Enhancing Distorted Metal–Organic Framework-Derived ZnO as

Oct 12, 2017 - *E-mail: [email protected]. ... The small weight ratio of Ag2S QDs to ZnO@C at 1:180 shows the best performance in lithium sto...
0 downloads 0 Views 2MB Size
Subscriber access provided by RMIT University Library

Article

Enhancing Distorted Metal Organic Framework Derived ZnO as Anode Material for Lithium Storage by the Addition of Ag2S Quantum Dots Weixin Song, Rowena Brugge, Ioannis G. Theodorou, Alvin Lukai Lim, Yuchen Yang, Tingting Zhao, Claire H. Burgess, Ian D. Johnson, A. Aguadero, Paul R Shearing, Dan J.L. Brett, Fang Xie, and D. Jason Riley ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.7b12661 • Publication Date (Web): 12 Oct 2017 Downloaded from http://pubs.acs.org on October 16, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 12

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Enhancing Distorted Metal Organic Framework Derived ZnO as Anode Material for Lithium Storage by the Addition of Ag2S Quantum Dots Weixin Songa, Rowena Bruggea, Ioannis G. Theodoroua, Alvin Lukai Limb, Yuchen Yangc, Tingting Zhaoc, Clare H. Burgessa, Ian D. Johnsonc, Ainara Aguaderoa, Paul R. Shearingb, Dan J.L. Brettb, Fang Xiea, D. Jason Rileya* a

Department of Materials, Imperial College London, London SW7 2AZ UK. Centre for Nanotechnology, London SW7 2AZ, UK. b

Department of Chemical Engineering, University College London, London WC1 E6BT UK.

c

Department of Chemistry, University College London, London WC1 E6BT UK.

KEYWORDS: Distorted MOFs; ZnO; ZnS; Sulfidation; Lithium storage

ABSTRACT: The lithium storage properties of the distorted metal-organic framework (MOF) derived nanosized ZnO@C are significantly improved by the introduction of Ag2S quantum dots (QDs) during the processing of the material. In the thermal treatment, the Ag2S QDs react to produce Ag nanoparticles and ZnS. The metal nanoparticles act to shorten electron pathways and improve the connectivity of the matrix and the partial sulfidation of the ZnO surface improves the cycling stability of the material. The electrochemical properties of ZnO@C, Ag2S QDs treated ZnO@C and the amorphous carbon in ZnO@C have been compared. The small weight ratio of Ag2S QDs to ZnO@C at 1:180 shows the best performance in lithium storage. The exhibited specific capacities are improved and retained remarkably in the cycling at high current rates. At low current densities (200 mA g-1) treatment of ZnO@C with Ag2S QDs results in a 38% increase in the specific capacity.

Introduction

ligands, offers a facile route to metal oxide-carbon nanocomposites with defined microstructure2-4. MOF-5, also called IRMOF-1, has been carbonized in a nitrogen atmosphere at 550 oC to obtain hierarchically porous carboncoated ZnO quantum dots (QDs)5. The resultant ZnO QDs, with mean particle size of 3 nm, show uniform dispersion without agglomeration in the carbon matrix and the ZnO QDs@porous carbon delivers promising storage performance in lithium-ion batteries. However, the so-called QDs ZnO should be highly dependant on the quality of the MOFs and pyrolysis method affecting the crystal size easily, especially for the MOFs with distorted metal oxide clusters which is common for MOF-56-11. Xie12 et al. and Wang13 et al. have demonstrated that introducing metal nanoparticles into a zinc oxide-carbon composite improves electron transport. It is reported that the as formed materials showed enhanced

Materials for lithium ion batteries must offer high capacity, widespread availability, be environmental benignity, exhibit good conductivity, and excellent stability. Whilst many metal oxides are able to meet the first three of these criteria, they are not employed in devices owing to their limited conductivity and poor stability1. The instability of many metal oxide based Li-battery anodes stems from the large volume changes during lithiation-delithiation; for example, bulk ZnO shows a volume change of 228% during charging and discharging. Preparing nanosized metal oxides of welldefined architecture has been demonstrated as a means to mitigate the problem of large volume changes and reduce the distance ions must diffuse, i.e., minimize the resistance. The pyrolysis of Metal Organic Frameworks (MOFs), porous crystalline solids composed of transition metal centers/clusters in coordination with functional organic

1

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 12

Synthesis of C550: 240 mg of as-prepared ZnO@C550 was mixed with 30 mL 3 mol L-1 KOH solution and stirred overnight. The precipitate was centrifuged and washed with water several times to remove K+ ions before drying in an oven at 80 oC. The powder was black and denoted C550.

reversible capacitance, improved rate performance and greater stability. Zinc sulfide has a slightly lower theoretical capacity to that of zinc oxide but the percentage volume change on lithiationdelithiation of the former material is reduced. This suggests lithium battery anodes incorporating zinc sulfide will be more stable than zinc oxide anodes. Fu14 et al. prepared a ZnS-carbon composite by reacting carbonized ZnO from pyrolysis of MOF-5 with thioacetamide in an autoclave for 24 h. It was demonstrated that the resultant precipitate was an excellent anode material in a Li-ion battery. Sulfidation of ZnO has also been employed to prepare materials for supercapacitors15. It was demonstrated that partial sulfidation of ZnO yielded a beneficial ZnO@ZnS material that possessed high capacity and excellent stability. The interface effect in the nanocrystals of the heterostructure induces electric field resulting in low ion-diffusion resistance and facile electron transfer16-17. The aim of this work is to enhance the performance of a carbon-metal oxide network formed upon pyrolysis of the distroted MOFs by the introduction of metal nanoparticles into the matrix, to enhance electron transport and connectivity, and the partial sulfidation of the surface of the oxide, to improve stability, in a simple one-step reaction, see Scheme 1. MOF-5 was synthesized by refluxing terephthalic acid (H2BDC) and Zn(NO3)2·6H2O in N,Ndmethylacetamide (DMA). The decomposition of MOF-5 in an argon atmosphere at 550 oC was performed to produce a nanosized ZnO-carbon composite (ZnO@C550). The resultant material was suspended in a glucose solution containing silver sulfide (Ag2S) quantum dots (SSQD) and subject to a hydrothermal reaction. Pyrolysis of the resultant material was performed at 550 oC to yield a ZnO-ZnS-Agcarbon composite. The performance of the ZnO-ZnS-Agcarbon composite as an anode in a lithium ion battery was compared to the parent ZnO@C550, a carbon anode (C550) prepared by treating ZnO@C550 in strong base and a ZnO@C550 sample processed in a glucose solution in the absence of Ag2S particles (ZnO@CC). It was demonstrated that the decomposition of the Ag2S QDs within the ZnOcarbon matrix resulted in a material with enhanced capacity and excellent cyclability.

