Mechanochemically Synthesized SnS Nanocrystals: Impact of

5 mins ago - We demonstrate non-toxic, earth-abundant light-absorbing SnS thin films fabricated by a low-cost, environmentally friendly non-vacuum pro...
1 downloads 11 Views 3MB Size
Subscriber access provided by Warwick University Library

Article

Mechanochemically Synthesized SnS Nanocrystals: Impact of Nonstoichiometry on Phase Purity and Solar Cell Performance Bo-In Park, Yoon Hee Jang, Seung Yong Lee, and Doh-Kwon Lee ACS Sustainable Chem. Eng., Just Accepted Manuscript • DOI: 10.1021/ acssuschemeng.7b02711 • Publication Date (Web): 29 Jan 2018 Downloaded from http://pubs.acs.org on February 3, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Sustainable Chemistry & Engineering is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Mechanochemically Synthesized SnS Nanocrystals: Impact of Nonstoichiometry on Phase Purity and Solar Cell Performance Bo-In Park,†,⊥ Yoon Hee Jang,‡,⊥ Seung Yong Lee,*,†,§ and Doh-Kwon Lee*,‡,§ †

Center for Materials Architecturing, Korea Institute of Science and Technology, Hwarang-ro

14-gil 5, Seongbuk-gu, Seoul 02792, Korea ‡

Photo-electronic Hybrids Research Center, Korea Institute of Science and Technology,

Hwarang-ro 14-gil 5, Seongbuk-gu, Seoul 02792, Korea §

Division of Nano and Information Technology, KIST School, Korea University of Science and

Technology, Hwarang-ro 14-gil 5, Seongbuk-gu, Seoul 02792, Korea KEYWORDS:

Tin

sulfide,

Mechanochemical,

Nanocrystals,

Thin-film

solar

cells,

Nonstoichiomentry

Corresponding Author * Tel: +82-2-958-6710. E-mail: [email protected] (D.-K. Lee), Tel: +82-2-958-5381. E-mail: [email protected] (S. Y. Lee).

ACS Paragon Plus Environment

1

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 38

We demonstrate non-toxic, earth-abundant light-absorbing SnS thin films fabricated by a lowcost,

environmentally

friendly

non-vacuum

process.

SnS

nanocrystals

(NCs)

are

mechanochemically synthesized from elemental powders without the use of any other additives or solvents. To investigate the effect of the Sn-to-S stoichiometric ratio on the crystalline phase of the SnS NCs, the nonstoichiometry is systematically controlled from 0.95 (Sn0.95S) to 1.05 (Sn1.05S) by adjusting the mixing ratio of the Sn and S powders. The crystallographic evolution with the milling time signifies that the formation of the SnS phase follows a mechanochemicallydriven self-propagation reaction mechanism. The as-synthesized SnS NCs with a stoichiometric composition (i.e., Sn1.00S) are found to contain a Sn2S3 impurity phase in a non-negligible amount, which can be subsequently eliminated by a post-heat treatment at 500 ºC in a reducing atmosphere. Interestingly, however, the formation of Sn2S3 during the mechanochemical synthesis process is greatly alleviated by introducing a Sn-excess composition (e.g., Sn1.05S). In addition, the solar cell with a Sn1.05S absorber exhibits a much higher efficiency as compared to the Sn0.95S- or Sn1.00S-based devices, which is likely attributed to the improved phase purity of Sn-excess SnS as well as to its better microstructure with higher crystallinity than the other compositions.

Introduction CuInS2 (CIS) and Cu(In,Ga)S2 (CIGS) thin-film solar cells have been intensively studied over the last few decades to increase their power conversion efficiency (PCE) by tailoring the materials properties and device structures as well as developing and optimizing the fabrication processes.1−5 The PCE of CIGS thin-film solar cells has recently reached 22.6% via high-vacuum evaporation techniques employing a multi-stage process.1 Despite the higher PCE level of CIGS

ACS Paragon Plus Environment

2

Page 3 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

solar cells than that of Si cells on a laboratory scale, their commercialization has not been as successful as that of Si-based cells, which is regarded as partly due to the higher cost per unit power generation. In this regard, the need for the development of cost-effective non-vacuum processes has been recognized.5−8 In addition, inexpensive, earth-abundant, and non-toxic new photovoltaic (PV) materials have received a considerable amount of interest as potential candidates to replace indium and gallium in CIGS. In recent years, headed by Cu2ZnSnS4 (CZTS)

and

related

quaternary

semiconducting

compounds,9

CuSbS2,10,11

FeS2,12−14

Fe2GeS4,15−16 and SnS17,18 compounds have been studied as alternative PV materials to CIGS. Among these materials, SnS has recently attracted particular interest as a promising PV absorber material as it is a simple binary compound consisting only of tin and sulfur, which are non-toxic and abundant in nature. Furthermore, SnS has suitable bandgap energies (1.1 ~ 1.5 eV) and high absorption coefficients (104 ~ 105 cm−1), enabling it to absorb sufficient light with a thickness of less than 1 µm.19,20 In the earlier stage, most studies focused on the fabrication and characterization of SnS thin films using various fabrication techniques such as RF-sputtering,21 electron beam evaporation,22 chemical vapor deposition,23 thermal evaporation,24,25 atomic layer deposition (ALD),26 sulfurization,27 chemical bath deposition,28 electrochemical deposition,29 and solution-phase deposition.30 Thus far, SnS solar cells capable of relatively high performance levels have been fabricated by high-vacuum techniques.

21,23,25,26

In 2014, Gordon et al.

demonstrated the promise of using SnS materials in solar cells, reporting a device with a 4.4% efficiency.26 In order to utilize the low-cost material advantage of SnS fully, however, it is necessary to develop a facile, low-cost, non-vacuum process for the fabrication of SnS films. Herein, we synthesized SnS nanocrystals (NCs) using a mechanochemical technique31,32 and applied them as precursor materials for the thin-film fabrication using a doctor-blade coating

ACS Paragon Plus Environment

3

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 38

method. In line with using the low-cost materials and processes to realize cost-effective solar cells, we employed a CdS buffer layer deposited by a chemical bath deposition method instead of the Z(O,S) layers that have been applied for the optimized devices using a high-vacuum process, ALD. 23,25,26 It has been reported that due to the various oxidation states available to Sn, other Sn−S impurity phases such as Sn2S3 and SnS2 often form concurrently during a variety of deposition processes of SnS, rendering the formation of phase-pure SnS challenging.30 In this work, in an attempt to resolve this issue, we investigate the effect of the Sn-to-S concentration ratio on the appearance of unfavorable secondary phases in mechanochemically synthesized SnS NCs. The microstructural features as well as the phase purity were characterized for SnS NCs with different stoichiometric ratios, and their impact on the performance of SnS solar cells fabricated using the NCs was discussed. Experimental Section Synthesis of SnS nanocrystals. SnS nanocrystals (NCs) were synthesized via a mechanochemical route. The elemental Sn (Alfa Aesar, 99.9%, ~100 mesh) and S powders (Sigma Aldrich, 99.8%) were weighed as received in a glove box filled with Ar gas and loaded (10 g in total) together with ZrO2 balls (25 g of 5-mm-diameter and 25g of 10-mm-diameter balls) into a stainless steel jar (80 mL in volume). In order to investigate the effect of the stoichiometry, the mixing ratios of the constituent elements, i.e., [Sn]/[S] ≡ x (where [k] denotes the concentration of species k) were varied from 0.95 to 1.05, while the ball-to-precursor ratio was fixed at 5:1 in weight. Solvent-free mechanochemical synthesis was carried out at a speed of 500 rpm for up to 5 h in a planetary ball-mill machine (Fritsch GmbH, Pulverisette 5 classic

