Engineering Reaction Kinetics by Tailoring the Metal Tips of Metal

Aug 29, 2017 - Semiconductor–metal hybrid nanostructures are one of the best model catalysts for understanding photocatalytic hydrogen generation. T...
1 downloads 16 Views 1001KB Size
Subscriber access provided by MT SINAI SCH OF MED

Communication

Engineering Reaction Kinetics by Tailoring the Metal Tips of Metal-Semiconductor Nanodumbbells Ji Yong Choi, Dahyi Jeong, Seon Joo Lee, Dong-gu Kang, Sang Kyu Kim, Ki Min Nam, and Hyunjoon Song Nano Lett., Just Accepted Manuscript • DOI: 10.1021/acs.nanolett.7b02582 • Publication Date (Web): 29 Aug 2017 Downloaded from http://pubs.acs.org on August 30, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Nano Letters is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

Engineering Reaction Kinetics by Tailoring the Metal Tips of Metal-Semiconductor Nanodumbbells Ji Yong Choi,1 Dahyi Jeong,1 Seon Joo Lee,1 Dong-gu Kang,1 Sang Kyu Kim,1,* Ki Min Nam,2,* and Hyunjoon Song1,3,*

1

Department of Chemistry, Korea Advanced Institute of Science and Technology, Daejeon 34141,

Republic of Korea 2

Advanced Materials Division, Korea Research Institute of Chemical Technology, 141 Gajeong-

ro, Yuseong-gu, Daejeon 34114, Republic of Korea 3

Department of Chemistry, Mokpo National University, Jeonnam 58554, Republic of Korea

4

Center for Nanomaterials and Chemical Reactions, Institute for Basic Science, Daejeon 34141,

Republic of Korea

ACS Paragon Plus Environment

1

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 22

ABSTRACT

Semiconductor-metal hybrid nanostructures are one of the best model catalysts for understanding photocatalytic hydrogen generation. To investigate the optimal structure of metal co-catalysts, metal-CdSe-metal nanodumbbells were synthesized with three distinct sets of metal tips, Pt-CdSePt, Au-CdSe-Au, and Au-CdSe-Pt. Photoelectrochemical responses and transient absorption spectra showed that the competition between the charge recombination at the metal-CdSe interface and the water reduction on the metal surface is a detrimental factor for the apparent hydrogen evolution rate. For instance, a large recombination rate (krec) at the Pt-CdSe interface limits the quantum yield of hydrogen generation despite a superior water reduction rate (kWR) on the Pt surface. To suppress the recombination process, Pt was selectively deposited onto the Au tips of Au-CdSe-Au nanodumbbells, in which the krec was diminished at the Au-CdSe interface, and the large kWR was maintained on the Pt surface. As a result, the optimal structure of the Pt-coated AuCdSe-Au nanodumbbells reached a quantum yield of 4.84%. These findings successfully demonstrate that the rational design of a metal co-catalyst and metal-semiconductor interface can additionally enhance the catalytic performance of the photochemical hydrogen generation reactions.

KEYWORDS: nanoparticles, photocatalyst, hydrogen generation, metal co-catalyst, charge recombination

ACS Paragon Plus Environment

2

Page 3 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

Solar hydrogen generation is an ideal alternative to fossil fuels due to its environmentally clean nature using plentiful resources, sun light and water.1 To get hydrogen from water at high efficiency, the rational design of photocatalysts is apparently the most detrimental problem.2-5 Among various materials, a hybrid structure of semiconductor and metal components is regarded as an ideal photocatalyst structure, in which photoinduced charge separation occurs at the semiconductor domain, and the subsequent electron transfer to the metal leads to efficient hydrogen generation on its surface.6,7 Although metal-semiconductor hybrid catalysts contain only two components, they exhibit sophisticated photophysical kinetics with multiple variables, such as charge separation,8-10 relative band alignment,11,12 hole transfer rate,13-16 and charge recombination17 during photocatalytic reactions. To address these kinetic issues, semiconducting nanorods decorated with metal tips are one of the best model catalysts because each domain is single-crystalline with a well-defined morphology,18 which induces simple catalytic pathways with effective charge separation through uniform electronic junctions.19 Since Banin et al. reported the selective growth of Au tips on semiconductor nanorods,20 many researchers have tried to carry out accurate kinetic studies on the catalyst structure to understand detailed reaction processes. Among various kinetic factors, recent works have particularly focused on charge separation and transfer that mainly occur at the semiconductor domains. For instance, Tang et al. investigated charge separation behaviors on CdSe-metal nanorods and found that Pt completely extracted excited electrons from the CdSe nanorod, but Au could not.9 Alivisatos et al. demonstrated that effective hole localization on the CdSe cores and the long distance between the CdSe and Pt tips significantly increased the hydrogen production efficiency in a CdSe core/CdS nanorod structure with Pt tips.11 Lian et al. investigated the trend in hydrogen evolution rates on CdS-Pt and CdSe/CdS-Pt nanorods with

