B, in press. (47) Zhang, X. H.; Li, C.; Wang, W. B.; Cheng, X. X.; Wang, X. S.; Zhang, B. W. J. Mater. Chem. 2007, 17, 42. (48) Peter, L. J. Electroanal. Chem. 2007, 599, 233–240. (49) Sommeling, P. M.; O’Regan, B. C.; Haswell, R. R.; Smit, H. J. P.; Bakker, N. J.; Smits, J. J. T.; Kroon, J. M.; Van oosmalen, J. A. M. J. Phys. Chem. B 2006, 110, 19191–19197. (50) Ito, S.; Liska, P.; Comte, P.; Charvet, R.; Pechy, P.; Bach, U.; Schmidt-Mende, L.; Zakeeruddin, S. M.; Kay, A.; Nazeeruddin, M. K.; Gratzel, M. Chem. Commun. 2005, 4351–4353. (51) Hart, J. N.; Menzies, D.; Cheng, Y. B.; Simon, G. P.; Spiccia, L. TiO2 C. R. Chim. 2006, 9, 622. (52) Yu, H.; Zhang, S.; Zhao, H.; Will, G.; Liu, P. Electrochim. Acta 2009, 54, 1319. (53) Edvinsson, T.; Li, C.; Pschirer, N.; Jan Schoneboom., J.; Eickemeyer, F.; Sens, R.; Boschloo, G.; Herrmann, A.; Klaus Mu¨llen, K.; Hagfeldt, A. J. Phys. Chem. C 2007, 111, 15137.

JP909353S