ACS Paragon Plus Environment

4

Page 5 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

line). No trace amount of impurities originating from the milling balls or container (such as Zr, Si, Fe, Al) was detected by X-ray photoelectron spectroscopy (Figure S1 in the Supporting Information (SI)). To elucidate the evolution of the crystalline phase, the milled powers were intermittently extracted and examined after every hour of the milling process. To examine if there were any phase changes at high temperatures, the as-synthesized NCs were post-heattreated at 300 °C or 500 °C for 1 h in an Ar (99%)/H2 (1%) gas atmosphere. Fabrication of SnS thin films and photovoltaic cells. SnS NC inks were prepared by dispersing the as-synthesized NCs into anhydrous ethanol as a solvent at a ratio of 160 mg/mL. In order to endow the NC ink with suitable rheological properties along with good colloidal stability, a wet-milling process was carried out using 1- and 5-mm-diameter ZrO2 balls at a ratio of 7 : 3 for 24 h with a horizontal ball-mill machine. The SnS nanocrystal layers were coated onto Mo-sputtered soda-lime glass (SLG) substrates (30 × 40 × 1 mm3) using a doctor-blade method with the prepared NC inks. In order to obtain dense and well-crystallized thin-film light absorbers, the as-coated films were annealed at 500 °C for 1 h in a sulfur-containing gas atmosphere (95% Ar/ 5% H2S at a flow rate of 100 sccm). Thin-film solar cell devices were fabricated in a configuration of Mo/SnS/CdS/ZnO/Al-doped ZnO/Ni/Al. A CdS buffer layer with a thickness of ca. 70 nm was deposited by chemical bath deposition on top of the as-annealed SnS absorber film. Subsequently, 50 nm thick ZnO and 500 nm thick Al-doped ZnO layers were deposited onto the CdS layer by means of RF sputtering. A Ni (50 nm)/Al (500 nm) grid pattern was deposited via thermal evaporation onto the Al-doped ZnO layer through a metal mask. The active area of the devices was around 0.4 cm2. Characterization of materials and devices. The mechanochemical phase evolution of the mixed powders and structural properties of the annealed NCs were analyzed by X-ray diffraction

ACS Paragon Plus Environment

5

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 38

(XRD; Bruker D8 Advance) with Cu Kα radiation (λ = 1.5406 Å) operated at 60 kV and 300 mA in the θ−2θ scan mode and Raman spectroscopy equipped with an excitation beam of a 5 W Arion laser source having a wavelength of 514.5 nm and a spectral resolution of 0.6 cm−1 (Horiba Jobin-Yvon LabRam Aramis spectrometer). The morphology, local crystal structure, and elemental distribution of the as-synthesized NCs were investigated using a high-resolution transmission electron microscope (HR-TEM; FEI Titan 80-300, Talos F200X) equipped with a scanning transmission electron microscopy-energy dispersive X-ray spectroscopy system (STEM-EDS). The optical absorption properties of the annealed NCs (under 99% Ar/1% H2 or 95% Ar/ 5% H2S) were examined by diffuse reflectance measurements using a VARIAN Cary 5000 UV−vis−NIR spectrometer. The as-coated and the annealed (under 95% Ar/ 5% H2S) films underwent an X-ray photoelectron spectroscopy (XPS) analysis using a PHI 5000 VersaProbe spectrometer (ULVAC-PHI) equipped with a monochromated Al Kα (1486.6 eV) X-ray source operating at 24.5 W and 15 kV with a pass energy of 23.5 eV and a spot size of 0.1 × 0.1 mm2. The carbon 1s peak (at 284.6 eV) was used as the energy reference for the calibration of the measured binding energies. The cross-sectional morphologies of the SnS solar cells were examined by scanning electron microscopy (SEM; FEI Inspect F) with an acceleration voltage of 15 kV. The current density−voltage (j−V) characteristics of the SnS solar cells were measured by a class-AAA solar simulator (Yamashita Denso, YSS-50S) under standard AM 1.5G 1-sun (100 mW cm−2) illumination. The light intensity of the solar simulator was calibrated using an NRELcalibrated Si reference solar cell. Results and Discussion Mechanochemical synthesis and post-heat treatment of Sn1.00S nanocrystals. Figure 1a shows the XRD patterns of the milled powders with a [Sn]/[S] mixing ratio (i.e., x in SnxS) of

ACS Paragon Plus Environment

6

Page 7 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

1.00 as a function of the milling time. From the spectra of the powders milled for up to 2 h, one can see that the elemental Sn (denoted by , according to JCPDS card no. 04-0673) and S (, JCPDS card no. 08-0247) powders remained unreacted. A dramatic change in the XRD pattern occurred after milling for 3 h. All of the diffraction peaks detected for the sample milled for 3 h turned out to belong to Herzenbergite SnS (α-SnS) in an orthorhombic crystal structure (Pbnm, JCPDS card no. 39-0354), and no further change in the peak position or intensity was identified in the spectra for up to 5 h (see also Figure S2). According to previous reports,33−36 this sudden and rapid crystallographic change is one of the unique characteristics of the mechanochemically induced self-propagation reaction mechanism, as schematically illustrated in Figure 1b. The mechanical energy provided in the first 2 h is suggested to be utilized to pulverize and activate the elemental precursor powders. When the mechanical stress possibly exceeds the activation barrier, the chemical reaction appears to be induced to form SnS between 2 to 3 h of milling, as follows, Sn (s) + S (s) = SnS (s); ∆H f = - 107,949 kJ mol -1 ,

(1)

where ∆H f denotes the enthalpy of formation of SnS. Upon the initiation of the reaction, the heat released in association with the formation enthalpy likely accelerates and propagates the reaction, enabling its completion within 1 h. The lower bound of the average crystallite size of the SnS NCs at 5 h was estimated to be ca. 15 nm using the full width at half maximum of the (111) reflection at 31.6° according to Scherrer’s equation. In this way, the α-SnS NCs (in a relatively large amount, 10 g) were successfully synthesized in a facile and environmentally friendly manner without using any expensive and/or toxic solvents or additives. It should also be noted that the present method is easy to scale up.

ACS Paragon Plus Environment

7

ACS Sustainable Chemistry & Engineering

(a)

Intensity / a.u.

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

♣ 5h ♣ ♣ ♣ ♣ 4h ♣ ♣ ♣♣ ♣ 3h ♣ ♣♣ ♣



Sn1.00S ♣ ♣♣



♣ ♣♣



♣ ♣♣



2h

1h

♣ SnS







♦ ♦♦♦♦



Page 8 of 38

Sn2S3 • Sn ♦S



• • •

♦ ♦♦♦ ♦



20 25 30 35 40 45 50 55 60

2θ /

o

Figure 1. Crystallographic phase evolution of the Sn and S powder mixture with a Sn-to-S mixing ratio of 1.00 during the solvent-free mechanochemical synthesis of SnS nanocrystals at 500 rpm: (a) XRD patterns of powders milled for various periods of time and (b) schematic illustration depicting the progress of the mechanochemical reaction.

