Magneto-Plasmonic Colloidal Nanoparticles Obtained by Laser Ablation of Nickel and Silver Targets in Water Cristina Gellini, Francis Leonard Deepak, Maurizio Muniz-Miranda, Stefano Caporali, Francesco Muniz-Miranda, Alfonso Pedone, Claudia Innocenti, and Claudio Sangregorio J. Phys. Chem. C, Just Accepted Manuscript • DOI: 10.1021/acs.jpcc.6b11628 • Publication Date (Web): 24 Jan 2017 Downloaded from http://pubs.acs.org on January 28, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

The Journal of Physical Chemistry C is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Magneto-Plasmonic Colloidal Nanoparticles Obtained by Laser Ablation of Nickel and Silver Targets in Water

Cristina Gellini a, Francis Leonard Deepak b, Maurizio Muniz-Miranda a,d,f *, Stefano Caporali a,d,f, Francesco Muniz-Miranda c, Alfonso Pedone c, Claudia Innocenti d,e, Claudio Sangregorio d,e a

Dipartimento di Chimica “Ugo Schiff”, Università di Firenze, Via b Lastruccia 3, 50019 Sesto Fiorentino (Italy); Department of Advanced Electron Microscopy, Imaging and Spectroscopy, International Iberian Nanotechnology Laboratory (INL), Avenida Mestre Jose Veiga, 4715-330 Braga (Portugal); c Dipartimento di Scienze Chimiche e Geologiche, Università di Modena e Reggio Emilia, Via Campi 103, 41125 Modena (Italy); d Consorzio Interuniversitario Nazionale per la Scienza e Tecnologia e dei Materiali (INSTM); Istituto di Chimica dei Composti Organometallici (ICCOM-CNR), Via Lastruccia 3, 50019 Sesto Fiorentino (Italy); f Istituto Sistemi Complessi (ISC-CNR), Via Madonna del piano 50019 Sesto Fiorentino (Italy) *corresponding author, e-mail: [email protected]

ABSTRACT

Stable magneto-plasmonic nanoparticles in colloidal suspensions are fabricated by two-step nanosecond-pulsed laser ablation of nickel and silver targets in pure water and characterized by UV-visible absorption, Raman, XPS and magnetic measurements, along with high-resolution electron microscopy analysis. These systems are constituted by a low-crystallinity matrix of ferromagnetic nickel hydroxide, where nickel oxide nanocrystals are embedded, with silver nanoparticles intimately linked to them. The SERS activity is assessed by adsorption of adenine as probe ligand. Spectroscopic investigation and DFT calculations revealed that adenine is linked to nickel oxide, while nanosilver essentially plays the role of ensuring the Raman enhancement for the adsorbed organic ligand. Both magnetic and plasmonic properties allow using these nanostructured bimetallic platforms as catalysts in chemical reactions or nanosensors in biomedicine as well as in environmental research.

ACS Paragon Plus Environment


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Introduction Due to the nature of transition metal, nanosized nickel has found applications in the fields of magnetic devices,1,2 catalysts,3,4 batteries,5 fuel cells,6,7solar cells8 among others. Hence, the synthesis of Ni nanoparticles has attracted considerable attention. The PLAL (Pulsed Laser Ablation in Liquid) technique allows obtaining Ni nanoparticles without reactants and byproducts in colloidal suspensions.9,10 However, when water is used as solvent, oxidized nickel nanoparticles are expected, due to the presence of oxygen dissolved in the aqueous environment. This can be a quite important result, because nanosized NiO is increasingly utilized in various fields as an efficient catalyst in the processes of decomposition, synthesis and transformation of organics, as well as a gas sensor in environmental investigation or biosensor in biomedical applications.11-18 In the bulk, whereas Ni is ferromagnetic, pure NiO exhibits insulating character and antiferromagnetic ordering at room temperature.19 Reducing the material size to the nanoscale, however, the resulting magnetic properties of NiO nanoparticles can be very complex depending on finite size effects and surface effects.20 In the present report, we have obtained magnetic nanoparticles by nanosecond-pulsed laser ablation of nickel in water and characterized them by spectroscopic and microscopic techniques. In addition, bimetallic (Ni-Ag) colloidal nanoparticles have been fabricated by successive ablation of silver in order to combine magnetic and catalytic properties, due to the nickel-containing nanoparticles, with the SERS (surfaceenhanced scattering) activity,21 ensured by the presence of nanosized silver. In the SERS effect, the strong localization of the electromagnetic field associated with the collective excitation waves, usually called plasmons, of the electrons localized at the nanostructured surface of metals with high optical reflectivity, such as silver, gold and copper, allows obtaining enhancements of several orders of magnitude (usually up to 107 factors) for the Raman response of the adsorbed molecules. In addition to this mechanism, also a chemical enhancement contribution, which usually provides Raman enhancement factors up to 102, can be effective, due to the perturbation of the molecular polarizability because of the formation of chemical complexes of the molecules with the active sites of the metallic surface. Hence, the SERS spectroscopy allows identifying, at trace level, reactants, products or by-products of reactions occurring where they take place, on the surface of the metal nanoparticles. Here we have employed a two-step laser ablation to fabricate nanostructured bimetallic systems, made of nickel, with strong performance in heterogeneous catalysis, and silver, as SERS-active metal. This preparation consists in


Page 2 of 39

Page 3 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


performing the laser ablation of a nickel target in pure water, followed by a successive laser ablation of a silver target in the same colloidal dispersion resulting from the first ablation. The aim of the present investigation is obtaining Ni-Ag nanocomposites to be employed as both catalysts and nanosensors, exploiting also their magnetic response, which could be useful in biomedicine and in environmental research, due to the particle mobility under magnetic field, allowing the transport of drugs in body fluids or the removal of contaminants in waters. Bimetallic nanosystems are usually prepared by following chemical routes, with consequent issues due to the presence of surfactants, organic stabilizers, reducing agents and reduction byproducts, which could cause interference in the SERS measurements, impairing the detection of the title analytes. The present work, based on the laser ablation of a nickel target, and successively of a silver target, in pure water in order to bypass the above purity problems, is, to our knowledge, the first work on nanoparticles containing nickel and silver obtained by this technique. The structural, spectroscopic, magnetic and plasmonic characterization of our bimetallic nanocomposites has been performed by UV-vis absorption, XPS and Raman spectroscopy, TEM/STEM microscopy, along with magnetization measurements at different temperatures. In particular, the SERS response has been tested by adopting adenine as probe molecule and analyzing the Raman data with the DFT (density functional theory) computational approach. This latter, based on model systems constituted by ligand molecules bound to adatoms or adclusters with one or few metal atoms, cannot reproduce the electromagnetic SERS enhancement, but it is generally sufficient to simulate the SERS profiles of the chemisorbed species, including band positions and relative intensities.22-25 In addition, these DFT calculations can provide information on the type of adsorbed species and of metal active-sites, as well as on the molecular sites of interaction with the substrate.

