Biomimetic Hydrogen Evolution: MoS2 Nanoparticles as Catalyst for Hydrogen Evolution Berit Hinnemann, Poul Georg Moses, Jacob Bonde, Kristina P. Jørgensen, Jane H. Nielsen, Sebastian Horch, Ib Chorkendorff, and Jens K. Nørskov* Center for Atomic-scale Materials Physics, Department of Physics, NanoDTU, Technical UniVersity of Denmark, DK-2800 Lyngby, Denmark Received January 24, 2005; E-mail: [email protected]

The electrochemical hydrogen evolution process whereby protons and electrons are combined into molecular hydrogen is catalyzed most effectively by the Pt group metals.1 The interest in hydrogen evolution catalysts is currently increasing, as molecular hydrogen, H2, is being considered as an energy carrier.2 Unlike the hydrocarbon fuels used today, hydrogen produces only water during oxidation, for instance in a fuel cell. For hydrogen to be a real alternative to hydrocarbons, it must be produced in a sustainable fashion. One possibility is to use sunlight directly or indirectly (through wind power, for instance) to split water.2 This requires an efficient catalyst for hydrogen evolution, preferably based on materials that are cheap and abundant. It is therefore important to find alternatives to the Pt group metals. Hydrogenases and nitrogenases are also effective catalysts for the hydrogen evolution process3,4 even though the catalytically active site of these enzymes contains the much less noble metals Fe, Ni, and Mo. Recently it has become possible to anchor hydrogenase to an electrode surface,5 and considerable progress has been made in the synthesis of compounds in solution resembling the hydrogenase active site and showing activity for hydrogen evolution.6 In the present communication, we use density functional calculations to guide us to a new inorganic analogue of the other hydrogenproducing enzyme, nitrogenase. We analyze the difference between the metallic and the biological catalysts and show that in terms of being able to stabilize intermediates involving atomic hydrogen they have very similar properties. This allows us to identify a parameter determining whether a certain compound will be suitable as a catalyst in electrochemical hydrogen evolution, and it provides an efficient way to search for new systems. Most water-splitting processes rely on electrochemical hydrogen evolution 2H+ + 2e- f H2 in the final step. The hydrogen evolution reaction must in the first step involve bonding of hydrogen to the catalyst H+ + e- +* f H*, where * denotes a site on the surface able to bind to hydrogen. The second step is the release of molecular hydrogen through one of the two processes:1 2H* f H2 + 2* or H+ + e- + H* f H2 + *. Using density functional theory (DFT) calculations, we can elucidate the thermochemistry (which is independent on the precise mechanism of the second step) of the reaction; see Figure 1.7 By calculating the free energy of atomic hydrogen bonding to the catalyst, one can compare different metal surfaces as catalysts. For a chemical process to proceed at or around room temperature, no reaction step can be associated with large changes in the free energy. This immediately excludes the metals that form strong bonds to atomic hydrogen (Ni and Mo in Figure 1) as good catalysts because the hydrogen release step will be slow. Metals that do not bind to atomic hydrogen (Au in Figure 1) are also excluded because here the proton/electron-transfer step will be thermodynamically uphill 5308

9

J. AM. CHEM. SOC. 2005, 127, 5308-5309

Figure 1. Calculated free energy diagram for hydrogen evolution at a potential U ) 0 relative to the standard hydrogen electrode at pH ) 0. The free energy of H+ + e- is by definition the same as that of 1/2 H2 at standard conditions. The free energy of H atoms bound to different catalysts is then found by calculating the free energy with respect to molecular hydrogen including zero-point energies and entropy terms. The comparison of different elemental metals is taken from ref 7. The results for hydrogenase are from ref 11. The included result for MoS2 is the free energy required to increase the hydrogen coverage from 25 to 50%; see Figure 2.

