Green, Water-Dispersible Photoluminescent On–Off–On Probe for

May 24, 2017 - Phone: +91-22-2559 2349. ... To the best of our knowledge, this is the first report based on CQDs and Eu3+ for the detection of fluorid...
2 downloads 5 Views 956KB Size
Subscriber access provided by Binghamton University | Libraries

Article

Green Water dispersible Photoluminescent on-offon Probe for Selective Detection of Fluoride Ions Pallavi Singhal, Bal Govind Vats, Sanjay Kumar Jha, and Suman Neogy ACS Appl. Mater. Interfaces, Just Accepted Manuscript • Publication Date (Web): 24 May 2017 Downloaded from http://pubs.acs.org on May 26, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Green Water dispersible Photoluminescent onoff-on Probe for Selective Detection of Fluoride Ions Pallavi Singhal±$*, Bal Govind Vats±#*, Sanjay K. Jha±$ and Suman Neogy! ±

Homi Bhabha National Institute, Mumbai 400094, India

$

Health Physics Division, Bhabha Atomic Research Centre, Mumbai 400085, India

#

Fuel chemistry Division, Bhabha Atomic Research Centre, Mumbai 400085, India

!

Mechanical Metallurgy Division, Bhabha Atomic Research Centre, Mumbai 400 085, India *E-mail: [email protected], [email protected]

Phone : +91-22-2559 2349, +91-22-2559 0643, Fax: +91-22-2550 5313, +91-22-2550 5151

Keywords: Quantum dots, fluoride ion, photoluminescence, sensors, aggregation

Abstract Considering the high toxicity and widespread availability of fluoride ion in different environmental matrices, it is imperative to design a probe for its detection. In view of this a selective fluorescent on-off-on probe based on carbon quantum dots (CQDs) and Eu3+ has been designed. We have synthesized water soluble carboxylic acid functionalized CQDs and monitored its interaction with Eu3+. On addition of Eu3+ ions luminescence quenching in

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

CQDs emission was observed (switch-off). We investigate the reason for this luminescence quenching using time resolved emission and high resolution transmission electron microscopy (HRTEM) studies and observed that both electron transfer from CQDs to Eu3+ and aggregation of CQDs are responsible for luminescence quenching. Zeta potential and Xray photoelectron spectroscopy studies confirm the Eu3+ binding with the COOH groups on CQDs surface. Interestingly luminescence regains after the addition of fluoride ions into the CQDs/Eu3+ system (switch- on). This has been assigned to the Eu3+ removal from CQDs surface due to the formation of EuF3 and is confirmed by X-ray diffraction and HRTEM measurements. The sensitivity of the probe was tested by carrying out experiments with other competing ions and was found to be selective for fluoride ions. Experiments with variable concentrations of fluoride ion suggest that the working range of probe is 1-25 ppm. The probe has been successfully tested for the detection of fluoride ions in toothpaste sample and results were compared with the observed value from ion chromatography. To the best of our knowledge this is the first report based on CQDs and Eu3+ ions for fluoride ion detection where a clear mechanism of detection has been demonstrated that in turn will help in future to design better detection methods. The suggested probe is green, economical, rapid, efficient, and most importantly selective and can be used for the detection of fluoride ions in real environmental samples.

ACS Paragon Plus Environment

Page 2 of 30

Page 3 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

1) Introduction The design of fluoride ion sensors is an active area of investigation1-17 because of its high toxicity18 and widespread availability in drinking water, toothpaste, and osteoporosis drugs4,19. It is considered as one of the major water pollutants and excess intake can harm different organs of human body18,20. It has also been realized that the prolonged exposure to fluoride ion can inhibit IQ development in children21-23 and as per World Health Organization (WHO) it can permanently damage bones, kidney and even leads to death24,25. Due to its severe health side effects, WHO limits the fluoride ion concentration in drinking water ~ 1.5 mg/L18,25. Hence it is very important to develop methods for fluoride ion detection that are highly sensitive, selective, cost effective, simple and allow real-time detection. A number of commercially developed methods are available for this purpose that includes ion selective electrode20, nuclear magnetic resonance spectroscopic analysis4 and colorimetric (UV) methods7,9. Among them, ion selective electrode methods are most widely used. However, both ion selective electrode and nuclear magnetic resonance spectroscopic methods have limitations such as requirement of complex instrumentation, well-equipped laboratories and trained personnel. Hence both the methods cannot be used in minimally resourced laboratories. To overcome these limitations, photoluminescence based detection methods are emerging as an alternate6,8,11,12,18,20-29. The method has advantages such as low cost, high sensitivity, low detection limit, ease of handling, and real-time detection. Considerable efforts have been made to develop this method by exploiting different strategies such as supramolecular recognition1-3, hydrogen bonding2,6, Lewis acid−base interactions2,19,30. However in most of the above stated strategies, organic molecules are being utilized1,19,30 and the synthesis of these molecules is a challenging task3. More importantly, most of these molecules are water insoluble3,19,30. Hence, the detection of the fluoride ions using these molecules cannot be done directly in water and further treatment is required to make them

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

water dispersible. At the same time interference from other competing anions is an issue that has to be resolved. Therefore, there is a need to develop new methods for fluoride ion detection that are much simpler and can overcome most of the above stated limitations. Recently, semiconductor quantum dots (SQDs) are emerging as an alternative to organic molecules and attains a lot of attention because of their exceptional properties such as high stability, high extinction coefficient and high photo-luminescence yield etc31-34. A lot of studies have been carried out earlier for detection of toxic ions using these SQDs33,34. However most of the studied SQDs use cadmium and owing to high toxicity of cadmium, application of these SQDs in real environment is a question of debate34-36. It is therefore utmost important to find alternate materials that are environmentally more benign and less toxic. In view of this, carbon based quantum dots (CQDs) attains a lot of attention37-39. The superior properties of CQDs, such as high aqueous stability, high biocompatibility and low toxicity make them an ideal candidate over cadmium and lead based SQDs to explore their applications in number of fields such as bioimaging25,40,41, biosensors40,42 and drug delivery43. Recently CQDs and their composites are also being utilized as chemo-sensors and their application to detect a wide range of cations and anions have been demonstrated18,21,44-49. The detection application of CQDs involves change in its photoluminescence intensity on interaction with foreign ions18,25. Dong et al.44 have utilized the photoluminescence property of polyamine functionalized CQDs for selective and sensitive detection of copper ions. They have shown that 6 nM copper ions can be detected using these CQDs. Xu et al.46 have demonstrated the application of these dots for detection of tartrazine in food samples. Gogoi et al.47 have utilized these dots for detection of number of heavy metals such as chromium, copper, iron, lead and manganese. It shows that a lot of work is going on where the application of these dots as a detection probe has been explored. However very few reports are available where its application for fluoride ion detection has been demonstrated18,21,25,50.

