Experimental Study on Heat Transfer and Thermo-Physical Properties

Feb 22, 2017 - Nanotechnology & Catalysis Research Centre (NANOCAT), IPS Building, University of Malaya, 50603 Kuala Lumpur, Malaysia. ABSTRACT: In or...
0 downloads 7 Views 1MB Size
Subscriber access provided by University of Newcastle, Australia

Article

Experimental study on heat transfer and thermo-physical properties of covalently functionalized carbon nanotubes nanofluids in an annular heat exchanger: A green and novel synthesis Maryam Hosseini, Rad Sadri, Salim Newaz Kazi, Samira Bagheri, Mohd Nashrul Mohd Zubir, Chew Bee Teng, and Tuan Zaharinie Energy Fuels, Just Accepted Manuscript • DOI: 10.1021/acs.energyfuels.6b02928 • Publication Date (Web): 22 Feb 2017 Downloaded from http://pubs.acs.org on March 2, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers

Energy & Fuels is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Subscriber access provided by University of Newcastle, Australia

and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Energy & Fuels is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42

Energy & Fuels

CNTs

Eugenol H2 O 2 Clove Ascorbic Acid

Heat & Ultra-sonication ACS Paragon Plus Environment

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Experimental study on heat transfer and thermo-physical properties of covalently functionalized carbon nanotubes nanofluids in an annular heat exchanger: A green and novel synthesis Maryam Hosseini*a, Rad Sadri*a, Salim Newaz Kazi*a, Samira Bagherib, Nashrul Zubir a, Chew Bee Tenga, Tuan Zaharinie a a

Department of Mechanical Engineering, Faculty of Engineering, University of Malaya, Kuala Lumpur 50603, Malaysia. b

Nanotechnology & Catalysis Research Centre (NANOCAT), IPS Building, University Malaya, 50603 Kuala Lumpur, Malaysia.

*Corresponding author. Tel.: +60 3 79674582; fax: +60 3 79675317. E-mail addresses: [email protected] (Maryam Hosseini), [email protected] (Rad Sadri), [email protected] (S.N. Kazi).

Abstract In order to eliminate the use of toxic acids in common carbon nanomaterial functionalization methods, a facile and eco-friendly procedure is introduced in this study to synthesize highly dispersed, covalently functionalized multi-walled carbon nanotubes (MWCNTs) for use in heat transfer fluids. The MWCNTs are treated covalently with clove buds in one pot using free radical grafting reaction. The clove-treated MWCNTs (C-MWCNTs) are then dispersed in distilled water (DI water) at three different concentrations of C-MWCNTs (0.075, 0.125 and 0.175 wt.%), resulting in C-MWCNT-DI water nanofluids. The effectiveness of the functionalization process is then verified using Fourier transform infrared (FTIR) spectroscopy, thermogravimetric analysis (TGA) and transmission electron microscopy (TEM). UV-vis spectroscopy is also used to examine the stability of the C-MWCNTs in the base fluid. The thermal conductivity, density and dynamic viscosity of the C-MWCNT-DI water nanofluids are studied experimentally, and the results show that there is significant thermal conductivity enhancement for the C-MWCNT-DI water nanofluids, whereas there is only a slight increase in the viscosity and density of these nanofluids. Lastly, convective heat transfer experiments are carried out for the C-MWCNT-DI water nanofluids flowing through an annular heat exchanger at constant heat flux and fully developed turbulent flow condition. The results show that there is a significant enhancement in the convective heat transfer coefficient and Nusselt number for the C-MWCNT-DI water nanofluids, whereas the increase in friction factor is almost negligible for these nanofluids. Based on the results, it can be concluded that the eco-friendly C-MWCNT-DI water nanofluids have strong potential for use as effective working fluids in various heat transfer applications. Keywords Multi-walled carbon nanotubes, clove, green functionalization, nanofluids, thermo-physical properties, convective heat transfer, annular heat exchanger

1 ACS Paragon Plus Environment

Page 2 of 29

Page 3 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

1. Introduction Heating or cooling fluids such as air, water, Freon, ethylene glycol and mineral oil play a vital role in various industrial sectors such as chemical production, power generation, microelectronics, transportation and air-conditioning. However, conventional heating or cooling fluids do not have superior capability to transfer or dissipate heat from industrial thermal equipment with high heat flux 1. One of the promising solutions to address this issue is to disperse nanoparticles with high thermal conductivity (e.g. metal, carbon or metal oxide nanoparticles) into the base fluid in order to enhance the thermal performance of heat transfer systems2-6. In this regard, Choi et al. 7 found that the thermal conductivity of the CNT-water nanofluids is higher compared to that for water. They measured the effective thermal conductivity of a nanofluid containing 1.0 vol.% of multi-walled carbon nanotubes (MWCNTs) dispersed in synthetic poly(α-olefin) oil and reported a thermal conductivity enhancement of 160% 8. Sadri et al. studied the sonication time effect on the dynamic viscosity, thermal conductivity and dispersion of MWCNT aqueous suspensions. The results represented that the viscosity decreases, whereas the thermal conductivity of the nanofluids increases with an increase in temperature and sonication time. The maximum thermal conductivity enhancement was found to be 22.31% (ratio of 1.22) at a temperature and sonication time of 45°C and 40 min, respectively 9. Philip et al.

10

investigated the thermal

conductivity enhancement of kerosene-based Fe3O4 nanofluids under the influence of a magnetic field and the results showed that the enhancement of thermal conductivity is 300% (knanofluid/kbase-fluid = 4.0) at a concentration of 6.3 vol.% and particle size of 6.7 nm. Pak and Cho

11

investigated the heat transfer performance of γ-Al2O3 and TiO2 nanoparticles

dispersed in water flowing through a horizontal circular tube under turbulent flow and constant heat flux conditions. The results represented that the Nusselt number of the

2 ACS Paragon Plus Environment

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 29

nanoparticles aqueous suspensions increases by increasing the Reynolds number and nanoparticles concentration. Moreover, they discovered that the convective heat transfer coefficient of the nanofluids is lower than that for water by 12% for a given condition when the particle loading is 3 vol.%. They proposed a new heat transfer correlation to predict the convective heat transfer coefficient of nanofluids in turbulent flow regime. Annular heat exchangers are commonly used in industrial applications, particularly in heat transfer equipment. These heat exchangers have gained much attention from scientists and researchers and they have been used in various thermal systems such as air-conditioning, electronic devices, heating and ventilation systems, turbomachinery, gas turbines and nuclear reactors. Hence, investigating the heat transfer characteristics of annular heat exchangers and devising a novel technique to improve their performance play a key role in promoting energy savings 12, 13

. Weerapun Duangthongsuk et al.14 studied the friction factor and convective heat transfer

of TiO2 aqueous suspensions (concentration of 0.2 vol.%) in a horizontal double-tube counter flow heat exchanger under turbulent conditions. They discovered that the convective heat transfer coefficient of nanofluids is slightly greater that of the base fluid by about 6-11% and increases by decreasing the fluid temperature. Moreover, they showed that the temperature of the heating fluid has no significant effect on the heat transfer coefficient of the nanofluid. Izadi et al.

