Exceptionally Stable and 20-connected ... - ACS Publications

efficient catalytic systems for selective capture and conversion of CO2 into useful chemicals has .... Single crystal X-ray structural data of MOF1 an...
2 downloads 11 Views 1MB Size
Subscriber access provided by University of Florida | Smathers Libraries

Exceptionally stable and 20-connected lanthanide metalorganic frameworks (MOFs) for selective CO2 capture and conversion to cyclic carbonates at atmospheric pressure Bharat Ugale, Sandeep Singh Dhankhar, and C. M. Nagaraja Cryst. Growth Des., Just Accepted Manuscript • DOI: 10.1021/acs.cgd.8b00065 • Publication Date (Web): 14 Mar 2018 Downloaded from http://pubs.acs.org on March 15, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

Exceptionally Stable and 20-connected Lanthanide Metal-Organic Frameworks for Selective CO2 Capture and Conversion at Atmospheric Pressure Bharat Ugale, Sandeep Singh Dhankhar and C. M. Nagaraja* Department of Chemistry, Indian Institute of Technology Ropar, Nangal Road, Rupnagar140001, Punjab, India. Tel: 91- 1881-242229. Email: [email protected]

ABSTRACT Highly thermal and chemical stable, 20-connected lanthanide MOFs, [{Ln(BTB)(H2O)}.H2O]n (where, Ln = Sm (MOF1)/Gd (MOF2), BTB = 1,3,5-tris (4-carboxy phenyl) benzene) have been synthesized solvothermally and characterized by single-crystal X-ray diffraction analysis and other physicochemical methods. MOF1 and 2 are isostructural and feature 3D honeycomb-like structure with large 1D hexagonal channels of dimension ~10.20 X 10.11 Å2. Gas uptake studies of the samples revealed selective adsorption properties of MOF1 for CO2 over other (N2, Ar, and H2) gases. The activated samples of the MOF1/2 act as efficient recyclable catalysts for heterogeneous cycloaddition of CO2 with styrene oxide resulting in cyclic carbonate with high yield and selectivity. Interestingly, the pore size-dependent catalytic conversion of epoxides has been observed suggesting the potential utility of MOF1 as promising heterogeneous catalyst for cycloaddition of carbon dioxide. Furthermore, the MOF1 catalyst can be easily recycled for several cycles without significant loss of catalytic activity as well as structural rigidity. The MOF1 and 2 represent rare examples of 20-c lanthanide MOFs exhibiting selective capture and efficient cycloaddition of CO2 with epoxides at mild conditions.

Keywords: Metal-organic frameworks, CO2 conversion, Epoxides, Heterogeneous catalysis, Atmospheric pressure 1

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Introduction Carbon dioxide (CO2) has attracted considerable attention not only as a greenhouse gas but also as an abundant C1 building block for organic transformations due to its free availability, non-toxicity and renewability.1 Therefore, intensive research efforts are being made by researchers worldwide for its efficient conversion to value-added chemicals.2-5 However, the thermodynamic stability and kinetic inertness of CO2 are the major limitations for its conversion at mild conditions. Hence, development of efficient catalytic systems for selective capture and conversion of CO2 into useful chemicals has gained significant importance. In this regard, cycloaddition of CO2 to epoxides represents one of the most promising methods for generation of cyclic carbonates.6-8 Further, cyclic carbonates offer widespread applications and they are industrially manufactured using highly toxic phosgene. Thus, it is highly desirable to develop alternative green routes for the synthesis of cyclic carbonates. Various homogeneous catalysts such as transition-metal complexes,9-15 ionic liquids,16 organocatalysts,17,18 and quaternary ammonium or phosphonium salts,19-22 etc., have been employed for catalytic cycloaddition of CO2 with epoxides to generate cyclic carbonates. However, these systems suffer from the limitations of catalyst recycling and separation of the product. Whereas, heterogeneous catalysts, such as, metal oxides,23 zeolites24 and functional polymers25-30 have also been developed for the catalytic conversion of CO2. However, these reactions often require high pressure of CO2 and/or high activation temperatures. On other hand, porous metal-organic frameworks or coordination polymers have emerged as promising candidate materials for selective capture of CO2.31-41 Further, MOFs are also known to act as heterogeneous catalysts for conversion of CO2 to cyclic carbonates.42-51 Moreover, few MOFs are known to exhibit both selective capture and conversion of CO2.52-64 However, limited number of

2

ACS Paragon Plus Environment

Page 2 of 30

Page 3 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

MOFs are known for efficient conversion of CO2 at mild conditions of atmospheric pressure and low loading of co-catalyst.65-69 Furthermore, MOFs based on polynuclear metal clusters with low-connected networks, such as, 3-, 4- and 6-connected topologies have been extensively studied. Whereas, the number of examples of highly-connected networks are relatively less.70 In this regard, MOFs based on lanthanides have gained special interest due to their rich coordination geometry, high stability, ability to form highly connected networks and interesting properties.71-76 Recently, the construction of Ln-MOFs with 12-,77 15-78 and 18-c79 metal clusters have been reported. However, the examples of highly connected (>18-c) LnMOFs based on the uni-nodal cluster are rare. Herein, we report synthesis of two new isostructural, 20-connected, lanthanide MOFs, [{Ln(BTB)(H2O)}.H2O]n (where, Ln=Sm(MOF1)/Gd(MOF2)) solvothermally at 100oC using 1,3,5tris(4-carboxyphenyl)benzoic acid (BTB) as a triangular tricarboxylate ligand. The X-ray structural analysis revealed that MOF1 and 2 exhibit an interesting 3D Honeycomb-like structure with 20-c, uninodal {3^78.4^106.5^6}-net topology. Further, the MOFs exhibit exceptionally high thermal and chemical stability and possess high surface area. Interestingly, MOF1/2 act as efficient recyclable catalysts for heterogeneous cycloaddition of CO2 with epoxides resulting cyclic carbonates with high yield and selectivity. Therefore, MOF1 and 2 represent the rare examples of 20-c lanthanide MOFs exhibiting selective capture and conversion of CO2 at mild conditions. Experimental Section Materials and Methods All the reagents used in this work were commercially available and used as received without any further purification. Sm(NO3)3.6H2O, Gd(NO3)3.6H2O and Ce(NO3)3.6H2O were purchased from Sigma Aldrich chemical Co. 1,3,5-tris (4-carboxyphenyl) benzene (H3BTB) was purchased from Alfa 3

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 30

Aesar Co. All the reagents and the internal standard used for catalytic reactions were purchased from TCI chemicals and used without further purification. Thermogravimetric analysis (TGA) of the MOFs was carried out using Metler Toledo Thermogravimetric analyzer in N2 atmosphere with a flow rate of 30 mL/min in the temperature range of 30–1000 °C and a heating rate of 10 °C/min. Powder XRD measurements were carried out on PANalytical’s X’PERT PRO diffractometer with Cu Kα radiation (λ = 1.54184 Å; 40 kV, 20 mA). Elemental analysis of the samples was carried out on Thermo Fischer Flash 2000 Elemental Analyzer. FTIR (Fourier transform infrared) spectra of the samples were recorded from 650 to 4000 cm-1 on a Perkin Elmer ATR-FTIR spectrometer. The products of catalytic reactions were identified and the catalytic conversions were determined using 1H NMR spectra recorded in CDCl3 on JEOL JNM-ECS400 spectrometer operating at a frequency of 400 MHz. Synthesis of [{Sm(BTB)(H2O)}.H2O]n (MOF1) MOF1 was prepared by employing solvothermal conditions at temperature of 100 °C. To a 4 ml DMF solution of H3BTB (0.044 g, 0.10 mmol) taken in a glass vial (30 ml), an aqueous solution (2 ml) of Sm(NO3)3.6H2O (0.045 g, 0.1 mmol) was added dropwise with constant stirring. The contents were stirred for 30 min and then transferred to a 23 ml Teflon lined stainless steel autoclave and heated at 100

o

C

for

72

h

and

cooled

naturally.

