Efficient Toughening of Epoxy–Anhydride Thermosets with a Biobased

Oct 24, 2016 - In this article, an approach to toughen epoxy resin with tannic acid, a common polyphenolic compound extracted from plants and microorg...
0 downloads 6 Views 1MB Size
Subscriber access provided by University of Idaho Library

Article

Efficient toughening of epoxy-anhydride thermosets with a bio-based tannic acid derivative Xiaoma Fei, Wei Wei, Fangqiao Zhao, Ye Zhu, Jing Luo, Mingqing Chen, and Xiaoya Liu ACS Sustainable Chem. Eng., Just Accepted Manuscript • DOI: 10.1021/ acssuschemeng.6b01967 • Publication Date (Web): 24 Oct 2016 Downloaded from http://pubs.acs.org on October 29, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Sustainable Chemistry & Engineering is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Efficient toughening of epoxy-anhydride thermosets with a bio-based tannic acid derivative Xiaoma Fei, Wei Wei, Fangqiao Zhao, Ye Zhu, Jing Luo, Mingqing Chen and Xiaoya Liu* The Key Laboratory of Food Colloids and Biotechnology, Ministry of Education, School of Chemical and Material Engineering, Jiangnan University, Wuxi, Jiangsu 214122, P. R. China *Correspondence to: Xiaoya Liu (E-mail: [email protected]) ABSTRACT Research thrust to toughen an epoxy resin using bio-based modifiers without trade-offs in its modulus, mechanical strength, and other properties still remains a challenge. In this article, an approach to toughen epoxy resin with tannic acid, a common polyphenolic compound extracted from plants and microorganisms, is presented. First, dodecane functionalized tannic acid (TA-DD) is prepared and subsequently incorporated into epoxy/anhydride curing system. Owing to the modification of long aliphatic chain, TA-DD can induce epoxy matrix yielding phase separation, forming micro-scaled separated phases. In the meantime, the terminal hydroxyl groups of TA-DD can participate in the curing process, which offers a good interfacial interaction between TA-DD and epoxy matrix. With such a mechanism, the results show that TA-DD can significantly toughen the epoxy resin without trade-offs in its strength, modulus and Tg. The thermoset with only 0.5 wt% TA-DD reaches a highest impact strength, which is 196% increase of that of neat epoxy. This article opens up the possibility of utilizing the renewable tannic acid as an effective modifier for epoxy resin with good mechanical and thermal properties. KEYWORDS: tannic acid; epoxy toughener; bio-based; hyperbranched 1. Introduction In recent years, the fast depletion of petroleum reserve and increasing

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

environmental problems, in addition to the global political toward the principles of sustainable development, have led to a growing interest in the use of bio-based sustainable feedstock in the synthesis of bio-based chemicals and products. In this context, preparing the partially or full bio-based materials is nowadays a real challenge from both academic and industrial points of view.1-3 Tannic acid (TA) is water-soluble high molecular weight polyphenolic compounds mostly extracted from plants and microorganisms. The chemical formula for the commercial TA is often given as C76H52O46, which corresponds with decagalloyl glucose. (Figure S1) As for the aspect of its chemical structure, its architectural is similar to a hyperbranched aromatic polyester core with abundant reactive terminal phenolic hydroxyl groups. Owing to such a specific structure, TA has been widely used in many applications, such as coatings, adsorption and antibacterial materials, and nanomaterials.4-10 Gogoi et al reported a simple approach to the synthesis of a sustainable and biodegradable waterborne hyperbranched polyurethane (WHPU) using TA as a bio-based component. The synthesized WHPU exhibited pronounced thermal and mechanical performance as well as a potent antioxidant activity and cytocompatibility with erythrocytes. Furthermore, WHPU could be degraded by Pseudomonas aeruginosa. As is said above, TA contains abundant terminal phenolic hydroxyl groups.4 Liu et al reported a series of TA based UV-curable antibacterial resins. The results showed that the antimicrobial effects of TA greatly depended on the content of phenolic hydroxyl groups. The resin with the highest phenolic hydroxyl groups content exhibited the highest antibacterial activity with 5 log reduction.5 Epoxy resin is one of the most important industrial materials with a long history.1 Owing to its outstanding properties, good processability and low cost, epoxy resin is widely used as coatings, adhesives, structural composites and electronic materials. However, its high crosslinking density leads to a relatively low impact resistance, which limits its use in many applications.11-14 Up to now, various modifiers, such as rubber, block copolymer, clay, hyperbranched polymers (HBPs), carbon materials and thermoplastic have been developed to improve the toughness of the epoxy resin.15-22 What should be pointed out is that the key issue for these approaches is to toughen an