15

simulated the forced convection flow of Al2O3/water aqueous suspensions

through a two-dimensional annular heat exchanger (in which the working fluid was Al2O3water nanofluid) using the single-phase method under turbulent conditions. The results showed that the dimensionless axial velocity profile does not remarkably vary with the nanoparticle volume fraction. However, the temperature profiles are affected by the nanoparticle concentration. They found that the convective heat transfer coefficient increases by increasing the nanoparticle concentration. CNTs have garnered much interest among scientists and researchers because of their remarkable physical and chemical properties

3 ACS Paragon Plus Environment

16, 17

Page 5 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

as well as excellent mechanical properties18-20. Indeed, it has been proven in previous studies that CNT nanofluids have high thermal and electrical conductivities 21-24 . However, the main disadvantage of CNTs is their poor solubility and processability since they easily become entangled and moreover, they tend to aggregate in most organic and aqueous solvents25. It has been shown that non-covalent functionalization of CNTs based on the π-π staking interaction and polymer wrapping of surfactants such as sodium dodecyl benzene sulphonate (SDBS), sodium dodecyl sulfate (SDS), gum arabic (GA) and cetyltrimethylammonium bromide (CTAB) improves the solubility of CNTs in polar solvents

9, 18, 26

. However, there are some

undesirable effects of the above mentioned surfactants on the thermophysial properties of carbon based nanofluids such as increasing viscosity and foam formation in the colloidal suspensions which have limited surfactant applications27. On the other hand, various techniques have been employed for covalent modification of carbon nanotubes such as treatment with ozone, oxidation, fluorination, free radical addition, 1,3-dipolar cycloaddition, nucleophilic addition, alkylation and plasma modification28-30. Among these techniques, free radical grafting is a desirable technique for large-scale synthesis of CNTs with versatile functional groups due to its facile treatment and high reactivity

28

.

In this technique,

peroxides, aryl diazonium salts, substituted anilines or benzophenone are used as the starting materials

28, 30

. However, all of the aforementioned techniques typically require very harsh

and drastic reaction conditions. In addition, most of these techniques involve many reaction steps, and the reagents and chemicals employed in these techniques are greatly prone to oxidation. These techniques can also damage the sp2 hybridized carbon atoms of nanotubes, which in turn, have an effect on the thermal, electrical and optical properties of the carbon nanotubes 28. These techniques also lead to other problems such as health hazards, equipment corrosion and environmental pollution. Hence, there is a critical need to develop a functionalization method which is environmentally friendly

31

4 ACS Paragon Plus Environment

in order to tackle the above-

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

mentioned issues. Clove, an aromatic flower bud, is one of the most widely cultivated spices in tropical countries. Clove bud is one of the main vegetal sources of phenolic compounds such as hydroxybenzoic acids, flavonoids, hydroxycinnamic acids and hydroxyphenyl propane

32

. Eugenol is the major bioactive compound of cloves, which is typically found in

concentrations of around 82.6 wt.% 33. Phenolic acid and gallic acid are also present in cloves at higher concentrations. A previous study

34

has shown that ascorbic acid is found in clove

flower buds with concentrations up to 0.08 wt.%. The unique properties and structure of cloves make them a suitable candidate to improve the functionalization of CNTs in aqueous media. Hence, the main objective of this study is to develop an environmentally friendly, cost-effective and industrially scalable method for synthesizing MWCNTs covalently functionalized with cloves, and to determine the effectiveness of this technique in improving convective heat transfer in an annular heat exchanger relative to that for water. In order to verify the success of the functionalization method, the clove-treated MWCNTs are characterized using Fourier transform infrared (FTIR) spectroscopy, thermogravimetric analysis (TGA), transmission electron microscopy (TEM), and ultraviolet-visible (UV-vis) spectroscopy. Following this, the clove-treated MWCNTs are dispersed into distilled water at three different nanoparticle concentrations (0.075, 0.125 and 0.175 wt.%) to prepare CMWCNT-DI water nanofluids and the rheological and thermo-physical properties of these nanofluids also investigated at various temperatures. The friction factor and Nusselt number values for the base fluid are determined from the experimental data and the results are validated against those calculated from empirical correlations. Lastly, the Nusselt number, convective heat transfer coefficient, pressure drop, friction factor and performance index are evaluated for the C-MWCNT-DI water nanofluids flowing through an annular heat exchanger in turbulent flow conditions.

5 ACS Paragon Plus Environment

Page 6 of 29

Page 7 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

2. Materials and methods Pristine multi-walled carbon nanotubes (MWCNTs) with a diameter less than 30 nm and purity of more than 95% were purchased from Nanostructured & Amorphous Materials Inc., (Houston, TX, USA). Hydrogen peroxide (H2O2, 30%) was purchased from Sigma-Aldrich (M) Sdn. Bhd., Selangor, Malaysia. Fresh cloves, which are a source of eugenol and vitamin C (ascorbic acid), were purchased from a grocery store in Iran.

2.1. Preparation of C-MWCNT-DI water nanofluids A novel, facile and eco-friendly technique for covalent functionalization of MWCNTs with cloves was introduced for the first time in this study in order to attain highly dispersed MWCNTs in aqueous media. In this technique, eugenol (which is the main component of cloves 33) was grafted onto the MWCNTs using hydrogen peroxide and ascorbic acid (also a component of cloves) as the redox initiator 34. The clove extract solution was prepared using the following procedure. Firstly, 15 g of ground cloves were added into a beaker containing 1000 ml of distilled water preheated at 80°C. The solution was then homogenized in heating mode at an agitation speed of 1200 rpm for 30 min. Lastly, the clove extract solution was filtered using a 45 µm polytetrafluoroethylene (PTFE) membrane in ambient conditions. The clove-treated MWCNTs (C-MWCNTs) were prepared using the following procedure. Firstly, 5 g of pristine MWCNTs were poured into a beaker filled with 1000 ml of clove extract solution, followed by continuous stirring for 15 min order to achieve a homogeneous black suspension. Following this, 25 ml of concentrated hydrogen peroxide was added gradually into the reaction mixture throughout the sonication time. The reaction mixture was ultra-sonicated for 10 min. After sonication, the reaction mixture was heated to 80°C under reflux for 14 h. The resultant suspension was centrifuged repeatedly at 14000 rpm and then washed with large amounts of distilled water until the suspension attained a neutral pH. The 6 ACS Paragon Plus Environment

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

functionalized sample was dried overnight in a vacuum oven set at 60°C. It was observed that the clove-treated MWCNTs are highly stable in aqueous medium. In order to synthesize the C-MWCNT-DI water nanofluids, the C-MWCNTs were ultrasonicated with distilled (DI) water as the base fluid for 10 min. The nanofluids were prepared for three different concentrations of C-MWCNTs: 0.075, 0.125 and 0.175 wt.%. The sample preparation procedure is summarized in Fig. 1.

