Wetting Properties of Seven Phosphonium Cation ... - ACS Publications

Subscriber access provided by Northern Illinois University

Article

Wetting properties of seven phosphonium cation-based ionic liquids David Blanco, Marlene Bartolome, Beatriz Ramajo, José Luis Viesca, Ruben Gonzalez, and Antolin E. Hernández Battez Ind. Eng. Chem. Res., Just Accepted Manuscript • DOI: 10.1021/acs.iecr.6b00821 • Publication Date (Web): 23 Aug 2016 Downloaded from http://pubs.acs.org on August 26, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Industrial & Engineering Chemistry Research is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Industrial & Engineering Chemistry Research

Wetting properties of seven phosphonium cation-based ionic liquids D. Blancoa, M. Bartoloméb, B. Ramajoc, J.L. Viescaa,d R. Gonzálezb,d, A. Hernández Batteza,d* a

Department of Construction and Manufacturing Engineering, University of Oviedo, Asturias, Spain b Department of Marine Science and Technology, University of Oviedo, Asturias, Spain c Department of Physical and Analytical Chemistry, University of Oviedo, Asturias, Spain d Department of Design and Engineering, Bournemouth University, Poole, BH12 5BB, UK ( ) * Email: [email protected]

Abstract This paper studies the wetting properties of seven phosphonium cation-based ionic liquids: trihexyltetradecylphosphonium

bis(2,4,4-trimethylpentyl)

phosphinate

[P66614][(iC8)2PO2],

trihexyltetradecylphosphonium bis(2-ethylhexyl)phosphate [P66614][BEHP], trihexyltetradecylphosphonium bis(trifluoromethylsulfonyl) imide

[P66614][NTf2], tributyltetradecylphosphonium dodecylbenzenesulfonate

[P44414][DBS], tributylethylphosphonium diethylphosphate [P4442][DEP], trihexyltetradecylphosphonium dicyanamide [P66614][DCA] and trihexyltetradecylphosphonium chloride [P66614][Cl]. The surface tension was analyzed using the Gibbs free energy in a temperature range of 293-353K, obtaining the expected linear decrease with temperature rise. The contact angle was measured on four different surfaces (AISI 52100 steel, CrN, TiN and ZrN) and all liquids with high surface tensions interacting with hydrophobic systems displayed high contact angles as expected. The polarity fraction (PF) and the spreading parameter (SP) were estimated to complete and improve the wetting characterization of these ionic liquids, finding TiN-[P66614][BEHP] and TiN-[P66614][(iC8)2PO2] as the most favorable surface-ionic liquid combinations from a wetting point of view.

Key words: phosphonium cation-based ionic liquids, contact angle, surface tension, wetting, polarity

1

ACS Paragon Plus Environment


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1. Introduction Ionic liquids (ILs) are attracting recent research interest as potential candidates for discovering clean technologies1-3 due to their unique properties such as low melting temperature, nonflammable behavior, high thermal stability, near-zero vapor pressure, wide electrochemical window, large liquid range, high ionic conductivity and a highly adjustable solvating capacity for both polar and non-polar compounds. Evaluating the physicochemical properties of these molten salts is essential to guarantee the use of such compounds in a broad range of applications.4-7 An accurate design of industrial processes based on ILs can only be achieved when their physicochemical properties are well known. Therefore, it is important to measure these properties in order to improve their characterization, not only for designing but also for developing correlations either between these properties or with performance parameters.8 One of the main advantages of working with ILs is the possibility of easily adapting their properties with small variations in the chemical composition, thus having a huge potential for engineering applications.2 This fact may be used as a tool for self-tuning the ILs with multiple and useful application possibilities by changing physicochemical properties, such as density, melting point, viscosity, conductivity or surface tension.9 For instance, water miscibility of ILs is usually controlled by the anion, although the cation can also affect the hydrophobicity of the substance. Moreover, increasing either the size of the anion or the alkyl side chains of the cation leads to a decrease in polarity due to the spreading of negative charge.10 Therefore, a study of the relationship between structure and physicochemical properties could enable designing ILs with tailored capabilities.1 From the lubrication point of view, understanding the tendency of a liquid to spread on a solid surface is a very important factor affecting the performance of the lubricant.11-13 Furthermore, thin hard physical vapordeposited (PVD) coatings are also frequently used in a number of engineering applications.12-20 Measuring surface tension and contact angle are a good way to evaluate wetting ability.21 The surface tension (Eq. 1) can be divided as a sum of independent contributions named dispersive (d) and non-dispersive (nd), with only dispersive interactions (determined using the geometric mean rule) occurring across the interface.22 Therefore, the work of adhesion (WSL) as depicted in Eq. 2 and Eq. 3 can relate these dispersive interactions with the solid-liquid interfacial tension (γSL), linked with the contact angle (θ) through the Young equation (Eq. 4), as

2


Page 2 of 25

Page 3 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


shown in Figure 1, where total surface energy (γSV) and interfacial tension liquid-vapor (γLV) are usually expressed as γS and γL, respectively.

γ = γ d + γ nd

(

WSL = 2 γ Sd ⋅ γ Ld

(1)

)

γ SL = γ S + γ L − WSL γ SL = γ S − γ L ⋅ cos θ

(2) (3) (4)

Figure 1. Relationship between surface tensions and contact angle (θ)

In order to obtain a unique contact angle for each three-phase system using this equation, it was assumed that the surface is homogeneous and flat so the surface tension of the interfaces remains constant.9 Merging the above equations (Eqs. 1-4), it is possible to correlate the most important wetting properties: contact angle and surface tension. This equation (Eq. 5) is valid when both phases are non-polar and may be a good estimate when at least one of them is non-polar.

γ L ⋅ (1 + cos θ ) = 2 γ Sd ⋅ γ Ld

(5)

In addition to the contact angle and the surface tension, wettability can also be evaluated using the spreading parameter (SP),12,13,20,23 which represents the difference between the work of adhesion defined in Eq. 2 and the work of cohesion (WC) within the liquid (Eqs. 6-7), defined as the work per unit area required to isothermally split a homogeneous liquid.2

SP = WSL − WC

WC = 2γ L 3


(6) (7)


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 25

From Eqs. 4 and 5, a new equation (Eq. 8) that enables estimating the spreading properties using data from both liquid and surface was derived by Kalin and Polajnar.12,13,20

SP = 2 γ Sd ⋅ γ Ld + 2 γ Snd ⋅ γ Lnd − 2γ L

(8)

The study of wetting properties for ILs (with the exception of imidazolium cation-based ILs) have been poorly investigated,1,4,7-10,21,24-46 even though the value of understanding and controlling wetting has become a key factor in many engineering applications, including lubrication. Due to its growing commercial availability and its good performance as a lubricant additive,47-51 wetting properties such as contact angle, surface tension, SP and PF of seven commercially available

phosphonium cation-based ILs: [P66614][BEHP],

[P66614][(iC8)2PO2], [P66614][NTf2], [P44414][DBS], [P4442][DEP], [P66614][DCA] and [P66614][Cl]

used as

supplied were measured or estimated in order to ensure their feasibility in the field of lubrication.

