Article

“Dispersion-Assembly” Approach to Synthesize ThreeDimensional Graphene/Polymer Composite Aerogel as a Powerful Organic Cathode for Rechargeable Li and Na Batteries Yu Zhang, Yanshan Huang, Guanhui Yang, Fanxing Bu, Ke Li, Imran Shakir, and Yuxi Xu ACS Appl. Mater. Interfaces, Just Accepted Manuscript • Publication Date (Web): 20 Apr 2017 Downloaded from http://pubs.acs.org on April 21, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Dispersion-Assembly” Approach to Synthesize Three-Dimensional Graphene/Polymer Composite Aerogel as a Powerful Organic Cathode for Rechargeable Li and Na Batteries Yu Zhang,1 Yanshan Huang,1 Guanhui Yang,1 Fanxing Bu,1 Ke Li,1 Imran Shakir,2* and Yuxi Xu1* 1

State Key Laboratory of Molecular Engineering of Polymers, Department of Macromolecular

Science, Fudan University, China. 2

Sustainable Energy Technologies Center, College of Engineering, King Saud University, Riyadh

11421, Kingdom of Saudi Arabia KEYWORDS Three-dimensional graphene, PAQS composite, organic cathode, lithium ion batteries, sodium ion batteries

ABSTRACT Polymer cathode materials are promising alternatives to inorganic counterparts for both lithium ion batteries (LIBs) and sodium ion batteries (SIBs) due to their high theoretical capacity, adjustable molecular structure and strong adaptability to different counter-ions in batteries, etc.

ACS Paragon Plus Environment

1

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 27

However, they suffer from poor practical capacity and low rate capability because of their intrinsically poor conductivity. Herein,

we report the synthesis of self-assembled

graphene/poly(anthraquinonyl sufide) (PAQS) composite aerogel (GPA) with efficient integration of three-dimensional (3D) graphene framework with electroactive PAQS particles via a novel dispersion-assembly strategy, which can be used as a free-standing flexible cathode upon mechanical pressing. The entire GPA cathode can deliver a highest capacity of 156 mAh g-1 at 0.1 C (1 C = 225 mAh g-1) with an ultrahigh utilization (94.9%) of PAQS and exhibit an excellent rate performance with 102 mAh g-1 at 20 C in LIBs. Furthermore, the flexible GPA film has also been tested as cathode for SIBs and demonstrated a high-rate capability with 72 mAh g-1 at 5 C and an ultralong cycling stability (71.4% capacity retention after 1000 cycles at 0.5 C) which has rarely been achieved before. Such excellent electrochemical performance of GPA as cathode for both LIBs and SIBs could be ascribed to the fast redox kinetics and electron transportation within GPA resulting from the interconnected conductive framework of graphene and the intimate interaction between graphene and PAQS through an efficient wrapping structure. This approach opens up a universal way to develop cathode materials for powerful batteries with different metal-based counter electrodes. 1. Introduction The application of rechargeable batteries is now recognized as an effective way to reduce our consumption of fossil fuels and decrease the CO2 emission, thereby alleviating the greenhouse effect.1-3 Lithium ion batteries (LIBs) have become the dominant energy storage device for powerful portable electronic devices as well as electrical vehicles over the past nearly two decades.4-6 However, the commercial LIBs meet their ceiling of the specific capacity which is heavily restricted by the limited choices of inorganic cathode materials in addition to suffering

ACS Paragon Plus Environment

2

Page 3 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

from the environmental issue brought by the use of transitional metals.7-9 Meanwhile, the development of sodium ion batteries (SIBs) would be the most attractive alternatives for portable rechargeable systems in concern of their abundance of sodium resources and excellent capacity (1166 Ah kg-1 ) of Na+/Na for the redox reactions, but is also restricted by the limited cathode materials and it is not easy to migrate the excellent Li+ intercalation compounds to SIBs electrodes because of the size restriction caused by the large different crystal structures.10-16 In this respect, new cathode materials going beyond to traditional materials which are mainly based on transition-metal oxides are perused. As alternatives, organic cathode materials draw much attention in recent years because they are not restricted by counter-ion as well as capable of providing high theoretical capacity owing to the multielectron reactions and their structures can be functionalized so that their operate voltages, solubility, and ionic conductivity can be tuned.9, 16-20

In addition, a polymer with highly electroactive functional groups and a stable skeleton can

potentially be a powerful cathode candidate because its redox kinetics are intrinsically faster than inorganic intercalation cathodes and it can avoid the unwanted dissolution in aprotic electrolyte which is always suffered by small organic molecules.21, 22 Among various organic polymers, conjugated carbonyl polymers have received intensive attention in the past few years due to their higher theoretical capacity.8, 17, 20, 23 For example, poly(anthraquinonyl sulfide) (PAQS) shows an excellent theoretical capability of 225 mAh g-1 and potentially has better stability compared with other organic cathode materials because the polymers based on the thioether bond are completely insoluble in any solvent.21, 22 However, the low mass density and intrinsically poor electronic conductivity of the polymers result in low utilization and poor rate performance.8, 17, 24 To surmount the electrical insulation of polymers, considerable amount of conductive additives which are electrochemically inactive are usually

ACS Paragon Plus Environment

3

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 27

introduced to create electrodes, leading to significantly compromised electrochemical performance of the whole electrode and greatly impeding the practical use of organic active materials.