ACS Paragon Plus Environment

Page 4 of 30

Page 5 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Mohapatra et. al.25 have used a composite system of CQDs and magnetically separable nickel ethylenediaminetetraacetic acid complex bound-silica coated magnetite nanoparticle for fluoride ion detection. The method shows a high selectivity but the synthesis of material involves a number of steps. At the same time a clear understanding on the detection mechanism has not been given which is equally important to design and understand better detection methods. Liu et. al.18 have designed a novel fluorescent probe for fluoride ion detection based on zirconium complexed CQDs. They have shown the application of their materials in real samples however the experimental condition required little higher temperature that makes the process tedious. Basu et. al.21 have also used CQDs for fluoride ion detection. They have demonstrated a ready to use detection device. However they have not shown its applicability in real environmental samples. All the above reports suggest that a number of materials have been developed for fluoride ion detection but still more improvement is needed. At the same time to design and develop better detection probes it is very important to understand the working mechanism of the probe and its applicability in real environmental samples which is still lacking in literature. Also the designed probe should be low cost and environment friendly so that it can be used in minimal resource laboratories and in different environmental matrices. In our present work we have focused on these issues by demonstrating a new method for fluoride ion detection. In spite of difficult synthesis and methodology adopted so far, our method is simple, selective, sensitive, green, low cost and can be directly used in aqueous medium. We have used a composite system of CQDs and europium where photoluminescence property of CQDs was used for fluoride ion sensing. We have demonstrated a clear mechanism on working on this probe which will help to design and develop better detection probes in future. Experiments with other competing ions suggest that the probe is selective in nature and can be used for real sample analysis.

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

2) Experimental (i) Material and methods (a) Materials Citric acid, europium (III) nitrate pentahydrate, dialysis membranes (1 kDa cut off), ammonium hydrogen fluoride, ammonium chloride, ammonium bromide, ammonium iodide, ammonium nitrate, ammonium acetate, ammonium carbonate were purchased from Aldrich and were used without further purification. Analytical grade sodium hydroxide was used. Ultrapure water used in this study was obtained from a Milli-Q ion exchange column (Millipore) with a resistivity of 18.2 MΩcm. (b) Synthesis of Carboxylic acid functionalized CQDs. Synthesis of CQDs was carried out using a previously reported procedure42. In brief, 6 g of citric acid in a glass beaker was taken and covered with a lid. It was heated at 205°C until the solid completely melt. The solution was maintained at this temperature for another 15 min. After cooling to room temperature, 50 mL of 0.25 M sodium hydroxide (NaOH) was added to the reaction mixture. The resulting solution was then adjusted to pH 6.0 with 0.05 M NaOH, followed by dialysis using a 1 kDa cut off membrane for 3 days before subsequent use. The colloidal solution of CQD was evaporated by vacuum evaporator at 40°C. The size of as synthesized dots was determined using TEM analysis. (c) Methodology To utilize CQDs as sensors for fluoride ion detection, a stock solution of CQDs of 100mg/L concentrations was prepared and was used throughout the photoluminescence measurements. To this solution, different concentration of europium (III) nitrate pentahydrate was added with Eu3+ concentration in the range from 10-1000 mg/L and change in photoluminescence

ACS Paragon Plus Environment

Page 6 of 30

Page 7 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

intensity was monitored. After Eu3+ addition different concentration of fluoride ion (0-50 ppm) was added and change in photoluminescence intensity was monitored. The selectivity of the method was also investigated by carrying out experiment with different anions such as chloride, bromide, iodide, nitrate, carbonate and acetate and change in photoluminescence intensity of CQDs-Eu3+ complex on interaction with these anions was monitored. To confirm the precision and accuracy of the method, each set of experiments was carried out in triplicate. (d) Analysis of fluoride ion in Toothpaste. To analyse fluoride ion in Toothpaste18, 1 g toothpaste was accurately weighed and dissolved in 30.0 ml water and stirred at 70°C for 3 h in a polypropylene vessel. The resulting solution was cooled to room temperature and then filtered with a membrane filter (pore size 0.45 mm) to eliminate solids in suspension. The insoluble part was washed several times with water, and the resulting solution was diluted to 200 ml with water for further use. (ii) Instrumentation Crystal phase of the samples were determined using Rigaku, Miniflex-600 X-ray diffractometer instrument with Ni-filtered Cu: Kα radiation. CQDs and europium fluoride samples were pasted on glass slide and it was mounted on the sample holder. X-ray diffraction (XRD) pattern was recorded at scanning rate of 2°/min. Particle size of samples was determined using Transmission electron microscope (TEM) (2000 FX, JEOL, Japan). For TEM, ~5 mg powdered CQDs was dispersed in 10 ml water under ultrasonic vibration for 1 h. A drop of the dispersed particles was put over the carbon coated copper grid and evaporated to dryness at room temperature. FTIR spectra were recorded using Platinum attenuated total reflection (ATR) technique. All spectra were obtained using a resolution of 4 cm-1 (wave number) and equal measurement conditions (4000–500 cm-1, 36 scans). Zeta

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

potential experiments have been carried out using a PSS/NICOMP 380 ZLS system with a red He–Ne laser diode at 632.8 nm in a fixed angle 90°. Zeta potential measurements were performed at 25° C after a temperature homogenization time of 5 min. For reproducibility, at least three measurements were conducted in all samples. The instrument calibration was checked before each experiment using a latex suspension of known zeta potential (i.e., 55±5 mV). X-ray photoelectron spectroscopy (XPS) measurements were carried out on a selfsupporting sample wafer (8 mm diameter, ~ 1 mm thick) adhered to a double sided carbon tape employing ESCA and AES system (SPECS Surface Nano Analysis GmbH, Germany), using Al Kα X-ray source (1486.74 eV) operating at a voltage of 13.85 kV (385 W) and PHOIBOS 150 hemispherical energy analyser and at pass energy of 50 eV. As an internal reference for the absolute binding energy, the C-1s peak (284.5 eV) was used. Ion chromatographic instrument from Metrohm (Herisau, Switzerland) consisting of a 709 IC Pump, 733 IC Separation Centre, a MSM Suppressor with 752 Pump unit and a 732 IC conductivity detector was used for the analysis. Steady-state optical absorption and emission spectra were recorded on a ThermoElectron model Biomate spectrophotometer and Hitachi model 4010 Spectrofluorometer respectively. Time resolved fluorescence measurements were carried out using a diode laser based spectrofluorimeter from IBH (UK). The instrument works on the principle of timecorrelated single photon counting (TCSPC). In the present work, 292 and 374 nm laser pulses were used as the excitation light sources and a TBX4 detection module (IBH) coupled with a special Hamamatsu PMT was used for fluorescence detection. 3) Results and Discussions The size and morphology of the CQDs were first characterized by high resolution transmission electron microscopy (HRTEM). The HRTEM image indicates that the formed CQDs are spherical in shape with average diameter of 4 ± 0.3 nm as shown as Figure 1A.

