Communication pubs.acs.org/cm
Synthesis of Zn3As2 and (CdyZn1−y)3As2 Colloidal Quantum Dots Benjamin A. Glassy, Nathan L. Lai, and Brandi M. Cossairt* Department of Chemistry, University of Washington, Box 351700, Bagley Hall, Seattle, Washington 98195-1700, United States S Supporting Information *
Q
maintained colloidal stability and a resolved lowest energy excitonic transition (LEET) was observed to shift as a function of time and temperature (Figure 1A).28 Further characterization showed that these particles are weakly luminescent (quantum yield