Figure 2 shows the detailed morphological and crystallographic characteristics of the mechanochemically synthesized SnS NCs (for 5 h) as investigated by TEM. The as-synthesized Sn1.00S powders were found to consist of agglomerates of non-uniform sizes ranging from 50 to 200 nm in diameter, as exemplified in Figure 2a. The primary particle size was estimated to be a few tens of nanometers, which is more easily observable in Figure S3 and is consistent with the aforementioned XRD analysis. Each primary nanoparticle was crystalline in nature, as shown in

ACS Paragon Plus Environment

8

Page 9 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

the HR-TEM image (Figure 2b), although some of the nanoparticle edges were found to be amorphous (see Figure S3c). In Figure 2b, the crystalline lattice fringes were clearly observed with interplanar distances of 0.200 ± 0.005 and 0.231 ± 0.004 nm, which can be indexed to the (002) and (131) planes of orthorhombic α-SnS according to JCPDS card no. 39-0354, respectively. As shown in Figure 2c, the selected area electron diffraction (SAED) pattern for the region marked in Figure 2a consistently indicates the {002} and {131} planes of α-SnS with the zone axis along the [3 1 0] direction. Both constituent elements (Sn and S) were homogenously distributed throughout the agglomerates of single-crystalline NCs, as demonstrated by the STEM image and the corresponding EDS mapping analysis (Figure 2d).

Figure 2. TEM analysis of the as-synthesized Sn1.00S nanocrystals: (a) TEM image, (b and c) HR-TEM image and SAED pattern for the marked area in part (a), and (d) STEM-EDS elemental mapping of the constituent elements (Sn and S).

ACS Paragon Plus Environment

9

ACS Sustainable Chemistry & Engineering

It should be noted here that the possible existence of secondary phases in the synthesized SnS NCs cannot be ruled out with the XRD analysis alone, as trace amounts of Sn2S3 and SnS2 phases may not be detected by XRD.37−40 Thus, Raman spectroscopy was employed to provide more decisive information on the phase purity of the Sn1.00S NCs prepared by milling for 5 h. This result is shown in Figure 3. While most of the detectable Raman signals can be assigned to the orthorhombic α-SnS phase, i.e., at 93, 180, and 218 cm−1 (Ag mode) and 160 cm−1 (B3g mode),41 a characteristic Raman peak for Sn2S3 was also observed at 305 cm−1, indicating that the as-synthesized SnS NCs coexist with the Sn2S3 impurity phase. The Sn2S3 phase has been reported to have its strongest Raman band at 305−308 cm−1 (Ag mode).37,42−44 On the other hand, as shown in Figure 3, no trace amounts of SnS2, of which the most intense Raman scattering is known to be at 312−316 cm−1 (A1g mode), were detected.37,44−46

As-synthesized NCs (5 h) Intensity / a.u.

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 38

B3g 160

Ag 180

Sn1.00S Ag 218 cm

−1

Sn2S3 (Ag) 305 cm

Ag −1 93 cm

−1

100 150 200 250 300 350 400 450 500 -1

Raman shift / cm

Figure 3. Raman spectra of the Sn1.00S nanocrystals synthesized by ball-milling for 5 h.

The secondary phase Sn2S3 may have an adverse effect on the performance of solar cells based on a p-type SnS absorber,40,47−49 as Sn2S3 is known as an n-type semiconductor.50,51 Therefore, the presence of the n-type Sn2S3 phase in SnS absorbers should be suppressed to achieve high-

ACS Paragon Plus Environment

10

Page 11 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

efficiency SnS solar cells. Steinmann et al. reported that Sn2S3 in a SnS powder sample can be removed by post-annealing under a vacuum (15 mTorr) at 500 °C for 1 h. Similarly, in an attempt to remove the Sn2S3 phase, the as-synthesized Sn1.00S NCs were post-heat-treated at 300 or 500 °C, but in an Ar (99%)/H2 (1%) gas atmosphere at ambient pressure. The XRD and Raman spectroscopy results are shown in Figure 4. Compared to the as-synthesized Sn1.00S NCs (Figure 1a), the intensity of the diffraction peaks was significantly augmented as the temperature of the post-heat treatment increases, enabling the clear identification of most of the characteristic diffraction peaks for α-SnS, as indexed in Figure 4a. On the other hand, it was also found that the secondary phase Sn2S3 still remained in the sample annealed at 300 °C, as indicated by the arrows in Figure 4c. The Sn2S3 impurity phase was finally eliminated at 500 °C, as shown in Figure 4b. This change can be more evidently observed in the Raman spectra (Figure 4d) from the disappearance of the 309 cm−1 peak corresponding to Sn2S3 at 500 °C. It may be worth noting here that the most intense vibration mode for SnS was blue-shifted as the annealing temperature increased, approaching its standard value of 192 cm−1.41 The shift of the Raman peaks could be induced by differences in the crystal growth conditions, chemical compositions, and surface roughness levels.52,53

ACS Paragon Plus Environment

11

ACS Sustainable Chemistry & Engineering

(b),(c)

20 25 30 35 40 45 50 55 60

2θ /

o

(d)

500 ° C

Post heat-treated Sn1.00S NCs 192 cm

300

−1

500 °C

200

300 °C

100

165

0

30

35

(c) 120

2θ /

o

40

45

300 °C 90 60

Sn2S3

Sn2S3

(212)

(015)

Intensity / a.u.

Intensity / a.u.

(231)/(061) (042) (250)

(200)

(131) (041) (210) (141) (002) (211) (112)/(151) (122)/(160)

(120) (021) (101) (040) (110)

500 °C 300 °C

(b) 400

Intensity / a.u.

Post heat-treated Sn1.00S NCs (111)

(a)

Intensity / a.u.

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 38

219 cm

95 cm

−1

−1

188 cm

161

−1

221 cm

−1

Sn2S3 309 cm

30

96 cm

−1

−1

0

30

35

2θ /

o

40

45

100 150 200 250 300 350 400

Raman shift / cm

-1

Figure 4. XRD and Raman investigation on the post-heat-treated Sn1.00S NCs at 300 and 500 °C under 99% Ar/1% H2: (a) XRD patterns, magnified XRD patterns of the samples annealed at (b) 300 °C and (c) 500 °C, and (d) corresponding Raman spectra.

Effect of the Sn-to-S ratio on the formation of the Sn2S3 secondary phase. We further investigated the effect of nonstoichiometry, i.e., the Sn-to-S concentration ratio ([Sn]/[S] ≡ x), on the formation of the Sn2S3 secondary phase. Both Sn-deficit (x = 0.95) and Sn-excess (x = 1.05) samples were additionally prepared in a manner identical to how the stoichiometric Sn1.00S NCs were prepared (see Figure S4). Figure 5a,b shows the XRD patterns and Raman spectra of the as-synthesized Sn0.95S, Sn1.00S, and Sn1.05S NCs. It is readily recognized that, irrespective of the mixing ratios, α-SnS was formed as a majority phase after milling for 5 h. The XRD patterns rendered lattice parameters of the synthesized NCs (a = 4.587(12), b = 10.02(2), and c = 4.044(15) Å for Sn0.95S; a = 4.315(8), b = 11.196(7), and c = 4.007(9) Å for Sn1.00S; a = 4.299(6), b = 11.241(5), and c = 3.999(6) Å for Sn1.05S). The evaluated values for Sn1.00S and Sn1.05S were in good agreement with the reported (a = 4.25−4.33, b = 11.18−11.23, and c =