Experimental Section Materials Nickel (0.25-mm thickness, 99.9% purity) and silver (0.5-mm thickness, 99.9% purity) targets were purchased from Aldrich. Colloidal suspensions were prepared by laser ablation in deionized water (18.2 MΩ.cm @ 25oC) and characterized within two hours from the preparation. Laser ablation



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Laser ablation of nickel and silver targets was performed with the fundamental wavelength (1064 nm) of a Q-switched Nd:YAG laser (Quanta System G90-10: rep. rate 10 Hz, pulse width 10 ns). We performed the laser ablation of a nickel target in pure water, in order to obtain the Ni colloid; a part of this latter was used as aqueous medium for the successive laser ablation of a silver target, in order to obtain the bimetallic Ni-Ag colloid. The laser pulse energy was set at 20mJ/pulse (200 mW) with a laser spot of approximately 1-mm diameter and corresponding fluence of 2.5 J/cm2. The target plate was fixed at the bottom of a glass vessel filled with ~6 ml of liquid (height above the target: 2 cm). The irradiation time of the metal targets was about 20 minutes. To minimize effects due to crater formation in the metal target, the glass vessel was manually rotated and translated, stopping the ablation process every 3’. The laser pulse entered the vessel from above, thus impinging perpendicularly onto the target. ICP-AES measurements The determination of the Ni/Ag concentration ratio in the bimetallic colloidal suspension was performed in triplicate by a Varian 720-ES Inductively Coupled Plasma Atomic Emission Spectrometer (ICP-AES). ζ-potential measurements ζ-potential and Dynamic Light Scattering (DLS) analysis were performed with a Zetasizer Nano ZS90, Malvern Instruments. The temperature was ﬁxed at 25° C. Particle size measurements, obtained by Dynamic Light Scattering, range from 0.3 nm (diameter) to 5 microns, using 90° scattering optics. UV-visible absorption measurements UV–vis absorption spectra of colloidal suspensions were obtained in the 200÷800 nm region by using a Cary 5 Varian spectrophotometer. XPS measurements XPS measurements were performed in an ultra-high vacuum (10-9 mbar) system equipped with a VSW HAC 5000 hemispherical electron energy analyser and a non-monochromatised Mg-Kα Xray source (1253.6 eV). The source power was 120 W (12 kV x 10 mA) and the spectra were acquired in the constant-pass-energy mode at Epas = 22 eV. The overall energy resolution was 1.2 eV as a full-width at half maximum (FWHM) for the Ag 3d5/2 line of a pure silver reference.


Page 4 of 39

Page 5 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


The recorded spectra were fitted using CasaXPS software employing Gauss-Lorentz curves after subtraction of a Shirley-type background. The sample was introduced in the UHV system via a loadlock under inert gas (N2) flux, in order to minimize the exposure to air contaminants and kept in the introduction chamber for at least 12 hours before the measurements. Raman measurements Micro-Raman spectra of metal nanoparticles deposited on an aluminium plate were measured by a Renishaw RM2000 instrument, equipped with a diode laser emitting at 785 nm. Sample irradiation was accomplished by using the 50x microscope objective of a Leica Microscope DMLM. The backscattered Raman signal was fed into the monochromator through 40 µm slits and detected by an air-cooled CCD (2.5 cm-1 per pixel) filtered by a double holographic Notch filters system. Spectra were calibrated with respect to a silicon wafer at 520 cm-1. SERS spectra in the Ni-Ag colloid were measured after addition of adenine (Aldrich, purity ≥ 99%) in 2.5x10-5 M concentration, by using the 514.5-nm line of a Coherent Argon ion laser, a Jobin-Yvon HG2S monochromator equipped with a cooled RCA-C31034A photomultiplier and a data acquisition facility. To reduce the thermal effects due to the laser light, a defocused beam with low power (50 mW) was used for irradiating the colloidal samples. Power density measurements were performed with a power meter instrument (model 362; Scientech, Boulder, CO, USA) giving ~5% accuracy in the 300-1000 nm spectral range. Electron microscopy analysis To prepare the specimen for TEM (Transmission Electron Microscopy) and STEM (Scanning/Transmission Electron Microscopy) analysis, the samples were dispersed in ethanol by ultrasonication and a drop of this dispersion was placed on a holey carbon grid and dried. TEM/STEM analysis at both 80 kV and 200 kV was performed on FEI Titan ChemiSTEM equipped with probe corrector, Super-X EDS detector and Gatan EELS spectrometer. EDS (Energy Dispersive X-ray Spectrometry) quantification was carried out by employing the CliffLorimer method in Esprit Software. Magnetic measurements Magnetic measurements were performed on dry powder samples by a Superconducting Quantum Interference Device (SQUID) magnetometer (MPMS-XL7 Quantum Design Ldt.) as a function of the magnetic field (up to ± 50 kOe) at different temperatures in the interval 2-300K.



