Article

Encapsulation of spherical cross-linked phenylalanine ammonia lyase aggregates in mesoporous biosilica Jiandong Cui, Ya Min Zhao, Yuxiao Feng, Tao Lin, Cheng Zhong, Zhilei Tan, and Shiru Jia J. Agric. Food Chem., Just Accepted Manuscript • DOI: 10.1021/acs.jafc.6b05003 • Publication Date (Web): 05 Jan 2017 Downloaded from http://pubs.acs.org on January 5, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Journal of Agricultural and Food Chemistry is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 35

Journal of Agricultural and Food Chemistry

of

spherical

1

Encapsulation

cross-linked

phenylalanine

2

ammonia lyase aggregates in mesoporous biosilica

3

Jiandong Cui1, 2 * Yamin zhao2 1 Yuxiao Feng2 Tao Lin2 Cheng Zhong1

4

1

5

of Science and Technology, No 29, 13th, Avenue, Tianjin Economic and Technological Development

6

Area (TEDA), Tianjin 300457, P R China

7

2

8

Hebei University of Science and Technology, 26 Yuxiang Street, Shijiazhang 050000, P R China

9

*

Zhilei Tan1 Shiru Jia1 *

Key Laboratory of Industrial Fermentation Microbiology, Ministry of Education, Tianjin University

Research Center for Fermentation Engineering of Hebei, College of Bioscience and Bioengineering,

Corresponding authors:

10

Jiandong Cui, E-mail: [email protected], Tel: +86-311-81668486

11

Shiru Jia, E-mail: [email protected], Tel: +86-022-60601598

12 13 14 15 16 17 18 19 20 21 22 23 24

1

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

25

Abstract

26

Cross-linked enzyme aggregates (CLEAs) have recently emerged as a promising method

27

for enzyme immobilization due to its simplicity and low cost. However, a lack of good

28

size and morphological control over the as-prepared CLEAs has limited their practical

29

applications. For example, the prepared CLEAs exhibit amorphous large clusters that

30

would cause significant mass-transfer limitations, which leading to low catalytic

31

efficiency. Here, inspired by biomineralized core–shell structures in nature, we develop a

32

novel mesoporous spherical CLEA with biosilica shell by using phenylalanine ammonia

33

lyase based on CaCO3 microtemplates and biomimetic mineralization. The resultant

34

CLEAs exhibited spherical structure with good monodispersity instead of the amorphous

35

clusters of conventional CLEAs, and showed higher activity than that of conventional

36

CLEAs. Moreover, the thermostability, the tolerance against denaturants, and mechanical

37

stability of the spherical CLEAs with biosilica shell were enhanced significantly

38

compared with conventional CLEAs. Especially, the spherical CLEAs with biosilica

39

shell still retained 70% of its original activity after 13 cycles. Whereas, the conventional

40

CLEAs only retained 35% of its original activity. This approach could be an efficient

41

strategy to improve catalytic properties of CLEAs.

42

Keywords: Biomimetic mineralization; CaCO3 microtemplates; Spherical CLEAs;

43

Immobilization enzyme

44 45

2

ACS Paragon Plus Environment

Page 2 of 35

Page 3 of 35

Journal of Agricultural and Food Chemistry

46

Introduction

47

Currently enzymes are widely used in diverse sectors owing to their ease of production,

48

substrate specificity and selectivity. However, for commercial viability, these biocatalysts

49

display low operational stability and difficulty in recovery, leading to high cost and the

50

contamination of the products.1, 2 Immobilization of enzymes is now providing powerful

51

tools and devices to develop novel alternative strategies for increasing the performance,

52

stability, and activities of enzymes for industrial application.3,4 The improvement of

53

operational stabilization of immobilized enzymes can be due to prevention of subunit

54

dissociation via multisubunit immobilization,5 prevention of aggregation, autolysis or

55

proteolysis by proteases,6 rigidification of the enzyme structure via multipoint covalent

56

attachment7,8 and generation of favorable microenvironments.9 The selectivity

57

improvement via immobilization can be due to alteration of the geometry of the active

58

center via immobilization,7,8 stabilizing enzyme conformation

59

diffusion limitation.11 Among such immobilization methods, carrier-free immobilization

60

has attracted a great deal of attention due to clear advantages: great volumetric

61

productivity, high stability and the low production cost due to the exclusion of an

62

additional carrier.12,13 Especially, cross-linked enzyme aggregates (CLEAs) seem to be a

63

promising method for enzyme immobilization.14,15 The enzyme is immobilized with high

64

stability and high volume activity by cross-linking the physical enzyme aggregates.16,17

65

Compared with free enzymes, CLEAs proved significantly more stable to denaturation

66

by heat, or organic solvents and proteolysis than the corresponding soluble enzyme.18,19

3

ACS Paragon Plus Environment

10

and elimination of

Journal of Agricultural and Food Chemistry

67

Moreover, CLEAs possess high space time yields, volumetric and catalyst

68

productivities.20 However, CLEAs technology has also some disadvantages.21 For

69

example, the CLEAs have wide particle distribution which affects enzyme activity and

70

reaction kinetics. Amorphous large clusters would result in significant mass-transfer

71

limitations, whereas the small particles cannot be filtered or recycled.22,23 Moreover,

72

CLEAs may still be considered too soft for many industrial applications. Therefore, it is

73

important to control the particle size of CLEA and improve their mechanical stability.24,25

74

In order to overcome these problems, CLEAs of papain in commercial macroporous

75

silica gel were prepared, and showed excellent operation stability.26 The formation of

76

CLEAs of phenylalanine ammonia lyase (PAL) from Rhodotorula glutinis into

77

macroporous silica gel exhibited good reusability.27 The magnetic CLEAs of α-amylase

78

were prepared on amino functionalized magnetite nanoparticles, and exhibited excellent

79

thermostability, storage stability and reusability.28 However, the noncatalytic mass of the

80

carrier causes decrease of the volumetric activity and production of the biocatalyst.