Fig.1. Schematic of functionalization procedure of carbon nanotubes

2.2. Experimental procedure The experiments were carried out in several stages. Firstly, the pristine MWCNTs were covalently functionalized with cloves, and the C-MWCNTs were characterized using various analytical instruments. Following this, the thermo-physical properties of the synthesized nanofluids and base fluid were determined. Lastly, the convective heat transfer and frictional properties of the C-MWCNT-DI water nanofluids flowing through an annular heat exchanger were investigated. Characterization of the C-MWCNTs was carried out using Fourier transform infrared (FTIR) spectroscopy (Bruker, IFS-66/S, Germany) and thermogravimetric analysis (TGA-50, Shimadzu, Japan). Hitachi HT7700 transmission electron microscope was

7 ACS Paragon Plus Environment

Page 8 of 29

Page 9 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

used to examine the morphological characteristics of the samples. For the TEM analysis, the samples were prepared by ultrasonically dispersing the nanoparticles in ethanol prior to collection on Lacey carbon grids. We used Shimadzu UV-1800 spectrophotometer to determine the dispersibility of C-MWCNT-DI water nanofluids. For the UV-vis analysis, we diluted the nanofluids with DI water at a dilution ratio of 1:20 in order to ensure that the detectable wavelengths of the UV-vis spectrometer are able to pass through the samples. Following this, we poured our samples into quartz cuvettes specialized for transmission of UV wavelengths and we measured the absorbance of the samples at pre-defined time intervals over the course of 63 days. The thermal conductivity of the samples was measured using KD-2 PRO portable field and laboratory thermal property analyser (Decagon Devices, USA). The KS-1 probe has a length and diameter of 60 and 1.3 mm, respectively. The accuracy of the thermal conductivity measurements is around 5%. In order to ensure equilibrium of the nanofluids, an average of 20 measurements were recorded over a 5-h period for each nanoparticle concentration and temperature. Calibration of the instrument was also conducted with DI water prior to measurements using nanofluids. The viscosity of the nanofluids was measured using Physica MCR rheometer (Anton Paar, Austria). The rotational rheometer consists of a moving cylindrical plate and a stationary cylindrical surface placed in parallel with a small gap between them. The density of the samples was measured using DE-40 density meter (Mettler Toledo, Switzerland), with an accuracy of 10−4 g/cm3. The measurements were made in triplicate for each sample and temperature. The overall experimental set-up for convective heat transfer measurements includes an annular flow test rig, a reservoir tank, a pump, a data acquisition system, a cooling unit, a heated test section, and measuring instruments including a differential pressure transmitter (DPT) and a flow meter. The experimental set-up is shown in Fig. 2. The aqueous suspensions were pumped using Araki EX-70 R magnet pump from a 10 L stainless steel jacketed tank at a flow rate of

8 ACS Paragon Plus Environment

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 29

0–14 L/min. The pressure loss and flow rate were measured using PX154 wet/wet low differential pressure transmitter (OMEGA Engineering Inc., USA) and SE 32 inline paddle wheel transmitter with display (Bürkert Contromatic Corp., USA), respectively. The pump flow was regulated using Hoffman Muller inverter. The concentric annular test rig consists of a cartridge heater (OMEGA Engineering Inc., USA) with a length of 600 mm and a Diameter of 15 mm, which was inserted in the centre of a straight, seamless and horizontal tube made from stainless steel with a length of 900 mm, an outer and inner diameter of 33.4 and 26.7 mm, respectively. The heater was linked to a QPS VT2-1 variable voltage transformer (Success Electronics & Transformer Manufacturer Sdn. Bhd., Malaysia) and, voltage and current were measured to set the desired heating power. Three built-in K-type thermocouples (OMEGA Engineering Inc., USA) cautiously installed a little away from the outside contact face of heater surface in order to prevent disturbance in the boundary layer caused by the thermocouple probes protruding into the internal surface of the tube. The bulk temperature of the flow was measured using two platinum resistance temperature detectors (Pt-100 RTDs) which were placed inside the pipe at the outlet and inlet of the test section. The maximum error for thermocouples was ± 0.2℃. The thermocouples were connected to a GL220 10channel midi logger (Graphtec Corporation, Japan) in order to monitor and record the temperature data. The test section was wrapped with thick fibreglass wool in order to reduce heat loss to the surroundings.

9 ACS Paragon Plus Environment

Page 11 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

Data Logger

Tout

Tin Insulting material

Test Cross section

T1T2T3

Thermocouples (T1-T2-T3)

Concentric Heater Insulting material DPT 15 mm

AC power supply

26.7 mm

Flow meter By pass flow

Mass flow meter

Tank

Pump

Cooling system

Fig. 2. Schematic diagram of the experimental set-up

2.3. Data analysis The experimental data were processed to evaluate the hydrodynamic and heat transfer performance of the annular heat exchanger. Taking into account conduction in the heater wall and convection heat transfer with the fluid in the test section, calibration was required to determine the temperature at the surface of the heater. Hence, an analysis based on the Wilson plot technique 35 was done by equating the wall resistance. It shall be noted that there are important parameters used to determine the effect of the C-MWCNTs on the thermal properties of DI water, namely, convective heat transfer coefficient (h), Nusselt number (Nu) and pressure drop. The experimental heat transfer coefficient was determined from the measured bulk, surface, outlet and inlet temperatures using the Newton’s law of cooling:

ℎ=

𝑞" (𝑇𝑤 − 𝑇𝑏 )

(1)

10 ACS Paragon Plus Environment

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 29

Where, 𝑇𝑤 , 𝑇𝑏 and 𝑞 " represents the wall temperature, bulk temperature and heat flux, respectively. 𝑇𝑏 is defined as

𝑇𝑜 +𝑇𝑖 2

, where 𝑇𝑜 and 𝑇𝑖 is the outlet and inlet temperature of the

flow, respectively. The heat flux was determined using the following equation:

𝑞" =

𝑄 𝐴

(2)

Here, Q is the input power (VI) generated by the voltage transformer and A is the internal surface area of the tube. Note that A =π𝐷ℎ 𝐿. 𝐷ℎ is the annulus hydraulic diameter, which is defined as the difference between the inner annulus diameter and outer heater diameter. L is the annulus heated length. The input power (VI) was kept fixed at 900 W for the experiments. The Reynolds number (Re) was calculated using the following equation:

𝑅𝑒 =

𝜌𝑣Dℎ 𝜇

(3)

Here, 𝜌, 𝑣 and 𝜇 represents the density, velocity and dynamic viscosity of the working fluid, respectively. The Nusselt number is given by:

𝑁𝑢 =

ℎ × Dℎ 𝐾

(4)

Where, k and h represents the thermal conductivity and convective heat transfer coefficient, respectively. The friction factor (f) of the DI water and C-MWCNT-DI water nanofluids was determined from the pressure drop across the test section measured from experiments using the following equation (Eq.5):

𝑓=

∆𝑃 𝐿 𝜌𝑣 2 ( )( ) Dℎ 2

(5)

Where, ∆𝑃 and 𝑣 represents the pressure drop and flow velocity, respectively.

