Sub-10 Nanometer Tunable Hybrid Dielectric Engineering on MoS2 for Two-Dimensional Material-Based Devices Lanxia Cheng, Jaebeom Lee, Hui Zhu, Arul Vigneswar Ravichandran, Qingxiao Wang, Antonio T. Lucero, Moon J. Kim, Robert M. Wallace, Luigi Colombo, and Jiyoung Kim ACS Nano, Just Accepted Manuscript • DOI: 10.1021/acsnano.7b04813 • Publication Date (Web): 23 Aug 2017 Downloaded from http://pubs.acs.org on August 23, 2017
Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.
ACS Nano is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.
Page 1 of 24
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Nano
Sub-10 Nanometer Tunable Hybrid Dielectric Engineering on MoS2 for TwoDimensional Material-Based Devices Lanxia Cheng,*† Jaebeom Lee,† Hui Zhu,† Arul Vigneswar Ravichandran,† Qingxiao Wang,† Antonio T. Lucero,† Moon J. Kim,† Robert M. Wallace,† Luigi Colombo,‡ Jiyoung Kim*† †
Dept. of Materials Science and Engineering, The University of Texas at Dallas, Richardson, TX
75080, USA ‡
Texas Instruments, Dallas, TX 75243, USA
*Corresponding authors: Tel:+1 972-883-6412, E-mail:
[email protected],
[email protected] ABSTRACT:
The
successful
realization
of
high-performance
2D
materials
based
nanoelectronics requires integration of high-quality dielectric films as a gate insulator. In this work, we explore the integration of organic and inorganic hybrid dielectrics on MoS2 and study the chemical and electrical properties of these hybrid films. Our atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), Raman and Photoluminescence (PL) results show that, aside from the excellent film uniformity and thickness scalability down to 2.5 nm, the molecular atomic layer deposition (MLD) of octenyltrichrolosilane (OTS) and Al2O3 hybrid films preserve the chemical and structural integrity of the MoS2 surfaces. The XPS band alignment analysis and electrical characterization reveal that through the inclusion of an organic layer in the dielectric film, the bandgap and dielectric constant can be tuned from ~7.00 to 6.09 eV and ~9.0 to 4.5, respectively. Furthermore, the hybrid films show promising dielectric properties, including high breakdown field of ~7.8 MV/cm, low leakage current density of ~1×10-6 A/cm2 at 1 MV/cm, small hysteresis of ~50 mV, and top gate sub-threshold voltage swing of ~79 mV/dec. Our experimental findings provide a facile way of fabricating scalable hybrid gate dielectrics on transition metal dichalcogenides（TMDs）for 2D-material-based flexible electronic applications. KEYWORDS: MLD, hybrid dielectric, MoS2 FETs, Raman, photoluminescence, dielectric scaling
1 ACS Paragon Plus Environment
ACS Nano
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 2 of 24
Since the pioneering work on the first single layer MoS2 switchable transistor,1 2D transitional metal dichalcogenides (TMDs) have ignited significant interest in pursuing them for electronic applications, including tunnel field transistors (TFETs),2,3 heterojunction p-n photodiodes,4 transparent flexible optoelectronics,5,6 and memory devices.7,8 However, achieving the physical limits of these 2D semiconductors has met many integration challenges, such as growth of wafer-scale channel materials,9,10 high Schottky barrier,11 doping strategies,12-14and scaling dielectrics,15,16 each of which requires sustained efforts before the full technological potential of these 2D materials can be implemented.17,18 Earlier studies on graphene18,19and MoS21, 20-22 transistors have shown a considerable mobility enhancement by having the 2D channel encapsulated with high-k dielectrics to screen charged impurities.23 Moreover, vertically-stacked 2D heterojunctions, being physically isolated by a few layers of hexagonal boron nitride (h-BN),2,3,24 have exhibited inter-band tunneling and negative differential resistance, allowing for further reduction of the sub-threshold slope below 60 mV/decade and supply voltages less than 0.5 V. In all cases, conformal pin-hole free and ultrathin