Fabrication of Hydrophilic and Hydrophobic Sites on Polypropylene

Feb 26, 2016 - School of Environmental and Chemical Engineering, Tianjin Polytechnic ... Tianjin Engineering Center for Safety Evaluation of Water Qua...
0 downloads 0 Views 2MB Size
Subscriber access provided by UNIV OF SOUTHERN QUEENSLAND

Article

Fabrication of hydrophilic and hydrophobic sites on polypropylene nonwoven for oil spill cleanup: Two dilemmas affecting oil sorption Xiangyu Zhou, Feifei Wang, Yali Ji, Weiting Chen, and Junfu Wei Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.5b06007 • Publication Date (Web): 26 Feb 2016 Downloaded from http://pubs.acs.org on February 28, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 22

Environmental Science & Technology

1

Fabrication of hydrophilic and hydrophobic sites on polypropylene nonwoven

2

for oil spill cleanup: Two dilemmas affecting oil sorption

3

Xiangyu Zhou1, 2, 3, Feifei Wang1, 3, Yali Ji1, 2, Weiting Chen1, 2, Junfu Wei1, 2, 4 *

4

1. State Key Laboratory of Hollow Fiber Membrane Materials and Processes, Tianjin

5

Polytechnic University, Tianjin 300387, P.R. China;

6

2. School of Environmental and Chemical Engineering, Tianjin Polytechnic

7

University, Tianjin 300387, P.R. China;

8

3. School of Materials Science and Engineering, Tianjin Polytechnic University,

9

Tianjin 300387, P.R. China

10

4. Tianjin Engineering Center for Safety Evaluation of Water Quality & Safeguards

11

Technology, Tianjin 300387, China

12 13 14 15 16 17

Correspondence to: Junfu Wei *([email protected]).

18

School of Environmental and Chemical Engineering, Tianjin Polytechnic University,

19

Tianjin 300387, P.R. China.

20

Tel.: +86-022-8395-5898

21 22

ACS Paragon Plus Environment

Environmental Science & Technology

23

Abstract

24

This article mainly deals with following dilemmas, which affect oil sorption and

25

sorbent preparation: (1) hydrophobization could facilitate oil sorption but had adverse

26

impacts on emulsion sorption; (2) Micropores of conventional oil sorbent did not

27

exhibit effectiveness to emulsion sorption. To solve above contradictions, hydrophilic

28

and hydrophobic sites were fabricated onto polypropylene (PP) nonwoven through

29

electron beam (EB) radiation and subsequent ring-opening reaction. Further, a similar

30

structure without hydrophilic site was constructed as comparison to verify the

31

dilemmas. Oil sorption and emulsion adsorption experiment revealed that the PP

32

nonwoven with specific hydrophilic and hydrophobic sites is more suitable for oil

33

cleanup. The hydrophobic site preserved its hydrophobicity and sorption capacity, and

34

the hydrophilic site on PP surface effectively increased the affinity between the

35

hydrophilic interface of emulsion and sorbent. The overlapped and intertwined

36

structures could provide spaces that large enough to accommodate oil and emulsion.

37

In addition, the oil and emulsion sorption behaviors were systematically analyzed.

38

The PP nonwoven fabricated in this study may find practical application in the

39

cleanup of oil spills and the removal of organic pollutants from water surfaces.

40

1. Introduction

41

With the rapid growth of offshore oil production and transportation, oil spillage and

42

chemical leakage accidents occur frequently worldwide. Such accidents can cause

43

severe ecological disasters and the cleanup of these organic pollutants from water

44

sources is a major environmental issue that continues to attract a great deal of

ACS Paragon Plus Environment

Page 2 of 22

Page 3 of 22

Environmental Science & Technology

45

attention.1-4 Current strategies used to tackle these problems can be usually

46

categorized into three main types: physical methods (e.g. sorbents skimmers, booms),

47

chemical methods (i.e. in situ burning, solidifiers), and biological methods (e.g.