11 ACS Paragon Plus Environment

Page 13 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

3. Results and discussion 3.1. Characterization of the C-MWCNTs In this study, various characterization techniques were used to characterize the C-MWCNTs. The morphology of the C-MWCNTs was examined using TEM. FTIR spectroscopy was used to identify the functional groups attached to the C-MWCNTs. Fig. 3(A) shows the FTIR spectra for the pristine MWCNTs and C-MWCNTs, which are represented by the transmittance (%) versus the wavenumber (cm-1). It can be observed from Fig. 3(A) that there are noticeable cues of the eugenol molecule for the C-MWCNTs compared to the pristine MWCNTs. The broad peak at 3448.19 cm-1 is ascribed to O–H stretching vibrations, which may be caused by the reaction between the MWCNTs and hydroxyl groups of eugenol and/or hydrogen peroxide. The symmetric and asymmetric sharp vibrations of C–H bonds are observed within a wavenumber range of 2850–3000 cm-1 for both MWCNTs and CMWCNTs. A couple of peaks are observed within the wavenumber range of 1579–1639 cm-1, which arise from C=C stretching vibrations of MWCNTs after opening due to the addition of electrophilic reactions between the main structure of MWCNTs and the –OH band of eugenol. The functionalization of MWCNTs by eugenol is confirmed by the peaks at 1428, 1386, 1113 and 1077 cm-1, which are ascribed to CH2 bending vibrations, out-of-plane CH vibrations and C–O stretching vibrations, respectively. The peaks within the wavenumber range of 1722–1763 cm-1 and the peak centred at 1621 cm-1 are assigned to O–C=O stretching vibrations, indicating the formation of carboxyl groups at the main structure of MWCNTs. TGA is a thermal analysis technique, whereby modifications in the structure of materials are evaluated as a function of temperature. TGA provides information about the quantitative amount of each functional groups on the surface of MWCNTs, which is why it was used to characterize the pristine MWCNTs and C-MWCNTs. Fig. 3(B) shows the TGA curves for pristine MWCNTs and C-MWCNTs and it can be seen that there is no weight loss in the

12 ACS Paragon Plus Environment

Energy & Fuels

pristine MWCNTs up to a temperature of ~700°C, which is the temperature at which the main graphitic structures begin to decompose. However, there is a gradual weight loss for the C-MWCNTs, which confirms the decomposition of the functional groups. There are three distinctive steps of weight loss for the clove-treated MWCNTs within a temperature range of 0–600°C. The first weight loss occurs at ~100°C, which is attributed to water whereas the second weight loss occurs between 200 and 300°C, which is due to the decomposition of the functional group (i.e. eugenol). The third weight loss occurs after 600°C, which caused by the degradation of the graphitic structures in air. The results indicate the successful covalent functionalization of MWCNTs with eugenol, which is evidenced by the gradual weight loss observed in the TGA curve for C-MWCNTs. Digital image of C-MWCNTs dispersed in DI water after 90 days, is shown in Fig. 3(C).

105 100

95 Weight loss (%)

Transmitance (%)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 29

90 85 80 75 70

(A)

MWCNT

65

C- MWCNT

(B)

MWCNT

C- MWCNT

60 900

1400

1900 2400 2900 Wave number (cm-1)

3400

3900

0

200

(C)

13 ACS Paragon Plus Environment

400 600 800 Temperature (°C)

1000

Page 15 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

Fig. 3. (A) FTIR spectra of pristine MWCNTs and C-MWCNTs, (B) TGA curves of pristine MWCNTs and C-MWCNTs, and (C) photograph of C-MWCNTs dispersed in DI water after three months

Even though the functional groups cannot be inferred from TEM images, these images can be used to examine the surface deterioration of MWCNTs, as evidence of functionalization. Figs. 4(A–C) show the TEM images of pristine MWCNTs and C-MWCNTs. It can be observed that the pristine MWCNTs have a relatively smooth surface and low wall defects (Fig. 4(A)). In contrast, there is an increase in surface roughness for the modified CMWCNTs (Figs. 4(B and C)). The cut and open ends of the MWCNTs are evident, which may be due to the partial damage of graphitic (sp2) carbon after functionalization. (A)

(B)

20 nm

20 nm

(C)

20 nm

Fig.4. TEM images of: (A) pristine MWCNTs, and (B and C) C-MWCNTs

UV-Vis spectroscopy is a technique used to study dispersibility of nanofluids with respect to the sedimentation time. Fig. 5 shows the colloidal stability of the C-MWCNT-DI water nanofluids with respect to the number of the days after preparation. It is obvious that the

14 ACS Paragon Plus Environment

Energy & Fuels

relative concentration of the aqueous suspensions reduces with the number of days. However, all of the samples have a fairly constant concentration after Day 45. The maximum magnitude of sedimentation is 7.6, 9.2 and 11.3% for a nanoparticle concentration of 0.075, 0.125 and 0.175 wt.%, which confirms the colloidal stability of the nanofluids containing CMWCNTs.

1.00

Relative concentration

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 29

0.95 0.90

0.85 0.80

C-MWCNTs 0.075 wt% C-MWCNTs 0.125 wt%

0.75

C-MWCNTs 0.175 wt% 0.70 0

10

20

30

40

50

60

70

No. of the day after preparation

Fig. 5. Colloidal stability of C-MWCNTs dispersed in DI water

3.2. Thermophysical properties The effective viscosity of nanofluids containing C-MWCNTs as and DI water were measured experimentally and the results are shown in Fig. 6. The dynamic viscosity is shown as a function of the nanoparticle concentration and temperature at a fixed shear rate of 150 s-1. It can be observed that there is a slight increase in the dynamic viscosity of the C-MWCNT-DI water nanofluids relative to that for DI water. This indicates that the C-MWCNTs remain suspended in the base fluid, which indicates successful covalent functionalization. It can also be observed from Fig. 6 that the dynamic viscosity of the C-MWCNTs nanofluids declines by increasing temperature, which may be attributed to weakening of intermolecular forces 15 ACS Paragon Plus Environment

36

.

Page 17 of 29

This observation corroborates well the findings of Aravind et al. 36, Ko et al. al.