ACS Paragon Plus Environment

3

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 22

respect to their hole transfer rates.13 The kinetics related to the metal domains and their interfaces are also important; however, these have been rarely investigated thus far. Banin et al. recently reported the importance of the metal tip size on the photocatalytic efficiency.8 Amirav et al. synthesized metal alloy tips, which greatly changed the catalytic properties on the surface by heterometallic bonding interactions.21,22 In the present work, we chose CdSe nanorods decorated with metals at both tips, usually referred it as nanodumbbells, as a model catalyst for photocatalytic hydrogen generation. In particular, we varied the metal tips, which largely altered the kinetic parameters related to the metal domains and the metal-semiconductor interface, and eventually determined the catalytic efficiency. By means of photoelectrochemical measurements and transient absorption spectroscopy, we show that the competition between the charge recombination at the metal-semiconductor interface and the water reduction on the metal surface significantly contributed to the apparent hydrogen production rate. As well as the optimization of the kinetics at the semiconductor domains, a rational tailoring of the metal domains can additionally enhance the catalytic activities of solar hydrogen production. To fix other structural factors except for the metal tips, Pt-CdSe-Pt and Au-CdSe-Au nanodumbbells were synthesized by modifying the methods according to the literature.23 In the PtCdSe-Pt nanodumbbells, the CdSe nanorods have an average dimension (length × diameter) of 13.6 × 5.0 nm with an average Pt tip size of 3.4 nm. The latter structure has a dimension of 13.0 × 4.6 nm with a Au tip size of 3.4 nm (Figure S1, Supporting Information). In addition, we synthesized asymmetric nanodumbbells with heterometal tips, Au-CdSe-Pt, by the sequential deposition of Pt and Au precursors on the CdSe nanorods, for the first time. After the formation of the Pt-CdSe single-tipped nanorods, the Au precursor solution was added to the particle dispersion in the presence of didodecyldimethylammonium bromide (DDAB) and dodecylamine (DDA), in

ACS Paragon Plus Environment

4

Page 5 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

which DDA had a dual role as a surfactant and a reductant. The inverse sequence of the precursor addition did not work at all because an irregular deposition of Au occurred at the CdSe nanorods during the formation of the Au-CdSe single-tipped nanorods through the Ostwald-ripening-like process.24 The transmission electron microscopy (TEM) image in Figure 1a shows that both ends of the CdSe nanorods are successfully decorated by tiny metal domains. The CdSe nanorods are uniform with an average length of 12.6 ± 1.5 nm and an average diameter of 4.6 ± 0.3 nm. The average diameters of the Au and Pt tips are 4.4 ± 0.4 nm 3.0 ± 0.3 nm, respectively, for which the positions were identified by elemental mapping (see below). The high-resolution TEM (HRTEM) image of an individual Au-CdSe-Pt nanodumbbell structure shows that each domain is single crystalline with the formation of a well-defined junction with the neighboring domains (Figure 1b). The lattice spacing of the metal domains matches the distance of the Au(200) (0.204 nm) or Pt(111) (0.227 nm) planes, respectively. The elemental mapping images inevitably prove that the Au-CdSe-Pt heterometal nanodumbbells are formed, the two ends of which are clearly distinguished by the Pt (green) and Au (red) elements (Figures 1c-f and S2, Supporting Information). The X-ray diffraction (XRD) data show the patterns from a combination of hexagonal wurtzite CdSe (JCPDS No. 08-0459) and face-centered cubic Pt (JCPDS No. 04-0802) and Au (JCPDS No. 04-0784) (Figure S3). The UV-visible absorption spectrum of the CdSe nanorods shows a strong absorption peak centered at 635 nm (Figure S4), which is assigned to the first excitonic transition (1σv → 1σc) from the valence band edge to the conduction band edge in the CdSe.9,25 This apparent peak was broadened after the deposition of the Au or Pt on the CdSe nanorods due to the delocalization of

