Densities, Viscosities, Refractive Indices, and Heat Capacities of Poly

Jun 8, 2009 - Densities, Viscosities, Refractive Indices, and Heat Capacities of Poly(ethylene glycol-ran-propylene glycol) + Esters of Carbonic Acid ...
1 downloads 0 Views 1MB Size
Download PDF
J. Chem. Eng. Data 2010, 55, 205–210

205

Densities, Viscosities, Refractive Indices, and Heat Capacities of Poly(ethylene glycol-ran-propylene glycol) + Esters of Carbonic Acid at (293.15 and 313.15) K and at Atmospheric Pressure Fabio Comelli,*,† Adriana Bigi,‡ Daniele Vitalini,§ and Katia Rubini‡ Istituto per la Sintesi Organica e la Fotoreattivita` (ISOF-CNR), via Gobetti 101, I-40129 Bologna, Italy, Dipartimento di Chimica “G. Ciamician”, Universita` degli Studi, via Selmi 2, I-40126 Bologna, Italy, and Istituto di Chimica e Tecnologia dei Polimeri (ICTP-CNR), via Paolo Gaifami 18, I-95125 Catania, Italy

Densities, F, dynamic viscosities, η, refractive indices, nD, and heat capacities, Cp, for the binary mixtures containing poly(ethylene glycol-ran-polypropylene glycol) + esters of carbonic acid were determined at (293.15 and 313.15) K and at atmospheric pressure using an Anton Paar density meter, a Schott-Gera¨te AVS viscometer, an Abbe refractometer, and a Perkin-Elmer differential scanning calorimeter. Volume variations, ∆V, during mixing and deviations of the dynamic viscosities, ∆η, were obtained at these temperatures and are negative for all mixtures. Experimental data were fitted to the Redlich-Kister equation, and the adjustable parameters and the standard deviations between experimental and calculated values were estimated.

Introduction Studies in thermodynamic and bulk properties of binary mixtures are being increasingly used as tools for the investigation of the properties of pure components and the nature of intermolecular interactions between the liquid mixture constituents. This paper continues our systematic studies for determination of the thermodynamic properties of binary mixtures containing glycols, polyglycols, and copolymers as one component.1-4 Here, we present experimental data of densities, F, dynamic viscosities, η, refractive indices, nD (sodium line), and heat capacities, Cp, of the binary mixtures containing poly(ethylene glycol-ran-propylene glycol) (COP) + three esters of carbonic acid, namely, dimethyl carbonate (DMC), diethyl carbonate (DEC), and propylene carbonate (PC). Measurements were determined at (293.15 and 313.15) K and at normal pressure. The copolymer (COP) was chosen because of its wide range of industrial applicability in hydraulic fluids, heat transfer fluids, lubricants, solvents, plasticizers, and foam control agents. Esters of carbonic acid are attracting an increasing interest due to their uses in extractions of industrial importance, such as the production of many synthetic and natural resins and polymers,5 in the synthesis of pharmaceuticals,6 in agricultural chemistry, and as fuel additives.7 Particularly, there is a high interest in the dimethyl carbonate and propylene carbonate applications to storage batteries,8,9 based on intercalation of solutions of carbonates with lithium and bromine in graphite. Such batteries can be recharged thermally at relatively low temperatures. Binary mixtures containing propylene carbonate and other organic solvents, especially aprotic ones, have also a great technological and theoretical interest.10 * Corresponding author. E-mail: [email protected]. Tel.: +39-0512094326. Fax: +39-051-2094325. † Istituto per la Sintesi Organica e la Fotoreattivita` (ISOF-CNR). ‡ Universita` degli Studi. § Istituto di Chimica e Tecnologia dei Polimeri (ICTP-CNR).

The thermodynamic properties of COP + esters of carbonic acid depend mostly on the interactions between the -OH terminal groups of the copolymer and the -COOR groups of esters. Densities, viscosities, refractive indices, and heat capacities were measured experimentally using standard techniques. From density and viscosity values, the volume variation, ∆V, and the deviation in viscosity, ∆η, were calculated. The Redlich-Kister equation was used to correlate the experimental data and the standard deviations, σ, between experimental and calculated values. No data on the binary mixtures studied in this paper were found in the literature.