Synthesis of ZnO@CC: 180 mg ZnO@C550 was added into 20 mL 0.1 mol L-1 solution of glucose and stirred for 30 min before transfer to the 120 mL autoclave. The autoclave was put into the oven and heated at a rate of 5 oC min-1 to 180 oC, left for 2 h and then cooled down to room temperature. The solution was then filtered and washed with ethanol and water several times before drying in vacuum at 80 oC. Synthesis of Ag2S quantum dots (SSQD): Silver sulfide (Ag2S) quantum dots (SSQD) were synthesized via thermaldecomposition of silver diethyldithiocarbamate, Ag(DDTC) as described in the literature18. Briefly, 0.1 mmol of Ag(DDTC) was added to 10 g of 1-dodecanethiol (DT) in a 100 mL three-necked flask at room temperature. Oxygen was removed from the slurry with vigorous magnetic stirring under vacuum for 5 min. The reaction flask was refilled with Ar and the reaction temperature was raised to 130 °C at a rate of 10 °C min-1 and retained at this temperature for 1 min to allow the growth of 2.7 nm SSQDs. The solution was cooled to room temperature under ambient atmosphere and 50 mL of ethanol was subsequently poured into the solution. Ag2S QDs were collected by centrifugation at 16,000 g for 30 minutes. In order to render Ag2S QDs hydrophilic with a carboxylic acid group capping, ligand exchange of DT with dihydrolipoic acid (DHLA) was performed.19 A mixture of asprepared Ag2S QDs (10 mg), cyclohexane (15 mL), ethanol (15 mL), and DHLA (100 g) was stirred at room temperature for 48 h. The hydrophilic Ag2S QDs were collected by centrifugation at 16,000 g for 1 h, washed with deionized water twice, redispersed in deionized water and stored at 4 oC in the dark. Synthesis of SSQD inlayed ZnO/C: 200 µL of as-prepared SSQD solution (5 mg mL-1) was mixed with 20 mL 0.1 mol L-1 solution of glucose by stirring. Then 180 mg ZnO@C550 was added and stirred for 30 min before transfer to the 120 mL autoclave. The autoclave was put into the oven and heated at a rate of 5 oC min-1 to 180 oC, left for 2 h and then cooled down to room temperature. The solution was then filtered and washed with ethanol and water several times before drying in vacuum at 80 oC. The powder obtained was heated in Ar at a rate of 2 oC min-1 to a temperature of 550oC and calcined for 5 h to transfer SSQDs into the ZnO@C composite, the final material being denoted as ZnO@CC/SSQDm. Similarly, when 600 µL SSQD solution was used with 180 mg ZnO/C550 with the same method, the product was labeled ZnO@CC/SSQD3m.

Materials and Methods

Material Characterization: The crystallographic structure of the as-prepared materials was studied by X-ray powder diffraction (XRD) using a Bruker D8 diffractometer with monochromatic Cu Kα radiation (λ = 1.5406 Å), and the diffraction data was recorded in the 2θ range of 10–80 o. Scanning electron microscopy (SEM) images were recorded on a LEO Gemini 1525 FEG with the electron energy of 5 kV. Electron Dispersive X-Ray Spectroscopy (EDS) was recorded on LEO Gemini 1525 FEG microscopy. Transmission electron microscopy (TEM) images, selected area electron diffraction (SAED), scanning transmission electron microscopy (STEM) were carried out on a JEM 2100F. X-ray photoelectron spectroscopy (XPS) was measured on a Thermo Scientific K-Alpha instrument. Raman spectroscopy was

Synthesis of MOF-5: 0.95 g terephthalic acid and 5.03 g Zn(NO3)2·6H2O were dissolved in 80 mL N,N-dimethylacetamide (DMA) in a 100 mL flask at room temperature. The solution was then continuously stirred at 600 rpm and refluxed at 120 oC for 17 h, heating rate 5 oC min-1. The precipitate obtained was collected after the solution had cooled down and was washed with DMA three times before drying under vacuum overnight at 80 oC. Synthesis of ZnO@C: The prepared MOF-5 was sintered at 550 o C and 700 oC in an Ar atmosphere, heating was performed at a rate of 8 oC min-1 followed by direct cooling. The samples obtained were denoted ZnO@C550 and ZnO@C700, respectively.

2

ACS Paragon Plus Environment

Page 3 of 12

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

performed using a RenishawinVia with 20× objective and 514 nm laser as excitation source. The thermogravimetric analysis/differential scanning calorimetry (TGA/DSC) of the samples was carried out on a Diamond TG thermo-analyzer.