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Magnetization induced by a 1 kOe static magnetic was recorded as a function of temperature (5300K). Samples were always cooled down in the absence of a magnetic field. Computational details Density Functional Theory (DFT) calculations for model systems constituted by adenine linked to Ag+ ion or to a NiO molecule were carried out using the Gaussian 09 package,26 the B3LYP hybrid exchange and correlation functional,27,28 along with the LanL2DZ combined pseudopotential and basis set.29-31 The latter has been chosen because it provides good structural and spectroscopic properties in metal-hybrid nanoclusters in a reasonable computational time.32,33 The molecular structures of the adenine complexes with silver or nickel oxide and the corresponding vibrational frequencies were computed adopting tight convergence criteria. By allowing all the parameters to relax, the optimized geometries corresponded to true energy minima, as revealed by the lack of imaginary values in the vibrational mode calculations. The calculated Raman activities (Ai) were converted to relative Raman intensities (Ii) using the following relationship, as reported in the literature,34,35 Ii = f ( νo - νi ) 4 Ai/νi [1- exp (- h c νi / k T)] where νo is the exciting frequency (in cm-1 units), νi is the vibrational frequency (in cm-1 units) of the ith normal mode, h, c and k are fundamental constants and f is a suitably chosen common normalization factor for all peak intensities.

Results Colloidal stability The preparation protocol of the colloid obtained by ablation of the Ni target, hereafter called Ni colloid, and of that obtained by two-step ablation of Ni and Ag targets, hereafter called Ni-Ag colloid, is shown in Fig. 1(A). Both colloids are quite stable, as evidenced by strong positive ζpotential values, +34.2 and +28.0 mV for the Ni and Ni-Ag colloids, respectively. The positive ζ-potential values suggest that nickel is oxidized. In this case the oxygen atoms, which have negative partial charges and are exposed to the aqueous solvent, are able to attract positivelycharged species (for example, hydroxonium cations, H3O+), determining positive zeta potentials.


Page 6 of 39

Page 7 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


For Ag nanoparticles, instead, the metal surface exposed to the aqueous solvent assumes positive partial charge, allowing the adsorption of hydroxide anions and determining negative values of zeta potential, as reported in the literature.36 This explains why the laser ablation of silver in the colloid obtained by nickel ablation provokes a decrease of the (positive) zeta potential. The Ni / Ag weight ratio of the Ni-Ag colloid, as determined by ICP-AES measurements, is 1.59; by increasing the silver content produced by laser ablation, the value of ζ-potential further decreases, with consequent colloidal instability. Fig. 1(B) shows the effect of magnetic attraction due to a magnetic stir bar immersed in the Ni colloid, and that observed in the Ni-Ag colloid. The figure below shows both colloids as obtained by laser ablation, the figure above, instead, shows metal nanoparticles adhering to the magnetic stir bars. In the same figure the two metal targets of nickel and silver are also shown.

Fig. 1 – (A) Picture describing the preparation protocol of the Ni and Ni-Ag colloids. (B) Lower image: Ni colloid (left) and Ni-Ag colloid (right), as obtained by laser ablation. Upper image: Ni colloid (left) and Ni-Ag colloid (right) after application of magnetic field for the presence of magnetic stir bars.



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Spectroscopic characterization

Fig. 2 - UV-visible absorption spectra of the Ni (A) and Ni-Ag (B) colloids. C and D correspond to the spectra of the supernatant solutions of the Ni and Ni-Ag samples, respectively, after application of magnetic field for the presence of magnetic stir bars. The UV-visible absorption spectra of the Ni colloid (A) and of Ni-Ag colloid (B) are shown in Figure 2. In particular, the strong band around 400 nm (B) corresponds to the plasmon resonance of spheroidal silver nanoparticles. In the same figure, C and D show the spectral results (practically identical) for the supernatant solutions of the Ni and Ni-Ag samples, respectively, after application of magnetic field. This latter is performed by introducing a magnetic stir bar into the bottle containing the colloidal suspension. The absence of the spectral features due to nickel and silver (see A and B spectra) indicates that all metal nanoparticles have been removed from the aqueous medium by means of magnetic attraction.

The XPS spectrum (Fig. 3) shows that in the colloidal nanoparticles obtained by laser ablation of the nickel target in water, within a depth of about 5 nm, oxidized nickel as Ni(II) is largely predominant with respect to the Ni(0) content, by considering the observed binding energies that closely correspond to those reported in the literature.37 The presence of metallic nickel, however, could play a role in the effect of magnetic attraction, which is observed in the Ni colloid as well as in the bimetallic Ni-Ag colloid.


Page 8 of 39

Page 9 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Fig. 3 - XPS spectra of the deposited Ni colloid, along with the deconvoluted bands.

Raman measurements have been performed for the colloidal samples deposited on aluminum plate in order to identify the species of oxidized nickel present. Figure 4 shows the spectra registered by micro-Raman instrumentation and 785-nm excitation for different points of the dry film obtained from the deposition of Ni colloid: in the 500-530 cm-1 region a Raman band always occurs, in particular around 505 cm-1 or 525 cm-1. These spectral features can be attributed to the Ni-O stretching mode of the Ni(II) oxide, in agreement with what reported in the literature.38-42 Actually, a Raman band in the 500-530 cm-1 region could also be attributed to Ni(II) hydroxide, Ni(OH)2,43,44 although it is generally accompanied by two other bands at about 315 and 445 cm-1. As a conclusion, the Raman spectra cannot exclude the concomitant presence of NiO and Ni(OH)2, also taking into account the fact that two bands are observed at slightly different wavenumbers (505-525 cm-1) for different points of the dry film. A possible formation mechanism of these two species by nickel ablation can be proposed: in the presence of an oxidizing agent such as oxygen dissolved in water, Ni+2 is formed, which reacts with the water molecules giving hydroxide, Ni(OH)2, which in turn is partially transformed by dehydration into oxide, NiO. This hypothesis, however, would require time-resolved measurements for monitoring the fast reactions occurring during the process of laser ablation. Also for the bimetallic Ni-Ag colloid quite similar Raman bands are observed, to be considered therefore corresponding to the NiO and Ni(OH)2 species.



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Fig. 4 - Raman spectra of the Ni colloid deposited on Al plate for different points of the dry film.

Electron Microscopy analysis

Fig. 5 - Low-magnification STEM image of the Ni sample.