Experimental Section Materials. All chemicals were from Aldrich and were used without further purification. COP shows a nominal molecular weight Mn ) 2500, and its characterization is reported below. DMC (anhydrous g 99 %), DEC (anhydrous g 99 %), and PC (anhydrous g 99.7 %) were degassed ultrasonically (ultrasonic bath, Hellma, type 460, Milan, Italy) and dried over freshly activated molecular sieves (Fluka, type 4 Å) for several days to remove any traces of moisture. The pure components were also kept in an inert argon atmosphere as soon as the bottles were used. The purity of liquids was confirmed by GLC analysis.1 Experimental values of densities, F, dynamic viscosities, η, refractive indices, nD, and heat capacities, Cp, of the pure liquids were reported in Table 1 and compared with available literature data,11-22 where possible. 1 H NMR Analysis. 1H NMR spectra were obtained on an AC 200 F Bruker spectrometer interfaced with an Aspect 3000 computer, using the Bruker DISR 90 acquisition software. Samples were dissolved in CDCl3 and the chemical shifts expressed in parts per million by comparison with the signal of TMS used as an internal standard. MALDI-TOF Mass Spectrometric Analysis. MALDI-TOF mass spectra of the copolymer sample were acquired by a 4800

10.1021/je900307z CCC: $40.75  2010 American Chemical Society Published on Web 06/08/2009

206

Journal of Chemical & Engineering Data, Vol. 55, No. 1, 2010

Table 1. Densities, G, Dynamic Viscosities, η, Refractive Indices, nD, and Heat Capacities, Cp, of Pure Components and Comparison with Literature Values F/g · cm-3 COP DMC

DEC

PC a

T/K

this paper

293.15 313.15 293.15

1.09306 1.07681 1.06980

313.15

1.04325

293.15

0.97584

313.15

0.95239

293.15 313.15

1.20466 1.18306

η/mPa · s lit.

1.06969a 1.06954d 1.0700e 1.043105a 1.04301d 1.0434e 0.97500g 0.9747h 0.95232g 0.9522h 1.1836m

this paper 629.534 295.555 0.629

lit.

0.623a 0.6173d

this paper 1.4667 1.4596 1.3689 1.3604

0.817

0.494f 0.4807d 0.486a 0.810h

0.623

0.625h

1.3764

2.778 1.909

2.770l

1.4223 1.4149

0.494

1.3858

Ref 11. b Ref 12. c Ref 13. d Ref 14. e Ref 15. f Ref 16. g Ref 17. h Ref 18. i Ref 19. l Ref 20.

Proteomics analyzer MALDI time-of-flight/time-of-flight mass spectrometer (Applied Biosystems, Framingham, MA) in reflectron mode and in positive polarity. The samples were prepared by mixing about 0.1 mmol of polymer and 40 mmol of trans-3-indoleacrylic acid (used as a matrix) on the sampler target, using tetrahydrofurane doped with NaCl (as cationizing agent) as a solvent. After instrument calibration, the number average, Mn () ΣNiMi/ΣNi), and the weight average, Mw () ΣNiMi2/ΣNiMi ) ΣwiMi), molecular masses were determined using the Grams/386 program (PerSeptive Biosystem) applied on spectra corrected for the offset and the baseline.23 In the above equalities, Ni is the number of moles of species i, having molecular mass Mi and weight fraction wi. The polydispersity index was also obtained as the ratio Mw/Mn. Measurement Techniques. Measurements of density, viscosity, refractive index, and heat capacity of the binary mixtures were carried out as previously reported.1 Density. The volume variation ∆V can be obtained by the following equation

∆V ) 1/F - w1 /F1-w2 /F2

(1)

where F is the density of the mixture, wi, and Fi (i ) 1, 2) are the mass fractions and densities of the ith component, respectively. The experimental values for the four binary mixtures COP + esters of carbonic acids are listed in Table 2. The uncertainty in the densities was ( 1.5 · 10-5 g · cm-3. Correspondingly, the uncertainty in the volume variation, ∆V, is estimated as < 1 %. The curves of the volume variations, ∆V, vs the composition of these binary systems at the two experimental temperatures are shown in Figure 2. Viscosity. The viscosities were obtained from the kinematic viscosities, ν, from the equation

η ) VF ) k(t - θ)/F

(2)

where η is viscosity; F is the density; k is the capillary constant; t is the flow time; and θ is the kinetic energy correction. In the whole set of experiments, flow times were maintained > 200 s, by selecting viscometers with appropriate values of k. On this subject, the capillary diameters of the viscometers, varying from 0.47 mm up to 2.65 mm, were used for kinematic ranges of (0.5 to 300) mm2 · s-1, respectively. The viscometers were filled with 15 cm3 of solution for each measurement. The calibration of the viscometers was carried out with double distilled water and by a standard oil specimen of known viscosity (Petrotest, DIN 51 550). Experiments were repeated at least five times at each temperature for all mixtures, and the results were averaged.

Cp/J · g-1 · K-1

nD

m

lit.

this paper

lit.