9, 16, 21, 22, 24, 25

To address these issues, it has been demonstrated that combing

graphene, carbon nanotubes or other nanocarbon materials which have high conductivity and large surface area with polymer is an effective approach for achieving advanced organic cathodes.26-29 As a result, some polymer/nanocarbon composites with improved performances have been prepared by method of ball milling and in-situ polymerization.30-35 Despite these achievements, many of them still show unsatisfactory capacities for the entire electrodes. Briefly, the method of ball milling limits the improvement of the conductivity of the electrode and influence the performance of active polymer because binders are typically electronic insulators as well as electrochemically inactive and cannot provide an effective interaction between conductive agent and active polymer because of the limited contact area. The method of in-situ polymerization is a promising strategy to develop favorable structures with strong coupling between conductive agent and in-situ grown active materials as well as high mass loading. However, the application range of this method is limited because it is unavoidable that serious side reactions may occur in many reaction systems during the process of in-situ polymerization, which may obtain unwanted structures of polymer and conductive agent in the final product, resulting in poor performance when used in batteries. Therefore, it remains a significant challenge to develop an effective and a universal method to construct advanced polymer cathodes with high active material content and excellent electrochemical performance for both LIBs and SIBs, which are essential for real-word applications. Herein, we report a universal dispersion-assembly method that is a combination of sonication and reduction process to prepare self-assembled graphene/PAQS composite aerogel (GPA)

ACS Paragon Plus Environment

4

Page 5 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

which can be mechanically pressed into highly conductive and flexible film and used directly as a free-standing cathode. The dispersion-assembly method can make PAQS dispersed uniformly on graphene surface and effectively wrapped by graphene sheets. Remarkably, due to the intrinsic structural advantages of three-dimensional (3D) graphene framework and high mass loading of PAQS as well as intimate interaction between them which enables rapid charge transfer, GPA was directly used as a binder-free cathode in LIB, delivering a very high discharge capacity of 156 mAh g-1 at 0.1 C with an ultrahigh utilization of PAQS (94.9%) and an impressive rate performance of 102 mAh g-1 at a high current density of 20 C. Moreover, GPA demonstrated an outstanding cycle stability with 84.1% capacity retention after a long term of 1000 cycles at 0.5 C. The electrochemical performance of GPA cathode is superior to those of most organic cathodes that have been reported before. Furthermore, GPA can also be used as a cathode for SIB, gaining a high initial capacity of 157 mAh g-1 with a utilization ratio (91.1%) of PAQS nearly equal with that in LIB and a superior rate capability with 72 mAh g-1 at 5 C which is among the highest value that has been achieved for sodium-organic batteries when normalized by the whole electrode mass. It also exhibits an excellent cycling stability with 71.4% capacity retention after 1000 cycles at 0.5 C. Such outstanding electrochemical performances achieved by a single polymer cathode for both LIB and SIB simultaneously have rarely been demonstrated in previous studies. 2. Experimental 2.1 Synthesis of PAQS. The PAQS was synthesized using the method reported by Song and his coworkers in 2009.21 Briefly, 1, 5 -dichloranthraquinone (0.554 g, 0.002 mol) were first dissolved in 5 mL 1-methyl-2pyrrolidinone (NMP). The solution was then sonicated for 20 min by a probe sonicator.

ACS Paragon Plus Environment

5

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 27

Subsequently, anhydrous sodium sulfide (0.156 g, 0.002 mol) was added into the mixture and the reaction proceeded under refluxing and stirring overnight. The product was centrifuged after cooling to room temperature, washed several times with deionized water and acetone, and then dried at 120 °C for 12 h. 2.2 Synthesis of GPA composites Graphene oxide (GO) was synthesized using a modified Hummers method.36 We synthesized three different GPA composites with different weight ratios. First, we added 24 mg, 14 mg and 9 mg PAQS into 5 ml 2 mg/ml GO/NMP solution, respectively. The mixtures of PAQS and GO suspension in NMP were sonicated for 2 h followed by adding 150 µL 1 M sodium ascorbate aqueous solution to reduce the GO into 3D graphene at 95 °C for 1.5 h without stirring and obtain the composites simultaneously. The as-prepared samples were dipped into DI water and washed for 3 times. Finally, the composites were frozen for 2 h and dried under vacuum for 12 h to obtain GPA composites with mass ratios of 2:8, 3:7, 4:6 between graphene and PAQS, respectively. 2.3 Characterizations SEM measurements were performed on a Zeiss Ultra-55 field emission scanning electron microscope. TEM studies were conducted on a FEI Tecnai G2 20TWIN electron microscope at an operating voltage of 200 kV. FTIR spectral measurements were performed using a PerkinElmer Paragon 1000. Raman measurements were recorded on an Invia/Reflrx Lasser MicroRaman spectroscope (Horiba Jobin Yvon, Franch) with excitation laser beam wavelength of 532 nm. XRD analysis was performed on a Rigaku D/Max 2500 X-ray diffractometer with CuK radiation (k = 1.54 Å) at a generator voltage of 40 kV and a generator current of 20 mA with a scanning speed of 5° min-1 from 10 to 50°.