The

colorless

needle-shaped

crystals

of

[{Sm(BTB)(H2O)}.H2O]n (1) were obtained. Yield: 88 %. The phase purity of the as-synthesized MOF1 was confirmed from powder X-ray diffraction pattern (Figure S1). Anal. calcd. For C27H19O8Sm: C, 52.15; H, 3.08. Found: C, 51.83; H, 3.22. IR (cm-1): 3374, 3012, 2980, 1580, 1507, 1408, 1187, 1016, 849, 780, 701 (Figure S2). As-prepared MOF1 was activated at 220oC under vacuum for 20 h prior to gas adsorption and catalytic studies. The phase purity of the activated sample

4

ACS Paragon Plus Environment

Page 5 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

was confirmed from powder XRD pattern (Figure S1). Anal. calcd. for C27H15O6Sm: C, 55.36; H, 2.58. Found: C, 54.93; H, 2.63. IR (cm-1): 2980, 2910, 1582, 1508, 1408, 1186, 1017, 849, 816, 781, 702 (Figure S2). Synthesis of [{Gd(BTB)(H2O)}.H2O]n (MOF2) MOF2 was prepared following the procedure similar to that of MOF1. Here, Gd(NO3)3.6H2O (0.046 g, 0.1 mmol) was used in place of Sm(NO3)3.6H2O. The colorless needle-shaped crystals of MOF2 was isolated. Yield: 87 %. The phase purity of the as-synthesized sample was confirmed by powder Xray diffraction pattern (Figure S3) Anal. calcd. for C27H19O8Gd: C, 51.58; H, 3.05. Found: C, 52.05; H, 3.21. IR (cm-1): 3359, 3014, 2980, 1655, 1579, 1511, 1407, 1276, 1184, 1105, 1016, 854, 815, 779, 703, 672 (Figure S2). As-prepared MOF2 was activated at 220 oC under vacuum for 20 h prior to gas adsorption and catalytic studies. The phase purity of the sample was confirmed from powder XRD pattern (Figure S3). Anal. calcd. for C27H15O6Gd: C, 54.72; H, 2.55. Found: C, 54.86; H, 2.47. IR (cm1

): 3007, 2970, 1609, 1582, 1530, 1505, 1381, 1275, 1181, 847, 815, 778, 764, 750, 671 (Figure S2).

For the sake of comparison of catalytic activity, an isostructural Ce-MOF was synthesized following procedure similar to that of MOF1 and characterized (Supporting Information File, Figure S4). X-ray Crystallography Single crystal X-ray structural data of MOF1 and 2 were collected on a CMOS based Bruker D8 Venture PHOTON 100 diffractometer equipped with an INCOATEC micro-focus source with graphite monochromated Mo Kα radiation (λ = 0.71073 Å) operating at 50 kV and 30 mA. The SAINT80 program was used for integration of diffraction profiles and absorption correction was made with SADABS program.81 The structures were initially solved by SIR 9282 and refined by full matrix least square method using SHELXL-201383 and WinGX system, Ver 2013.3.84 The nonhydrogen atoms in 5

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

both the structures were located from the difference Fourier map and refined anisotropically. All the hydrogen atoms were fixed by HFIX and placed in ideal positions and included in the refinement process using riding model with isotropic thermal parameters. The disordered guest solvent molecules in MOFs1 and 2 were treated with SQUEEZE option of PLATON85 multipurpose crystallographic software. The molecular formula of MOF1 and 2 was determined based on the elemental analyses and TGA. The potential solvent accessible void space was calculated using the PLATON85 software. All the crystallographic and structure refinement data of the MOFs1-2 are summarized in Table 1. Selected bond lengths, angles and hydrogen bond details are summarized in Tables S1-S2, respectively. The crystallographic information files are deposited with the CCDC numbers 1555305 and 1555306 for MOFs 1 and 2, respectively. Gas adsorption measurements N2 adsorption-desorption measurements were carried out at 77 and 273K, whereas, CO2 adsorptiondesorption measurements were carried out at 273, 298 and 195K using QUANTACHROME Quadrasorb-SI automated surface area and pore size analyzer. For selectivity study, adsorption of H2 and Ar were carried out at 273K. Ultrapure (99.995%) N2, He, H2, Ar and CO2 gases were used for the adsorption-desorption measurements. Prior to adsorption measurements, the samples (~ 100 mg) were evacuated at 493 K under vacuum (20 mTorr) for 20 h using QUANTACHROME Flovac degasser and further purged with ultrapure N2 (99.995%) gas on cooling. Then the degassed sample was introduced to the instrument and all the further operations were computer controlled. The Brunauer−Emmett−Teller (BET) surface area was estimated from N2 sorption isotherms carried out at 77K. The temperature, 77 K was achieved using liquid N2 and 273 and 298K were achieved using a chiller with an ethylene glycol-water mixture (1:1) as a coolant. The gas selectivity studies were carried out at 273K. Dead volume of the sample cell was measured using Helium gas (99.995%). 6

ACS Paragon Plus Environment

Page 6 of 30

Page 7 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

Catalytic cycloaddition reactions of CO2 The catalytic cycloaddition reactions of CO2 with epoxides were carried out in a 50 ml stainless steel reactor at 1 atm pressure of CO2. Prior to catalytic reactions, the MOFs were activated at 493 K for 20 h under vacuum to remove the guest and metal-coordinated water molecules. All the reactants/reagents were added at room temperature and the reactor was pressurized with CO2, flushed twice and then the required pressure (1bar) was attained. The reagent, 1,2-epoxypropane was handled at low temperature due to its low boiling point. The reaction mixture was stirred at 1000 rpm for 15h. After the catalytic reactions, the pressure was released slowly and the catalyst was separated by filtration and the catalytic conversion was determined by 1H NMR spectroscopy. The recovered catalyst after the catalytic reaction was washed with water and methanol three times, dried at r.t. and then at 493 K for 20 h under vacuum and reused for successive cycles. Results and discussion Synthesis and crystal structure The reaction of Ln(NO3)3.6H2O (Ln = Sm/Gd) with H3BTB in a mixture of DMF:H2O in 2:1 ratio at 100oC afforded the MOFs, [{Ln(BTB)(H2O)}.H2O]n (Ln = Sm (MOF1)/Gd(MOF2)). Single crystal Xray structural determination revealed that MOF1 and 2 are isostructural to the analogues Ln-MOFs (Ln = La, Tb and Eu) reported by the research groups of Ferey and Kitagawa.86-88 Both MOF1/2 crystallize in Trigonal system with non-centrosymmetric R32 space group (Table 1). The asymmetric unit contains a Sm3+/Gd3+ ion in MOF 1/2, a BTB3- ligand and a coordinated water molecule along with a solvent water molecule of crystallization (Figure 1a and b). The Sm1/Gd1 ions are in a tricapped trigonal prismatic geometry with SmO9/GdO9 chromophore satisfied by eight carboxylate oxygen atoms from three BTB3- ligands and an oxygen from coordinated water molecule (Figure 1). These

7

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

[LnO9] secondary building units (SBUs) are extended as 1D chain along the crystallographic c-axis (Figure 1c).