ACS Paragon Plus Environment

Page 8 of 30

Page 9 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 1. (A) HRTEM image of CQDs, (B) XRD pattern of CQDs, (C) FTIR spectrum of CQDs, (D) Deconvoluted spectrum of C 1s XPS. HRTEM measurement also reveals the crystalline nature of synthesized dots with lattice spacing of 0.33 nm and is consistent with (006) diffraction plane of graphitic carbons (JCPDS 26-1076). This observation suggests that the CQDs obtained herein are of graphitic structure51. We have recorded the XRD pattern of synthesized dots and are shown as Figure 1B. XRD shows a broad diffraction peak at ∼23.7° suggesting nanoparticle formation37. FTIR spectrum was recorded to determine the surface functional groups and is shown as Figure 1C. FTIR spectrum shows a very broad trough in the range of 2500-3300 cm-1 that clearly signifies the presence of acid –OH group on the surface of CQDs. FTIR peak at 1680 cm-1 corresponds to the carboxylic acid C=O group51 and peak at 1650 cm-1 signifies the presence of C=C graphitic carbon in CQDs37. FTIR data confirms that the formed CQDs are decorated with surface COOH functional groups. We have recorded the C 1s XPS spectrum of the synthesized dots and are shown as Figure 1D. Deconvoluted XPS spectrum shows

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

three peaks at 284.5 eV, 286.9 eV and 288.8 eV corresponding to the sp2 C=C, C-O and C=O respectively52. This again confirms that the formed CQDs have graphitic structure with surface carboxylic acid functional groups. To determine the optical properties of these dots steady state optical absorption spectrum was recorded and is shown as Figure 2A, inset. Steady state optical absorption spectrum suggests that CQDs have strong absorption in UV region with a hump at 350 nm. The band at 350 nm has been assigned to the n−π* transition corresponding to the carboxyl functional groups on the surface and the strong absorption below 300 nm suggests the π-π* transition of the conjugated C=C units in the carbon core as reported earlier also37. Steady state emission spectrum was recorded by exciting the sample at different wavelengths and is shown as Figure 2B. Steady state emission spectra clearly reveals that on photo-excitation at 290-320 nm CQDs exhibit two emission bands peaking at 385 nm and 450 nm. However the emission band at 385 nm vanishes as the sample was excited at wavelengths greater than 340 nm. We have also recorded the excitation spectrum of these dots to find out the states responsible for emission and are shown as Figure 2A. Excitation spectra indicate the presence of two bands peaking at 310 nm and 343 nm that corresponds to the λem 385 and 450 nm respectively. This suggests that the emission band at 385 nm corresponds to π-π* transition of the conjugated C=C units in the carbon core whereas the emission band at 450 nm corresponds to the n−π* transition of carboxyl functional groups on the surface of CQDs. It is interesting to observe from Figure 2B that the emission intensity at 385 nm is much less as compared to at 450 nm. It shows that the surface state emission dominates over core emission in the synthesized dots. Another feature to be noted from Figure 2B is that there is no change in emission peak position as the excitation wavelength is changed. Earlier many authors have carried out similar studies where they have shown that the emission spectra of CQDs is a function of excitation wavelength and both position as well as intensity changes with change

ACS Paragon Plus Environment

Page 10 of 30

Page 11 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 2. (A) Steady state excitation spectra of CQDs at two different emission wavelengths, λem- 450 nm and 380 nm. (A: Inset) Steady state absorption spectrum of CQDs. (B) Steady state emission spectra of CQDs at different excitation wavelengths. CQDs concentration was 50 ppm. in excitation wavelength31,37,38,45,46. They have suggested that such a change in position is due to different size of CQDs present in the sample31,38. However in our present investigation we have observed that only emission intensity changes with change in excitation wavelength while no change in emission position was observed. This observation further suggests that the synthesized dots are nearly mono disperse in nature and have similar type of emissive surface defects. As mentioned above that we aim to use these CQDs for fluoride ion detection, for this first we have monitored the interaction of CQDs with Eu3+. Since Eu3+ is a hard acid, it can interact with hard base, fluoride ion and a fluoride ion sensitive probe can be realized. Earlier few reports were available for fluoride ion detection12,34 based on this interaction. Butler12 have used two different complexes of europium for the detection of fluoride ion. However the synthesis of these complexes was a challenging task. Singh et al.34 have proposed CdTe QDs coupled Eu3+ system for selective detection of fluoride ions. However the toxicity of cadmium based QDs is well known and their application in real environment is a question of

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 30

debate. To overcome these difficulties and realizing a more economical and environmental friendly probe we have used a coupled system of CQDs with Eu3+ and carry out steady state absorption and emission studies. Steady state absorption studies suggest no complex formation between CQDs and Eu3+ (Figure S1). Steady state emission studies were carried out by exciting the samples at two different wavelengths and monitoring the emission. Figure 3A shows the steady state luminescence spectra of CQDs with different concentrations of Eu3+ by exciting the samples at 280 nm corresponding to the carbon core excitation and monitoring the emission. It is interesting to observe from Figure 3A that on addition of Eu3+ emission intensity decreases. Similar studies were also carried out by exciting the samples at 340 nm corresponding to the surface state excitation and monitoring the emission and is shown as Figure 3B. There also we have observed similar features and decrement in emission intensity on addition of Eu3+. However the decrement was more in surface state emission as compared to core emission. We compared these results and shown in Figure 3C. From Figure 3C it is clear that the effect of Eu3+ addition is more pronounced in surface state emission as

Figure 3. (A) and (B) Steady state emission spectrum of CQDs in absence and presence of different concentration of Eu3+ (A) λex- 280 nm, (B) λex- 340 nm, (a) [Eu3+] = 0 ppm

(b)

[Eu3+] = 10 ppm, (c) [Eu3+] = 20 ppm, (d) [Eu3+] = 50 ppm, (e) [Eu3+] = 100 ppm, (f) [Eu3+] = 250 ppm. (C) Comparison of emission intensity of CQDs on addition of Eu3+ at two different excitation wavelengths, λex- 280 nm and λex- 340 nm. CQDs concentration for all above experiments was 50 ppm.