ACS Paragon Plus Environment

12

Page 13 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

3.98−4.02),44,54−56 whereas the a and b values for Sn0.95S were found to deviate significantly. Indeed, the XRD pattern of the only Sn0.95S NCs (Figure 5a) unambiguously shows the presence of the Sn2S3 impurity phase at 21.3, 23.6, 28.7, and 40.0°, which can correspondingly be assigned to the (103), (202), (112), and (015) planes of orthorhombic Sn2S3 (Pnma, JCPDS card no. 30-1379), indicating that the amount of the impurity phase in Sn0.95S is significantly larger than that in the Sn1.00S samples. Likewise, the Raman spectrum of the Sn0.95S NCs (Figure 5b) also indicates that the characteristic Raman peak for Sn2S3 (at 306 cm−1) was more pronounced, as compared to the Sn1.00S sample. In contrast, no peaks indicative of Sn2S3 were detected in either XRD or Raman spectra of the Sn1.05S sample. It is emphasized here that SnS NCs having no detectable secondary phases (Sn2S3 or SnS2) were successfully synthesized simply by controlling the Sn-to-S concentration ratio without a high-temperature annealing step. The assynthesized SnxS NCs with different x values were further heat-treated at 500 °C for 1 h in an Ar (99%)/H2 (1%) gas atmosphere. As shown in the XRD patterns (Figure 5c) and by the Raman spectra (Figure 5d), a significant amount of the Sn2S3 phase remained in the Sn0.95S sample even after the heat treatment. With regard to Sn1.05S, no secondary phases emerged due to this annealing process. We note here that a heat treatment in a sulfur-containing (95% Ar/5% H2S) atmosphere had a similar effect on the phase purity of SnxS NCs, as shown in Figure S5,S6. However, since the sulfur-containing atmosphere is known to have beneficial effects on the microstructural development during sintering as well as on the electrical properties of SnS films,23,26,57 a 95% Ar/5% H2S atmosphere was employed in the sintering process for the solar cell absorbers. The measured Sn-to-S concentration ratios ([Sn]/[S] ≡ x) using TEM-EDS on the SnxS NCs after the heat-treatment under a 95% Ar/5% H2S gas atmosphere were summarized in Figure S7 and Table S1 along with those of the as-synthesized NCs. All of the measured

ACS Paragon Plus Environment

13

ACS Sustainable Chemistry & Engineering

compositions were in good agreement with the initial compositions within the experimental error bound. (b)

♣♣ ♣



(116) /(314)



(015)

(212)







220

160

Sn1.05S

♣ ♣ ♣♣ Sn1.00S

∇∇

As-syn. NCs

94 187

Intensity / a.u.



As-syn. NCs

(112)

Intensity / a.u.

♣ SnS ♣ ∇ Sn2S3

(103) (202)

(a)

Sn2S3 Sn1.05S

93 180 160 218

305 cm

183

220

158

306 cm

♣ SnS ∇ Sn2S3

Post-heattreated NCs

100 150 200 250 300 350 400 −1

Raman shift / cm

(d)

Post-heat-treated NCs 191





Sn1.05S

♣ ♣ ♣ ♣ ♣♣♣

(212)

(015)

(116) /(314)

Sn1.00S

∇∇







∇ Sn0.95S

20 25 30 35 40 45 50 55

2θ / °

Intensity / a.u.

95

♣♣ ♣

(112)

Intensity / a.u.

♣♣

-1

Sn0.95S

20 25 30 35 40 45 50 55 2θ / °

(c)

-1

Sn1.00S

93

Sn0.95S

(103) (202)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 38

Sn2S3

163 219

Sn1.05S

192 95

95

165

219

Sn1.00S

186 158

220 236

308 cm

−1

Sn0.95S 100 150 200 250 300 350 400

Raman shift / cm

−1

Figure 5. (a,c) XRD patterns and (b,d) Raman spectra of SnxS nanocrystals with x values of 0.95, 1.00, and 1.05 for (a,b) as-synthesized NCs by ball-milling for 5 h and (c,d) post-heattreated NCs at 500 °C for 1 h under a 99% Ar/1% H2 gas atmosphere.

SnS has been known to accommodate Sn-deficiency to a certain degree,58 which is regarded as responsible for its intrinsic p-type conductivity via the formation of Sn vacancies.47 On the other hand, studies on the Sn-excess stoichiometry are relatively scarce in the literature. Several research groups have reported that phase-pure SnS could be obtained with off-stoichiometric [Sn]/[S] ratios of 1.02−1.15.40,44,49,53,59 However, the Sn-excess compositions in most previous works were not deliberately controlled but were instead a consequence of volatile sulfur loss

ACS Paragon Plus Environment

14

Page 15 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

during high-temperature annealing and/or vacuum deposition processes. Huang et al. claimed that Sn-excess SnS films ([Sn]/[S] = 1.11) also exhibited a p-type behavior with a higher hole concentration than a Sn-deficit sample ([Sn]/[S] = 0.96).60 In the present work, in addition to the improved phase purity of Sn-excess SnS, slightly higher diffraction peak intensities of the Sn1.05S samples were recognized (Figure 5a and c), implying their better crystallinity than the other compositions. Optical and photovoltaic properties of SnxS annealed in a 5% H2S atmosphere. As solar cell absorbers, the doctor-blade-coated SnxS films (with x = 0.95, 1.00, and 1.05) were employed after annealing at 500 °C for 1 h in a 95% Ar/5% H2S atmosphere instead of the heat treatment in a Ar/H2 (1%) atmosphere to achieve a better microstructure. First, to evaluate the optical bandgap (Eg) values, the diffuse reflectance spectra of the SnxS NCs annealed in an identical manner were measured, with which Kubelka−Munk transformations were conducted according to the relationship of F(R) = (1 − R)2/2R. Here, F(R) and R denote the Kubelka−Munk function and the diffuse reflectance, respectively. The calculated F(R) function was analyzed using the equation, [F(R)hν]n ∝ hν − Eg, near the band edge regime, where hν is the photon energy and the n values are 2 or 1/2 corresponding to the direct and indirect allowed transition models.59 In order to examine the type of band transition of the present samples, both models were employed to extract Eg values by extrapolating the linear regime of the plots to the abscissa, where [F(R)hν]n = 0. The results are as shown in Figure 6. The evaluated direct and indirect bandgaps ( E gdir and Egind ) of the SnxS NCs were 1.19 eV and 1.08~1.09 eV, respectively, for all of the samples. The composition dependence of the optical bandgap was found to be negligible. The nature of the band-to-band transition of SnS has been controversial in the literature, which we summarize in a comprehensive manner in Table S2. Despite such controversy, there have been

ACS Paragon Plus Environment

15

ACS Sustainable Chemistry & Engineering

several attempts to extract both types of bandgaps from a single optical measurement.30,44,57,60,61 The evaluated bandgaps in the present work are in fairly good agreement with the reported values (1.26 < E gdir /eV < 1.34 and 1.00 < Egind /eV < 1.17). Nonetheless, it is worth noting that, as can be recognized in Figure 6a,b, the direct transition model yielded a better R-squared value (> 0.999 in comparison with ~0.99 for the indirect transition model), possibly suggesting the direct transition characteristic of the SnxS NCs prepared in this work. Furthermore, we note that a slightly smaller E gdir value for the present samples is presumably attributed to the hightemperature annealing process according to Malaquias et al.44 They found that the E gdir values of SnS films sulfurized at 520 °C were reduced to 1.26 eV from 1.45 eV for such films sulfurized at 300 °C. In passing, it is noted that the E gdir and Egind values of SnxS NCs annealed in a 99% Ar/1% H2 atmosphere were also measured and found to be 1.24 and 1.08 eV, respectively, regardless of the composition (Figure S8). The reason for the slight difference in E gdir between the two groups of samples is yet to be elucidated. (b)

1.0

/ a.u.