Figure 1. The asymmetric unit of MOF1 (a) and MOF2 (b) (insets: coordination environment of Sm3+/Gd3+ in MOF1/2, the hydrogen atoms and solvent molecules are omitted for clarity (c) [SmO9] SBUs in MOF1 forming a 1D chain along the crystallographic c-axis.

Further, the [LnO9] SBUs are further connected by three tritopic BTB3- ligands resulting in a 20-c Sm1/Gd1 node (Figure. 2a-b and Figure S5) which are extended in three dimensions to generate a 3D Honeycomb-like framework with 1D hexagonal channels of dimension ~10.20 X 10.11 Å2 (Figure 2c). Topological analysis by TOPOS89 suggests that the Sm/Gd center acts as a 20-c node and the overall structure has {3^78.4^106.5^6}-net topology (Figure 2d). The 3D frameworks possess void volume of

8

ACS Paragon Plus Environment

Page 8 of 30

Page 9 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

~47.5 and ~49.6 % per unit cell for MOF1 and 2 respectively, calculated using PLATON85 after removal of guest water molecules. The selected bond lengths and angles are summarized in Table S1 and S2.

Figure 2. (a) View of the 20-connected Sm3+/Gd3+ node (central polyhedron shown in magenta color). (b) A simplified view of 20-c, Sm/Gd center. (c) View of 3D honeycomb-like framework with 1D channels. (d) Topological representation of the 3D framework in MOF1 and 2.

Chemical and Thermal Stability of MOF1/2 Interestingly, the as-synthesized MOFs were found to exhibit high chemical and thermal stability and such MOFs are beneficial for large-scale industrial applications. To test the chemical stability,

9

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

MOF1 was soaked in different organic solvents (ranging from highly protic to aprotic) with vigorous stirring for 48h and then the solids were recovered by filtration washed thoroughly before recording their powder XRD patterns (Figure S6). The water stability was tested at various pH conditions in which MOF1 was stirred in aqueous acidic (pH = 2 to 6) and basic (pH = 8 to 12) solutions for 48h. The powder XRD patterns of the recovered samples of MOF1 indicate retaining of the original framework structure (Figure S6 and S7) suggesting their high chemical and water stability. This unusual behavior could be originating due to the rigidity of the framework constituted by highly connected Sm3+/Gd3+ ions and the close stacking of aromatic rings of BTB ligand providing a hydrophobic surface. Thermogravimetric analysis of the MOFs revealed loss of coordinated water molecules in the temperature range of 100-120°C and the dehydrated frameworks of MOF1 and 2 were found to be stable up to 600°C, suggesting their high thermal stability with retaining of the original framework structure. Further, to test the regeneration of the MOFs, the activated MOFs were soaked in water for 4h and the isolated samples were analyzed by TGA and powder XRD measurements. TGA of the resolvated samples showed weight loss corresponding to coordinated water molecules (Figure S8). In addition, powder XRD patterns of the resolvated samples are in good agreement with the assynthesized samples indicating regeneration of the original structure (Figure S9). Interestingly, the TGA of the isostructural MOFs, MIL-103(Ln) (Ln = Ce, Tb) carried out under N2 and O2 gas flow show an interesting difference in thermal stabilities. There is an increase in stability of about 200°C observed when carried out under N2 atmosphere compared to those carried out under O2 atmosphere. The relatively lower stability of the MOFs under O2 atmosphere has been attributed to the redox character of the MOFs.

10

ACS Paragon Plus Environment

Page 10 of 30

Page 11 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

Gas adsorption study N2 adsorption-desorption measurements of the activated samples of MOF1 and 2 revealed a typical type-I isotherm with a steep uptake at low-pressure region, supporting their microporous nature (Figure S10). The estimated value of Brunauer-Emmett-Teller (BET) surface area for MOF1 and 2 were 946.74 and 834.26 m2/g, respectively, which are in accordance with the surface area reported for isostructural MOFs reported by Kitagawa and co-workers.88 Further, N2 adsorption measurements of MOF1 recovered after chemical treatment showed type-I behavior similar to that of pristine MOF suggesting retaining of micro-porosity (Figure S11). Further, the pore size distribution for MOF1 and 2 calculated from the N2 adsorption isotherms was found to be 10.2 Å (inset of Figure S10) and is consistent with the pore diameter observed from the crystal structure. Furthermore, CO2 adsorption isotherms of MOF1 and 2 carried out at 273K and 1 atm pressure follow a typical type-I profile with the volumetric uptake of 1.29 and 1.87mmol/g, respectively (Figure 3a and S12). While, at 195K, MOF1 and 2 show steep uptake of CO2 at lowpressure range with the volumetric uptake of 9.12 and 8.89 mmol/g respectively, confirming the inherent permanent porosity. The observed CO2 uptake by MOF1 and 2 are comparable to the analogues La-MOF reported by Ferey and coworkers.87 The adsorption branches of the isotherms carried out at 273 and 298 K were fitted to Freundlich−Langmuir equation90 (Figure S13 and S14) to obtain a precise prediction over the quantity of CO2 adsorbed at saturation point. The estimated values of isosteric heat of adsorption (Qst) for MOF 1 and 2 were found to be 21.6 and 24.5 kJ/mol, respectively (Figure S15 and S16), calculated using the Clausius-Clapeyron equation.91, 92

11

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 3. (a) CO2 adsorption-desorption isotherms carried out at 195, 273 and 298K for MOF1. (b) Adsorption-desorption isotherms of MOF1 for different adsorbates (CO2, H2, Ar, N2) at 273K showing selective adsorption for CO2. Interestingly, the gas adsorption studies of MOF1 for other gases (N2, H2 and Ar) showed negligible uptake of 0.20, 0.18 and 0.09 mmol/g for Ar, N2 and H2, respectively (Figure 3b) indicating the selective adsorption property of MOF1 for CO2 over other gases. The observed selectivity for CO2 can be attributed due to its significant quadrupole moment (-1.4 X 10-39Cm2) and polarizability over other gases leading to its stronger interaction with the unsaturated Sm3+ ions lined in the 1D channels of MOF1. Literature survey revealed that, the observed CO2 uptake by MOF1 is not significantly high in comparison to the well-known MOFs reported in literature.31-41 However, the uptake is comparable amongst the lanthanide MOFs, known for CO2 storage (Table S3).

Catalytic cycloaddition of CO2 with epoxides As it can be seen in Figure 2, the hexagonal channels of MOF1 and 2 are decorated with Sm3+ and Gd3+ ions, respectively. Upon activation, the coordinated water molecule on the lanthanide ion can be reversibly removed to obtain framework composed of unsaturated, Lewis acidic lanthanide centers 12

ACS Paragon Plus Environment

Page 12 of 30

Page 13 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

which can act as potential catalytic sites for acid catalyzed organic transformations. Motivated by the high thermal stability and selective CO2 capture properties of the MOF1 and 2, we envisioned that the activated MOFs can act as efficient heterogeneous catalysts for cycloaddition of CO2. Therefore, the catalytic activity of MOF1 and 2 was investigated for cycloaddition of CO2 and styrene oxide as a model substrate (epoxide) at mild conditions of 1 atm of CO2 and in presence of 1 mol% TBAB as cocatalyst. Interestingly, the catalytic results showed the formation of the corresponding cyclic carbonate with about 93% conversion in 15h (Table S4). Further, controlled experiments revealed that both catalyst (MOF1/2) and TBAB are essential for the catalytic activity. It is known that TBAB acts as a nucleophilic co-catalyst and facilitates the ring opening of the epoxides.93-95 For high catalytic activity, the synergistic effect between the catalyst (MOF) and TBAB is essential. Further, the progress of the catalytic reaction can be easily monitored by recording the 1H NMR spectra of the aliquots taken at regular time intervals with reference to an internal standard (1,1′,2,2′-tetrachloroethane). Remarkably, 100% selectivity for cyclic carbonates was observed with no additional by-products (Figure S17). For the sake of comparison, a Ce-MOF isostructural to MOF1/2 was synthesized and its catalytic activity was studied at similar conditions mentioned before.86 The catalytic investigation revealed that CeMOF catalyzes the cycloaddition of CO2 with styrene oxide to corresponding cyclic carbonate with high yield (98%) reltively higher than those of MOF1 and 2 (Table S4, Figure S18). The scope of the reaction was further extended to cycloaddition of CO2 with alkyl epoxides with increasing alkyl chain length and using MOF1 as the catalyst (Table 2).