1.3687b

2.041 2.151 1.844

1.734c

1.896

1.808c

1.790

1.861c

1.827

1.907c

1.645 1.706

1.705c 1.742c

1.3852i

1.4158n

Ref 21. n Ref 22.

The overall uncertainty of viscosity measurements depends on equilibrium temperature, flow time, mass fraction, and calibration fluid. So, according to the precision of all experimental instruments, the experimental average uncertainties of kinematic viscosity were estimated to be ( 0.01 cm2 · s-1. Equation 2 and the values of F allow calculation of the deviation in viscosity, ∆η, from the definition

∆η ) η - w1η1 - w2η2

(3)

where ηk is the viscosity of the pure component k and wk is its mass fraction in the mixture. Values of ∆η are reported in Table 2 and plotted in Figure 3 against the mass fraction, w1, of the copolymer. The uncertainty of the viscosity deviations was estimated to be less than 0.02 mPa · s. RefractiWe Indices. Values of the refractive indices (sodium line), fitted to a three parameter polynomial, are reported in Table 2 and plotted in Figure 4. Heat Capacity. The experimental heat capacities, C0p, of pure components from (288.15 to 323.15) K vs the temperature T/K, at normal pressure, are listed in Table 3 and represented in Figure 5. The experimental values of the heat capacities, Cp, of mixtures vs the mass fraction, w1, of polymer are reported in Table 4 and represented in Figure 6. The expression used to fit C0p as a function of temperature is

C0p ) c0 + c1(T/K) + c2(T/K)2

(4)

Analogous expression is used to fit Cp as a function of w1: C0p and (T/K) in eq 4 are substituted by Cp and w1, respectively. Values of the parameters ck (k ) 0, 1, and 2) are listed in Tables 5 and 6 together with the standard deviations σ (Cp).

Characterization of the Copolymer Poly(ethylene glycol-ran-propylene glycol) (COP) is a random copolymer having the following general Structure I HO-(-CH2-CH2-O-)n-[-CH(CH3)-CH2-O-]m-H (Structure I)

The relative abundance of ethylene glycol (E.G., -CH2CH2-O-) and propylene glycol [P.G., -CH(CH3)-CH2-O-] units in the copolymer sample has been achieved by 1H NMR analysis. In the spectrum (omitted for brevity), two clusters of signals are present between (1.0 and 1.2) ppm (due to the CH3 group of P.G.) and between (3.3 and 3.8) ppm (due to CH2 groups of P.G. and E.G. and to a CH group of P.G.); on the

Journal of Chemical & Engineering Data, Vol. 55, No. 1, 2010 207 Table 2. Densities, G, Volume Variations, ∆V, Dynamic Viscosities, η, Deviations in Dynamic Viscosities, ∆η, and Refractive Indices, nD, of COP + Esters of Carbonic Acid at (293.15 and 313.15) K w1

F

∆V

η

∆η

g · cm-3

cm3 · g-1

mPa · s

mPa · s

nD

Table 3. Experimental Liquid Heat Capacities, C0p, of Pure Components at Atmospheric Pressure T/K

COP

DMC

1.993 2.041 2.100 2.144 2.155 2.155 2.146 2.123

C p (J · g · K ) 1.837 1.844 1.855 1.870 1.884 1.896 1.911 1.928 0

COP (1) + DMC (2) 0.0259 0.0530 0.1199 0.1990 0.2925 0.4243 0.4936 0.5934 0.6957 0.7862 0.8739 0.9505

1.07070 1.07164 1.07386 1.07650 1.07941 1.08313 1.08483 1.08715 1.08927 1.09087 1.09221 1.09296

T/K ) 293.15 -0.00026 0.784 -0.00054 0.936 -0.00113 1.565 -0.00183 2.730 -0.00246 5.049 -0.00300 11.717 -0.00306 21.243 -0.00303 34.072 -0.00276 64.121 -0.00229 120.398 -0.00166 235.987 -0.00076 433.589

-16.13 -33.06 -74.47 -123.08 -179.51 -255.76 -289.78 -339.73 -374.02 -374.69 -314.22 -164.79

1.3712 1.3741 1.3810 1.3890 1.3983 1.4115 1.4183 1.4280 1.4380 1.4466 1.4550 1.4622

0.0259 0.0530 0.1199 0.1990 0.2925 0.4243 0.4935 0.5934 0.6957 0.7862 0.8739 0.9505

1.04450 1.04581 1.04888 1.05241 1.05634 1.06147 1.06395 1.06719 1.07027 1.07262 1.07447 1.07594