ACS Paragon Plus Environment

Page 2 of 22

Page 3 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

epoxy resin without trade-offs in its modulus, mechanical strength, and thermal properties. In addition, developing high efficient toughener especially under a low loading amount is still a big problem. Recently, it has been proved that the incorporation of hyperbranched aromatic polyester toughener into epoxy resin may improve the toughness of epoxy resin by a phase-separated or nonphase-separated mechanism, meanwhile minimizing the deterioration of the Tg and strength.23-26 In this context, TA seems to be an attractive candidate for effective epoxy toughener. We had tried to add TA into epoxy formula without any modification. However, TA is immiscible in epoxy resin, leading to precipitation during curing as a result of intermolecular hydrogen bonds, Van der Waals interactions and π−π stacking of aromatic groups, as seen in ESI (Figure S2). Accordingly, a certain extent of chemical modification of TA is necessary to weaken the intermolecular interaction and improve the miscibility of TA in epoxy matrix. In this work, TA-DD was synthesized by a triphenylphosphine-catalyzed ring-opening reaction between TA and 1,2-epoxydodecane, and subsequently used as an toughener for epoxy/anhydride system. Owing to the chemical modification, TA-DD could easily disperse in epoxy resin and induced epoxy matrix yielding phase separation during the curing process, forming micro-scaled separated phases with good interfacial interaction. The introduction of TA-DD could significantly improve the toughness of cured thermosets with a great increase in impact strength under a very low loading amount, and simultaneously improve the Tg and strength. In addition, other thermal properties and toughening mechanism were also studied.

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

2. Experimental 2.1. Materials TA and 1,2-epoxydodecane were purchased from Aladdin (Shanghai, China). Triphenylphosphine (TPP) was supplied by Hexion Specialty Chemical Management Co., Ltd. (Shanghai, China). All the organic solvents were purchased from Sinopharm Chemical Reagent Co., Ltd. (Shanghai, China). The diglycidyl ether of bisphenol A (DGEBA) with an epoxy equivalent weight of 171-175 g per equivalent was supplied by Kukdo Chemical (Kunshan, China). Methylhexahydrophthalic anhydride (MeHHPA) used as anhydride hardener was supplied by Dow Chemicals. All reagents was used without further purification. 2.2. Synthesis of dodecane functionalized tannic acid (TA-DD) TA (17 g, 0.01 mol), TPP (0.865 g, 1.5 wt% of 1,2-epoxydodecane), 50 mL of butyl acetate were mixed in a 250 mL three-neck round-bottom flask which was equipped with a thermometer, a dropping funnel and a cold-water condenser. The reaction system was moved into an oil bath and heated to 100 oC. Then 22 mL (0.10 mol) of 1,2-epoxydodecane was slowly added into the mixture using a dropping funnel under gentle magnetic stirring. The reaction was kept at 100 ◦C for 48 h under N2 atmosphere. Once the reaction was completed, the solution was washed thrice with petroleum ether to remove the unreacted epoxydodecane. The mixture was then precipitated into water twice. Finally, the product was dried in a vacuum oven at 60 °C for 24 h to give a brown waxy product. 2.3 Preparation of the curing mixtures A desired amount of TA-DD and 50 g of epoxy monomer were added in a one-necked 250 mL flask. The mixture was heated and kept at 90 °C for 12 h with vigorous stirring until the TA-DD was dissolved and the solution became clear. Then MeHHPA and catalyst (ethyl triphenyl phosphonium bromide, 1 wt % of the total weight) were added to the mixture, followed by the degas process. Finally, the mixture was poured into mold. The Samples for thermal and mechanical characterization were cured using the following profile: 80 °C for 1.5 h, 100 °C for 1 h, 120 °C for 1 h, and 140 °C for 2 h. Neat epoxy which contains epoxy resin,

ACS Paragon Plus Environment

Page 4 of 22

Page 5 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

MeHHPA and catalyst was prepared following the same procedure as mentioned above. 2.4 Characterization Fourier transform infrared (FTIR) spectra were obtained using a Thermo Fisher Scientific Nicolet iS50 spectrometer at room temperature in the wavenumber range of 600−4000 cm−1.

13

C NMR was measured using a Bruker Avance 400 MHz

spectrometer equipped with autotunable BBO probe. Dynamic rheological measurements were performed on a TA Instruments Discovery DHR-2 rheometer at room temperature. Calorimetric analyses were carried out on a NETZSCH 204 F1 thermal analyzer. The Samples of ~5 mg in weight were placed in aluminum pans under nitrogen atmosphere. Dynamic mechanical analysis (DMA) was conducted on a TA Instruments DMA Q800 at a heating rate of 3 °C min−1 and a frequency of 1 Hz under an air atmosphere. The tests were carried out using the double cantilever mode. Thermal stability was measured using a METTLER TOLEDO 1100SF thermo gravimetric analyzer (TGA) from 50 to 800 °C at a heating rate of 10 K/min under nitrogen. The tensile strengths of the cured hybrids were characterised by an Instron 1185 test machine according to ISO 527:1993. Un-notched impact strength tests were performed on a Ceast Resil impact tester according to ISO 179:1982. For each composition, at least 5 samples were measured. The fracture surfaces from fracture toughness tests were investigated by a HITACHI S-4800 field-emission scanning electron microscope (FESEM). The samples were coated with gold. Atomic force microscopy (AFM) was performed by a Bruker Multimode 8 (Bruker, Germany) using mapping mode. For sample preparation, the uncured resin was first mixed and casted on a clean mica. Then it was cured in oven as the same procedure as preparing thermoset.