form a rigid and porous structure, as depicted in the inset of Figure 1a (also see Figure S1)20-21. The central cluster of MOF-5 is zinc oxide, resulting from the combination of Zn2+ and carboxylic acid, and the Zn-O-C motifs are formed and linked with benzene struts20-21. Figure 2a indicates that at a 2θ value greater than 30° the XRD pattern of the as-prepared MOF-5 displays peaks that match those of zincite. At lower angles, the positions of the peaks are in good agreement with those calculated for MOF-56-8. However, the measured intensities of the XRD peaks, especially at low-angles, are different from those calculated and published11, 22. It has been reported that this discrepancy may result from species, e.g. Zn(OH)2, in the pores that can reduce the intensity of the diffraction at 6.9° and split the peak, owing to a symmetry distortion from cubic to trigonal, at 9.7°. On pyrolysis of the as-formed MOF at 550 °C and 700 °C in an Ar atmosphere, denoted ZnO@C550 and ZnO@C700 respectively, composites containing zincite (ZnO) are obtained, as evidenced by the diffraction pattern in Figure 1b and Figure S2. The crystal size of ZnO in ZnO/C550, calculated by application of the Scherrer equation on the (103) peak, is 25 nm resulting from the distorted metal cluster in the MOFs. When ZnO/C550 was placed in a glucose solution, hydrothermally treated and the recovered solid calcined at 550 °C, the XRD pattern of the resultant solid, ZnO@CC, indicated that the zincite was maintained throughout the processing (Figure S2). Zincite is also observed in the XRD patterns, Figure 1b, obtained when 2.7 nm SSQDs (Figure S3) are added to the glucose solution at Zn to Ag ratios in mass of 180:1 and 60:1 prior to processing, samples termed ZnO@CC/SSQDm and ZnO@CC/SSQD3m, respectively. The XRD pattern of the sample infused with the greater concentration of SSQDs, ZnO@CC/SSQD3m, also shows weak features at 2θ angles of 38.1 o and 44.2 o consistent with the (111) peaks and (200) peaks of silver metal, indicating the silver sulfide particles undergo thermal decomposition when heated to give silver nanoparticles in the resultant matrix.

Electrochemical Tests: The as-prepared material was mixed with acetylene black and binder (sodium carboxymethyl cellulose, CMC) in a weight ratio of 8:1:1 by using distilled water as the solvent and a copper foil as the current collector, followed by drying in vacuum at 100 oC for 24 h. The R2016 coin cell was assembled in an argon-filled glove box using metallic lithium as the cathode and Celgard 2500 membrane as the separator. The electrolyte was 1 M LiPF6 dissolved in a mixture of ethylene carbonate (EC), dimethyl carbonate (DMC) (v/v, 1/1). Cyclic voltammetry (CV) and galvanostatic charge/discharge cycling tests were carried out in a set voltage range using an Autolab workstation (GPES software) and a 580 Bycycle battery test system, respectively. Electrochemical impedance spectroscopy (EIS) was studied using a Solartron Analytical 1260 FRA and a Solartron 1286 potentiostat, an amplitude of 5 mV in the frequency range from 1000 Hz to 10 mHz was applied. All electrochemical tests were carried out at room temperature.

Scheme 1 Ag2S QDs decompose in the pyrolysis of cubic ZnO@C (left) to produce ZnS layer on the surface of ZnO@C matrix and silver nanoparticles conductor (right).

Results and Discussion The as-synthesized MOF-5 has a structural formula of Zn4O(BDC)3 that reticulates cubes in three dimensions to

3

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 12

Figure 1 (a) XRD patterns of the as-prepared MOF-5. References are XRD patterns from zincite and the calculated MOF-5 crystallite. The inset is the schematic structure of MOF-5; the red spheres are O atoms, white spheres are H atoms, black spheres are C atoms and blue spheres are Zn atoms. (b) XRD patterns of ZnO@C550, ZnO@CC/SSQDm and ZnO@CC/SSQD3m. N2 absorption/desorption curve of: (c) ZnO@C550, (d) ZnO@CC and (e) ZnO@CC/SSQDm. The inset is the corresponding pore size distribution curve. (f) Raman spectra of ZnO@C550 and ZnO@CC/SSQDm. N2 absorption/desorption isotherms of ZnO@C550, low-frequency phonons, E2(L), and high-frequency phonons, ZnO@CC and ZnO@CC/SSQDm are shown in Figure 1c-e, E2(H). The bands around 435 and 327 cm-1 (inset of Figure which are typical type IV curves. The Brunauer–Emmett– 1f) are due to the E2(H) mode and multi-phonon scattering Teller (BET) theory was used to deduce the surface area of consisting of predominant A1 and smaller E2 and E1 all the samples, the pore size distributions of ZnO@C550 symmetry24-25. The bands at 1340 and 1589 cm-1 are typical and ZnO@CC/SSQDm were determined using the BarretD and G modes of carbon materials, and the intensity ratio of Joyner-Halenda (BJH) method on account of their mixed ID/IG is indicative of the fraction of graphite structure23. The macroporosity and mesoporosity, Density Functional Theory ID/IG ratios of ZnO@CC/SSQDm and ZnO@C550 are 0.83 (DFT) was employed to find the pore size distribution of the and 0.95 respectively, indicating that the degree of mesoporous ZnO@CC sample. ZnO@C550 has a BET graphitization increases as glucose decomposes in surface area of 222 m2 g-1, with pore sizes distributed around ZnO@C550. 49 and 545 nm and a pore volume of 0.352 m3 g-1. ZnO@CC has a BET surface area of 252 m2 g-1, a pore size below 20 nm and a pore volume of 0.387 m3 g-1. ZnO@CC/SSQDm shows 231 m2 g-1 with pore sizes around 41 and 576 nm and a pore volume of 0.366 m3 g-1. The enlarged surface area and pore volume of ZnO@CC and ZnO@CC/SSQDm indicates that the penetrated glucose in the pores larger than micro size, has decomposed in hydrothermal and calcination treatment to become amorphous carbon which contributes more pore area and volume23. The total carbon contents of ZnO@C550, ZnO@CC and ZnO@CC/SSQDm are 20%, 17.4% and 14.3%, respectively, see Figure S4. Figure 1f displays the Raman spectra of ZnO@C550 and ZnO@CC/SSQDm. ZnO has optical phonons represented as A1, E1, 2E2 and 2B1 amongst which the A1 and E1 modes are polar modes active for both Raman and Infrared, the E2 mode is nonpolar only active for Raman and the B1 mode is a silent mode24. A1 and E1 modes split into longitudinal (LO) and Figure 2 SEM images of (a) Zn-MOF, (b) ZnO@C550, (d) ZnO@CC/SSQDm, (e) ZnO@CC/SSQD3m and (f) C550. transverse (TO) components, and the E2 mode comprises

4

ACS Paragon Plus Environment

Page 5 of 12

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

EDS Elemental mapping of (c) ZnO@C550 and (g-k) ZnO@CC/SSQD3m.