13

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 30

Table 2. Cycloaddition of various substituted epoxides catalyzed by MOF1

S. No.

Substrate

Conversion[a]

Catalyst

TON[a]

(%)

[R]

TOF[a] (h-1)

1

MOF1

100

196

13.07

2

MOF1

>99

194

12.93

3

MOF1

>98

194

12.93

4

MOF1

90.1

177

11.80

5

MOF1

92.7

182

12.13

Reaction conditions: epoxide (20 mmol), Catalyst:TBAB (0.5 : 1.0 mol%), temperature of 80°C. [a]

Conversion: the catalytic conversions were determined by 1H NMR analysis using 1,1',2,2'-

tetrachloroethane as the internal standard.[b]TON: moles of cyclic carbonate /moles of catalyst used. [c]

TOF: TON/reaction time in hours.

Interestingly, the catalytic conversion of 1, 2-epoxypropane, 1, 2-epoxybutane and 1, 2epoxyhexane were found to be almost similar (Table 2, entries 1-3 and Figure S19-21). This observation can be attributed due to the large hexagonal pore channels of MOF1 (10.20 X 10.11 Å2) which are sufficiently bigger than the size of the substrates (Table S5). On the other hand, the relatively lower catalytic conversion of 1, 2-epoxydecane (Table 2, entries 4 and Figure S22) can be ascribed due to its larger size compared to the pore size of MOF1 (revealed from the optimized geometries of the cyclic carbonates using Gaussian09 at B3LYP/6-311G (d,p) level) (Table S5). Furthermore, the catalytic activity of MOF1 was compared with other lanthanide-based MOFs known 14

ACS Paragon Plus Environment

Page 15 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

for cycloaddition of CO2 and remarkably, the reaction conditions employed in this work are milder than the previously reported examples of Ln-MOFs (Table 3).

Table 3. Catalytic conditions employed for cycloaddition of CO2 with epoxides by various lanthanide MOFs. S. No

1

Catalyst

M-BDC/NDC

TBAB

Pressure

Temperature

Conversion

Reference

(mol%)

[MPa]

[°C]

(%)

1.5

1.0

60

89/87

42

[M=Y, Er, Tb] 2

Gea-MOF1

0.75

2.0

120

88

79

3

Eu-BTB-Phen

5.0

0.1

70

97

32

4

[Tb-M(BPD)2

2.5/5

0.1

70

77

67

(µ2H2O)Cl] 5

Gd-MOF

2.5

2.0

80

98.4

68

6

Sm/Gd-BTB

1.0

0.1

80

100

This work

Furthermore, to rule out the possibility of homogeneous catalysis by the MOF leached into solution, the reaction was stopped at 6h and at that time, the conversion of styrene oxide was found to be 54%, then the MOF catalyst was removed by filtration and the filtrate was allowed stir for additional 6h. The analysis of the aliquot taken at 12h revealed slight increase (~5%) in the conversion of styrene oxide, which is considerably low in comparison with the reaction carried out in presence of MOF catalyst (Figure S23 and S24). The slight increase in the conversion of styrene oxide can be attributed due to the presence of co-catalyst, TBAB. Thus, the high catalytic efficiency and size-dependent

15

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

selectivity for epoxides suggest the potential utility of MOF1 as a promising heterogeneous catalyst for cycloaddition of CO2 at mild conditions. Furthermore, the MOF1 catalyst can be easily separated from the reaction mixture by simple filtration followed by washing with H2O/EtOH and reused for five consecutive cycles without significant loss of catalytic activity (Figure 4). Remarkably, powder XRD analysis of the recycled catalyst after five catalytic cycles matches well with the parent MOF, suggesting retention of the original framework (Figure S25).

Figure 4. Recycling test of MOF1 for five successive cycles. The plausible mechanism for cycloaddition of CO2 with epoxides catalyzed by MOFs has been reported in the literature. It involves binary catalytic system composed of a Lewis acid catalytic site and a nucleophilic co-catalyst (TBAB) required for ring opening of epoxide.42-69 The proposed mechanism is shown in Scheme 1, the first step involves coordination of the epoxide to the Lewis acidic Sm/Gd center. The evidence for the coordination of epoxide with the unsaturated metal center

16

ACS Paragon Plus Environment

Page 16 of 30

Page 17 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

has been shown in the literature by means of theoretical calculations and structural determination of an epoxide coordinated to nickel center in MOF.6,7 The next step involves the nucleophilic attack of Br¯ anion of TBAB leading to ring opening of the epoxide and formation of metal-coordinated bromoalkoxide. Subsequent insertion of CO2 to generate metal carbonate species which undergoes an intramolecular ring-closure reaction to form the cyclic carbonate and its elimination from the metal center results in regeneration of the active catalyst.

Scheme 1. The plausible reaction mechanism for the cycloaddition of CO2 with epoxides. CONCLUSIONS In conclusion, synthesis of high thermal and chemical stable, 20-c lanthanide MOFs of Sm3+/Gd3+ ions featuring interesting 3D honeycomb-like structure with large 1D hexagonal channels of dimension ~10.20 X 10.11 Å2 is reported. Further, the MOFs exhibit selective adsorption properties for CO2 over other (N2, Ar, and H2) gases. More interestingly, the activated samples of MOF1/2 act as

17

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

efficient recyclable catalysts for heterogeneous cycloaddition of CO2 with epoxides resulting cyclic carbonates with high yield and selectivity. Further, the pore size-dependent catalytic conversion of epoxides has been observed suggesting the potential utility of MOF1 as promising heterogeneous catalyst for cycloaddition of carbon dioxide. Remarkably, MOF1 catalyst can be easily recycled for several cycles without significant loss of catalytic activity as well as structural rigidity. Therefore, MOF1 and 2 represents rare examples of 20-c lanthanide MOFs exhibiting selective capture and efficient cycloaddition of CO2 with epoxides at mild conditions.

Supporting Information The Supporting Information is available free of charge on the ACS Publications website http://pubs.acs.org. Crystallographic data of MOFs1 and 2 (CIF) PXRD plots for the compounds, structural data, TGA plots, gas adsorption-desorption isotherms, 1H NMR spectra, optimized geometries of epoxides.

AUTHOR INFORMATION Corresponding Author * Email: [email protected]. Notes The authors declare no competing financial interests.

18

ACS Paragon Plus Environment

Page 18 of 30

Page 19 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

Table 1. Crystal data and structure refinement parameters for MOF1 and 2.