ACS Paragon Plus Environment

5

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 22

Figure 1. (a) TEM and (b) HRTEM images of Au-CdSe-Pt nanodumbbells. (c) HAADF-STEM image of the nanodumbbells. Elemental mapping of (d) both Pt (green) and Au (red), (e) Cd (orange), and (f) Se (sky blue). The bars represent (a) 20 nm and (b) 5 nm.

the electronic states of the semiconductor into the metal domains. In the photoluminescence spectra, all the nanodumbbells exhibit complete quenching of the signals implying effective electron transfer from the CdSe nanorods to the metal tips (Figure S5).23 This photophysical feature provides the evidence that the metal tip growth on the semiconductor nanorods develops effective electronic junctions between the metal and the semiconductor domains.

ACS Paragon Plus Environment

6

Page 7 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

The metal-semiconductor nanodumbbells are excellent model catalysts for hydrogen production from water. To investigate their catalytic properties, three distinct nanodumbbells, Pt-CdSe-Pt, Au-CdSe-Au, and Au-CdSe-Pt, were transferred to aqueous media through surfactant exchange with mercaptoundecanoic acid (MUA).11 Hydrogen production was induced by the illumination of visible light (λ ≥ 420 nm) in the presence of hole scavengers, Na2SO3 and Na2S. Figure 2 shows that hydrogen evolution continuously occurs along the reaction progress for all catalysts; however, the evolution rate is highly dependent upon the metal component. After a 2 h irradiation, the amount of hydrogen production was on the order of Au-CdSe-Pt (61 μmol) > Pt-CdSe-Pt (30 μmol) > Au-CdSe-Au (6.0 μmol). The quantum efficiency was estimated to be 2.45% for Au-CdSe-Pt, 1.55% for Pt-CdSe-Pt, and 0.22% for Au-CdSe-Au, respectively, by irradiation from a light emitting diode at 420 nm (see Supporting Information).

Figure 2. Photocatalytic H2 evolution by Au-CdSe-Au (green), Pt-CdSe-Pt (blue), and Au-CdSePt (red) nanodumbbells, in a 0.35 M Na2SO3/0.25 M Na2S aqueous solution (4.0 mg catalyst; 300 W Xe lamp with a UV cut-off filter (λ ≥ 420 nm)).

ACS Paragon Plus Environment

7

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 22

In general, Pt is known as the best co-catalyst for photocatalytic hydrogen generation due to its favorable proton binding energy12 and low electrochemical impedance facilitating electron diffusion into the surface-adsorbed species.2,26 In the case of junction formation with semiconductors, Pt completely extracts electrons from the semiconductor and transfers them to the surface adsorbed species, but Au cannot.9 Based on these properties, it is easy to propose that the Pt-CdSe-Pt may facilitate electron transfer more efficiently than that of the others due to the existence of the double Pt tips. In this regard, the present twice larger activity of the Au-CdSe-Pt nanodumbbells compared to that of the Pt-CdSe-Pt is totally unexpected. It indicates that the electron transfer rate through metal co-catalysts is not the only critical factor dominating the apparent reaction activity. To investigate the photocatalytic properties in detail, the photoelectrochemical responses of the nanodumbbells were examined. The catalysts were drop-casted onto a SnO2/ITO plate, and the resulting electrode was used as a working electrode in a three-electrode photoelectrochemical cell (see Supporting Information). The resulting nanodumbbell films on the electrodes had the thicknesses of 35 nm and showed nearly identical optical behaviors to the CdSe films (Figure S6, Supporting Information). A current-time response curve was measured at an applied potential of 0.5 V versus Ag/AgCl under visible light irradiation (λ ≥ 420 nm) (Figure 3a). By the irradiation of light, electrons are excited to the conduction band edge of the catalyst generating photocurrents. Photogenerated holes are simultaneously transferred to the hole scavengers, Na2SO3 and Na2S, in the aqueous medium. The hole transfer efficiency in this cell is considered to be 100% due to the fast kinetics at the electrode-medium interface.27 The photocurrent densities of the bare and Pttipped CdSe nanorods tend to decrease due to the increase in the number of metal tips (CdSe (0.105 mA/cm2) > CdSe-Pt (-0.079 mA/cm2) > Pt-CdSe-Pt (-0.058 mA/cm2)). Moreover, it is