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

3. Results and discussion 3.1. Preparation and characterization of TA-DD

Scheme 1. Synthesis of TA-DD and TA-DD modified epoxy thermoset. TA is water-soluble high molecular weight polyphenolic compounds, mostly extracted from plants and microorganisms. It contains abundant phenolic hydroxyl groups, which could serve as reactive sites and be exploited for the functionalization of TA through various reactions.4-7,27 As we said above, TA is immiscible with epoxy resin and could not be added into epoxy formula without modification. In this work, TA was modified by a TPP-catalyzed ring-opening reaction with 1,2-epoxydodecane, generating dodecyl modified TA (TA-DD). The structure and notation of TA-DD are represented in Scheme 1. The aim of such a strategy is that first, introducing aliphatic chain could weaken the intermolecular interaction between TA, enhancing its miscibility in epoxy resin. Second, long aliphatic chain can induce the phase separation of TA-DD from the epoxy matrix during curing. The separated phase with an adequate size could increase the toughness of the TA-DD modified epoxy thermoset, to a certain extent. Last, TA-DD contains a few unreacted phenolic

ACS Paragon Plus Environment

Page 6 of 22

Page 7 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

hydroxyl groups and hydroxyl groups which generated by ring-opening reaction of epoxy group. These hydroxyl groups could take part in the curing process, thus increase the interface interaction between TA-DD and epoxy matrix.

Figure 1. FT-IR (a) and 13C NMR (b) of TA and TA-DD. The epoxide equivalent (EEW) of the reaction system first increases with the reaction time and then reach a stable EEW about 15000. (Figure S3) So the reactions were carried out for 48 h at 100 oC. The chemical structure of TA-DD was first confirmed by FTIR, and the results are given in Figure 1a. The band in the spectrum of TA at 1720 cm−1 and 1200 cm−1 are ascribed to carbonyl (C=O) and C-O-C groups, respectively. TA shows a broad hydroxyl band in the region of 2500−3500 cm−1, which is attributed to the great hydrogen bonding interaction of phenol groups. After modified with epoxydodecane, this broad band decrease and a new OH peak occurred attributed to the hydroxyl groups generated by the by ring-opening reaction of epoxy group. In the meantime, The peaks at 2960 cm−1 and 2880 cm−1 are observed which are attributed to the stretching of CH3 and CH2 from dodecane, respectively. The structure of TA-DD was further confirmed by NMR spectroscopy. Figure 1b showed the

13

C NMR spectrum of TA-DD with the corresponding assignments. The

core signals can be appreciated as a complex multiplet in the aromatic zone, which is consistent with that of TA (shown in Figure S1). The methylene and methyl signals of the dodecane unit appear at 13.5, 22.4 and 31.8. These above results were indicative of the reaction between TA and epoxydodecane and successful incorporation of dodecane groups to TA. In addition, owing to the modification of dodecane, TA-DD

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

exhibits improved organic compatibility, which can be dissolved in common organic solvents. 3.2. Effects of TA-DD on rheological properties and curing behaviors. Viscosity is very important for the processability of an epoxy resin, so, the rheological behaviors of uncured neat epoxy resin and the epoxy precursors with different TA-DD loadings are shown in Table 1. Typically, when an epoxy resin is toughened by a toughener, its viscosity increases to a great extent. Such a phenomenon is more distinct in the rubber toughen epoxy system. In our case, when TA-DD was added to the formula, all the samples shows similar and relatively low viscosity, although, the viscosity (η) slightly increases with the increase of TA-DD loading. The viscosity at room temperature (shear rate = 1.0 s−1) of sample with 2.0% TA-DD loading is still only 790 mPa s. Which seems to be an excellent candidate for toughening epoxy resin without much affecting the processability of the formulation. Such a good mobility could be explained in the following way: (a) The loading amount of TA-DD is relatively low. (b) It has been reported that hyperbranched toughener usually has a low melt viscosity because of its globular structure, which is favor of maintaining low viscosity. (c) The long terminal aliphatic chain could play a role of an inner lubricant, like a wax, enhancing the mobility.

Figure 2. (a) DSC thermograms of neat epoxy and the TA-DD modified epoxy resins and (b) degree of conversion against temperature of the curing of neat epoxy and the TA-DD modified epoxy resins.