48

bioremediation).5,6 Among these methods, sorbents are considered as economical and

49

efficient countermeasures for combating oil spills.7-9

50

It is generally considered that the excellent oil sorbent should have following

51

characteristics: (1) Hydrophobicity. Component analysis reveals that crude oil mainly

52

consists of paraffins (alkanes that can be linear or branched), naphthenes

53

(non-aromatic multi-ring structures) and aromatic compounds.10 Thus enhancing

54

hydrophobicity of sorbent surface will facilitate the Van der Waals force or

55

hydrophobic interaction between oil molecules and sorbent and increase the sorption

56

capacity. (2) Sufficient porosity and large specific surface area. Sorbents with

57

sufficient specific surface area and porosity will provide enough sorption sites or

58

spaces for oil entrapment. Guided by above principles, most researches of oil sorbent

59

materials are focused on hydrophobic modification and porous structure development.

60

In recent years, numerous superhydrophobic sorbents (contact angle > 150o) with

61

spectacular specific surface area such as carbon fiber, aerogel, carbon nanotube

62

sponge, etc. have been developed as promising candidates for potential

63

application.11-15

64

However, both principles are on the basis of ideal experiments. It should be noted

65

that researchers on fabrication of oil sorbent are excessively focused on sorption

66

capacity, but ignore a fundamental fact: the complexity of natural water and crude oil.

ACS Paragon Plus Environment

Environmental Science & Technology

67

Some chemicals in practical contaminated water e.g., auxiliary agent used in oil

68

production, surfactant discharged in ecological environment, metabolites of marine

69

creatures, etc. can be regarded as emulsifiers or dispersants. Apart from oil spreading

70

over water, plenty of oil is in the form of oil-in-water emulsion and steadily exists in

71

natural water.10 Compared with surface spill, the oil emulsion has quite different

72

physical nature and morphological structure. Figure 1 reveals the schematic diagram

73

of typical oil slicks. Generally, the hydrophobic ends of emulsifiers are embedded in

74

the oil droplet and the hydrophilic groups are exposed to water. The stable structure in

75

water indicates that the oil emulsion is actually hydrophilic. This can be viewed as the

76

first dilemma: Enhancing the affinity between oil molecule and sorbent means

77

increasing the hydrophobicity of sorbent surface. However, excessively hydrophobic

78

nature weakens the interaction between the hydrophilic emulsion and hydrophobic

79

sorbent. This dilemma seriously impedes the sorption efficiency and performance in

80

application. We believe that the key to conquer the first challenge is amphiphilicity.

81

This notion is originated from biochemistry and widely researched in pollution

82

resistance and cell adhesion. Inspired by this notion, the hydrophilic and the

83

hydrophobic sites were introduced onto polypropylene (PP) nonwoven, which is the

84

most commercialized material for oil sorption.16 The amphiphilic modification will

85

perfectly solve the problem.

86

ACS Paragon Plus Environment

Page 4 of 22

Page 5 of 22

Environmental Science & Technology

87 88

Figure 1. Schematic diagram of typical oil slicks.

89

Another dilemma pertains to the pore size of sorbent. In recent years, many

90

researchers have been attempting to improve the sorption performance of oil sorbent.

91

Theoretically, remarkable oil sorbents should have excellent sorption capacity for oil,

92

which means the oil sorbent should theoretically provide enough spaces or sites to

93

accommodate oil molecules. Accordingly, researchers have developed numerous

94

sorbents with huge specific surface area and porosity. However, they seem to ignore

95

the diameter of emulsified oil droplet in real application. For many oil sorbents, it

96

may be unsuitable for emulsion sorption, because the emulsion can not penetrate into

97

the micropores of sorbent.

98

Thus in this study, two dilemmas on oil sorption and sorbent preparation were

99

proposed: (1) hydrophobization could facilitate oil sorption but had adverse impacts

100

on emulsion sorption; (2) Micropores of conventional oil sorbent did not exhibit

ACS Paragon Plus Environment

Environmental Science & Technology

101

effectiveness to emulsion sorption. Accordingly, hydrophilic and hydrophobic sites

102

were fabricated onto PP nonwoven fabric. The hydrophobic site preserved its

103

hydrophobicity and sorption capacity. The hydrophilic site on PP surface effectively

104

increased the affinity between the hydrophilic interface of emulsion and sorbent. As a

105

result, the emulsion could be adsorbed as well. In addition, the overlapped and

106

intertwined structures of PP nonwoven provided enough interspaces that large enough

107

to accommodate oil emulsion. The PP nonwoven fabricated in this study may find

108

practical application in the cleanup of oil spills and the removal of organic pollutants

109

from water surface.