interpenetration of ZnO crystals with random lattice orientations. The axes labelled a and c are at an angle of 90o and the reciprocal points of the (101) and (103) planes from a single zincite crystal have an angle of approximately 30o (see Figure S7). Comparing θ1 and θ2, the point circled is formed from the second crystal. The polycrystalline nature of the material is confirmed in the HRTEM image in Figure 3b in which the (103) and (110) lattice planes of ZnO are both observed. The two (110) planes show different orientations, indicating they originate from different ZnO crystal. The Fast Fourier Transform (FFT) image of the lattice mixed area in Figure 3b is displayed in the inset. In reciprocal space the (110) plane is at 40o with respect to the (101) plane when viewed along the [1,-1, -1] direction (Figure S7b) and the stereographic projection, see Figure S7c, indicates that the (110) plane should be at an angle larger than 40o with (103) plane. Therefore, the red circled (110) plane in the inset corresponding to the green dotted plane (d=1.65 Å) in HRTEM is from the second crystal. The bright field (BF) and dark field (DF) scanning transmission electron microscope (STEM) images in Figure 3c illustrate the porous structure of ZnO@CC/SSQDm. That the carbon component is amorphous is confirmed by the TEM images of C550 and the corresponding electron diffraction patterns in Figure 3d.

The scanning electron microscopy (SEM) image of the asprepared MOF-5 shows a cubic microstructure with a rough surface (Figure 2a). The surface is patterned with spherical solids of approximately 1 µm inlayed into the MOF-5 matrix (inset of Figure 2a). On calcination at 550 oC the resultant ZnO@C550 is transformed into a highly porous composite in which the cubic sized particles of the parent MOF are maintained, see Figure 2b. Elemental mapping indicates that the Zn is dispersed uniformly in the ZnO@C550 composite, Figure 2c. In ZnO@C700, formed at the higher sintering temperature of 700 oC, the cubic structure is destroyed, see Figure S5, and the composite contains smaller sized features. Exposure of ZnO@C550 to glucose solution and glucose solution containing SSQDs followed by hydrothermal processing and calcination at 550 °C does not alter further the microstructure of the composite, Figures 2d and e. The cubic microstructure is again preserved, Figure 2f, when ZnO@C550 is subject to treatment in a strong base to dissolve the ZnO and yield C550, which is composed of amorphous carbon, as indicated by the broad XRD peak at approximately 22o, (see Figure S6)26. Elemental mapping of ZnO@CC/SSQD3m, Figure 2(g-k), shows Ag agglomerates and a uniform distribution of C, O and Zn. EDX also shows the presence of S in the composite, the nature of the S in the material is discussed below.

Figure 3 (a) SAED of the circle part from TEM images of ZnO@CC/SSQDm. (b) HRTEM image of ZnO@CC/SSQDm, the inset is the FFT pattern from the mixed area. (c) BF and DF STEM images of ZnO@CC/SSQDm. (d) TEM images of C550 and the corresponding SAED pattern. ZnO@CC/SSQDm was subject to intense sonication to destroy the cubic microstructure and yield particles suitable for TEM analysis. Figure 3a shows that ZnO@CC/SSQDm contains nanosized components and a selective area electron diffraction (SAED) pattern of the sample, is consistent with a material containing ZnO crystals. Two unrelated reciprocal points from (101) planes are observed, pointing to

Figure 4 High resolution XPS spectra of (a) Ag 3d, (b) S 2p and (c) Zn 2P3/2 of ZnO@CC/SSQDm.

5

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 4 displays the high-resolution XPS spectra of Ag, S and Zn of ZnO@CC/SSQDm. The spectrum of Ag 3d in Figure 4(a) shows characteristics typical of a metal27. This spectrum contains two components: one at 368.3 eV for Ag 3d5/2 and the other at 374.3 eV for Ag 3d3/2, the difference in binding energy of 6 eV results from spin-orbital effects28. The orbital spin of silver metal leads to the loss of features at the higher binding energy side of each component. The intensity of the S 2p spectrum, Figure 4(b), is considerably weaker than that for Ag. The S 2p spectrum is consistent with the presence of ZnS and a very small amount of S in the as-prepared composite, with the absence of Ag-S confirming that all the SSQds have been reacted to Ag nanoparticles, in agreement with the Ag 3d XPS deconvolution and XRD analysis. The S 2p3/2 of ZnS is located at 161.7 eV and that of S is at 163.8 eV29. The spin-orbit of S 2p results in 1.16 eV difference between S 2p3/2 and S 2p1/2. In agreement, the Zn 2p spectrum, Figure 4(c) displays two 2p3/2 components at 1022.1 and 1021.9 eV pointing to Zn-O and Zn-S respectively29-31. The spin orbital of Zn 2p results in a pair of 2p3/2 and 2p1/2 with a difference of 23 eV in binding energy. The atomic ratio of S:Ag:Zn is 0.9:7.6:91.5 through the XPS survey of S 2p3/2, Ag 3d5/2 and Zn 2p3/2, see Figure S8. The small amount of ZnS in the composite, consistent with a submonolayer of ZnS on the ZnO surface, explains the absence of ZnS signals in the XRD patterns and the Raman spectra. Figure S9 shows the atom ratio of S:Ag:Zn is 2.9:7:90.1 in ZnO@CC/SSQDm, thus the ratio of ZnS:ZnO increased from 1:90 to 1: 30 when 3-times more SSQDs are added in the synthesis of ZnO@CC/SSQD3m. The Ag content is found to be lower than that in ZnO@CC/SSQDm, indicating the Ag particles aggregate during sulfidation reaction, consistent with the EDX mapping. Electrodes comprising ZnO@C550, ZnO@CC, ZnO@CC/SSQDm and ZnO@CC/SSQD3m were electrochemically tested in coin cells with lithium metal as the counter electrode material. Cyclic voltammograms (CV) of the samples were obtained between 0.01 and 3.00 V vs. Li+/Li at a scan rate of 0.5 mV s−1, see Figure 5. The smaller areas under the CV curves of ZnO@C550 and ZnO@CC, in comparison to the samples ZnO@CC/SSQDm and ZnO@CC/SSQD3m, indicates a lower capacity for the former. This is confirmed by integration of the CV peak at 0.5 V where a larger capacity is observed when SSQDs are used in the processing (see Table S1). The CV measured at 0.5 mV s−1 of ZnO@CC/SSQDm shows more features that those of ZnO@C550, ZnO@CC and ZnO@CC/SSQD3m at the same scan rate. The additional peaks observed in ZnO@CC/SSQDm can be observed for all electrodes when lower scan rates are employed, for ZnO@C550 see Figure 5b, for ZnO@CC see Figure S10 and for ZnO@CC/SSQD3m see Figure 6d. The fact that the additional features are