2. Experimental Details 2.1 ILs In order to carry out this study, all ILs were selected from an available family of these substances, recently and widely used in a number of applications such as extraction solvents, chemical synthesis, electrolytes, corrosion protection and tribology.52 [P66614][(iC8)2PO2], [P66614][BEHP], [P66614][NTf2], [P44414][DBS], [P4442][DEP] and [P66614][DCA] were provided by Ionic Liquid Technologies GmbH (Io-Li-Tec). In addition, [P66614][DCA] was provided by Sigma-Aldrich. Table 1 shows the chemical description of the ILs and Figure 2 depicts their chemical structure. Table 1. Chemical description of ILs used in this work. IUPAC name Trihexyltetradecylphosphonium bis(2,4,4-trimethylpentyl) phosphinate Trihexyltetradecylphosphonium bis(2-ethylhexyl)phosphate Trihexyltetradecylphosphonium bis(trifluoromethylsulfonyl) imide Tributyltetradecylphosphonium dodecylbenzenesulfonate Tributylethylphosphonium Diethylphosphate

Acronym

CAS Number

Purity (%)

Molecular weight

Empirical formula

[P66614][(iC8)2PO2]

465527-59-7

95

773.27

C48H102O2P2

[P66614][BEHP]

1092655-30-5

98

805.29

C48H102O4P2

[P66614][NTf2]

460092-03-9

98

764.01

C34H68F6NO4PS2

[P44414][DBS]

-

95

725.18

C44H85O3PS

[P4442][DEP]

20445-94-7

95

384.47

C18H42O4P2

4


Page 5 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Trihexyltetradecylphosphonium

dicyanamide Trihexyltetradecylphosphonium chloride

[P66614][DCA]

701921-71-3

95

550.91

C34H69PN3

[P66614][Cl]

258864-54-9

95

519.31

C32H68PCl

[P66614][(iC8)2PO2]

[P66614][NTf2]

[P66614][BEHP]

[P44414][DBS]

[P4442][DEP]

[P66614][DCA]

[P66614][Cl]

Figure 2. Chemical structure of the ionic liquids.

A Stabinger SVM3000 rotational Couette viscometer was used to measure viscosity and density (vibrating tube density meter incorporated) according to ASTM D7042 at atmospheric pressure from 10 to 100ºC. The viscosity index (VI) was also automatically calculated5 by the software according to ASTM D2270-04. Experimental density results were quite consistent with those found in the literature. On the other hand, experimental viscosity results showed some differences with values reported in the literature (especially for [P4442][DEP] and [P66614][DCA]), likely related to variations in purity values of the samples tested (Table 2).

5



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 25

Table 2. Comparison between density and viscosity experimental values (Exp.) of the ILs versus values (Ref.) found in the literature. 25,33,44,51,53,54 Ionic liquids Density Short name

ρ (g/cm ) / 20ºC

Exp. [P66614][(iC8)2PO2] [P66614][BEHP] [P66614][NTf2] [P44414][DBS]

Viscosity

3

Ref. 53

0.8867

0.8877

0.9116

51

1.0711 0.9554

0.91

1.070

44

0.9384

25

33

ν (mPa·s) / 25ºC

ν (mPa·s) / 40ºC

Exp.

Exp.

1064 1050 295.9

Ref.

1058

53

1031

51

336.74

4212

44

-

462.5 474.3 130.4 1278

33

171.4

Ref.

447.95 418.4

53

51

151.85

44

124.7

33

ν (mPa·s) / 100ºC

VI

Exp.

Ref.

46.2

42.7953

169

50.8

49.251

181

16.4

-

140

56.5

-

98

[P4442][DEP]

1.0112

1.014

454.8

316.8

14.2

-

83

[P66614][DCA]

0.9010

0.898954

284.4

418.3354

131.6

-

15.1

-

117

[P66614][Cl]

0.8921

0.882625

1875.9

-

631.3

-

38.1

-

97

2.2 Wetting properties In order to carry out a proper thermophysical characterization, several properties related to the wettability of the studied ILs were analyzed. Surface tension of the ILs was measured following Du Noüy’s platinum ring method55 using a KSV Sigma 700 tensiometer (KSV Instruments Ltd., Finland) in a temperature range 2080ºC. The reported values were the average of at least 10 different measurements at each temperature and the standard deviations were less than 0.04 mJ/m2 degrees in each case. According to the methodology described by Tadros et al.,56 contact angles of the ILs were calculated using sessile drops with a KSV CAM 200 goniometer equipped with a micrometer syringe. The drop expanded during the room temperature experiments in order to allow for measurement of dynamic advancing contact angles (θA), recorded from digital images taken at a fixed time interval (first 8 images were taken every half second and the following 30 every 6 seconds). The advancing contact angle was measured on both sides of the drop and this methodology is usually performed to characterize solid surfaces. The reference plane that contains the three-phase line (Figure 1) is located at the interphase, so the contact angle θ is calculated as an optimization parameter, using a Laplacian curve to fit the drop image from the contact point to a certain height of the drop.57 The substrates used for these tests were: AISI 52100 steel discs (machined from annealed rod) with a hardness of 190–210 HV30 and a surface finish (Ra) of 0.0489 µm and 3 alloy nitride coatings (TiN, CrN, ZrN) obtained by Physical Vapor Deposition (PVD) on the same steel discs. Surface finish (Ra) was measured after the deposition process reached the following values: 0.0477 µm for TiN, 0.0474 µm for

6


Page 7 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


CrN and 0.0487 µm for ZrN. All substrates used were cleaned before the wetting tests with acetone in an ultrasonic bath for 2 minutes and dried with air. The reported contact angles were the average of at least ten different points when the steady state was reached and the standard deviations were less than 0.7 degrees in each case.