T/K ) 313.15 -0.00037 0.607 -0.00076 0.763 -0.00156 1.251 -0.00239 2.099 -0.00314 3.743 -0.00378 8.219 -0.00390 12.352 -0.00378 22.064 -0.00341 40.532 -0.00275 69.092 -0.00174 124.515 -0.00073 209.126

-7.53 -15.38 -34.62 -57.12 -83.05 -117.47 -133.77 -153.51 -165.23 -163.39 -133.82 -71.81

1.3627 1.3655 1.3724 1.3804 1.3900 1.4032 1.4102 1.4200 1.4302 1.4391 1.4475 1.4549

COP (1) + DEC (2) 0.0836 0.1546 0.2017 0.3097 0.3904 0.4608 0.5237 0.6253 0.7019 0.8219 0.8931 0.9567

0.98511 0.99330 0.99881 1.01154 1.02104 1.02936 1.03674 1.04865 1.05776 1.07214 1.08064 1.08812

T/K ) 293.15 -0.00045 1.485 -0.00103 2.451 -0.00140 3.343 -0.00213 6.750 -0.00247 11.306 -0.00264 17.712 -0.00264 26.366 -0.00243 51.351 -0.00222 85.913 -0.00171 212.678 -0.00123 337.947 -0.00060 494.274

-51.91 -95.56 -124.31 -188.80 -234.94 -272.82 -303.72 -342.59 -356.23 -304.91 -224.37 -108.05

1.3920 1.3976 1.4013 1.4097 1.4161 1.4218 1.4268 1.4351 1.4414 1.4512 1.4573 1.4628

0.0836 0.1546 0.2017 0.3097 0.3904 0.4608 0.5237 0.6253 0.7019 0.8219 0.8931 0.9567

0.96271 0.97160 0.97755 0.99104 1.00126 1.00998 1.01777 1.03031 1.03973 1.05452 1.06330 1.07135

T/K ) 313.15 -0.00110 1.093 -0.00200 1.746 -0.00254 2.327 -0.00337 4.415 -0.00388 7.038 -0.00396 10.543 -0.00390 15.141 -0.00355 27.120 -0.00304 43.100 -0.00196 88.987 -0.00117 141.529 -0.00051 217.993

-24.19 -44.47 -57.80 -87.56 -108.72 -125.99 -139.95 -157.92 -164.55 -154.05 -122.50 -64.80

1.3829 1.3886 1.3924 1.4015 1.4081 1.4140 1.4192 1.4277 1.4343 1.4446 1.4507 1.4562

COP (1) + PC (2) 0.0681 0.1271 0.2097 0.2736 0.3436 0.4162 0.4466 0.5862 0.6431 0.7562 0.8621 0.9337

1.19696 1.19078 1.18226 1.17557 1.16806 1.16006 1.15667 1.14080 1.13432 1.12144 1.10945 1.10114

T/K ) 293.15 -0.00043 4.985 -0.00110 7.826 -0.00204 14.152 -0.00264 21.782 -0.00311 34.112 -0.00336 51.039 -0.00340 63.517 -0.00322 130.926 -0.00302 172.974 -0.00249 274.680 -0.00182 395.529 -0.00196 505.993

-40.04 -74.18 -119.68 -152.14 -183.69 -212.32 -218.89 -239.09 -232.71 -201.92 -147.51 -81.98

1.4255 1.4286 1.4327 1.4359 1.4393 1.4428 1.4440 1.4503 1.4528 1.4574 1.4617 1.4644

0.0681 0.1271 0.2097 0.2736 0.3436 0.4162 0.4466 0.5862 0.6431 0.7562 0.8621 0.9337

1.17621 1.17007 1.16187 1.15545 1.14846 1.14111 1.13803 1.12358 1.11755 1.10537 1.09350 1.08506

T/K ) 313.15 -0.00076 3.258 -0.00121 4.886 -0.00207 8.301 -0.00262 12.138 -0.00319 17.939 -0.00364 26.172 -0.00380 31.099 -0.00415 59.972 -0.00409 78.028 -0.00365 123.143 -0.00267 184.190 -0.00153 233.682

-18.65 -34.33 -55.18 -70.12 -84.86 -97.95 -101.94 -114.09 -112.73 -100.82 -70.87 -42.42

1.4183 1.4213 1.4253 1.4285 1.4319 1.4354 1.4368 1.4430 1.4455 1.4502 1.4545 1.4570

288.15 293.15 298.15 303.15 308.15 313.15 318.15 323.15

-1

DEC

PC

1.779 1.790 1.799 1.810 1.819 1.827 1.850 1.865

1.629 1.645 1.660 1.673 1.687 1.706 1.723 1.738

-1

Table 4. Experimental Heat Capacities, Cp, for Binary Mixtures Containing COP + Esters of Carbonic Acid Cp w1