Sn1.00S Sn1.05S

1.1

1.2

Annealed NCs (in 5% H2S)

1/2

2

Annealed NCs (in 5% H2S) Sn0.95S

(F(R)hν)

(a) (F(R)hν) / a.u.

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 38

1.3

1.4 1.0

hν / eV

Sn0.95S Sn1.00S Sn1.05S 1.1

1.2

1.3

1.4

hν / eV

Figure 6. Tauc’s plots of the annealed SnxS NCs under 95% Ar/5% H2S with x = 0.95, 1.00, and 1.05: (a) [F(R)hν]2 vs. hν and (b) [F(R)hν]1/2 vs. hν plots to extract Eg for direct and indirect transitions, respectively.

ACS Paragon Plus Environment

16

Page 17 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

To demonstrate their potential as absorber materials, the SnxS films fabricated from the mechanochemically synthesized NCs were integrated into solar cells, as depicted schematically in Figure 7a. Figure 7b−d shows cross-sectional SEM images of the completed devices with Sn0.95S, Sn1.00S, and Sn1.05S, respectively. One can immediately recognize that as the [Sn]/[S] ratio increases, the microstructure of the SnxS absorber films gradually improves (in terms of the grain size and porosity). This trend of variation in the microstructure appears to be coincident with the variation in the amount of elemental Sn existing in the as-coated films (see Figure S9). One may surmise that elemental Sn with a low melting point (231.9 °C) may act as a sintering agent during the annealing step. However, further studies are required to clarify the correlation between the elemental Sn content and the morphological development of SnS films. Figure 7e shows the j−V characteristics of SnS solar cells under AM 1.5G 1 sun illumination and in the dark. The corresponding photovoltaic parameters are summarized in Table 1. The performance of the solar cells with Sn0.95S and Sn1.00S absorber layers was quite low, while the device with a Sn1.05S absorber exhibited a power conversion efficiency (η) of 1.71% with a short-circuit current density (jSC) of 18.14 mA cm−2, an open-circuit voltage (VOC) of 0.215 V, and a fill factor (FF) of 0.438 (see Figure S10 for the PV performance of six devices with Sn1.05S absorbers prepared in a single batch). The significantly enhanced performance of the Sn1.05S-based solar cell compared with Sn0.95S- and Sn1.00S-based devices could be attributed to the improved microstructure, crystallinity, and possibly to the suppressed formation of Sn2S3 impurity phase (Figure S5,S6), achieved by introducing a Sn-excess composition of the starting materials.

ACS Paragon Plus Environment

17

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 38

Figure 7. Characterization of SnS thin-film solar cells fabricated using mechanochemically synthesized SnxS nanocrystals: (a) Schematic of a SnS solar cell; cross-sectional SEM images of completed devices with (b) Sn0.95S, (c) Sn1.00S, (d) Sn1.05S absorbers; and (e) j–V curves measured under AM 1.5G 1 sun illumination (closed circle) and in the dark (dashed lines).

Table

1.

Photovoltaic

parameters

of

SnS

thin-film

solar

cells

fabricated

using

mechanochemically synthesized SnxS nanocrystals Absorber

VOC / V

jSC / mA cm−2

FF

η/%

Sn0.95S

0.085

2.82

0.358

0.09

Sn1.00S

0.047

5.75

0.317

0.09

ACS Paragon Plus Environment

18

Page 19 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Sn1.05S

0.215

18.14

0.438

1.71

In this study, we have demonstrated a simple, environmentally friendly, up-scalable route for synthesizing phase-pure SnS nanocrystals (NCs) and SnS-based thin-film solar cells via a solvent-free mechanochemical method. The α-SnS phase was abruptly formed after 2 to 3 h of milling, which is indicative of a mechanochemically induced self-propagating reaction mechanism. The as-synthesized SnS NCs prepared with compositions of Sn1.00S, Sn0.95S were found to coexist with a secondary phase of Sn2S3 in a non-negligible amount, which may deteriorate the solar cell performance. Meanwhile, the Sn-excess composition led to the formation of phase-pure SnS NCs without an additional thermal process. In addition, with an increase in the Sn content, the crystallinity and morphology of the annealed films were found to have been improved. As a consequence, the solar cells with a Sn1.05S absorber layer exhibited a much higher PCE (1.7%) than the other compositions. From this work, it is suggested that preventing the formation of unfavorable secondary phases as well as achieving a wellcrystallized microstructure are major challenges to achieve highly efficient SnS thin-film solar cells.

ASSOCIATED CONTENT Supporting Information. The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acssuschemeng. XPS spectra of as-coated and as-annealed SnxS, comparison of XRD patterns of Sn1.00S powders milled for 3 to 5 h, TEM images of Sn1.00S powders milled for 5 h, phase evolution of Sn0.95S

ACS Paragon Plus Environment

19

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 38

powders, XRD, Raman spectra, and STEM-EDS mapping results with chemical composition of SnxS NCs annealed under a 95% Ar/5% H2S gas atmosphere, comparison of the reported values for optical bandgap of SnS, Tauc’s plots for post heat-treated SnxS NCs under an Ar/H2 gas mixture, XPS spectra of SnxS thin films, comparison of binding energies of Sn 3d5/2 and their assignments (PDF)

AUTHOR INFORMATION Corresponding Author * Tel: +82-2-958-6710. E-mail: [email protected] (D.-K. Lee), Tel: +82-2-958-5381. E-mail: [email protected] (S. Y. Lee). Author Contributions The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript. ⊥These authors contributed equally. Notes The authors declare no competing financial interest.

ACKNOWLEDGMENT This

work

was

financially

supported

by

the

KIST-UNIST

partnership

program

(1.160097.01/2.160482.01), by the Korea Institute of Energy Technology Evaluation and Planning (KETEP) and the Ministry of Trade, Industry & Energy (MOTIE) (20163010012580, 20163010012450), and by the KIST institutional program.

ACS Paragon Plus Environment

20

Page 21 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

REFERENCES (1)

Jackson, P; Wuerz, R; Hariskos, D.; Witte, W.; Powalla, M. Effects of Heavy Alkali

Elements in Cu(In,Ga)Se2 Solar Cells with Efficiencies up to 22.6%. Phys. Status Solidi RPL 2016, 10 (8), 583−586. (2)

Chopra, K. L.; Paulson, P. D.; Dutta, V. Thin-Film Solar Cells: An Overview. Prog.

Photovoltaics 2004, 12 (2−3), 69−92. (3)

Repins, I.; Contreras, M. A.; Egaas, B.; DeHart, C.; Scharf, J.; Perkins, C. L.; To, B.;

Noufi, R. 19·9%-Efficient ZnO/CdS/CuInGaSe2 Solar Cell with 81.2% Fill Factor. Prog. Photovoltaics 2008, 16 (3), 235−239. (4)

Green, M. A.; Emery, K.; Hishikawa, Y.; Warta, W.; Dunlop, E. D. Solar Cell Efficiency

Tables (version 47). Prog. Photovoltaics 2016, 24 (1), 3−11. (5)

Habas, S. E.; Platt, H. A. S.; van Hest, M. F. A. M.; Ginley, D. S. Low-Cost Inorganic

Solar Cells: From Ink to Printed Device. Chem. Rev. 2010, 110 (11), 6571−6594. (6)

Kaelin, M.; Rudmann, D.; Tiwari, A. N. Low Cost Processing of CIGS Thin Film Solar

Cells. Sol. Energy 2004, 77 (6), 749−756. (7)

Lee, B.-S.; Hwang, Y.; Pham, H. N.; Kim, J. Y.; Song, M. H.; Lee, D.-K. High-Density

Cu–In Intermetallic Nanocrystal Layers: Towards High-Efficiency Printable CuInSe2 Solar Cells. J. Mater. Chem. A 2015, 3 (31), 15889−15896.