dielectrics are desired to minimize the OFF-state power dissipation. However, direct ALD growth of thin dielectrics on clean untreated 2D channels exhibits poor nucleation due to the dearth of dangling-bonds.15,16,20 To date, most reported conformal ALD dielectrics were grown on 2D surfaces pre-treated with oxygen species,15,16,25 seeding layers, e.g. organic TiOPc,26,27 or metal oxide buffer layers,28,29 showing performance tradeoffs between dielectric thickness and the electrical metrics. Whereas h-BN, an intrinsic 2D insulator, exhibits nearly ideal dielectric properties,2,30 such as wide band-gap (6 eV), high breakdown field (7 V/cm), and low interface trapped charges, the unavailability of high quality large-area material has been a major roadblock for process integration.9,10 Alternatively, the use of hybrid dielectrics, a family of self-assembled organic and inorganic nano-laminate films, on MoS2, has not yet been explored. Their low process temperature, large-area deposition capability, and great mechanical flexibility combined with the excellent in-plane stiffness of MoS2,31 could provide a great step forward to the practical application of TMDs for large-area 2D materials-based flexible electronics.6,17 Herein, we explored the integration of an organic and inorganic hybrid film on MoS2 using molecular layer deposition (MLD) and investigated the dielectric properties using dual-gated MoS2 devices. Since MLD utilizes a self-limiting surface reaction mechanism similar to ALD, it not only enables film deposition with precise thickness control, but also permits the “tuning” of 2 ACS Paragon Plus Environment
Page 3 of 24
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Nano
the film chemical and electrical properties by modulating the functionality of the relevant organic and inorganic components and their relative composition ratio.32,33 Here, we employed the MLD of octenyltrichrolosilane (OTS) to form the self-assembled organic layer and used ALD of TMA/H2O to deposit the Al2O3 linker between the neighboring OTS layers. By combing MLD and ALD, a hybrid dielectric composed of alternatively arranged OTS-Al2O3-OTS film is achievable on the MoS2 substrate. Our results show the formation of a pinhole free and uniform hybrid dielectrics on the MoS2 surface with a sub-nanometer growth rate of 0.5 nm/cycle and excellent thickness scalability down to 2.5 nm. The interface chemistry studies using XPS, Raman, and PL suggest that MoS2 maintains excellent structural and composition integrity after deposition of OTS-Al2O3 films. Electrical results of top-gated MoS2 devices showed that these films exhibit promising transistor dielectric properties, such as low leakage current (10-6 A/cm2 at 1 MV/cm), minimal doping, small hysteresis and sub-threshold voltage at zero back-gate bias. Our experimental findings provide a way of fabricating scalable hybrid gate dielectrics on TMDs for 2D material-based electronics. RESULTS AND DISCUSSION MLD dielectric development and characterization. Figure 1a shows the schematic integration
process of the MLD OTS-Al2O3 hybrid films on the MoS2 substrate (see Experimental and Methods for details). Since the as-exfoliated MoS2 surface is relatively inert due to the low dangling bond density, which limits its reactions with the incoming precursors, we employ an insitu ozone pretreatment to functionalize the MoS2 with oxygen adsorbates that are necessary to anchor the alkyltrichlorosilane (R-SiCl3) forming densely packed self-assembled alkyl-packed films.34,35 Ozone or oxygen plasma enhanced ALD dielectrics have been demonstrated in several recent studies,15,16,25 in which a reactive oxygen species exposure prior to ALD can significantly improve the dielectric nucleation originating from the resultant weak sulfur-oxygen interactions. After ozone pre-exposure at 100 C°, a monolayer of OTS organic layer is deposited via 5 repeated OTS/H2O sub-cycles to promote the hydrolysis of the trichlorosilane (-SiCl3) to form (CH2)n-Si-O-S (Mo) chains until a saturated monolayer OTS is reached as shown in Figure 1a(iiii). To initiate the MLD super-cycle for a continuous hybrid film growth, a second ozone exposure of 10 s is performed immediately on the self-assembled OTS film to chemically convert the OTS terminal C=C bond into carboxyl (-COOH) group.34,36 The resultant hydrophilic
