Stabilization of a Highly Concentrated Colloidal Suspension of Pristine

Jan 24, 2019 - A colloidal suspension containing a high concentration of metallic nanoparticles (NPs) finds potential applications in flexible electro...
0 downloads 0 Views 4MB Size
Subscriber access provided by Iowa State University | Library

Interface Components: Nanoparticles, Colloids, Emulsions, Surfactants, Proteins, Polymers

Stabilization of Highly Concentrated Colloidal Suspension of Pristine Metallic Nanoparticles Nirmal Kumar Katiyar, Krishanu Biswas, Chandra Sekhar Tiwary, Leonardo D. Machado, and Raju Kumar Gupta Langmuir, Just Accepted Manuscript • DOI: 10.1021/acs.langmuir.8b03401 • Publication Date (Web): 24 Jan 2019 Downloaded from http://pubs.acs.org on January 25, 2019

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

Stabilization of Highly Concentrated Colloidal Suspension of Pristine Metallic Nanoparticles Nirmal Kumar Katiyar1, Krishanu Biswas1*, Chandra Sekhar Tiwary2*, Leonardo Dantas Machado3, Raju Kumar Gupta4, 5 1

Department of Material Science & Engineering, Indian Institute of Technology Kanpur -208016, India Department of Metallurgical and Material Engineering, Indian Institute of Technology Kharagpur, West Bengal-721302, India 3 Departamento de FísicaTeórica e Experimental, Universidade Federal do Rio Grande do Norte, NatalRN, 59072-970, Brazil. 4 Department of Chemical Engineering, Indian Institute of Technology Kanpur -208016, India 5 Center for Nanosciences and Center for Environmental Science and Engineering, Indian Institute of Technology Kanpur -208016, India 2

ABSTRACT The colloidal suspension containing a high concentration of metallic nanoparticles (NPs) find potential applications in flexible electronic printing, nanofluids, healthcare, and antifouling coating, etc. Here, we demonstrate a generic, easily scalable, simple and contamination free cryogenic temperature grinding method, which can effectively be used to prepare pristine NPs and can be stabilized in polar liquids in high-concentrations. These surfactant free pristine nanoparticles have been found to remain dispersed in different polar liquids (CH3OH, C2H5OH, Glycol, etc.) for weeks. The long term stability of the nanoparticles in these liquids has been investigated using zeta potentials, in-situ FTIR spectroscopy indicating electrostatic stabilization for ultra pure, surfactant free NPs. Furthermore, stabilization of the NPs has been probed detailed calculation using DLVO theory as well as atomistic molecular dynamic simulation (MD). Experimental measurements along with theoretical calculation categorically indicate the electrostatic energy is helping these nanoparticles to be stabilized in a polar liquid.

Keywords: Nanoparticle colloids, Metallic NPs, Microscopy, Zeta potentials, DLVO, MD simulation.

*email- [email protected], [email protected] 1

ACS Paragon Plus Environment

Langmuir 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Introduction Metallic nanoparticles (NPs) can be made to free stand in colloidal suspension due to two distinctly different mechanisms, depending on whether NPs are capped by organic molecules or native1-3. It is well known that the former is stabilized in the colloids due to steric forces because of the presence of the capping agent. On the other hand, the uncapped NPs are electrostatically stabilized due to the native surfaces4-6. Although the capping agents help in the steric stabilization of the NPs in liquids, but they reduce the direct interaction of NPs with each other as well as the space for preferential adsorptions of ions/molecules on the surfaces of the NPs. It also modifies the surface properties of the NPs drastically limiting the application of the NPs7-10. However, the uncapped NPs provide more freedom to engineer the surfaces and hence properties and they can find more applications. These applications require large scale synthesis of the surfactant of free uncapped metallic NPs, which can be stabilized in polar liquids to form a colloidal solution containing a high concentration of NPs. The last two decades have witnessed extensive research to develop processing techniques suitable to prepare free standing ultra-pure metallic NPs to fulfill the requirements for different applications. These research activities have categorically indicated that grinding/milling at cryogenic temperature (30 mV, indicating Cu and Zn are highly stable. Similarly, shown in Figure 3(d) Cu NPs remain dispersed for 10 days and Zn NPs (longer than a month) as well Al (+23 mV at pH 7) remain to disperse for a month. However, Ag (-20 mV at 7 pH) and Fe NPs have dispersion strength for approximate a day or two. This can further be explained by NPNP interaction in the solvent (methanol) using atomistic molecular dynamics (MD) simulations and DLVO theory (Movie showing Cu NPs interacting with methanol molecules is included in the supporting information). To investigate the distribution of charges near the native surface of a metallic nanoparticle (copper as a representative) immersed in methanol, a detailed MD simulation has been carried and the results are shown in Figure 4. A snapshot of the atomic configuration after equilibration is presented in Figure 4(a), for an NP separation distance of 1 nm. Notice most solvent atoms are transparent, with the exception of those located within 2.5 – 3.0 Å of the nanoparticle surface. To determine the distance of a given solvent atom to the NP surface, its distance to the nearest Cu atom was calculated. Qualitatively, near the NP, mostly oxygen atoms were found followed by hydrogen atoms, and next to a mix of 9