ACS Paragon Plus Environment

21

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(8)

Page 22 of 38

Lee, B.-S.; Park, S.-Y.L.; Lee, J. M.; Jeong, J.-H.; Kim, J. Y.; Chung, C.-H.; Lee, D.-K.

Suppressed Formation of Conductive Phases in One-Pot Electrodeposited CuInSe2 by Tuning Se Concentration in Aqueous Electrolyte. ACS Appl. Mater. Interfaces 2016, 8 (37), 24585−24593. (9)

Katagiri, H.; Sasaguchi, N.; Hando, S.; Hoshino, S.; Ohashi, J.; Yokota, T. Preparation

and Evaluation of Cu2ZnSnS4 Thin Films by Sulfurization of E-B Evaporated Precursors. Sol. Energy Mater. Sol. Cells 1997, 49 (1−4), 407−414. (10) Yu, L.; Kokenyesi, R. S.; Keszler, D. A.; Zunger, A. Inverse Design of High Absorption Thin-Film Photovoltaic Materials. Adv. Energy Mater. 2013, 3 (1), 43−48. (11) Septina, W.; Ikeda, S.; Iga, Y.; Harada, T.; Matsumura. M. Thin Film Solar Cell Based on CuSbS2 Absorber Fabricated from an Electrochemically Deposited Metal Stack. Thin Solid Films 2014, 550, 700−704. (12) Puthussery, J.; Seefeld, S.; Berry, N.; Gibbs, M.; Law. M. Colloidal Iron Pyrite (FeS2) Nanocrystal Inks for Thin-Film Photovoltaics. J. Am. Chem. Soc. 2011, 133 (4), 716−719. (13) Bi, Y.; Yuan, Y.; Exstrom, C. L.; Darveau, S. A.; Huang, J. Air Stable, Photosensitive, Phase Pure Iron Pyrite Nanocrystal Thin Films for Photovoltaic Application. Nano Lett. 2011, 11 (11), 4953−4957. (14) Wang, D.-Y.; Jiang, Y.-T.; Lin, C.-C.; Li, S.-S.; Wang, Y.-T.; Chen, C.-C.; Chen, C.-W. Solution-Processable Pyrite FeS2 Nanocrystals for the Fabrication of Heterojunction Photodiodes with Visible to NIR Photodetection. Adv. Mater. 2012, 24 (25), 3415−3420.

ACS Paragon Plus Environment

22

Page 23 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(15) Yu, L.; Lany, S.; Kykyneshi, R.; Jieratum, V.; Ravichandran, R.; Pelatt, B.; Altschul, E.; Platt, H. A. S.; Wager, J. F.; Keszler, D. A.; Zunger, A. Iron Chalcogenide Photovoltaic Absorbers. Adv. Energy Mater. 2011, 1 (5), 748−753. (16) Fredrick, S. J.; Prieto, A.L. Solution Synthesis and Reactivity of Colloidal Fe2GeS4: A Potential Candidate for Earth Abundant, Nanostructured Photovoltaics. J. Am. Chem. Soc. 2013, 135 (49), 18256−18259. (17) Reddy, K. T. R.; Reddy, N. K.; Miles, R. W. Photovoltaic Properties of SnS Based Solar Cells. Sol. Energy Mater. Sol. Cells 2006, 90 (18−19), 3041−3046. (18) Sinsermsuksakul, P.; Hartman, K.; Kim, S. B.; Heo, J.; Sun, L.; Park, H. H.; Chakraborty, R.; Buonassisi, T.; Gordon, R. G. Enhancing the Efficiency of SnS Solar Cells via Band-Offset Engineering with a Zinc Oxysulfide Buffer Layer. Appl. Phys. Lett. 2013, 102 (5), 0539011−053901-5. (19) Noguchi, H.; Setiyadi, A.; Tanamura, H.; Nagatomo, T.; Omoto, O. Characterization of Vacuum-Evaporated Tin Sulfide Film for Solar Cell Materials. Sol. Energy Mater. Sol. Cells 1994, 35, 325−331. (20) Reddy, N. K.; Hahn, Y. B.; Devika, M.; Sumana, H. R.; Gunasekhar, K. R. TemperatureDependent Structural and Optical Properties of SnS Films. J. Appl. Phys. 2007, 101 (9), 0935221−093522-7. (21) Ikuno, T.; Suzuki, R.; Kitazumi, K.; Takahashi, N.; Kato, N.; Higuchi, K. SnS Thin Film Solar Cells with Zn1−xMgxO Buffer Layers. Appl. Phys. Lett. 2013, 102 (19), 193901-1−1939014.

ACS Paragon Plus Environment

23

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 38

(22) Tanuševski, A.; Poelman, D. Optical and Photoconductive Properties of SnS Thin Films Prepared by Electron Beam Evaporation. Sol. Energy Mater. Sol. Cells 2003, 80 (3), 297−303. (23) Park, H. H.; Heasley, R.; Sun, L.; Steinmann, V.; Jaramillo, R.; Hartman, K.; Chakraborty, R.; Sinsermsuksakul, P.; Chua, D.; Buonassisi, T.; Gordon, R. G. Co-Optimization of SnS Absorber and Zn(O,S) Buffer Materials for Improved Solar Cells. Prog. Photovoltaics 2015, 23 (7), 901−908. (24) Ogah, O. E.; Zoppi, G.; Forbes, I.; Miles, R. W. Thin Films of Tin Sulphide for Use in Thin Film Solar Cell Devices. Thin Solid Films 2009, 517 (7), 2485−2488. (25) Steinmann, V.; Jaramillo, R.; Hartman, K.; Chakraborty, R.; Brandt, R. E.; Poindexter, J. R.; Lee, Y. S.; Sun, L.; Polizzotti, A.; Park, H. H.; Gordon, R. G.; Buonassisi, T. 3.88% Efficient Tin Sulfide Solar Cells Using Congruent Thermal Evaporation. Adv. Mater. 2014, 26 (44), 7488−7492. (26) Sinsermsuksakul, P.; Sun, L.; Lee, S. W.; Park, H. H.; Kim, S. B.; Yang, C.; Gordon, R. G. Overcoming Efficiency Limitations of SnS-Based Solar Cells. Adv. Energy Mater. 2014, 4 (15), 1400496-1−1400496-7. (27) Mutsumi, S.; Keisuke, M.; Takehiro, M.; Kenichi, O.; Koji, N.; Hisayuki, N. Preparation of SnS Films by Sulfurization of Sn Sheet. Jpn. J. Appl. Phys. 2008, 47 (6), 4494−4495. (28) Pramanik, P.; Basu, P. K.; Biswas, S. Preparation and Characterization of Chemically Deposited Tin(II) Sulphide Thin Films. Thin Solid Films 1987, 150 (2−3), 269−276. (29) Takeuchi, K.; Ichimura, M.; Arai, E.; Yamazaki, Y. SnS Thin Films Fabricated by Pulsed and Normal Electrochemical Deposition. Sol. Energy Mater. Sol. Cells 2003, 75 (3−4), 427−432.