ACS Paragon Plus Environment

Page 8 of 22

Page 9 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

The influence of introducing TA-DD on the curing behaviors of DGEBA/MeHHPA system was also studied. Typically, adding non-reactive toughener into epoxy system will decrease the curing activity because of the increased viscosity. As we said above, the viscosity did not increase a lot. Thus, we would see the curing process would not be much affected. Figure 2a shows the DSC exothermic curves of neat epoxy and epoxy resins with different TA-DD loadings. Data of peak temperature and total enthalpy of curing a listed in Table 1. It can be seen that all the samples showed similar curing behavior and curing enthalpy. However, there is a slight difference should be pointed out, that is the peak temperature (given in Table 1.) shift to a lower temperature after adding TA-DD. This means TA-DD has a positive effect on the curing process. Similar result could also be achieved by the conversion against temperature curve (Figure 2b) where the addition of the TA-DD leads to a slight increase in the conversion at a given temperature. Table 1. Viscosity and DSC results of the neat epoxy and TA-DD modified epoxy resins.

a

Sample

DGEBA : TA-DD (Weight Ratio)

ηa (Pa·S)

Tp (°C)

∆H (J/g)

NEAT

1:0

0.69

148.3

315.1

TA-DD0.25

1:0.05

0.63

TA-DD0.5

1:0.1

0.68

TA-DD1.0

1:0.2

0.72

147.2

314.3

TA-DD2.0

1:0.4

0.79

146.3

303.5

shear rate = 1.0 s-1 at room temperature. These results reveal that TA-DD could slightly accelerative the curing process.

Such an experimental behavior could be explained as following: Anhydrides can react with both epoxide and hydroxyl groups by a complex reaction mechanism. The terminal hydroxyl groups on the TA-DD can react with anhydrides by an esterification, giving rise to ester units and carboxyl groups which can subsequently react with epoxide, forming new ester and hydroxyl. Similar phenomena were also described by

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

other researchers

28-29

. What is more, such a mechanism allows the covalent

incorporation of the TA-DD through hydroxyl groups to the epoxy matrix and leads to a good interface interaction. 3.3. Mechanical properties.

Figure 3. Impact (a) and tensile (b) properties of the neat epoxy and TA-DD modified epoxy resins. It has been reported that hyperbranched tougheners could effectively toughen epoxy resins with a phase separated or an in-suit toughening mechanism.21-24,28-31 The reinforcing and toughening effects of the incorporated TA-DD into system were investigated by impact and tensile test. The results are shown in Figure 3. It can be observed that the impact strength was distinctly improved with the incorporation of TA-DD. Thermoset with 0.5 wt % TA-DD loadings shows the best toughening effect and the impact strength of cured hybrid reaches to 38.8 kJ/m2, which is almost twice higher than that of neat epoxy (13.1 kJ/m2). Such a result shows that TA-DD could effectively toughen DGEBA/MHHPA system. What should be pointed out here is that the loading amount is relatively low. For general hyperbranched polymer toughen epoxy system, like Bolton toughen epoxy system, the loading amount at maximum of impact strength is usually around 10 wt%.30-31 However, in our study, the impact strength is enhanced with a very low loading amount, as low as 0.5%. Such an efficient toughen effect could be attribute to the specific structure of TA-DD with a rigid aromatic core and flexible aliphatic arms, which induce a micro-scaled phase separation during curing, as will be discussed in SEM. In the meantime, the terminal reactive hydroxyl groups offer enough interfacial

ACS Paragon Plus Environment

Page 10 of 22

Page 11 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

interaction. As is reported by other researches that compared with the macro-scaled phase separation, the micro-scaled separated phase is in favour of enhancing modulus and lowing the loading amount.32 In typical epoxy materials, improving toughness is usually accompanied by sacrificing the stiffness. However, tensile test results showed that the tensile strength and Young’s modulus also increased after adding TA-DD. The tensile strength and Young’s modulus of the cured sample with 2.0 wt % TA-DD loadings reachs 73.5 MPa and 2092 MPa respectively, which were 56% increase in tensile strength and 2.5% increase in Young’s modulus with respect to those of neat epoxy (47.1 MPa in tensile strength and 2042 MPa in Young’s modulus). Such increases could be explained by the micro-phase separation and introducing of rigid aromatic structure. Hagg Lobland et al recently reported a definition of brittleness (B) and connected B to many other properties such as sliding wear and impact strength.33-34 B can be calculated according to following equation:

‫=ܤ‬

ଵ ఌ್ ா’

(1)

Where εb is the tensile elongation at break and E’ is the storage modulus as determined by DMA. Here, B of neat epoxy and TA-DD modified epoxy resin were calculated and given in Table 2. It can be seen, TA-DD modified epoxy resin showed lower B than neat epoxy. Which consist with the result of impact strength, meaning TA-DD can efficiently toughen the epoxy resin. All the impact and tensile test indicated that TA-DD could simultaneously improve toughness and stiffness, which could serve as an all purposed toughener.