ACS Paragon Plus Environment

8

Page 9 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

Figure 3. (a) Current-time response curves and (b) action spectra of CdSe nanorods (black), PtCdSe tipped-rods (pink), and Pt-CdSe-Pt (blue), Au-CdSe-Pt (red), and Au-CdSe-Au (green) nanodumbbells in 0.35 M Na2SO3/0.25 M Na2S aqueous solution, respectively.

clearly dependent upon the metal tip composition of the nanodumbbells on the order of Au-CdSeAu (-0.068 mA/cm2) > Au-CdSe-Pt (-0.062 mA/cm2) > Pt-CdSe-Pt (-0.058 mA/cm2). The smaller photocurrent density in the presence of the metal tips is attributed to electron-hole recombination at the metal-semiconductor interface.28 In particular, the distinct decrease of the photocurrent by increasing the number of Pt tips compared to that of the Au tips indicates that the recombination rate at the Pt interface is larger than that at the Au tips (see below for krec). The action spectra in Figure 3b show that all the catalysts exhibit absorption patterns in the range of 300 – 700 nm

ACS Paragon Plus Environment

9

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 22

similar to that of the bare CdSe nanorods.29 In these spectra, the increase in the number of Pt tips leads to a decrease in the absorption intensity, also indicating that facile charge recombination occurs at the Pt-CdSe interface. Transient absorption (TA) spectroscopy is an excellent measurement that can provide kinetic information on the charge carrier dynamics. TA was measured after photoexcitation by pump pulses at 400 nm with a laser fluence of 30 nJ/pulse. The TA spectra of the nanodumbbells exhibit a strong negative absorption peak at 635 nm due to the state filling of the first excitonic transition (1σv → 1σc), and derivative-like positive absorptions at 670 nm formed from a Stark-shifted 1σv → 1σc transition (Figure 4a and S7, Supporting Information).9 The weak negative absorptions at 537.5 nm and the positive peaks at 595 nm are assigned to the bleaching and Stark shift of the 1π v →1π c transition.30 Normalized TA time traces of the bleach recovery at the band edge emission are shown in Figure 4b. For all the samples, kinetic decays are successfully fitted to tri-exponential functions (Figure 4b, fit and Table S1, Supporting Information). At early delay times within 1 ps, the bleach signals are dominated by state filling of the lowest energy exciton states, which corresponds to the charge separation kinetics from the conduction band edge of the CdSe to the metal tips.31 The lifetimes (τ1) of the first decays are estimated to be 876.82 fs for Au-CdSe-Au, 270.12 fs for Au-CdSe-Pt, and 263.51 fs for Pt-CdSe-Pt nanodumbbells, respectively. Another kinetic process, electron trapping on the interfacial defect sites, exists in a longer time scale of >100 ps.32,33 This is fitted with second decays, the lifetimes (τ2) of which are 1.24 ns for Au-CdSe-Au, 1.86 ns for Au-CdSePt, and 1.68 ns for Pt-CdSe-Pt nanodumbbells, respectively. However, this process is very slow compared to the direct electron transfer to the metal centers, and is also effectively

ACS Paragon Plus Environment

10

Page 11 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

Figure 4. (a) Transient absorption spectra of Au-CdSe-Pt nanodumbbells with time delays after 400 nm excitation. (b) Normalized TA time traces and fits (black) of Pt-CdSe-Pt (blue), Au-CdSePt (red), and Au-CdSe-Au nanodumbbells (green) after 400 nm excitation with a laser fluence of 30 nJ/pulse. (c) Energy band alignment diagram with available kinetic routes at pH 13. (d) Measured rate constants and calculated quantum yield of Pt-CdSe-Pt, Au-CdSe-Pt, and Au-CdSeAu nanodumbbells. * was taken from ref. 31.