ACS Paragon Plus Environment

Page 13 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

compared to core emission. Earlier Singh et al.34 have also carried out similar studies where they have monitored a quenching in CdTe QDs emission after interaction with Eu3+ and assigned to the aggregation of QDs. In our present study we have also observed the similar features and tried to understand the mechanism of this interaction. Earlier many authors demonstrated that CQDs are excellent electron donors and used them in variety of applications45,53,54. Das et al.45 have used these dots for degradation of organic pollutants where they have shown that electron transfer from CQDs to pollutants is responsible for degradation. Zhou et al.49 have used CQDs for detection of Hg2+ ions. They have shown that electron transfer process from CQDs to Hg2+ ions leads to luminescence quenching of CQDs. Wang et al.53 have demonstrated the application of these dots for detection of different derivatives of toluene and for photo-conversion of Ag+ to Ag through electron transfer process from CQDs. In our present study we have also observed a decrement in luminescence intensity of both core and surface state luminescence on addition of Eu3+ that might be due to electron transfer process from CQDs to Eu3+. To demonstrate this we have carried out time resolved emission studies and are shown as Figure 4A and 4B. Figure 4A shows the time resolved emission decay traces of CQDs in absence and in presence of Eu3+ by exciting the samples at 292 nm and monitoring the emission at 340 nm that corresponds to core state excitation and emission respectively. It is interesting to observe from Figure 4A that on addition of Eu3+, emission decay trace are faster (Figure 4A, b and 4A, c) as compared to pure CQDs (Figure 4A, a). This observation suggests that electron transfer process from CQDs to Eu3+ is favourable thereby a faster emission decay trace on addition of Eu3+ was observed. Similar studies were also carried out by exciting the samples at 374 nm and monitoring the emission at 450 nm that corresponds to surface state excitation and emission respectively and are shown as Figure 4B. Here also we have observed similar features and faster emission decay trace on addition of Eu3+ (Figure

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 4. (A and B) Time resolved emission decay trace of CQDs in presence of Eu3+, (A) λex- 292 nm, λem- 340 nm, (B) λex- 374 nm, λem- 450 nm, (a) pure CQDs, (b) CQDs + 50 ppm Eu3+, (c) CQDs + 250 ppm Eu3+. CQDs concentration for all above experiments was 50 ppm. (C) HRTEM image of CQDs on addition of 2500 ppm of Eu3+. CQDs concentration for HRTEM measurements was 500 ppm. 4B, b and 4B, c) as compared to without Eu3+ addition (Figure 4B, a). This again suggests electron transfer process from CQDs to Eu3+. Now it is interesting to observe from Figure 4A and 4B that the luminescence decay trace at surface state (Figure 4B) is much faster as compared to at core state (Figure 4A). Similar behaviours we have also observed in our steady state luminescence study where more decrement in surface state luminescence as compared to core state luminescence was observed after Eu3+ addition (Figure 3C). As we understand that electron transfer is distance dependent phenomenon and the rate of electron transfer decreases as distance increases55. The faster decay in surface state emission as compared to core state might be due to less distance of electron transfer in former as compared to later. To verify this we have carried out XPS studies of CQDs with Eu3+ and are shown as Figure S2. XPS analysis shows that Eu3+ binds with COOH group on surface state. This suggests a direct binding of Eu3+ with surface state thereby leading to both higher luminescence quenching and faster decay trace in surface state as compared to core state. Now to check the feasibility of other mechanism that is the aggregation of CQDs on addition

ACS Paragon Plus Environment

Page 14 of 30

Page 15 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

of Eu3+ we have carried out zeta potential measurements of CQDs in absence and in presence of Eu3+ and are given in Table 1. Here we would like to mention that we tried to carry out zeta potential studies at 50 ppm CQDs concentrations but the concentration was too low to get any significant value. Therefore we increased the CQDs concentration to 500 ppm and in the same ratio Eu3+ concentration was also increased. Zeta potential value for pure CQDs suggests that the surface charge is negative. The negative surface charge is due to the presence of COOH groups present on CQDs surface. This negative charge allows CQDs to be well separated from each other and chances of aggregation will be minimal as suggested by HRTEM measurements also (Figure 1A). Now on addition of Eu3+ surface charge decreases and becomes very less as given in Table 1. This suggests the interaction of Eu3+ ions with the surface COOH groups. This in turn has been confirmed by our XPS analysis (Figure S2) where Eu3+ binding with the surface COOH groups has been demonstrated clearly. This suggests that after Eu3+ addition CQDs interact with each other via Eu3+ thereby leading to aggregation of CQDs. This is confirmed by HRTEM image of CQDs after Eu3+ addition and is shown as Figure 4C. HRTEM measurement clearly shows aggregation of CQDs after Eu3+ addition. We have also carried out DLS measurement of CQDs before and after Eu3+ addition to further confirm this process and are shown as Figure S3. DLS measurement clearly Table 1: Zeta potential values of CQDs in presence and absence of Eu3+ and fluoride ion Concentration ratio

Zeta Potential

Concentration ratio

Zeta Potential

[CQDs:Eu3+]

(mV)

[CQDs:Eu3+: F-]

(mV)

No Eu3+ addition

-145±15

No Eu3+and F- addition

-145±15

2.5:1

-10±1

2.5:1:1

-70±5

1:1

9±1

1:1:1

-10±1

1:2

20±3

1:2

2±3

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

suggests that after Eu3+ addition, CQDs gets agglomerated and particle size increases substantially. The similar observation was also supported by our steady state absorption studies where on addition of Eu3+, the surface absorption peak shape changes and becomes less confined suggesting interaction of Eu3+ with COOH functional groups on CQDs surface (Figure S1). This observation suggests that the faster luminescence quenching of surface state as compared to core state is also due to aggregation of CQDs on addition of Eu3+. Therefore in our present investigation both electron transfer and aggregation are responsible for surface state luminescence quenching of CQDs on addition of Eu3+. We have shown these processes diagrammatically in Scheme 1. On photoexcitation of CQDs both core as well as surface state will be excited as shown in Scheme 1A and 1B respectively. Now on Eu3+ addition luminescence quenching occurs however only electron transfer from CQDs to Eu3+ is responsible for core state luminescence quenching as shown in Scheme 1A while both

Scheme 1: CQDs and its interaction with Eu3+. (A) Photoexcitation of core state of CQDs and subsequent electron transfer to Eu3+ (B) Photoexcitation of surface state of CQDs and subsequent electron transfer to Eu3+ (a) and aggregation of CQDs on Eu3+ addition (b).