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

3.4. Dynamic mechanical properties.

Figure 4. Tan δ versus temperature for the neat epoxy and the TA-DD modified epoxy resins. The Dynamic mechanical behaviors of neat and TA-DD modified epoxy were measured to further realize the toughening and reinforcing effects. The results are given in Figure 4 and Table 2. As shown in Table 2, all the TA-DD modified epoxy resin showed higher rubbery plateau modulus (Er), the Er was first increased with increasing TA-DD loadings and then decreased at 2.0% TA-DD loading. According to the theory of rubber elasticity, the Er is proportional to average crosslinking density (ρ) of a cured epoxy network. The crosslinking density could be calculated using the equation: ߩ=

ா௥ ଷோ்

(2)

Where ρ represents the crosslinking density per unit volume (mol cm−3), Er is rubbery modulus (MPa), R is the gas constant, and T is the absolute temperature at Tg + 30 °C.35 The calculated crosslinking density is also given in Table 2. Theoretically, adding TA-DD may reduce the crosslinking density because the plasticizing effect of the long aliphatic chains. However, samples with different TA-DD loadings show higher crosslinking density than neat epoxy. This is presumably due to the presence of internal branching points in TA-DD structure and also the -OH groups outside of

ACS Paragon Plus Environment

Page 12 of 22

Page 13 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

TA-DD could take part in the curing process, which makes the TA-DD as a chemical crosslinking points. Table 2. Thermomechanical properties and brittleness of the neat epoxy and TA-DD modified epoxy resins.

a

Sample

Tga (°C)

T5% (°C)

Erb (MPa)

ρ (10-3 mol/cm3)

B (% Pa/1010)

NEAT

136.8

373

13.9

1.27

1.73

TA-DD0.25

150.6

357

15.4

1.31

1.33

TA-DD0.5

148.4

358

15.8

1.35

1.42

TA-DD1.0

148.1

365

15.9

1.35

1..48

TA-DD2.0

147.5

378

15.1

1.28

1.13

Tg determined using DMA. b Storage modulus at Tg + 30 °C. The Tan δ plot against temperature for all the sample with different TA-DD

loadings are represented in Figure 4. The peak of the tan δ versus temperature curve is considered as Tg. It can be seen, all the TA-DD modified epoxy thermosets showed higher Tg than that of neat epoxy thermoset. As the TA-DD loading increases, the Tg of TA-DD modified epoxy thermosets decrease slightly. Tg was also measured by DSC and the variation of Tg at different TA-DD loadings is similar with the results of DMA. This is an unexpected result, because adding of bio-based toughener will generally decrease the Tg.36-37 Although the long aliphatic chains in TA-DD have a plasticizing effect, the enhanced Tg in this study may could be explained as following: (a) The rigid inner aromatic core as well as the ester group of TA-DD can limit the chain mobility. (b) As is said above, TA-DD contains some unreacted phenolic hydroxyl group and hydroxyl groups generated by the ring-opening reaction of epoxide group. These groups may take part in the curing process and increase the crosslinking density to some degree.38 (c) Owing to the ester and hydroxyl groups, some hydrogen bonds may be formed between TA-DD and other oxygen-containing functional groups from the epoxy matrix.39 As for increase the TA-DD loading, Tg slightly decrease. This may be due to that at low TA-DD loading, the size of TA-DD phase is small, which shows a higher internal cohesion between the epoxy matrix and

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

TA-DD. But at high TA-DD loading, the size of TA-DD phase increase as will be discussed in SEM section. This may lead to a decrease in crosslinking density and enhance the plasticizing effect. Thus the Tg decrease. 3.6. Toughening mechanism. The toughness behavior of neat and TA-DD modified DGEBA/MeHHPA thermosets can be explained in terms of morphology observed by SEM. Figure 5 presents the SEM micrographs of impact fractured surfaces of the thermosets prepared. First of all, the fracture surface of the neat epoxy exhibit a characteristic epoxy fracture-surface morphology, with minimal deformation observed from the smooth surface pattern, which can account for the low impact strength. For the TA-DD modified epoxy thermosets, it can be seen that the spherical domains of the TA-DD were formed and dispersed within the continuous epoxy resin phase, which indicates that phase separation was occurred during curing process. The size of these separation phase is relatively uniform. Uniform distribution of the separation phase throughout the matrix is very important for toughening. It allows the yielding process to operate throughout the matrix.40 On the other hand, the TA-DD phase did not undergo cavitations, which suggested a good adhesion between TA-DD and the epoxy matrix. Such a good interface interaction could efficiently transfer the stress between the TA-DD and epoxy matrix, induce the plastic deformation and crack deflection, which is benefit for toughness.41-42 In addition, the AFM images of the neat epoxy and epoxy resin with 2.0 wt % TA-DD loadings are shown in Figure 6. In the same way as in the SEM images, a micro-phase separation of TA-DD in the epoxy matrix is observed. The size of the TA-DD domains is about 100-200 nm. Such a micro-phase separation is benefit to enhancing the toughness.