110

2. Experimental section

111

2.1 Sorbent preparation. The polypropylene nonwoven with hydrophilic and

112

hydrophobic site was prepared by grafting of glycidyl methacrylate (GMA) onto PP

113

nonwoven through electron beam (EB) radiation induced graft polymerization, and

114

subsequently converted the epoxy group of GMA to hydrophilic hydroxyl and

115

hydrophobic long-chain alkylamine through reaction with n-octylamine.17 The

116

schematics of surface modification are shown in Figure 2.

ACS Paragon Plus Environment

Page 6 of 22

Page 7 of 22

Environmental Science & Technology

117 118

Figure 2. Synthetic route and chemical structure of PP-g-GMA-OA nonwoven.

119

2.2 Characterization. The surface morphologies of PP nonwoven were observed

120

using the scanning electron microscopy (SEM) by an S-2500C (Hitachi, Japan)

121

microscope (Figure S1). The surface chemical composition of polypropylene

122

nonwoven was characterized by X-ray photoelectron spectroscopy (XPS), and the

123

analysis was carried out on an AEM PHI 5300X spectrometer with an Al Kα X-ray

124

source (1486.71 eV of photons) to determine the C, N and O (Figure S2). The

125

software package Thermo Avantage 3.9.3 was used to fit the spectra peaks. To analyze

126

the functional groups on the surface of PP samples, the FTIR spectra was recorded on

127

Fourier transform infrared spectrometer (Necolet 6700, USA) in the wavenumber

128

range of 600-4000 cm-1 under ambient condition (Figure S3). To observe the

129

three-dimensional structures of PP substrate, confocal laser scanning microscopy

130

(Leica TCS SP8, Germany) was utilized in this study. In addition, the emulsion

131

diameters were recorded by dynamic light scattering analyzer (Beckman Coulter LS

132

13-320, USA).

ACS Paragon Plus Environment

Environmental Science & Technology

133

2.3 Oil sorption experiment. The practical use of sorbent for oil cleanup might

134

take place in the presence of water. In a typical measurement of this study, 400ml of

135

water was poured into a 500 ml glass beaker with appropriate oil to form 6 mm oil

136

film. Diesel, gasoline, crude oil (ρ 0.89g/mL, γ 0.032 N/m, η 0.132 Pas), kerosene and

137

toluene were employed. The PP nonwoven (3 × 3 cm) was slowly placed on oil

138

surface for oil/water sorption. After 30 min of sorption, the samples were weighed and

139

the oil sorption capacity was calculated as:

140

‫ݍ‬୫ = (݉୤ − ݉଴ )/݉଴

141

where qm is the maximum sorption capacity (g/g), mf is the final weight of the of

142

samples after sorption and m0 is the initial weight of PP samples. All the sorption

143

measurements were performed in triplicate.

(1)

144

2.4 Emulsion adsorption experiment. In this section, sodium dodecylbenzene

145

sulfonate (SDBS), sodium dodecyl sulfate (SDS) and Tween 80 (C64H124O26) were

146

used to stabilize diesel emulsion. Predetermined surfactant (0.05g for SDBS and SDS,

147

100 µL for Tween 80) was added to 500mL water with 5mL diesel under the agitation

148

of 1000 rpm. After equilibrium, the mixture was stabilized and separated. The

149

emulsion phase was selected for emulsion adsorption experiment. The concentration

150

of oil in emulsion phase was measured by analyzing the total organic carbon (TOC) in

151

the mixture.

152

3. Results and discussion

153

3.1 Explorations on hydrophobicity. As discussed previously, the weak interaction

154

between hydrophobic sorbent surface and hydrophilic interface of emulsion may

ACS Paragon Plus Environment

Page 8 of 22

Page 9 of 22

Environmental Science & Technology

155

hinder the sorption process. To test this hypothesis, a similar structure without

156

hydrophilic site is fabricated. It is noticed that the structure of lauryl methacrylate

157

(LMA) is similar to grafted monomer in this study but lacks the hydrophilic part

158

(Figure 3a). Therefore, PP-g-LMA nonwoven is prepared as comparison. The contact

159

angle (CA) is a parameter of surface wettability and is demonstrated in Figure 3b. It is

160

demonstrated that hydrophobic LA monomers significantly raised the contact angle

161

(from 111.3o to 130.7o), while the hydrophilic site reduced the contact angle (41.7o).