ACS Paragon Plus Environment

Page 16 of 30

Page 17 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

electron transfer as well as aggregation are responsible for surface state luminescence quenching as shown in Scheme 1B. The aggregation induced luminescence quenching effects will be pronounced at surface state position but not in core as Eu3+ binds to the surface COOH groups of CQDs as shown in Scheme 1B and confirmed by XPS (Figure S2) and HRTEM studies (Figure 4C). Earlier many authors have shown the quenching of QDs luminescence in presence of foreign ions34,44,45,47,53,56 and assigned either to the charge transfer process or aggregation but in our present investigation we have observed that both the mechanisms are responsible for luminescence quenching. As demonstrated above that on addition of Eu3+ ions, photoluminescence of CQDs quenches (off). We use this system as a photoluminescent on-off-on probe for the detection of fluoride ions. We have already shown above that the surface state is much more luminescent as compared to core state (Figure 2). Also the effect of Eu3+ addition is much more pronounced in surface state as compared to core state. Taking into account both of these factors we have carried out steady state photoluminescence experiment of CQDs/Eu3+ system with different concentration of fluoride ions by exciting the surface state. Here we would like to mention that for fluoride ion detection we have chosen CQDs:Eu3+ concentration ratio 1:1. Although we have carried out experiment with higher concentration of Eu3+ also (Figure S4) but we did not get satisfactory results and change in luminescence intensity was marginal on addition of low concentration of fluoride ion. Therefore we have chosen the CQDs:Eu3+ concentration ratio 1:1. Figure 5A shows the change in photoluminescence intensity of CQDs/Eu3+ system on addition of fluoride ions. It is interesting to observe from Figure 5A that the luminescence intensity increases with increase in concentration of fluoride ion. This observation suggests that on addition of fluoride ions CQDs restores its photoluminescence properties (on) and this change in luminescence intensity can be used to quantify fluoride ion concentrations. We have also plotted corresponding calibration curve and is shown as Figure

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 5. (A) Photoluminescence spectra of CQDs-Eu3+ with increase in concentration of fluoride ion in water. (B) Respective graphical relationship of the Photoluminescence intensity against concentration of fluoride ion. CQDs and Eu3+ concentration are 50 ppm each. Bottom panel shows the mechanism of interaction involved. 5B. It is worth to note from Figure 5B that the calibration curve shows linearity in the concentration range 1-25 ppm of fluoride ion with R2 value of 0.991. We have also monitored the photoluminescence intensity of pure CQDs on addition of fluoride ion and are shown as Figure S5. From Figure S5 it is clear that there is no effect of only fluoride ion addition on CQDs emission intensity. This observation suggests that the interaction between fluoride ions and Eu3+ is involved for using CQDs as a probe for fluoride ion detection. To validate it further we have carried out experiments with higher concentration of fluoride ions (>50 ppm). Interestingly we have observed a precipitate formation in CQDs/Eu3+ sample after adding higher concentrations of fluoride ion. We separate this precipitate and recorded its

ACS Paragon Plus Environment

Page 18 of 30

Page 19 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

XRD pattern and are shown as Figure 6A. XRD pattern shows the formation of EuF3 in the sample. This observation further suggests that fluoride ion interacts with Eu3+ leading to the formation of EuF3 as shown in Figure 5 bottom panel. We have also taken TEM image of

Figure 6. (A) XRD pattern of EuF3, (B) HRTEM image of EuF3. (B: Inset) TEM image of EuF3. CQDs/Eu3+ with 100 ppm fluoride ion and are shown as Figure 6B, inset. TEM image show the formation of needle shaped crystal of EuF3. HRTEM image of these crystals are shown as Figure 6B that again confirms the formation of EuF3. These observations clearly suggest that fluoride ion interact with the Eu3+ ions bonded with CQDs surface and form EuF3. This leads to the removal of Eu3+ from the surface of CQDs thereby an increment in luminescence intensity of CQDs/Eu3+ after addition of fluoride ion was observed. We have also carried out elemental analysis of the precipitate that shows the presence of europium and fluoride in the sample. To support it further we have measured the zeta potential value after fluoride ion addition and are given in Table 1. Zeta potential value of CQDs/Eu3+ becomes negative after fluoride addition that clearly suggests that fluoride ion take away Eu3+ from CQDs surface thereby surface charge again becomes negative. Earlier Singh et al.34 have also used the similar strategy for fluoride ion detection. However they have used cadmium based QDs and

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

the toxicity of cadmium is well known. Therefore their application in real environment is a question of debate. Here we would like to mention that we have used carbon based QDs that are completely green and cost effective. Therefore using CQDs as a probe is both environmentally and economically more appreciable as compared to cadmium based QDs. As mentioned that CQDs coupled Eu3+ system can be used for the detection of fluoride ions, but in any environmental sample lot of other competing ions are also present. Therefore, to find the selectivity of the suggested probe for fluoride ion detection, we have carried out steady state luminescence measurements of CQDs/Eu3+ in presence of other major competing ions such as Cl-, Br-, I-, NO3-, CH3COO- and NO3- and are shown as Figure 7. It is interesting to observe from Figure 7 that only in presence of fluoride ion, luminescence intensity recovers to its original position while in presence of other ions such changes were not observed and the increment in photoluminescence intensity was not appreciable. This observation suggests that the suggested probe is selective for fluoride ion and can be used to detect fluoride ion in environmental samples. This high specificity could be attributed to the

100

%PL Intensity

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 30

F

QD

80

60

Cl

3+ Eu

40

2- CO3 NO 3

Br

I

CH3COO

Figure 7: Bar diagram for the selectivity test results obtained with the addition of different anions into the CQDs/Eu3+ system. CQDs and Eu3+ concentration are 50 ppm each. Concentrations of anions are 100 ppm each.