Parameters

MOF 1

MOF 2

C27H17O7Gd Empirical formula C27H17O7Sm Formula mass 603.76 610.66 Crystal system Trigonal Trigonal Space group R32(No.155) R32(No.155) a /Å 28.561(5) 28.550(5) b /Å 28.561(5) 28.550(5) c /Å 12.317(5) 12.212(5) α (°) 90.00 90.00 β (°) 90.00 90.00 γ(°) 120.00 120.00 3 V(Å ) 8701(4) 8620(4) 9 9 Z -3 1.040 1.060 ρ(g cm ) -1 1.546 1.759 µ(mm ) 2745 2691 F(000) 298 298 T(K) 0.71073 0.71073 λ(Mo Kα)(Å) 2.3 2.3 Θmin(°) 28.4 28.4 Θmax(°) 56272 64365 Total data 4844 4797 Unique data 0.092 0.061 Rint 4428 4573 Data[I>2σ(I)] a 0.0643 0.0267 R1 b 0.1627 0.0573 wR2 1.17 1.11 S 1555305 1555306 CCDC numbers 0.025(11) 0.028(7) Flank Parameter a b R1 = ∑║Fo│-│Fc║/∑│Fo│, wR2 = [ ∑w(Fo2-Fc2)2/∑w(Fo2)2]1/2

19

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

REFERENCES 1. Sakakura, T.; Choi, J. C.; Yasuda, H. Transformation of Carbon Dioxide. Chem. Rev. 2007, 107, 2365−2387. 2. Omae, I. Recent developments in carbon dioxide utilization for the production of organic chemicals. Coord. Chem. Rev. 2012, 256, 1384−1405. 3. North, M.; Pasquale, R.; Young, C. Synthesis of cyclic carbonates from epoxides and CO2. Green Chem. 2010, 12, 1514−1539. 4. Maeda, C.; Miyazaki, Y.; Ema, T. Recent progress in catalytic conversions of carbon dioxide. Catal. Sci. Technol. 2014, 4, 1482−1497. 5. Alves, M.; Grignard, B.; Mereau, R.; Jerome, C.; Tassaing, T.; Detrembleur, C. Organocatalyzed coupling of carbon dioxide with epoxides for the synthesis of cyclic carbonates: catalyst design and mechanistic studies. Catal. Sci. Technol. 2017, 7, 2651−2684. 6. Kathalikkattil, A. C.; Babu, R.; Roshan, R. K.; Lee, H.; Kim, H.; Tharun, J.; Suresh, E.; Park, D. J. An lcy-topology amino acid MOF as eco-friendly catalyst for cyclic carbonate synthesis from CO2: Structure-DFT corroborated study. J. Mater. Chem. A 2015, 3, 22636−22647. 7. Zhou, Z.; He, C.; Xui, J.; Yang, L.; Duan,C. Metal–Organic Polymers Containing Discrete Single-Walled Nanotube as a Heterogeneous Catalyst for the Cycloaddition of Carbon Dioxide to Epoxides. J. Am. Chem. Soc. 2015, 137, 15066−15069. 8. Taherimehr, M.; Van de Voorde, B.; Wee, L. H.; Martens, J. A.; De Vos, D. E.; Pescarmona, P. P. Strategies for Enhancing the Catalytic Performance of Metal–Organic Frameworks in the Fixation of CO2 into Cyclic Carbonates. ChemSusChem. 2017, 10, 1283–1291. 9. Man, M. L.; Lam, K. C.; Sit, W. N.; Ng, S. M.; Zhou, Z.; Lin, Z.; Lau, C. P. Synthesis of Heterobimetallic Ru-Mn Complexes and the Coupling Reactions of Epoxides with Carbon Dioxide Catalyzed by these Complexes. Chem. Eur. J. 2006, 12, 1004−1015. 10. Ma, R.; He, L. N.; Zhou, Y. B. An efficient and recyclable tetraoxo-coordinated zinc catalyst for the cycloaddition of epoxides with carbon dioxide at atmospheric pressure. Green Chem. 2016, 18, 226−231. 11. Ema, T.; Miyazaki, Y.; Shimonishi, J.; Maeda C.; Hasegawa, J. Y. Bifunctional Porphyrin Catalysts for the Synthesis of Cyclic Carbonates from Epoxides and CO2: Structural Optimization and Mechanistic Study. J. Am. Chem. Soc. 2014, 136, 15270−15279.

20

ACS Paragon Plus Environment

Page 20 of 30

Page 21 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

12. Clegg, W.; Harrington, R. W.; North M.; Pasquale, R. Cyclic Carbonate Synthesis Catalysed by Bimetallic Aluminium-Salen Complexes. Chem. Eur. J. 2010, 16, 6828−6843. 13. Escárcega-Bobadilla, M. V.; Martínez Belmonte, M.; Martin, E.; EscuderoAdán, E. C.; Kleij, A. W. A recyclable trinuclear bifunctional catalyst derived from a tetraoxobis-Zn (salphen) metalloligand. Chem. Eur. J. 2013, 19, 2641−2648. 14. Elmas, S.; Subhani, M. A.; Harrer, M.; Leitner, W.; Sundermeyer, J.; Müller, T. E. Highly active Cr(III) catalysts for the reaction of CO2 with epoxides. Catal. Sci. Technol. 2014, 4, 1652−1657. 15. Liu, M.; Gao, K.; Liang, L.; Sun, J.; Sheng, L.; Arai, M. Experimental and theoretical insights into binary Zn-SBA-15/KI catalysts for the selective coupling of CO2 and epoxides into cyclic carbonates under mild conditions. Catal. Sci. Technol. 2016, 6, 6406−6416. 16. Yang, Z. Z.; Zhao, Y. N.; He, L. N.; Gao, J.; Yin, Z. S. Highly efficient conversion of carbon dioxide catalyzed by polyethylene glycol-functionalized basic ionic liquids. Green Chem. 2012, 14, 519−527. 17. Whiteoak, C. J.; Nova, A.; Maseras, F.; Kleij, A. W. Merging Sustainability with Organocatalysis in the Formation of Organic Carbonates by Using CO2 as a Feedstock. ChemSusChem. 2012, 5, 2032−2038. 18. Wilhelm, M. E.; Anthofer, M. H.; Cokoja, M.; Markovits, I. I. E.; Herrmann, W. A.; Kuhn, F. E. Cycloaddition of Carbon Dioxide and Epoxides using Pentaerythritol and Halides as Dual Catalyst System. ChemSusChem. 2014, 7, 1357−1360. 19. Monassier, A.; D’Elia, V.; Cokoja, M.; Dong, H.; Pelletier, J. D. A.; Basset, J. M.; Kühn, F. E. Synthesis of Cyclic Carbonates from Epoxides and CO2 under Mild Conditions Using a Simple, Highly Efficient Niobium-Based Catalyst. ChemCatChem. 2013, 5, 1321−1324. 20. Langanke, J.; Greiner, L.; Leitner, W. Substrate dependent synergetic and antagonistic interaction of ammonium halide and polyoxometalate catalysts in the synthesis of cyclic carbonates from oleochemical epoxides and CO2. Green Chem. 2013, 15, 1173−1182. 21. Ren, Y.; Shim, J. J. Efficient Synthesis of Cyclic Carbonates by MgII/Phosphine-Catalyzed Coupling Reactions of Carbon Dioxide and Epoxides. ChemCatChem. 2013, 5, 1344−1349. 22. Song, Q. W.; He, L. N.; Wang, J. Q.; Yasuda, H.; Sakakura, T. Catalytic fixation of CO2 to cyclic carbonates by phosphonium chlorides immobilized on fluorous polymer. Green Chem. 2013, 15, 110−115. 21

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 30

23. Yasuda, H.; He, L. N.; Sakakura, T.; Hu, C. Efficient synthesis of cyclic carbonate from CO2 catalyzed by polyoxometalate: the remarkable effects of metal substitution. J. Catal. 2005, 233, 119−122. 24. Kinage, A. K.; Gupte, S. P.; Chaturvedi, R. K.; Chaudhari, R. V. Highly selective synthesis of mono-ethylene glycol phenyl ethers via hydroxyalkoxylation of phenols by cyclic carbonates using large pore zeolites. Catal. Commun. 2008, 9, 1649–1655. 25. Xie, Y.; Zhang, Z.; Jiang, T.; He, J.; Han, B.; Wu, T.; Ding, K. CO2 Cycloaddition Reactions Catalyzed by an Ionic Liquid Grafted onto a Highly Cross-Linked Polymer Matrix. Angew. Chem. Int. Ed. 2007, 46, 7255–7258. 26. Meng, X. L.; Nie, Y.; Sun, J.; Cheng, W. G.; Wang, J. Q.;

He, H. Y.; Zhang, S. J.