81

In the past decades, inorganic materials have been successfully used as hard templates

82

for the synthesis of immobilized enzyme particles with control over internal structure,

83

morphology, and composition.29,30 The most straightforward method towards such

84

assemblies employs inorganic materials as templates such as microporous silica,31

85

ploymer,32 and porous CaCO3.33 Among templates, CaCO3 microspheres have nowadays

86

become one of the most popular decomposable matrices because of easy preparation

87

procedure, low costs, biocompatibility, and mild decomposition conditions.34,35

4

ACS Paragon Plus Environment

Page 4 of 35

Page 5 of 35

Journal of Agricultural and Food Chemistry

88

Moreover, some enzymes have been successfully entrapped into the pores of the CaCO3

89

microspheres by the co-precipitation, infiltration by solvent exchange, and physical

90

adsorption.30,36,37 Although the resulting immobilized enzyme particles by CaCO3

91

templating exhibit regular size and monodispersity, they may still be considered too soft

92

for industrial application.

93

In nature, many living organisms can fabricate silica coatings to survive environmental

94

stresses. This biologically induced, self-assembly process, called biosilicification, is

95

formed in biological environments under mild reaction conditions.38 Generally,

96

biomimetic silica can be produced in vitro by mixing silicic acid with silaffin,39 or

97

synthetic R5 peptide (part of the silaffin repeating unit),40 or even polymers such as

98

poly(lysine)

99

biosilicification have hierarchical structures, multiple morphologies with mesopores, and

100

superior mechanical properties. In the study, inspired from biosilicification, we

101

developed a new method to prepare a mesoporous spherical CLEA with biosilica shell

102

based on CaCO3 microtemplates and biomimetic mineralization. The method mainly

103

consists of a sequential reaction involving preparation of spherical CLEA particles based

104

on porous CaCO3 microtemplate, and controlled self-assembly and subsequent

105

polycondensation of silanes, thus resulting in the formation of biosilica coatings around

106

CLEA particles (Figure 1). It is conceivable that the resultant CLEAs can form regular

107

spherical particles with appropriate size under suitable conditions that would overcome

108

the formation of conventional CLEAs with amorphous clusters. More importantly, the

and

polyallylamine.41 Moreover,

silica

materials

5

ACS Paragon Plus Environment

synthesized

by

Journal of Agricultural and Food Chemistry

Page 6 of 35

109

biosilica shell could afford unprecedented protection from biological, thermal and

110

chemical degradation. In this work, the phenylalanine ammonia-lyase (PAL, EC 4.3.1.24)

111

from recombinant E. coli was selected to explore the validity of this approach. To

112

prevent PAL subunit dissociation, polyethyleneimine(PEI) was used to protect PAL, and

113

promote biomimetic silica formation. In addition, the structure and some properties of

114

prepared spherical CLEAs with biosilica shell were investigated.

115 116

Materials and Methods

117

Chemicals

118

glutaraldehyde and coomassie brilliant blue R-250 were purchased from Sigma

119

Chemical Co. (St Louis, MO, USA). Trypsin (500 U/mg), tetramethoxysilane (TMOS),

120

and polyethyleneimine (PEI, 1.8 kDa) were purchased from International Aladdin

121

Reagent Inc (Shanghai, China), and stored at 4 °C. L-Phenylalanine was obtained from

122

Beijing Chemical Reagent Company (Beijing, China). All of other chemicals were of

123

analytical grade and were purchased from commercial suppliers. The recombinant BL21

124

(DE3) E. coli cells (carrying recombinant expression plasmid pET28a-PAL) was

125

constructed and maintained as 40% (v/v) glycerol stock at -80 °C in Luria-Bertani (LB)

126

medium in our lab.

127

Production and purification of PAL from recombinant E. coli. BL21 (DE3) E. coli

128

with pET28a-PAL was inoculated in 5 mL of LB broth with kanamycin (35 mg/L), and

129

grown at 37 °C on a shaker at 200 rpm for 12 h. Subsequently, 1 mL of culture was

and

microorganism.