3 ACS Paragon Plus Environment
ACS Nano
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 4 of 24
carboxyl tail groups then serves as nucleation sites for the subsequent TMA/H2O surface chemical adsorption, leading to the formation of an atomic layer of inorganic linkers (C-OAl(OH)-OH) that connects with the successive OTS layer through an O-Si bond. By repeating the pulse of each precursor in such a sequence as shown in Figure 1a(iii-vi), that organicinorganic OTS-Al2O3 hybrid film ranging from monolayer organic film to tens of nanometer of hybrid films are achievable by controlling the MLD growth super-cycles. The surface morphology and energy (wettability) changes of MoS2 are monitored using AFM and DI-water contact angle measurement. As shown in Figure 1b-c, the pristine MoS2 surface is smooth with a root mean squared (RMS) roughness of 0.06 nm and a contact angle of ~55°, suggesting that the MoS2 surface is hydrophobic. Ozone exposure under static vacuum condition (10 s pulse with 100 s “static vacuum” see Experimental and Methods for details) results in a slight increase of the RMS roughness to 0.09 nm and a decrease of the contact angle to less ~10° due to the oxygen adsorption, indicative of the formation of a completely oxygen- or hydroxylcovered MoS2 surface. Adsorption of oxygen species on MoS2 is also confirmed by the appearance of the O 1s peak in the corresponding XPS results shown in Figure S1a-b. Notably, the relevant XPS spectra of Mo 3d and S 2p chemical binding states reveal neither the detection of Mo oxidation states (232.7 eV) nor the formation of a weak S-O binding state (164.8 eV) after brief ozone exposure,37 where the latter is claimed to stem from the UV light exposure16 or longer oxygen radical treatment.37 Since all of the MoS2 flake surface characterization after ozone exposure was carried outside of the deposition chamber, contact angle measurements and XPS characterization were completed within 5 minutes in order to minimize the ambient air exposure. In accordance with the phenomena reported on the short time oxygen species pretreated MoS2 surface,15,25 it is likely that only physisorbed oxygen species are introduced onto the MoS2 surface during the brief ozone exposure, which merely functionalizes the MoS2 surface with O atoms but does not introduce noticeable oxidation states (i.e. etching) in the MoS2 lattice structure. Our findings, together with other studies16,38,39provide substantial evidence that ozone, rather than an oxygen plasma, provides a gentle and efficient functionalization of the MoS2 surface, given the presence of relatively stronger Mo-S covalent bonds.15 The MoS2 surface contact angle changes to ~78 ° after 5 successive sub-cycles of OTS/H2O exposures at 100 °C, signifying the formation of saturated OTS self-assembled layers that increases the MoS2 surface RMS roughness to 0.12 nm as shown in Figure 1d. In contrast to the 4 ACS Paragon Plus Environment
Page 5 of 24
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Nano
rough surface prepared in wet solution self-assembled OTS film shown in Figure S1c, the MLD monolayer OTS film tends to be clean and smooth without formation of any island-aggregates arising from the trichlorosilane intermolecular cross-link reactions or solvent residues.35 Figure 2d shows the AFM surface morphology of an MLD prepared OTS-Al2O3 film after 10 supercycles; the low RMS roughness of 0.15 nm suggests that a very smooth and uniform hybrid dielectric film can be achieved on the MoS2 surfaces, enabling the formation of the hydrophobic surface with a high contact angle of ~80°. Hydrophobic surfaces