162

However, due to the addition of hydrophobic site and inherent hydrophobicity of PP

163

substrate, the water droplet cannot completely penetrate into the nonwoven.

164

165 166

Figure 3. (a) Structure of PP-g-GMA-OA and PP-g-LMA nonwoven and (b) water

ACS Paragon Plus Environment

Environmental Science & Technology

167

contact angle of PP substrate, PP-g-GMA-OA and PP-g-LMA nonwoven.

168

The results of emulsion adsorption are presented in Figure 4a. Compared with

169

initial concentration, the hydrophobic PP-g-LMA nonwoven showed little sorption

170

capacity towards emulsion. The tiny decrease of TOC may be ascribed to the

171

dissolved and dispersed ingredient of diesel that adsorbed on PP-g-LMA. Meanwhile,

172

PP-g-GMA-OA nonwoven presented a considerable effect and approximately 60-70%

173

of TOC can be removed. We believe that the most predominant reason for this

174

phenomenon is the special structure of emulsion. For oil-in-water emulsion, the

175

hydrophilic end of surfactant faces outward, which lower the interaction between the

176

hydrophilic interface and hydrophobic surface. In other words, the hydrophilic

177

interface impedes the contact of emulsion and sorbent (Figure 4b). However, the

178

hydrophilic site on PP-g-GMA-OA reduces these diffusion resistances and increases

179

their interaction. Thus emulsion adsorption could take place.

180

The results can be explained by capillary theory. Previous studies revealed that the

181

capillary action played a dominant role in oil sorption, which can be quantitatively

182

described by Young-Laplace equation:18

183

∆ܲ =

184

where ∆P is capillary pressure between PP filaments. γlν is surface tension that liquid

185

oil spreads on solid PP surface. θ is contact angle of oil and PP substrate. r is

186

equivalent radius of capillary. In theory, the addition of surfactant will significantly

187

decrease the surface tension γlν and accordingly the capillary as the driving force for

188

oil sorption is seriously affected. However, the hydrophilic site on PP surface could

ଶఊౢν ୡ୭ୱఏ ௥

(2)

ACS Paragon Plus Environment

Page 10 of 22

Page 11 of 22

Environmental Science & Technology

189

counteract this decline. Amphiphilic PP-g-GMA-OA nonwoven still had strong

190

affinity to oil emulsion.

191 192

Figure 4. (a) Emulsion adsorption experiment and (b) schematic of hydrophobic

193

sorbent surface and hydrophilic emulsion interface.

194

Many studies mentioned the sorption selectivity, i.e. the sorbent should adsorb oil

195

preferentially instead of water.19,20 Figure 5a reveals the pure oil sorption experiment

196

on water surface. Compared with hydrophobic PP-g-LMA nonwoven, merely a small

197

decrease could be observed and amphiphilic PP-g-GMA-OA nonwoven showed a

198

moderate sorption capacity. The optical microscope images of emulsion before and

199

after PP-g-GMA-OA sorption are shown in Figure S4. Importantly, no obvious water

ACS Paragon Plus Environment

Environmental Science & Technology

200

uptake was observed. We considered that this is mainly ascribed to the inherent

201

hydrophobicity of polypropylene substrate (hydrophobic carbon backbone) and the

202

introduction of hydrophobic site. Another point we believe is that, due to the lower

203

densities of oil and PP substrate, they will contact preferentially on the surface of

204

water. This initial oil sorption step can be regarded as hydrophobic coating in some

205

sense. Thus some hydrophilic natural materials such as woolen, cotton and so forth

206

can be utilized in oil sorption as well.21,22 The dynamic sorption process of oil droplet

207

(toluene, 0.8µL) on PP-g-GMA-OA nonwoven is presented in Figure 5b. The droplet

208

could rapidly penetrate into the nonwoven within 0.36s, which indirectly reveals the

209

loose structure and hydrophobic nature of PP substrate.

210 211

Figure 5. (a) Oil sorption experiment and (b) dynamic sorption process of toluene

ACS Paragon Plus Environment

Page 12 of 22

Page 13 of 22

Environmental Science & Technology

212

droplet.

213

3.2 Explorations on porous structure. In recent years, most researchers have been

214

attempting to enhance the sorption capacity of sorbent. As mentioned above, an

215

excellent sorbent should provide enough spaces to accommodate oil molecules.