Functionalized dicyandiamide–formaldehyde polymers as efficient heterogeneous catalysts for conversion of CO2 into organic carbonates. Green Chem. 2014, 16, 2771–2778. 27. Chen, Y.; Luo, R.; Xu, Q.; Jiang, J.; Zhou, X.; Ji, H. Charged Metalloporphyrin Polymers for Cooperative Synthesis of Cyclic Carbonates from CO2 under Ambient Conditions. ChemSusChem. 2017, 10, 2534–2541. 28. Li, J.; Jia, D.; Guo, Z.; Liu, Y.; Lyu, Y.; Zhou, Y.; Wang, J. Imidazolinium based porous hypercrosslinked ionic polymers for efficient CO2 capture and fixation with epoxides. Green Chem. 2017, 19, 2675–2686. 29. Roeser, J.; Kailasam, K.; Thomas, A. Covalent Triazine Frameworks as Heterogeneous Catalysts for the Synthesis of Cyclic and Linear Carbonates from Carbon Dioxide and Epoxides. ChemSusChem. 2012, 5, 1793–1799. 30. Xu, K.; Dai, Y.; Yea, B.; Wang, H. Two dimensional covalent organic framework materials for chemical fixation of carbon dioxide: excellent repeatability and high selectivity. Dalton Trans. 2017, 40, 10780–10785. 31. Sumida, K.; Rogow, D. L.; Mason, J. A.; McDonald, T. M.; Bloch, E. D.; Herm, Z. R.; Bae T. H.; Long, J. R. Carbon Dioxide Capture in Metal–Organic Frameworks. Chem. Rev. 2012, 112, 724–781. 32. Xiang, S. He, Y. Zhang, Z. Wu, H. Zhou, W. Krishna, R.; Chen, B. Microporous metal-organic framework with potential for carbon dioxide capture at ambient conditions. Nature Commun. 2012, 3, 954–962.

22

ACS Paragon Plus Environment

Page 23 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

33. Nugent, P.; Belmabkhout, Y.; Burd, S. D.; Cairns, A. J.; Luebke, R.; Forrest, K.; Pham, T.; Ma, S.; Space, B.; Wojtas, L.; Eddaoudi, M.; Zaworotko, M. J. Porous materials with optimal adsorption thermodynamics and kinetics for CO2 separation. Nature 2013, 495, 80–84. 34. Maji, T. K.; Matsuda, R.; Kitagawa, S. A flexible interpenetrating coordination framework with a bimodal porous functionality. Nat. Mater. 2007, 6, 142–148. 35. Nagaraja, C. M.; Haldar, R.; Maji T. K.; Rao, C. N. R. Chiral Porous Metal–Organic Frameworks of Co(II) and Ni(II): Synthesis, Structure, Magnetic Properties, and CO2 Uptake. Cryst. Growth Des. 2012, 12, 975–981. 36. Alsmail, N. H.; Suyetin, M.; Yan, Y.; Cabot, R.; Krap, C. P.; Lü, J.; Easun, T. L.; Bichoutskaia, E.; Lewis, W.; Blake, A. J.; Schröder, M. Analysis of High and Selective Uptake of CO2 in an Oxamide Containing {Cu2(OOCR)4}-Based Metal–Organic Framework. Chem. Eur. J. 2014, 24, 7317–7324. 37. Kleist, W.; Jutz, F.; Maciejewski, M.; Baiker, A. Mixed-Linker Metal-Organic Frameworks as Catalysts for the Synthesis of Propylene Carbonate from Propylene Oxide and CO2. Eur. J. Inorg. Chem. 2009, 3552–3561. 38. Trickett, C. A.; Hela, A.; Al-Maythalony, B. A.; Yamani, Z. H.; Cordava, K. E.; Yaghi, O. M. The chemistry of metal–organic frameworks for CO2 capture, regeneration and conversion. Nat. Rev. Mater. 2017, 2, 1–16. 39. Sarwade, P.; Tan, H.; Polshettiwar, V. Shape- and Morphology-Controlled Sustainable Synthesis of Cu, Co, and In Metal Organic Frameworks with High CO2 Capture Capacity. ACS Sustainable Chem. Eng. 2013, 1, 66–74. 40. Sarwade, P.; Tan, H.; Anjum, D.; Cha, D.; Polshettiwar, V. Size- and Shape-Controlled Synthesis of Hexagonal Bipyramidal Crystals and Hollow Self-Assembled Al-MOF Spheres. ChemSusChem. 2014, 7, 529–535. 41. Mohamedali, M.; Nath, D.; Ibrahim, H.; Henni, A. Review of Recent Developments in CO2 Capture Using Solid Materials: Metal Organic Frameworks (MOFs) (http://dx.doi.org/ 10.5772/62275) 42. Wei, N.; Zuo, R. X.; Zhang, Y. Y.; Han, Z. B.; Gu, X. J. Robust high-connected rare-earth MOFs as efficient heterogeneous catalysts for CO2 conversion. Chem. Commun. 2017, 53, 3224–3227.

23

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

43. Xu, H.; Zhai, B.; Cao, C. S.; Zhao, B. A Bifunctional Europium–Organic Framework with Chemical Fixation of CO2 and Luminescent Detection of Al3+. Inorg. Chem. 2016, 55, 9671– 9676. 44. Yang, L.; Yu, L.; Diao, G.; Sun, M.; Cheng, G.; Chen, S. Zeoliticimidazolate framework-68 as an efficient heterogeneous catalyst for chemical fixation of carbon dioxide. J. Mol. Catal. A 2014, 392, 278–283. 45. Cho, H. Y.; Yang, D. A.; Kim, J.; Jeong, S. Y.; Ahn, W. S. CO2 adsorption and catalytic application of Co-MOF-74 synthesized by microwave heating. Catal. Today 2012, 185, 35–40. 46. Zalomaeva, O. V.; Chibiryaev, A. M.; Kovalenko, K. A.; Kholdeeva, O. A.; Balzhinimaev, B. S.; Fedin, V. P. Cyclic carbonates synthesis from epoxides and CO2 over metal–organic framework Cr-MIL-101. J. Catal. 2013, 298, 179–185. 47. Jiang, W.; Yang, J.; Liu, Y. Y.; Song, S. Y.; Ma, J. F. Porphyrin-Based Porous rtl Metal–Organic Framework as an Efficient Catalyst for the Cycloaddition of CO2 to Epoxides. Chem. Eur. J. 2016, 22, 16991–16997. 48. Gao, W. Y.; Wojtas, L.; Ma, S. A porous metal–metalloporphyrin framework featuring highdensity active sites for chemical fixation of CO2 under ambient conditions. Chem. Commun. 2014, 50, 5316–5318. 49. Han, X.; Wang, X. J.; Li, P. Z.; Zou, R.; Li, M.; Zhao, Y. Controlled synthesis of concave cuboctahedral nitrogen-rich metal–organic framework nanoparticles showing enhanced catalytic activation of epoxides with carbon dioxide. CrystEngComm. 2015, 17, 8596–8601. 50. Dong, J.; Cui, P.; Shi, P. F.; Cheng, P.; Zhao, B. Ultrastrong Alkali-Resisting LanthanideZeolites Assembled by [Ln60] Nanocages. J. Am. Chem. Soc. 2015, 137, 15988–15991. 51. Kathalikkattil, A. C.; Kim, D. W.; Tharun, J.; Soek, H. G.; Roshan,R.; Park, D. W. Aqueousmicrowave synthesized carboxyl functional molecular ribbon coordination framework catalyst for the synthesis of cyclic carbonates from epoxides and CO2. Green Chem. 2014, 16, 1607– 1616. 52. Feng, D.; Chung, W. C.; Wei, Z.; Gu, Z. Y.; Jiang, H. L.; Chen, Y. P.; Darensbourg, D. J.; Zhou, H. C. Construction of Ultrastable Porphyrin Zr Metal–Organic Frameworks through Linker Elimination. J. Am. Chem. Soc. 2013, 135, 17105–17110.