of low roughness have led to several beneficial impacts on the electrical performance of graphene40,41 and MoS242,43 transistors in terms of enhanced carrier mobility, controllable doping and improved device stability. The excellent film uniformity and smoothness of the MLD prepared OTS-Al2O3 suggest these materials hold great prospects as dielectric film for improving the electrical performance of 2D material-based electronics. To ascertain the integration of OTS-Al2O3 films on the MoS2 surface using the MLD process, XPS characterization of the film composition and interfacial chemical states of MoS2 were conducted. Figure 2a shows the peak evolution of Mo 3d and S 2p binding states as a function of MLD super-cycles in reference to that of the as-exfoliated MoS2 surface. The prominent doublet peaks located at 229.5 eV and 232.6 eV are ascribed to Mo 3d5/2 and Mo 3d3/2 component of the Mo 3d chemical state in MoS2, whereas similar doublet peaks appearing at 162.3 eV and 163.5 eV correspond to the S 2p3/2 and S 2p1/2 signals of S 2p binding state, respectively. Close examination of the XPS binding states of the as-exfoliated MoS2 does not reveal any detectable additional chemical states ca. 232.7 eV (Mo 6+) or 229.2 eV (Mo 4+), and S-O (164.8 eV) associated with either molybdenum or sulfur oxidization.37 In addition, the peak intensities of both the Mo 3d and S 2p states display continuous attenuation as result of the deposition of thicker hybrid dielectrics. The XPS intensity attenuation of Mo 3d peak is estimated to be 25% after 5 successive OTS/H2O sub-cycles, which is complementary to the appearance of the asymmetric Si 2p binding states at 102.8 (Si-O) and 101.5 eV (Si-C),35 provides convincing evidence for the formation of monolayer OTS hydrocarbon layer on MoS2. As indicated in Figure 2b, the lower binding energy peak at 101.5 eV is assigned to the Si-C bond from the alkane-silicon backbone, and the higher binding energy peak corresponds to the Si-O bond resulting from the hydrolysis interaction of Si-OH group with the oxygen adsorbates on the MoS2 interface. It is noted that our XPS survey spectra and Cl 2p core level shown in Figure 5 ACS Paragon Plus Environment
ACS Nano
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 6 of 24
S2a,c do not reveal any detectable chlorine, which is indicative of complete hydrolysis of chlorosilane and the removal of inorganic byproducts during the purge process step. After five OTS-Al2O3 super-cycles, along with further attenuation of Mo 3d peak intensity, the Al 2p chemical binding state at 74.6 eV emerges and is attributed to the formation the Al-O bond as the result of the chemical reaction between the carboxyl (COOH) tail group and TMA precursor. As depicted in Figure S2b, the conversion of C=C tail group of OTS into carboxylate species (COOH) is also clearly identified from the presence of multiple C 1s chemical binding states deconvoluted at 288.6 eV (C=O), 285.8 eV (C-O), and 284.6 eV that is attributed to the -CH2 component of OTS hydrocarbon backbone.44 Based on the Mo 3d peak intensity attenuation (detailed in Supporting Information), the overlayer thickness is calculated to be 0.63 ± 0.1 nm for monolayer, 2.3 ± 0.2 nm for five, and 5.3 ± 0.5 nm for ten MLD OTS-Al2O3 super-cycles, in good agreement with the corresponding thickness measured on hydrogen terminated Si as shown in Figure 2c. This growth rate indicates a further tilted OTS molecular orientation of ~60° from the surface normal.36 The constant growth rate of approximately 0.5 nm/super-cycle is further verified with the cross-sectional highangle annular dark field (HAAF)-scanning transismission electron microscopy (STEM) thickness measured on five MLD super-cycles of OTS-Al2O3 films. Figure 2d shows the STEM image from a uniform pin-hole free organic-inorganic hybrid layer of 2.5 nm on the surface of MoS2 with an atomically sharp interface. The corresponding EELS result shown in Figure S3 confirms the composition of