Cp

J · g-1 · K-1

w1

J · g-1 · K-1

COP (1) + DMC (2) 0.0259 0.0530 0.1199 0.1990 0.2925 0.4243

1.851 1.852 1.858 1.868 1.878 1.900

T/K ) 293.15 0.4936 0.5934 0.6957 0.7862 0.8739 0.9505

1.912 1.932 1.956 1.978 2.003 2.025

0.0259 0.0530 0.1199 0.1990 0.2925 0.4243

1.899 1.902 1.915 1.932 1.958 1.989

T/K ) 313.15 0.4936 0.5934 0.6957 0.7862 0.8739 0.9505

1.995 2.024 2.055 2.087 2.106 2.136

COP (1) + DEC (2) 0.0836 0.1546 0.2017 0.3097 0.3904 0.4608

1.805 1.815 1.826 1.856 1.866 1.890

T/K ) 293.15 0.5237 0.6253 0.7019 0.8219 0.8931 0.9567

1.895 1.927 1.944 1.975 2.004 2.025

0.0836 0.1546 0.2017 0.3097 0.3904 0.4608

1.846 1.863 1.876 1.905 1.939 1.955

T/K ) 313.15 0.5237 0.6253 0.7019 0.8219 0.8931 0.9567

1.971 2.005 2.032 2.075 2.106 2.136

COP (1) + PC (2) 0.0681 0.1271 0.2097 0.2736 0.3436 0.4162

1.666 1.685 1.716 1.733 1.763 1.785

T/K ) 293.15 0.4466 0.5862 0.6431 0.7562 0.8621 0.9337

1.797 1.856 1.880 1.926 1.975 2.010

0.0681 0.1271 0.2097 0.2736 0.3436 0.4163

1.726 1.748 1.780 1.805 1.836 1.860

T/K ) 313.15 0.4466 0.5862 0.6431 0.7562 0.8621 0.9337

1.880 1.940 1.966 2.021 2.075 2.110

basis of the intensities of these signals, the values of [n] (% mol E.G. component abundance) and [m] (% mol P.G. component abundance) have been determined. The obtained results are reported in Table 7. The chemical characterization of the copolymer, to determine both average molecular mass and microstructure, has been attempted by MALDI-TOF mass spectrometry. In a previous work,4 because of the lower molecular mass of polymeric samples investigated, the interpretation of mass

208

Journal of Chemical & Engineering Data, Vol. 55, No. 1, 2010

Figure 1. Positive MALDI-TOF mass spectrum of COP. In the insets, on the top of each peak due to an oligomeric species present in the copolymer, the rounded m/z value is indicated. The composition (in the order, “n” and “m”, see Structure I) is given in the following: m/z 1838 (25, 12), m/z 1840 (29, 9), m/z 1842 (4, 28; 33, 6), m/z 1844 (8, 25; 37, 3), m/z 3085 (23, 35; 52, 13), m/z 3087 (27, 32; 56, 10), m/z 3089 (2, 51; 31, 29; 60, 7), m/z 3091 (6, 48; 35, 26; 64, 4), m/z 3093 (10, 45; 39, 23; 68, 1).

Figure 2. Volume variations, ∆V, for the binary mixtures containing COP (1) + esters of carbonic acid (2): b,O, COP + DMC; 9,0, COP + DEC; 2,∆, COP + PC. Full points, T/K ) 293.15; open points, T/K ) 313.15. Full lines, eq 5.

Figure 3. Deviation in viscosity, ∆η, for the binary mixtures containing COP (1) + esters of carbonic acid (2): b,O, COP + DMC; 9,0, COP + DEC; 2,∆, COP + PC. Full points, T/K ) 293.15; open points, T/K ) 313.15. Full lines, eq 5.

spectra was made rounding the atomic mass of C, H, and O to 12, 1, and 16, respectively. In the present case, in consequence of the high mass of COP, the correct attribution of peaks present in its mass spectrum can be obtained only by determining the exact mass of oligomers having Structure I. So, considering that the exact mass of the most abundant isotope of C, H, and O is 12.0000, 1.0078, and 15.9949, respectively, the molecular masses of repeating units result, E.G. ) 44.026 and P.G. ) 58.042; consequently, molecular masses of macromolecules

Figure 4. Refractive indices, nD, vs the mass fraction, w1, of the binary mixtures containing COP (1) + esters of carbonic acid (2): b,O, COP + DMC; 9,0, COP + DEC; 2,∆, COP + PC. Full points, T/K ) 293.15; open points, T/K ) 313.15. Full lines correspond to a three parameter polynomial regression.