24

ACS Paragon Plus Environment

Page 24 of 30

Page 25 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

53. Li, P. Z.; Wang, X. J.; Liu, J.; Lim, J. S.; Zou, R.; Zhao, Y. A Triazole-Containing Metal– Organic Framework as a Highly Effective and Substrate Size-Dependent Catalyst for CO2 Conversion. J. Am. Chem. Soc. 2016, 138, 2142–2145. 54. Lu, L.; Wang, S. M.; Han, Z. B.; Ding, M.; Yuan, D. Q.; Jiang, H. L. Exceptionally Robust InBased Metal–Organic Framework for Highly Efficient Carbon Dioxide Capture and Conversion. Inorg. Chem. 2016, 55, 3558–3565. 55. Gao, C. Y.; Tian, H. R.; Ai, J.; Lei, L. J.; Dang, S.; Lan, Y. Q.; Sun, Z. M. A microporous CuMOF with optimized open metal sites and pore spaces for high gas storage and active chemical fixation of CO2. Chem. Commun. 2016, 52, 11147–11150. 56. De, D.; Pal, T. K.; Neogi, S.; Senthilkumar, S.; Das, D.; Guptaand, S. S.; Bharadwaj, P. K. A Versatile CuII Metal–Organic Framework Exhibiting High Gas Storage Capacity with Selectivity for CO2: Conversion of CO2 to Cyclic Carbonate and Other Catalytic Abilities. Chem. Eur. J. 2016, 22, 3387–3396. 57. Ren, Y.; Cheng, X.; Yang, S.; Qi, C.; Jiang, H.; Mao, Q. A chiral mixed metal–organic framework based on a Ni(saldpen) metalloligand: synthesis, characterization and catalytic performances. Dalton Trans. 2013, 42, 9930–9937. 58. Yang, D. A.; Cho, H. Y.; Kim, J.; Yang, S. T.; Ahn, W. S. CO2 capture and conversion using Mg-MOF-74 prepared by a sonochemical method. Energy Environ. Sci. 2012, 5, 6465–6473. 59. Li, J.; Fan, Y.; Ren, Y.; Liao, J.; Qi, C.; Jiang, H. Development of Isostructural PorphyrinSalen Chiral Metal-Organic Frameworks through Postsynthetic Metalation Based on SingleCrystal to Single-Crystal Transformation. Inorg. Chem. 2018, 57, 1203–1212. 60. Nguyen, P. T. K.; Nguyen, H.T. D.; Nguyen, H. N.; Trickett, C. A.; Ton, Q. T.; GutierrezPuebla, E.; Monge, M. A.; Cordova, K. E.; Gandara, F. New Metal-Organic Frameworks for Chemical Fixation of CO2. ACS Appl. Mater. Interfaces 2018, 10, 733–744. 61. Liang, J.; Xie, Y. Q.; Wang, X. S.; Wang, Q.; Liu, T. T.; Huang, Y. B.; Cao, R. An imidazolium-functionalized mesoporous cationic metal-organic framework for cooperative CO2 fixation into cyclic carbonate. Chem. Commun. 2018, 54, 342–345. 62. Li, J,; Ren, Y.; Qi C.; Jiang, H. A chiral salen-based MOF catalytic material with high thermal, aqueous and chemical stabilities. Dalton Trans. 2017, 46, 7821–7832.

25

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

63. Wang, H. H.; Hou, L.; Li, Y. Z.; Jiang, C. Y.; Wang, Y. Y.; Zhu, Z. Porous MOF with Highly Efficient Selectivity and Chemical Conversion for CO2. ACS Appl. Mater. Interfaces 2017, 9, 17969–17976. 64. Maina, J. W.; Gonzalo, C. P.; Kong, L.; Schütz, J.; Hill, M.; Dumée L. F. Metal organic framework based catalysts for CO2 conversion. Mater. Horiz. 2017, 4, 345-361. 65. Gao, W. Y.; Chen, Y.; Niu, Y.; Williams, K.; Cash, L.; Perez, P. J.; Wojtas, L.; Cai, J.; Chen, Y. S.; Ma, S. Crystal Engineering of an nbo Topology Metal–Organic Framework for Chemical Fixation of CO2 under Ambient Conditions. Angew. Chem. Int. Ed. 2014, 126, 2653–2657. 66. Beyzavi, M. H.; Klet, R. C.; Tussupbayev, S.; Borycz, J.; Vermeulen, N. A.; Cramer, C. J.; Stoddart, J. F.; Hupp, J. T.; Farha, O. K. A Hafnium-Based Metal–Organic Framework as an Efficient and Multifunctional Catalyst for Facile CO2 Fixation and Regioselective and Enantioretentive Epoxide Activation. J. Am. Chem. Soc. 2014, 136, 15861−15864. 67. Qiao, W. Z.; Xu, H.; Cheng, P.; Zhao, B. 3d-4f Heterometal–Organic Frameworks for Efficient Capture and Conversion of CO2. Cryst. Growth Des. 2017, 17, 3128−3133. 68. Xue, Z.; Jiang, J.; Ma, M. G.; Li, M. F.; Mu, T. Gadolinium-Based Metal–Organic Framework as an Efficient and Heterogeneous Catalyst To Activate Epoxides for Cycloaddition of CO2 and Alcoholysis. ACS Sustainable Chem. Eng. 2017, 5, 2623−2631. 69. Kathalikkattil, A. C.; Roshan, R.; Tharun, J.; Babu, R.; Jeong, G. S.; Kim, D. W.; Cho, S. J.; Park, D. W. A sustainable protocol for the facile synthesis of zinc-glutamate MOF: an efficient catalyst for room temperature CO2 fixation reactions under wet conditions. Chem. Commun. 2016, 52, 280−283. 70. O’Keeffe, M.; Peskov, M. A.; Ramsden, S. J.; Yaghi, O. M. The Reticular Chemistry Structure Resource (RCSR) Database of, and Symbols for, Crystal Nets. Acc. Chem. Res. 2008, 41, 1782-1789. 71. Yang, Q. Y.; Li, K.; Luo, J.; Pan, M.; Su, C. Y. A simple topological identification method for highly (3,12)-connected 3D MOFs showing anion exchange and luminescent properties. Chem. Commun. 2011, 47, 4234–4236. 72. Seth, S.; Savitha, G.; Jhulki, S.; Moorthy, J. N. Diverse Metal–Organic Materials (MOMs) Based on 9,9′-Bianthryl-Dicarboxylic Acid Linker: Luminescence Properties and CO2 Capture. Cryst. Growth Des. 2016, 16, 2024−2032.