216

However, most researchers seemed to ignore the diameter of oil emulsion. Generally,

217

sorbent with abundant porosity and large specific surface area usually have

218

micropores. Figure 6 demonstrates the optical microscope image and diameter

219

distribution of emulsified oil (SDBS+diesel in section 2.4) in aqueous solution. It can

220

be observed that the light interface wraps the emulsion and the diameter of oil

221

emulsion is in the range of 1-100 µm. The median particle diameters (D0.5) calculated

222

by dynamic light scattering analyzer is 20.7 µm, which is much larger than typical

223

pore size (micropore < 2nm, mesopore 2-50nm, macropore >50nm). Although the

224

emulsion diameter could be influenced by factors such as agitation, surfactant and oil

225

types, surfactant and oil content, etc., a typical emulsion diameter is mostly in the

226

range of micron-scale.23 The differences of oil diameter and pore size may in turn

227

impact the emulsion adsorption.

228 229

Figure 6. (a) Optical microscope image and (b) diameter distribution of emulsified oil.

ACS Paragon Plus Environment

Environmental Science & Technology

230

In fact, due to the complexity of emulsion structure and poor sorption performance,

231

seldom studies have focused on emulsion sorption process. It is assumed that the

232

process may occur in either of the following ways: (1) Due to the stronger

233

hydrophobic interaction between oil molecules and sorbent, the oil is adsorbed

234

preferentially, and the surfactant is released. In other words, this process can be seen

235

as demulsification. (2) The emulsified oil is adsorbed onto or penetrates into sorbent

236

pores as a whole. In this case, both the oil and surfactant molecules are adsorbed.

237

It is difficult to directly observe this process at molecular level. However, it is noted

238

that the major differences for both processes are the content of oil and surfactant that

239

remained in solution. In this part, toluene and SDBS were utilized to simulate

240

emulsion and the contents of the compositions before and after sorption were

241

quantitatively detected by high performance liquid chromatography (HPLC). The

242

result indicated that the content of toluene and SDBS reduced simultaneously,

243

revealing that the emulsion was adsorbed as a whole and nonselective sorption

244

occurred (Figure7).

245 246

Figure 7. Schematic of emulsion adsorption on PP substrate.

ACS Paragon Plus Environment

Page 14 of 22

Page 15 of 22

Environmental Science & Technology

247

Theoretically, adsorption is an exothermic and the energy that discharged in

248

physical adsorption is usually less that 42 kJ/mol.24 Apparently, the energy discharged

249

in sorption can not afford to break emulsion. In addition, the hydrophobic interaction

250

is not a selective driving force. Thus the emulsion was adsorbed onto PP-g-GMA-OA

251

nonwoven as a whole. This test reveals that appropriate pore size is needed in oil

252

sorption. If the pore size is far less than emulsion diameter, the emulsion droplet may

253

not penetrate into the tiny pores. In this case, most of specific surface area and pore

254

volume of sorbent are wasted (Figure 8).

255 256

Figure 8. Schematic of emulsion diameter and conventional pores.

257

Compared with porous materials, the overlapped and intertwined structure of PP

258

filament perfectly solves this contradiction. The scanning electron microscope (SEM)

259

and three-dimensional confocal laser scanning images of PP nonwoven are shown in

260

Figure 9. Even though there are no porous structure that can be observed on the

261

smooth surface (Figure 9a), the overlapped and intertwined structure provides enough

262

macropores that in the range of micron-scale for oil uptake. The emulsion can be

ACS Paragon Plus Environment

Environmental Science & Technology

263

stored in the interspaces of PP filaments.

264 265

Figure 9. (a) Scanning electron microscope image and (b) three-dimensional

266

confocal laser scanning image of PP nonwoven.

267

4. Conclusion

268

In summary, two dilemmas affecting oil sorption in practical application were

269

proposed. The first is that hydrophobicity could enhance the hydrophobic interaction

270

between oil and sorbent, but lower the affinity of hydrophilic emulsion interface. The

271

second pertains to the pore size. HPLC analysis revealed that the emulsion was

272

adsorbed as a whole. Typical pore size (micropore < 2nm, mesopore 2-50nm,

273

macropore >50nm) is much smaller than emulsion diameter (micron-scale), thus

ACS Paragon Plus Environment

Page 16 of 22

Page 17 of 22

Environmental Science & Technology

274

leading to the fact that the emulsion droplet cannot penetrate into the tiny pores.