quenched through the interfacial electron transfer to the metals;32-34 therefore, it does not influence on the whole catalytic activity. The recombination kinetics are fitted from the subsequent bleach recovery, reflecting the decay of the exciton population.30,35 The lifetimes (τ3) of the third decays are 45.74 ns for Au-CdSe-Au, 31.15 ns for Au-CdSe-Pt, and 24.36 ns for Pt-CdSe-Pt, respectively. These relaxation times are considered to result from the recombination of the photoelectrons with

ACS Paragon Plus Environment

11

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 22

the trapped holes.17 The short lifetime in the Pt-tipped nanodumbbells indicate that the charge recombination rate at the Pt tips is larger than that of the Au tips. Based on the experimental results for the hydrogen evolution reactions, photoelectrochemical responses and transient absorption spectra, the photophysical behaviors are rationalized using a kinetic model shown in Figure 4c.8 All energy levels in the scheme are adjusted with respect to our experimental conditions at pH 13. The morphology of the nanodumbbells, including the size of the CdSe and metal domains and their interface structure, is essentially uniform, which renders the kinetic model simple with less kinetic parameters. The photoexcited electrons either directly undergo recombination with the holes on the CdSe domain (with a rate of ke-h) or are transferred to the metal tips (with kET). The electrons on the metal domain either proceed the water reduction reaction on the surface (with kWR) or are recombined with the holes at the interface region (with krec). The photogenerated holes are trapped with a rate of kST, which is relevant to the electron transfer kinetics.8 According to this simplified kinetic model, the efficiency of the hydrogen evolution reactions can be derived with the following equation (Supporting Information): QY =

𝑘𝑘ET 𝑘𝑘WR

(𝑘𝑘WR +𝑘𝑘rec )(𝑘𝑘ET +𝑘𝑘ST +𝑘𝑘e−h )

(1)

In this equation, the electron-hole recombination rate (ke-h) is known to be very slow (4.9 ns for CdSe) compared to the other processes.19,31 The hole trapping rate (kST) is estimated to be 0.14 ns1

(τ = 7 ns) in the CdSe nanorods, for which the rate negligibly changed after the metal deposition.31

The electron transfer rates to the metal tips (kET) on all the nanodumbbells are estimated in the magnitude of ps-1 from the lifetimes of the bleached signals (τ1) in the TA spectra. If we accept these values, kET is much larger than ke-h and kST, and equation (1) can be further simplified by kET + kST + ke-h ≒ kET as follows: QY =

𝑘𝑘WR

𝑘𝑘WR + 𝑘𝑘rec

(2)

ACS Paragon Plus Environment

12

Page 13 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

This equation means that the competition between the charge recombination at the metalsemiconductor interface (with krec) and the water reduction reaction on the metal surface (with kWR) is critical to determine the quantum yield of the catalytic system. Using equation (2), all rate constants in this kinetic model, kET, kWR, krec and kST, are quantitatively analyzed from the quantum yields measured by the experiments (Figure 4d). As we expected from the photocurrent generation data, the krec of the Au-CdSe-Au dumbbells is at the minimum, although the quantum yield of the hydrogen generation is the lowest due to the significantly low value of the kWR. In contrast, both the krec and kWR are large in the Pt-CdSe-Pt and Au-CdSe-Pt dumbbells, and the krec mainly influences the quantum yields. It is very difficult to extract the contribution of each metal tip (either Au or Pt) on these double-tipped structures, but it is clear at least that the number of Pt tips tends to largely increase the krec, resulting in the relatively low quantum yield of the Pt-CdSe-Pt compared to that of the Au-CdSe-Pt. The decrease in the quantum yield by recombination losses was similarly reported in multiple Pt clusters on CdS nanorods.17 It is noted that the kWR of the Au-CdSe-Pt is even larger than the kWR of the Pt-CdSe-Pt, although the latter structure has multiple Pt tips. Amirav et al. found that a single catalytic site per excitation unit is statistically advantageous to form all intermediates on the same catalytic site in multielectron reactions.34 Pt has a far lower H+ chemisorption energy than Au22 so that all reaction intermediates majorly form at the Pt sites, as similarly occurred in single Pt-tipped nanorods. In regard to the electron transfer, Au has a tendency to store electrons without transferring them to the surrounding media,12,36 which promote the electron transfer towards the Pt tips. These factors may induce the high value of the kWR in the Au-CdSe-Pt nanodumbbells. For the single Pt-tipped CdSe nanorods, the amount of hydrogen production was measured to be 140 μmol by a 2 h