the hybrid film is dominant with C, O elements. Notably, as is demonstrated in Figure S4, this uniform and conformal deposition of OTS-Al2O3 ultrathin hybrid films can also be transferred onto the WSe2 surface with excellent film uniformity and thickness scalability down to 2.3 nm, in addition to the preservation of the surface structural and chemical integrity of WSe2 substrate. To gain further insight into the energy band alignment at the interface of MoS2 and OTSAl2O3 hybrid dielectrics, XPS analysis of the valence band-edge spectra of the bulk MoS2 and OTS-Al2O3 film (~15.7 nm prepared by 30 MLD super-cycles) is performed according to the photoelectron spectroscopic method elaborated in previous studies.45,46As shown in Figure 3a, the relevant valence band maximum (VBM) is extracted by linearly extrapolating the leading valence band edge of an experimental VB spectrum to the baselines collected on the bulk MoS2 and OTS-Al2O3 dielectric, which is determined to be ~1.04 eV for MoS2 and ~3.08 eV for thick 6 ACS Paragon Plus Environment
Page 7 of 24
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Nano
OTS-Al2O3 dielectric. Since XPS core level binding energies of the interface Mo 3d and Al 2p remain the same, the valence band offset (VBO) is therefore directly determined from VBM difference and is ~2.04 eV at the MoS2 and hybrid dielectric interface. The XPS binding energy accuracy we defined here is ± 0.1 eV37,62 and is due to the linear extrapolation errors associated with the scatter of VB spectrum and O 1s loss feature. Figure 3b shows the energy separation between the O 1s core level of OTS-Al2O3 films and the onset of O 1s loss feature that correlates to the excitation of electrons from valence band maximum to conduction band minimum, which enable a direct determination of band gap to be ~6.09 eV for OTS-Al2O3 hybrid film.47,48 Based on these experimentally determined values in reference to the band gap of ~1.2 eV for bulk MoS2, the schematic energy band diagram for MoS2 and OTS-Al2O3 dielectric is proposed in Figure 3c, where the related conduction band offset (CBO) is inferred to be ~2.85 eV. In contrast to the relatively wider VBO and CBO found for the MoS2/Al2O3 interface,45 our results suggest that the inclusion of organic OTS component in ALD high-k dielectric films can lower the inorganic dielectric bond gap, but still render a sufficient barrier to be used as a dielectric. In addition to the preservation of the surface chemical and structural integrity, Raman and photoluminescence (PL) spectroscopic studies of the electronic band structure of MoS2 after OTS-Al2O3 film deposition is also important. Recently, there have been several studies reporting the charge carrier doping of TMD channels utilizing self-assembled organic monolayers e.g. Octadecyltrichlorosilane (OTS)
49,50
or Alkanethiol,51 by virtue of their inherent molecular
polarity and functionality. However, since in all of these studies the monolayer self-assembling process involves the dipping of TMDs in solution for varying times, the doping impact arising from the physisorbed polar solvent molecule and reaction by-products can not be excluded, and this may account for the inconsistent doping behaviors observed with the OTS treated MoS2.42,50In contrast, the vapor based MLD process employed here provides a very clean film growth environment (vacuum chamber with base pressure ~4×10-2 mTorr) for deposition of SAMs or hybrid dielectric films on MoS2 surface, which gives the least concerns over the film reproducibility arising from any uncontrollable preparation conditions. Raman and PL response of MoS2 with a hybrid dielectric. Figure 4 displays the Raman and PL spectra, along with the corresponding peak position mapping images, of MoS2 flake of varied thicknesses prior to and after MLD of OTS-Al2O3 films. The layer thickness of MoS2 flake is verified by a combination of optical contrast, AFM and spectroscopic measurement as shown in 7 ACS Paragon Plus Environment