38

37

and Sadri et

, who observed that there is decrease in viscosity when the fluid temperature is

increased. The rather mild increase in the effective viscosity with nanoparticle concentration is an important advantage, since the increase in viscosity could undermine the overall positive impact of enhanced conductivity in heat transfer due to the pumping fluid penalty. 1.2 C-MWCNTs 0.175 wt% C-MWCNTs 0.125 wt%

1.1

C-MWCNTs 0.075 wt% DI water

1.0 Viscosity (mPa.s)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

0.9 0.8 0.7 0.6 0.5 15

20

25

30

35

40

45

50

55

Temperature (°C)

Fig. 6. Dynamic viscosity of nanofluids containing C-MWCNTs and DI water at a shear rate of 150 s-1 (mPa·s)

The density was measured for the C-MWCNT aqueous suspensions and base fluid at various temperatures and the results are presented in Table 1. It can be seen that there is a decrease in the density of the C-MWCNT-DI water nanofluids and DI water with an increase in fluid temperature, which can be attributed to the liquid thermal expansion. There is a slight increment in the density for the C-MWCNT-DI water nanofluids with an increase in nanoparticle concentration. The increase in density can be attributed to the density of the CMWCNTs, which is higher than that of the base fluid. Hence, increasing the particle loading will increase the density of the nanofluid. The maximum increase in density of the CMWCNT-DI water nanofluid is 0.08% for a nanoparticle concentration of 0.175 wt.% at

16 ACS Paragon Plus Environment

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 29

20℃. However, the density decreases by approximately 0.6% when the temperature is increased from 20 to 40℃ for the same nanoparticle concentration. Table 1. Density of C-MWCNT-DI water nanofluids and DI water as a function of temperature

20 998.00 998.30 998.55 998.80

Concentration/temperature (℃) DI water 0.075 wt% 0.125 wt% 0.175 wt%

Density (kg/m3) 25 996.85 997.25 997.50 997.70

30 995.50 995.80 996.00 996.20

35 993.90 994.15 994.35 994.50

40 992.00 992.25 992.40 992.55

The thermal conductivity of a coolant is one of the parameters that play a significant role in increasing the heat transfer rate of heat exchangers. Hence, the thermal conductivity of the CMWCNT-DI aqueous suspensions was measured experimentally in this study and the results are shown in Fig. 7. The thermal conductivity of the C-MWCNT-DI water nanofluids was plotted as a function of temperature and nanoparticle concentration. It could be noted that only nanofluids with low concentrations of C-MWCNTs were considered in this study in order to prevent a drastic increase in viscosity. The thermal conductivity of the base fluid was compared with that from the National Institute of Standards and Technology (NIST) database and there is good agreement between these values 39, with a maximum error of 2% at 20℃. It is evident from Fig. 7 that the thermal conductivity of the C-MWCNT-DI water nanofluids is significantly greater than that for the base fluid. Moreover, it is evident that the thermal conductivity of the C-MWCNT aqueous suspensions and base fluid increases with an increase in fluid temperature. Nonetheless, the thermal conductivity enhancement is higher for the C-MWCNT-DI water nanofluids at higher nanoparticle concentrations. Based on Fig. 7, it can be deduced that temperature plays a vital role on enhancing the effective thermal conductivity of nanofluids, which is due to the Brownian motion of the C-MWCNTs dispersed in the base fluid

36

. The maximum thermal conductivity enhancement obtained is

20.15% for a nanoparticle concentration of 0.175 wt.% at 50℃. 17 ACS Paragon Plus Environment

Page 19 of 29

0.80 Thermal conddictivity (W/mK)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

C-MWCNTs 0.175 wt% C-MWCNTs 0.125wt% C-MWCNTs 0.075 wt% DI water NIST value for water

0.75 0.70

0.65 0.60 0.55 15

25

35

45

55

temperature (℃)

Fig. 7. Thermal conductivity of C-MWCNT-DI water nanofluids and DI water

3.3. Thermal performance of C-MWCNT-DI water nanofluids To evaluate the reliability and accuracy of the experimental set-up, preliminary experiments were carried out for the base fluid prior to systematic experiments involving nanofluids in the annular heat exchanger. The results for the base fluid flowing through the experimental set-up at constant heat flux boundary conditions were compared with the data calculated using two empirical correlations proposed by Petukhov

40

and Gnielinski41 for turbulent flow regime.

These empirical correlations are given by Eq. (6) and (7) respectively.

𝑁𝑢 =

𝑓 (8)𝑅𝑒𝑃𝑟 0.5

𝑓 1.07 + 12.7 (8)

(6)

(𝑃𝑟

2⁄ 3

− 1)

Where, the friction factor (𝑓) is defined as 𝑓 = (0.79 𝐿𝑛 𝑅𝑒 − 1.64)−2 . It could be noted Eq. (6) is applicable for a Reynolds number range of 4000 < Re < 5(106) and Prandtl number range of 0.5 < Pr < 2000.

𝑁𝑢 =

(𝑓𝑎𝑛𝑛 ⁄8)𝑅𝑒𝑃𝑟 𝑘1 +12.7√𝑓𝑎𝑛𝑛 ⁄8(𝑃𝑟 2⁄3 −1)

𝐷

2⁄3

[1 + ( 𝐿ℎ )

] 𝐹𝑎𝑛𝑛 K

18 ACS Paragon Plus Environment

(7)

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 29

With 𝑘1 = 1.07 +

900 0.63 − 𝑅𝑒 (1 + 10𝑃𝑟)

(8)

Eq. (7) is used for a Reynolds number range of Re >4000, Prandtl number range of 0.1 ≤ Pr ≤ 1000 and(𝐷ℎ ⁄𝐿 ) ≤ 1. The factor “ 𝐹𝑎𝑛𝑛 ” in Eq.7 representing the boundary condition of “heat transfer at the inner wall with the outer wall insulated” and the factor “K” for liquids as variation of fluid properties with temperature can be calculated by Eq.(9) and (10) respectively. 𝐹𝑎𝑛𝑛 = 0.75𝑎−0.17

𝐾=(

(9)

𝑃𝑟𝑏 0.11 ) 𝑃𝑟𝑤

(10)

The friction factor (𝑓𝑎𝑛𝑛 ) in Eq. (7) is given by Gnielinski 41 as: 𝑓𝑎𝑛𝑛 = (1.8 log10 𝑅𝑒 ∗ − 1.5)−2

(11)

Where, (1 + 𝑎2 ) ln 𝑎 + (1 − 𝑎2 ) 𝑅𝑒 = 𝑅𝑒 (1 − 𝑎)2 ln 𝑎

(12)



Fig. 8 shows the comparison between the experimentally measured average Nusselt number and those calculated using the aforementioned empirical correlations for the base fluid at a fixed water inlet temperature of 30ºC. Indeed, the Nusselt number increases with an increase in the Reynolds number, as expected. The maximum error between the values obtained from experiments and Petukhov

40

approximately 3.5 and 9.5%,

and Gnielinski respectively.