ACS Paragon Plus Environment

24

Page 25 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(30) Antunez, P. D.; Torelli, D. A.; Yang, F.; Rabuffetti, F. A.; Lewis, N. S.; Brutchey, R. L. Low Temperature Solution-Phase Deposition of SnS Thin Films. Chem. Mater. 2014, 26 (19), 5444−5446. (31) Rusanov, V.; Chakurov, C. On the Development Mechanism and Kinetics of the Explosive Mechanochemical Synthesis. J. Solid State Chem. 1989, 79, 181−188. (32) Li, Y.; Tu, J. P.; Wu, H. M.; Yuan, Y. F.; Shi. D. Q. Mechanochemical Synthesis and Electrochemical Properties of Nanosized SnS as An Anode Material for Lithium Ion Batteries. Mater. Sci. Eng. B 2006, 128, 75–79. (33) Wada, T.; Kinoshita, H. Rapid Exothermic Synthesis of Chalcopyrite-Type CuInSe2. J. Phys. Chem. Solids 2005, 66 (11), 1987−1989. (34) Ma, X.; Yuan, W.; Bell, S. E.; James, S. L. Better Understanding of Mechanochemical Reactions: Raman Monitoring Reveals Surprisingly Simple ‘Pseudo-Fluid’ Model for a Ball Milling Reaction. Chem. Commun. 2014, 50 (13), 1585−1587. (35) Park, B.-I.; Yu, S.; Hwang, Y.; Cho, S.-H.; Lee, J.-S.; Park, C.; Lee, D.-K.; Lee, S. Y. Highly Crystalline Fe2GeS4 Nanocrystals: Green Synthesis and Their Structural and Optical Characterization. J. Mater. Chem. A 2015, 3 (5), 2265−2270. (36) Park, B.-I.; Hwang, Y.; Lee, S. Y.; Lee, J.-S.; Park, J.-K.; Jeong, J.; Kim, J.Y.; Kim, B.; Cho, S.-H.; Lee, D.-K. Solvent-Free Synthesis of Cu2ZnSnS4 Nanocrystals: A Facile, Green, UpScalable Route for Low Cost Photovoltaic Cells. Nanoscale 2014, 6 (20), 11703−11711.

ACS Paragon Plus Environment

25

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 26 of 38

(37) Price, L. S.; Parkin, I. P.; Hardy, A. M. E.; Clark, R. J. H.; Hibbert, T. G.; Molloy, K. C. Atmospheric Pressure Chemical Vapor Deposition of Tin Sulfides (SnS, Sn2S3, and SnS2) On Glass. Chem. Mater. 1999, 11 (7), 1792−1799. (38) Mathews, N. R.; Anaya, H. B. M.; Cortes-Jacome, M. A.; Angeles-Chavez, C.; ToledoAntonio, J. A. Tin Sulfide Thin Films by Pulse Electrodeposition: Structural, Morphological and Optical Properties. J. Electrochem. Soc. 2010, 157 (3), H337−H341. (39) Sinsermsuksakul, P.; Heo, J.; Noh, W.; Hock, A. S.; Gordon, R. G. Atomic Layer Deposition of Tin Monosulfide Thin Films. Adv. Energy Mater. 2011, 1 (6), 1116−1125. (40) Steichen, M.; Djemour, R.; Gütay, L.; Guillot, J.; Siebentritt, S.; Dale, P.J. Direct Synthesis of Single-Phase p-Type SnS by Electrodeposition from a Dicyanamide Ionic Liquid at High Temperature for Thin Film Solar Cells. J. Phys. Chem. C 2013, 117 (9), 4383−4393. (41) Chandrasekhar, H. R; Humphreys, R. G.; Zwick, U.; Cardona, M. Infrared and Raman Spectra of the IV-VI Compounds SnS and SnSe. Phys. Rev. B 1977, 15 (4), 2177−2183. (42) Chandrasekhar, H. R.; Mead, D. G. Long-Wavelength Phonons in Mixed-Valence Semiconductor SnIISnIVS3. Phys. Rev. B 1979, 19 (2), 932−937. (43) Barone, G.; Hibbert, T. G.; Mahon, M. F.; Molloy, K. C.; Price, L. S.; Parkin, I. P.; Hardy, A. M. E.; Field, M. N. Deposition of Tin Sulfide Thin Films from Tin(IV) Thiolate Precursors. J. Mater. Chem. 2001, 11 (2), 464−468. (44) Hibbert, T. G.; Mahon, M .F.; Molloy, K. C.; Price, L. S.; Parkin, I. P. Deposition of Tin Sulfide Thin Films from Novel, Volatile (Fluoroalkythiolato)Tin(IV) Precursors. J. Mater. Chem. 2001, 11 (2), 469−473.

ACS Paragon Plus Environment

26

Page 27 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(45) Lucovsky, G.; Mikkelsen, J. C.; Liang, W. Y.; White, R. M.; Martin, R. M. Optical Phonon Anisotropies in the Layer Crystals SnS2 and SnSe2. Phys. Rev. B 1976, 14 (4), 1663−1669. (46) Malaquias, J.; Fernandes, P. A.; Salomé, P. M. P.; da Cunha, A. F. Assessment of the Potential of Tin Sulphide Thin Films Prepared by Sulphurization of Metallic Precursors as Cell Absorbers. Thin Solid Films 2011, 519 (21), 7416−7420. (47) Albers, W.; Haas, C.; Vink, H. J.; Wasscher, J. Investigations on SnS. J. Appl. Phys. 1961, 32 (10), 2220−2225. (48) Nassary, M. M. Temperature Dependence of the Electrical Conductivity, Hall Effect and Thermoelectric Power of SnS Single Crystals. J. Alloys Compd. 2005, 398 (1−2), 21−25. (49) Burton, L. A.; Colombara, D.; Abellon, R. D.; Grozema, F. C.; Peter, L. M.; Savenije, T. J.; Dennler, G.; Walsh, A. Synthesis, Characterization, and Electronic Structure of Single-Crystal SnS, Sn2S3, and SnS2. Chem. Mater. 2013, 25 (24), 4908−4916. (50) Sanchez-Juarez, A.; Ortiz, A. Effects of Precursor Concentration on the Optical and Electrical Properties of SnXSY Thin Films Prepared by Plasma-Enhanced Chemical Vapour Deposition. Semicond. Sci. Technol. 2002, 17 (9), 931−937. (51) Khadraoui, M.; Benramdane, N.; Mathieu, C.; Bouzidi, A.; Miloua, R.; Kebbab, Z.; Sahraoui, K.; Desfeux, R. Optical and Electrical Properties Sn2S3 Thin Films Grown by Spray Pyrolysis. Solid State Commun. 2010, 150 (5−6), 297−300.

ACS Paragon Plus Environment

27

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 28 of 38

(52) Devika, M.; Reddy, N. K.; Prashantha, M.; Ramesh, K.; Reddy, S. V.; Hahn, Y. B.; Gunasekhar, K. R. The Physical Properties of SnS Films Grown on Lattice-Matched and Amorphous Substrates. Phys. Status Solidi A 2010, 207 (8), 1864−1869. (53) Reddy,

N.

K.