ACS Nano
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 8 of 24
Figure S5a-b. It should be noted that SiTO Raman mode at 520.5 cm-1 is calibrated before each Raman and PL measurement to assure the consistency in monitoring the MoS2 Raman and PL shifts. Figure 4a shows the typical Raman spectra of MoS2 flakes with two dominant peaks at 385.6 cm-1 and 404.4 cm-1 that are assigned to the S-Mo-S in-plane (E2g1) and out-of-plane (A1g) mode, respectively. As the MoS2 thickness increases, the peak separation also increases from 18.8 to 20.5 and 24.5 cm-1, corresponding to 1, 2 and 4 L of MoS2 according to the published literature.52After MLD, both the E2g1 and A1g modes of 1 L MoS2 exhibit slight redshift of 1.2 ± 0.1 cm-1 and 0.4 ± 0.1 cm-1, respectively. The redshift E2g1 most likely originates from the strain induced phonon softening that has been discussed by Conley et al.,53 in which an increase of the uniaxial tensile strain on monolayer MoS2 is found to downshift and split the in-plane E2g1 resonance mode due to the crystal symmetry breaking. However, since the tensile strain imposes a negligible effect on the A1g mode, the observed minor redshift of A1g resonance frequency may be related to the carrier doping effect that alters the strength of electron-phonon interactions contributing to mostly the shift of the out-of-plane vibration mode. In contrast to the significant doping phenomena discovered with solution-based self-assembled monolayer49,50 or chemical doping, (≥1.0×1013/cm2),13,54 the observed A1g shift after MLD dielectric deposition is nearly negligible, within the error of Raman spectra resolution (0.5 cm-1). Moreover, both the strain and doping effects become completely suppressed as the MoS2 thickness increases to more than 2 layers, as seen from the related Raman mapping images (Figure 5b-c). This suggests that any electronic structure variations introduced from the OTS-Al2O3 film deposition exist only in the topmost layer of the MoS2 flake. Similar minor redshifts (~0.3 cm-1) of MoS2 vibration modes are also visible with the ALD-Al2O3 covered monolayer MoS2 (Figure S5e), indicating that the strain effect is the main reason accounting for the observed Raman shifts. In agreement with the Raman spectra (Figure 4a), the slight A1g Raman resonance softening merely happens to the monolayer region and is nearly suppressed entirely as the film thickness increases (Figure S5c-d). In agreement with the Raman results, the PL signal of monolayer MoS2 exhibits tensile strain associated redshift and intensity attenuation after OTS-Al2O3 deposition.53 As shown in Figure 5d, as-exfoliated MoS2 shows two characteristic PL peaks at 1.82 eV (A exciton) and 1.98 eV (B exciton), respectively, that are associated with the direct-gap transition from the spin-orbit valence band splitting to the conduction band edge. The intensity of the A exciton peak decreases as the thickness of MoS2 increases from 1 to 2, 4 L layers, in accordance to the published 8 ACS Paragon Plus Environment
Page 9 of 24
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Nano
results,14,55 due to the thickness related direct to indirect band-gap transition. Similar to the Raman findings, the relatively minimal energy shift occurring to the A exciton of the bilayer and multilayer MoS2, the growth of OTS-Al2O3 dielectric only redshifts the monolayer A peak by 20 meV. This energy shift, in addition to the decreased PL intensity, suggests that only a small amount of tensile strain, ca. less than 1%,53 is introduced into the topmost layer of MoS2 flakes. Like the Raman mapping results, the PL mapping images (Figure 5d-e) suggest that this A peak energy shift is only noticeable in the monolayer MoS2 region, and is attenuated considerably as the MoS2 thickness increases. It is important to note that an unambiguous determination of the reasons causing the redshifts of MoS2 Raman and PL phonon emission modes is nontrivial when considering the complex phonon-electron