ACS Paragon Plus Environment

Langmuir 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

carbon and hydrogen atoms. Though oxygen atoms adhered strongly to the surface, dissociation of methanol was never observed. To quantify the observations, the average charge values were measured at varying distances from the NP surface. We divided the space around the NPs in regions 0.5 Å wide, starting with one located between 1.0 – 1.5 Å of the nanoparticle surface, and then determined the average charge value for atoms within this layer. The results for two NP separation distances are presented in Figure 4(b). The average charge at the first data point in this graph is exactly zero because there is no atom this close to the nanoparticles. Next, one can also observe high negative average values at the second layer, due to the predominance of oxygen atoms at this distance. While individual charge values varied depending on location, we typically found partial charge figures of -0.5e for oxygen atoms, +0.3e for hydrogen atoms belonging to hydroxyl groups, +0.1e for other hydrogen atoms, and -0.1e for carbon atoms. At the layer centered at 2.25 Å, a mixture of hydrogen and oxygen atoms was found, and in the next layer (whose atoms are highlighted in Figure 4(a)), mostly hydrogen atoms were found. After some layers with mixed composition, we also found a mostly positive layer at 3.75 Å and then another mostly negative layer at 4.75 Å. At distances so near the surface, we found that the location of the second nanoparticle had very little influence on the results. For larger radii, we observed a slight long-range modulation in average charge values when the NPs were close – see Figure 4(b). This clustering of like charges in layers prevents the aggregation of nanoparticles within the methanol solution, as Coulombic repulsion between the negative outer layers (at 4.75 Å) should prevent NP agglomeration. Finally, in Figure 4(c), we examined how atomic composition is evolved in time in the layer at 2.75 Å. Notice that the composition is steady, outside of slight fluctuations, ensuring the long-term stability of the electrostatic barriers that separate nanoparticles. It is to be noted here that the above formalism works only for nanoparticles when electrostatic force and Van der Waals force overcome the gravitational force 10

ACS Paragon Plus Environment

Page 10 of 20

Page 11 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

(movie is included in supporting information). Therefore, the nanoparticles formation below 10 nm is also a main challenge for longer stabilization. Conclusion The present investigation of nanoparticles formation by cryo-milling reveals that the free particles have a native surface (virgin surface bounded by dangling bond), which can easily disperse in polar solvents. The dispersion of NPs in solvent makes them uniformly dispersed as free for longer times due to high repulsion force between two nanoparticles. The highest repulsion force between two particles induced due to physisorption of the methanol molecules over the native surface of nanoparticles, which is responsible for the formation of electrical double layer (EDL) and similar charge over the slipping plane. This similar charge is strongly repelled and hence, can reduce the tendency of agglomeration in the polar solvents. The above study demonstrates a generic method to synthesis highly concentrated metallic colloids, which can be potentially useful for different applications starting from electronic, energy and biomedical. Supporting Information Supporting Information is included with 21 pages, 7 figures, and 2 tables. Acknowledgment Authors would like to thank SERB-DST for the funding to carry out this research work. LDM acknowledges the Brazilian Research Agencies CNPq and CAPES for financial support. References 1.

Bakshi, M. S.; Possmayer, F.; Petersen, N. O., Simultaneous Synthesis of Au and Cu

Nanoparticles in Pseudo-Core−Shell Type Arrangement Facilitated by DMPG and 12-6-12 Capping Agents. Chem. Mater. 2007, 19 (6), 1257-1266.

11

ACS Paragon Plus Environment

Langmuir 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

2.

Bhaumik, J.; Thakur, N. S.; Aili, P. K.; Ghanghoriya, A.; Mittal, A. K.; Banerjee, U. C.,

Bioinspired Nanotheranostic Agents: Synthesis, Surface Functionalization, and Antioxidant Potential. ACS Biomater. Sci. Eng. 2015, 1 (6), 382-392. 3.

Tanner, E. E. L.; Sokolov, S. V.; Young, N. P.; Batchelor-McAuley, C.; Compton, R. G.,

Fluorescence Electrochemical Microscopy: Capping Agent Effects with Ethidium Bromide/DNA Capped Silver Nanoparticles. Angew. Chem. Int. Ed. 2017, 56 (41), 12751-12754. 4.