26

ACS Paragon Plus Environment

Page 26 of 30

Page 27 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

73. Xue, D. X.; Cairns, A. J.; Belmabkhout, Y.; Wojtas, L.; Liu, Y. L.; Alkordi, M. H.; Eddaoudi, M. Tunable Rare-Earth fcu-MOFs: A Platform for Systematic Enhancement of CO2 Adsorption Energetics and Uptake. J. Am. Chem. Soc. 2013, 135, 7660−7667. 74. Chandrasekhar, P.; Savitha, G.; Moorthy, J. N. Robust MOFs of “tsg” Topology Based on Trigonal Prismatic Organic and Metal Cluster SBUs: Single Crystal to Single Crystal Postsynthetic Metal Exchange and Selective CO2 Capture. Chem. Eur. J., 2017, 23, 7297−7305. 75. Seth, S.; Savitha, G.; Moorthy, J. N. Carbon Dioxide Capture by a Metal–Organic Framework with Nitrogen-Rich Channels Based on Rationally Designed Triazole-Functionalized Tetraacid Organic Linker. Inorg. Chem. 2015, 54, 6829−6835. 76. Chandrasekhar, P.; Mukhopadhyay, A.; Savitha, G.; Moorthy, J. N. Orthogonal self-assembly of a trigonal triptycene triacid: signaling of exfoliation of porous 2D metal–organic layers by fluorescence and selective CO2 capture by the hydrogen-bonded MOF. J. Mater. Chem. A 2017, 5, 5402−5412. 77. Xue, D. X.; Belmabkhout, Y.; Shekhah, O.; Jiang, H.; Adil, K.; Cairns, A. J.; Eddaoudi, M. Tunable Rare Earth fcu-MOF Platform: Access to Adsorption Kinetics Driven Gas/Vapor Separations via Pore Size Contraction. J. Am. Chem. Soc. 2015, 137, 5034−5040. 78. Li, Y. J.; Wang, Y. L.; Liu, Q. Y. The Highly Connected MOFs Constructed from Nonanuclear and Trinuclear Lanthanide-Carboxylate Clusters: Selective Gas Adsorption and Luminescent pH Sensing. Inorg. Chem. 2017, 56, 2159−2164. 79. Guillerm, V.; Weselin´ski, Ł. J.; Belmabkhout, Y.; Cairns, A. J.; D’Elia, V.; Wojtas, Ł.; Adil, K.; Eddaoudi, M. Discovery and introduction of a (3,18)-connected net as an ideal blueprint for the design of metal–organic frameworks. Nat. Chem. 2014, 6, 673−680. 80. SMART (V 5.628), SAINT (V 6.45a), XPREP, SHELXTL; Bruker AXS Inc., Madison, Wisconsin, USA, 2004. 81. Sheldrick, G. M. Siemens Area Detector Absorption Correction Program, University of Göttingen, Göttingen, Germany, 2004. 82. Altomare, A.; Cascarano, G.; Giacovazzo, C.; Guagliardi, A. Completion and refinement of crystal structures with SIR92. J. Appl. Crystallogr. 1993, 26, 343−350. 83. Sheldrick, G. M. SHELXL-2014, Program for Crystal Structure Solution and Refinement; University of Göttingen, Göttingen, Germany, 2014. 27

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

84. Farrugia, L. J. WinGX-A Windows Program for Crystal Structure Analysis. J. Appl. Crystallogr. 2012, 45, 849−854. 85. Spek, A. L. Single-crystal structure validation with the program PLATON. J. Appl. Crystallogr. 2003, 36, 7−13. 86. Devic, T.; Serre, C.; Audebrand, N.; Marrot, J.; Férey, G. MIL-103, A 3-D Lanthanide-Based Metal Organic Framework with Large One-Dimensional Tunnels and A High Surface Area. J. Am. Chem. Soc. 2005, 127, 12788−12789. 87. Duan, J.; Higuchi, M.; Horike, S.; Foo, M. L.; Rao, K. P.; Inubushi, Y.; Fukushima, T.; Kitagawa, S. High CO2/CH4 and C2 Hydrocarbons/CH4 Selectivity in a Chemically Robust Porous Coordination Polymer. Adv. Funct. Mater. 2013, 23, 3525−3530. 88. Devic, T.; Wagner, V.; Guillou, N.; Vimont, A.; Haouas, M.; Pascolini, M.; Serre, C.; Marrot, J.; Daturi, M.; Taulelle F.; Férey, G. Synthesis and characterization of a series of porous lanthanide tricarboxylates. Micro. Meso. Mater. 2011, 140, 25−33. 89. Blatov, V. A.; Shevchenko, A. P.; Proserpio, D. M. Applied Topological Analysis of Crystal Structures with the Program Package ToposPro. Cryst. Growth Des. 2014, 14, 3576−3589. 90. Yang, R. T. Gas Separation by Adsorption Processes, Butterworth, Boston, 1997. 91. Pan, H.; Ritter, J. A.; Balbuena, P. B. Examination of the Approximations Used in Determining the Isosteric Heat of Adsorption from the Clausius-Clapeyron Equation. Langmuir 1998, 14, 6323−6327. 92. Sikdar, N.; Hazra A.; Maji, T. K. Stoichiometry-Controlled Two Flexible Interpenetrated Frameworks: Higher CO2 Uptake in a Nanoscale Counterpart Supported by Accelerated Adsorption Kinetics. Inorg. Chem. 2014, 53, 5993−6002. 93. Beyzavi, M. H.; Stephenson, C. J.; Liu, Y.; Karagiaridi, O.; Hupp, J. T.; Farha, O. K. Metal– organic framework-based catalysts: Chemical fixation of CO2 with epoxides leading to cyclic organic carbonates. Front. Energy Res. 2015, 2, 63−72. 94. Ugale, B.; Dhankhar, S. S.; Nagaraja, C. M. Construction of 3-Fold-Interpenetrated ThreeDimensional Metal–Organic Frameworks of Nickel(II) for Highly Efficient Capture and Conversion of Carbon Dioxide. Inorg. Chem. 2016, 55, 9757−9766. 95. Ugale, B.; Dhankhar, S. S.; Nagaraja, C. M. Interpenetrated Metal–Organic Frameworks of Cobalt(II): Structural Diversity, Selective Capture and Conversion of CO2. Cryst. Growth Des. 2017, 17, 3295−3305. 28

ACS Paragon Plus Environment

Page 28 of 30

Page 29 of 30 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

96. Frisch, M. J.; Trucks, G. W.; Schlegel, H. B.; Scuseria, G. E.; Robb, M. A.; Cheeseman, J. R.; Scalmani, G.; Barone, V.; Mennucci, B.; Petersson, G. A. Gaussian 09, Revision D.01,;Revision B.01,; Gaussian, Inc.: Wallingford CT, 2010.

29

ACS Paragon Plus Environment

Crystal Growth & Design 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

For Table of Contents Use Only Exceptionally Stable and 20-connected Lanthanide Metal-Organic Frameworks for Selective CO2 Capture and Conversion at Atmospheric Pressure Bharat Ugale, Sandeep Singh Dhankhar and C. M. Nagaraja*

Highly thermal and chemical stable, 20-connected, lanthanide MOFs, [{Ln(BTB)(H2O).H2O]n (where, Ln = Sm (MOF1)/Gd(MOF2), BTB = 1,3,5-tris(4-carboxyphenyl) benzene) have been synthesized solvothermally. The MOFs feature 3D Honeycomb-like structure and exhibit selective adsorption of CO2 and act as efficient heterogeneous catalysts for cycloaddition of carbon dioxide with epoxides at mild conditions.

30