interaction scenarios in carrier-doped, strained and oxygen radical degraded MoS2 structures.14,39,51,53 Nevertheless, based on our Raman and PL observation of the minimal peak shifts in comparison to aforementioned studies, MLD deposition of OTS-Al2O3 on MoS2 tends to maintain the electronic band structure of underlying MoS2 resembling Raman spectra changes caused by ALD high-k dielectric process.15,25,38 Electrical characterization of MoS2 FETs using MLD dielectrics. Figure 5a displays the schematic diagram of a representative dual-gated MoS2 field effect transistor with 7.5 nm OTSAl2O3 as a hybrid top-gate dielectric to evaluate the electrical performance of MoS2 devices. The dual-gated MoS2 FETs are fabricated with few-layer MoS2 (~6-10 layers) exfoliated on 285 nm SiO2/ n+Si substrate. Source/drain and top gate regions are patterned using e-beam lithography followed by electron-beam deposited Cr/Au (15/65 nm) as contact metals. Figure 5b-c compare the transfer and output characteristics of the back-gated MoS2 transistor before and after dielectric deposition. The transfer curve of as-fabricated MoS2 exhibits a typical n-type transistor behavior with an on/off ratio of ~106 and hysteresis of ~∆Vth = 15 V as the back-gate voltage sweeps back and forth from -30 V to 30 V at fixed Vds of 0.5 V. Upon encapsulation with OTSAl2O3 dielectric, the threshold voltage (Vth) shifts positively ~4.1 V with hysteresis reduced to 5.3 ± 0.5 V. The positive Vth is indicative of a p-doping effect, in contrast to the negative Vth shifts reported on most ALD Al2O320 or HfO222,56oxides. This opposite doping behavior may be explained by the presence of interface trapped charges from H2O or O2 adsorbates during MLD OTS layer deposition, whereas ALD oxides tends to introduce positive fixed charges.20 Using the formula: ne=Q/e=CBG|∆Vth|/q, where q is the elementary charge, the doping carrier concentration is estimated to be ~3×1011/cm2, which is smaller than the doping concentrations (~7×1012/cm2) 9 ACS Paragon Plus Environment
ACS Nano
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 10 of 24
introduced by solution based self-assembled organic films.42,51In addition, using the following equation: µ=gm L/WCbgVds where L and W are the channel length and width, respectively and g =
is the transconductance, the effective carrier mobility of the pristine MoS2 back gated
devices fabricated prior to MLD is around 28.7 cm2/Vs, which increases to 39.1 cm2/Vs after OTS-Al2O3 dielectric deposition. The Ids-Vbg curve shows a slight increase in current density (~10%) from 0.95 to 1.1 µA/µm measured at Vds=0.5 and Vbg = 10 V and saturates at 3.4 µA/µm at a high drain bias region, this is likely owing to the pinch-off of the conducting channel. Although, in comparison to the considerable charge carrier mobility improvement reported in ALD high-k dielectric encapsulated MoS2 devices,20,28,57 our electrical characteristics of OTSAl2O3 capped MoS2 show no significant charge carrier mobility enhancements. However, the back-gate hysteresis, 5.3 ± 0.5 eV (Figure S6a-b), and the interfacial trapped charge density, according to the subs-threshold swing to be ~1.95×1012/cm2, are close to the those reported results (~1012-1013 /cm2) using UV-ozone functionalized ALD-oxides38,57,58 or low temperature ALD process,20,59 which is likely due to the trapped H2O or O2 interfacial charge scattering. Figure 5d shows the current density as a function of top gate voltage (Vtg = -1 to +1 V) with the back-gate bias sweeping from Vbg = -60 to +60 V at a step of 10 V. As the Vbg is varied from negative to positive voltage, the carrier density in the MoS2 channel region is changed from p to n-type doping, therefore, shifting the threshold voltages negatively and leading to the increase of current density.60 At zero back gate voltage, a small hysteresis less than ~50 mV is identified as the top gate bias sweeps from -1 to 1 V forward and backward, which, using geometrical capacitance