ACS Paragon Plus Environment

Page 14 of 22

Page 15 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Figure 5. SEM images of impact fracture surfaces. (a and b) neat epoxy: (c and d) TA-DD modified epoxy resins.

Figure 6. AFM mages of (a) neat epoxy and (b) the TA-DD modified epoxy resins.

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

3.7. Thermogravimetric analysis.

Figure 7. TGA curves of the neat epoxy and TA-DD modified epoxy resins. The thermal stability of the thermosets was studied by TGA. Figure 7 shows the thermogravimetric for the thermosets with different TA-DD loadings and the data are collected in Table 2. As we can see, both neat epoxy and TA-DD modified epoxy show only one degradation stage and without any apparent differences in thermal stability, indicating that a homogenous structure of the matrix is formed and the breakage of bonds in the network structure occurs simultaneously. The only differences in the thermal stability can be observed in the initial degradation temperature (T5%) which is given in Table 1. It can be seen, compared to that of neat epoxy (373 °C), sample with 0.25% TA-DD loading shows a lower onset degradation temperature (357 °C). This is due to the lower thermal stability of ester groups and aliphatic chain, which are more degradable. The T5% of TA-DD modified epoxy increases with further increasing the content of TA-DD. The Sample with 2.0% TA-DD loading shows an initial decomposition temperature at (378 °C) which is a little higher than that of neat epoxy. This fact can be attributed to the high content of aromatic components in TA-DD and the hydroxyl groups of the TA-DD provide miscibility during cure and allow reaction with other network functional groups,

ACS Paragon Plus Environment

Page 16 of 22

Page 17 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

which in turn produces greater adhesion to the matrix and may prevent the elimination of volatile fragments. 4. Conclusion The present study reported an approach to synthesize an efficient epoxy toughener using

TA

as

a

bio-based

triphenylphosphine-catalyzed

feedstock. ring-opening

TA-DD

was

reaction

synthesized between

TA

by

a and

1,2-epoxydodecane. The obtained TA-DD could be easily dispersed in epoxy resin and then was used as a modifier for epoxy/anhydride system. Owing to the chemical modification, TA-DD could induce epoxy matrix yielding phase separation during the curing process, forming micro-scaled separated phases. In the meantime, the terminal hydroxyl groups of TA-DD react with epoxy matrix, which offers a good interfacial interaction. With such a mechanism, TA-DD could efficiently toughen the epoxy resin under a low loading amount. The Results showed the impact strength of the thermoset with 0.5 wt% TA-DD reached to 38.8 kJ/m2, which is almost twice higher than that of neat epoxy (13.1 kJ/m2). What is more, introducing TA-DD into epoxy matrix could simultaneously enhance modulus, mechanical strength, and thermal properties. We believe that this effective toughener coming from the low-cost and renewable tannic acid have considerable potential for epoxy thermosets with high performance.

Supporting Information The

13

C-NMR spectrum of TA; picture of TA modified epoxy thermosets with

different loadings and change in the EEW of the reaction mixture as a function of time for the synthesis of TA-DD. This material is available free of charge via the Internet at http://pubs.acs.org.

Author contributions The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript. *Correspondence to: Xiaoya Liu (E-mail: [email protected])

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

[email protected] (X.F.); [email protected] (W.W); [email protected] (F.Z.); [email protected].(Y.Z.); [email protected] (J.L.);[email protected](M.C.)

Acknowledgement We are grateful for the financial support from the Enterprise-University-Research Prospective Program, Jiangsu Province (BY2013015-08 and BY2015019-08) and MOE & SAFEA for the 111 Project (B13025).

References (1) Auvergne, R.; Caillol, S.; David, G.; Boutevin, B.; Pascault, J. P. Biobased thermosetting epoxy: Present and future. Chem. Rev. 2014, 114, 1082–1115. (2) Raquez, J.; Deléglise, M.; Lacrampe, M.; Krawczak, P. Thermosetting (bio)materials derived from renewable resources: A critical review, Progress in Polymer Science, 2010, 35, 487-509. (3) Ding, C.; Matharu, A. S. Recent developments on biobased curing agents: A review of their preparation and use. ACS Sustain. Chem. Eng. 2014, 2, 2217–2236. (4) Gogoi, S.; Karak, N. Biobased biodegradable waterborne hyperbranched polyurethane as an ecofriendly sustainable material. ACS Sustainable Chem. Eng. 2014, 2, 2730–2738. (5) Liu, R.; Zheng, J. C.; Guo, R. X.; Luo, J.; Yuan, Y.; Liu, X. Y. Synthesis of new biobased antibacterial methacrylates derived from tannic acid and their application in UV-cured coatings. Ind. Eng. Chem. Res. 2014, 53, 10835–10840. (6) Liu, R.; Zhu, J. J.; Luo, J.; Liu, X. Y. Synthesis and application of novel UV-curable hyperbranched methacrylates from renewable natural tannic acid. Prog. Org. Coat. 2014, 77, 30–37. (7) Luo. J.; Lai, J. P.; Zhang, N.; Liu, Y. B.; Liu, R.; Liu, X.Y. Tannic acid induced self-assembly of three-dimensional graphene with good adsorption and antibacterial properties. ACS Sustainable Chem. Eng. 2016, 4, 1404–1413.