Pensado, A. S.; Pádua, A. A. H., Solvation and Stabilization of Metallic Nanoparticles in

Ionic Liquids. Angew. Chem. Int. Ed. 2011, 50 (37), 8683-8687. 5.

Xu, M.; Jiang, J.; Pei, X.; Song, B.; Cui, Z.; Binks, B. P., Novel Oil-in-Water Emulsions

Stabilised by Ionic Surfactant and Similarly Charged Nanoparticles at Very Low Concentrations. Angew. Chem. Int. Ed. 2018, 57 (26), 7738-7742. 6.

Min, Y.; Akbulut, M.; Kristiansen, K.; Golan, Y.; Israelachvili, J., The role of

interparticle and external forces in nanoparticle assembly. Nat. Mater. 2008, 7, 527. 7.

Saterlie, M. S.; Sahin, H.; Kavlicoglu, B.; Liu, Y.; Graeve, O. A., Surfactant Effects on

Dispersion Characteristics of Copper-Based Nanofluids: A Dynamic Light Scattering Study. Chem. Mater. 2012, 24 (17), 3299-3306. 8.

Selvakannan, P. R.; Mandal, S.; Phadtare, S.; Pasricha, R.; Sastry, M., Capping of Gold

Nanoparticles by the Amino Acid Lysine Renders Them Water-Dispersible. Langmuir 2003, 19 (8), 3545-3549. 9.

Taguchi, T.; Isozaki, K.; Miki, K., Enhanced Catalytic Activity of Self-Assembled-

Monolayer-Capped Gold Nanoparticles. Adv. Mater. 2012, 24 (48), 6462-6467. 10.

Willert, M.; Rothe, R.; Landfester, K.; Antonietti, M., Synthesis of Inorganic and

Metallic Nanoparticles by Miniemulsification of Molten Salts and Metals. Chem. Mater. 2001, 13 (12), 4681-4685. 12

ACS Paragon Plus Environment

Page 12 of 20

Page 13 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

11.

Kumar, N.; Biswas, K.; Gupta, R. K., Green synthesis of Ag nanoparticles in large

quantity by cryomilling. RSC Advances 2016, 6 (112), 111380-111388. 12.

Barai, K.; Tiwary, C. S.; Chattopadhyay, P. P.; Chattopadhyay, K., Synthesis of free

standing nanocrystalline Cu by ball milling at cryogenic temperature. Mater. Sci. Eng. A. 2012, 558 (0), 52-58. 13.

Kumar, N.; Biswas, K., Cryomilling: An environment friendly approach of preparation

large quantity ultra refined pure aluminium nanoparticles. J. Mater. Res. Technol. 2017. 14.

Zhu, J.; Hersam, M. C., Assembly and Electronic Applications of Colloidal

Nanomaterials. Adv. Mater. 2017, 29 (4), 1603895. 15.

Kim, J.; Park, Y.-S.; Veriansyah, B.; Kim, J.-D.; Lee, Y.-W., Continuous Synthesis of

Surface-Modified Metal Oxide Nanoparticles Using Supercritical Methanol for Highly Stabilized Nanofluids. Chem. Mater. 2008, 20 (20), 6301-6303. 16.

Nandasiri, M. I.; Liu, J.; McGrail, B. P.; Jenks, J.; Schaef, H. T.; Shutthanandan, V.; Nie,

Z.; Martin, P. F.; Nune, S. K., Increased Thermal Conductivity in Metal-Organic Heat Carrier Nanofluids. Sci. Rep. 2016, 6, 27805. 17.

Jimenez de Aberasturi, D.; Montenegro, J.-M.; Ruiz de Larramendi, I.; Rojo, T.; Klar, T.

A.; Alvarez-Puebla, R.; Liz-Marzán, L. M.; Parak, W. J., Optical Sensing of Small Ions with Colloidal Nanoparticles. Chem. Mater. 2012, 24 (5), 738-745. 18.

Na, H. B.; Song, I. C.; Hyeon, T., Inorganic Nanoparticles for MRI Contrast Agents. Adv.

Mater. 2009, 21 (21), 2133-2148. 19.

Magin, C. M.; Cooper, S. P.; Brennan, A. B., Non-toxic antifouling strategies. Mater.

Today 2010, 13 (4), 36-44. 20.

Sen, T.; Bruce, I. J., Surface engineering of nanoparticles in suspension for particle based

bio-sensing. Sci. Rep. 2012, 2, 564. 13

ACS Paragon Plus Environment

Langmuir 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

21.

Derjaguin, B., On the repulsive forces between charged colloid particles and on the

theory of slow coagulation and stability of lyophobe sols. Trans. Faraday Soc. 1940, 35 (0), 203215. 22.