of gate stack, yields top-gate trap charge density of ~1.8×1011 /cm2 at the interface of MoS2 and OTS-Al2O3 dielectric. The field effect mobility of this top gate device is extracted to be ~25 cm2/Vs under Vds =0.5 V with the sub-threshold voltage of ~79 mV/dec, which is similar to the report values for thin top-gate ALD-Al2O3 on MoS2.20,25 Figure 5e shows a corresponding two-dimensional (2D) current density map of dual-gate MoS2 FET with 7.5 nm OTS-Al2O3 film as top gate and 285 nm SiO2 as bottom gate dielectric, representing the combined dual gates (Vtg and Vbg) modulation of the channel current density (Ids) at Vds = 0.5 V. By calculating the slope of current maxima in the 2D current density plot, the OTS-Al2O3 top gate dielectric constant and capacitance can be extracted using the following equation: Cbg/Ctg= 1/slope, where the Ctg and Cbg refer to the top and back gate capacitances, 10 ACS Paragon Plus Environment
Page 11 of 24
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Nano
respectively. The back-gate capacitance is calculated to be 12 nF/cm2, which gives a top gate capacitance of 563 nF/cm2 and a dielectric constant of 4.5 ± 0.5 OTS-Al2O3 hybrid films, in close agreement with the value extracted from the Au/ OTS-Al2O3/Si metal-insulator-metal structures shown in Figure S6c.60 This dielectric constant is lower than that of ALD-Al2O3 (~9.0) because of the incorporation of OTS component with lower dielectric constant (2.5),60 which, hence, offers a way to tune the dielectric constant of the stack by incorporation of proper organic moieties. Furthermore, the breakdown voltage of our hybrid films is determined to be 7.8 ± 0.2 MV/cm, in close to the prior reported breakdown field of high-k ALD oxides.25,57 Figure 5f displays the top gate leakage current density of hybrid OTS-Al2O3 film scaling down from 7.5 nm to 2.5 nm using Ru as a top metal contact to prevent leakage current reduction from metal oxidation. The leakage current density through a 7.5 nm thick OTS-Al2O3 films is ~1×10-6 A/cm2 at an electric field of ±1 MV/cm, and it increases to ~2.3×10-4A/cm2 and ~10 A/cm2 as the dielectric thickness scales down to 5 and 2.5 nm. The leakage current density of the 7.5 nm thick hybrid dielectric resembles the minimal leakage level measured for thicker OTS-Al2O3 dielectrics and is comparable to those reported high-k ALD dielectrics of similar thickness.25-27 In light of the electrical characterization, along with the other interesting properties including low integration temperature, film flexibility and ultralow water permeability,61 the OTS-Al2O3 hybrid film presents a promising dielectric candidate for diverse applications in 2D materialbased flexible electronics. CONCLUSION In summary, we have explored the deposition of hybrid dielectrics on the MoS2 surface by combining the molecular layer deposition of organic OTS layer and atomic layer deposition of the inorganic Al2O3 linker. The self-limiting surface reactions of MLD OTS-Al2O3 demonstrates a constant sub-nanometer deposition rate of 0.5 nm/super-cycle, allowing for scalable dielectric film thickness down to 2.5 nm with excellent preservation of the surface chemical and structural properties. XPS and electrical characterization suggest that a reduction of the inorganic metal oxide band gap to 6.09 eV and dielectric constant of 4.5 by incorporation of organic OTS component in the dielectric films, suggesting possible band structure tunability by a proper selection of organics. Additionally, the Raman and PL spectroscopic characterization reveal minimal alteration of the interfacial electronic structure of few-layer MoS2 flakes after OTS11 ACS Paragon Plus Environment
ACS Nano
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 12 of 24
Al2O3 dielectric integration. The electrical results of dual-gate MoS2 transistor exhibit promising dielectric properties including a small sub-threshold swing (~79 mV/dec), small hysteresis (~50 mV) and a low leakage current density (