Isopropyl-β-D-thiogalactopyranoside

6

ACS Paragon Plus Environment

(IPTG),

Page 7 of 35

Journal of Agricultural and Food Chemistry

130

transferred to a 250 mL Erlenmeyer flask containing 100 mL of LB broth and 100 µL of

131

kanamycin (35 mg/mL). The bacteria were grown at 37 °C in an incubator (200 rpm)

132

until the OD600 reached approx. 0.6 and induced by adding 1 mM IPTG, and incubated at

133

30 °C for 4 h. For recombinant PAL purification, E. coli cells were separated from the

134

culture media by centrifugation at 4 °C. Cells pellets were resuspended in ice-cold lysis

135

buffer (50 mM Tris-HCl, 500 mM NaCl, pH 8.0), and were sonicated until the solution

136

became clear. The lysate was clarified by centrifugation at 4 °C, 15,000 ×g for 20 min.

137

Then, the solution was loaded onto a 5 mL nickel Sepharose 6 Fast Flow column. After

138

the protein was loaded onto the column, the column was washed with 5 column-volumes

139

of washing buffer (50 mM Tris-HCl, 500 mM NaCl, 5 mM imidazole, pH 8.0). The

140

target protein was eluted with a stepwise gradient of 10, 50, 100, and 200 mM imidazole,

141

using two column volumes for each step. Elution fractions of 1 mL were collected and

142

analyzed by SDS-PAGE.

143

Preparation of CaCO3 microtemplates. CaCO3 microtemplates were prepared by a

144

modification of the procedure of Volodkin et al. 33 Briefly, the crystallization process was

145

initiated by rapid mixing of 0.33 M CaCl2 and 0.33 M Na2CO3 solutions (including 30%

146

ethylene glycol). The mixture was intensively agitated at 500 rpm with a magnetic stirrer

147

for 2 h. After centrifugation, the white precipitate of CaCO3 particles was washed three

148

times with ethanol and dried in oven at 60 °C for 1 h.

149

Preparation of conventional CLEAs and spherical CLEAs with biosilica shell. The

150

conventional CLEAs were prepared as the general procedure.27 For preparation of

7

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

151

spherical CLEA with biosilica shell, 50 mg CaCO3 microparticles were added into

152

purified recombinant PAL solution (6 mg/mL). The suspension was stirred at room

153

temperature for 0.5 h. Then ammonium sulfate was added to yield a final ammonium

154

sulfate saturation of 40%. After shaking the mixture at 100 rpm for 5 min, the particles

155

were crosslinked via glutaraldehyde (25 % v/v) at a final concentration of 0.3% (v/v) for

156

1 h at 4 °C under shaking at 100 rpm. After centrifugation, the precipitates were washed

157

for three times by 25 mM Tris-HCl buffer (pH 8.8) and resuspended in deionized water.

158

The suspension was slowly titrated with 0.1 M HCl till pH 5.2. After the CaCO3

159

templates were dissolved, the spherical CLEA particles were obtained. Subsequently, the

160

prepared spherical CLEA particles (20 mg) and 6 mg/mL PEI were mixed in 25 mM

161

potassium phosphate buffer (pH 6.8) at room temperature. The resultant mixtures were

162

mixed with 10 µL of 1 M hydrolyzed TMOS, and after 5 min, the mixtures were

163

centrifuged for 5 min at 10,000 ×g at 4 °C. The resultant spherical CLEAs with biosilica

164

shell were washed three times with deionized water and resuspended in 25 mM Tris-HCl

165

buffer (pH 7.0) at 4 °C prior to use.

166

Activity assay. The activities of free recombinant PAL, conventional CLEAs, spherical

167

CLEAs, and spherical CLEAs with biosilica shell were measured by the modification of

168

the procedure.23 A small amount of enzyme samples was added to an enzymatic reaction

169

medium. The reaction mixture containing 25 mM Tris-HCl buffer (pH 8.8), 25 mM

170

L-phenylalanine, and enzyme samples was incubated at 30 °C for 20 min. The reaction

171

was terminated by addition of 1 M of HCl. After centrifugation, the absorbance of the

8

ACS Paragon Plus Environment

Page 8 of 35

Page 9 of 35

Journal of Agricultural and Food Chemistry

172

clear supernatant was measured at 278 nm with a 752 spectrophotometer (Shanghai

173

precision and scientific instrument Co., China). One unit of PAL activity was defined as

174

the amount of enzyme required to convert one µmol of L-phenylalanine to

175

trans-cinnamic acids per min under the above conditions.

176

Characterization. Scanning electron microscope (SEM, JEOL S4800) and transmission

177

electron microscope (TEM, JEOL JEM2100) was used for imaging morphologies of the

178

CaCO3 microparticles, conventional CLEAs, spherical CLEAs, and spherical CLEAs

179

with biosilica shell, respectively. The pore size distributions of spherical CLEAs with

180

biosilica shell were determined following the Brunauer-Emmett-Teller (BET) method of

181

nitrogen adsorption/desorption on a Beckman coulter SA3100 analyzer at 77 K. The

182

chemical structures of spherical CLEAs with biosilica shell were analyzed with a Fourier

183

Transform Infrared Spectroscopy (FTIR) spectrum (NEXUS870 infrared spectrometer,

184

(Thermo Nicolet Corporation, Madison, WI). Energy-dispersive spectrometer (EDS) (S2

185

Ranger, Bruker, Germany) was utilized for the elemental composition of spherical

186

CLEAs with biosilica shell. Thermal gravimetric analysis (TGA) of spherical CLEAs

187

with biosilica shell was conducted with a SDT Q600 analyzer (TA Instruments-Waters

188

LLC, USA) by heating from 25 to 800 °C under nitrogen gas.