Page 6 of 12

retained at higher scan rates for ZnO@CC/SSQDm electrodes points to an enhanced rate performance for this material. Displayed in Figure 5c, the CV curves of ZnO@CC/SSQDm have two cathodic peaks at 0.55 V and 0.2 V corresponding to the reduction of ZnO/ZnS to Zn (Reaction 1), and the formation of Zn-Li alloys (Reaction 2) and/or the decomposition of electrolyte30, 32-33. The multiple anodic peaks before 1 V result from the multi-step de-alloying reaction among LiZn, Li2Zn3, LiZn2 and Li2Zn5 and the peak at 1.5 V is due to the decomposition of Li2O. / +  + ↔  +  /  (Reaction 1)  +  + ↔   ↔  ↔    ↔  (Reaction 2) CV curves at different scan rates are shown in Figure 5d-f for ZnO@C550, ZnO@CC/SSQDm and ZnO@CC/SSQD3m. For ZnO@C550 the cathodic peak is extremely depressed at high rates and the anodic peak II moves to higher potential with increased scan rate. In contrast, for ZnO@CC/QQSDm the potential of the CV peaks is stable and for ZnO@CC/SSQD3m peak II downshifts with increasing scan rate. The upshift of the anodic peak with scan rate for ZnO@C550 points to high internal resistance in the system. SSQDs incorporation decreases the resistance, leading to lower distortion of the CV peaks for the ZnO@CC/QQSDm and ZnO@CC/SSQD3m systems. In cyclic voltammetry the peak current (ip) and the scan rate (v) are related by the expression ip=avb, where b, the slope of the lg(v)-lg(ip) plot, has a value of 0.5 for a diffusion-controlled process and unity when charge transfer is surface-controlled. Figure S11 shows the relationship between lg(v) and lg(ip) of peak I and peak II from ZnO@C550 and ZnO@CC/SSQD3m, respectively. The b values from peak I and peak II of ZnO@C550 are 0.69 and 0.76 and for ZnO@CC/SSQD3m are 0.98 and 0.8 at a scan rate above 0.2 mV s-1. The switch to surface control of the electrochemical reaction in ZnO@CC/SSQD3m at high scan rates indicates a more facile injection of Li+ into the ZnS coated material at high current densities34. The Li+ iondiffusion capability is evaluated by the appearent diffusion coefficient. The linear relationship between the anodic peak current (ip) and square root of scan rates resulting from the CV curves of ZnO@C550 and ZnO@CC/SSQD3m is depicted in Figure S12. Thus the ion diffusion coefficients are calculated using the Randle-Sevcik equation35-36. It is found that the coefficients are 3.6✕10-11 and 1.7✕10-11 cm2 s-1 for anodic peaks I and II respectively of ZnO@C550 and increase to 9.9✕10-10 and 4.7✕10-10 cm2 s-1 for ZnO@CC/SSQD3m, demonstrating the facile lithium diffusion in the compound after sulfidation.

6

ACS Paragon Plus Environment

Page 7 of 12

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 5 Cyclic voltammetry of the as-prepared materials. (a) Scan rate is 0.5 mV s-1 for ZnO@C550, ZnO@CC, ZnO@CC/SSQDm and ZnO@CC/SSQD3m. (b) ZnO@C550 cycled at 0.1 and 0.2 mV s-1. (c) First two cycles of ZnO@CC/SSQDm at 0.5 mV s-1. Cycles at different scan rates of (d) ZnO@C550, (e) ZnO@CC/QQSDm and (f) ZnO@CC/SSQD3m.

7

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 12

Figure 6 Galvanostatic charge/discharge properties of (a) ZnO@C550, (b) ZnO@CC, (c) ZnO@CC/SSQDm, (d)ZnO@CC/SSQD3m and (e) C550. The capacities at different current densities are compared in (f). Rate and cycling performance of (g) ZnO@C550 at 200 mA g-1, (h) ZnO@CC/SSQDm at 500-1000 mA g-1 and (i) ZnO@CC/SSQDm at 5 A g-1. decomposed organic makes a negligible contribution to the increased capacity. When 1 mg SSQDs were added to 180 mg ZnO@C550 to form ZnO@CC/SSQDm,, this improves both the capacity at low current density, owing to the silver nanoparticles increasing the connectivity in the matrix, and leads to a lower drop in performance with increasing current density. Further increase of the amount of SSQDs (3 mg) in the composite, ZnO@CC/SSQD3m, results in only a limited change in the device performance at higher current densities but an enhanced capacity at low current densities, 50 and 100 mA g-1. The amorphous carbon, C550 derived by treating ZnO@C550 in a strong base, has negligible capacity (see Figure S13). At 200 mA g-1 as shown in Figure 6g, ZnO@C550 shows stable cycling performance in capacity and coulobmic efficiency. The device maintains a capacity of 332.3 mAh g-1 with an efficiency of nearly 100% after 100 cycles. At higher current density (500mA g-1) the capacity of ZnO@C550 suffers fluctuations (200 mAh g-1 at the 500th cycle) which

Table 1 The specific capacity (mAh g-1) of the as-prepared samples at the specific current densities. sample 50 100 200 500 1000 mA mA mA gmA g- mA 1 -1 -1 -1 1 g g g ZnO@C550 667 465 318 185 118 ZnO@CC 492 325 233 154 115 ZnO@CC/SSQDm 690 544 438 288 213 ZnO@CC/SSQD3m 1030 560 418 274 205 C550 226 193 164 116 89 Figures 6a-e display the galvanostatic charge/discharge curves of ZnO@C550, ZnO@CC, ZnO@CC/SSQDm, ZnO@CC/SSQD3m and C550. The specific capacities at corresponding current densities are listed in Table 1 and plotted in Figure 6f. ZnO@CC has lower capacities than the parent matrix, ZnO@C550, indicating that when SSQDs are introduced into the system in a glucose solution the