ACS Paragon Plus Environment

13

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 22

irradiation of visible light (Figure S8, Supporting Information), which was much larger than that of the Au-CdSe-Pt nanodumbbells. This high activity cannot be directly compared to those of the nanodumbbell structures, due to superior hole transfer to the sacrificial reagents through the open ends.10,23 The charge recombination rate at the interface is also the lowest as shown in Figure 3a.17 However, it still indicates that the smaller number of active cocatalyst per catalyst unit is essential to enhance the photocatalytic activity.35

Figure 5. (a) TEM and (b,c,d) HADDF-STEM images of Pt-coated Au-CdSe-Au nanodumbbells. (e) Photocatalytic H2 evolution and (f) current-time response curve at -0.5 V versus Ag/AgCl in a 0.35 M Na2SO3/0.25 M Na2S aqueous solution by irradiation of visible light (λ ≥ 420 nm). The bars represent (a) 10 nm and (b-d) 4 nm.

ACS Paragon Plus Environment

14

Page 15 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

The findings in our experiments provide intuition for the rational design of a metal cocatalyst with high efficiency; i.e., the suppression of krec as well as the enhancement of kWR. The Pt tips induce a high kWR but also a high krec, whereas the Au tips exhibit a very low kWR but also a low krec in the nanodumbbell structure. Apparently, the hybridization between the low krec of the Au domains and the high kWR of the Pt surface would be able to maximize the total catalytic performance. The resulting design is a Pt coating on the surface of the Au tips in the Au-CdSe-Au nanodumbbells. In this structure, the low krec is conserved at the Au-CdSe interface, and the Pt surface coating on the Au tips would significantly increase the kWR (Figure 5). To synthesize the Pt-coated Au-CdSe-Au nanodumbbells, the Pt precursor was added to the Au-CdSe-Au dispersion in oleylamine at high temperature. Figure 5a shows that the dumbbell structure is well maintained after the Pt deposition. The energy dispersive X-ray spectroscopic analysis indicates that the product contains 7.6 atomic% Pt. Elemental mapping of an individual nanodumbbell also shows that Pt selectively coats the surface of the Au tips, but not the CdSe wall (Figures 5b-d). Nearly all Au tips of the nanodumbbells are coated with the Pt layers (Figure S9, Supporting Information). As shown in Figure 5e, the hydrogen evolution rate under the present reaction conditions remarkably increases as we expected; for a 2 h irradiation of visible light, the amount of hydrogen generation was measured to be 125 μmol, which is tremendously increased from the uncoated AuCdSe-Au (6.0 μmol), and is even twice larger than that of the Au-CdSe-Pt (61 μmol). This value is also comparable to that of the single tipped Pt-CdSe, although the number of metal tips per a single catalyst unit is twice. The quantum yield of the Pt-coated Au-CdSe-Au reached 4.84%, which is also superior to the other nanodumbbells. A similar bimetallic approach with Pt and Au was reported in CdSe@CdS nanorods, in which the authors proposed that the exposed interfaces between the Pt and Au are a key factor.21 In our catalysts, the photochemical response shows that