41

empirical correlation is found to be

In general, the results obtained from the

experiments are in good agreement with those from empirical correlations within the range of Reynolds number investigated in this study. Hence, it can be deduced that the experimental

19 ACS Paragon Plus Environment

Page 21 of 29

set-up is reliable and it can be utilized to assess the heat transfer properties of the C-MWCNT aqueous suspensions. 80

Average Nusselt number ((Nu)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

70 60 50

40 exprimental data Gnielinski

30

petukhov 20 2000

3000

4000

5000 6000 Reynolds number, Re

7000

8000

9000

Fig. 8. Comparison between the measured Nusselt numbers of DI water with those calculated from empirical correlations

A series of experiments were conducted for the C-MWCNT-DI water nanofluids (nanoparticle concentration: 0.075, 0.125 and 0.175 wt.%) by varying the Reynolds number from 3055 ± 5 to 7944 ± 5 in order to determine the convective heat transfer of the aqueous suspensions in turbulent flow regime. The input power was kept fixed at 900 W. The results are shown in Fig. 9 for a constant inlet temperature of 30℃. It can be observed that the convective heat transfer coefficient increases when the Reynolds number is increased for both the base fluid and C-MWCNT-DI water nanofluids. It can also be observed that the nanoparticle concentration affects the heat transfer coefficient of the nanofluids. The remarkable enhancement in convective heat transfer coefficient of the C-MWCNT-DI water nanofluids is mainly due to the narrow thermal boundary layer resulting from the thermal conductivity enhancement of C-MWCNT-DI water nanofluids as well as a decrease in thermal resistance between the flowing nanofluids and inner wall surface of the annular tube at higher Reynolds number. According to

1, 36

, carbon nanomaterials (e.g. carbon nanotubes

20 ACS Paragon Plus Environment

Energy & Fuels

and graphene nanoplatelets) tend to reduce the thickness of the thermal boundary layer. The specific surface area and Brownian motion of the nanoparticles also play a role in influencing the convective heat transfer coefficient. In this study, the convective heat transfer coefficient of the nanofluids increases by 12.38, 24.1 and 35.89% for a nanoparticle concentration of 0.075, 0.125 and 0.175 wt.%, respectively.

5500 Average Heat transfer coefficient, h (W/m2K)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 29

5000

C-MWCNTs 0.175 wt% C-MWCNTs 0.125 wt%

4500

C-MWCNTs 0.075 wt%

4000

DI water

3500 3000 2500 2000 1500 1000 2000

3000

4000

5000 6000 Reynolds number, Re

7000

8000

9000

Fig. 9. Variation of the average heat transfer coefficient for C-MWCNT/ DI water nanofluids versus Reynolds number

To assess the convective-to-conductive heat transfer ratio of C-MWCNT aqueous suspensions, the average Nusselt number determined from Eq. 4 was plotted as a function of Reynolds number and nanoparticle concentration. The results are shown in Fig. 10 and it can be seen that there is a significant increase in the Nusselt number with an increase in the Reynolds number as well as concentration of C-MWCNTs relative to that for the base fluid. The greater Nusselt number for the C-MWCNT nanofluids is attributed to the higher thermal conductivity of the nanofluids, which is associated with the Brownian motion of the CMWCNTs

42

. The maximum increase in the Nusselt number of the C-MWCNT-DI water

nanofluids is found to be 6.96, 13.66 and 20.15% for a nanoparticle concentration of 0.075, 0.125 and 0.175 wt.%, respectively. This maximum increase is achieved when Re = 7944 ± 5. 21 ACS Paragon Plus Environment

Page 23 of 29

90

Average Nusselt number, Nu

80 70 60 50 C-MWCNTs 0.175 wt%

40

C-MWCNTs 0.125 wt% C-MWCNTs 0.075 wt%

30

DI water 20 2500

3500

4500

5500 6500 Reynolds number, Re

7500

8500

Fig.10. Variation of the Nusselt number for C-MWCNT-DI water nanofluids as a function of Reynolds number

In order to validate the pressure drop accuracy in the experimental set-up, the variation of the measured friction factor for the DI water was compared with the values calculated from empirical correlation proposed by Gnielinski 41 (Eq. 11) and the results are shown in Fig. 11. It can be observed that there is only a slight deviation between the data obtained from experiments and those calculated from empirical model. The deviation between the experimental friction factor values and those calculated using the Gnielinski empirical correlation is less than 4.15%. Hence, it can be stated that the experimental set-up used to measure the pressure drop is validated for the range of Reynolds number investigated in this study.

0.060 Gnielinski

0.055

Friction factor, f

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

experimental

0.050 0.045 0.040 0.035 0.030 2000

3000

4000

5000 6000 7000 Reynolds number, Re

22 ACS Paragon Plus Environment

8000

9000

Energy & Fuels

Fig.11. Plot of the friction factor as a function of Reynolds number for DI water obtained from experiments and empirical correlation

The pressure drop of the C-MWCNT-DI water nanofluids flowing through the test section recorded over a range of Reynolds number is shown in Fig. 12(a). The corresponding friction factor values were calculated using Eq. (5) and the results are shown in Fig. 12(b). The results show that there is a small increment in both the pressure drop and friction factor for the C-MWCNT-DI water nanofluids relative to those for DI water .The maximum increase in the friction factor and pressure drop is found to be ~3% and 23%, respectively, for a nanoparticle concentration of 0.175 wt.%. This increment in pressure drop is mainly due to the slight increment in viscosity for all C-MWCNT-DI water nanofluids (Fig. 6) which required slight increment in fluid velocity since the corresponding Reynolds number is constant (Eq.3). Hence, it can be seen that the velocity of the working fluid plays a vital pattern in increasing the pressure drop and friction factor compared to DI water in convective heat transfer systems. This matter can be acknowledged by revisiting Eq. (5) for the pressure drop and friction factor, and Eq. (3) for the Reynolds number. 700

0.056 C-MWCNTs 0.175 wt% C-MWCNTs 0.125 wt% C-MWCNTs 0.075 wt% DI water

600

C-MWCNTs 0.175 wt% C-MWCNTs 0.125 wt% C-MWCNTs 0.075 wt% DI water

0.052 Friction factor, f

500 ΔP/L (Pa/m)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 29

400 300

0.048

0.044

200 0.04 100

(B)

(A)

0 2000

3000

4000 5000 6000 7000 Reynolds number, Re

8000

0.036 2500

9000

3500

4500 5500 6500 Reynolds number, Re

7500

8500

Fig.12. Plot of (A) pressure drop and (B) friction factor versus the Reynolds number for C-MWCNT-DI water nanofluids in the annular test section

23 ACS Paragon Plus Environment

Page 25 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

The performance index (ε) was calculated using Eq. (13) in order to assess the economic performance of the novel, eco-friendly C-MWCNT-DI water nanofluids synthesized in this study as potential fluids in heat transfer systems such as solar collectors and heat exchangers43.

𝜀=

ℎ𝑛𝑓 ⁄ℎ𝑏𝑓 𝑅ℎ = ∆𝑃𝑛𝑓 ⁄∆𝑃𝑏𝑓 𝑅∆𝑃

(13)

Where, 𝑅∆𝑃 is the ratio of pressure drop of the C-MWCNs aqueous suspensions to the base fluid, and 𝑅ℎ is the ratio of heat transfer enhancement of C-MWCNTs nanofluids relative to the base fluid. Fig. 13 indicates the performance index of the C-MWCNT aqueous suspensions over a range of Reynolds number and various nanoparticle concentrations. It can be observed that the performance index is higher than 1 for all samples, which shows the advantage of using these novel nanofluids in heat transfer systems. It is apparent that the performance index increases with increasing the concentration of C-MWCNTs in the base fluid. This implies that these eco-friendly nanofluids have higher effectiveness when the particle loading is increased. Fig. 13 shows that the performance index of the C-MWCNT nanofluids tends to increase with an increase in the Reynolds number (regardless of the nanoparticle concentration), indicating that the C-MWCNT-DI water nanofluids are suitable alternative coolants for heat transfer applications.