ACS Paragon Plus Environment

6

Page 7 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

2.4 Electrochemical Measurements Electrochemical experiments were carried out in CR2016 coin-type cells. The GPA composites were directly pressed and cut into pieces as the working electrodes for LIBs and SIBs with an areal mass loading of ~2.3 mg/cm2 and the GPA film samples were cut into rectangle for the conductivity measurement by the four-probe system (Keithley 6221 and 6514). The pristine PAQS electrode was prepared by mixing pure PAQS, carbon black (Super-P) and poly (vinyl difluoride) (PVDF) at a weight ratio of 60:30:10 and pasted on glass slide for conductivity measurement or pure Al foil (99.6%) with an areal mass loading of ~2 mg/cm2 for SIBs and LIBs test. For LIB fabrication, the metallic lithium foil was used as the counter electrode. The electrolyte was 1 M LiTFSI in 1,2-dimethoxy ethane (DME)/1,3-dioxolane (DOL) (1:2 by volume ratio). The polypropylene (PP) film (Cellgard 2400) was used as the separator. For SIB fabrication, the metallic sodium foil was used as the counter electrode. The electrolyte was 0.1 M NaPF6 in DME/DOL (1:1 by volume ratio). The glass fiber was used as the separator. The cells were assembled in an argon-filled glove box with the concentrations of moisture and oxygen below 0.1 ppm. CV was performed at a scan rate of 1 mV/s on a CHI 660D electrochemical workstation (CH Instruments). The galvanostatic charge–discharge experiments were tested using an LANHE instruments testing system in the potential range from 1.5 to 3.5 V for LIBs and 1.2-2.8 V for SIBs at different current rates. 3. Results and Discussion The typical synthesis process of GPA composite is shown in Figure 1a. We synthesized PAQS firstly and mixed it with graphene oxide (GO) in N-methylpyrrolidone (NMP) to form a homogenous dispersion upon sonication. Then, it formed a gel after the system was heated at 95 °C for 1.5 h without stirring using sodium ascorbate as reducing agent. Meanwhile, the solution

ACS Paragon Plus Environment

7

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 27

became clear indicating the brown PAQS particles were effectively encapsulated into the graphene sheets (Figure 1b). Finally, GPA composite was obtained after a freeze-drying process (Figure 1c). The mass percentage of PAQS in typical GPA was determined to be about 70% by the thermogravimetric analysis (TGA, Figure S1a). The self-assembled graphene aerogel (SGA) was also prepared by the same method without adding PAQS.

Figure 1. (a) Schematic of the synthesis process of GPA; (b) Homogenous mixture of GO and PAQS in NMP and reduction and self-assembly of GO to form 3D graphene framework with PAQS particle encapsulated; (c) The freeze-dried aerogel of graphene/PAQS composite; (d) Preparation of a flexible binder-free GPA film electrode by mechanical pressing; (e) Synthetic route to PAQS; (f) The reversible redox mechanisms of PAQS in LIBs and SIBs.

The formation of PAQS and GPA were confirmed through the Fourier-transform infrared spectra (FTIR) (Figure 2a). The appearance of 1129 and 1413 cm-1 bands in the FTIR spectra, which can be assigned to the ring-sulfur stretching and ring stretching of sulfur disubstituted

ACS Paragon Plus Environment

8

Page 9 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

aromatic ring respectively, as the evidence of the successful synthesis of PAQS.21, 37 For GPA composite, the C=C vibration from unsaturated sp2 C=C bonds (1619 cm-1) is significant downshifted, indicating a charge transfer between the PAQS and graphene due to the intimate interaction between them. X-ray diffraction (XRD) pattern of GPA composite (Figure 2b) shows two peaks at 2θ = 23.2° and 24.8°, same as that of pure PAQS, indicating the particles of PAQS were successfully wrapped by the graphene sheets in the 3D graphene framework. Raman spectra of PAQS and GPA composite also demonstrate the PAQS particles have been effectively embedded during the process of synthesizing composite (Figure 2c). The Raman peaks at 1667 and 1585 cm-1 correspond to the C=O of anthraquinonyl group in PAQS and the peaks at 1335 and 1597 cm-1 are D and G bonds from graphene. Compared to that of the pure graphene aerogel, a little bit red shift can be found in the Raman spectra of GPA also supporting the charge transfer between the three-dimensional graphene framework and PAQS.38 Furthermore, we also tested the Raman spectra of samples with different mass ratio of PAQS (Figure S1b). It is easy to find that, with more PAQS we added in the precursor mixture, the peaks of PAQS in the finally product becomes more obvious in the spectra indicating that this method allows plenty of PAQS to be impregnated into the graphene.39, 40

Figure 2. (a) FTIR of SGA, PAQS and GPA; (b) XRD patterns of PAQS, GPA and SGA; (c) Raman of SGA, PAQS and GPA.

ACS Paragon Plus Environment

9

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 27

Figure 3. (a) SEM image of pristine PAQS; (b-c) TEM images of GPA with different magnification; (d) Low- and (e) high-magnification SEM images of GPA; (f-i) Elemental mapping images of GPA (by SEM): Carbon (g), oxygen (h), and sulfur (i) distribution in the selected area. The morphology and microstructure of pristine PAQS and as-prepared GPA composites were characterized by field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM), respectively. The particles of pristine PAQS with sizes ranging from hundreds of nanometers to several micrometers were stacking seriously (Figure 3a). TEM images of GPA (Figures 3b, c) show polymer particles (100-200 nm) were uniformly dispersed on graphene surface and wrapped by graphene sheets, indicating ultrasonication can effectively

ACS Paragon Plus Environment

10

Page 11 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

disperse PAQS particles in NMP solution and decrease the particle size to some extent and these particles can be effectively encapsulated within graphene sheets via the π-π stacking interaction during the 3D self-assemble of graphene. The FESEM images of GPA (Figures 3d, e) show an interconnected 3D graphene framework with pore sizes ranging from several micrometers to submicrometers which is beneficial for electrolyte penetration and enables fast ion transportation. Both SEM and TEM images revealed that most PAQS particles are uniformly wrapped between the graphene walls, indicating the efficient integration of 3D graphene framework with active PAQS particles. Furthermore, the elemental mappings of the GPA composite for C, O and S distribution also demonstrate that the PAQS particles were homogeneously distributed in the composite (Figures 3f-i), which were consistent with FESEM and TEM results.