2.3 Error analysis All experimental equipment used in this research was calibrated before carrying out each experimental series. After the tests, no appreciable deviation compared to standard substances was found; therefore the inherent error was negligible. Moreover, all experimental data reported were the result of several runs in the same experimental conditions, adding the uncertainty as standard deviation to the average value and thus quantifying the magnitude of random error. The propagation of individual uncertainties associated with the measured variables (throughout the different equations used) was determined from the law of propagation of uncertainty, with the general equation shown in Eq. 9. The obtained values were associated with each considered parameter and are reported in Tables 7 and 8. 2

N −1 N  ∂f  2 ∂f ∂f σ ( y) = ∑   σ ( xi ) + 2∑ ∑ COVxi x j i =1  ∂xi  i =1 j =i +1∂xi ∂x j N

2 C

(9)

3. Results and Discussion 3.1 Surface tension Surface tension ( γ ) is a measure of the free energy of a minimum surface area at a boundary layer that separates liquid and vapor phases. Surface tensions of neat phosponium-based ILs are presented in Table 3, adding the standard deviation ( σ ) from at least 10 measurements in each case to the surface tension ( γ ) and temperature (T) average values. The basic thermodynamic relationship applied to the surface of a homogeneous liquid was analyzed using Gibbs free energy definition,25 showing the surface tension linearly decreasing with temperature rise (Eq. 10).

γ = a − b ⋅T

7


(10)


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 25

Table 3. Experimental surface tension data for pure ionic liquids. [P66614][(iC8)2PO2]

[P66614][BEHP]

[P66614][NTf2]

T ± σ (ºC )

γ ± σ (mJ / m2 )

T ± σ (ºC )

γ ± σ (mJ / m2 )

T ± σ (ºC )

γ ± σ (mJ / m2 )

21.105 ± 0.060

28.289 ± 0.006

20.431 ± 0.064

27.525 ± 0.007

21.181 ± 0.128

29.327 ± 0.009

29.916 ± 0.114

27.345 ± 0.028

30.978 ± 0.518

27.021 ± 0.015

30.799 ± 0.266

28.607 ± 0.013

40.012 ± 0.096

26.553 ± 0.009

40.302 ± 0.419

26.353 ± 0.018

39.698 ± 0.049

27.969 ± 0.029

48.557 ± 0.342

25.879 ± 0.017

50.209 ± 0.261

25.640 ± 0.036

50.363 ± 0.337

27.154 ± 0.026

60.426 ± 0.600

24.933 ± 0.067

59.451 ± 0.163

24.945 ± 0.016

59.631 ± 0.115

26.486 ± 0.022

69.983 ± 0.591

24.226 ± 0.068

70.244 ± 0.617

24.109 ± 0.047

69.265 ± 0.150

25.798 ± 0.018

78.734 ± 0.130

23.619 ± 0.015

79.047 ± 0.357

23.530 ± 0.014

78.531 ± 0.044

25.147 ± 0.011

81.562 ± 0.090

23.378 ± 0.012

81.017 ± 0.042

23.355 ± 0.013

78.887 ± 0.036

25.143 ± 0.014

[P44414][DBS]

[P4442][DEP]

[P66614][DCA]

T ± σ (ºC )

γ ± σ (mJ / m2 )

T ± σ (ºC )

γ ± σ (mJ / m2 )

T ± σ (ºC )

γ ± σ (mJ / m2 )

20.672 ± 0.152

29.834 ± 0.015

21.239 ± 0.069

29.433 ± 0.006

20.535 ± 0.195

31.720 ± 0.019

30.726 ± 0.042

29.274 ± 0.030

31.082 ± 0.497

28.471 ± 0.069

29.939 ± 0.277

31.074 ± 0.030

40.105 ± 0.390

28.590 ± 0.025

39.867 ± 0.122

27.863 ± 0.021

39.410 ± 0.229

30.388 ± 0.022

50.989 ± 0.775

28.002 ± 0.045

49.979

± 0.133

27.261 ± 0.026

49.463 ± 0.153

29.657 ± 0.013

59.531 ± 0.299

27.498 ± 0.025

59.729

± 0.095

26.712 ± 0.026

59.067 ± 0.179

28.950 ± 0.028

69.319 ± 0.265

26.890 ± 0.019

78.249 ± 0.256 81.693 ± 0.069

± 0.421 26.020 ± 0.042 69.448 ± 0.209 28.202 ± 0.027 26.308 ± 0.035 78.819 ± 0.404 25.389 ± 0.024 78.014 ± 0.569 27.175 ± 0.053 26.091 ± 0.012 81.711 ± 0.088 25.171 ± 0.017 79.099 ± 0.043 26.938 ± 0.095 69.582

[P66614][Cl]

T ± σ (ºC )

γ ± σ (mJ / m2 )

19.941 ± 0.190

30.122 ± 0.034

30.750 ± 0.267

29.599 ± 0.043

40.443 ± 0.274

28.783 ± 0.043

49.355 ± 0.105

28.072 ± 0.026

59.625 ± 0.088

27.426 ± 0.029

69.388 ± 0.339

26.650 ± 0.034

78.150 ± 0.215

25.818 ± 0.034

8


Page 9 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


81.296 ± 0.067

25.408 ± 0.013

The measured surface tensions (Table 4) were fitted to Eq. 10 where the y-intercept “a” can be read as the surface excess energy (ES), and the slope “b” can be associated with the surface excess entropy (SS).10 In general, the surface tensions of the ILs were much smaller than water and higher than those of most volatile organic solvents.3 With regard to the structure-surface tension relationship, variations in surface tension with ion size changes were observed. Table 4. Surface tension of the ionic liquids.

Ionic liquids

ES (mJ/m2)

SS (mJ/m2.K)

Equation (γ = a – b·T)

R2

[P66614][(iC8)2PO2]

29.788

0.0792

29.788 - 0.0792T

0.9974

[P66614][BEHP]

29.126

0.0707

29.126 - 0.0707T

0.9972

[P66614][NTf2]

30.846

0.0727

30.846 - 0.0727T

0.9997

[P44414][DBS]

31.108

0.0612

31.108 - 0.0612T

0.9991

[P4442][DEP]

30.681

0.0674

30.681 - 0.0674T

0.9952

[P66614][DCA]

33.452

0.0784

33.452 - 0.0784T

0.9912

[P66614][Cl]

31.805

0.0754

31.805 - 0.0757T

0.9939

A decrease in the size of the anion led to an increase in surface tension, explaining the high values shown by [P66614][DCA] and [P66614][Cl] given the small size of their anion.8 Similarly, [P66614][(iC8)2PO2] and [P66614][BEHP] displayed the lowest values for surface tension according to their high cation and anion alkyl chain length. This fact can be explained by the dispersion of the charge10 on a large-sized cation like [P66614]. In addition, the two ILs with smaller cations ([P4442][DEP] and [P44414][DBS]) exhibited intermediate values. Figure 3 plots the surface tension values of the phosphonium ILs studied versus the temperature, using all data available from the experimental measurements.