Growth-Temperature

Dependent

Physical

Properties

of

SnS

Nanocrystalline Thin Films. ECS J. Solid State Sci. Technol. 2013, 2 (6), 259−263. (54) Boudjouk, P.; Seidler, D. J.; Bahr, S. R.; McCarthey, G. J. Bis(Triphenyltin) Chalcogenides as Convenient Precursors to Phase-Pure Binary Semiconductors. Chem. Mater. 1994, 6 (11), 2108−2112. (55) Formstone, C. A.; Fitzgerald, E. T.; Cox, P. A.; O'Hare, D. Photoelectron Spectroscopy of the Tin Dichalcogenides SnS2−xSex Intercalated with Cobaltocene. Inorg. Chem. 1990, 29 (19), 3860−3866. (56) Shibata, T.; Mironushi, Y.; Miura, T.; Kishi, T. Chemical and Structural Characterization of SnS2 Single Crystals Grown by Low-Temperature Chemical Vapour Transport. J. Mater. Sci. 1991, 26 (18), 5105−5112. (57) Ghosh, B.; Bhattacharjee, R.; Banerjee, P.; Das, S. Structural and Optoelectronic Properties of Vacuum Evaporated SnS Thin Films annealed in Argon ambient. Appl. Surf. Sci. 2011, 257 (8), 3670−3676. (58) Sharma, R. C.; Chang, Y. A. The S−Sn (Sulfur−Tin) System. Bull. Alloy Phase Diagr. 1986, 7 (3), 269−273.

ACS Paragon Plus Environment

28

Page 29 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(59) Ahmet, I. Y.; Hill, M. S.; Johnson, A. L.; Peter, L. M. Polymorph-Selective Deposition of High Purity SnS Thin Films From a Single Source Precursor. Chem. Mater. 2015, 27 (22), 7680−7688. (60) Huang, C.-C.; Lin, Y.-J.; Chuang, C.-Y.; Liu, C.-J.; Yang, Y.-W. Conduction-Type Control of SnSx Films Prepared by the Sol–Gel Method for Different Sulfur Contents. J. Alloys Compd. 2013, 553, 208−211. (61) Tauc, J.; Grigorovici, R.; Vancu, A. Optical Properties and Electronic Structure of Amorphous Germanium. Phys. Status Solidi 1966, 15 (2), 627−637. (62) Ichimura, M.; Takeuchi, K.; Ono, Y.; Arai, E. Electrochemical Deposition of SnS Thin Films. Thin Solid Films 2000, 361−362, 98−101. (63) Rath, T.; Gury, L.; Sanchez-Molina, I.; Martinez, L.; Haque, S. A. Formation of Porous SnS Nanoplate Networks from Solution and Their Application in Hybrid Solar Cells. Chem. Commun. 2015, 51 (50), 10198−10201.

ACS Paragon Plus Environment

29

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 30 of 38

For Table of Contents Use Only TOC/Abstract Graphic

SnS Nanocrystals

Sn0.95S Sn1.00S Sn1.05S

SYNOPSIS As a sustainable synthetic route of nanocrystals, a dry mechenochemical method provides phasepure SnS nanocrystals, resulting in photovoltaic devices with a higher efficiency than those with impurity phases.

ACS Paragon Plus Environment

30

Page 31 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41

ACS Sustainable Chemistry & Engineering

SnS Nanocrystals

Sn0.95S Sn1.00S Sn1.05S

ACS Paragon Plus Environment

TOC/Abstract Graphic

ACS Sustainable Chemistry & Engineering

(a)

Intensity / a.u.

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41

 5h     4h     3h   



2h



Sn1.00S  



 



   SnS







 



1h

Page 32 of 38



 

  

Sn2S3  Sn S

 

20 25 30 35 40 45 50 55 60

2/

o

ACS Paragon Plus Environment

Fig. 1

Page 33 of 38 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41

ACS Sustainable Chemistry & Engineering

ACS Paragon Plus Environment

Fig. 2

ACS Sustainable Chemistry & Engineering

As-synthesized NCs (5 h)

Intensity / a.u.

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41

Page 34 of 38

B3g A g 160 180

Sn1.00S Ag

1

218 cm

Sn2S3 (Ag) 1

305 cm

Ag 1 93 cm

100 150 200 250 300 350 400 450 500

Raman shift / cm

-1

ACS Paragon Plus Environment

Fig. 3

(b),(c)

20 25 30 35 40 45 50 55 60

2 /

o

Intensity / a.u.

(231)/(061) (042) (250)

(200)

(131) (041) (210) (141) (002) (211) (112)/(151) (122)/(160)

(120) (021) (101) (040) (110)

500 C 300 C

(b)

400

(d)

500 C

Post heat-treated Sn1.00S NCs 1

192 cm

300

500 C

200

300 C

100

165

0

30

35

(c) 120 Intensity / a.u.

Post heat-treated Sn1.00S NCs (111)

(a)

Intensity / a.u.

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41

ACS Sustainable Chemistry & Engineering

2 /

o

40

45

300 C

90

Sn2S3

Sn2S3

60

Intensity / a.u.

Page 35 of 38

95 cm

1

1

188 cm

161

1

221 cm

Sn2S3

1

309 cm

(015)

(212)

1

219 cm

30

1

96 cm

0

30

35

2 /

o

40

ACS Paragon Plus Environment

45

100 150 200 250 300 350 400

Raman shift / cm

-1

Fig. 4

ACS Sustainable Chemistry & Engineering



As-syn. NCs

 



(b) 94

  



(116) /(314)



(015)



(212)

(112)

Sn1.00S



As-syn. NCs

187

220

160

Sn1.05S

Intensity / a.u.

 SnS   Sn2S3

(103) (202)

Intensity / a.u.

(a)

Sn2S3 Sn1.05S

93 180 160 218

305 cm

158



183

220

306 cm

 SnS  Sn2S3

Post-heattreated NCs





Sn1.05S

    



(116) /(314)



(015)



(212)

(112)

(103) (202)

Sn1.00S



Raman shift / cm

(d)

Post-heat-treated NCs 163

95

95

165

Sn1.05S 219

Sn1.00S

186 158

220 236

308 cm

1

Sn0.95S

Sn0.95S

2

Sn2S3 219

192



20 25 30 35 40 45 50 55

1

191

Intensity / a.u.



100 150 200 250 300 350 400

95

 

-1

Sn0.95S

20 25 30 35 40 45 50 55 2

(c)

-1

Sn1.00S

93

Sn0.95S

Intensity / a.u.

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41

Page 36 of 38

100 150 200 250 300 350 400

Raman shift / cm ACS Paragon Plus Environment

1

Fig. 5

Page 37 of 38

(b)

1.0

/ a.u.

Sn1.00S Sn1.05S

1.1

1.2

h / eV

Annealed NCs (in 5% H2S)

1/2

2

Annealed NCs (in Ar/5% H2S) Sn0.95S

(F(R)h)

(a) (F(R)h) / a.u.

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41

ACS Sustainable Chemistry & Engineering

1.3

1.4 1.0

Sn0.95S Sn1.00S Sn1.05S 1.1

1.2

1.3

1.4

h / eV

ACS Paragon Plus Environment

Fig. 6

(b) Sn0.95S

ACS Sustainable Chemistry & Engineering

(a)

2㎛ (c) Sn1.00S

(d) Sn1.05S AZO CdS SnS Mo

(e)

Sn0.95S Sn1.00S Sn1.05S

2

20

j / mA cm

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41

Page 38 of 38

10 0 -10 -20

0.0ACS Paragon0.1 0.2 Plus Environment

V/V

0.3

Fig. 7