ACS Paragon Plus Environment

11

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 27

Figure 4. (a-b) Cross section SEM images of the pressed GPA film; (c) SEM image of the interior microstructure of the pressed GPA film; (d) I-V curves of GPA composite film at its initial, folded and recovered states. The as-prepared GPA with a thickness of ~4 mm could be greatly compressed to form ~30 µm thick GPA film (Figure 4a) with a packing density of 0.75 g/cm3 calculated by dividing the areal mass loading (2.3 mg/cm2) by thickness and a conductivity of 3.6 S/cm. The 3D continuous porous network was well maintained in the GPA film and the PAQS particles were still wrapped by the graphene sheets (Figures 4b, c), which indicated the intrinsically excellent mechanical stability of GPA. Furthermore, after folding the GPA film and unfolding it, there was no obvious change in the electrical conductivity, indicating a superior mechanical flexibility for the GPA film (Figure 4d). Together, these structure characterizations confirm the intimate interaction between the unique 3D porous graphene and small PAQS particles, which can afford rapid charge transfer from graphene substrate to PAQS. The mechanically strong and electrical conductive GPA film was directly used as cathode material for the electrochemical test in cointype cells with lithium foil as the counter electrode (Figure 5). For comparison, the pristine PAQS electrode was fabricated by mixing 60% active material, 30% super P and 10% PTFE and denoted as C-PAQS in which the particle sizes of PAQS are about 1 µm and relatively larger than that in GPA (Figure S2a). The cyclic voltammetry (CV) was conducted to compare the lithium-ion intercalation/de-intercalation behaviors of C-PAQS and GPA between 1.2 V and 3.2 V at a scan rate of 1 mV/s (Figure 6a). For C-PAQS, the reduction phase was observed at around 2.07 V corresponding to the insertion of Li ions, while the oxidation phase was located at around 2.52 V, reflecting the de-insertion of Li ions and consistent with the charge-discharge profiles of C-PAQS (Figure S2b). For GPA, the reduction and oxidation phase are around 2.11 V and 2.39

ACS Paragon Plus Environment

12

Page 13 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

V, indicating the smaller polarization and the faster reaction rate for the GPA. The typical charge/discharge profiles of GPA displayed an average discharge plateau of ~2.15 V and charge plateau of ~2.35 V (Figure 6b), which were consistent with the CV studies. Meanwhile, the capacity and discharge plateau of GPA gradually decreased with the increase of current density because of the unavoidable electrochemical polarization. The electrochemical impedance spectroscopy (EIS) was further performed (Figure S3). The high-to-medium frequency region of semicircle was assigned to the charge-transfer resistance (Rct) between electrode and electrolyte and an inclined line in the low frequency part corresponding to Warburg impedance (Zw) associated with lithium-ion diffusion in the electrode.41 It can be found that GPA exhibited a lower charge-transfer resistance (Rct) and this can be ascribed to the increased conductivity mainly caused by the structure advantages of 3D graphene network (Table S1).

Figure 5. Schematic drawing of the Li (Na)/GPA cell during discharge. On the anode side, metallic Li or Na are transformed into Li+ or Na+ during discharging, and the reverse reaction takes place during charging. On the cathode side, Li+ or Na+ are insertion and de-insertion into GPA during discharge and charge reactions, respectively.

ACS Paragon Plus Environment

13

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 27

When considering the performance of a whole electrode, the proportion between active material and conductive additives can influence the performance seriously. In general, with the increased mass loading of active materials and reduced the proportion of conductive agent, the conductivity of whole electrode will be decreased, leading to a poor electrochemical performance. However, although electrical conductivity of electrode and utilization ratio of active material can be improved obviously by adding a large amount of conductive additive, the electrochemical performance of electrode may still unsatisfactory because the capacity was compromised by the typically electrochemical inactive conductive additive. Therefore, in order to explore the best ratio between graphene and active material for the optimum performance, we further synthesized another two GPA composites with different weight ratios of PAQS and they were noted as GPA-H (80 wt.% PAQS) and GPA-L (60 wt.% PAQS) whose mass loadings were characterized by TGA (Figure S1b).

Figure 6. Electrochemical characterization of GPA composites and C-PAQS as LIB cathodes. (a) CV curves of PAQS and its composites at a scan rate of 1 mV/s; (b) Charge/discharge profiles of GPA at different C-rates. The specific capacity is calculated based on the mass of the whole

ACS Paragon Plus Environment

14

Page 15 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

composite; (c) Rate performance of PAQS and its composites at different C-rates. The specific capacity is calculated based on the mass of the whole composite; (d) Cycling performance of GPA at 0.5 C.