The STEM (Scanning/Transmission Electron Microscopy) images of the Ni colloid at low magnification (Fig. 5) show spherical nanoparticles immersed in a low-crystallinity matrix with


Page 10 of 39

Page 11 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


mucilaginous aspect (low contrast). The spherical nanoparticles shown in Figure 5 have diameters varying between 3 and 22 nm, with the mean value of 9.8 ± 0.1 nm (σ σ = 4.3 nm), but always with crystalline structure, as highlighted by HR-TEM (High-Resolution Transmission Electron Microscopy) and SAED (Selected Area Electron Diffraction) measurements shown in Figure 6 and Figure 7. This analysis shows interplanar distances corresponding to the planes (111), (200), (220) and (222) of nickel oxide (NiO). By considering these results, it is reasonable to assume the crystalline nanoparticles are made by NiO, whereas the mucilaginous material with low-crystallinity is probably formed by nickel hydroxide, Ni(OH)2.

Fig. 6 - HRTEM images of NiO nanocrystals with interplanar distances (Ni sample).

Fig. 7 - SAED analysis of NiO nanocrystals (Ni sample).

Fig. 8 - Low-magnification STEM image (Ni-Ag sample).



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

We have also performed the electron microscopy analysis of the bimetallic Ni-Ag colloid. A quite similar low-contrast matrix is observed (Fig. 8), where crystalline metal nanoparticles are interspersed. STEM-EDS (Scanning/Transmission Electron Microscopy -Energy Dispersive Xray Spectrometry) measurements (see Fig. 9), performed on these nanoparticles, show different situations occurring in the bimetallic colloid: Ag nanoparticles mixed with those of nickel (top panel); heterodimers consisting of Ag nanoparticles on the top of Ni nanoparticles (middle panel); silver clusters deposited on the surface of Ni nanoparticles (bottom panel). In all the cases, silver is intimately mixed with the nickel nanoparticles and this explains why silver nanoparticles are not observed in the Ni-Ag colloidal suspension after application of the magnetic field (see Fig. 1(B) and Fig. 2). The size distribution of the nanoparticles exhibits a mean value of 13.0 ± 0.1 nm (σ = 6.6 nm) in the range between 4 and 27 nm. The EDS maps of Ni, Ag and O for the bimetallic colloid, reported in Fig. S1 of the Supporting Information, show that nickel is really oxidized, unlike silver.

Fig. 9 - STEM-EDS images of NiO and Ag nanoparticles in the Ni-Ag sample.


Page 12 of 39

Page 13 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Magnetic properties

The magnetic characterization of the metal nanoparticles containing only nickel clearly shows the presence of a sharp transition around Tt = 20K, as evidenced by the magnetization data measured as a function of the temperature with a 1 T applied field (inset of Fig. 10). Moreover, the hysteresis cycles acquired at decreasing temperatures (Fig. 10) display a paramagnetic behaviour above Tt, while the onset of a magnetic order is observed below this temperature. This behaviour can be ascribed to Ni(OH)2, which is ferromagnetic in its α-phase with Curie temperature TC=13-23K and antiferromagnetic in the β-phase with Nèel temperature TN = 25-26 K.45 Due to the reduced size of the system, however, a shift of the characteristic transition temperatures to lower values is often observed and the two phases can be hardly distinguished and identified on the basis of the magnetic data. The shape of the low-temperature hysteresis loop, for instance, suggests the presence of the ferromagnetic α-Ni(OH)2, but, dealing with a nanosized system, it can be also originated by a strongly spin canted magnetic structure of the antiferromagnetically coupled β-phase.

Fig. 10 - Hysteresis loops measured at various temperatures for the Ni sample. In the inset, magnetization data as a function of temperature acquired with a 1 T magnetic field applied. The magnetization value is reported per gram of sample.



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The metal nanoparticles containing both nickel and silver display a similar behaviour with respect to the Ni colloidal sample (Fig. 11). The low temperature hysteresis loops of the two samples normalized to the remnant magnetization value are indeed superimposable (inset Fig. 11, left panel), the only small difference being in the approach to saturation at high field, which is less pronounced in the Ni sample. In addition, the high field magnetization per Ni gram is very similar for the two samples being 33.4 and 36.5 emu/g_Ni for the Ni and the Ni-Ag samples, respectively. Overall these data suggest that, in the Ni-Ag sample, nickel mostly occurs as hydroxide with a very small amount of Ni(0), while the presence of NiO nanoparticles cannot be unambiguously detected due to the very low signal of this magnetic phase. Since the Ni hydroxide is paramagnetic above Tt, the effect of this phase is less evident in the loop recorded at room temperature (Fig. 11, right panel) for Ni-Ag, where the weight of the diamagnetic contribution of silver determines a negative slope of the magnetization curve in the high field range.

Fig. 11 - Comparison of the hysteresis loops of the Ni sample (red lines) and Ni-Ag sample (black lines) at 2.5K (left panel) and 300K (right panel). Data are reported for gram of Ni occurring in the samples. The inset of left panel shows the magnetization curves normalized to the remanence value (M at H = 0).

SERS activity We have analysed the SERS response of the Ni-Ag colloid in order to verify the plasmonic characteristics of the bimetallic nanoparticles, in addition to the magnetic properties. Therefore, we have examined the SERS signal of adsorbed adenine (2.5x10-5 M concentration), by using the


Page 14 of 39

Page 15 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


laser excitation at 514.5 nm, suitable wavelength for the Raman enhancement of the Ag nanoparticles. Adenine has been chosen as probe molecule in the SERS experiments because it was widely studied spectroscopically and theoretically in previous articles.46,47