Kumar, N.; Biswas, K., Fabrication of novel cryomill for synthesis of high purity metallic

nanoparticles. Rev. Sci. Instrum. 2015, 86 (8), 083903-8. 23.

Van Duin, A. C. T.; Dasgupta, S.; Lorant, F.; Goddard Iii, W. A., ReaxFF: A reactive

force field for hydrocarbons. J. Phys. Chem. A 2001, 105 (41), 9396-9409. 24.

Monti, S.; Li, C.; Carravetta, V., Reactive dynamics simulation of monolayer and

multilayer adsorption of glycine on Cu(110). J. Phys. Chem. C 2013, 117 (10), 5221-5228. 25.

Plimpton, S., Fast Parallel Algorithms for Short-Range Molecular Dynamics. J. Comput.

Phys. 1995, 117 (1), 1-19. 26.

Aktulga, H. M.; Fogarty, J. C.; Pandit, S. A.; Grama, A. Y., Parallel reactive molecular

dynamics: Numerical methods and algorithmic techniques. Parallel Computing 2012, 38 (4-5), 245-259. 27.

Linic, S.; Aslam, U.; Boerigter, C.; Morabito, M., Photochemical transformations on

plasmonic metal nanoparticles. Nat Mater 2015, 14 (6), 567-576. 28.

Rak, M. J.; Friscic, T.; Moores, A., One-step, solvent-free mechanosynthesis of silver

nanoparticle-infused lignin composites for use as highly active multidrug resistant antibacterial filters. RSC Advances 2016, 6 (63), 58365-58370. 29.

Hunter, R. J.; Ottewill, R. H.; Rowell, R. L., Zeta Potential in Colloid Science: Principles

and Applications. Elsevier Science: 1981. 30.

Verwey, E. J. W.; Overbeek, J. T. G., Theory of the Stability of Lyophobic Colloids.

Dover Publications: 1948.

14

ACS Paragon Plus Environment

Page 14 of 20

Page 15 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

31.

Wang, L.; Albouy, P.-A.; Pileni, M.-P., Synthesis and Self-Assembly Behavior of

Charged Au Nanocrystals in Aqueous Solution. Chem. Mater. 2015, 27 (12), 4431-4440.

15

ACS Paragon Plus Environment

Langmuir 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figures

Figure 1: (a) UV-spectra of metal nanoparticles dispersed in pure methanol; inset shows different NPs in methanol; (b) optical image of Cu NPs dispersed in CH3OH with different concentration; (c) UV–spectra of Cu-NPs dispersed with varying concentration; (d) FTIR spectra of NPs dispersed in CH3OH; (e) XPS spectra of O Corresponding to Ag NPs; (f) XPS spectrum Ag NPs.

16

ACS Paragon Plus Environment

Page 16 of 20

Page 17 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

Figure 2: Bright field -Transmission electron microscopic images with inset showing high resolution image (a) Ag NPs; (b) Al-NPs; (c) Cu-NPs; (d) Fe NPs; (e) Zn NPs; (f) FFT filtered image of Zn NP.

17

ACS Paragon Plus Environment

Langmuir 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 3: (a) Metal-solvent interaction (EDL formation) and (b) Schematic diagram of NP-NP interaction force profile in the polar solvent; (c) Zeta potentials of the metallic NPs dispersed in methanol with varying pH (d) Calculated force profiles of Ag, Al, Cu and Zn NPs at 7 pH and 2 nm Debye length (k-1).

18

ACS Paragon Plus Environment

Page 18 of 20

Page 19 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

Figure 4: (a) Snapshot at the end of an MD equilibration process, for a system where the copper nanoparticles are 1 nm apart. Most solvent atoms are transparent to aid visualization, with the exception of those located within 2.5 – 3.0 Å of the nanoparticle surface. (b) Graph displaying average charge values at a distance from the nanoparticle surface, for two NP separation values. For instance, to obtain the data point at 2.75 Å, we considered in the average all opaque atoms from (a). The yellow curve is merely a guide to the eye. (c) Graph is presenting the number of atoms located within 2.5 – 3.0 Å of the nanoparticle surface versus elapsed simulation time, for copper NPs 1 nm apart. Notice the stability in atomic composition.

19

ACS Paragon Plus Environment

Langmuir 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 20

Table 1: Size of metals nanoparticles and position of surface plasmon resonance (SPR) dispersed in methanol.

Metal NPs

Size (nm)

SPR band(lmax) (Methanol)

Ag NPs

6±2

465

Al NPs

6±3

266

Cu NPs

7±2

375

Zn NPs

3±1

274

Fe NPs

8±3

310

TOC

20