24 ACS Paragon Plus Environment

Energy & Fuels

1.12 C-MWCNTs 0.175 wt% 1.10

C-MWCNTs 0.125 wt% C-MWCNTs 0.075 wt%

1.08

Performance Index

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 26 of 29

1.06 1.04 1.02 1.00 0.98 2000

3000

4000

5000

6000

7000

8000

9000

Reynolds number, Re

Fig. 13. Plot of performance index versus Reynolds number for the C-MWCNT-DI water nanofluids

4. Conclusion An environmentally friendly and cost-effective procedure for synthesizing covalently functionalized multi-walled carbon nanotubes with cloves (C-MWCNTs) has been developed in this study. The C-MWCNT-DI water nanofluids are then prepared by ultra-sonicating CMWCNTs with distilled water as the base fluid for three different nanoparticle concentrations (i.e. 0.075, 0.125 and 0.175 wt.%). The potential of these nanofluids as heat transfer fluids is investigated by convective heat transfer experiments through an annular heat exchanger at turbulent flow regime. The exceptional performance of the functionalization method is confirmed by TGA, FTIR spectroscopy, UV-vis spectroscopy and TEM. Based on the UVvis absorption spectra, the C-MWCNT-DI water nanofluids have remarkable stability over the course of 63 days. Based on the thermo-physical properties of the C-MWCNT-DI water nanofluids, it can be deduced that these nanofluids are potential working fluids in heat transfer systems. It is found that there is significant enhancement in the convective heat transfer coefficient and Nusselt number up to 35.89 and 20.15%, respectively. This 25 ACS Paragon Plus Environment

Page 27 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

significant enhancement is attained at a Reynolds number of 7944, nanoparticle concentration of 0.175 wt.% and constant heat flux of 38346 W/m2. The maximum increase in friction factor of the C-MWCNT-DI water nanofluids is about 3 %, relative to that for the base fluid, for a nanoparticle concentration of 0.175 wt.%. In addition, it is found that the performance index of the C-MWCNT-DI water nanofluids is more than 1 (regardless of the nanoparticle concentration investigated in this study), indicating that these nanofluids are potential working fluids in heat transfer systems in terms of overall thermal performance and energy savings.

Acknowledgement The authors gratefully acknowledge the financial support provided by University of Malaya under the Fundamental Research Grant Scheme (Project no.: FP060-2015A) and University of Malaya Research Grant Scheme (Project no.: RP012B-13AET). The authors also greatly appreciate the assistance provided by the technical and administrative staff of Faculty of Engineering, University of Malaya, in carrying out this study.

References 1.

2.

3. 4.

5.

6.

7. 8.

Ding, Y.; Alias, H.; Wen, D.; Williams, R. A., Heat transfer of aqueous suspensions of carbon nanotubes (CNT nanofluids). International Journal of Heat and Mass Transfer 2006, 49, (1), 240250. Fox, E. B.; Visser, A. E.; Bridges, N. J.; Amoroso, J. W., Thermophysical properties of nanoparticle-enhanced ionic liquids (NEILs) heat-transfer fluids. Energy & Fuels 2013, 27, (6), 3385-3393. Wang, X.-j.; Li, X.; Yang, S., Influence of pH and SDBS on the stability and thermal conductivity of nanofluids. Energy & Fuels 2009, 23, (5), 2684-2689. Devarajan, Y.; Munuswamy, D. B., Analysis on the Influence of Nano Particles of Alumina, Copper Oxide and Zirconium Oxide on the Performance of a Flat Plate Solar Water Heater. Energy & Fuels 2016. Suresh, S.; Venkitaraj, K.; Selvakumar, P.; Chandrasekar, M., Synthesis of Al 2 O 3–Cu/water hybrid nanofluids using two step method and its thermo physical properties. Colloids and Surfaces A: Physicochemical and Engineering Aspects 2011, 388, (1), 41-48. Amiri, A.; Sadri, R.; Ahmadi, G.; Chew, B.; Kazi, S.; Shanbedi, M.; Alehashem, M. S., Synthesis of polyethylene glycol-functionalized multi-walled carbon nanotubes with a microwave-assisted approach for improved heat dissipation. RSC Advances 2015, 5, (45), 35425-35434. Choi, S. U.; Eastman, J. A., Enhanced heat transfer using nanofluids. In Google Patents: 2001. Choi, S.; Zhang, Z.; Yu, W.; Lockwood, F.; Grulke, E., Anomalous thermal conductivity enhancement in nanotube suspensions. Applied physics letters 2001, 79, (14), 2252-2254.

26 ACS Paragon Plus Environment

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

9.

10. 11.

12. 13.

14.

15.

16.

17. 18.

19. 20.

21. 22. 23.

24.

25.

26.