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Fig. 12 – (A) SERS spectra of adenine: in the Ni-Ag colloid (bottom panel); on Ni plate after deposition of silver colloidal nanoparticles (middle panel); in the monometallic Ag colloid (top panel). (B) DFT-simulated SERS spectra of the Ade(N7)/Ag+, Ade(N7)/NiO and Ade(N9)/NiO complexes. Fig. 12(A) shows the SERS spectrum of adenine in the bimetallic Ni-Ag colloid (bottom panel), compared with that of adenine added with the same concentration to the monometallic Ag colloid obtained by laser ablation (top panel). These spectra appear very different, in the band positions but especially in the relative intensities. However, the spectrum in the Ni-Ag colloid is quite similar to that obtained on smooth Ni plate after immersion in adenine water solution and deposition of silver colloidal nanoparticles (middle panel). This procedure was previously adopted to obtain the SERS spectra of organic ligands adsorbed on transition metals thanks to the activation due to the dry film of Ag colloidal nanoparticles deposited on smooth metal plates after incubation in the ligand aqueous solution and accurate rinsing with running solvent.48-51 The evident similarity points to the preferential adsorption of adenine on nickel in the Ni-Ag colloid, while the presence of nanosized silver has merely the role of ensuring the electromagnetic enhancement necessary for the observation of the SERS signal. As well as adenine results in being adsorbed on the nickel plate that is oxidized in the surface layer, similarly in the Ni-Ag colloid adenine is adsorbed on the surface of the nickel oxide nanoparticles. By analyzing in more detail the spectra shown in Fig. 12(A), we note that the SERS spectrum of adenine adsorbed on silver nanoparticles is dominated by a band at about 735 cm-1, corresponding to the ring breathing mode of all the aromatic system.46 In the case of adsorption on NiO nanoparticles, instead, the ring breathing band has intensity comparable to those of the bands recorded at higher frequencies. We have analysed this spectral evidence by DFT (density functional theory) calculations, by considering model systems constituted by an adenine molecule linked to an Ag+ adatom, as well as previously performed,47 or to the nickel atom of a NiO molecule. Adenine is known to exist in aqueous solution in two tautomeric forms,52,53 shown in Fig. S2 of the Supporting Information, by considering a hydrogen atom bound to the nitrogen atom N7 or N9. In the literature,47,54,55 the ring atom N3 of adenine was ascertained by SERS results and DFT calculations to be the preferential candidate to link metal nanoparticles, for both N7 and N9 tautomers. Here, we have considered a model, called Ade(N7)/NiO, with the tautomer N7 interacting with nickel oxide, similarly to that assumed for adenine adsorbed on silver and gold.47 The simulated Raman spectra, shown in Fig. 12(B), allow reproducing the different intensity patterns of the SERS spectra in Ag and Ni-Ag colloids


Page 16 of 39

Page 17 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


reported in Fig. 12(A), with prominent bands corresponding to the observed SERS bands (see Table S1 of the Supporting Information). Normal modes of the Ade(N7)/NiO model are described in Fig. S3 of the Supporting Information. The DFT-optimized structures of Fig. 13 show that the interaction of adenine with silver involves both rings of the molecule, which instead is linked to nickel oxide only through the atom N3 of the pyrimidinic ring. Another model has been considered, consisting of the tautomer N9 linked to NiO through the N3 atom (Ade(N9)/NiO model), whose DFT-optimized structure is also shown in Fig.13, but its simulated SERS profile and calculated frequencies strongly differ from the experimental ones (see Fig. 12(B) and Table S1). As a conclusion, the DFT approach allows confirming the adsorption of adenine on NiO, as suggested by the SERS measurements, instead of on Ag nanoparticles. This result could be important in view of possible applications of our Ni-Ag nanocomposites in catalytic reactions that provide for the direct interaction of organic reagents with the surface of the NiO nanoparticles. Finally, a consideration on the SERS intensities observed in the colloids is necessary. The intensity of the SERS spectrum in laser-ablated Ag colloid could be strongly increased by addition of chloride anions, as recently reported,56 but our aim here was to compare the SERS spectra obtained in Ag and Ni-Ag colloids without the chloride activation. The SERS spectrum of adenine in the bimetallic colloid appears weaker than that recorded in silver colloid, as immediately deduced from the signal-to-noise ratios. One must consider that in the Ag colloid the SERS intensity depends essentially on the electromagnetic effect due to the silver nanoparticles, to which the molecule is chemically bound. In the bimetallic colloid, instead, the SERS/DFT analysis has showed that the molecule is not linked to silver, but to nickel oxide, which is incapable of promoting enhancement. In this case, the electromagnetic enhancement is ensured by the silver nanoparticles that are located in the immediate vicinity. Therefore, it is expected a weaker SERS effect than that found by adsorption on silver.



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Fig. 13 - DFT-optimized structures of Ade(N7)/Ag+, Ade(N7)/NiO, Ade(N9)/NiO complexes. Bond distances in Å.

Conclusions We have obtained stable bifunctional nanoparticles in colloidal suspension by a two-step laser ablation of nickel and silver in pure water, exhibiting both magnetic and plasmonic properties. This procedure avoids the presence of surfactants, organic stabilizers, reducing agents and reduction by-products, which could represent an impediment to both the absorption of organic ligands and the observation and interpretation of the SERS bands. To our knowledge, this is the first work on colloidal nanoparticles containing nickel and silver obtained by this technique. Magnetic, UV-vis absorption, Raman and XPS measurements, along with high-resolution TEM analysis, show that such systems are constituted by a low-crystallinity matrix of nickel hydroxide, where nickel oxide nanocrystals are embedded, with silver nanoparticles intimately linked to them. The SERS activity is assessed by the adsorption of adenine, which results in being linked to nickel oxide by spectroscopic investigation corroborated by DFT computational approach, while nanosilver essentially plays the role of ensuring the Raman enhancement for the adsorbed organic ligand. This study paves the way to the use of these nanostructured platforms as both catalysts, due to the presence of nickel oxide, and nanosensors in environmental research, due to the silver nanoparticles. Actually, nickel and its compounds, especially in nanometric form, are able to promote different catalytic reactions; the presence of nanometric silver, instead, allows identifying, by SERS measurements, adsorbed reactants, products and byproducts. In addition, being our bimetallic material completely separable by magnetic attraction from the aqueous environment where it is dispersed, it will be possible to identify traces of possible adsorbed contaminants by means of the SERS spectroscopy and to remove them by application of magnetic field. Unlike colloidal nanoparticles consisting of iron oxides, for example magnetite (Fe3O4), which are widely used in biomedicine (see, for example, ref. 57), in our case biomedical applications appear to be less suitable, since nickel is not biocompatible, being allergenic, with possible carcinogenic effects (see, for example, ref. 58). Finally, for the proposed applications, the “purity“ of our colloidal suspensions, free from the presence of chemical products as obtained by laser ablation of metal targets in water, is a very important requisite.