9



36

[P66614][(iC8)2PO2] [P66614][NTf2] [P4442][DEP] [P66614][Cl]

Surface tension (mN/m)

34

[P66614][BEHP] [P44414][DBS] [P66614][DCA]

32 30 28 26 24 22 0

20

40

60

80

100

Temperature (ºC) Figure 3. Temperature-dependent surface tensions of phosphonium-based ionic liquids.

3.2 Contact angle Figure 4 shows the evolution of the contact angle during 28 different dynamic sessile drop tests (7 ILs on 4 substrates). In order to measure advancing contact angles, the drop formed was grown for about 180 seconds to ensure that the steady state was reached. Analysis of the contact angle evolution of seven ILs on all surfaces studied showed that [P66614][NTf2], [P4442][DEP] and [P66614][DCA] reached the steady state sooner than the others.

90

a)

80 Contact angle (deg)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 25

70 60


[P66614][BEHP] [P44414][DBS] [P66614][DCA]

50 40 30 20 10 0 0

50

100 Time (s)

150

10


200

Page 11 of 25

90

[P66614][(iC8)2PO2]

[P66614][BEHP]

70

[P66614][NTf2] [P4442][DEP]

[P44414][DBS] [P66614][DCA]

60

[P66614][Cl]

b)

Contact angle (deg)

80

50 40 30 20 10 0 0

90

Contact angle (deg)

50

c)

80 70 60

100 Time (s)

[P66614][(iC8)2PO2]

[P66614][BEHP]

[P66614][NTf2]

[P44414][DBS]

[P4442][DEP]

[P66614][DCA]

150

200

[P66614][Cl]

50 40 30 20 10 0 0

50

90

d)

80 Contact angle (deg)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


70 60

100 Time (s)

[P66614][(iC8)2PO2]

[P66614][BEHP]

[P66614][NTf2]

[P44414][DBS]

[P4442][DEP]

[P66614][DCA]

150

200

[P66614][Cl]

50 40 30 20 10 0 0

50

100 Time (s)

150

200

Figure 4. Evolution of the advancing contact angle of the ionic liquids on four different surfaces: a) Steel b) TiN c) CrN d) ZrN

11



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 25

From a surface point of view (Table 5), high surface energy values are favorable for wetting a surface. Moreover, surfaces become more hydrophilic with increasing polar components, i.e. the contact angle of all ILs on TiN (Figure 4b) is expected to be low due to high total and polar component values, provoking better wetting.23 Although similar behavior would be expected for steel (Figure 4a) due to its high polar component, the low value of the total energy negatively affects wettability. In the case of CrN surface (Figure 4c), higher values of contact angle in comparison with the other substrates were observed for liquids [P66614][(iC8)2PO2] and [P66614][BEHP]. This fact occurs because both low values of polar and total components adversely affect wettability. Finally, it is possible to explain the similar trend of contact angle behavior on ZrN and steel surfaces (Figures 4d and 4a, respectively) because of their surface energy intermediate behavior.

Table 5. Surface energy found in the literature20,58 for all substrates used at 293K.

γ S (mJ/m2)

Surfaces

γ Sd

(mJ/m2)

γ Snd

(mJ/m2)

AISI 52100 Steel

43.4

31.2

12.2

ZrN

52.2

48.1

4.1

CrN

44.5

39.1

5.4

TiN

63.2

50.2

13

With the aim of complementing the results shown in Figure 4, Table 6 shows the average steady state contact angle and the standard deviations for the ILs studied on the four surfaces (AISI 52100 Steel, TiN, CrN and ZrN). Table 6. Steady state values of contact angles for the ionic liquids. Short name

Steel

θ ± σ (deg)

TiN

CrN

θ ± σ (deg)

θ ± σ (deg)

ZrN

θ ± σ (deg)

[P66614][(iC8)2PO2]

5.177 ± 0.219

5.787 ± 0.237

13.946 ± 0.076

5.536 ± 0.256

[P66614][BEHP]

4.113 ± 0.243

6.701 ± 0.626

9.982 ± 0.307

4.362 ± 0.286

[P66614][NTf2]

18.158 ± 0.121

12.957 ± 0.224

17.417 ± 0.064

17.460 ± 0.089

[P44414][DBS]

18.345 ± 0.223

20.350 ± 0.134

19.409 ± 0.399

17.742 ± 0.129

[P4442][DEP]

27.850 ± 0.124

5.328 ± 0.220

8.314 ± 0.376

28.740 ± 0.060

[P66614][DCA]

19.390 ± 0.120

19.589 ± 0.027

29.096 ± 0.249

22.689 ± 0.061

[P66614][Cl]

5.299 ± 0.276

5.848 ± 0.357

16.182 ± 0.107

17.510 ± 0.170

Analyzing the obtained results for the most hydrophobic surface used in this work (ZrN), [P66614][(iC8)2PO2] and [P66614][BEHP] showed the lowest contact angle values whereas [P4442][DEP] and [P66614][DCA] had the 12


Page 13 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


highest ones. In addition, [P66614][NTf2], [P44414][DBS] and [P66614][Cl] had intermediate contact angles. However, comparing these values with those reported in the literature is not possible due to the absence of data on the same surfaces. Changes in drop volume, type of needle, measuring software, analysis lab, etc., can affect the results obtained.59 Since all surfaces are characterized by time-dependent contact angles, this property does not contain enough information about the solid-liquid interaction resulting in the inability to define the wetting properties.12 Therefore, additional parameters are recommended in order to improve the understanding and explanation of wettability.

3.3 Polarity fraction and SP From a lubrication point of view, the use of ILs as an additive to base oils is limited by their solubility. Therefore, the estimation of polarity related parameters of the ILs, like polarity fraction, can be useful in order to predict the solubility of ILs in base oils. In order to obtain this parameter, both components of the surface tension (polar and dispersive) were calculated. The dispersive component of the surface tension (γ L ) was d

obtained from data of the seven ILs measured on the ZrN surface (Table 5). The negligible polar

(γ Snd )

component of the surface energy allows for using Eq. 5 or OWRK60 (Owens–Wendt–Rabel–Kaelble) method. The polar or non-dispersive component of surface tension was determined using the Fowkes22 method (Eq. 1). The polarity fraction (PF) is defined as the ratio between the non-dispersive or polar component (γ L ) and nd

the total surface tension (γ L ) . Table 7 summarizes the results obtained applying Eq. 1 and Eq. 5 for the ILs used in this study, while using Eq. 9 to obtain the combined uncertainty associated with each one of these calculated parameters. As expected, ILs with large cation and anion alkyl chains ([P66614][(iC8)2PO2] and [P66614][BEHP]) had the lowest non-dispersive component for surface tension. In addition, the polarity fraction seemed to be more affected by the cation type according to the highest value obtained for [P4442][DEP], whereas the others containing similar cations showed closer PF values. This trend may be associated with the length of both cation and anion alkyl chains, which is inversely proportional to the non-dispersive (polar) component of surface tension.