CV curves of GPA-H and GPA-L are displayed in Figure 6a. It is important to note that the polarization of GPA becomes weaker and the rate of electron transfer is improved significantly with the increasing content of graphene, evidenced by smaller separation between the redox peaks. The EIS of GPA-H and GPA-L were also tested and indicated that the Rct became lower with the increased amount of graphene (Figure S3 and Table S1). The rate performance of all kinds of electrodes were tested and shown in Figure 6c. C-PAQS delivered a discharge capacity of 108 mAh g-1 at 0.1 C corresponding to a PAQS utilization ratio of 80% considering that the theoretical capacity of PAQS is 225 mAh g-1 based on a two-redox process (Figure 1f) (detailed calculation method see Supporting Information). In contrast, the GPA exhibited a much higher capacity of 156 mAh g-1 at 0.1 C, based on the total mass of the entire electrode. Under the same testing condition, three-dimensional graphene aerogel itself showed a low capacity of only about 22 mAh g-1 and thus made a negligible contribution (~6.6 mAh g-1) to the capacity based on its weight percentage of 30 wt.% in the composite (Figure S4). Therefore, the utilization ratio of PAQS in the GPA was determined to be 94.9%, much higher than that of C-PAQS. The discharge capacity of GPA at an ultrahigh current density of 20 C still remained 65.4% of that at 0.1 C, delivering 102 mAh g-1, whereas C-PAQS showed nearly no electrochemical activity at 20 C. The GPA demonstrates much better rate capability than C-PAQS at each current density, which may be largely attributed to fast electrode reaction of PAQS by its efficient integration with 3D graphene framework. Correspondingly, GPA shows much higher conductivity than C-

ACS Paragon Plus Environment

15

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 27

PAQS (1.1 S/cm). The prominent performance of our GPA was higher than any other PAQS electrodes and most other polymer electrodes in LIBs (Table S2). The high-rate performance of GPA-H and GPA-L were studied under the same test conditions. As shown in Figure 6c, the capacities of GPA-H and GPA-L at 0.1 C are 171 mAh g-1 and 139 mAh g-1, corresponding to the utilization ratios of 92.6% and 96.4%, respectively. As expected, with the graphene content increasing, the utilization ratio of PAQS tends to be higher, because more graphene in the GPA composites means more ions and electron transport pathways to achieve full usage of PAQS. The discharge capacity of GPA-L at an exceptionally high current density of 30 C still remained 60% of that at 0.1 C, delivering 83.1 mAh g-1 which is slightly higher than that of GPA, indicating that rate performance can be improved obviously with the help of the increased content of graphene. Meanwhile, GPA-H showed much lower electrochemical activity at the same current density. These results demonstrate that it is the highly interconnected 3D graphene framework with the wrapping function that ensures excellent conductivity and efficient ion transport to enable rapid and adequate electrochemical reaction of PAQS. When considering the capacity performance of whole electrode, it is obvious that the performance of GPA is better than GPA-H at almost all current densities while GPA-L is just slightly better than GPA until the current density achieves 30 C, indicating that the capacity performance cannot be improved obviously by continuing to decrease the proportion of PAQS when its weight mass has been reached 70 wt.% in the composite. Correspondingly, GPA-L showed a little higher conductivity (3.9 S/cm) than GPA (3.6 S/cm), which is much higher than that of GPA-H (2.6 S/cm). Therefore, the proportion of PAQS in GPA is optimum among these three different composites in the aspect of comprehensive electrochemical performance.

ACS Paragon Plus Environment

16

Page 17 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

The sustainable cycling performance of GPA composite was further highlighted by the outstanding galvanostatic discharge/charge performance after 1000 cycles at 0.5 C. As shown in Figure 6d, the initial reversible capacity of GPA cathode was 138 mAh g-1 and reached 157 mAh g-1 after several cycles of activation. After 500 cycles, the capacity of GPA still remained 142 mAh g-1, corresponding to 90% of the highest capacity. Furthermore, after a long term of 1000 deep cycles, the capacity still reached as high as 132 mAh g-1 with a decay rate of 0.015 mAh g-1 cycle-1, and thus the capacity remains 84.1% at the 1000th cycle. Such excellent cycling stability has rarely been demonstrated in previous work and indicates that the wrapping structure of PAQS particles by the 3D graphene framework can accommodate the volume change and promote the structural integrity of PAQS during the charge/discharge process.

Figure 7. (a) Nyquist plots for C-PAQS, GPA and GPA after 1000 cycles at 0.5 C; (b) Low- and (c) high-magnification SEM images of the GPA after 1000 cycles in a rechargeable lithium battery; (d) TEM image of GPA after 1000 cycles in a rechargeable lithium battery.

ACS Paragon Plus Environment

17

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 27

To explain the outstanding electrochemical performance of GPA, ESI was performed and the morphology and microstructure of the GPA after 1000 cycles in LIBs were characterized by SEM and TEM (Figure 7). From Figure 7a and Table S1, it can be found that the increase in the Rct of GPA was not obvious after 1000 cycles (Figure 7a). SEM and TEM images revealed that most PAQS particles in GPA were still uniformly distributed and intact in 3D graphene frameworks after 1000 cycles (Figures 7b, c), illustrating the ideal protection of PAQS polymer by the 3D graphene framework. These results can be attributed to two main reasons. First, ultrasonic method can promote the polymer particles to be dispersed uniformly and prevent accumulation among the particles, so as to effectively reduces the resistance as well as facilitate the charge transfer in the electrode. Meanwhile, the polymer particles can be tightly wrapped by the graphene sheets via π-π stacking interaction during 3D self-assembly process of graphene so that the graphene can protect the polymer particles and improve the conductivity of them effectively. Second, the mechanically strong 3D graphene with hierarchical porous can not only offer a continuous network of open channels for efficient ion transport but also provide multidimensional electron transport pathway to achieve rapid and exhaustive electrochemical reaction of active polymers.