ACS Paragon Plus Environment

Page 18 of 22

Page 19 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(8) Shin, M.; Kim, K.; Shim, W.; Yang, J. W.; Lee, H. Tannic acid as a degradable mucoadhesive compound. ACS Biomater. Sci. Eng. 2016, 2, 687–696. (9) Rivero, S.; García, M. A.; Pinotti, A. Crosslinking capacity of tannic acid in plasticized chitosan films. Carbohydr. Polym. 2010, 82, 270–276. (10) Pan, L.; Wang, H.B.; Wu, C. L. M.; Liao, C. B.; Li, L. Tannic-acid-coated polypropylene membrane as a separator for lithium-ion batteries. ACS Appl. Mater. Interfaces. 2015, 7, 16003–16010. (11) Bouer, R. S. In Epoxy Resin Chemistry, American Chemical Society, Washington DC, 1983. (12) Auvergne. R.; Caillol. S.; David. G.; Boutevin. B.; Pascault. J. P. Biobased thermosetting epoxy: Present and future. Chemical Reviews. 2014, 114, 1082-1115. (13) Jin, F.; Li, X.; Park, S. Synthesis and application of epoxy resins: A review. J. Ind. Eng. Chem. 2015. 29. 1-11. (14) Tripathy R., Ojha U., Faust R., Macromolecules. 2011, 44, 6800-6809. (15) Chonkaew, W.; Sombatsompop, N.; Brostow, W. High impact strength and low wear of epoxy modified by a combination of liquid carboxyl terminated poly(butadiene-co-acrylonitrile) rubber and organoclay. Eur. Polym. J. 2013, 49, 1461–1470. (16) Gan, W. J.; Zhan, G. Z.; Wang, M. H.; Yu , Y. F.; Xu, Y. Z.; Li, S. J. Rheological behaviors and structural transitions in a polyethersulfone-modified epoxy system during phase separation. Colloid. Polym. Sci. 2007, 285, 1727−1731. (17) Wang, K.; Chen, L.; Wu, J. S.; Toh, M. L.; He, C. B.; Yee, A. F. Epoxy nanocomposites with highly exfoliated clay:  mechanical properties and fracture mechanisms. Macromolecules. 2005, 38, 788–800. (18) Bibekananda, D.; Karak, N. Ultralow dielectric, high performing hyperbranched epoxy thermosets: synthesis, characterization and property evaluation. RSC Adv. 2015, 5, 35080−35088. (19) Ma, Q.; Luo, J.; Chen, Y. X.; Wei, W.; Liu, R.; Liu, X. Y. Reactive copolymer functionalized graphene sheet for enhanced mechanical and thermal properties of epoxy composites. J. Polym. Sci., Part A: Polym. Chem. 2015, 53, 2776–2785.