13



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 25

Table 7. Polarity of the ionic liquids at 293K. ZrN Ionic liquids

d 2 nd 2 γ L ± σ (mJ / m 2 ) γ L ± σ C (mJ / m ) γ L ± σ C (mJ / m )

PF ± σ C

[P66614][BEHP]

28.289 ± 0.006 27.525 ± 0.007

16.560 ± 0.410 15.705 ± 0.342

11.729 ± 0.410 11.820 ± 0.342

0.415 ± 0.014 0.429 ± 0.012

[P66614][NTf2]

29.327 ± 0.009

17.067 ± 0.467

12.260 ± 0.467

0.418 ± 0.016

[P44414][DBS]

29.834 ± 0.015

17.635 ± 0.710

12.199 ± 0.710

0.409 ± 0.024

[P4442][DEP]

29.433 ± 0.006

15.860 ± 0.488

13.573 ± 0.488

[P66614][DCA]

31.720 ± 0.019

19.331 ± 0.474

12.389 ± 0.474

0.461 ± 0.017 0.391 ± 0.015

[P66614][Cl]

30.122 ± 0.034

18.000 ± 0.943

12.122 ± 0.943

0.402 ± 0.031

[P66614][(iC8)2PO2]

These results explain the behavior of [P66614][NTf2], [P4442][DEP] and [P66614][DCA] seen in Figure 4. These three ILs reached the steady state earlier than the other lubricants due to the higher obtained polar components for surface tension (γ L ) . Although the polarity fractions were between 0.39 and 0.46, when compared with nd

values for traditional polar liquids like water (0.70) and glycerol (0.47), the ILs used in this work can be considered as moderately polar.10 Due to the similarity in the polarity fraction values, no conclusions can be made about the solubility of these ILs in base oils. The nature of spreading is manifested in two completely opposite behaviors: spreading-wetting (time dependent contact angle and positive SP) or adhesion-wetting (constant contact angle, negative SP, no cases in this study). A negative value for the SP means that cohesion work between molecules within the ILs is greater than on the solid–liquid interface.12-13,20 Therefore, lower values of SP indicate that a liquid will spread less easily over the surface. However, it is true that a time-dependent contact angle has a positive SP, which occurred in all 28 IL-substrate combinations studied in this work (Table 8 and Figure 5), making the TiN surface much better than the others from a wetting point of view.

14


Page 15 of 25

Table 8. Spreading parameter uncertainty. ZrN

CrN

Steel

TiN

SP ± σ C

SP ± σ C

SP ± σ C

SP ± σ C

[P66614][BEHP]

13.737 ± 0.740 13.843 ± 0.632

10.231 ± 0.689 10.490 ± 0.588

12.807 ± 0.701 13.239 ± 0.595

25.783 ± 0.834 25.899 ± 0.709

[P66614][NTf2]

12.829 ± 0.829

9.284 ± 0.771

11.957 ± 0.784

25.136 ± 0.934

[P44414][DBS]

12.725 ± 1.244

9.082 ± 1.159

11.644 ± 1.182

25.025 ± 1.405

[P4442][DEP]

11.294 ± 0.891

8.061 ± 0.825

11.360 ± 0.826

24.134 ± 0.990

[P66614][DCA]

11.800 ± 0.796

7.903 ± 0.744

10.265 ± 0.765

24.244 ± 0.905

[P66614][Cl]

12.704 ± 1.638

8.995 ± 1.528

11.474 ± 1.563

24.982 ± 1.855

Ionic liquids

[P66614][(iC8)2PO2]

Analyzing the results obtained, it is possible to discern a trend for all surfaces studied: [P66614][(iC8)2PO2] and [P66614][BEHP] had the highest values, thus having the best wettability on hydrophobic surfaces. Furthermore, the differences between ILs were more noticeable in the most hydrophobic surfaces (CrN, ZrN), thus making a comparison more difficult for the less hydrophobic one (TiN) because the values were very close and the error was in the same magnitude order as the differences between SP values.

30 25

SP (mJ/m2)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60



[P66614][BEHP] [P44414][DBS] [P66614][DCA]

20 15 10 5 0 ZrN

CrN

Steel

Figure 5. Spreading parameter of the ionic liquids.

15


TiN


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 25

The wetting parameters studied above are very important whenever a solid–liquid interface is present, which usually occurs in different applications.12,20 Although this scenario is not usually encountered in tribology, the study of wetting could be useful in order to properly design tribological contacts.13 The tribological behavior of the same phosphonium-based ILs has been tested in a previous work.5 [P4442][DEP] presented the worst wetting properties on the steel surface (contact angle around 28º, ES=31.11mJ/m2, SP=11.4 and 0.46 of polarity fraction), but the reactivity of the phosphate anion provided better friction reduction for this IL (CoF=0.06) in comparison with the other four ILs (CoF>0.07). Despite the fact that no critical relationship between wetting behavior and tribological performance with these specific ILs was found after making the comparison, wettability is desired (SP>0) in order to achieve proper lubrication.

4. Conclusions From the study of the wetting properties of seven phosphonium-based ILs: [P66614][(iC8)2PO2], [P66614][BEHP], [P66614][NTf2], [P44414][DBS], [P4442][DEP], [P66614][DCA] and [P66614][Cl], on four different surfaces (AISI 52100 steel and three PVD coatings: CrN, TiN, ZrN) some conclusions can be drawn: •

[P66614][DCA],

[P44414][DBS],

and

[P66614][Cl]

showed

higher

surface

tension

values

while

[P66614][(iC8)2PO2] and [P66614][BEHP] exhibited lower ones. The difference between the lowest and the highest values was about 13%. Increasing alkyl chain length and anion size causes a dispersion of the charge and the surface tension values should decrease. •

Steel and ZrN surfaces exhibited the expected trend on hydrophobic surfaces: ILs with the lowest surface tensions led to the lowest contact angles. In addition, a drop of contact angle values around 85% between [P4442][DEP] and [P66614][BEHP] was achieved on the two surfaces mentioned above.

•

PF behavior of all ILs studied were in a 15% narrow range (0.39-0.46) between [P66614][DCA] and [P4442][DEP]. Although these values were much lower than the value for water (0.7), these phosphoniumbased ILs can be considered as moderately polar.