189

Measurement of kinetic parameters. Kinetic parameters of free PAL, conventional

190

CLEAs, and spherical CLEAs with biosilica shell were estimated by measuring initial

191

reaction rates using different L-Phenylalanine concentrations in the range of 1.25-50 mM

192

in buffer solution (Tris-HCl, 50 mM, pH 8.8) at 30 °C. Km and Vmax for free PAL,

9

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

193

conventional CLEAs, and spherical CLEAs with biosilica shell were calculated by the

194

Lineweaver-Burk double-reciprocal plot method of Michaelis-Menten Equation,

195

respectively.

196

The stability of spherical CLEAs with biosilica shell. Thermal stability of the free

197

PAL, conventional CLEAs, and spherical CLEAs with biosilica shell was evaluated by

198

measuring the residual activity after incubating at 60 °C for 10-60 min, respectively. The

199

stability of free PAL, conventional CLEAs, and spherical CLEAs with biosilica shell

200

against different chemical denaturants was tested by measuring the residual activity after

201

incubating at 30 °C for 30 min. The denaturing solutions consisted of urea (6 M), sodium

202

dodecyl sulfate (SDS, 2 %, w/v) or ethanol (40 %, v/v) in 25 mM Tris-HCl buffer (pH

203

8.8). Enzyme resistance to proteolysis in the presence of trypsin was also tested by

204

incubating free PAL, conventional CLEAs, and spherical CLEAs with biosilica shell in

205

25 mM Tris-HCl buffer (pH 8.8) containing 5 mg/mL of trypsin for a certain time at

206

50 °C. The residual activities of free PAL, conventional CLEAs, and spherical CLEAs

207

with biosilica shell were measured, respectively. In addition, the free PAL, conventional

208

CLEAs, and spherical CLEAs with biosilica shell were immersed in 50 mM sodium

209

phosphate buffer solution (pH 7.5) at 25 °C and shaken at 200 rpm for a certain time to

210

detect mechanical stability. Then the enzyme samples were taken out and centrifuged at

211

each time point, the residual activities in these immobilized enzymes and the supernatant

212

liquid were measured, respectively. Lastly, the reusability of immobilized PAL was

213

assessed by measuring the activity in each cycle. The conventional CLEAs and spherical

10

ACS Paragon Plus Environment

Page 10 of 35

Page 11 of 35

Journal of Agricultural and Food Chemistry

214

CLEAs with biosilica shell were collected and washed with buffer solution (Tris-HCl, 50

215

mM, pH 8.8) after each batch and then added to the next cycle, respectively.

216 217

Results and discussion

218

Preparation and characterization of spherical CLEAs with biosilica shell. The

219

preparation of the spherical CLEAs with biosilica shell is shown schematically in Figure

220

1. First, the CaCO3 vaterite particles was synthesized by simply mixing CaCl2 and

221

Na2CO3 solutions (including ethylene glycol). Second, PALs were precipitated into the

222

pores of the CaCO3 templates by addition of ammonium sulfate, and crosslinked by

223

addition of glutaraldehyde. Third, the CaCO3 templates were removed by change of the

224

pH to acidic region (up to pH 5.2), and spherical CLEAs were obtained. In a final step

225

the resulting spherical CLEAs were encapsulated in biomimetic silica by biosilicifiation

226

to form spherical CLEAs with biosilica shell. The morphologies of the prepared CaCO3

227

templates, conventional CLEAs, spherical CLEAs, and spherical CLEAs with biosilica

228

shell were characterized by SEM and TEM. As shown in Fig. 2, the spherical CaCO3

229

microspheres with a diameter about 2 µm possessed coarse and robust surface (Fig. 2a

230

and 2b), and it also can be observed clearly that the CaCO3 microspheres are composed

231

from channel-like spherulitic nanocrystals of a size of nanometers, suggesting that the

232

CaCO3 microspheres had a highly developed porous internal structure (Fig. 2c) (the

233

channel-like structure is indicated by the arrow). To further confirm the porous internal

234

structure of the CaCO3 microspheres, we conducted the TEM images. As can be seen

11

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

235

from Fig. 3a, the CaCO3 microspheres exhibited well-defined channel-like structures

236

with interconnected pores (the channel-like structure is indicated by the arrow). The

237

porous structure of the CaCO3 microspheres are also found in previous reports.36,37 The

238

channel-like structures with interconnected pores allow one to load a large amount of

239

adsorbing enzyme molecules, due to the high surface area available in the porous

240

structure. Fig. 2d showed that conventional CLEAs exhibited large size particles with

241

amorphous clusters and no defined morphologies. Whereas, spherical CLEAs and

242

spherical CLEAs with biosilica shell were relatively uniform architectures with ball

243

shape (Fig 2e and 2f). Furthermore, TEM further confirmed that spherical CLEAs and

244

spherical CLEAs with biosilica shell had higher monodispersity than that of

245

conventional CLEAs (Fig 3c and 3d). Especially, a silica coating of higher contrast

246

surrounding the spherical CLEA particles could be clearly observed by TEM (Fig. 3d),

247

indicating that the spherical CLEAs were successfully encapsulated in biomemitic silica.