Figure 5. Heat capacities, C0p, of pure components in the range (288.15 to 323.15) K. [, b, 9, 2 refer to COP, DMC, DEC, and PC, respectively. Full line, eq 4.

constituting COP, cationized with Na+, will be given from the following equation

m/z ) (18.011 + 22.990) + n · 44.026 + m · 58.042 Accordingly, the mass spectrum of COP, reported in Figure 1, shows a series of peaks whose masses, included between ≈ m/z 1500 and ≈ m/z 4000, correspond to those expected. Although each signal of the overall mass spectrum looks like a single peak, it is really constituted of a cluster of peaks due not only to the isotopic pattern of different compounds but

Journal of Chemical & Engineering Data, Vol. 55, No. 1, 2010 209

evidenced in the insets of Figure 1 (enlargements of the zone of the spectrum included between m/z 1837 and 1846 and between m/z 3084 and 3094) in which, on the top of each peak due to an oligomeric component of the copolymer, the rounded m/z value and, in the captions, the E.G. and P.G. composition (in the order: “n” and “m”) are indicated. Remarkably, referring to the first inset, for peaks at m/z 1842 and m/z 1844, two different compositions are reported because, owing to the high average molecular mass of COP, isobaries are possible (on the contrary, each one of the other two peaks is associable to only one oligomer). So, for example, the peak at m/z 1842 can be generated from the two following species

Figure 6. Heat capacities, Cp, for the binary mixtures containing COP (1) + esters of carbonic acid (2): b,O, COP + DMC; 9,0, COP + DEC; 2,∆, COP + PC. Full points, T/K ) 293.15; open points, T/K ) 313.15. Full lines, eq 4.

HO-(-CH2-CH2-O-)33-[-CH(CH3)-CH2-O-]6-H Na+ m/z 1842.111 HO-(-CH2-CH2-O-)4-[-CH(CH3)-CH2-O-]28-H Na+ m/z 1842.281

Table 5. Adjustable Parameters of Equation 4 and Standard Deviation of Pure Components σ(Cp) component

c0

c1

c2

J · g-1 · K-1

COP DMC DEC PC

-27.0693882 2.9823099 3.9643096 1.6204181

0.1873377 -0.0098881 -0.0164375 -0.0027068

-0.0003002 0.0000205 0.0000308 0.0000095

0.0071 0.0018 0.0034 0.0016

which, although with a different probability, are both present in the copolymer sample. Because the instrument resolution, at these mass values, is not sufficient to discriminate peaks which differ by less than one amu, they are recorded as a single signal. The higher the masses are, the more numerous the isobaries became; for example, the peak at m/z 3089 corresponds to three different oligomers [n ) 2 and m ) 51 (m/z 3089.195), n ) 31 and m ) 29 (m/z 3089.025), n ) 60 and m ) 7 (m/z 3088.855)], while the one at m/z 4400 corresponds to four [n ) 12 and m ) 66 (m/z 4400.085), n ) 41 and m ) 44 (m/z 4399.915), n ) 70 and m ) 22 (m/z 4399.745), n ) 99 and m ) 0 (m/z 4399.575)]. However, all peaks recorded in the mass spectrum of the analyzed copolymer are leading back to compounds having Structure I, with different values of “n” and “m”; because no peaks due to impurities are found, COP can be considered substantially pure. The average molecular mass of COP (both Mn and Mw) has been determined, using the Grams/386 program (PerSeptive Biosystem), from the corresponding positive MALDI mass spectrum in the mass range 500 to 10000. The obtained values are reported in Table 7.

Table 6. Adjustable Parameters of Equation 4 and Standard Deviation of COP (1) + Esters of Carbonic Acid (2) at (293.15 and 313.15) K σ(Cp) c1

c2

J · g-1 · K-1

T/K

c0

293.15 313.15

1.845114 1.894952

COP (1) + DMC (2) 0.080629 0.113824 0.171387 0.086091

0.0029 0.0039

293.15 313.15

1.790979 1.826795

COP (1) + DEC (2) 0.161799 0.085071 0.227585 0.097231

0.0039 0.0035

293.15 313.15

1.645531 1.704250

COP (1) + PC (2) 0.301647 0.093920 0.337814 0.108502

0.0019 0.0027

mostly to the presence of oligomers of different compositionswhose masses differ by about 2 amu. This fact is well Table 7. Chemical Composition and Average Molecular Mass of COP sample

E.G. mol % (wt. %) (our data)

P.G. mol % (wt. %) (our data)

Mn (Aldrich)

Mn (our data)

Mw (our data)

Mw/Mn (our data)