•

The SP values of all ILs on TiN surface were two times higher than the values obtained for steel and ZrN ones, and 2.5 times higher than CrN surface. These results showed that TiN coating displays the best wettability with these ILs. In addition, the SP results were in agreement with the ones obtained for contact angle and surface tension. Therefore, [P66614][(iC8)2PO2] and [P66614][BEHP] showed the highest SP values

16


Page 17 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


besides the lowest contact angle and surface tension data. All ILs ‘wet’ the surfaces (SP>0) and differences between the highest and lowest values of this parameter for each surface ranged from about 7% for TiN to almost 25% for CrN. Finally, this parameter could be helpful for understanding the wetting behavior of ILs on these surfaces, especially due to the spreading-wetting behavior found in this research.

Associated Content Supporting Information The Supporting Information is available free of charge on the ACS Publications website. Previous works on wettability of ionic liquids (Table S1); Images during the advancement of sessile drop on the steel and coated surfaces (Table S2).

Acknowledgments The authors would like to thank the Ministry of Economy and Competitiveness (Spain) and FICYT (Foundation for the Promotion in Asturias of the Applied Scientific Research and Technology) for supporting the research projects STARLUBE (DPI2013-48348-C2-1-R) and GRUPIN14-023, respectively, under which this research was developed. The Emulsions and Interfacial Phenomena research group from University of Oviedo, as well as Professors Celestino Ordóñez Galán and Manuel Montenegro Hermida are also acknowledged.

Nomenclature θ

Contact angle

σ

Standard deviation

σc

Combined uncertainty

COV

γ d γ d = γ Ld = γ LV nd γ nd = γ Lnd = γ LV

deg deg or mJ/m2 mJ/m2 or -

Covariance

-

Surface tension

mJ/m2

Dispersive component of surface tension

mJ/m2

Polar component of surface tension

mJ/m2

17



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

WSL

Work of adhesion (solid-liquid interface)

mJ/m2

WC

Work of cohesion (liquid)

mJ/m2

Total surface energy

mJ/m2

γ Sd

Dispersive component of surface energy

mJ/m2

γ Snd

Polar component of surface energy

mJ/m2

γ SL

Solid-liquid interfacial tension

mJ/m2

γ L = γ LV

Vapor-liquid interfacial tension

mJ/m2

ES

Surface excess energy

mJ/m2

SS

Surface excess entropy

mJ/m2.K

SP

Spreading parameter

PF

Polarity fraction

-

Friction coefficient

-

γ S = γ SV

CoF

mJ/m2

References (1) Castejón, H. J.; Wynn, T. J.; Marcin, Z. M. Wetting and Tribological Properties of Ionic Liquids. J. Phys. Chem. 2014, 118, 3661. (2) Delcheva, I.; Ralston, J.; Beattie, D. A.; Krasowska, M. Static and Dynamic Wetting Behaviour of Ionic Liquids. Adv. Colloid Interface Sci. 2014, 222, 162. (3) Zhang, X.; Huo, F.; Liu, X.; Dong, K.; He, H.; Yao, X.; Zhang, S. Influence of Microstructure and Interaction on Viscosity of Ionic Liquids. Ind. Eng. Chem. Res. 2015, 54 (13), 3505. (4) Carrera, G. V. S. M.; Afonso, C. a M.; Branco, L. C. Interfacial Properties, Densities, and Contact Angles of Task Specific Ionic Liquids. J. Chem. Eng. Data. 2010, 55 (2), 609. (5) Hernández Battez, A.; Bartolomé, M.; Blanco, D.; Viesca, J. L.; Fernández-González, A.; González, R. Phosphonium Cation-Based Ionic Liquids as Neat Lubricants: Physicochemical and Tribological Performance. Tribol. Int. 2016, 95, 118. 18


Page 18 of 25

Page 19 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


(6) Alcalde, R.; García, G.; Atilhan, M.; Aparicio, S. Systematic Study on the Viscosity of Ionic Liquids: Measurement and Prediction. Ind. Eng. Chem. Res. 2015, 54, 10918. (7) Shirota, H.; Mandai, T.; Fukazawa, H.; Kato, T. Comparison between Dicationic and Monocationic Ionic Liquids: Liquid Density, Thermal Properties, Surface Tension, and Shear Viscosity. J. Chem. Eng. Data. 2011, 56 (5), 2453. (8) Freire, M. G.; Carvalho, P. J.; Fernandes, A. M.; Marrucho, I. M.; Queimada, A. J.; Coutinho, J. A. P. Surface Tensions of Imidazolium Based Ionic Liquids: Anion, Cation, Temperature and Water Effect. J. Colloid Interface Sci. 2007, 314 (2), 621. (9) Poleski, M.; Luczak, J.; Aranowski, R.; Jungnickel, C. Wetting of Surfaces with Ionic Liquids. Physicochem. Probl. Miner. Process. 2013, 49 (1), 277. (10) Restolho, J.; Mata, J. L.; Saramago, B. On the Interfacial Behavior of Ionic Liquids: Surface Tensions and Contact Angles. J. Colloid Interface Sci. 2009, 340 (1), 82. (11) Matos, M.; Lobo, A.; Benito, J. M.; Coca, J.; Pazos, C. Extending the Useful Life of Metalworking Fluids in a Copper Wire Drawing Industry by Monitoring Their Functional Properties. Tribol. Trans. 2012, 55 (5), 685. (12) Kalin, M.; Polajnar, M. The Correlation between the Surface Energy, the Contact Angle and the Spreading Parameter, and Their Relevance for the Wetting Behaviour of DLC with Lubricating Oils. Tribol. Int. 2013, 66, 225. (13) Kalin, M.; Polajnar, M. The Effect of Wetting and Surface Energy on the Friction and Slip in OilLubricated Contacts. Tribol. Lett. 2013, 52 (2), 185. (14) Hernández Battez, A.; González, R.; Viesca, J. L.; Fernández-González, A.; Hadfield, M. Lubrication

of

PVD

Coatings

with

Ethyl-Dimethyl-2-Methoxyethylammonium

Tris(pentafluoroethyl)trifluorophosphate. Tribol. Int. 2013, 58, 71. (15) González, R.; Hernández Battez, A.; Blanco, D.; Viesca, J. L.; Fernández-González, A. Lubrication of

TiN,

CrN

and

DLC

PVD

Coatings

with

1-Butyl-1-

Methylpyrrolidinium

Tris(pentafluoroethyl)trifluorophosphate. Tribol. Lett. 2010, 40 (2), 269. (16) Blanco, D.; Battez, A. H.; Viesca, J. L.; González, R.; Fernández-González, A. CrN