ACS Paragon Plus Environment

18

Page 19 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 8. Electrochemical characterization of GPA and C-PAQS as SIB cathodes. (a) The CV curves of PAQS and GPA as cathodes for SIBs at a scan rate of 1 mV/s; (b) Charge/discharge profiles of GPA at different C-rates; (c) The rate performance of PAQS and GPA. The specific capacity is calculated based on the whole mass of the composite; (d) The cycle performance of GPA at 0.5 C. The specific capacity is calculated based on the whole mass of the composite. As mentioned before, organic compounds show little sensitivity to the counter-ion theoretically due to their “soft” molecular structure.35 Therefore, we also evaluated the electrochemical performance of GPA as the SIB cathode and expected desirable performance. As demonstrated in Figure 8a, the CV curve of pristine PAQS clearly exhibits two pairs of redox peaks at 1.53/1.71 V and 1.85/2.19 V respectively, which are associated with the reduction of the first and second carbonyl groups to the anions and are consistent with the charge-discharge profiles of CPAQS (Figure S5a). Similarly, GPA shows two redox peaks at 1.58/1.79 V and 1.92/2.18 V at a scan rate of 1 mV/s and the curves are quite consistent with the charge-discharge profiles (Figure 8b) in which there are two slope voltage curves of about 1.75 and 2.16 V in the charge profile, and two slope voltage curves of about 1.54 and 1.82 V in the discharge profile. It indicates that

ACS Paragon Plus Environment

19

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 27

the uniquely designed GPA electrode also exhibits obviously faster electrochemical kinetics for sodium-ion transportation. In contrast to with the CV curves in LIBs, the two pairs of redox peaks from GPA and C-PAQS are well separated in SIBs, probably due to a larger steric and/or coulombic repulsion for the second step Na+ association when the first Na+ ion is associated with the anthraquinonyl group of the polymer.24 The GPA electrode delivered a very high reversible specific capacity of 157 mAh g-1 at 0.1 C based on the mass of entire electrode and achieved a high PAQS utilization ratio of 91.1% which is comparable to that in LIBs (Figure 8c). SGA itself achieved a discharge capacity of only 45 mAh g-1 at the same current density (Figure S5b) and also made a negligible contribution about 13.5 mAh g-1 to the reversible capacity of GPA. By contrast, the reversible capacity of the C-PAQS electrode reached only 93 mAh g-1 at 0.1 C based on the whole mass of the electrode, corresponding to a much lower PAQS utilization ratio of 68.9%. At a high current density of 5 C, GPA can still achieve a high specific capacity of 72 mAh g-1 which is higher than almost all organic cathodes when normalized by the mass of the whole electrode (Table S3). Furthermore, the GPA electrode exhibited an excellent cycling performance (Figure 8d). It elivered an initial discharge capacity of 138.3 mAh g-1 and retained a capacity of 98.7 mAh g-1 (71.4% of its initial capacity) after 1000 cycles with a Coulombic efficiency near to 100%. Such outstanding cycling stability is much better than those of most reported sodium-organic batteries and potentially satisfy the demand of practical use. Similar to that in LIB, the increase in the Rct of GPA was not significant after 1000 deep cycles in SIB (Figure S6 and Table S4). The similarly prominent electrochemical performance of GPA for SIBs indicates that with our method it is simple to transplant promising organic LIBs cathodes to SIBs despite of the large ionic radius difference between Na+ and Li+ which is highly desirable for the metal-organic batteries.

ACS Paragon Plus Environment

20

Page 21 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

As mentioned above, in-situ polymerization is a promising strategy to produce highperformance composite materials, however, suffers from unavoidable side reactions in many reaction systems. We have also tried to synthesize graphene/PAQS composite using in-situ polymerization and perform the same electrochemical characterizations (Figure S7). We found that it was difficult to obtain well-defined structure of PAQS as well as 3D graphene network which leads to a much worse performance than GPA composite and could be ascribed to the serious side reactions between GO and Na2S during the reaction process. 4. Conclusion In conclusion, we have developed a simple dispersion-assembly method to prepare GPA composites as a highly flexible high-performance cathode for both LIB and SIB. This methodology can create a unique porous structure with the PAQS particles uniformly dispersed within the skeleton of 3D graphene framework and tightly encapsulated by graphene sheets to ensure rapid charge transfer between graphene and PAQS and fast charge transport throughout the whole composite. The flexible and binder-free GPA can be directly used as LIB cathode and deliver a capacity of 102 mAh g-1 at a high current density of 20 C and excellent cycle stability with 84.1% retention after 1000 cycles at 0.5 C. Furthermore, GPA composites also show superior rate capability with 72 mAh g-1 at 5 C and excellent cycling stability with 71.4% retention after 1000 cycles at 0.5 C when used as SIBs cathode, which have rarely been reported in previous work. We believe this universal dispersion-assembly strategy can be extended to synthesize a wide range of 3D graphene/polymer composites with controlled microstructures as high-performance electrodes for LIBs and SIBs as well as other promising battery systems, such as Al-ion battery, K-ion battery and Mg-ion battery. ASSOCIATED CONTENT

ACS Paragon Plus Environment

21

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 27

Supporting Information Further details of the in-situ polymerization, EIS measurements, electrochemical performance, FTIR and Raman spectroscopy measurements are supplied as Supporting Information. AUTHOR INFORMATION Corresponding Author E-mail: [email protected] [email protected] Author Contributions The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript. ACKNOWLEDGMENT We acknowledge support by the Program for Professor of Special Appointment (Eastern Scholar) at Shanghai Institutions of Higher Learning (No. TP2015002), and the National Natural Science Foundation of China (51673042). We also like to extend our sincere appreciation to the Deanship of Scientific Research at the King Saudi University for its funding of this research wor k through the International Research Group Project No: IRG14-19. REFERENCES (1) Armand, M.; Tarascon, J. M. Building Better Batteries. Nature 2008, 451, 652-657. (2) Dunn, B.; Kamath, H.; Tarascon, J. M. Electrical Energy Storage for the Grid: A Battery of Choices. Science 2011, 334, 928-935.