COP

79.7 (74.9)

20.3 (25.1)

∼ 2500

2676

2730

1.020

Table 8. Adjustable Parameters, ak, from Equation 5, and Standard Deviations σ(Q), from Equation 6, of COP + Esters of Carbonic Acid at (293.15 and 313.15) K function

T/K

a0

∆V/cm3 · g-1

293.15 313.15 293.15 313.15

-0.012312 -0.015620 -1169.655 -535.674

293.15 313.15 293.15 313.15 293.15 313.15 293.15 313.15

∆η/mPa · s

∆V/cm3 · g-1 ∆η/mPa · s

∆V/cm3 · g-1 ∆η/mPa · s

a1

a2

a4

σ(Q)

COP (1) + DMC (2) -0.000919 -0.001270 -1027.166 -434.474

-0.001112 0.000198 -1071.651 -421.491

-0.003030 0.000959 -701.606 -284.865

0.000019 0.000028 2.37 1.39

-0.010512 -0.0158231 -1177.984 -534.128

COP (1) + DMC (2) 0.0002421 0.001980 -1006.784 -424.514

0.001306 0.003461 -577.201 -417.932

-0.006827 -0.0008456 -72.107 -307.039

0.000017 0.000036 2.05 1.61

-0.013072 -0.015908 -918.754 -432.721

COP (1) + PC (2) 0.002195 -0.006160 -322.262 -190.803

0.001570 -0.002022 -53.659 -51.191

-0.010948 -0.002430 -113.743 -26.932

0.000016 0.000042 2.04 0.92

210

Journal of Chemical & Engineering Data, Vol. 55, No. 1, 2010

Results Changes in volume variations, ∆V, and in deviation of viscosities, ∆η, with composition can be expressed by the Redlich-Kister-type equation

Qcalc ) w1w2

∑ ak(w1 - w2)k

(5)

kg0

where Qcalc refers to ∆V or ∆η. The adjustable parameters ak were determined by a least-squares method. The corresponding results are reported in Table 8. The tabulated standard deviations, σ(Q), reported in the same table, are defined as

|

σ(Q) ) ξmin /(N - n)

|

0.5

(6)

with N and n being the number of experimental points and of parameters, respectively, whereas ξmin is the minimum value of the objective function ξ, defined as N

ξ)

∑ (Qcalc - Q)2

(7)

k)1

and Q is the experimental value.

Discussion As can be seen from experimental data of Table 2 and Figure 2, the variations in densities, ∆V, for the binary mixtures COP + esters of carbonic acid are always negative. This is due to a volume contraction on mixing correlated, probably, to several effects, such as interactions between COP molecules and esters of carbonic acid and steric hindrance. The ∆V values of the binary mixtures follow the order DEC > DMC > PC, although the observed variations are quite small. The viscosity deviations, ∆η, present negative values over the whole mass fraction range at T ) (293.15 and 313.15) K. They become less negative following the sequence DMC < DEC < PC at 293.15 K, whereas at T ) 313.15 K they follow the order DMC = DEC < PC. ∆η values decrease with increasing temperature. All values of refractive indices, nD, and heat capacities, Cp, are always positive. Values of nD decrease in the order PC > DEC > DMC, while for Cp, the order becomes DMC > DEC > PC. Acknowledgment The authors thank Dr. Sandro Dattilo and Sig. Gaetano Pasorelli for their valuable technical assistance in measurements.

Literature Cited (1) Francesconi, R.; Bigi, A.; Rubini, K.; Comelli, F. Molar heat hapacities, densities, viscosities, and refractive indices of Poly(ethylene glycols) + 2-methyltetrahydrofuran at (293.15, 303.15, and 313.15) K. J. Chem. Eng. Data 2007, 52, 2020–2025. (2) Castellari, C.; Vitalini, D.; Comelli, F.; Francesconi, R. Effect of excess enthalpies on binary mixtures containing propylene glycols and poly(propylene glycols)+ dimethyl carbonate at 308.15 K. Thermochim. Acta 2004, 412, 125–129. (3) Comelli, F.; Ottani, S. Excess Enthalpies, Densities, viscosities, and refractive indices of binary mixtures involving some poly(glycols) + diethyl Carbonate at 308.K. J. Chem. Eng. Data 2004, 49, 970–975.