Coating

with

Lubrication of

Ethyl-Dimethyl-2-Methoxyethylammonium

19



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Tris(pentafluoroethyl)trifluorophosphate Ionic Liquid as Additive to PAO 6. Tribol. Lett. 2011, 41 (1), 295. (17) Blanco, D.; González, R.; Hernández Battez, A.; Viesca, J. L.; Fernández-Gonzlez, A. Use of EthylDimethyl-2-Methoxyethylammonium Tris(pentafluoroethyl) Trifluorophosphate as Base Oil Additive in the Lubrication of TiN PVD Coating. Tribol. Int. 2011, 44 (5), 645. (18) González, R.; Battez, A. H.; Viesca, J. L.; Higuera-Garrido, A.; Fernández-González, A. Lubrication of DLC Coatings with Two Tris(pentafluoroethyl)trifluorophosphate Anion-Based Ionic Liquids. Tribol. Trans. 2013, 56 (5), 887. (19) Carlsson, P.; Olsson, M. PVD Coatings for Sheet Metal Forming Processes—a Tribological Evaluation. Surf. Coatings Technol. 2006, 200 (14-15), 4654. (20) Kalin, M.; Polajnar, M. The Wetting of Steel, DLC Coatings, Ceramics and Polymers with Oils and Water: The Importance and Correlations of Surface Energy, Surface Tension, Contact Angle and Spreading. Appl. Surf. Sci. 2014, 293, 97. (21) Batchelor, T.; Cunder, J.; Fadeev, A. Y. Wetting Study of Imidazolium Ionic Liquids. J. Colloid Interface Sci. 2009, 330 (2), 415. (22) Fowkes, F. M. Attractive Forces at Interfaces. Ind. Eng. Chem. 1964, 56 (12), 40. (23) Lugscheider, E.; Bobzin, K. The Influence on Surface Free Energy of PVD-Coatings. Surf. Coatings Technol. 2001, 142-144, 755. (24) Sedev, R. Surface Tension, Interfacial Tension and Contact Angles of Ionic Liquids. Curr. Opin. Colloid Interface Sci. 2011, 16 (4), 310. (25) Kilaru, P.; Baker, G. A.; Scovazzo, P. Density and Surface Tension Measurements of Imidazolium-, Quaternary Phosphonium-, and Ammonium-Based Room-Temperature Ionic Liquids: Data and Correlations. J. Chem. Eng. Data. 2007, 52 (6), 2306. (26) Tiago, G.; Restolho, J.; Forte, A.; Colaço, R.; Branco, L. C.; Saramago, B. Novel Ionic Liquids for Interfacial and Tribological Applications. Colloids Surfaces A Physicochem. Eng. Asp. 2015, 472, 1. (27) Restolho, J.; Mata, J. L.; Saramago, B. Choline Based Ionic Liquids: Interfacial Properties of RTILs with Strong Hydrogen Bonding. Fluid Phase Equilib. 2012, 322-323, 142.

20


Page 20 of 25

Page 21 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


(28) Espinosa, T.; Sanes, J.; Jiménez, A. E.; Bermúdez, M. D. Surface Interactions, Corrosion Processes and Lubricating Performance of Protic and Aprotic Ionic Liquids with OFHC Copper. Appl. Surf. Sci. 2013, 273, 578. (29) Tariq, M.; Freire, M. G.; Saramago, B.; Coutinho, J. A. P.; Lopes, J. N. C.; Rebelo, L. P. N. Surface Tension of Ionic Liquids and Ionic Liquid Solutions. Chem. Soc. Rev. 2012, 41 (2), 829. (30) Almeida, H. F. D.; Carvalho, P. J.; Kurnia, K. A.; Lopes-da-Silva, J. A.; Coutinho, J. A. P.; Freire, M. G. Surface Tensions of Ionic Liquids: Non-Regular Trend along the Number of Cyano Groups. Fluid Phase Equilib. 2016, 409, 458. (31) Pereira, M. M.; Kurnia, K. A.; Sousa, F. L.; Silva, N. J. O.; Lopes-da-Silva, J. A.; Coutinho, J. A. P.; Freire, M. G. Contact Angles and Wettability of Ionic Liquids on Polar and Non-Polar Surfaces. Phys. Chem. Chem. Phys. 2015, 17 (47), 31653. (32) Koller, T. M.; Rausch, M. H.; Pohako-esko, K.; Wasserscheid, P.; Fro, A. P. Surface Tension of Tricyanomethanide- and Tetracyanoborate-Based Imidazolium Ionic Liquids by Using the Pendant Drop Method. J. Chem. Eng. Data. 2015, 60 (9), 2665−2673. (33) Bhattacharjee, A.; Lopes-da-Silva, J. A.; Freire, M. G.; Coutinho, J. A. P.; Carvalho, P. J. Thermophysical Properties of Phosphonium-Based Ionic Liquids. Fluid Phase Equilib. 2015, 400, 103. (34) Shah, S. N.; Lethesh, K. C.; Mutalib, M. I. A.; Pilus, R. B. M. Evaluation of Thermophysical Properties of Imidazolium-Based Phenolate Ionic Liquids. Ind. Eng. Chem. Res. 2015, 54 (14), 3697. (35) Bhattacharjee, A.; Luis, A.; Santos, J. H.; Lopes-da-Silva, J. A.; Freire, M. G.; Carvalho, P. J.; Coutinho, J. A. P. Thermophysical Properties of Sulfonium- and Ammonium-Based Ionic Liquids. Fluid Phase Equilib. 2014, 381, 36. (36) Bhattacharjee, A.; Carvalho, P. J.; Coutinho, J. A. P. The Effect of the Cation Aromaticity upon the Thermophysical Properties of Piperidinium- and Pyridinium-Based Ionic Liquids. Fluid Phase Equilib. 2014, 375, 80. (37) Almeida, H. F. D.; Freire, M. G.; Fernandes, A. M.; Lopes-da-Silva, J. A. J. A.; Morgado, P.; Shimizu, K.; Filipe, E. J. M.; Canongia Lopes, J. N.; Santos, L. M. N. B. F.; Coutinho, J. A. P.