8

ACS Paragon Plus Environment

Page 9 of 12

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces ZnO@CC/SSQDm at a current density of 200 mA g-1 are displayed in Figure 7. This representation exaggerates peaks due to charge transfer processes and makes it easier to differentiate redox processes than the CVs discussed above. The differential capacity trace for C550 shows no sharp peaks and is consistent with lithiation/delithiation of an amorphous carbon material. ZnO@C550 and ZnO@CC display five and three peaks in charge and discharge, consistent with multiple redox reactions and alloying/dealloying steps. The features for the ZnO@CC/SSQDm are much sharper than for the other samples, pointing to improved electron transport in the matrix. In the top plot of Figure 7 the first charging peak is clearly split into two, possibly as a result of the voltage shift for the reactions of ZnS and ZnO with lithium.

are ascribed to the activation of dispersed ZnO crystals, see Figure S14. ZnO@CC/SSQDm retains a capacity of 294 mAh g-1after 500 cycles while ZnO@CC/SSQD3m only retains 136mAh g-1 and suffers fluctuant capacities during cycling. The in-situ high frequency resistance (HFR) measurement tracing the 500 cycles of ZnO@CC/SSQD3m displays the point resistance at 1000 and 100 HZ respectively. The up and down of the HFR correlate with the decrease and increase in capacity well, indicating the HFR of the electrode is responsible for the fluctuations in capacity during cycling. Figure 6h shows the rate performance of ZnO@CC/SSQDm at 1, 2, 5 and 10 A g-1 and each current has 100 cycles. The stable and average capacities are 208, 175, 118 and 81 mAh g-1 respectively, and after 400 cycles, the average value of 248mAh g-1 is recovered at 1 A g-1. The long-term and highrate cycling of ZnO@CC/SSQDm at 5A g-1 is shown in Figure 6i. The capacity is still 97 mAh g-1 after 1000 cycles with a high coulombic efficiency of 99.8%. The ZnS layer out of ZnO crystal is able to buffer the volume change during lithiation and delithiation, and the performance in lithium ion storage is comparable with the published works30, 33, 37.

Figure 8 EIS of ZnO@CC/SSQDm and the fitted results for the (a) 12th and (b) 500th cycle. The inset shows the relevant equivalent circuit. The impedance change of the as-prepared ZnO@CC/SSQDm anode materials with cycling was monitored using Electrochemical Impedance Spectroscopy (EIS). Figures 8(a) and (b) depict the Nyquist plots for ZnO@CC/SSQDm electrodes cycled 12 and 500 times. The equivalent circuits employed to fit the experimental data are shown as insets. In both equivalent circuits, R1 represents the purely Ohmic internal resistance of the cell that results from the electrode and electrolyte. CPE1 (constant phase element) is the pseudocapacitance of the porous electrode. R2 represents the charge transfer resistance and W1 is a Warburg component arising from the solid-state diffusion of Li ions into the bulk. Long-term cycling, 500 cycles, produces R3 in Figure 8(b), which is the surface resistance attributed to the thickening solid electrolyte interphase (SEI) film on the electrode38-40, and C1, the capacitor in the bulk associated with Li+ ions insertion. The values of the components that yielded the best fit to the experimental data are shown in Figures 8a and 8b, with values, errors listed in Table S2 and S3. For both ZnO@CC/SSQDm and ZnO@C550, shown in Figure S15-16, the charge transfer resistance, R2, is found to decrease after 500 cycles, pointing to the facile insertion/desertion reaction of lithium ions through an enhanced electrochemical interface of the electrode with cycling. The smaller R2 value for ZnO@CC/SSQDm, in comparison to that of ZnO@C550,

Figure 7 The dCapacity/dVoltage vs. V curve calculated from the galvanostatic charge/discharge curves at 200 mA g-1 of C550, ZnO@C550, ZnO@CC and ZnO@CC/SSQDm. The differential capacity, d(Capacity)/d(Voltage) against Voltage curves of C550, ZnO@C550, ZnO@CC and

9

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 12

5. Yang, S. J.; Nam, S.; Kim, T.; Im, J. H.; Jung, H.; Kang, J. H.; Wi, S.; Park, B.; Park, C. R., Preparation and Exceptional Lithium Anodic Performance of Porous Carbon-coated ZnO Quantum Dots Derived from a Metalorganic Framework. J. Am. Chem. Soc. 2013, 135 (20), 7394-7397. 6. Kim, J.; Dolgos, M. R.; Lear, B. J., Isolation and Chemical Transformations Involving a Reactive Intermediate of MOF-5. Cryst. Growth Des. 2015, 15 (10), 4781-4786. 7. Huang, L.; Wang, H.; Chen, J.; Wang, Z.; Sun, J.; Zhao, D.; Yan, Y., Synthesis, Morphology Control, and Properties of Porous Metal–organic Coordination Polymers. Microporous Mesoporous Mater. 2003, 58 (2), 105-114. 8. Hafizovic, J.; Bjørgen, M.; Olsbye, U.; Dietzel, P. D. C.; Bordiga, S.; Prestipino, C.; Lamberti, C.; Lillerud, K. P., The Inconsistency in Adsorption Properties and Powder XRD Data of MOF-5 Is Rationalized by Framework Interpenetration and the Presence of Organic and Inorganic Species in the Nanocavities. J. Am. Chem. Soc. 2007, 129 (12), 3612-3620. 9. Lu, L.; Li, X.-Y.; Liu, X.-Q.; Wang, Z.-M.; Sun, L.-B., Enhancing the Hydrostability and Catalytic Performance of Metal-organic Frameworks by Hybridizing with Attapulgite, a Natural Clay. J. Mater. Chem. A 2015, 3 (13), 6998-7005. 10. Wu, C.-M.; Rathi, M.; Ahrenkiel, S. P.; Koodali, R. T.; Wang, Z., Facile Synthesis of MOF-5 Confined in SBA-15 Hybrid Material with Enhanced Hydrostability. Chem. Commun. 2013, 49 (12), 1223-1225. 11. Chen, B.; Wang, X.; Zhang, Q.; Xi, X.; Cai, J.; Qi, H.; Shi, S.; Wang, J.; Yuan, D.; Fang, M., Synthesis and Characterization of the Interpenetrated MOF-5. J. Mater. Chem. 2010, 20 (18), 3758-3767. 12. Xie, Q.; Ma, Y.; Wang, X.; Zeng, D.; Wang, L.; Mai, L.; Peng, D.-L., Electrostatic Assembly of Sandwichlike Ag-C@ZnO-C@Ag-C Hybrid Hollow Microspheres with Excellent High-Rate Lithium Storage Properties. ACS Nano 2016, 10 (1), 1283-1291. 13. Wang, Y.; Jiang, X.; Yang, L.; Jia, N.; Ding, Y., In Situ Synthesis of C/Cu/ZnO Porous Hybrids as Anode Materials for Lithium Ion Batteries. ACS Appl. Mater. Interfaces 2014, 6 (3), 1525-1532. 14. Fu, Y.; Zhang, Z.; Yang, X.; Gan, Y.; Chen, W., ZnS Nanoparticles Embedded in Porous Carbon Matrices as Anode Materials for Lithium Ion Batteries. RSC. Adv. 2015, 5 (106), 86941-86944. 15. Yan, H.; Li, T.; Lu, Y.; Cheng, J.; Peng, T.; Xu, J.; Yang, L.; Hua, X.; Liu, Y.; Luo, Y., Template-free Synthesis of Ordered ZnO@ZnS Core-shell Arrays for High Performance Supercapacitors. Dalton Trans. 2016, 45 (44), 17980-17986. 16. Zheng, Y.; Zhou, T.; Zhao, X.; Pang, W. K.; Gao, H.; Li, S.; Zhou, Z.; Liu, H.; Guo, Z., Atomic Interface Engineering and Electric-Field Effect in Ultrathin Bi2MoO6 Nanosheets for Superior Lithium Ion Storage. Adv. Mater. 2017, 29 (26), 1700396(1)-1700396(8).