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 22

(20) Thompson, Z. J.; Hillmyer, M.; Liu, J.; Sue, H. J.; Dettloff, M. B.; Frank. S. Block copolymer toughened epoxy: Role of cross-link density. Macromolecules, 2009, 42, 2333–2335. (21) Miao, X. P.; Meng, Y.; Lia, X. Y. A novel all-purpose epoxy-terminated hyperbranched polyether sulphone toughener for an epoxy/amine system. Polymer. 2015, 60, 88–95. (22) Wang, R.; Zhuo, D. X.; Weng, Z. X.; Wu, L. X.; Cheng, X. Y.; Zhou, Y.; Wang, J. L.; Xuan, B. W. A novel nanosilica/graphene oxide hybrid and its flame retarding epoxy resin with simultaneously improved mechanical, thermal conductivity, and dielectric properties. J. Mater. Chem. A, 2015, 3, 9826–9836. (23) Liu, D.; Wang, H. M.; Jiang, H. S.; Zhou, D. P. Improving the heat-resistance and toughness performance of phenolic resins by adding a rigid aromatic hyperbranched polyester. J. Appl. Polym. Sci. 2016, 133, 42734. (24) Miao, X. P.; Meng, Y.; Li, X. Y. Epoxide-terminated hyperbranched polyether sulphone as triple enhancement modifier for DGEBA. J. Appl. Polym. Sci. 2015, 132, 41910. (25) Li, T.; Qin, H. J.; Liu, Y.; Zhong, X. H.; Yu, Y. F.; Serra, A. Hyperbranched polyester as additives in filled and unfilled epoxy-novolac systems. Polymer. 2012, 53, 5864–5872. (26) Saha, P.; Chowdhury, S.; Manna, S.; Roy, D.; Adhikari, B.; Thomas, S. New biobased surface treatment to improve strength and durability of bombax ceiba. ACS Sustainable Chem. Eng. 2016, 4, 76-84. (27) Haider, M.; Hubert, P.; Lessard, L. Cure shrinkage characterization and modeling of a polyester resin containing low profile additives. Compos. Part A: Appl. Sci. Manufact. 2007, 38, 994-1009. (28)Fernández-Francos, X.; Rybak, A.; Sekula, R.; Ramis, X.; Serra, A. Modification of epoxy-anhydride thermosets using a hyperbranched poly(ester-amide): I. Kinetic study. Polym Int. 2012, 61, 1710–1725. (29) Foix, D.; Yu, Y. F.; Serra, A.; Ramis, X.; Salla, J. M. Study on the chemical modification

of

epoxy/anhydride

thermosets

using

ACS Paragon Plus Environment

a

hydroxyl

terminated

Page 21 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

hyperbranched polymer. Eur. Polym. J. 2009, 45, 1454–1466. (30) Parzuchowski, P. G.; Kiźlińska, M.; Rokicki, G. New hyperbranched polyether containing cyclic carbonate groups as a toughening agent for epoxy resin. Polymer. 2007, 48, 1857–1865. (31) Tomuta, A.; Ferrando, F.; Serra, A.; Ramis, X. New aromatic–aliphatic hyperbranched polyesters with vinylic end groups of different length as modifiers of epoxy/anhydride thermosets. React. Funct. Polym. 2012, 72, 556–563. (32) Redline, E. M,; Declet-Perez, C,; Bates, F. S,; Francis, L. F. Effect of block copolymer concentration and core composition on toughening epoxies. Polymer. 2014, 55, 4172-4181. (33) Brostow, W.; Hagg Lobland, H. E. Brittleness of materials: Implications for composites and relation to impact strength. J. Mater. Sci. 2010, 45, 242-250. (34) Brostow, W.; Hagg Lobland, H. E.; Khoja, S. Brittleness and toughness of polymers and other materials. Mater. Letters. 2015, 159, 478-480.

(35) Kaji, M.; Nakahara, K.; Endo, T. Synthesis of a bifunctional epoxy monomer containing biphenyl moiety and properties of its cured polymer with phenol novolac. J. Appl. Polym. Sci. 1999, 74, 690-698. (36) Liu, W. S.; Zhou, R.; Goh, H. L. S.; Huang, S.; Lu, X. H. From waste to functional additive: toughening epoxy resin with lignin. ACS Appl. Mater. Interfaces, 2014, 6, 5810–5817. (37) Satheesh, B.; Tshai, K. Y.; Warrior, N. A. Effect of chitosan loading on the morphological, thermal, and mechanical properties of diglycidyl ether of bisphenol A/hexamethylenediamine epoxy system. Journal of Composites, 2014, 8. (38) Oh, J. H.; Jang, J.; Lee, S. H. Curing behavior of tetrafunctional epoxy resin/hyperbranched polymer system. Polymer. 2001, 42, 8339-8347. (39) Yang, J. P.; Chen, Z. K.; Yang, G.; Fu, S. Y.; Ye, L., Simultaneous improvements in the cryogenic tensile strength, ductility and impact strength of epoxy resins by a hyperbranched polymer. Polymer. 2008, 49, 3168-3175. (40) Pearson, R. A.; Yee, A. F. Influence of particle size and particle size distribution

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

on toughening mechanisms in rubber-modified epoxies. J Mater Sci. 1991, 26, 3828-3844. (41) Boogh, L.; Pettersson, B.; Manson, JA. E. Dendritic hyperbranched polymers as tougheners for epoxy resins. Polymer. 1999, 40, 2249-2261. (42) Paweł, G. P.; Magdalena, K.; Gabriel, R. New hyperbranched polyether containing cyclic carbonate groups as a toughening agent for epoxy resin. Polymer. 2007, 48, 1857-1865.

For Table of Contents Use Only

Efficient toughening of epoxy-anhydride thermosets with a bio-based tannic acid derivative Xiaoma Fei, Wei Wei, Fangqiao Zhao, Ye Zhu, Jing Luo, Mingqing Chen and Xiaoya Liu Utilizing the renewable TA as an effective modifier for epoxy resin with high performance is conducive to sustainable development.