ACS Paragon Plus Environment

Page 21 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

specific and strong interaction of Eu3+ towards fluoride ion as compared to other ions. We also tested this probe for detection of fluoride ion in toothpaste sample where we found that the concentration of fluoride ion in the sample was ~ 350±20 µM that matches well with the result obtained from IC ~ 380±10 µM. 4) Conclusions To conclude, we have demonstrated a green, economic, rapid, sensitive, and specific photoluminescent on−off−on probe for the detection of fluoride ions. Our probe is based on CQDs and Eu3+ where we have clearly explained the working principle of this probe. On addition of Eu3+ ions photoluminescence of CQDs quenched (switch-off). This has been assigned to the both electron transfer from CQDs to Eu3+ ions and aggregation of CQDs on addition of Eu3+ and is confirmed by the time resolved measurements and HRTEM studies respectively. Interestingly on addition of fluoride ions luminescence intensity again increases (switch-on). This has been assigned to the detachment of Eu3+ from CQDs surface due to the formation of EuF3 that has subsequently been confirmed by XRD and HRTEM measurements. Furthermore the probe is found to be selective for fluoride ions and was also tested for real sample. To the best of our knowledge, this is the first report where CQDs coupled Eu3+ system is used as a photoluminescent probe for speedy and specific sensing of fluoride ions. The suggested probe is environmental friendly and cost effective and allows the detection of fluoride ions in real environmental samples. ASSOCIATED CONTENT Corresponding Author [email protected] (Pallavi Singhal), Phone: +91-22-2559 2349; [email protected] (Bal Govind Vats), Phone: +91-22-2559 0643. ORCID

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Pallavi Singhal: 0000-0003-0035-7846. Bal Govind Vats: 0000-0002-4936-6957. Author Contributions The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript. Funding Sources The authors declare no competing financial interest. ACKNOWLEDGMENTS The authors would like to acknowledge Dr K.K. Swain, ACD, BARC to provide IC facility, Dr. Deepak Tyagi, Chemistry Division, BARC for recording the XPS spectra. PS and SKJ would like to acknowledge Dr R. M. Tripathi, HS&EG, BARC for his support. BGV would like to acknowledge Dr. S. Kannan, FCD. BARC for his support. Supporting Information Supporting information is available free of charge on the ACS Publications website. Steady state absorption spectra of CQDs and CQDs/Eu3+ complex. C 1s XPS spectrum in CQDs/Eu3+ complex. Average size distribution of CQDs and CQDs/Eu3+. Photoluminescence spectra of CQDs/Eu3+ with increase in fluoride ion concentration. Photoluminescence spectra of CQDs with increase in concentration of fluoride ion in water. ABBREVIATIONS WHO, World Health Organization; SQDs, semiconductor quantum dots; CQDs, carbon quantum dots; TEM, transmission electron microscopy; XRD, X-ray diffraction; XPS; X-ray photoelectron spectroscopy; TCSPC, time-correlated single photon counting.

ACS Paragon Plus Environment

Page 22 of 30

Page 23 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

REFERENCES (1) Schmidtchen, F. P.; Berger, M.: Artificial Organic Host Molecules for Anions. Chemical Reviews 1997, 97, 1609-1646. (2) Martínez-Máñez, R.; Sancenón, F.: Fluorogenic and Chromogenic Chemosensors and Reagents for Anions. Chemical Reviews 2003, 103, 4419-4476. (3) Kang, S. O.; Llinares, J. M.; Powell, D.; VanderVelde, D.; Bowman-James, K.: New Polyamide Cryptand for Anion Binding. Journal of the American Chemical Society 2003, 125, 10152-10153. (4) Hudnall, T. W.; Chiu, C.-W.; Gabbaï, F. P.: Fluoride Ion Recognition by Chelating and Cationic Boranes. Accounts of Chemical Research 2009, 42, 388-397. (5) Gale, P. A.: Anion and Ion-Pair Receptor Chemistry: Highlights from 2000 and 2001. Coordination Chemistry Reviews 2003, 240, 191-221. (6) Sui, B.; Kim, B.; Zhang, Y.; Frazer, A.; Belfield, K. D.: Highly Selective Fluorescence Turn-On Sensor for Fluoride Detection. ACS Applied Materials & Interfaces 2013, 5, 29202923. (7) Yamaguchi, S.; Akiyama, S.; Tamao, K.: Colorimetric Fluoride Ion Sensing by BoronContaining π-Electron Systems. Journal of the American Chemical Society 2001, 123, 1137211375. (8) Kim, S. Y.; Park, J.; Koh, M.; Park, S. B.; Hong, J.-I.: Fluorescent Probe for Detection of Fluoride in Water and Bioimaging in A549 Human Lung Carcinoma Cells. Chemical Communications 2009, 4735-4737. (9) Vázquez, M.; Fabbrizzi, L.; Taglietti, A.; Pedrido, R. M.; González-Noya, A. M.; Bermejo, M. R.: A Colorimetric Approach to Anion Sensing: A Selective Chemosensor of Fluoride Ions, in which Color is Generated by Anion-Enhanced π Delocalization. Angewandte Chemie 2004, 116, 1996-1999.

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(10) Kim, T.-H.; Swager, T. M.: A Fluorescent Self-Amplifying Wavelength-Responsive Sensory Polymer for Fluoride Ions. Angewandte Chemie International Edition 2003, 42, 4803-4806. (11) Zheng, F.; Zeng, F.; Yu, C.; Hou, X.; Wu, S.: A PEGylated Fluorescent Turn-On Sensor for Detecting Fluoride Ions in Totally Aqueous Media and Its Imaging in Live Cells. Chemistry – A European Journal 2013, 19, 936-942. (12) Butler, S. J.: Quantitative determination of Fluoride in Pure Water using Luminescent Europium Complexes. Chemical Communications 2015, 51, 10879-10882. (13) Yang, C.; Xu, J.; Li, J.; Lu, M.; Li, Y.; Wang, X.: An Efficiently Colorimetric and Fluorescent Probe of Fluoride, Acetate and Phosphate Ions Based on a Novel Trinuclear EuComplex. Sensors and Actuators B: Chemical 2014, 196, 133-139. (14) Yang, C.; Xu, J.; Ma, J.; Zhu, D.; Zhang, Y.; Liang, L.; Lu, M.: An Efficient Long Fluorescence Lifetime Polymer-Based Sensor Based on Europium Complex as Chromophore for the Specific Detection of F-, CH3COO-, and H2PO4-. Polymer Chemistry 2012, 3, 26402648. (15) Yang, C.; Xu, J.; Zhang, R.; Zhang, Y.; Li, Z.; Li, Y.; Liang, L.; Lu, M.: An Efficient Eu-Based Anion-Selective Chemosensor: Synthesis, Sensing Properties, and its use for the Fabrication of Fluorescent Hydrogel Probe. Sensors and Actuators B: Chemical 2013, 177, 437-444. (16) Hu, J.; Zhang, G.; Geng, Y.; Liu, S.: Micellar Nanoparticles of Coil–Rod–Coil Triblock Copolymers for Highly Sensitive and Ratiometric Fluorescent Detection of Fluoride Ions. Macromolecules 2011, 44, 8207-8214. (17) Jiang, Y.; Hu, X.; Hu, J.; Liu, H.; Zhong, H.; Liu, S.: Reactive Fluorescence Turn-On Probes for Fluoride Ions in Purely Aqueous Media Fabricated from Functionalized Responsive Block Copolymers. Macromolecules 2011, 44, 8780-8790.