Page 18 of 39

Page 19 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Supporting Information: microscopic measurements and computational details.

Ackowledgments The CINECA consortium granted computation time within the research project AUNANMRHP10CJ027S. Francis Leonard Deepak acknowledges the financial support provided by NORTE 2020 through the European Regional Development Fund (ERDF). The authors thank Dr. Giancarlo Margheri (CNR-ISC) for the zeta potential measurements.

References 1. Mary, A. P. R.; Sandeep, C. S. S.; Narayanan, T. N.; Philip, R.; Moloney, P.; Ajayan, P. M.; Anantharaman, M. R. Nonlinear and Magneto-Optical Transmission Studies on Magnetic Nanofluids of Non-Interacting Metallic Nickel Nanoparticles. Nanotechnology 2011, 22, 375702. 2. Pascu, O.; Caicedo, J. M.; Fontcuberta, J.; Herranz, G.; Roig, A. Magneto-Optical Characterization of Colloidal Dispersions. Application to Nickel Nanoparticles. Langmuir 2010, 26, 12548-12552. 3. Metin, Ö.; Mazumder, V.; Özkar, S.; Sun, S. Monodisperse Nickel Nanoparticles and Their Catalysis in Hydrolytic Dehydrogenation of Ammonia Borane. J. Am. Chem. Soc. 2010, 132, 1468-1469. 4. Aguilhon, J.; Boissière, C.; Durupthy, O.; Thomazeau, C.; Sanchez, C. Nickel Nanoparticles with Controlled Morphologies Application in Selective Hydrogenation Catalysis. Stud. Surf. Sci. Catal. 2010, 175, 521-524. 5. Mai, Y. J.; Tu, J. P.; Gu, C. D.; Wang, X. L. Graphene Anchored with Nickel Nanoparticles as a High-Performance Anode Material for Lithium Ion Batteries. J. Power Sources 2012, 209, 1-6.



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

6. Tehrani, R. M. A.; Ab Ghani, S. The Nanocrystalline Nickel with Catalytic Properties on Methanol Oxidation in Alkaline Medium. Fuel Cells 2009, 9, 579-587. 7. Ewing, S. J.; Lan, R.; Xu, X. X.; Tao, S. W. Synthesis of Dendritic Nano-Sized Nickel for Use as Anode Material in an Alkaline Membrane Fuel Cell. Fuel Cells 2010, 10, 72-76. 8. Rahman, Md. M.; Im, S. H.; Lee, J.-J. Enhanced Photoresponse in Dye-Sensitized Solar Cells Via Localized Surface Plasmon Resonance Through Highly Stable Nickel Nanoparticles. Nanoscale 2016, 8, 5884-5891. 9. Jung, H. J.; Choi, M. Y. Specific Solvent Produces Specific Phase Ni Nanoparticles: A Pulsed Laser Ablation in Solvents. J. Phys. Chem. C 2014, 118, 14647-14654. 10. Ganjali, M.; Ganjali, M.; Vahdatkhah, P.; Marashi, S. M. B. Synthesis of Ni Nanoparticles by Pulsed LaserAblation Method in Liquid Phase. Procedia Materials Science 2015, 11, 359363. 11. Cruz-Ortiz, B. R.; Garcia-Lobato, M. A.; Larios-Duran, E. R.; Muzquiz-Ramos, E. M.; Ballesteros-Pacheco, J. C. Potentiostatic Electrodeposition of Nanostructured NiO Thin Films for Their Application as Electrocatalyst. J. Electroanal. Chem. 2016, 772, 38-45. 12. Singh, A.; Fekete, M.; Gengenbach, T.; Simonov, A. N.; Hocking, R. K.; Chang, S. L. Y.; Rothmann, M.; Powar, S.; Fu, D.; Hu, Z.; et al. Catalytic Activity and Impedance Behavior of Screen-Printed Nickel Oxide as Efficient Water Oxidation Catalysts. ChemSusChem 2015, 8, 4266-4274. 13. Patra, A. K.; K. Kundu, S. K.; Kim, D.; Bhaumik, A. Controlled Synthesis of a HexagonalShaped NiO Nanocatalyst with Highly Reactive Facets {110} and Its Catalytic Activity. ChemCatChem 2015, 7, 791-798. 14. Yang, F.; Guo, Z. Engineering NiO Sensitive Materials and Its Ultra-Selective Detection of Benzaldehyde. J. Colloid Interface Sci. 2016, 467, 192-202. 15. Chen, N.; Li, Q.; Li, Y.; Deng, D.; Xiao, X.; Wang, Y. Facile Synthesis and Gas Sensing Performances Based on Nickel Oxide Nanoparticles/Multi-Wall Carbon Nanotube Composite. J Mater Sci: Mater Electron. 2015, 26, 8240-8248.