Page 28 of 29

Sadri, R.; Ahmadi, G.; Togun, H.; Dahari, M.; Kazi, S. N.; Sadeghinezhad, E.; Zubir, N., An experimental study on thermal conductivity and viscosity of nanofluids containing carbon nanotubes. Nanoscale research letters 2014, 9, (1), 1-16. Philip, J.; Shima, P.; Raj, B., Enhancement of thermal conductivity in magnetite based nanofluid due to chainlike structures. Applied physics letters 2007, 91, (20), 203108. Pak, B. C.; Cho, Y. I., Hydrodynamic and heat transfer study of dispersed fluids with submicron metallic oxide particles. Experimental Heat Transfer an International Journal 1998, 11, (2), 151170. Abu-Nada, E.; Oztop, H. F., Effects of inclination angle on natural convection in enclosures filled with Cu–water nanofluid. International Journal of Heat and Fluid Flow 2009, 30, (4), 669-678. Abu-Nada, E.; Masoud, Z.; Hijazi, A., Natural convection heat transfer enhancement in horizontal concentric annuli using nanofluids. International Communications in Heat and Mass Transfer 2008, 35, (5), 657-665. Duangthongsuk, W.; Wongwises, S., Heat transfer enhancement and pressure drop characteristics of TiO 2–water nanofluid in a double-tube counter flow heat exchanger. International Journal of Heat and Mass Transfer 2009, 52, (7), 2059-2067. Izadi, M.; Behzadmehr, A.; Jalali-Vahida, D., Numerical study of developing laminar forced convection of a nanofluid in an annulus. International journal of thermal sciences 2009, 48, (11), 2119-2129. Pramanik, N. B.; Singha, N. K., Direct functionalization of multi-walled carbon nanotubes (MWCNTs) via grafting of poly (furfuryl methacrylate) using Diels–Alder “click chemistry” and its thermoreversibility. RSC Advances 2015, 5, (114), 94321-94327. Gan, Y.; Qiao, L., Optical properties and radiation-enhanced evaporation of nanofluid fuels containing carbon-based nanostructures. Energy & Fuels 2012, 26, (7), 4224-4230. Salavati-Niasari, M.; Bazarganipour, M., Synthesis, characterization and catalytic oxidation properties of multi-wall carbon nanotubes with a covalently attached copper (II) salen complex. Applied Surface Science 2009, 255, (17), 7610-7617. Yu, M.-F.; Files, B. S.; Arepalli, S.; Ruoff, R. S., Tensile loading of ropes of single wall carbon nanotubes and their mechanical properties. Physical review letters 2000, 84, (24), 5552. Bazarganipour, M.; Salavati-Niasari, M., Synthesis, characterization and chemical binding of a Ni (II) Schiff base complex on functionalized MWNTs; Catalytic oxidation of cyclohexene with molecular oxygen. Chemical Engineering Journal 2016, 286, 259-265. Harris, P., Carbon Nanotubes and Related Structures: New Materials for the Twenty-first Century. 1999. In Cambridge University Press, Cambridge. Otsubo, Y.; Fujiwara, M.; Kouno, M.; Edamura, K., Shear-thickening flow of suspensions of carbon nanofibers in aqueous PVA solutions. Rheologica acta 2007, 46, (7), 905-912. Zubir, M. N. M.; Badarudin, A.; Kazi, S. N.; Misran, M.; Ibrahim, R.; Amiri, A.; Sadri, R., Exploration of the environmentally benign and highly effective approach for improving carbon nanotube homogeneity in aqueous system. Journal of Thermal Analysis and Calorimetry 2016, 124, (2), 815-825. Mohd Zubir, M. N.; Badarudin, A.; Kazi, S.; Nay Ming, H.; Sadri, R.; Amiri, A., Investigation on the Use of Graphene Oxide as Novel Surfactant for Stabilizing Carbon Based Materials. Journal of Dispersion Science and Technology 2016, 37, (10), 1395-1407. Salavati-Niasari, M.; Badiei, A.; Saberyan, K., Oxovanadium (IV) salophen complex covalently anchored to multi-wall carbon nanotubes (MWNTs) as heterogeneous catalyst for oxidation of cyclooctene. Chemical Engineering Journal 2011, 173, (2), 651-658. Amiri, A.; Sadri, R.; Shanbedi, M.; Ahmadi, G.; Chew, B.; Kazi, S.; Dahari, M., Performance dependence of thermosyphon on the functionalization approaches: an experimental study on thermo-physical properties of graphene nanoplatelet-based water nanofluids. Energy Conversion and Management 2015, 92, 322-330.

27 ACS Paragon Plus Environment

Page 29 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

27. Sarsam, W. S.; Amiri, A.; Kazi, S.; Badarudin, A., Stability and thermophysical properties of noncovalently functionalized graphene nanoplatelets nanofluids. Energy Conversion and Management 2016, 116, 101-111. 28. Yang, Y.; Qiu, S.; Xie, X.; Wang, X.; Li, R. K. Y., A facile, green, and tunable method to functionalize carbon nanotubes with water-soluble azo initiators by one-step free radical addition. Applied Surface Science 2010, 256, (10), 3286-3292. 29. Tasis, D.; Tagmatarchis, N.; Bianco, A.; Prato, M., Chemistry of carbon nanotubes. Chemical reviews 2006, 106, (3), 1105-1136. 30. Peng, X.; Wong, S. S., Functional covalent chemistry of carbon nanotube surfaces. Advanced Materials 2009, 21, (6), 625-642. 31. Yang, Y.; Qiu, S.; He, C.; He, W.; Yu, L.; Xie, X., Green chemical functionalization of multiwalled carbon nanotubes with poly (ɛ-caprolactone) in ionic liquids. Applied Surface Science 2010, 257, (3), 1010-1014. 32. Neveu, V.; Perez-Jimenez, J.; Vos, F.; Crespy, V.; du Chaffaut, L.; Mennen, L.; Knox, C.; Eisner, R.; Cruz, J.; Wishart, D., Phenol-Explorer: an online comprehensive database on polyphenol contents in foods. Database 2010, 2010, bap024. 33. Parthasarathy, V. A.; Chempakam, B.; Zachariah, T. J., Chemistry of spices. CABI: 2008. 34. Mohammed, K. A. K.; Abdulkadhim, H. M.; Noori, S. I., Chemical Composition and Anti-bacterial Effects of Clove (Syzygium aromaticum) Flowers. Int. J. Curr. Microbiol. App. Sci 2016, 5, (2), 483-489. 35. Fernandez-Seara, J.; Uhía, F. J.; Sieres, J.; Campo, A., A general review of the Wilson plot method and its modifications to determine convection coefficients in heat exchange devices. Applied Thermal Engineering 2007, 27, (17), 2745-2757. 36. Aravind, S. J.; Baskar, P.; Baby, T. T.; Sabareesh, R. K.; Das, S.; Ramaprabhu, S., Investigation of structural stability, dispersion, viscosity, and conductive heat transfer properties of functionalized carbon nanotube based nanofluids. The Journal of Physical Chemistry C 2011, 115, (34), 16737-16744. 37. Ko, G. H.; Heo, K.; Lee, K.; Kim, D. S.; Kim, C.; Sohn, Y.; Choi, M., An experimental study on the pressure drop of nanofluids containing carbon nanotubes in a horizontal tube. International journal of heat and mass transfer 2007, 50, (23), 4749-4753. 38. Sadri, R.; Zangeneh Kamali, K.; Hosseini, M.; Zubir, N.; Kazi, S.; Ahmadi, G.; Dahari, M.; Huang, N.; Moradi, A., Experimental Study on Thermo-Physical and Rheological Properties of Highly Stable and Green Reduced Graphene Oxide Nanofluids: Hydrothermal Assisted Technique. Journal of Dispersion Science and Technology 2016, (just-accepted). 39. Ramires, M. L.; de Castro, C. A. N.; Nagasaka, Y.; Nagashima, A.; Assael, M. J.; Wakeham, W. A., Standard reference data for the thermal conductivity of water. Journal of Physical and Chemical Reference Data 1995, 24, (3), 1377-1381. 40. Petukhov, B., Heat transfer and friction in turbulent pipe flow with variable physical properties. Advances in heat transfer 1970, 6, 503-564. 41. Gnielinski, V., Turbulent Heat Transfer in Annular Spaces—A New Comprehensive Correlation. Heat Transfer Engineering 2015, 36, (9), 787-789. 42. Sundar, L. S.; Singh, M. K.; Sousa, A. C., Enhanced heat transfer and friction factor of MWCNT– Fe 3 O 4/water hybrid nanofluids. International Communications in Heat and Mass Transfer 2014, 52, 73-83. 43. Amiri, A.; Sadri, R.; Shanbedi, M.; Ahmadi, G.; Kazi, S.; Chew, B.; Zubir, M. N. M., Synthesis of ethylene glycol-treated graphene nanoplatelets with one-pot, microwave-assisted functionalization for use as a high performance engine coolant. Energy Conversion and Management 2015, 101, 767-777.

28 ACS Paragon Plus Environment