ACS Paragon Plus Environment

Page 24 of 30

Page 25 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

(18) Liu, J.-M.; Lin, L.-p.; Wang, X.-X.; Jiao, L.; Cui, M.-L.; Jiang, S.-L.; Cai, W.-L.; Zhang, L.-H.; Zheng, Z.-Y.: Zr(H2O)2EDTA Modulated Luminescent Carbon Dots as Fluorescent Probes for Fluoride Detection. Analyst 2013, 138, 278-283. (19) Hudnall, T. W.; Kim, Y.-M.; Bebbington, M. W. P.; Bourissou, D.; Gabbaï, F. P.: Fluoride Ion Chelation By a Bidentate Phosphonium/Borane Lewis Acid. Journal of the American Chemical Society 2008, 130, 10890-10891. (20) Chavali, R.; Gunda, N. S. K.; Naicker, S.; Mitra, S. K.: Rapid Detection of Fluoride in Potable Water using a Novel Fluorogenic Compound 7-O-tert-butyldiphenylsilyl-4methylcoumarin. Analytical Chemistry Research 2015, 6, 26-31. (21) Basu, A.; Suryawanshi, A.; Kumawat, B.; Dandia, A.; Guin, D.; Ogale, S. B.: Starch (Tapioca)

to

Carbon

Dots:

An

Efficient

Green

Approach

to

an

On-Off-On

Photoluminescence Probe for Fluoride Ion Sensing. Analyst 2015, 140, 1837-1841. (22) Cametti, M.; Rissanen, K.: Highlights on Contemporary Recognition and Sensing of Fluoride Anion in Solution and in the Solid State. Chemical Society Reviews 2013, 42, 20162038. (23) Roy, A.; Datar, A.; Kand, D.; Saha, T.; Talukdar, P.: A Fluorescent Off-On NBD-Probe for F- Sensing: Theoretical Validation and Experimental Studies. Organic & Biomolecular Chemistry 2014, 12, 2143-2149. (24) Zheng, X.; Zhu, W.; Liu, D.; Ai, H.; Huang, Y.; Lu, Z.: Highly Selective Colorimetric/Fluorometric Dual-Channel Fluoride Ion Probe, and Its Capability of Differentiating Cancer Cells. ACS Applied Materials & Interfaces 2014, 6, 7996-8000. (25) Mohapatra, S.; Sahu, S.; Nayak, S.; Ghosh, S. K.: Design of Fe3O4@SiO2@Carbon Quantum Dot Based Nanostructure for Fluorescence Sensing, Magnetic Separation, and Live Cell Imaging of Fluoride Ion. Langmuir 2015, 31, 8111-8120.

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(26) Zhou, Y.; Zhang, J. F.; Yoon, J.: Fluorescence and Colorimetric Chemosensors for Fluoride-Ion Detection. Chemical Reviews 2014, 114, 5511-5571. (27) Hinterholzinger, F. M.; Rühle, B.; Wuttke, S.; Karaghiosoff, K.; Bein, T.: Highly Sensitive and Selective Fluoride Detection in Water Through Fluorophore Release from a Metal-Organic Framework. Scientific Reports 2013, 3, 2562. (28) Kim, S. Y.; Hong, J.-I.: Chromogenic and Fluorescent Chemodosimeter for Detection of Fluoride in Aqueous Solution. Organic Letters 2007, 9, 3109-3112. (29) Wan, X.; Liu, T.; Liu, S.: Thermoresponsive Core Cross-Linked Micelles for Selective Ratiometric Fluorescent Detection of Hg2+ Ions. Langmuir 2011, 27, 4082-4090. (30) Liu, X. Y.; Bai, D. R.; Wang, S.: Charge-Transfer Emission in Nonplanar ThreeCoordinate Organoboron Compounds for Fluorescent Sensing of Fluoride. Angewandte Chemie 2006, 118, 5601-5604. (31) Dekaliuk, M. O.; Viagin, O.; Malyukin, Y. V.; Demchenko, A. P.: Fluorescent Carbon Nanomaterials: "Quantum Dots" or Nanoclusters? Physical Chemistry Chemical Physics 2014, 16, 16075-16084. (32) Demchenko, A. P.; Dekaliuk, M. O.: The Origin of Emissive States of Carbon Nanoparticles Derived from Ensemble-Averaged and Single-Molecular Studies. Nanoscale 2016, 8, 14057-14069. (33) Lou, Y.; Zhao, Y.; Zhu, J.-J.: Ultrasensitive Optical Detection of Anions by Quantum Dots. Nanoscale Horizons 2016, 1, 125-134. (34) Singh, P.; Prabhune, A. A.; Tripathi, C. S. P.; Guin, D.: Water-Soluble Photoluminescence on–off–on Probe for Speedy and Selective Detection of Fluoride Ions. ACS Sustainable Chemistry & Engineering 2017, 5, 982-987. (35) Singhal, P.; Ghorpade, P. V.; Shankarling, G. S.; Singhal, N.; Jha, S. K.; Tripathi, R. M.; Ghosh, H. N.: Exciton Delocalization and Hot Hole Extraction in CdSe QDs and CdSe/ZnS