ACS Paragon Plus Environment

22

Page 23 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

(3) Bruce, P. G.; Scrosati, B.; Tarascon, J. M. Nanomaterials for Rechargeable Lithium Batteries. Angew. Chem., Int. Ed. 2008, 47, 2930-2946. (4) Bruce, P. G.; Freunberger, S. A.; Hardwick, L. J.; Tarascon, J. M. Li-O2 and Li-S Batteries with High Energy Storage. Nat. Mater. 2012, 11, 19-29. (5) Luntz, A. C.; McCloskey, B. D. Nonaqueous Li–Air Batteries: A Status Report. Chem. Rev. 2014, 114, 11721-11750. (6) Goodenough, J. B.; Park, K. S. The Li-Ion Rechargeable Battery: A Perspective. J. Am. Chem. Soc. 2013, 135, 1167-1176. (7) Wu, H.; Yang, Q.; Meng, Q.; Ahmad, A.; Zhang, M.; Zhu, L.; Liu, Y.; Wei, Z. A Polyimide Derivative Containing Different Carbonyl Groups for Flexible Lithium Ion Batteries. J. Mater. Chem. A 2016, 4, 2115-2121. (8) Song, Z.; Zhou, H. Towards Sustainable and Versatile Energy Storage Devices: an Overview of Organic Electrode Materials. Energy Environ. Sci. 2013, 6, 2280-2301. (9) Song, Z.; Qian, Y.; Zhang, T.; Otani, M.; Zhou, H. Poly(benzoquinonyl sulfide) as a HighEnergy Organic Cathode for Rechargeable Li and Na Batteries. Adv. Sci. 2015, 2, 1500124. (10) Sakaushi, K.; Hosono, E.; Nickerl, G.; Zhou, H.; Kaskel, S.; Eckert, J. Bipolar Porous Polymeric Frameworks for Low-Cost, High-Power, Long-Life All-Organic Energy Storage Devices. J. Power Sources 2014, 245, 553-556. (11) Sakaushi, K.; Nickerl, G.; Wisser, F. M.; Nishio-Hamane, D.; Hosono, E.; Zhou, H.; Kaskel, S.; Eckert, J. An Energy Storage Principle using Bipolar Porous Polymeric Frameworks. Angew. Chem., Int. Ed. 2012, 51, 7850-7854.

ACS Paragon Plus Environment

23

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 27

(12) Yabuuchi, N.; Kubota, K.; Dahbi, M.; Komaba, S. Research Development on Sodium-Ion batteries. Chem. Rev. 2014, 43, 11636-11628. (13) Sakaushi, K.; Hosono, E.; Nickerl, G.; Gemming, T.; Zhou, H.; Kaskel, S.; Huang, R.; Jiang, J. -S. Aromatic Porous-Honeycomb Electrodes for a Sodium-Organic Energy Storage Device. Nat. Commun. 2013, 4, 1485. (14) Dong, X.; Chen, L.; Liu, J.; Haller, S.; Wang, Y.; Xia, Y. Environmentally-Friendly Aqueous Li (or Na)-Ion Battery with Fast Electrode Kinetics and Super-Long Life. Sci. Adv. 2016, 2, e1501038. (15) Palomares, V.; Serras, P.; Villaluenga, I.; Hueso, K. B.; Carretero-Gonzalez, J.; Rojo, T. Na-Ion Batteries, Recent Advances and Present Challenges to Become Low Cost Energy Storage Systems. Energy Environ. Sci. 2012, 5, 5884-5901. (16) Lei, K.; Li, F.; Mu, C.; Wang, J.; Zhao, Q.; Cheng, C.; Chen, J. High K-storage Performance Based on the Synergy of Dipotassium Terephthalate and Ether-Based Electrolytes Energy Environ. Sci. 2017, 10, 552-557. (17) Schon, T. B.; McAllister, B. T.; Li, P. -F.; Seferos, D. S. The Rise of Organic Electrode Materials for Energy Storage. Chem. Soc. Rev. 2016, 45, 6345-6404. (18) Pan, B.; Huang, J.; Feng, Z.; Zeng, L.; He, M.; Zhang, L.; Vaughey, J. T.; Bedzyk, M. J.; Fenter, P.; Zhang, Z.; Burrell, A. K.; Liao, C. Polyanthraquinone-Based Organic Cathode for High-Performance Rechargeable Magnesium-Ion Batteries. Adv. Energy Mater. 2016, 6, 1600140. (19) Song, Z.; Qian, Y.; Gordin, M. L.; Tang, D.; Xu, T.; Otani, M.; Zhan, H.; Zhou, H.; Wang, D. Polyanthraquinone as a Reliable Organic Electrode for Stable and Fast Lithium Storage. Angew. Chem., Int. Ed. 2015, 54, 13947-13951. (20) Haeupler, B.; Wild, A.; Schubert, U. S. Carbonyls: Powerful Organic Materials for Secondary Batteries. Adv. Energy Mater. 2015, 5, 1402034.