ACS Paragon Plus Environment

15

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 22

the photocurrent of the Pt-coated Au-CdSe-Au nanodumbbells is identical to that of the original Au-CdSe-Au nanodumbbells, implying that the recombination rate at the Au-CdSe interface does not change during the Pt coating process (Figure 5f). The lifetime (τ2) of the second decay in the TA spectrum was measured as 38.86 ns, which is also comparable with the Au-CdSe-Au (40.60 ns). Consequently, the selective Pt coating at the Au tips largely enhances the kWR without damaging the krec of the original Au-CdSe-Au nanodumbbells. In conclusion, we synthesized metal-semiconductor nanodumbbells with three distinct sets of metal tips, Pt-CdSe-Pt, Au-CdSe-Au, and Au-CdSe-Pt, all with an identical morphology and size. The photocatalytic activity and quantum yield in the hydrogen evolution reaction are on the order of Au-CdSe-Pt > Pt-CdSe-Pt > Au-CdSe-Au. On the other hand, the photocurrent generation follows the order of the number of Au tips, which reveals a low recombination rate at the Au-CdSe interface compared to that at the Pt-CdSe interface. The results of the transient absorption experiment show that the competition between the charge recombination at the metal-CdSe interface and the water reduction on the metal surface is critical in determining the quantum yield. Based on these findings, we successfully demonstrate that the Pt-coated Au-CdSe-Au nanodumbbell is an optimized catalyst structure bearing a low charge recombination rate and a high water reduction rate at the same time, resulting in a quantum yield reaching 4.84%, which is twice larger than the value of the Au-CdSe-Pt and forty times larger than that of the original AuCdSe-Au nanodumbbells. As well as the optimization of the hole transfer kinetics, the rational design and precise engineering of the electron transfer kinetics of the metal cocatalyst and metalsemiconductor interface can further enhance the catalytic performances of photochemical hydrogen generation reactions.

ACS Paragon Plus Environment

16

Page 17 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

ASSOCIATED CONTENT Supporting Information. The Supporting Information is available free of charge on the ACS Publications website at DOI: Experimental section, calculation of quantum yield, method of transient absorption spectroscopy and additional figures (PDF)

AUTHOR INFORMATION Corresponding Author * E-mail: [email protected] * E-mail: [email protected]

* E-mail: [email protected]

Author Contributions J.Y.C., S.J.L., and H.S. designed the experiments, and prepared the samples. D.J., D.K., and S.K.K. contributed to transient absorption measurements. J.Y.C., K.M.N., and H.S. analyzed the photophysical mechanism of the hydrogen evolution reaction. J.Y.C., S.J.L., and H.S. wrote the manuscript. Notes The authors declare no competing financial interest.

ACS Paragon Plus Environment

17

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 22

ACKNOWLEDGMENT This work was supported by the Saudi-Aramco and KAIST CO2 management center. This work was also supported by the Institute for Basic Science (IBS-R004-D1) and the National Research Foundation

of

Korea

(NRF)

funded

by

the

Korea

Government

(MSIP)

(NRF-

2015R1A2A2A01004196). D.J., D.K., and S.K.K thank to the support by NRF funded by the Korea Government (MSIP) (NRF-2015R1A2A1A01004470).

REFERENCES (1) Rajeshwar, K.; McConnell, K.; Licht, S. Solar Hydrogen Generation Toward a Renewable Energy Future; Springer: New York, 2008. (2) Osterloh, F. E. Chem. Mater. 2008, 20, 35−54. (3) Fujishima, A.; Honda, K. Nature 1972, 238, 37. (4) Kudo, A.; Miseki, Y. Chem. Soc. Rev. 2009, 38, 253-278. (5) Chen, X.; Shen, S.; Guo, L.; Mao, S. S. Chem. Rev. 2010, 110, 6503-6570. (6) Kudo, A. MRS Bull. 2011, 36, 32-38. (7) Kamat, P. V. J. Phys. Chem. Lett. 2012, 3, 663-672. (8) Ben-Shahar, Y.; Scotognella, F.; Kriegel, I.; Moretti, L.; Cerullo, G.; Rabani, E.; Banin, U. Nat. Comm. 2016, 7, 10413.