248

Fourier-transform infrared (FTIR) spectra of spherical CLEAs with biosilica shell were

249

shown in Fig 4a. The characteristic absorption bands observed at 1627 cm-1 and 3430

250

cm-1 could be attributed to amide group and -N-H stretching vibrations, indicating the

251

presence of CLEAs. Similar absorption bands were also observed in FTIR spectra of

252

spherical CLEAs (Fig. 4b). The sharp absorption band observed at 1079 cm-1 is ascribed

253

to Si-O-Si antisymmetric stretching, the band at 876 cm-1 is attributed to Si-OH

254

stretching vibrations, indicating the formation of SiO2. In addition, the spherical CLEAs

255

with biosilica shell were characterized by TG and DTG analysis under N2 atmosphere.

12

ACS Paragon Plus Environment

Page 12 of 35

Page 13 of 35

Journal of Agricultural and Food Chemistry

256

Three distinct weight loss steps were observed for the spherical CLEAs with biosilica

257

shell (Fig. 4c). The first weight loss step occurred at 31-115 °C due to the loss of water.

258

The second weight loss step occurred in the range 200-300 °C and was attributed to the

259

decomposition of CLEA particles. The third weight loss step occurred in the range

260

300-500 °C, which was ascribed to the content of SiO2. EDS experiment showed that

261

signals for Si, C and O were present in the spherical CLEAs with biosilica shell (Fig. 5).

262

The results revealed that the spherical CLEAs with biosilica shell are composed by

263

CLEA particles and SiO2. Figure 6 showed the nitrogen-adsorption isotherms for the

264

spherical CLEAs with biosilica shell. The spherical CLEAs with biosilica shell exhibited

265

mesoporous structure, and had the multiple level pore size distribution (a broad size

266

between 2 and 40 nm). The porous structure might be critical for ensuring high catalytic

267

efficiency, due to an decrease in mass transfer limitation for substrates with the interior

268

enzymes of CLEAs. This hypothesis was further demonstrated by a kinetic study of the

269

enzymatic activity. Although the higher value of Michaelis–Menten constant (Km) could

270

be observed for spherical CLEAs with biosilica shell (Table 1) in comparison to that for

271

the free PAL, Km values of the spherical CLEAs with biosilica shell were lower than that

272

of conventional CLEAs, indicating that the biosilica shell did not cause the increased

273

mass transfer limitation for substrates. Furthermore, it is worth noting that the maximal

274

reaction rate (Vmax) of the spherical CLEAs with biosilica shell was 5-fold in comparison

275

with conventional CLEAs, indicating the higher catalytic rate. In our previous study,

276

conventional CLEAs was encapsulated in biomimetic silica by biosilicifiation

13

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

277

(CLEAs-Si). The resultant CLEAs-Si exhibited higher stability than native enzyme and

278

conventional CLEAs.23 However, it is difficult to efficiently encapsulate conventional

279

CLEAs into biomimetic silica due to wide particle distribution and high polydispersity,

280

which cause low activity recovery. In contrast, in this study, spherical CLEAs with high

281

monodispersity were easily embedded into biomimetic silica. As a result, the spherical

282

CLEAs with biosilica shell exhibited higher activity than CLEAs-Si.

283

Stability of the spherical CLEAs with biosilica shell. The stability of free PAL,

284

conventional CLEAs and the spherical CLEAs with biosilica shell against high

285

temperature and denaturants was showed in Figure 7. The spherical CLEAs with

286

biosilica shell exhibited the higher stability against high temperature than free PAL and

287

conventional CLEAs after incubating at 60 °C for 60 min. Free PAL and conventional

288

CLEAs only retained 19% and 25% of their initial activity, respectively, whereas the

289

activity of the spherical CLEAs with biosilica shell still remained about 80% of initial

290

activity (Figure 7a). Similarly, the spherical CLEAs with biosilica shell showed the high

291

stability against denaturants compared to free PAL and conventional CLEAs. For

292

example, in the presence of 6 M urea, both free PAL and conventional CLEAs lost most

293

of activity. However, the spherical CLEAs with biosilica shell retained 85% of its initial

294

activity (Figure 7b). These results indicated that the biosilica shell had a beneficial effect

295

on the resilience of the enzyme against high temperature and denaturants. The effect of

296

the biosilica shell against proteolysis was studied in the presence of the higher trypsin

297

concentration (5 mg/mL). The results were showed in Figure 8. Remarkably, in the

14

ACS Paragon Plus Environment

Page 14 of 35

Page 15 of 35

Journal of Agricultural and Food Chemistry

298

presence of trypsin, both free PAL and conventional CLEAs lost activity after they were

299

incubated in the presence of trypsin for 30 min, whereas the spherical CLEAs with

300

biosilica shell still retained more than 80% of its initial activity, confirming the shielding

301

effect of biosilica shell towards proteolysis. In addition, we evaluated the stability of free

302

PAL, conventional CLEAs and the spherical CLEAs with biosilica shell against

303

mechanical damage by incubating them in aqueous solution under shaking conditions

304

(200 rpm). As shown in Figure 9, activity of free PAL and conventional CLEAs

305

decreased considerably and lost most activity after 16 days. However, the spherical

306

CLEAs with biosilica shell still retained about 90% of its initial activity after 16 days of

307

shaking. These results clearly demonstrated that the biosilica shell afforded

308

unprecedented protection from biological, thermal, chemical, and mechanical

309

degradation for CLEA particles.