21



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Cation Alkyl Side Chain Length and Symmetry Effects on the Surface Tension of Ionic Liquids. Langmuir. 2014, 30 (22), 6408. (38) Ghatee, M. H.; Bahrami, M.; Khanjari, N. Measurement and Study of Density, Surface Tension, and Viscosity of Quaternary Ammonium-Based Ionic Liquids ([N222(n )]Tf2N). J. Chem. Thermodyn. 2013, 65, 42. (39) Bittner, B.; Wrobel, R. J.; Milchert, E. Physical Properties of Pyridinium Ionic Liquids. J. Chem. Thermodyn. 2012, 55, 159. (40) Almeida, H. F. D.; Passos, H.; Lopes-Da-Silva, J. A.; Fernandes, A. M.; Freire, M. G.; Coutinho, J. A. P. Thermophysical Properties of Five Acetate-Based Ionic Liquids. J. Chem. Eng. Data. 2012, 57 (11), 3005. (41) Capelo, S. B.; Méndez-Morales, T.; Carrete, J.; López Lago, E.; Vila, J.; Cabeza, O.; Rodríguez, J. R.; Turmine, M.; Varela, L. M. Effect of Temperature and Cationic Chain Length on the Physical Properties of Ammonium Nitrate-Based Protic Ionic Liquids. J. Phys. Chem. B. 2012, 116 (36), 11302. (42) Xu, A.; Wang, J.; Zhang, Y.; Chen, Q. Effect of Alkyl Chain Length in Anions on Thermodynamic and Surface Properties of 1-Butyl-3-Methylimidazolium Carboxylate Ionic Liquids. Ind. Eng. Chem. Res. 2012, 51 (8), 3458. (43) Almeida, H. F. D.; Lopes-Da-Silva, J. A.; Freire, M. G.; Coutinho, J. A. P. Surface Tension and Refractive Index of Pure and Water-Saturated Tetradecyltrihexylphosphonium-Based Ionic Liquids. J. Chem. Thermodyn. 2013, 57, 372. (44) Neves, C. M. S. S.; Carvalho, P. J.; Freire, M. G.; Coutinho, J. A. P. Thermophysical Properties of Pure and Water-Saturated Tetradecyltrihexylphosphonium-Based Ionic Liquids. J. Chem. Thermodyn. 2011, 43 (6), 948. (45) Tong, J.; Yang, H.X.; Liu, R.J.; Li, C.; Xia, L.X.; Yang, J.Z. Determination of the Enthalpy of Vaporization and Prediction of Surface Tension for Ionic Liquid 1-Alkyl-3-methylimidazolium Propionate [Cnmim][Pro](n =4,5,6). J Phys Chem 2014;118:12972−78.

22


Page 22 of 25

Page 23 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


(46) Fang, D.W; Yan, Q.; Li, D.; Xia, L.X.; Zang, S.L. Estimation of physicochemical properties of 1alkyl-3-methylimidazolium

glutamate.

J

Chem

Thermodyn

2014;79:12–18.

doi:10.1016/j.jct.2014.06.022. (47) Somers, A. E.; Khemchandani, B.; Howlett, P. C.; Sun, J.; Macfarlane, D. R.; Forsyth, M. Ionic Liquids as Antiwear Additives in Base Oils: Influence of Structure on Miscibility and Antiwear Performance for Steel on Aluminum. ACS Appl. Mater. Interfaces. 2013, 5 (22), 11544. (48) Qu, J.; Bansal, D. G.; Yu, B.; Howe, J. Y.; Luo, H.; Dai, S.; Li, H.; Blau, P. J.; Bunting, B. G.; Mordukhovich, G.; et al. Antiwear Performance and Mechanism of an Oil-Miscible Ionic Liquid as a Lubricant Additive. ACS Appl. Mater. Interfaces. 2012, 4 (2), 997. (49) Yu, B.; Bansal, D. G.; Qu, J.; Sun, X.; Luo, H.; Dai, S.; Blau, P. J.; Bunting, B. G.; Mordukhovich, G.; Smolenski, D. J. Oil-Miscible and Non-Corrosive Phosphonium-Based Ionic Liquids as Candidate Lubricant Additives. Wear, 2012, 289, 58. (50) Barnhill, W. C.; Qu, J.; Luo, H.; Meyer, H. M.; Ma, C.; Chi, M.; Papke, B. L. PhosphoniumOrganophosphate Ionic Liquids as Lubricant Additives: Effects of Cation Structure on Physicochemical and Tribological Characteristics. ACS Appl. Mater. Interfaces. 2014, 6 (24), 22585. (51) Qu, J.; Luo, H.; Chi, M.; Ma, C.; Blau, P. J.; Dai, S.; Viola, M. B. Comparison of an Oil-Miscible Ionic Liquid and ZDDP as a Lubricant Anti-Wear Additive. Tribol. Int. 2014, 71, 88. (52) Fraser, K. J.; MacFarlane, D. R. Phosphonium-Based Ionic Liquids: An Overview. Aust. J. Chem. 2009, 62 (4), 309. (53) Blahušiak, M.; Schlosser, Š. Physical Properties of Phosphonium Ionic Liquid and Its Mixtures with Dodecane and Water. J. Chem. Thermodyn. 2014, 72, 54. (54) Pereiro, A.B.; Veiga, H.I.M.; Esperança, J.M.S.S.; Rodríguez, A. Effect of temperature on the physical

properties

of

two

ionic

liquids.

J

Chem

Thermodyn

2009;41:1419–23.

doi:10.1016/j.jct.2009.06.020. (55) Cambiella, A.; Benito, J. M.; Pazos, C.; Coca, J.; Hernández, A.; Fernández, J. E. Formulation of Emulsifiable Cutting Fluids and Extreme Pressure Behaviour. J. Mater. Process. Technol. 2007, 184 (1-3), 139.

23



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(56) Tadros, T. F., Vincent, B. Liquid/Liquid Interfaces. Encyclopedia of Emulsion Technology Vol.1; Marcel Dekker Inc.: New York, 1983. (57) Cabezas, M. G.; Bateni, A.; Montanero, J. M.; Neumann, A. W. Determination of Surface Tension and Contact Angle from the Shapes of Axisymmetric Fluid Interfaces without Use of Apex Coordinates. Langmuir. 2006, 22 (24), 10053. (58) Sun, C.-C.; Lee, S.-C.; Hwang, W.-C.; Hwang, J.-S.; Tang, I.-T.; Fu, Y.-S. Surface Free Energy of Alloy Nitride Coatings Deposited Using Closed Field Unbalanced Magnetron Sputter Ion Plating. Mater. Trans. 2006, 47 (10), 2533. (59) Cwikel, D.; Zhao, Q.; Liu, C.; Su, X.; Marmur, A. Comparing Contact Angle Measurements and Surface Tension Assessments of Solid Surfaces. Langmuir. 2010, 26 (19), 15289. (60) Owens, D. K.; Wendt, R. C. Estimation of the Surface Free Energy of Polymers. J. Appl. Polym. Sci. 1969, 13, 1741.

24


Page 24 of 25

Page 25 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


For Table of Contents Only

25