(4) Comelli, F.; Bigi, A.; Vitalini, D.; Rubini, K.; Francesconi, R. Densities, viscosities, refractive indices and heat capacities of poly(propylene glycols) or poly(ethylene glycol)-poly(propylene glycol)poly(ethylene glycol)-block-copolymers + 2- methyltetrahydrofuran at (298.15 and 313.15) K and at atmospheric pressure. J. Chem. Eng. Data 2008, 53, 1302–1308. (5) The Merck Index, 13th ed.; Merck & Co., Inc.: Whitehouse Station, NJ, 2001. (6) Annesini, M. C.; De Sanctis, R.; Kikic, I.; Marrelli, R. Excess enthalpy and T-x data of aromatic-propylene carbonate mixtures. J. Chem. Eng. Data 1984, 29, 39–41. (7) Pardo, J. M.; Tovar, C. A.; VCerdeireina, C. A.; Carballo, E.; Romani, L. Excess molar volumes and excess molar heat capacities of(dimethyl carbonate or diethyl carbonate + n- heptane) at several temperatures. J. Chem. Thermodyn. 1999, 31, 787–796. (8) Pistoia, G. Lithium Batteries: New materials, deVelopments and perspectiVes. Industrial Chemical Library; Elsevier: Amsterdam, 1994; Vol 5. (9) Tobishima, S.; Arakawa, M.; Yamaki, E. Electrolytic properties of LiClO4-propylene carbonate mixed with amiele-solvents for lithium batteries. Electrochim. Acta 1988, 33, 239–244. (10) Gabano, J.-P.-, Ed. Lithium Batteries; Academic Press: New York, 1983. (11) Romano, E.; Trenzado, J. L.; Matos, J. S.; Segade, L. E. Termophysical properties of four binary dimethyl carbonate + 1-alcohol systems at 288.15-313.15 K. Fluid Phase Equilib. 2003, 211, 219–240. (12) Ping, Y. Y.; Lapidus, A. L. Oxidative carbonylation of organic compounds by carbon monoxide and transition-metal salt catalysts. Russ. Chem. Bull. 1977, 26, 325–327. (13) Comelli, F.; Francesconi, R.; Bigi, A.; Rubini, K. Excess molar enthalpies, molar heat capacities, densities, viscosities, and refractive indices of dimethyl sulfoxide plus esters of carbonic acid at 308.15 K and atmospheric pressure. J. Chem. Eng. Data 2006, 51, 665–670. (14) Yang, C.; Xu, W.; Ma, P. Excess Molar Volumes and Viscosities of Binary Mixtures of Dimethyl Carbonate with Chlorobenzene, Hexane, and Heptane from (293.15 to 353.15) K and at Atmospheric Pressure. J. Chem. Eng. Data 2004, 49 (6), 1802–1808. (15) Rodriguez, A.; Canosa, J.; Tojo, J. Physical Properties of Binary Mixtures (Dimethyl Carbonate + Alcohols) at Several Temperatures. J. Chem. Eng. Data 2001, 46, 1476–1486. (16) Rodriguez, A.; Canosa, J.; Dominguez, a.; Tojo, J. Viscosities of dimethyl carbonate or diethyl carbonate with alkanes at four temperatures. New UNIFAC-VISCO parameters. J. Chem. Eng. Data 2003, 48, 146–151. (17) Changsheng, Y.; Hexi, L.; Zanguang, L.; Peisheng, M. Densities and viscosities of diethyl carbonate + toluene, and + methanol, and + 2-propanol from (293.15 to 363.K. J. Chem. Eng. Data 2006, 51, 584– 589. (18) Comunas, M. J. P.; Baylaicq, A.; Boned, C.; Fernandez, J. Highpressure measurements of the viscosity and densities of two polyethers and two dialkyl carbonates. Int. J. Thermophys. 2001, 22, 749–768. (19) Bowman, N. S.; Rexford, D. R. A synthesis of R-ethoxymethylene and R-chloromethylene carboxylic esters. J. Org. Chem. 1954, 19 (8), 1219–1224. (20) Riddick, J. A.; Bunger, W. B.; Sakano, T. K. Organic SolVents, 4th ed.; Interscience: New York, 1986. (21) Moumouzias, G.; Panapoulos, D. K.; Ritzoulis, G. Excess properties of the binary liquid systems propylene carbonate + acetonitrile. J. Chem. Eng. Data 1991, 36, 20–23. (22) Peppel, W. J. Preparation and Properties of the Alkylene Carbonates. Ind. Eng. Chem. 1958, 50, 767–770. (23) Vitalini, D.; Mineo, P.; Scamporrino, E. Further Application of a Procedure for Molecular Weight and Molecular Weight Distribution Measurements of Polydisperse Polymers from Their Matrix-Assisted Laser Desorption/Ionization Time-of-Flight Mass Spectra. Macromolecules 1996, 29, 5285–5289.

Received for review March 27, 2009. Accepted May 21, 2009.

JE900307Z