310

Reusability of the spherical CLEAs with biosilica shell. Reusability of enzyme is a

311

key factor for its cost-effective industrial use.42 The reusability of conventional CLEAs

312

and the spherical CLEAs with biosilica shell was investigated with 13 cycles. The results

313

were showed in Figure 10. The conventional CLEAs lost more than 65% of its original

314

activity after 13 cycles. In contrast, the spherical CLEAs with biosilica shell still retained

315

70% of its original activity after 13 cycles, demonstrating a very efficient recovery of the

316

enzyme catalyst. This result proved that the formation of silica shell around the spherical

317

CLEA particles readily facilitated the reuse of CLEAs, offering a long-term operational

318

stability and reusability. According to the results, the spherical CLEAs with biosilica

15

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

319

shell have potential use in industrial applications.

320

Acknowledgements

321

This work is partially supported by the National Natural Science Foundation of China

322

(project no. 21676069) and the Natural Science Foundation of Hebei Province, China

323

(project no. B2014208054). Dr. J. D. Cui also thanks supports from the Open Foundation

324

of Bio-manufacturing Subject at Hebei University of Science and Technology (project no.

325

SW5) and Key Foundation of Hebei University of Science and Technology, China

326

(project no. 2016ZDYY26).

327 328 329 330 331 332 333 334 335 336 337 338 339

16

ACS Paragon Plus Environment

Page 16 of 35

Page 17 of 35

Journal of Agricultural and Food Chemistry

340

References

341

(1) Cowan, D. A.; Fernandez-Lafuente, R. Enhancing the functional properties of thermophilic

342

enzymes by chemical modification and immobilization. Enzyme Microb. Tech. 2011, 49, 326-346.

343

(2) Liese, A.; Hilterhaus, L. Evaluation of immobilized enzymes for industrial applications. Chem.

344

Soc. Rev. 2013, 42, 6236-6249.

345

(3) Rodrigues, R. C.; Ortiz, C.; Berenguer-Murcia, Á.; Torres, R.; Fernández-Lafuente, R. Modifying

346

enzyme activity and selectivity by immobilization. Chem. Soc. Rev. 2013, 42, 6290-6307.

347

(4) Ding, S.; Cargill, A. A.; Medintz, I. L.; Claussen. J. C. Increasing the activity of immobilized

348

enzymes with nanoparticle conjugation. Curr. Opin. Biotechnol. 2015, 34, 242-250.

349

(5) Fernandez-Lafuente, R. Stabilization of multimeric enzymes: Strategies to prevent subunit

350

dissociation. Enzyme Microb. Tech. 2009, 45, 405-418.

351

(6) Mateo, C.; Palomo, J. M.; Fernandez-Lorente, G.; Guisan, J. M.; Fernandez-Lafuente, R.

352

Improvement of enzyme activity, stability and selectivity via immobilization techniques. Enzyme

353

Microb. Tech. 2007, 40, 1451-1463.

354

(7) Secundo, F. Conformational changes of enzymes upon immobilisation. Chem. Soc. Rev. 2013, 42,

355

6250-6261.

356

(8) Adlercreutz, P. Immobilisation and application of lipases in organic media. Chem. Soc. Rev. 2013,

357

42, 6406-6436.

358

(9) Sheldon, R.A.; Van Pelt, S. Enzyme immobilisation in biocatalysis: Why, what and how? Chem.

359

Soc. Rev. 2013, 42, 6223-6235.

17

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

Page 18 of 35

360

(10) Cantone, S.; Ferrario, V.; Corici, L.; Ebert, C.; Fattor, D.; Spizzo, P.; Gardossi, L. Efficient

361

immobilisation of industrial biocatalysts: Criteria and constraints for the selection of organic

362

polymeric carriers and immobilisation methods. Chem. Soc. Rev. 2013, 42, 6262-6276.

363

(11) Rodrigues, R. C.; Ortiz, C.; Berenguer-Murcia, A.; Torres, R.; Fernández-Lafuente, R.

364

Modifying enzyme activity and selectivity by immobilization. Chem. Soc. Rev. 2013, 42, 6290-6307.

365

(12) Cao, L. Q.; Langen, L. V.; Sheldon, R. A. Immobilised enzymes: carrier-bound or carrier-free?

366

Curr. Opin. Biotechnol. 2003, 14, 387-394.

367

(13) Velasco-Lozana, S.; López-Gallego, F.; Mateos-Díaz, J. C.; Favela-Torres. E. Cross-linked

368

enzyme aggregates (CLEA) in enzyme improvement–a review. Biocatalysis, 2015, 1, 166-177.

369

(14) Cao, L.; van Rantwijk, F.; Sheldon, R. A. Cross-linked enzyme aggregates: a simple and

370

effective method for the immobilization of penicillin acylase. Org. Lett. 2000, 2, 1361-1364.