ACS Paragon Plus Environment

18

Page 19 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

(9) Yu, P.; Wen. X.; Lee, Y.-C.; Lee, W.-C.; Kang, C.-C.; Tang, J. J. Phys. Chem. Lett. 2013, 4, 3596-3601. (10) Zhu, H.; Song, N.; Lv, H.; Hill, C. L.; Lian, T. J. Am. Chem. Soc. 2012, 134, 11701-11708. (11) Amirav, L.; Alivisatos, A. P. J. Phys. Chem. Lett. 2010, 1, 1051-1054. (12) Wood, A.; Giersig, M.; Mulvaney, P. J. Phys. Chem. B 2001, 105, 8810-8815. (13) Wu, K.; Chen. Z.; Lv, H.; Zhu, H.; Hill, C. L.; Lian, T. J. Am. Chem. Soc. 2014, 136, 77087716. (14) Acharya, K. P.; Khnayzer, R. S.; O’Connor, T.; Diederich, G.; Kirsanova, M.; Klinkova, A.; Roth, D.; Kinder, E.; Imboden, M.; Zamkov, M. Nano Lett. 2011, 11, 2919-2926. (15) Kalisman, P.; Nakibli, Y.; Amirav, L. Nano Lett. 2016, 16, 1776-1781. (16) Simon, T.; Bouchonville, N.; Berr, M. J.; Vaneski, A.; Adrović, A.; Volbers, D.; Wyrwich, R.; Döblinger, M.; Susha, A. S.; Rogach, A. L.; Jäckel, F.; Stolarczyk, J. K.; Feldmann, J. Nature Mater. 2014, 13, 1013-1018. (17) Simon, T.; Carlson, M. T.; Stolarczyk, J. K.; Feldmann, J. ACS Energy Lett. 2016, 1, 11371142. (18) Ben-Sharhar, Y.; Banin, U. Top. Curr. Chem. 2016, 374, 54. (19) Wu, K.; Zhu, H.; Liu, Z.; Rodriguez-Córdoba, W.; Lian, T. J. Am. Chem. Soc. 2012, 134, 10337-10340. (20) Mokari, T.; Rothenberg, E.; Popov, I.; Costi, R.; Banin, U. Science 2004, 304, 1787-1790.

ACS Paragon Plus Environment

19

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 22

(21) Kalisman, P.; Houben, L.; Aronovitch, E.; Kauffmann, Y.; Bar-Sadan, M.; Amirav, L. J. Mater. Chem. A. 2015, 3, 19679-19682. (22) Aronovitch, E.; Kalisman, P.; Mangel, S.; Houben, L.; Amirav, L.; Bar-Sadan, M. J. Phys. Chem. Lett. 2015, 6, 3760-3764. (23) Bang, J. U.; Lee, S. J.; Jang, J. S.; Choi, W.; Song, H. J. Phys. Chem. Lett. 2012, 3, 37813785. (24) Mokari, T.; Sztrum, C. G.; Salant, A.; Rabani, E.; Banin, U. Nature Mater. 2005, 4, 855863. (25) Khon, E.; Mereshchenko, A.; Tarnovsky, A. N.; Acharya, K.; Klinkova, A.; HewaKasakarage, N. N.; Nemitz, I.; Zamkov, M. Nano Lett. 2011, 11, 1792-1799. (26) Tongying, P.; Vietmeyer, F.; Aleksiuk, D.; Ferraudi, G. J.; Krylova, G.; Kuno, M. Nanoscale 2014, 6, 4117-4124. (27) Shi, X.; Choi, I. Y.; Zhang, K.; Kwon, J.; Kim, D. Y.; Lee, J. K.; Oh, S. H.; Kim, J. K.; Park, J. H. Nat. Comm. 2014, 5, 4775. (28) Choi, W.; Park, G.; Bae, K-L.; Choi, J. Y.; Nam, K. M.; Song, H. J. Mater. Chem. A 2016, 4, 13414-13418. (29) Guzmán, D.; Isaacs, M.; Osorio-Román, I.; García, M.; Astudillo, J.; Ohlbaum, M. ACS Appl. Mater. Interfaces 2015, 7, 19865-19869. (30) Jiang, Z.-J.; Kelley, D. F. J. Phys. Chem. C 2011, 115, 4594-4602. (31) Zhu, H.; Lian, T. J. Am. Chem. Soc. 2012, 134, 11289-11297.

ACS Paragon Plus Environment

20

Page 21 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

(32) Wheeler, D. A.; Zhang, J. Z. Adv. Mater. 2013, 25, 2878-2896. (33) Tvrdy, K.; Frantsuzov, P. A.; Kamat, P. V. Proc. Natl. Acad. Sci. U. S. A. 2011, 108, 29-34. (34) Wu, K.; Li, Q.; Du, Y.; Chen, Z.; Lian, T. Chem. Sci. 2015, 6, 1049-1054 (35) Nakibli, Y.; Kalisman, P.; Amirav, L. J. Phys. Chem. Lett. 2015, 6, 2265-2268. (36) Subramanian, V.; Wolf, E. E.; Kamat, P. V. J. Phys. Chem. B 2003, 107, 7479-7485.

ACS Paragon Plus Environment

21

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 22

SYNOPSIS

ACS Paragon Plus Environment

22