275

Accordingly, to overcome the challenges inherent in adsorbing both emulsified and

276

liquid oil, hydrophilic and hydrophobic sites were fabricated onto polypropylene (PP)

277

nonwoven through electron beam (EB) radiation and subsequent ring-opening

278

reaction. On the one hand, the hydrophobic site preserved its hydrophobicity and

279

sorption capacity. On the other hand, the hydrophilic site on PP surface effectively

280

increased the affinity between the hydrophilic interface of emulsion and sorbent. As a

281

result, the emulsion could be adsorbed as well. In addition, the overlapped and

282

intertwined structures of PP nonwoven provided interspaces that large enough to

283

accommodate oil emulsion.

284

Acknowledgements

285

This research was supported by the National Natural Science Foundation of China

286

(No. 41301542), National High Technology Research and Development Program of

287

China (2013AA065601) and Key Technologies R&D Program of Tianjin

288

(15ZCZDSF00880).

289

Supporting Information Available

290

Experimental details and characterizations of original and modified PP nonwoven are

291

presented. This material is available free of charge via the Internet at

292

http://pubs.acs.org.

293

References

294

(1) Conmy, R. N.; Coble, P. G.; Farr, J.; Wood, A. M.; Lee, K.; Pegau, W. S.; Lacoste,

295

J. Submersible optical sensors exposed to chemically dispersed crude oil: wave tank

ACS Paragon Plus Environment

Environmental Science & Technology

296

simulations for improved oil spill monitoring. Environ. Sci. Technol. 2014, 48,

297

1803-1810.

298

(2) Bi, H.; Yin, Z.; Cao, X.; Xie, X.; Tan, C.; Huang, X.; Zhang, H. Carbon fiber

299

aerogel made from raw cotton: a novel, efficient and recyclable sorbent for oils and

300

organic solvents. Adv. Mater. 2013, 25, 5916-5921.

301

(3) Chen, B.; Ma, Q.; Tan, C.; Lim, T.; Huang, L.; Zhang, H. Carbon-based sorbents

302

with three-dimensional architectures for water remediation. Small 2015, 11,

303

3319-3336.

304

(4) Franco, C. A.; Nassar, N. N.; Cortés, F. B. Removal of oil from oil-in-saltwater

305

emulsions by adsorption onto nano-alumina functionalized with petroleum vacuum

306

residue. J. Colloid Interf. Sci. 2014, 433, 58-67.

307

(5) Wahi, R.; Chuah, L. A.; Choong, T. S. Y.; Ngaini, Z.;Nourouzi, M. M. Oil removal

308

from aqueous state by natural fibrous sorbent: an overview. Sep. Purif. Technol. 2013,

309

113, 51–63.

310

(6) Al-Majed, A. A.; Adebayo, A. R.; Hossain, M. E. A sustainable approach to

311

controlling oil spills. J. Environ. Manage. 2012, 113, 213-227.

312

(7) Wang, F.; Sheng, L.; Li, C.; Ou, J.; Xue, M.; Wen, L. Superhydrophobic Cu mesh

313

combined with a superoleophilic polyurethane sponge for oil spill adsorption and

314

collection. Ind. Eng. Chem. Res. 2014, 53, 7141-7148.

315

(8) Deschamps, G.; Caruel, H.; Borredon, M. E.; Bonnin, C.; Vignoles, C. Oil

316

removal from water by selective sorption on hydrophobic cotton fibers. 1. Study of

317

sorption properties and comparison with other cotton fiber-based sorbents. Environ.

ACS Paragon Plus Environment

Page 18 of 22

Page 19 of 22

Environmental Science & Technology

318

Sci. Technol. 2003, 37, 1013-1015.

319

(9) Deschamps, G.; Caruel, H.; Borredon, M. E.; Albasi, C.; Riba, J. P.; Bonnin, C.;

320

Vignoles, C. Oil removal from water by sorption on hydrophobic cotton fibers. 2.

321

Study of sorption properties in dynamic mode. Environ. Sci. Technol. 2003, 37,

322

5034-5039.

323

(10) Hubbe, M. A.; Rojas, O. J.; Fingas, M.; Gupta, B. S. Cellulosic substrates for

324

removal of pollutants from aqueous systems: A Review. 3. Spilled oil and emulsified

325

organic liquids. BioResources 2013, 8, 3038-3097.