371

(15) Kumar,

372

aggregates-bioremediation tool for decolorization of distinct classes of recalcitrant dyes. Sci. Total.

373

Environ. 2014, 487, 830-839.

374

(16) Torres, M. P. G.; Foresti, M. L.; Ferreira, M. L. Effect of different parameters on the hydrolytic

375

activity of cross-linked enzyme aggregates (CLEAs) of lipase from Thermomyces lanuginosa.

376

Biochem. Eng. J. 2013, 72, 18-23.

377

(17) Cui, J. D. Zhang, S.; Sun, L. M. Cross-linked enzyme aggregates of phenylalanine ammonia

378

lyase: novel biocatalysts for synthesis of L-phenylalanine. Appl. Biochem. Biotechol. 2012, 167,

379

835-844.

V.

V.;

Sivanesan,

S.;

Cabana,

H.

Magnetic

18

ACS Paragon Plus Environment

cross-linked

laccase

Page 19 of 35

Journal of Agricultural and Food Chemistry

380

(18) Cui, J. D.; Jia, S. R. Optimization protocols and improved strategies of cross-linked enzyme

381

aggregates technology: current development and future challenges. Crit. Rev. Biotechnol. 2015, 35,

382

15-28.

383

(19) Yu, H.; W. Chen, H.; Wang, X.; Yang, Y. Y.; Ching, C. B. Cross-linked enzyme aggregates

384

(CLEAs) with controlled particles: application to Candida rugosa lipase. J. Mol. Catal. B-Enzym.

385

2006, 43, 124-127.

386

(20) Sheldon, R. A. Cross-linked enzyme aggregates as industrial biocatalysts. Org. Process Res. Dev.

387

2011, 15, 213-223.

388

(21) Garcia-Galan, C., Berenguer-Murcia, A., Fernandez-Lafuente, R., Rodrigues, R.C. Potential of

389

different enzyme immobilization strategies to improve enzyme performance. Adv. Syn. Catal. 2011,

390

353, 2885-2904.

391

(22) Yamaguchi, H.; Miyazaki, M.; Asanomi, Y.; Maeda, H. Poly-lysine supported cross-linked

392

enzyme aggregates with efficient enzymatic activity and high operational stability. Catal. Sci. Technol.

393

2011, 1, 1256-1261.

394

(23) Cui, J. D.; Jia, S. R.; Liang, L. H.; Zhao, Y. M.; Feng. Y. X. Mesoporous CLEAs-silica

395

composite microparticles with high activity and enhanced stability. Sci. Rep. 2015, 5, 14203.

396

(24) Talekar, S.; Shah, V.; Patil, S.; Nimbalkar, M. Porous cross linked enzyme aggregates (p-CLEAs)

397

of Saccharomyces cerevisiae invertase. Catal. Sci. Technol. 2012, 2, 1575-1579.

398

(25) Nadar, S. S.; Rathod, V. K. Magnetic macromolecular cross linked enzyme aggregates (CLEAs)

399

of glucoamylase. Enzyme. Microb. Technol. 2016, 83, 78-87.

19

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

400

(26) Wang, M. F.; Qi, W.; Yu, Q. X.; Su, R. X.; He, Z. M. Cross-linking enzyme aggregates in the

401

macropores of silica gel: a practical and efficient method for enzyme stabilization. Biochem. Eng. J.

402

2010, 52, 168-174.

403

(27) Cui, J. D.; Li L. L.; Zhao Y. M. Simple technique for preparing stable and recyclable

404

crosslLinked enzyme aggregates with crude-pored microspherical silica core. Ind. Eng. Chem. Res.

405

2014, 53, 16176-16182.

406

(28) Talekar, S.; Ghodake, V.; Ghotage, T.; Rathod, P.; Deshmukh, P.; Nadar, S.; Mulla, M.; Ladole,

407

M. Novel magnetic cross-linked enzyme aggregates (magnetic CLEAs) of alpha amylase. Bioresour.

408

Technol. 2012, 123, 542-547.

409

(29) Lu, Z.; Zhang, J.; Ma, Y. Z.; Song, S.Y.; Gu, W. Biomimetic mineralization of calcium

410

carbonate/carboxymethylcellulose microspheres for lysozyme immobilization. Mater. Sci. Eng. C.

411

Mater. Biol. Appl. 2012, 32, 1982-1987.

412

(30) Thomas, A.; Kuhn, P.; Weber J.; Titirici M. M.; Antonietti, M. Porous polymers: enabling

413

solutions for energy applications. Macromol. Rapid Commun. 2009, 30, 221-236.

414

(31) Wang, Y. J.; Caruso, F. Nanoporous protein particles through templating mesoporous silica

415

spheres. Adv. Mater. 2006, 18, 795- 800.

416

(32) Balabushevich, N. G.; Pechenkin, M. A.; Shibanova, E. D.; Volodkin, D. V.; Mikhalchik, E. V.

417

Multifunctional polyelectrolyte microparticles for oral insulin delivery. Macromol. Biosci. 2013, 13,

418

1379–1388.

20

ACS Paragon Plus Environment

Page 20 of 35

Page 21 of 35

Journal of Agricultural and Food Chemistry

419

(33) Balabushevich, N. G.; de Guerenu, A. V. L.; Feoktistova, N. A.; Volodkin, D. Protein loading into

420

porous CaCO3 microspheres: adsorption equilibrium and bioactivity retention. Phys. Chem. Chem.