ACS Paragon Plus Environment

Page 26 of 30

Page 27 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Type 1 Core Shell QDs Sensitized with Newly Synthesized Thiols. Nanoscale 2016, 8, 18231833. (36) Singhal, P.; Ghosh, H. N.: Ultrafast Hole/Electron Transfer Dynamics in a CdSe Quantum Dot Sensitized by Pyrogallol Red: A Super-Sensitization System. The Journal of Physical Chemistry C 2014, 118, 16358-16365. (37) Dhenadhayalan, N.; Lin, K.-C.; Suresh, R.; Ramamurthy, P.: Unravelling the Multiple Emissive States in Citric-Acid-Derived Carbon Dots. The Journal of Physical Chemistry C 2016, 120, 1252-1261. (38) Wang, Y.; Hu, A.: Carbon Quantum Dots: Synthesis, Properties and Applications. Journal of Materials Chemistry C 2014, 2, 6921-6939. (39) Sun, Y.-P.; Zhou, B.; Lin, Y.; Wang, W.; Fernando, K. A. S.; Pathak, P.; Meziani, M. J.; Harruff, B. A.; Wang, X.; Wang, H.; Luo, P. G.; Yang, H.; Kose, M. E.; Chen, B.; Veca, L. M.; Xie, S.-Y.: Quantum-Sized Carbon Dots for Bright and Colorful Photoluminescence. Journal of the American Chemical Society 2006, 128, 7756-7757. (40) Qian, Z.; Shan, X.; Chai, L.; Ma, J.; Chen, J.; Feng, H.: Si-Doped Carbon Quantum Dots: A Facile and General Preparation Strategy, Bioimaging Application, and Multifunctional Sensor. ACS Applied Materials & Interfaces 2014, 6, 6797-6805. (41) Bhunia, S. K.; Saha, A.; Maity, A. R.; Ray, S. C.; Jana, N. R.: Carbon Nanoparticlebased Fluorescent Bioimaging Probes. Scientific Reports 2013, 3, 1473. (42) Loo, A. H.; Sofer, Z.; Bouša, D.; Ulbrich, P.; Bonanni, A.; Pumera, M.: Carboxylic Carbon Quantum Dots as a Fluorescent Sensing Platform for DNA Detection. ACS Applied Materials & Interfaces 2016, 8, 1951-1957. (43) Liu, Z.; Chen, X.; Zhang, X.; Gooding, J. J.; Zhou, Y.: Targeted Drug Delivery: CarbonQuantum-Dots-Loaded Mesoporous Silica Nanocarriers with pH-Switchable Zwitterionic Surface and Enzyme-Responsive Pore-Cap for Targeted Imaging and Drug Delivery to

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Tumor (Adv. Healthcare Mater. 12/2016). Advanced Healthcare Materials 2016, 5, 13801380. (44) Dong, Y.; Wang, R.; Li, G.; Chen, C.; Chi, Y.; Chen, G.: Polyamine-Functionalized Carbon Quantum Dots as Fluorescent Probes for Selective and Sensitive Detection of Copper Ions. Analytical Chemistry 2012, 84, 6220-6224. (45) Das, R. K.; Kar, J. P.; Mohapatra, S.: Enhanced Photodegradation of Organic Pollutants by Carbon Quantum Dot (CQD) Deposited Fe3O4@mTiO2 Nano-Pom-Pom Balls. Industrial & Engineering Chemistry Research 2016, 55, 5902-5910. (46) Xu, H.; Yang, X.; Li, G.; Zhao, C.; Liao, X.: Green Synthesis of Fluorescent Carbon Dots for Selective Detection of Tartrazine in Food Samples. Journal of Agricultural and Food Chemistry 2015, 63, 6707-6714. (47) Gogoi, N.; Barooah, M.; Majumdar, G.; Chowdhury, D.: Carbon Dots Rooted Agarose Hydrogel Hybrid Platform for Optical Detection and Separation of Heavy Metal Ions. ACS Applied Materials & Interfaces 2015, 7, 3058-3067. (48) Li, H.; Zhai, J.; Sun, X.: Sensitive and Selective Detection of Silver(I) Ion in Aqueous Solution Using Carbon Nanoparticles as a Cheap, Effective Fluorescent Sensing Platform. Langmuir 2011, 27, 4305-4308. (49) Zhou, L.; Lin, Y.; Huang, Z.; Ren, J.; Qu, X.: Carbon Nanodots as Fluorescence Probes for Rapid, Sensitive, and Label-Free Detection of Hg2+ and Biothiols in Complex Matrices. Chemical Communications 2012, 48, 1147-1149. (50) Baruah, U.; Gogoi, N.; Majumdar, G.; Chowdhury, D.: β-Cyclodextrin and calix[4]arene-25,26,27,28-tetrol Capped Carbon Dots for Selective and Sensitive Detection of Fluoride. Carbohydrate Polymers 2015, 117, 377-383. (51) Tian, L.; Ghosh, D.; Chen, W.; Pradhan, S.; Chang, X.; Chen, S.: Nanosized Carbon Particles From Natural Gas Soot. Chemistry of Materials 2009, 21, 2803-2809.

ACS Paragon Plus Environment

Page 28 of 30

Page 29 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

(52) Jia, X.; Li, J.; Wang, E.: One-Pot Green Synthesis of Optically pH-Sensitive Carbon Dots with Upconversion Luminescence. Nanoscale 2012, 4, 5572-5575. (53) Wang, X.; Cao, L.; Lu, F.; Meziani, M. J.; Li, H.; Qi, G.; Zhou, B.; Harruff, B. A.; Kermarrec, F.; Sun, Y.-P.: Photoinduced Electron Transfers with Carbon Dots. Chemical Communications 2009, 3774-3776. (54) Fernando, K. A. S.; Sahu, S.; Liu, Y.; Lewis, W. K.; Guliants, E. A.; Jafariyan, A.; Wang, P.; Bunker, C. E.; Sun, Y.-P.: Carbon Quantum Dots and Applications in Photocatalytic Energy Conversion. ACS Applied Materials & Interfaces 2015, 7, 8363-8376. (55) Jia, Y.; Chen, J.; Wu, K.; Kaledin, A.; Musaev, D. G.; Xie, Z.; Lian, T.: Enhancing Photo-Reduction Quantum Efficiency using Quasi-Type II core/shell quantum dots. Chemical Science 2016, 7, 4125-4133. (56) Singhal, P.; Ghosh, H. N.: Hot-Hole Extraction from Quantum Dot to Molecular Adsorbate. Chemistry – A European Journal 2015, 21, 4405-4412.

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

TOC

ACS Paragon Plus Environment

Page 30 of 30