Figure 2. (Left) Nitrogenase FeMo cofactor (FeMoco) with three hydrogen atoms bound at the equatorial µ2S sulfur atoms. (Middle) Hydrogenase active site with one hydrogen atom bound. The structure is taken from ref 11. (Right) MoS2 slab with sulfur monomers present at the Mo edge. The coverage is 50%, i.e., hydrogen is bound at every second sulfur atom. The lines mark the dimension of the unit cell in the x-direction.

and therefore slow. There could be extra energy barriers associated with the proton-transfer steps or H2 recombination, but independent of this it is a necessary, but not sufficient, criterion for a material to be a good catalyst that the free energy of adsorbed H is close to that of the reactant or product (i.e., ∆G°H = 0). This principle can explain available experimental observations regarding metals as catalysts and electrode materials for hydrogen evolution.7 It is interesting to apply the same analysis to the active sites in nitrogenases and hydrogenases. For nitrogenase we have considered the model of the active site, the FeMo cofactor (FeMoco) shown in Figure 2.8 We find that hydrogen atoms can only bind exothermically to the three equatorial sulfur ligands (µ2S ligands) on the FeMoco. When the free energy of hydrogen atoms bound to the equatorial sulfur of the FeMoco is included in Figure 1, it 10.1021/ja0504690 CCC: $30.25 © 2005 American Chemical Society

COMMUNICATIONS

Figure 3. (Left) Polarization curve for hydrogen evolution on Pt, daihope C-support, and MoS2 cathodes. The polarization curves for Pt and C support are made at 25 °C. The potentials are measured with respect to a carbonsupported Pt anode in a proton exchange membrane electrode assembly. (Right) STM images of MoS2 nanoparticles on modified graphite.

results in a binding energy close to that of Pt. The FeMoco thus complies with the ∆G°H = 0 requirement.9 A number of researchers have performed computational studies of hydrogenase,10,11 and the results obtained by Siegbahn11 allow us to calculate the atomic hydrogen adsorption free energy for a [NiFe]-hydrogenase system. The Siegbahn model for the hydrogenase active site is shown in Figure 2. When the free energy is included in Figure 1, one can see that hydrogenase also fulfils the ∆G°H = 0 requirement and fulfils it best for all considered systems.9 We therefore conclude that ∆G°H is a good descriptor of materials that can catalyze hydrogen evolution and applies to a broad range of systems, both metals and enzymes. This means that we can use the same calculations to search for other systems, which could be candidates as catalysts for hydrogen evolution. One compound we have found computationally to obey the criterion is MoS2; see Figure 1. Comparing the nitrogenase active site and the MoS2 edge structure, we see that they bear a close resemblance, as shown in Figure 2. In both structures, the sulfur atom, which binds the hydrogen, is 2-fold coordinated to metal atoms, either to molybdenum or to iron. Only the edges of MoS2 are interesting in this context, as the basal plane of MoS2 is catalytically inactive.12 The first H that bonds to the edge is strongly bound, but at an H coverage above 0.25, the differential free energy of adsorption is 0.1 eV. According to the calculations, additional H atoms should then be able to adsorb with a low barrier or, equivalently, a low overpotential of the order 0.1 V. A good material would be nanometer-large MoS2 crystallites supported on, for example, graphite, which is conducting but otherwise inert. Such materials are used as catalysts for hydrotreating (hydrogenation of sulfur compounds in crude oil13), and methods for their preparation can be found in the literature.14 It is indeed possible to prepare nanosized MoS2 clusters on a graphite support, as can be seen in the scanning tunnel microscope (STM) image shown in Figure 3. The MoS2 nanoparticles are approximately 4 nm in diameter and 1 nm in apparent height, and nucleate along the graphitic steps. We have tested experimentally whether MoS2 nanoparticles supported on carbon can be used as catalyst for electrochemical hydrogen evolution. This was done by preparing a membrane electrode assembly (MEA), based on a Nafion proton exchange membrane, with a standard platinum electrode on one side and a