confirms the improved conductivity, indicating a conductive network of Ag nanoparticles (Scheme 1).

Conclusions It has been demonstrated that introduction of silver sulfide nanoparticles into a carbon/nano-ZnO matrix, formed by the decomposition of distorted MOF-5, and the subsequent heat treatment of the composite significantly enhances the performance of the material as an anode in a lithium ion battery. At low current densities (200 mA g-1), treatment of ZnO@C with Ag2S QDs results in a 38% improvement in the specific capacity. High-rate and cycling performance are also improved remarkably compared with untreated samples. Characterization of the composite and analysis of its performance as an anode material points to improved connectivity and electron transport as a result of incorporation of Ag nanoparticles in the matrix and improved cyclability due to the partial sulfidation of the surface of the material. The methodology has the potential to be used with other carbon-metal oxide composites to improve their performance in energy storage applications.

ASSOCIATED CONTENT Supporting Information. More characterization results.

AUTHOR INFORMATION Corresponding Author [email protected] (Jason Riley)

Notes The authors declare no competing interests.

ACKNOWLEDGMENT We thank the President's Ph.D. Scholarship of Imperial College London, the Engineering and Physical Sciences Research Council (EPSRC, Grant: EP/L015277/1) and STFC Futures Early Career Award for financial support.

REFERENCES 1. Mahmood, N.; Tang, T.; Hou, Y., Nanostructured Anode Materials for Lithium Ion Batteries: Progress, Challenge and Perspective. Adv. Energy Mater. 2016, 6 (17), 1600374(1)-1600374(22). 2. Xi, K.; Cao, S.; Peng, X.; Ducati, C.; Kumar, R. V.; Cheetham, A. K., Carbon with Hierarchical Pores from Carbonized Metal-organic Frameworks for Lithium Sulphur Batteries. Chem. Commun. 2013, 49 (22), 21922194. 3. Lu, Y.; Zhan, W.; He, Y.; Wang, Y.; Kong, X.; Kuang, Q.; Xie, Z.; Zheng, L., MOF-templated Synthesis of Porous Co3O4 Concave Nanocubes with High Specific Surface Area and Their Gas Sensing Properties. ACS Appl. Mater. Interfaces 2014, 6 (6), 4186-4195. 4. Luz, I.; Loiudice, A.; Sun, D. T.; Queen, W. L.; Buonsanti, R., Understanding the Formation Mechanism of Metal Nanocrystal@MOF-74 Hybrids. Chem. Mater. 2016, 28 (11), 3839-3849.