ACS Paragon Plus Environment

24

Page 25 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

(21) Song, Z.; Zhan, H.; Zhou, Y. Anthraquinone Based Polymer as High Performance Cathode Material for Rechargeable Lithium Batteries. Chem. Commun. 2009, 4, 448-450. (22) Jian, Z. L.; Liang, Y. L.; Rodriguez-Perez, I. A.; Yao, Y.; Ji, X. L. Poly(anthraquinonyl sulfide) Cathode for Potassium-Ion Batteries. Electrochem. Commun. 2016, 71, 5-8. (23) Oltean, V. A.; Renault, S.; Valvo, M.; Brandell, D. Sustainable Materials for Sustainable Energy Storage: Organic Na Electrodes. Mater. 2016, 9, 27. (24) Deng, W.; Liang, X.; Wu, X.; Qian, J.; Cao, Y.; Ai, X.; Feng, J.; Yang, H. A Low Cost, All-Organic Na-Ion Battery Based on Polymeric Cathode and Anode. Sci. Rep. 2013, 3, 2671. (25) Xu, W.; Read, A.; Koech, P. K.; Hu, D.; Wang, C.; Xiao, J.; Padmaperuma, A. B.; Graff, G. L.; Liu, J.; Zhang, J. -G. Factors Affecting the Battery Performance of Anthraquinone-Based Organic Cathode Materials. J. Mater. Chem. 2012, 22, 4032-4039. (26) Wang, M.; Duan, X. D.; Xu, Y. X.; Duan, X. F. Functional Three-Dimensional Graphene/Polymer Composites. ACS Nano 2016, 10, 7231-7247. (27) Song, Z.; Xu, T.; Gordin, M. L.; Jiang, Y. -B.;Bae, I. -T.;Xiao, Q.; Zhan, H.; Liu, J.; Wang, D. Polymer–Graphene Nanocomposites as Ultrafast-Charge and -Discharge Cathodes for Rechargeable Lithium Batteries. Nano Lett. 2012, 12, 2205-2211. (28) Geim, A. K.; Novoselov, K. S. The Rise of Graphene. Nat. Mater. 2007, 6, 183-191. (29) Yang, G.; Zhang, Y.; Huang, Y.; Shakir, M. I.; Xu, Y. Incorporating Conjugated Carbonyl Compounds into Carbon Nanomaterials as Electrode Materials for Electrochemical Energy Storage. Phys. Chem. Chem. Phys. 2016, 18, 31361-31377. (30) Wu, H. P.; Shevlin, S. A.; Meng, Q. H.; Guo, W.; Meng, Y. N.; Lu, K.; Wei, Z. -X.; Guo, Z. -X. Flexible and Binder-Free Organic Cathode for High-Performance Lithium-Ion Batteries. Adv. Mater. 2014, 26, 3338-3343.

ACS Paragon Plus Environment

25

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 26 of 27

(31) Meng, Y.; Wu, H.; Zhang, Y.; Wei, Z. A Flexible Electrode Based on a ThreeDimensional Graphene Network-Supported Polyimide for Lithium-Ion Batteries. J. Mater. Chem. A 2014, 2, 10842-10846. (32) Ahmad, A.; Wu, H.; Guo, Y.; Meng, Q.; Meng, Y.; Lu, K.; Liu, L.; Wei, Z. A Graphene Supported Polyimide Nanocomposite as a High Performance Organic Cathode Material for Lithium Ion Batteries. RSC Adv. 2016, 6, 33287-33294. (33) Wu, H.; Meng, Q.; Yang, Q.; Zhang, M.; Lu, K.; Wei, Z. Large-Area Polyimide/SWCNT Nanocable Cathode for Flexible Lithium-Ion Batteries. Adv. Mater. 2015, 27, 6504-6510. (34) Wu, H.; Wang, K.; Meng, Y.; Lu, K.; Wei, Z. An Organic Cathode Material Based on a Polyimide/CNT Nanocomposite for Lithium Ion Batteries. J. Mater. Chem. A 2013, 1, 63666372. (35) Song, Z. P.; Zhan, H.; Zhou, Y. H. Polyimides: Promising Energy-Storage Materials. Angew. Chem., Int. Ed. 2010, 49, 8444-8448. (36) Xu, Y.; Bai, H.; Lu, G.; Li, C.; Shi, G. Flexible Graphene Films via the Filtration of WaterSoluble Noncovalent Functionalized Graphene Sheets. J. Am. Chem. Soc. 2008, 130, 5856-5857. (37) Piaggio, P.; Cuniberti, C.; Dellepiane, G.; Campani, E.; Gorini, G.; Masetti, G.; Novi, M.; Petrillo, G. Vibrational-Spectra and Assignment of Poly-(para-phenylene sulfide) and Its Oligomers. Spectrochim. Acta, Part A 1989, 45, 347-356. (38) Chen, W. F.; Li, S. R.; Chen, C. H.; Yan, L. F. Self-Assembly and Embedding of Nanoparticles by In Situ Reduced Graphene for Preparation of a 3D Graphene/Nanoparticle Aerogel. Adv. Mater. 2011, 23, 5679-5683. (39) Zhang, K.; Guo, C.; Zhao, Q.; Niu, Z.; Chen, J. High-Performance Organic Lithium Batteries with an Ether-Based Electrolyte and 9,10-Anthraquinone (AQ)/CMK-3 Cathode. Adv. Sci. 2015, 2, 1500018.

ACS Paragon Plus Environment

26

Page 27 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

(40) Guo, C.; Zhang, K.; Zhao, Q.; Peia, L.; Chen, J. High-Performance Sodium Batteries with the 9,10-Anthraquinone/CMK-3 Cathode and an Ether-Based Electrolyte. Chem. Commun. 2015, 51, 10244-10247. (41) Wang, G. X.; Yang, L.; Chen, Y.; Wang, J. Z.; Bewlay, S.; Liu, H. K. An Investigation of Polypyrrole-LiFePO4 Composite Cathode Materials for Lithium-Ion Batteries. Electrochim. Acta 2005, 50, 4649-4654.