MoS2/graphite electrode on the other side. By having the same hydrogen pressure on both sides, we could make the electrochemical measurements using a Parstat 2273 potentiostat resulting in the I-V curve shown in Figure 3. The experimental approach has been used successfully in other studies.15 The conditions of the experiment correspond to pH ) 0 as in the calculations. As shown in Figure 3, MoS2/graphite is a quite reasonable material for hydrogen evolution with an overpotential in the range 0.1-0.2 V. We note that MoS2 has been found to be a promoter for the hydrogen evolution activity of NiSx electrodes,16 which can be understood from our findings. Furthermore, MoS2 has been tested for photocatalytic hydrogen evolution and shows activity but with significantly lower currents.17 Our findings suggest that we can begin searching for new catalytic materials using quantum chemical methods. The MoS2 nanoparticles supported on graphite may be an example of a new class of electrode materials. Acknowledgment. M. Brorson is gratefully thanked for providing us the samples. We thank P. E. M. Siegbahn for providing us results and structures prior to publication. We acknowledge support from the Danish Center of Scientific Computing through Grant No. HDW-1101-05. Supporting Information Available: Details of the DFT calculations, experimental setup, and obtained data. This material is available free of charge via the Internet at http://pubs.acs.org. References (1) (a) Trasatti, R. S. J. Electroanal. Chem. 1972, 39, 163. (b) Bockris, J. O’M.; Reddy, A. K. N.; Gamboa-Aldeco, M. Modern Electrochemistry 2A 2nd ed.; Kluwer Academic/Plenum Publishers: New York, 1998. (2) Dresselhaus, M. S.; Thomas, I. L. Nature 2001, 414, 332. (3) (a) Evans, D. J.; Pickett C. J. Chem. Soc. ReV. 2003, 32, 268. (b) Vollbeda, A.; Fontecilla-Camps, J. C. J. Chem. Soc., Dalton Trans. 2003, 21, 4030. (4) (a) Rees, D. C.; Howard, J. B. Science 2003, 300, 929. (b) Lee, S. C.; Holm, R. H. Proc. Natl. Acad. Sci. U.S.A. 2003, 100, 3595. (5) Lamle, S. E.; Vincent, K. A.; Halliwell, L. M.; Albracht, S. P. J.; Armstrong, F. A. J. Chem. Soc., Dalton Trans. 2003, 21, 4152. (6) (a) Rauchfuss, T. B. Inorg. Chem. 2004, 43, 14. (b) Meija-Rodriguez, Chong, D.; Reibenspies, J. H.; Soriaga, M. P.; Darensbourg, M. Y. J. Am. Chem. Soc. 2004, 126, 12004. (c) Razavet, M.; Davies, S. C.; Hughes, D. L.; Barclay, J. E.; Evans, D. J.; Fairhurst, S. A.; Liu, X.; Pickett, C. J. Chem. Soc., Dalton Trans. 2003, 4, 586. (7) Nørskov, J. K.; Bligaard, T.; Logado´ttir, A Ä .; Kitchin, J. R.; Chen, J. G.; Pandelov, S.; Stimming, U. J. Electrochem. Soc. 2005, 152. J23. (8) Hinnemann, B.; Nørskov, J. K. J. Am. Chem. Soc. 2004, 126, 3920. (9) The difference in pH and chemical potential for electron transfer is of the same order and cancel each other; see Supporting Information. (10) (a) Cao, Z.; Hall, M. B. J. Am. Chem. Soc. 2001, 123, 3734. (b) Liu, Z.-P.; Hu, P. J. Chem. Phys. 2002, 117, 8177. (c) Bruschi, M.; Fantucci, P.; De Goia, L. Inorg. Chem. 2004, 43, 3733. (11) Siegbahn, P. E. M. AdV. Inorg. Chem. 2004, 56, 101. (12) Raybaud, P.; Hafner, J.; Kresse, G.; Kasztelan, S.; Toulhoat, H. J. Catal. 2000, 189, 129. (13) Topsøe, H.; Clausen, B. S.; Massoth, F. E. Hydrotreating CatalysisScience and Technology, Springer-Verlag: Berlin, 1996. (14) Chorkendorff, I.; Niemantsverdriet, J. W. Concepts of Modern Catalysis and Kinetics; Wiley-VCH: New York, 2003. (15) Davies, J. C.; Nielsen, R. M.; Thomsen, L. B.; Chorkendorff, I.; Logado´ttir, A Ä .; Łodziana, Z.; Nørskov, J. K.; Li, W. X.; Hammer, B.; Longwitz, S. R.; Schnadt, J.; Vestergaard, E. K.; Vang, R. T.; Besenbacher, F. Fuel Cells 2004, 4, 309. (16) Nidola, A.; Schira, R. Int. J. Hydrogen Energy 1986, 11, 449. (17) Sobczynski, A. J. Catal. 1991, 131, 156.

JA0504690