Page 20 of 39

Page 21 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


16. Yu, T.; Cheng, X.; Zhang, X.-F.; Sui, L.; Xu, Y.; Gao, S.; Zhao, H.; Huo, L.-H. Highly Sensitive H2S Detection Sensors at Low Temperature Based on Hierarchically Structured NiO Porous Nanowall Arrays. J. Mat. Chem. A 2015, 3, 11991-11999. 17. Aydogdu, G.; Zeybek, D. K.; Zeybek, B.; Pekyardimci, S. Electrochemical Sensing of NADH on NiO Nanoparticles-Modified Carbon Paste Electrode and Fabrication of Ethanol Dehydrogenase-Based Biosensor. J. Appl. Electrochem. 2013, 43, 523-531. 18. Li, C.; Liu, Y.; Li, L.; Du, Z.; Xu, S.; Zhang, M.; Yin, X.; Wang, T. A Novel Amperometric Biosensor Based on NiO Hollow Nanospheres for Biosensing Glucose. Talanta 2008, 77, 455-459. 19. Kodama, R. H.; Makhlouf, S. A.; Berkowitz, A. E. Finite Size Effects in Antiferromagnetic NiO Nanoparticles. Phys. Rev. Lett. 1997, 79, 1393-1396. 20. Kisan, B.; Shyni, P. C.; Layek, S.; Verma, H. C.; Hesp, D.; Dhanak, V.; Krishnamurthy, S.; Perumal, A. Finite Size Effects in Magnetic and Optical Properties of Antiferromagnetic NiO Nanoparticles. IEEE Trans. Magn. 2014, 50, 2300704. 21. Schlücker, S. Surface Enhanced Raman Spectroscopy: Analytical, Biophysical and Life Science Applications; Wiley-VCH: Weinheim, Germany, 2011. 22. Owen, A. R.; Golden, J. W.; Price, A. S.; Henry, W. A.; Barker, W. K.; Perry, D. A. SurfaceEnhanced Vibrational Spectroscopy and Density Functional Theory Study of Isoniazid Layers Adsorbed on Silver Nanostructures. J. Phys. Chem. C 2014, 118, 28959-28969. 23. Muniz-Miranda, M.; Pagliai, M. Positively Charged Active Sites for the Adsorption of FiveMembered Heterocycles on Silver Colloids. J. Phys. Chem. C 2013, 117, 2328-2333. 24. Huang, W.; Jiang, J.-Z., Chen, L.; Zhang, B.-Q.; Deng, S.-F.; Sun, J. J.; Chen, W.-K. Density Functional Theory and Surface Enhanced Raman Spectroscopy Studies of Tautomeric Hypoxanthine and Its Adsorption Behaviors in Electrochemical Processes. Electrochim. Acta 2015, 164, 132-138. 25. Muniz-Miranda, M.; Muniz-Miranda, F.; Pedone, A. Raman and DFT Study of Methimazole Chemisorbed on Gold Colloidal Nanoparticles. Phys. Chem. Chem. Phys. 2016, 18, 59745980.



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 39

26. Frisch, M. J.; Trucks, G. W.; Schlegel, H. B; et al. Gaussian 09, Revision D.01. Gaussian, Inc., Wallingford, CT (USA). 27. Becke, A. D. Density‐Functional Thermochemistry. III. The Role of Exact Exchange. J. Chem. Phys. 1993, 98, 5648-52. 28. Lee, C.; Yang, W.; Parr, R. G. Development of the Colle-Salvetti Correlation-Energy Formula Into a Functional of the Electron Density. Phys. Rev. B 1988, 37, 785-89. 29. Hay, P. J.; Wadt, W. R. Ab Initio Effective Core Potentials for Molecular Calculations. Potentials for the Transition Metal Atoms Sc to Hg. J. Chem. Phys. 1985, 82, 270. 30. Wadt, W. R.; Hay, P. J. Ab Initio Effective Core Potentials for Molecular Calculations. Potentials for Main Group Elements Na to Bi. J. Chem. Phys. 1985, 82, 284. 31. Hay, P. J.; Wadt, W. R. Ab Initio Effective Core Potentials for Molecular Calculations. Potentials for K to Au Including the Outermost Core Orbitals. J. Chem. Phys. 1985, 82, 299. 32. Muniz-Miranda, F.; Menziani, M. C.; Pedone, A. Assessment of Exchange-Correlation Functionals in Reproducing the Structure and Optical Gap of Organic-Protected Gold Nanoclusters. J. Phys. Chem. C 2014, 118, 7532-7544. 33. Muniz-Miranda, F.; Menziani, M. C.; Pedone, A. DFT and TD-DFT Assessment of the Structural and Optoelectronic Properties of an Organic–Ag14 Nanocluster. J. Phys. Chem. A 2015, 119, 5088-5098. 34. Keresztury, G.; Holly, S.; Besenyei, G.; Varga, J.; Wang, Aiying; Durig, J. R. Vibrational Spectra of Monothiocarbamates-II. IR and Raman Spectra, Vibrational Assignment, Conformational

Analysis

and

Ab

Initio

Calculations

of

S-Methyl-N,N-

Dimethylthiocarbamate. Spectrochim. Acta A. 1993, 49, 2007-2017; 2019-2026. 35. Keresztury, G. in Handbook of Vibrational Spectroscopy, J. M. Chalmers, P. R. Griffiths (Eds.), Wiley & Sons: Chichester, U.K., 2002, vol. 1, p. 71. 36. Perito, B.; Giorgetti, E.; Marsili, P.; Muniz-Miranda, M. Antibacterial Activity of Silver Nanoparticles Obtained by Pulsed Laser Ablation in Pure Water and in Chloride Solution. Beilstein J. Nanotechnol. 2016, 7, 465–473.