10

ACS Paragon Plus Environment

Page 11 of 12

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

17. Zheng, Y.; Zhou, T.; Zhang, C.; Mao, J.; Liu, H.; Guo, Z., Boosted Charge Transfer in SnS/SnO2 Heterostructures: Toward High Rate Capability for Sodium-Ion Batteries. Angew. Chem., Int. Ed. 2016, 55 (10), 3408-3413. 18. Zhang, Y.; Liu, Y.; Li, C.; Chen, X.; Wang, Q., Controlled Synthesis of Ag2S Quantum Dots and Experimental Determination of the Exciton Bohr Radius. J. Phys. Chem. C 2014, 118 (9), 4918-4923. 19. Zhang, Y.; Hong, G.; Zhang, Y.; Chen, G.; Li, F.; Dai, H.; Wang, Q., Ag2S Quantum Dot: A Bright and Biocompatible Fluorescent Nanoprobe in the Second NearInfrared Window. ACS Nano 2012, 6 (5), 3695-3702. 20. Li, H.; Eddaoudi, M.; O'Keeffe, M.; Yaghi, O. M., Design and Synthesis of an Exceptionally Stable and Highly Porous Metal-organic Framework. Nature 1999, 402 (6759), 276-279. 21. Yaghi, O. M.; O'Keeffe, M.; Ockwig, N. W.; Chae, H. K.; Eddaoudi, M.; Kim, J., Reticular Synthesis and the Design of New Materials. Nature 2003, 423 (6941), 705714. 22. Liu, D.; Purewal, J. J.; Yang, J.; Sudik, A.; Maurer, S.; Mueller, U.; Ni, J.; Siegel, D. J., MOF-5 Composites Exhibiting Improved Thermal Conductivity. Int. J. Hydrogen Energy 2012, 37 (7), 6109-6117. 23. Liu, H.; Li, W.; Shen, D.; Zhao, D.; Wang, G., Graphitic Carbon Conformal Coating of Mesoporous TiO2 Hollow Spheres for High-Performance Lithium Ion Battery Anodes. J. Am. Chem. Soc. 2015, 137 (40), 13161-13166. 24. Cuscó, R.; Alarcón-Lladó, E.; Ibáñez, J.; Artús, L.; Jiménez, J.; Wang, B.; Callahan, M. J., Temperature Dependence of Raman Scattering in ZnO. Phys. Rev. B 2007, 75 (16), 165202(1)-165202(11). 25. Zeng, Y.; Zhang, T.; Wang, L.; Wang, R.; Fu, W.; Yang, H., Synthesis and Ethanol Sensing Properties of Self-Assembled Monocrystalline ZnO Nanorod Bundles by Poly(ethylene glycol)-Assisted Hydrothermal Process. J. Phys. Chem. C 2009, 113 (9), 3442-3448. 26. Lee, K. T.; Ji, X.; Rault, M.; Nazar, L. F., Simple Synthesis of Graphitic Ordered Mesoporous Carbon Materials by a Solid-state Method Using Metal Phthalocyanines. Angew. Chem., Int. Ed. 2009, 48 (31), 5661-5665. 27. Gaarenstroom, S. W.; Winograd, N., Initial and final state effects in the ESCA spectra of cadmium and silver oxides. J. Chem. Phys. 1977, 67 (8), 3500-3506. 28. Chen, C.; Li, Z.; Lin, H.; Wang, G.; Liao, J.; Li, M.; Lv, S.; Li, W., Enhanced Visible Light Photocatalytic Performance of ZnO Nanowires Integrated with CdS and Ag2S. Dalton Trans. 2016, 45 (9), 3750-3758. 29. Barreca, D.; Gasparotto, A.; Maragno, C.; Tondello, E.; Spalding, T. R., Analysis of Nanocrystalline ZnS Thin Films by XPS. Surf. Sci. Spectra 2002, 9 (1), 5461.

30. Ahmad, M.; Yingying, S.; Nisar, A.; Sun, H.; Shen, W.; Wei, M.; Zhu, J., Synthesis of Hierarchical Flower-like ZnO Nanostructures and Their Functionalization by Au Nanoparticles for Improved Photocatalytic and High Performance Li-ion Battery Anodes. J. Mater. Chem. 2011, 21 (21), 7723-7729. 31. Liao, H.-C.; Kuo, P.-C.; Lin, C.-C.; Chen, S.-Y., Synthesis and Optical Properties of ZnO–ZnS Core-shell Nanotube Arrays. J. Vac. Sci. Technol. B 2006, 24 (5), 2198-2201. 32. Shilpa; Basavaraja, B. M.; Majumder, S. B.; Sharma, A., Electrospun Hollow Glassy Carbon-reduced Graphene Oxide Nanofibers with Encapsulated ZnO Nanoparticles: a Free Standing Anode for Li-ion Batteries. J. Mater. Chem. A 2015, 3 (10), 5344-5351. 33. Sun, X.; Zhou, C.; Xie, M.; Sun, H.; Hu, T.; Lu, F.; Scott, S. M.; George, S. M.; Lian, J., Synthesis of ZnO Quantum Dot/Graphene Nanocomposites by Atomic Layer Deposition with High Lithium Storage Capacity. J. Mater. Chem. A 2014, 2 (20), 7319-7326. 34. Chen, C.; Wen, Y.; Hu, X.; Ji, X.; Yan, M.; Mai, L.; Hu, P.; Shan, B.; Huang, Y., Na+ Intercalation Pseudocapacitance in Graphene-coupled Titanium Oxide Enabling Ultra-fast Sodium Storage and Long-term Cycling. Nat. Commun. 2015, 6 (6929), 1-8. 35. Song, W.; Cao, X.; Wu, Z.; Chen, J.; Zhu, Y.; Hou, H.; Lan, Q.; Ji, X., Investigation of the Sodium Ion Pathway and Cathode Behavior in Na3V2(PO4)2F3 Combined via a First Principles Calculation. Langmuir 2014, 30 (41), 12438-12446. 36. Song, W. X.; Ji, X. B.; Wu, Z. P.; Zhu, Y. R.; Yao, Y. P.; Huangfu, K.; Chen, Q. Y.; Banks, C. E., Na2FePO4F Cathode Utilized in Hybrid-ion Batteries: a Mechanistic Exploration of Ion Migration and Diffusion Capability. J. Mater. Chem. A 2014, 2 (8), 2571-2577. 37. Liu, J.; Li, Y.; Ding, R.; Jiang, J.; Hu, Y.; Ji, X.; Chi, Q.; Zhu, Z.; Huang, X., Carbon/ZnO Nanorod Array Electrode with Significantly Improved Lithium Storage Capability. J. Phys. Chem. C 2009, 113 (20), 9008-9008. 38. Wu, Q.; Xu, J.; Yang, X.; Lu, F.; He, S.; Yang, J.; Fan, H. J.; Wu, M., Ultrathin Anatase TiO2 Nanosheets Embedded with TiO2-B Nanodomains for Lithium-Ion Storage: Capacity Enhancement by Phase Boundaries. Adv. Energy Mater. 2015, 5 (7), 1401756(1)-1401756(9). 39. Song, W.; Chen, J.; Ji, X.; Zhang, X.; Xie, F.; Riley, D. J., Dandelion-shaped TiO2/Multi-layer Graphene Composed of TiO2(B) Fibrils and Anatase TiO2 Pappi Utilizing Triphase Boundaries for Lithium Storage. J. Mater. Chem. A 2016, 4 (22), 8762-8768. 40. Cheng, X.-B.; Zhang, Q., Dendrite-free Lithium Metal Anodes: Stable Solid Electrolyte Interphases for High-efficiency Batteries. J. Mater. Chem. A 2015, 3 (14), 7207-7209.

11

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

Page 12 of 12

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60 ACS Paragon Plus Environment