326

(11) Fan, Z.; Yan, J.; Ning, G.; Wei, T.; Qian, W.; Zhang, S.; Wei, F. Oil sorption and

327

recovery by using vertically aligned carbon nanotubes. Carbon 2010, 48, 4197-4200.

328

(12) Wang, D.; McLaughlin, E.; Pfeffer, R.; Lin, Y. S. Adsorption of oils from pure

329

liquid and oil–water emulsion on hydrophobic silica aerogels. Sep. Purif.

330

Technol. 2012, 99, 28-35.

331

(13) Duan, B.; Gao, H.; He, M.; Zhang, L. Hydrophobic Modification on Surface of

332

Chitin Sponges for Highly Effective Separation of Oil. ACS Appl. Mater. Inter. 2014,

333

6, 19933-19942.

334

(14) Wu, Z. Y.; Li, C.; Liang, H. W.; Zhang, Y. N.; Wang, X.; Chen, J. F.; Yu, S. H.

335

Carbon nanofiber aerogels for emergent cleanup of oil spillage and chemical leakage

336

under harsh conditions. Sci. Rep. 2014, 4.

337

(15) Kabiri, S.; Tran, D. N. H.; Altalhi, T.; Losic, D. Outstanding adsorption

338

performance

339

removal. Carbon 2014, 80, 523-533.

of

graphene–carbon

nanotube

aerogels

ACS Paragon Plus Environment

for

continuous

oil

Environmental Science & Technology

340

(16) Wei, Q. F.; Mather, R. R.; Fotheringham, A. F.; Yang, R. D. Evaluation of

341

nonwoven polypropylene oil sorbents in marine oil-spill recovery. Mar. Pollut.

342

Bull. 2003, 46, 80-783.

343

(17) Zhou, X.; Wei, J.; Liu, K.; Liu, N.; Zhou, B. Adsorption of bisphenol a based on

344

synergy between hydrogen bonding and hydrophobic interaction. Langmuir 2014, 30,

345

13861-13868.

346

(18) Rengasamy, R. S.; Das, D.; Karan, C. P. Study of oil sorption behavior of filled

347

and structured fiber assemblies made from polypropylene, kapok and milkweed

348

fibers. J. Hazard. Mater. 2011, 186, 526-532.

349

(19) Payne, K. C.; Jackson, C. D.; Aizpurua, C. E.; Rojas, O. J.; Hubbe, M. A. Oil

350

spills abatement: factors affecting oil uptake by cellulosic fibers. Environ. Sci.

351

Technol. 2012, 46, 7725-7730.

352

(20) Haitao, Z.; Shanshan, Q.; Wei, J.; Daxiong, W.; Canying, Z. Evaluation of

353

electrospun polyvinyl chloride/polystyrene fibers as sorbent materials for oil spill

354

cleanup. Environ. Sci. Technol. 2011, 45, 4527-4531.

355

(21) Singh, V.; Kendall, R. J.; Hake, K.; Ramkumar, S. Crude oil sorption by raw

356

cotton. nd. Eng. Chem. Res. 2013, 52, 6277-6281.

357

(22) Singh, V.; Jinka, S.; Hake, K.; Parameswaran, S.; Kendall, R. J.; Ramkumar, S.

358

Novel natural sorbent for oil spill cleanup. Ind. Eng. Chem. Res. 2014, 53,

359

11954-11961.

360

(23) Franco, C. A.; Cortés, F. B.; Nassar, N. N. Adsorptive removal of oil spill from

361

oil-in-fresh water emulsions by hydrophobic alumina nanoparticles functionalized

ACS Paragon Plus Environment

Page 20 of 22

Page 21 of 22

Environmental Science & Technology

362

with petroleum vacuum residue. J. Colloid Interf. Sci. 2014, 425, 168-177.

363

(24) Önal, Y.; Akmil-Başar, C.; Sarıcı-Özdemir, Ç. Elucidation of the naproxen

364

sodium adsorption onto activated carbon prepared from waste apricot: kinetic,

365

equilibrium and thermodynamic characterization. J. Hazard. Mater. 2007, 148,

366

727-734.

367

ACS Paragon Plus Environment

Environmental Science & Technology

368

TOC

369 370

ACS Paragon Plus Environment

Page 22 of 22