Page 23 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


37. Grosvenor, A. P.; Biesinger, M. C.; Smart, R. St. C.; McIntyre, N. S. New Interpretation of XPS Spectra of Nickel Metal and Oxides. Surf. Sci. 2006, 600, 1771-1779. 38. Yuvakkumar, R.; Lee, S.; Lee, G. W.; Hong, S. I. An Environment Benign Biomimetic Synthesis of Mesoporous NiO Concentric Stacked Doughnuts Architecture. Micropor. Mesopor. Mat. 2015, 207, 185-194. 39. Tadic, M.; Panjan, M; Markovic, D; Stanojevic, B; Jovanovic, D.; Milosevic, I.; Spasojevic, V. NiO Core–Shell Nanostructure with Ferromagnetic-Like Behavior at Room Temperature. J. Alloys Compd. 2014, 586, S322-S325. 40. Leontyeva, D. V.; Leontyev, I. N.; Avramenko, M. V.; Yuzyuk, Yu. I.; Kukushkina, Yu. A.; Smirnova, N. V. Electrochemical Dispergation as a Simple and Effective Technique Toward Preparation of NiO Based Nanocomposite for Supercapacitor Application. Electrochim. Acta 2013, 114, 356– 362. 41. Vidales-Hurtado, M. A.; Mendoza-Galván, A. Electrochromism in Nickel Oxide-Based Thin Films Obtained by Chemical Bath Deposition. Solid State Ionics 2008, 179, 2065–2068. 42. Dharmaraj, N.; Prabu, P.; Nagarajan, S.; Kim, C. H.; Park, J. H.; Kim, H. Y. Synthesis of Nickel Oxide Nanoparticles Using Nickel Acetate and Poly(vinyl acetate) Precursor. Mat. Sci. Eng. B 2006, 128, 111-114. 43. Hermet, P.; Gourrier, L.; Bantignies, J.-L.; Ravot, D.; Michel, T.; Deabate, S.; Boulet, P.; Henn, F. Dielectric, Magnetic, and Phonon Properties of Nickel Hydroxide. Phys. Rev. B 2011, 84, 235211. 44. Murli, C.; Sharma, S. M.; Kulshreshtha, S. K.; Sikka, S. K. High-Pressure Behavior of βNi(OH)2 - A Raman Scattering Study. Physica B 2011, 307, 111-116. 45. Hall, D. S.; Lockwood, D. J.; Bock, C.; MacDougall, B. R. Nickel Hydroxides and Related Materials: a Review of Their Structures, Synthesis and Properties. Proc. Royal Soc. A 2015, 471, 20140792. 46. Muniz-Miranda, M.; Gellini, C.; Pagliai, M.; Innocenti, M.; Salvi, P. R; Schettino, V. SERS and Computational Studies on MicroRNA Chains Adsorbed on Silver Surfaces. J. Phys. Chem. C 2010, 114, 13730-13735.



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

47. Pagliai, M.; Caporali, S.; Muniz-Miranda, M.; Pratesi, G.; Schettino, V. SERS, XPS, and DFT Study of Adenine Adsorption on Silver and Gold Surfaces. J. Phys. Chem. Lett. 2012, 3, 242-245. 48. Muniz-Miranda, M. Surface Enhanced Raman Scattering of 2,2'-Bipyridine Adsorbed on Smooth Nickel Surfaces. J. Raman Spectrosc. 2000, 31, 637-639. 49. Muniz-Miranda, M.; Pergolese, B.; Bigotto, A.; Giusti, A.; Innocenti, M. A Raman and AFM Investigation on Metal Surfaces SERS-Activated by Silver Colloidal Nanoparticles. Mat. Sci. Eng. C 2007, 27, 1295-1299. 50. Muniz-Miranda, M.; Pergolese, B.; Bigotto, A. SERS and DFT Investigation on the Adsorption of 1,10-Phenanthroline on Transition Metal Surfaces. Phys. Chem. Chem. Phys. 2010, 12, 1145-1151. 51. Muniz-Miranda, M.; Pergolese, B.; Muniz-Miranda, F.; Caporali, S. SERS Effect from Pd Surfaces Coated with Thin Films of Ag Colloidal Nanoparticles. J. Alloys Compd. 2014, 615, S357-S360. 52. Dreyfus, M.; Dodin, G.; Bensaude, O.; Dubois, J. E. Tautomerism of Purines. I. N(7)H↔N(9)H Equilibrium in Adenine. J. Am. Chem. Soc. 1975, 97, 2369-2376. 53. Wiórkiewicz-Kuczera, J.; Karplus, M. Ab Initio Study of the Vibrational Spectra of N9-H and N7-H Adenine and 9-Methyladenine. J. Am. Chem. Soc. 1990, 112, 5324-5340. 54. Kundu, J.; Neumann, O.; Janesko, B. G.; Zhang, D.; Lal, S.; Barhoumi, A.; Scuseria, G. E.; Halas, N. J. Adenine - and Adenosine Monophosphate (AMP) - Gold Binding Interactions Studied by Surface-Enhanced Raman and Infrared Spectroscopies. J. Phys. Chem. C 2009, 113, 14390-1439. 55. Lang, X.-F.; Yin, P.-G.; You, T.-T.; Jiang, L.; Guo, L. A DFT Investigation of SurfaceEnhanced Raman Scattering of Adenine and 2’-Deoxyadenosine 5’-Monophosphate on Ag20 Nanoclusters. ChemPhysChem 2011, 12, 2468-2475. 56. Giorgetti, E.; Marsili, P.; Giammanco, F.; Trigari, S.; Gellini, C.; Muniz-Miranda, M. Ag Nanoparticles Obtained by Pulsed Laser Ablation in Water: Surface Properties and SERS Activity. J. Raman Spectrosc. 2015, 46, 462–469.


Page 24 of 39

Page 25 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


57. Pang, Y.; Wang, C.; Wang, J.; Sun, Z.; Xiao, R.; Wang, S. Fe3O4@Ag Magnetic Nanoparticles for MicroRNA Capture and Duplex-Specific Nuclease Signal Amplification Based SERS Detection in Cancer Cells, Biosens. Bioelectron. 2016, 79, 574–580. 58. Siddiqui, M. A.; Ahamed, M; Ahmad, J.; Majeed Khan, M. A.; Musarrat, J.; Al-Khedhairy, A. A.; Alrokayan, S. A. Nickel Oxide Nanoparticles Induce Cytotoxicity, Oxidative Stress and Apoptosis in Cultured Human Cells That Is Abrogated by the Dietary Antioxidant Curcumin, Food Chem. Toxicol. 2012, 50, 641–647.



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

82x46mm (96 x 96 DPI)


Page 26 of 39

Page 27 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Fig. 1 238x174mm (96 x 96 DPI)



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 2 262x194mm (96 x 96 DPI)


Page 28 of 39

Page 29 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60





1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60



Page 30 of 39

Page 31 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 5



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60



Page 32 of 39

Page 33 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60





1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60



Page 34 of 39

Page 35 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60





1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Fig. 10 145x117mm (96 x 96 DPI)


Page 36 of 39

Page 37 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Fig.11 237x100mm (96 x 96 DPI)



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Fig.12 183x275mm (96 x 96 DPI)


Page 38 of 39

Page 39 of 39

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Fig. 13 525x219mm (96 x 96 DPI)