421

Phys. 2015, 17, 2523-2530.

422

(34) Volodkin, D. CaCO3 templated micro-beads and -capsules for bioapplications. Adv. Colloid.

423

Interface. Sci. 2014, 207, 306-324.

424

(35) Volodkin, D.; Skirtach, A.; Möhwald, H. Bioapplications of light-sensitive polymer films and

425

capsules assembled using the layer-by-layer technique. Polym.. Int.. 2012, 61, 673–679.

426

(36) Volodkin, D. V.; Schmidt, S.; Fernades, P.; Larionova, N. I.; Sukhorukov, G. B.; Duschl, C.;

427

Möhwald, H.; von Klitzing, R. One-step formulation of protein microparticles with tailored properties:

428

Hard templating at soft conditions. Adv. Funct. Mater. 2012, 22, 1914-1922.

429

(37) Schmidt, S.; Behra, M.; Uhig, K.; Nadaboosi, N.; Hartmann, L.; Duschl, C.; Volodkin, D.

430

Mesoporous protein particles through colloidal CaCO3 templates. Adv. Funct. Mater. 2013, 23,

431

116-123.

432

(38) Sumper, M.; Kröger, N. Silica formation in diatoms: the function of long-chain polyamines and

433

silaffins. J. Mater. Chem. 2004, 14, 2059–2065.

434

(39) Kröger, N.; Lorenz, S.; Brunner, E.; Sumper, M. Self-assembly of highly phosphorylated

435

silaffins and their function in biosilica morphogenesis. Science 2002, 298, 584–586.

436

(40) Knecht, M. R.; Wright, D. W. Functional analysis of the biomimetic silica precipitating activity

437

of the R5 peptide from Cylindrotheca fusiformis. Chem. Commun. 2003, 3038–3039.

438

(41) Patwardhan, S. V.; Clarson, S. J.; Perry, C. C. On the role(s) of additives in bioinspired

439

silicification. Chem. Commun. 2005, 1113–1121.

21

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

440

(42) Sheldon, R. A. Characteristic features and biotechnological applications of cross-linked enzyme

441

aggregates (CLEAs). Appl. Microbiol. Biotechnol. 2011, 92, 467–477.

442 443 444 445 446 447 448 449 450 451 452 453 454 455 456 457 458 459 460

22

ACS Paragon Plus Environment

Page 22 of 35

Page 23 of 35

Journal of Agricultural and Food Chemistry

461 462

Figure legends

463

Figure 1 Schematic illustration of the synthesis of spherical CLEAs with biosilica shell.

464

Figure 2 SEM images of (a, b) CaCO3 microsphere, (c) broken CaCO3 microsphere, (d)

465

conventional CLEAs, (e) spherical CLEAs (f) spherical CLEAs with biosilica

466

shell.

467 468 469 470

Figure 3 TEM images of (a) CaCO3 microsphere, (b) conventional CLEAs, (c) spherical CLEAs, (d) spherical CLEAs with biosilica shell. Figure 4 the FTIR data of spherical CLEAs with biosilica shell (a) and the conventional CLEA (b), and TGA (c) analysis of spherical CLEAs with biosilica shell.

471

Figure 5 Element mapping of the spherical CLEAs with biosilica shell via EDS.

472

Figure 6 N2 adsorption-desorption isotherms and pore size distribution curves of

473 474 475

spherical CLEAs with biosilica shell. Figure 7 Stability of free PAL, conventional CLEAs and spherical CLEAs with biosilica shell against high temperature (a) and denaturants (b).

476

Figure 8 Enzyme resistance to proteolysis in the presence of trypsin.

477

Figure 9 Mechanical stability of free PAL, conventional CLEAs and spherical CLEAs

478 479 480

with biosilica shell. Figure 10 Recyclability of conventional CLEAs and spherical CLEAs with biosilica shell.

481

23

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

Table 1. Comparison of kinetic parameters of free PAL, conventional CLEAs, and spherical CLEAs with biosilica shell

Enzyme

Km (mM)

Vmax (mM/min)

Free PAL

9.97

0.026

Conventional CLEAs

76.68

0.001

Spherical CLEAs with biosilica shell

71.28

0.005

ACS Paragon Plus Environment

Page 24 of 35

Page 25 of 35

Journal of Agricultural and Food Chemistry

Figure 1

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

Figure 2

ACS Paragon Plus Environment

Page 26 of 35

Page 27 of 35

Journal of Agricultural and Food Chemistry

Figure 3

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

Figure 4

ACS Paragon Plus Environment

Page 28 of 35

Page 29 of 35

Journal of Agricultural and Food Chemistry

Figure 5

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

Figure 6

ACS Paragon Plus Environment

Page 30 of 35

Page 31 of 35

Journal of Agricultural and Food Chemistry

Figure 7

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

Figure 8

ACS Paragon Plus Environment

Page 32 of 35

Page 33 of 35

Journal of Agricultural and Food Chemistry

Figure 9

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

Figure 10

ACS Paragon Plus Environment

Page 34 of 35

Page 35 of 35